Vertical heterostructures of transition metal dichalcogenides (TMDs) host interlayer excitons with electrons and holes residing in different layers. With respect to their intralayer counterparts, interlayer excitons feature longer lifetimes and diffusion lengths, paving the way for room temperature excitonic optoelectronic devices. The interlayer exciton formation process and its underlying physical mechanisms are largely unexplored. Here we use ultrafast transient absorption spectroscopy with a broadband white-light probe to simultaneously resolve interlayer charge transfer and interlayer exciton formation dynamics in a MoSe2/WSe2 heterostructure. We observe an interlayer exciton formation timescale nearly an order of magnitude (~1 ps) longer than the interlayer charge transfer time (~100 fs). Microscopic calculations attribute this relative delay to an interplay of a phonon-assisted interlayer exciton cascade and thermalization, and excitonic wave-function overlap. Our results may explain the efficient photocurrent generation observed in optoelectronic devices based on TMD heterostructures, as the interlayer excitons are able to dissociate during thermalization.
Similar content being viewed by others
Introduction
Monolayer (ML) transition metal dichalcogenides (TMDs) exhibit remarkable physical properties which make them an ideal platform to study exciton physics and to realize novel optoelectronic devices1. The dimensional reduction from bulk to 2D results in the formation of strongly bound excitons due to increased quantum confinement and reduced Coulomb screening, along with spin-valley locking due to the inversion symmetry breaking2,3. The ability to vertically stack multiple TMDs, forming van der Waals heterostructures (HS) without lattice matching constraints, has dramatically increased recent interest in these materials4. Despite the fact that weak out-of-plane interactions largely preserve the electronic structures of each layer, stacked HS display novel properties and functionalities not present in constituent monolayers. HS with Type II band alignment, where the valence band maximum and the conduction band minimum are in different layers, can host interlayer excitons (ILX) (Fig. 1a) which arise following interlayer charge transfer (ICT) (Fig. 1b)5,6,7 and consist of spatially separated Coulomb-bound electron-hole states with binding energies up to 100s meV8. The ILX in TMD-HS is commonly detected via its photoluminescence (PL) in the near-infrared (NIR), below the energy of the optical gap of the two layers (Fig. 1c)9,10,11,12,13. The ILX is characterized by a long recombination time (up to hundreds of nanoseconds14,15) and reduced oscillator strength (two orders of magnitude lower than that of intralayer excitons) due to the small spatial overlap of the electron and hole wave functions and, in some instances, their momentum-indirect character9,12,16,17,18. One of the most intriguing properties of TMD-HS is the lateral confinement of the ILX within moiré potentials, which are formed at small interlayer twist angles13,19,20,21,22.
ILX dynamics have been explored in different TMD-HS by time-resolved techniques8. The ILX recombination dynamics measured by time-resolved PL exhibit multiple decay components which exceed the recombination lifetimes of intralayer excitons by several orders of magnitude9,23. The ILX relaxation dynamics have also been indirectly inferred from the photobleaching (PB) dynamics of intralayer excitons as measured by transient absorption (TA) optical spectroscopy24. On the other hand, the formation dynamics of the ILX are very difficult to access directly due to several factors, including the weak oscillator strength25,26 and the rapidity of the ICT process that leads to ILX formation, which typically ranges from tens to hundreds of femtoseconds5,6,7,24,27,28. Time-resolved PL lacks the temporal resolution required to observe these processes. Attempts to resolve the transition from intralayer excitons to ILX have been done by measuring the formation of a novel 1s-2p transition in the mid-IR range29. More recently, time- and angle-resolved photoemission spectroscopy (tr-ARPES) experiments have addressed ILX formation dynamics30,31 by probing the energy-momentum dispersion of photoexcited quasiparticles in real time and distinguishing excitons from single particle states according to their energy-momentum dispersion31,32,33,34,35,36. A recent tr-ARPES study31 was able to track the ILX formation process following a phonon-assisted interlayer electron transfer as mediated by intermediate scattering to the Σ valleys, where Σ has also been referred to as the Q/Λ point12,37,38. Despite the strengths of this technique, the limited energy resolution and the extremely low intensity of the photoemission signal above the Fermi level complicates the ability to disentangle ILX formation from ICT dynamics39.
Here we use ultrafast optical TA spectroscopy to directly probe the transient optical response of the ILX in a MoSe2/WSe2 HS. These measurements are enabled by highly stable and broadband white light probe pulses spanning the visible to the NIR. The resulting high signal-to-noise measurements are capable of resolving the ILX formation dynamics through its weak TA signal (two orders of magnitude lower than the TA of the intralayer exciton) while simultaneously measuring intralayer exciton and interlayer hole transfer (IHT) dynamics. The ILX signal shows a delayed growth on a picosecond timescale, which is significantly longer than the experimentally measured 100-fs IHT process from MoSe2 to WSe2. We simulate the exciton dynamics by solving the microscopic Heisenberg equations of motion and find that the difference in formation timescales is due to phonon-assisted hole tunneling of photo-excited excitons which gives rise to hot ILX populations that quickly exchange energy and momentum with phonons. The relaxation down to the ILX ground state proceeds through multiple scattering processes involving higher energy interlayer s states. Our simulations demonstrate that these hot ILX populations contribute strongly to the WSe2 PB signal but only weakly to the optically bright ILX transition, resulting in the relative delay of the ILX signal as the populations cool.
Results
Experimental results
Experiments are performed on a large-area (mm-scale) MoSe2/WSe2 HS fabricated using a gold tape exfoliation method (see details in Supplementary Note 1.1)40. The HS is prepared with a 4∘, or near aligned, interlayer twist angle, characterized using polarization-resolved second harmonic generation (Supplementary Fig. 1a). We focus on the 4∘ HS in the main manuscript, though experiments were also performed on a nearly anti-aligned MoSe2/WSe2 HS with twist angle of 57∘ (Supplementary Fig. 1b). HS prepared with small twist angles away from either aligned (0∘) or anti-aligned (60∘) have been shown to have strong ILX PL signals11. A clear signature of the ILX in the 4∘ HS is the low-energy peak in the PL spectrum at ℏω = 1.35 eV (Fig. 1c) to the red of the intralayer PL peaks, which are quenched relative to the PL signals of the individual MLs (Supplementary Fig. 7). Both momentum-direct (K − K) and momentum-indirect (Σ − K) electron-hole transitions are expected to contribute to the PL of the ILX9,12,16,38 which can help to account for the width of the peak in Fig. 1c. We apply ultrafast TA spectroscopy with a broadband white-light continuum (WLC) probe to study the ILX formation dynamics. We selectively photoexcite the MoSe2 layer by tuning a narrow-band (10 nm) 70-fs pump pulse on resonance with the A exciton peak of MoSe2 (ℏω = 1.58 eV) with a fluence of 3 μJ/cm2 (Supplementary Fig. 2a). For simplicity, when discussing the experimental results, we adopt a notation for the intralayer A and B excitons of each layer using a subscript corresponding to the layer’s transition metal (AX and BX where X = Mo or W). The WLC probe beam is generated in an yttrium aluminum garnet (YAG) crystal pumped by a 1 eV pulse and spans a broad spectral window (1.2–2.3 eV) that includes both intralayer excitons and the ILX of the HS (Supplementary Fig. 2a). The pump and probe are focused to spot diameters on the order of 100 μm, such that sample heterogeneity contributes to inhomogeneous broadening of the TA peaks. Unless otherwise stated, the pump and probe pulses are co-circularly polarized such that they access the (K − K) optical transitions.
Figure 2a reports a 2D map of the differential transmission (ΔT/T) signal at 77 K as a function of pump-probe delay and probe photon energy. The spectrum is dominated by positive PB signals (red contours) at the energies of the intralayer excitons of both layers (i.e. AMo, AW, BMo, BW) with signal strengths on the order of ΔT/T ~ 10−2. The transient signal at the energy of AMo exciton displays an instantaneous (i.e. pulsewidth-limited) build-up and is the result of the interplay of multiple processes, including quenching of the exciton oscillator strength due to phase-space filling, energy renormalization, and lineshape broadening of the exciton resonance due to Coulomb many-body effects41. The same formation dynamics are observed for the BMo resonance as a consequence of the exchange-driven mixing of the excitons in the (K − K) valley42 and light-induced reduction of the Coulomb screening, leading to an instantaneous renormalization of the exciton resonances43. Following excitation of the AMo exciton, the AW resonance shows a delayed PB due to IHT from MoSe2 to WSe2. The finite build-up time of the AW PB signal (0.20 ± 0.06 ps, Fig. 2c) provides a direct estimate of the timescale of the hole scattering process, which is in good agreement with previous observations24. The BW excitonic resonance shows the same delayed signal formation owing to coupling with the AW exciton.
Focusing on the ILX energy region of the 2D ΔT/T map below the optical gap of the intralayer excitons, the TA spectrum at 4 ps pump-probe delay shows a broad peak with a signal strength ΔT/T ~ 10−4 (Fig. 2b). We confirm that this peak is unique to the HS through control measurements on isolated MoSe2 and WSe2 MLs (see Supplementary Note 2.5) and attribute it to PB of the ILX following IHT. The relative strengths of the TA signals of the intralayer excitons and of the ILX are in good agreement with the two orders of magnitude difference in the static transition dipole moments predicted by theory44 and measured experimentally25,26. Moreover, ILX exhibits valley circular dichroism as reported in Supplementary Note 2.6. We note that the ILX signature is peaked at slightly higher energy in the TA measurements compared to the ILX emission peak in Fig. 1. We attribute this energy mismatch to the fact that the optically bright ILX signal measured via TA is dominated by momentum-direct (K − K) transitions26 compared to the ILX PL signal which includes contributions from momentum-direct and momentum-indirect transitions12,17. Figure 2c reports the formation dynamics of the ILX. Compared with the dynamics of AMo and AW excitons (red and purple, respectively in Fig. 2c), the ILX TA signal (green) shows a remarkably slower formation timescale (0.8 ± 0.3 ps), significantly longer than the timescale of IHT. This behavior suggests that the optically bright ILX does not form immediately upon IHT and that inferring ILX formation timescales from ICT signatures may be inadequate. The instantaneous peak in the ILX TA signal is due to the weak coherent artifact of the substrate during the pulse overlap, as confirmed by a control measurement on a blank substrate (see Supplementary Note 2.4). This weak coherent signal is not observed at AW due to its much higher signal strength.
A recent ultrafast TA experiment performed with excitation densities above the exciton Mott transition reported the generation of an interlayer electron-hole plasma whose optical signature consisted of a broad photoinduced absorption (PIA) plateau extending below the optical gap of the HS14. The peak we observe at 1.37 eV is not related to this effect because (i) our excitation density (≈3.6 × 1011cm−2, see Methods for details) is well below the Mott threshold and (ii) the ILX signal shows a positive signal consistent with a PB signature. At higher excitation densities, we find that the ILX PB signal persists while a negative PIA signal, related to pump-induced modification of the AMo excitonic resonance43, increases in strength with fluence until it obscures the weak ILX signature (Supplementary Fig. 9).
Theoretical model
To understand the observed delayed rise in the ILX signal compared to the IHT process, we developed a microscopic model45,46 for the exciton dynamics in a perfectly aligned (i.e. 0∘ twist angle) MoSe2/WSe2 HS. A complete picture of the momentum-resolved formation and decay dynamics of excitons is achieved by solving the excitonic Bloch equations for the coherent excitonic polarizations, P, and the incoherent excitonic populations, N47. In our model, we include one optically excited excitonic polarization, PMo, which decays into incoherent exciton populations, N, by exciton-phonon scattering processes48. The incoherent intralayer population contributions considered in our model, \({N}^{Mo/W,{\xi }_{e}}\), are denoted by a superscript ξe corresponding to the valley location of the electron where \({\xi }_{e}=K/{K}^{{\prime} }/{{\Sigma }}/{{{\Sigma }}}^{{\prime} }\) (holes are always located at the K valley of the MoSe2 layer). The considered ILX population is similarly denoted as \({N}^{IL,{\xi }_{e}}\) (hole always at the K valley of the WSe2 layer).
In Fig. 3a–d we sketch the sequence of excitation and scattering processes leading to the formation of the incoherent excitonic populations included in our model. After the optical excitation (Fig. 3a), intraband phonon scattering leads to a decay of exciton polarization, PMo, in expense of the nearly instantaneous formation of an intravalley incoherent exciton population at the K valley of MoSe2 layer, NMo,K. Subsequent intervalley phonon-assisted electron scattering depletes the population NMo,K, leading to the formation of intervalley excitons within the MoSe2, \({N}^{Mo,{K}^{{\prime} }/{{\Sigma }}/{{{\Sigma }}}^{{\prime} }}\) (Fig. 3b). In the model, we include electron scattering to the \({{\Sigma }}/{{{\Sigma }}}^{{\prime} }\) valleys which, in this particular HS, are energetically close to the \(K/{K}^{{\prime} }\) valleys because of the strong interlayer hybridization (see Supplementary Note 1.4). Finally, interlayer phonon-assisted hole tunneling to the K valley of WSe2 results in the formation of momentum direct ILX populations, NIL,K, and momentum indirect ILX populations, \({N}^{IL,{K}^{{\prime} }/{{\Sigma }}/{{{\Sigma }}}^{{\prime} }}\), with electrons located at the K or \({K}^{{\prime} }/{{\Sigma }}/{{{\Sigma }}}^{{\prime} }\) valleys in the MoSe2 layer and holes located at the K valley in the WSe2 layer (Fig. 3c).
The differential transmission signals (DTS) (Eq. (2) in the Methods section) calculated from these dynamics (Fig. 3a–c) are depicted in Fig. 3d. Different probe energies of AMo, (Eq. (6)), AW (Eq. (7)), and the momentum-direct ILX (Eq. (8)) are considered. The DTS temporal signatures emerge due to Pauli-blocking processes: Electrons and/or holes forming coherent excitonic polarizations and incoherent excitonic populations (PMo, \({N}^{Mo,{\xi }_{e}}\) and \({N}^{IL,{\xi }_{e}}\)) reduce the absorption of the corresponding optical transition and lead to a positive DTS signal. Excitonic effects are manifest in the Pauli-blocking weights (Eqs. (2), (3) in the “Methods” section). These weights are momentum-dependent such that excitonic populations can still contribute to the DTS even if they lie outside the light cone. In this way, excitons encode information on the Pauli blocking of the electron and hole momentum distribution and define the DTS. The calculated DTS timetraces are reported in Fig. 3e together with the bleaching contributions of the individual excitonic populations, Fig. 3f–h. The DTS calculations qualitatively reproduce the experimental dynamics of intralayer excitons and the ILX (Fig. 2c), in particular their different formation timescales. We discuss now the signals at AMo (i), AW (ii) and ILX (iii).
(i) The DTS of AMo exhibits a sharp rise followed by a fast decay and a second delayed rise component (Fig. 3f). The sharp initial peak is mainly due to Pauli-blocking by the instantaneous coherent exciton polarization photoexcited at the K valley (pink line, Fig. 3f) and by the Pauli-blocking weighted incoherent excitonic populations formed in the MoSe2 layer following phonon-mediated dephasing (blue lines, Fig. 3). The second delayed rise component originates from the Pauli-blocking contribution of ILX populations (black line, Fig. 3f) following the decay of intralayer exciton populations via phonon-assisted hole tunneling. This behavior of MoSe2 is also present in the experimental transient optical response of the HS (Fig. 2). A comparison of the DTS signals, both measured and calculated, for the AMo exciton of an isolated ML and the HS (Supplementary Fig. S16) confirms that the presence of ILX populations strongly affects the DTS dynamics of the intralayer AMo transition.
(ii) The DTS of AW displays a longer formation time than for AMo as the signal is not influenced by the excitonic intralayer populations in MoSe2 (Fig. 3g). Here, only the ILX populations arising from IHT contribute to the Pauli-blocking of the AW signal.
(iii) The DTS of ILX shows similar behavior as the AW but with a significantly longer risetime (Fig. 3h). We attribute this longer formation time to the relaxation dynamics of hot ILX populations, represented schematically in Fig. 4a. The difference of the risetimes of the DTS at AW and at the ILX occurs because hot ILX populations unequally contribute to the Pauli-blocking of AW and ILX: Since the binding energies of the ILX (≈100 meV) are lower than the difference between the transition energies of AMo and ILX (≈300 meV), phonon-mediated hole transfer creates hot ILX populations, NIL,ξ (Fig. 4a). Figure 4 shows how these populations scatter to lower-energy momenta and bound states via optical and acoustic phonons until most of the interlayer populations are in the 1s state. In the following time period, the hot ILX slowly thermalize into a Boltzmann distribution. Figure 4b shows the calculated momentum-dependent ILX populations of the 1s state at different times. Following IHT, the ILX population is initially peaked at higher momenta, after which phonon-assisted scattering processes gradually confine the ILX populations to lower momenta.
This behavior along with the Pauli-blocking weights of the ILX and AW transitions (green and purple shaded areas, respectively, in Fig. 4b) translates into the DTS and determines the different DTS dynamics. Therefore, the physical origin of the relative delay in the DTS of AW and ILX can be explained as the following. The larger binding energy of the AW exciton compared to the ILX leads to a Pauli-blocking weight displaying a broad momentum distribution compared to the ILX Pauli-blocking weight, as shown in Fig. 4b (see Supplementary Note 1.6). This results in the increased sensitivity of the intralayer AW transition to the overall excitonic population, whereas the probed ILX transition is mainly sensitive to the low-momenta states. Consequently, only the cold and lowest-energy bound ILX populations populated at later delay times significantly contribute to the DTS signal of the ILX transition in Fig. 3h, while the delayed risetime of the ILX compared to the AW is related to the longer timescale of thermalization of the hot ILX populations. By directly comparing the DTS signals of the probed AW and ILX transitions, we are able to trace the microscopic mechanisms of the ILX formation and relaxation processes.
All the theoretical results shown so far hold for a HS characterized by a 0∘ twist angle. Small and finite twist angle effects are not taken into account in our model because we do not expect small twist angles to greatly influence the ILX dynamics. Because of the fermionic character of electron and hole forming the exciton as a quasi-boson, finite center-of-mass (COM) excitons lead to bleaching of the bright excitonic transitions via Pauli blocking and result in DTS dynamics that are only weakly dependent on the twist angle at the relatively small angles deviating from perfectly aligned and anti-aligned stacking11. This assumption is supported by transient optical experiments which have shown the timescale of ICT processes (and consequently hot ILX formation) to be weakly dependent on the angular alignment and thus the momentum mismatch between the two layers49,50.
Discussion
We have used TA spectroscopy with a combination of high sensitivity and broad spectral coverage to directly track the formation dynamics of ILX in a TMD HS. We find that ILX PB signal rises on a picosecond timescale, significantly slower than the build-up dynamics of intralayer exciton PB signals in general and of IHT specifically. Microscopic calculations reproduce the experimental transient signals and explain the formation timescale in terms of different contributions. The hundreds of femtoseconds build-up time of the WSe2 PB signal is mainly related to interlayer scattering of hot holes and therefore represents a rather direct estimation of the hot carrier injection process between the TMD layers of the HS. The slower rise time of the ILX signal is the result of the combination of two scattering processes: (1) phonon-mediated exciton cascade process from unbound and/or higher energy excitonic s states to the ground state and (2) intra-exciton energy and momentum relaxation of hot ILX populations. Our simulations also demonstrate that the dynamics of optically bright intra- and inter- layer excitons are influenced by optically dark momentum-indirect excitons.
Besides its fundamental interest, the delayed ILX formation observed and discussed here could explain a long-standing puzzle in optoelectronic devices based on TMD HS, namely the observation of efficient generation of photocurrent despite the large binding energy of the ILX51,52,53,54,55. During their several-hundred femtosecond thermalization process, in fact, the hot ILX have an opportunity to dissociate and form free charge carriers. We foresee that our combined theoretical-experimental approach can be extended to study in real-time exciton formation process in other systems, such as hybrid organic/TMD HS56 and mixed dimensional van der Waals HS57.
Methods
Sample preparation
Large-area MoSe2/WSe2 HS are prepared using a modified gold tape exfoliation method40 resulting in mm-scale ML flakes deposited onto 200 μm thick transparent SiO2 substrates. TMD HS with varying twist angles are prepared and characterized using polarization-resolved second harmonic generation (Supplementary Fig. 1). We have mainly reported the static and time-domain measurements on a near aligned HS with a 4∘ twist angle. Similar measurements were performed on a near anti-aligned HS characterized by 57∘ twist angle (Supplementary Fig. 18). The HS are prepared with unoverlapped regions where the individual ML can be accessed for control measurements.
Transient absorption spectroscopy
Time-resolved and static optical measurements are performed at 77 K. TA spectroscopy measurements are performed in a transmission geometry (Supplementary Fig. 2b) with pump and probe beam diameters of 200 μm and 100 μm at the sample surface, respectively. The relatively large sample region accessed in these TA experiments represents a sort of ensemble measurement where sample heterogeneity contributes to the inhomogeneous broadening, as seen previously on similar samples6. The delay dependent ΔT/T map and spectra in Fig. 2a, b are measured by dispersing the transmitted broadband probe and acquiring it with a fast silicon spectrometer (Entwicklungsbuero EB Stresing) working at 1 kHz laser repetition rate. The probe pulse is a WLC generated by focusing the output of a homemade NIR Optical Parametric Amplifier (OPA) centered at 1 eV into a YAG plate; the WLC spectrum extends from 1.2 to 2.3 eV, covering A/B intralayer and ILX of the HS (Supplementary Fig. 2a). The NIR OPA is seeded with a regeneratively amplified Ti-sapphire laser (Coherent, Libra) emitting 100-fs pulses at 1.55 eV at a repetition rate of 1 kHz. The pump pulse is generated by a narrowband OPA tuned to the AMo excitonic resonance (ℏω = 1.59 eV) and modulated at half the repetition rate of the laser. The exciton density of ≈ 3.6 × 1011cm−2 is calculated using the pump fluence of 2.8 μJ cm−1, the pump spectrum and the linear absorption spectrum of the TMD HS at 77 K (Supplementary Fig. 2). The temporal dynamics of the excitonic resonances (Fig. 2c) are measured by a second TA optical setup based on a Yb:KGW regenerative amplifier (Pharos, Light Conversion) providing 200-fs pulses at 1.2 eV and at a higher repetition rate of 100 kHz. The pump pulse is generated by the second harmonic of a near-IR OPA58 tuned to the same energy and fluence conditions as experiments performed on the lower repetition rate TA setup. The WLC is generated by focusing the fundamental of the laser into a YAG crystal. The transmitted probe beam is then sent to a monochromator and a photodiode for lock-in detection. The pump is modulated by a Pockels cell to 50 kHz allowing to reach higher signal-to-noise ratio with respect to the 1 kHz system. The rise times of the TA signals are estimated by fitting the time traces with a rising exponential convoluted with a Gaussian function with full width at half maximum of the instrument response function (FWHM-IRF) of the respective TA setup. The estimated FWHM-IRF is 140 fs for both TA instruments.
Theoretical calculations
To obtain the DTS theoretically, we solve the Bloch equations for the excitonic polarizations \({P}_{\mu,{{{{{{{\bf{Q}}}}}}}}}^{i}=\langle {\hat{P}}_{\mu,{{{{{{{\bf{Q}}}}}}}}}^{i}\rangle\) up to third order in the electric field as in ref. 45. Here, \({\hat{P}}_{\mu,{{{{{{{\bf{Q}}}}}}}}}^{i}\) are the excitonic operators46 carrying excitonic radial quantum number μ, center of mass momentum Q and compound layer and valley index i = {lh, ξh, le, ξe} with electron/hole layer le/h = M/W for MoSe2 and WSe2, electron valley index \({\xi }_{e}=K/{K}^{{\prime} }/{{\Sigma }}/{{{\Sigma }}}^{{\prime} }\) and hole valley index ξh = K. Performing a linearization in the weak probe pulse limit59, we are able to separate the pump induced coherent polarizations \({P}_{\mu,{{{{{{{\bf{Q}}}}}}}}}^{i}\) and incoherent populations
from the probe-induced dynamics. The coupled equations of motion47 are then solved in the time domain. The hole tunneling process is implemented as in ref. 60. The subscript c in Eq. (1) accounts for the purely correlated (or incoherent) part of the expectation value in the spirit of ref. 47,61. By assuming a Dirac delta-shaped probe pulse, we find an expression for the probe- and pump-induced macroscopic polarization \({{{{{{{{\bf{P}}}}}}}}}^{i}=\frac{1}{A}{\sum }_{\mu }{{{{{{{{\bf{d}}}}}}}}}_{\mu }^{i}{P}_{\mu,{{{{{{{\bf{Q}}}}}}}}={{{{{{{\bf{0}}}}}}}}}^{i}\) which couples to Maxwell’s equations giving the total electric field and therefore the transmission at the HS as in ref. 62,63. Here, \({{{{{{{{\bf{d}}}}}}}}}_{\mu }^{i}\) is the excitonic dipole moment and A is the illuminated area of the sample. The DTS is then given by subtracting the transmission Tt of the probe pulse without pump pulse from the transmission Tt+p of the probe pulse with pump pulse: ΔT(ω, τ) = Tt+p(ω, τ) − Tt(ω)64. In our case, since we are only interested in timetraces, we neglect Coulomb renormalization and nonlinear broadening65 and focus solely on the Pauli-blocking induced PB dynamics, so that the DTS signal dependent on the time delay τ between pump and probe pulses can be expressed as
where the matrix elements are given by
Here, \({{{{{{{{\bf{d}}}}}}}}}_{\mu }^{i}={\sum }_{{{{{{{{\bf{q}}}}}}}}}{\varphi }_{\mu,{{{{{{{\bf{q}}}}}}}}}^{i}{{{{{{{{\bf{d}}}}}}}}}_{{{{{{{{\bf{q}}}}}}}}}^{*,cv,i}\) are the excitonic and \({{{{{{{{\bf{d}}}}}}}}}_{{{{{{{{\bf{q}}}}}}}}}^{cv,i}\) the electronic dipole moments, \({\varphi }_{\mu,{{{{{{{\bf{q}}}}}}}}}^{i}\) are the excitonic wave functions obtained by solving the Wannier equation for the respective excitonic configuration i with radial quantum number μ and relative momentum q. αi and βi are the ratios of the effective masses37. In Eq. (3), the indices μ and i refer to the optically bright probed transition, whereas ν and \({i}^{{\prime} }\) reflect the bright as well as dark excitonic populations responsible for the Pauli blocking. These matrix elements can be viewed as convolutions in momentum space of the excitonic wave functions \({\varphi }_{\mu,{{{{{{{\bf{q}}}}}}}}}^{i}\) of the probed transitions i with the excitonic wave functions \({\varphi }_{\nu,{{{{{{{\bf{q}}}}}}}}}^{{i}^{{\prime} }}\) of the pumped populations \({i}^{{\prime} }\) and constitute the crucial part of the explanation regarding the different DTS risetimes of the AW and ILX transition as described in the Results section. The Wannier equation is solved for a HS using a Coulomb potential for two dielectric slabs in three dielectric environments, ϵ1 = 3.9 (SiO2 substrate on the MoSe2 side), ϵg = 1 (assuming a vacuum environment between the layers) and ϵ2 = 1 (vacuum on the WSe2 side), as in ref. 66. Our calculation includes both high energy bound exciton interlayer s states and unbound states above the band edge.
In the following, and to be in line with the notation used in the main part of the manuscript, we denote the excitonic populations under consideration as:
and the excitonic coherent polarizations as:
Therefore, the DTS signal for the probed AMo transition reads explicitly:
for the probed AW transition we obtain:
and for the probed ILX transition it reads:
Equation (6) displays the contribution of the probed AMo transition (red ellipse in Fig. 3d) with Pauli blocking due to electron and hole of the pumped momentum-direct excitonic polarizations PMo and populations NMo,K (first two terms) as well as due to the blocking of the hole of momentum-indirect excitonic populations \({N}^{Mo,{K}^{{\prime} }/{{\Sigma }}/{{{\Sigma }}}^{{\prime} }}\) (third term) and blocking of the electron of momentum-direct interlayer populations NIL,K (last term). Equation (7) describes the probed AW transition (purple ellipse in Fig. 3d) with Pauli blocking contributions due to holes of all four possible interlayer populations \({N}^{IL,{\xi }_{e}}\). Equation (8) shows the probed ILX transition (green ellipse in Fig. 3d), where the first two terms account for Pauli blocking due to the electron of the pumped momentum-direct excitonic polarizations PMo and populations NMo,K, the third term accounts for the blocking of electron and hole of the momentum-direct interlayer population NIL,K, whereas the last term shows the contribution of the PB by the hole of the other momentum-indirect interlayer populations \({N}^{IL,{K}^{{\prime} }/{{\Sigma }}/{{{\Sigma }}}^{{\prime} }}\). All Pauli blocking terms feature distinctive momentum- and excitonic quantum number-dependent Pauli-blocking weights \({D}_{{{{{{{{\bf{Q}}}}}}}},\mu,\nu }^{e/h,i,{i}^{{\prime} }}\), which are given in Eq. (3).
Data availability
The processed spectroscopic data of the manuscript are available at https://doi.org/10.6084/m9.figshare.24428992. Supplementary information data will be made available by request to the corresponding authors.
Code availability
Code pertaining to the theoretical model in this work will be made available by request to the corresponding authors.
References
Wang, Q. H., Kalantar-Zadeh, K., Kis, A., Coleman, J. N. & Strano, M. S. Electronics and optoelectronics of two-dimensional transition metal dichalcogenides. Nat. Nanotechnol. 7, 699–712 (2012).
Qiu, D. Y., da Jornada, F. H. & Louie, S. G. Optical spectrum of MoS2: many-body effects and diversity of exciton states. Phys. Rev. Lett. 111, 216805 (2013).
Schaibley, J. R. et al. Valleytronics in 2D materials. Nat. Rev. Mater. 1, 16055 (2016).
Geim, A. K. & Grigorieva, I. V. Van der Waals heterostructures. Nature 499, 419–425 (2013).
Hong, X. et al. Ultrafast charge transfer in atomically thin MoS2/WS2 heterostructures. Nat. Nanotechnol. 9, 682–686 (2014).
Policht, V. R. et al. Dissecting interlayer hole and electron transfer in transition metal dichalcogenide heterostructures via two-dimensional electronic spectroscopy. Nano Lett. 21, 4738–4743 (2021).
Purz, T. L. et al. Coherent exciton-exciton interactions and exciton dynamics in a MoSe2/WSe2 heterostructure. Phys. Rev. B 104, 1–6 (2021).
Jiang, Y., Chen, S., Zheng, W., Zheng, B. & Pan, A. Interlayer exciton formation, relaxation, and transport in TMD van der Waals heterostructures. Light Sci. Appl. 10, 1–29 (2021).
Rivera, P. et al. Observation of long-lived interlayer excitons in monolayer MoSe2-WSe2 heterostructures. Nat. Commun. 6, 6242 (2015).
Nagler, P. et al. Giant magnetic splitting inducing near-unity valley polarization in van der Waals heterostructures. Nat. Commun. 8, 1–6 (2017).
Nayak, P. K. et al. Probing evolution of twist-angle-dependent interlayer excitons in MoSe2/WSe2 van der Waals heterostructures. ACS Nano 11, 4041–4050 (2017).
Hanbicki, A. T. et al. Double indirect interlayer exciton in a MoSe2/WSe2 van der Waals heterostructure. ACS Nano 12, 4719–4726 (2018).
Tran, K. et al. Evidence for moiré excitons in van der Waals heterostructures. Nature 567, 71–75 (2019).
Wang, J. et al. Optical generation of high carrier densities in 2D semiconductor heterobilayers. Sci. Adv. 5, 2–10 (2019).
Jauregui, L. A. et al. Electrical control of interlayer exciton dynamics in atomically thin heterostructures. Science 366, 870–875 (2019).
Miller, B. et al. Long-lived direct and indirect interlayer excitons in van der Waals heterostructures. Nano Lett. 17, 5229–5237 (2017).
Okada, M. et al. Direct and indirect interlayer excitons in a van der Waals heterostructure of hBN/WS2/MoS2/hBN. ACS Nano 12, 2498–2505 (2018).
Kunstmann, J. et al. Momentum-space indirect interlayer excitons in transition-metal dichalcogenide van der Waals heterostructures. Nat. Phys. 14, 801–805 (2018).
Jin, C. et al. Observation of moiré excitons in WSe2/WS2 heterostructure superlattices. Nature 567, 76–80 (2019).
Alexeev, E. M. et al. Resonantly hybridized excitons in moiré superlattices in van der Waals heterostructures. Nature 567, 81–86 (2019).
Seyler, K. L. et al. Signatures of moiré-trapped valley excitons in MoSe2/WSe2 heterobilayers. Nature 567, 66–70 (2019).
Huang, D., Choi, J., Shih, C. K. & Li, X. Excitons in semiconductor moiré superlattices. Nat. Nanotechnol. 17, 227–238 (2022).
Nagler, P. et al. Interlayer exciton dynamics in a dichalcogenide monolayer heterostructure. 2D Mater. 4, 025112 (2017).
Wang, Z. et al. Phonon-mediated interlayer charge separation and recombination in a MoSe2/WSe2 heterostructure. Nano Lett. 21, 2165–2173 (2021).
Ross, J. S. et al. Interlayer exciton optoelectronics in a 2D heterostructure p-n junction. Nano Lett. 17, 638–643 (2017).
Barré, E. et al. Optical absorption of interlayer excitons in transition-metal dichalcogenide heterostructures. Science 376, 406–410 (2022).
Liu, F., Li, Q. & Zhu, X. Y. Direct determination of momentum-resolved electron transfer in the photoexcited van der Waals heterobilayer WS2/MoS2. Phys. Rev. B 101, 201405 (2020).
Zimmermann, J. E. et al. Ultrafast charge-transfer dynamics in twisted MoS2/WSe2 heterostructures. ACS Nano 15, 14725–14731 (2021).
Merkl, P. et al. Ultrafast transition between exciton phases in van der Waals heterostructures. Nat. Mater. 18, 691–696 (2019).
Karni, O. et al. Structure of the moiré exciton captured by imaging its electron and hole. Nature 603, 247–252 (2022).
Schmitt, D. et al. Formation of moiré interlayer excitons in space and time. Nature 608, 1–6 (2022).
Perfetto, E., Sangalli, D., Marini, A. & Stefanucci, G. First-principles approach to excitons in time-resolved and angle-resolved photoemission spectra. Phys. Rev. B 94, 245303 (2016).
Rustagi, A. & Kemper, A. F. Photoemission signature of excitons. Phys. Rev. B 97, 1–7 (2018).
Christiansen, D., Selig, M., Malic, E., Ernstorfer, R. & Knorr, A. Theory of exciton dynamics in time-resolved ARPES: Intra- and intervalley scattering in two-dimensional semiconductors. Phys. Rev. B 100, 205401 (2019).
Dong, S. et al. Direct measurement of key exciton properties: energy, dynamics, and spatial distribution of the wave function. Nat. Sci. 1, 1–8 (2021).
Man, M. K. L. et al. Experimental measurement of the intrinsic excitonic wave function. Sci. Adv. 7, 1–7 (2021).
Kormányos, A. et al. k ⋅ p theory for two-dimensional transition metal dichalcogenide semiconductors. 2D Mater. 2, 022001 (2015).
Rivera, P. et al. Interlayer valley excitons in heterobilayers of transition metal dichalcogenides. Nat. Nanotechnol. 13, 1004–1015 (2018).
Lee, W. et al. Time-resolved ARPES determination of a quasi-particle band gap and hot electron dynamics in monolayer MoS2. Nano Lett. 21, 7363–7370 (2021).
Liu, F. et al. Disassembling 2D van der Waals crystals into macroscopic monolayers and reassembling into artificial lattices. Science 367, 903–906 (2020).
Trovatello, C. et al. Disentangling many-body effects in the coherent optical response of 2D semiconductors. Nano Lett. 22, 5322–5329 (2022).
Guo, L. et al. Exchange-driven intravalley mixing of excitons in monolayer transition metal dichalcogenides. Nat. Phys. 15, 228–232 (2019).
Pogna, E. A. A. et al. Photo-induced bandgap renormalization governs the ultrafast response of single-layer MoS2. ACS Nano 10, 1182–1188 (2016).
Yu, H., Wang, Y., Tong, Q., Xu, X. & Yao, W. Anomalous light cones and valley optical selection rules of interlayer excitons in twisted heterobilayers. Phys. Rev. Lett. 115, 1–5 (2015).
Selig, M. et al. Ultrafast dynamics in monolayer transition metal dichalcogenides: interplay of dark excitons, phonons, and intervalley exchange. Phys. Rev. Res. 1, 1–6 (2019).
Katsch, F., Selig, M., Carmele, A. & Knorr, A. Theory of exciton-exciton interactions in monolayer transition metal dichalcogenides. Phys. Status Solidi (B) Basic Res. 255, 1–16 (2018).
Thränhardt, A., Kuckenburg, S., Knorr, A., Meier, T. & Koch, S. W. Quantum theory of phonon-assisted exciton formation and luminescence in semiconductor quantum wells. Phys. Rev. B 62, 2706–2720 (2000).
Selig, M. et al. Dark and bright exciton formation, thermalization, and photoluminescence in monolayer transition metal dichalcogenides. 2D Mater. 5, 035017 (2018).
Zhu, H. et al. Interfacial charge transfer circumventing momentum mismatch at two-dimensional van der Waals heterojunctions. Nano Lett. 17, 3591–3598 (2017).
Ji, Z. et al. Robust stacking-independent ultrafast charge transfer in MoS2/WS2 bilayers. ACS Nano 11, 12020–12026 (2017).
Bernardi, M., Palummo, M. & Grossman, J. C. Extraordinary sunlight absorption and one nanometer thick photovoltaics using two-dimensional monolayer materials. Nano Lett. 13, 3664–3670 (2013).
Lee, C.-H. et al. Atomically thin p-n junctions with van der Waals heterointerfaces. Nat. Nanotechnol. 9, 676–681 (2014).
Furchi, M. M., Pospischil, A., Libisch, F., Burgdörfer, J. & Mueller, T. Photovoltaic effect in an electrically tunable Van der Waals heterojunction. Nano Lett. 14, 4785–4791 (2014).
Cheng, R. et al. Electroluminescence and photocurrent generation from atomically sharp WSe2/MoS2 heterojunction p-n diodes. Nano Lett. 14, 5590–5597 (2014).
Zhang, K. et al. Interlayer transition and infrared photodetection in atomically thin type-II MoTe2/MoS2 van der Waals heterostructures. ACS Nano 10, 3852–3858 (2016).
Zhu, T. et al. Highly mobile charge-transfer excitons in two-dimensional WS2/tetracene heterostructures. Sci. Adv. 4, 1–9 (2018).
Jariwala, D., Sangwan, V. K., Lauhon, L. J., Marks, T. J. & Hersam, M. C. Emerging device applications for semiconducting two-dimensional transition metal dichalcogenides. ACS Nano 8, 1102–1120 (2014).
Villa, A. et al. Broadly tunable mid-infrared femtosecond pulses directly generated by an optical parametric amplifier. OSA Contin. 4, 2837 (2021).
Wegener, M., Chemla, D. S., Schmitt-Rink, S. & Schäfer, W. Line shape of time-resolved four-wave mixing. Phys. Rev. A 42, 5675–5683 (1990).
Holler, J. et al. Interlayer exciton valley polarization dynamics in large magnetic fields. Phys. Rev. B 105, 1–9 (2021).
Fricke, J. Transport equations including many-particle correlations for an arbitrary quantum system: a general formalism. Ann. Phys. 252, 479–498 (1996).
Hübner, M. et al. Collective effects of excitons in multiple-quantum-well Bragg and anti-Bragg structures. Phys. Rev. Lett. 76, 4199–4202 (1996).
Knorr, A., Hughes, S., Stroucken, T. & Koch, S. Theory of ultrafast spatio-temporal dynamics in semiconductor heterostructures. Chem. Phys. 210, 27–47 (1996).
Malic, E. & Knorr, A. Graphene and Carbon Nanotubes (Wiley, 2013).
Katsch, F., Selig, M. & Knorr, A. Exciton-scattering-induced dephasing in two-dimensional semiconductors. Phys. Rev. Lett. 124, 257402 (2020).
Ovesen, S. et al. Interlayer exciton dynamics in van der Waals heterostructures. Commun. Phys. 2, 23 (2019).
Acknowledgements
We are grateful to C. J. Sayers for helpful discussions and acknowledge F. Morabito, C. Trovatello, A. Genco, S. Sardar and C. D’Andrea for experimental contributions. We would like to thank the IT and data services members of Zuse Institute Berlin for providing the computing infrastructure. S.D.C. acknowledge financial support from MIUR through the PRIN 2017 Programme (Prot. 20172H2SC4). G.C. acknowledge support by the European Union Horizon 2020 Programme under Grant Agreement 881603 Graphene Core 3. X.Y.Z. acknowledges support for sample fabrication by the Materials Science and Engineering Research Center (MRSEC) through NSF grant DMR-2011738. F.S. and A.V. acknowledge support by the European Research Council (ERC) under the European Union’s Horizon 2020 research and innovation programme (grant agreement No. 816313). We acknowledge financial support from the Deutsche Forschungsgemeinschaft (DFG) through SFB 951 Project No. 182087777 (M.K., M.S., and A.K) and Project KN 427/11-2 (H.M. and A.K.) Project No. 420760124.
Author information
Authors and Affiliations
Contributions
V.R.P. and S.D.C. devised the experimental work. V.R.P., O.D., and A.V. performed the experimental work; V.R.P. and O.D. performed data analysis. H.M., M.K., and B.K. performed the theoretical work. Q.L. prepared and characterized the TMD HS samples. All authors contributed to the interpretation of the results and preparation of the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Xianghong Niu, and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Policht, V.R., Mittenzwey, H., Dogadov, O. et al. Time-domain observation of interlayer exciton formation and thermalization in a MoSe2/WSe2 heterostructure. Nat Commun 14, 7273 (2023). https://doi.org/10.1038/s41467-023-42915-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-023-42915-x
- Springer Nature Limited
This article is cited by
-
Correlation-driven nonequilibrium exciton site transition in a WSe2/WS2 moiré supercell
Nature Communications (2024)