Abstract
Electrochemical oxygen reduction could proceed via either 4e−-pathway toward maximum chemical-to-electric energy conversion or 2e−-pathway toward onsite H2O2 production. Bulk Pt catalysts are known as the best monometallic materials catalyzing O2-to-H2O conversion, however, controversies on the reduction product selectivity are noted for atomic dispersed Pt catalysts. Here, we prepare a series of carbon supported Pt single atom catalyst with varied neighboring dopants and Pt site densities to investigate the local coordination environment effect on branching oxygen reduction pathway. Manipulation of 2e− or 4e− reduction pathways is demonstrated through modification of the Pt coordination environment from Pt-C to Pt-N-C and Pt-S-C, giving rise to a controlled H2O2 selectivity from 23.3% to 81.4% and a turnover frequency ratio of H2O2/H2O from 0.30 to 2.67 at 0.4 V versus reversible hydrogen electrode. Energetic analysis suggests both 2e− and 4e− pathways share a common intermediate of *OOH, Pt-C motif favors its dissociative reduction while Pt-S and Pt-N motifs prefer its direct protonation into H2O2. By taking the Pt-N-C catalyst as a stereotype, we further demonstrate that the maximum H2O2 selectivity can be manipulated from 70 to 20% with increasing Pt site density, providing hints for regulating the stepwise oxygen reduction in different application scenarios.
Similar content being viewed by others
Introduction
Electrocatalytic oxygen reduction reaction (ORR) is an important reaction in the process of renewable energy conversion and utilization. Molecular O2 can be reduced via a 4e−-pathway into H2O or via a 2e−-pathway into H2O2. The former serves as the vital reaction in proton exchange membrane fuel cells (PEMFCs) and metal-air batteries to maximize chemical energy conversion efficiency1,2,3, the latter represents an environmentally benign method for the onsite production of hydrogen peroxide commodity4,5,6,7. Therefore, a facile ORR reaction pathway tuning is highly demanded for both fundamental mechanistic investigations and different application scenarios.
Earlier theoretical studies suggest the above two ORR pathways share a common intermediate of *OOH, for which its binding strength determines the reaction products8. A strong binding of *OOH with a parallel orientation to electrode surface tends to dissociate O–O bond, leading to the total reduction product of H2O9. In contrast, weak *OOH interaction with a perpendicular orientation to the surface tends to preserve O–O bond and gives rise to the production of H2O210,11.
Among various transition metal based ORR catalysts, Pt has the highest intrinsic activity for reducing O2 into H2O toward a full chemical-to-electrical energy conversion and thus been intensively investigated as a model system for decades12,13. For the three low-index Pt(hkl) surfaces, the 4e−-pathway selectivity increases in the order of Pt(111) < Pt(100) < Pt(110) within 0.1 M HClO4 at large overpotential regime14. For nanosized Pt, it is noted that the 2e−-pathway selectivity increases with decreasing Pt particle size as well as increasing particle inter-spacing15,16,17. Moreover, isolating of continuous Pt surface sites by carbon layers18, calix[4]arene molecules19, halogen20,21 or cyanide22 anions, or by alloying with a secondary metal23,24,25,26,27 has been demonstrated to significantly alter the ORR pathway toward H2O2 generation. Siahrostami et al. have computationally screened a wide range of bulk alloys containing a single active element toward ORR surrounded by an inert element of Hg and Au4. The active element like Pt is capable of adsorbing molecular O2 and reducing it to *OOH but is unable to dissociate the O−O bond due to the neighboring environment. This prediction has been experimentally verified on Pt-Hg/C to deliver a H2O2 selectivity over 90% at the potential ranging from 0.3 to 0.5 V vs. reversible hydrogen electrode (RHE)4.
Along this line, it is very interesting to see if ultimately isolated Pt single atom sites could exhibit a sole selectivity toward 2e− ORR pathway. Indeed, atomic dispersed Pt sites over TiN28, TiC29 and carbon nanotube (CNT)30 substrates are reported with preferential H2O2 selectivity over 65% in acidic electrolyte and an onset potential up to 0.45 V vs. RHE. Other Pt single atom catalysts (SACs) supported on highly sulfur-doped zeolite template carbon substrate31, AuCu metallic aerogels32 or CuSx hollow nanosphere33 even deliver a H2O2 selectivity above 90% over a wide potential range. Nevertheless, there’re recent studies showing that Pt SACs efficiently convert O2 into H2O via the 4e− pathway comparable to bulk Pt but at a much lower Pt usage34,35,36. Sun et al. demonstrated a maximum single-cell power density of 0.68 W cm−2 using carbon black supported Pt single atoms as the cathode catalyst in PEMFC, corresponding to a Pt utilization efficiency of 0.13 gPt kW−1,37. This single-cell performance has been further boosted to 0.09 gPt kW−1 on carbon-defect-anchored Pt SAC in a latest report38. These conflicting observations suggest that the ORR pathway and product selectivity on isolated Pt sites may be tailored by different reactivity of Pt central atom as arisen from different coordination environment39,40,41,42,43. How to address the above controversy, to correlate the apparent ORR performance with Pt-coordinated motifs at atomic level is therefore highly demanded.
Herein, we aim to address the above controversy with the merits of investigating Pt local coordination environment effect on the ORR products selectivity. By dispersing isolated Pt atoms over carbon nanotube substrates with different metalloid dopant, a series of Pt-X-C (X = S, C, N) motifs have been prepared, and the selectivity of 2e− ORR pathway increases in the order of Pt-C < Pt-N < Pt-S moieties in acidic media. Then Pt-N-CNT is deployed as a prototype to screen the Pt sites density effect on ORR pathway tuning, the selectivity of 2e− pathway decreases from 70 to 20% with increasing isolated Pt sites density from 0.7 to 11.2 µg cm−2, providing hints for regulating the stepwise oxygen reduction in different application scenarios.
Results
Effect of local coordination environment on ORR selectivity
To prepare the atomic dispersed Pt-X-CNT catalysts, a small amount of Pt cations (~ 0.03 at%) were firstly dispersed with aqueous CNT suspension, followed by lyophilization and thermal annealing with certain dopant precursor (see Experimental). Given a constant Pt loading of ~ 0.7 wt%, no metal clusters nor nanoparticles were observed from bright field transmission electron microscopy (TEM) images (Supplementary Fig. 1). High-resolution XRD patterns in Supplementary Fig. 2 also reveal the absence of any long-range ordered Pt crystalline structure or nanoparticles. Figure 1a-c show the aberration-corrected high angle annular dark field scanning TEM (HAADF-STEM) characterizations of Pt-S-CNT, Pt-N-CNT and Pt-C-CNT, respectively. The edges of multiple rolled graphene layers are clearly resolved, and isolated Pt single atoms are identified as the bright dots due to their higher Z contrast compared to the neighboring C/N/S sites. This atomically dispersed feature has been confirmed by Fourier-transformed extended X-ray absorption fine structure spectra (FT-EXAFS) at the Pt L3-edge (Fig. 1d). Pt foil exhibits a typical first shell Pt–Pt pair at ~ 2.55 Å, while Pt–O interaction in PtO2 locates at 1.93 Å, neither of them is observed on the as-prepared catalysts. The major R-space feature is noted as 1.90 Å for Pt-S-CNT, 2.36 Å for Pt-C-CNT and 1.60 Å for Pt-N-CNT, probably arisen from the characteristic bonding of Pt-S, Pt-N and Pt-C, respectively33,36 (EXAFS fitting results show in Supplementary Fig. 3).
HAADF-STEM images of a Pt-S-CNT, b Pt-N-CNT, and c Pt-C-CNT, the bright dots (as marked by red arrows) represent typical Pt single atoms. Scale bars, 5 nm. d k2-weighed Pt L3-edge FT-EXAFS spectra for as-prepared Pt-X-CNT in the R space, e core-level XPS spectra for Pt 4 f region, and f corresponding XANES spectra at Pt L3-edge in comparison to Pt foil and PtO2 references.
The composition of Pt-X-CNT and relevant Pt valence state are further probed by ex situ X-ray photoelectron spectroscopy (XPS). XPS survey spectra in Supplementary Fig. 4 depict the componential information, for which a similar Pt content of ~ 0.03 at% (ca. 0.7 wt%) is observed on all three samples. For Pt-N-CNT, core-level deconvoluted XPS spectrum on N 1 s region is plotted in Supplementary Fig. 5, with five different coordination structures pinpointed as pyridine-N (398.5 eV, 23.55%), pyrrole-N (400.4 eV, 33.81%), graphitic-N (401.6 eV, 16.40%), oxidized-N (403.1 eV, 10.63%) and N-Pt bonding (399.2 eV, 15.62%)37,44. For Pt-S-CNT, the S 2p spectrum shows two major peaks located at 164.2 eV and 165.9 eV (Supplementary Fig. 6), attributable to C-S-C (90.37%) and –SOx (9.63%) coordination, respectively45. Figure 1e plots the core-level XPS spectra for Pt 4 f region, in which the Pt 4f7/2 binding energy increases in the order of Pt-C-CNT (71.97 eV) < Pt-N-CNT (72.35 eV) < Pt-S-CNT (72.52 eV). Notably, all these values are higher than that of metallic Pt (71.2 eV)31, indicating a partial charge transfer from Pt central atom to neighboring metalloid dopant and in good agreement with previous SACs report43,46. This characteristic of partial depleted free electrons from Pt valence band has been further reinforced by the X-ray absorption near-edge structure (XANES) spectra shown in Fig. 1f, in which the white line peaks for Pt SACs locate in between Pt foil and PtO2.
The ORR performance was evaluated 0.1 M HClO4 electrolyte on Pt-X-CNT catalysts cast rotating ring disk electrode (RRDE). Prior to RRDE measurements, the collection coefficient of Pt ring electrode was pre-calibrated as 37.09% through the redox reaction of [Fe(CN)6]4−/[Fe(CN)6]3− (Supplementary Fig. 7)47. Figure 2a shows the polarization curve and corresponding H2O2 partial current recorded on Pt-X-CNT in comparison to bare N-CNT, relevant H2O2 selectivity and electron transfer number (n) as a function of applied potential are plotted in Fig. 2b. Other linear sweep voltammograms of S-CNT and defective CNT substrates are depicted in Supplementary Fig. 8. At the absence of Pt, N-CNT demonstrates the earliest onset potential of 0.42 V (defined as the potential delivering 0.1 mA cm−2 H2O2 partial current density) and maintains 47.9–59.1% H2O2 selectivity throughout the investigated potential window, which is comparable to literature reports33,37,38,48,49. Defective CNT prepared from hydrothermal treatment38 shows an even higher H2O2 selectivity up to ~ 75%, which could be attributable to carbon defect sites50 and/or oxygen functional groups modification51.
a Linear sweep voltammetry (LSV) of Pt-N-CNT (blue), Pt-S-CNT (red), Pt-C-CNT (green) and N-CNT reference recorded at 1600 rpm and a scan rate of 5 mV s−1, together with the detected H2O2 currents on the ring electrode (upper panel) at a fixed potential of 1.2 V vs. RHE. The catalyst loading was fixed at 0.1 mg cm−2. b Calculated H2O2 selectivity and electron transfer number (n) during LSV scan. H2O2 selectivity and n were plotted from the onset potential that reached 0.1 mA cm−2 H2O2 partial current density. c Performance map for the electrocatalytic O2-to-H2O2 conversion in acidic electrolyte, the detailed sample information could be found in Supplementary Table 1.
Besides, taken Pt-S-CNT, S-CNT and reported O-CNT51 for example, the recorded current densities within kinetics-controlled regime as well as the overall H2O2 selectivity are significantly improved as compared to Pt-free counterparts, indicating that Pt central atoms rather than the metalloid doped C sites or the O-dopants serve as the main active center for peroxide generation (Supplementary Fig. 9). During the negative-going potential sweep, Pt-S-CNT tends to catalyze the O2-to-H2O2 conversion, delivering a maximum H2O2 selectivity above 88% and an early onset potential of 0.51 V with optimized preparation conditions (Supplementary Fig. 10). This 2e− ORR performance is among the first echelon of reported values in acidic media, as summarized in Fig. 2c and Supplementary Table 1. An even higher kinetic current density may be expected from a higher concentration of isolated Pt-Sx moieties like Pt/HSC and Pt1-CuSx31,33. For Pt-N-CNT, the electrocatalytic ORR pathway is found to be affected by the annealing temperature. Supplementary Fig. 11 shows the H2O2 generation profile as a function of pyrolysis temperature, in which the 800 °C annealed Pt-N-CNT delivers a highest H2O2 selectivity up to 72.5% and an early onset potential of 0.62 V as plotted in Fig. 2a and b. As to Pt-C-CNT, the 4e− ORR pathway dominates at small overpotential region, while H2O2 selectivity increases with increasing overpotential. By increasing Pt loading from 0.7 to 4.3 µg cm−2, an even higher diffusion limited current density of 5.7 mA cm−2 can be achieved (Supplementary Fig. 12), in good agreement with earlier report38.
To further evaluate the intrinsic ORR activity and selectivity, electrochemical active surface area and relevant Pt site density over Pt-X-CNT are quantified by CO stripping measurements52,53, assuming a 1:1 molar ratio for COad to the adsorbed Pt sites given its predominant linear adsorption configuration on Pt surface54 (Supplementary Fig. 13 and Supplementary Table 3). As shown in Supplementary Fig. 14, the determined TOFsH2O2 on Pt-S-CNT and Pt-N-CNT are significantly higher than TOFsH2O, while a reverse trend is observed on Pt-C-CNT. Based on the ratio of TOFH2O2/TOFH2O, an increasing 2e−/4e− ORR pathway selectivity is noted as the order of Pt-C-CNT < Pt-N-CNT < Pt-S-CNT, which is in good agreement with RRDE results. Noteworthy, by switching the coordination motif from Pt-C to Pt-N and Pt-S, the H2O2 selectivity at a given potential of 0.4 V increases from 23.3% to 62.5% and 81.4% and a TOFH2O2/TOFH2O increases from 0.30 to 1.67 and 2.67, respectively, highlighting the role of local coordination environment in determining the oxygen reduction pathway.
Theoretical calculations
The above electrochemical measurements suggest ORR product selectivity largely depends on the Pt coordination environment. Herein, we performed density functional theory (DFT) calculations on Pt-X-C moieties to shed light on the origin of observed pathway tuning. In line with earlier report, a two-dimensional graphene structure is deployed to model the CNT support43, and Fig. 3a shows the simplified coordination of Pt-S4, Pt-N4 and Pt-C4 motifs in comparison to Pt(111) surface upon the adsorption of *OOH. The formation energy (ΔEf) is ca. −0.16, −2.09 and −1.61 eV for each motif, suggestive a stable coordination configuration.
a Examined configurations for Pt single atom coordinated in two-dimensional carbon matrix with different metalloid doping, *OOH adsorption is preferable on central Pt sites over neighboring S/N/C atoms. b Illustration of oxygenated intermediates adsorption taking Pt-S4 as an example, and relevant free energy diagrams for 2e– (red) or 4e– (black) ORR pathway on c Pt-S4, d Pt-N4 and e Pt-C4 motif. Insert numbers represent the kinetic barriers for *OOH to H2O2 or *O, as computed by the Climbing Image Nudged Elastic Band (CI-NEB) approach.
Prior to ORR simulations, a simple electrochemical hydrogen evolution (HER) measurement coupled with thermodynamic analysis have been carried out as a probe reaction to examine the proposed models. Supplementary Fig. 15 shows the voltammograms of Pt-X-CNT as recorded in 0.1 M Ar-saturated HClO4 electrolyte from −0.05 to 1.05 V vs. RHE. Only hydrogen evolution and oxidation peaks are observed during the cyclic voltammetry, the absence of Pt redox peaks at high potential region confirms the highly dispersed feature of prepared Pt-X-CNT catalysts. The Gibbs free energy of adsorbed *H (ΔGH, Supplementary Fig. 16) is used as the descriptor for HER activity, for which the absolute value decreases in the order of Pt-S4 > Pt-N4 > Pt-C4, in good harmony with our experimental observation thus confirming the validity of proposed configurations.
Fig. 3b schematically compares associative and dissociative O2 reduction pathway55,56, and the free energy diagram for each reaction step on different moieties, including Pt(111) model surface, is calculated at 0.4 V and plotted in Fig. 3c–e. The hydrogeneration of *OOH intermediate is found to be the critical knob branching ORR pathway4. Similar to that on Pt(111), a dissociate reduction of *OOH to *O is found to be energetically favored on Pt-C4, while the associate reduction of *OOH to H2O2 is favored on Pt-S4 and Pt-N4 moieties. The energetic differences between 2e− and 4e− ORR pathways, i.e., ΔGassoc‒ΔGdissoc, are comparatively depicted in Supplementary Fig. 17, in which a most energetic favorable O2-to-H2O2 conversion of ca. −0.71 eV is noted on Pt-S4, followed by −0.41 eV on Pt-N4 and unfavorable conversion of +1.65 eV on Pt-C4 and +2.67 eV on Pt(111). We also compare this energetic difference on Pt single atom site versus that on Pt cluster using Pt1-S4-C and Pt6-S4-C as a representative57, i.e., −0.71 eV for the former and +2.83 eV for the latter (Supplementary Fig. 18), which in turn verifies the isolated Pt sites feature from theoretical side. Besides, we consider both the Pt-C4 (Fig. 3a) and the Pt-C3 coordination (Supplementary Fig. 19) for Pt-C-CNT, as derived from EXAFS fitting results, the 4e– pathway is found to be more energetic favorable on both Pt-C motifs. Despite these thermodynamic simulations, we further compare the kinetic barriers for both 4e− and 2e− ORR pathways over different Pt-coordinated moieties. The results show that Pt-S4 exhibits the lowest kinetic energy barrier for 2e− pathway (0.87 eV), followed by Pt-N4 of 1.01 eV and Pt-C4 of 2.02 eV. The simplified analysis on thermodynamics and reaction kinetics actually matches well with the trend of experimentally determined H2O2 selectivity, reinforcing the Pt local coordination environment effect on fine tuning the binding strength of *OOH intermediate and thus altering the oxygen reduction pathway.
H2O2 production from bulk electrolysis
Decentralized H2O2 production with tunable aqueous concentration is ideal for onsite applications58,59. Herein, we cast the above pinpointed Pt-S-CNT catalyst onto a 1 × 1 cm2 carbon fiber paper electrode and further investigate its potential toward H2O2 generation from bulk electrolysis. The H-type reactor is schematically shown in Fig. 4a, where the cathodic catalyst loading of Pt-S-CNT is fixed at 0.5 mg cm−2 (ca. 3.5 µgPt cm−2). A homogeneous dispersion of Pt-S-CNT over carbon fibers substrate can be seen from the scanning electron microscopic image (SEM, Fig. 4b) and the MicroCT 3D tomography (Supplementary Fig. 20). The ORR activity for as-prepared catalyst and the one post long-term electrolysis are evaluated in 25 mL of 0.1 M O2-saturated HClO4, and corresponding LSV curves are plotted in Fig. 4c. For as-prepared catalyst, the ORR onset potential locates at ~ 0.6 V, and the current density reaches ~ 10 mA cm−2 at 0.05 V vs RHE. Long-term electrolysis is then carried out at a constant current density of 10 mA cm−2. 1 mL of electrolyte solution was extracted from cathodic chamber every 30 min during the electrolysis, and the content of H2O2 was determined by potassium permanganate titration60. Figure 4d shows a negligible potential decay to deliver the constant current of 10 mA, and Supplementary Fig. 21 depicts the inductive coupled plasma - mass spectroscopic results of ~ 0.29 at.% Pt leaching from Pt-S-CNT into bulk electrolyte (ICP-MS, ca. 0.4 ppb Pt leaching in total). Moreover, ~ 70% selectivity of O2-to-H2O2 conversion is maintained during the 500-min electrolysis, demonstrating a stable peroxide generation performance over Pt-S-CNT. After this long-term operation, the ORR current density is noted to exceed 15 mA cm−2 (Fig. 4c) at 0.05 V but at the sacrifice of onset potential, which may arise from the gradually increased hydrophilicity of the electrode surface as can be seen from the decreased contact angle. More than 1100 ppm H2O2 was accumulated during this electrolysis (Fig. 4e), which can be further scaled up by integrating with gas diffusion electrodes into solid-state electrolyzers and flow cell reactors61,62.
a Schematic of a home-made H-type electrolyzer. b SEM image of Pt-S-CNT cast carbon fiber paper as working electrode, scale bar: 500 nm. c LSV curves recorded on either pristine or post-electrolysis working electrode within 0.1 M O2-saturated HClO4 at a scan rate of 5 mV s−1, inset shows the contact angles of a same working electrode prior to and post 500-min electrolysis at the scale bar of 1 mm. d The ORR stability test of working electrode potential and H2O2 selectivity under a fixed current density of 10 mA cm−2 for 500 min continuous electrolysis. e The accumulated H2O2 concentration during the stability measurement. The error bars represent two independent samples.
Effect of Pt sites density on H2O2 generation
In addition to the above coordination environment tuning, increasing metal loading63,64 and/or peroxide diffusion paths65 have also been demonstrated to improve the selectivity of O2-to-H2O conversion. Along this line, we adapted a series of Pt-N-CNT catalysts with different Pt loadings as a stereotype to investigate the isolated Pt site density effect on ORR pathway tuning, since M-N-C moiety66 is generally considered as the most promising alternative to Pt in 4e− ORR.
The amount of Pt precursor solution was adjusted from 200 to 2000 µL, namely 200-, 400-, 800- and 2000-Pt-N-CNT, corresponding to the Pt loading of 0.7 wt.%, 1.4 wt.%, 2.8 wt.% and 7.0 wt.%, respectively. An identical CNT structure is found on all the four catalysts as shown in Fig. 5a of bright field TEM characterization. No Pt nanoparticles were observed at relatively low Pt loading of 200-, 400- and 800-Pt-N-CNTs, indicating a highly dispersed feature of Pt sites in these samples as due to the strong Pt-N interaction35,37. For 2000-Pt-N-CNT, Pt aggregates at a diameter of ~ 10 nm were found as black spots on CNT substrate. XPS survey spectra over these Pt-N-CNTs are plotted in Supplementary Fig. 22, in which only C, O, N, Pt elements were identified. Besides, the content of surface Pt species increases with increasing Pt precursor amount from 200 to 800 µL but decreases for 2000-Pt-N-CNT probably arisen from the lower percentage of (sub)surface atoms in nanoparticles as compared to single atom catalyst. The core level XPS on Pt 4 f region are plotted in Fig. 5b, a sole characteristic of Ptδ+ peak located at 72.35 eV is noted on 200-, 400- and 800-Pt-N-CNTs while both Pt0 (71.46 eV) and Ptδ+ peaks are resolved on 2000-Pt-N-CNT, in good agreement with above microscopic characterization.
a TEM images of 200-, 400-, 800- and 2000-Pt-N-CNT. Scale bars, 50 nm. Inserts are the zoom-in view of certain carbon nanotubes at a fixed scale bar of 10 nm. b Core-level XPS spectra for Pt 4 f region. c The maximum H2O2 selectivity as a function of Pt loading. The rightmost data point was measured on commercial TKK 30 wt.% Pt/C catalyst and plotted with actual Pt weight loading, while all other data on Pt-N-CNT were plotted using determined Pt content from XPS measurements. d Calculated TOFs of 200-Pt-N-CNT with different catalyst loading, and e calculated TOFs of n-Pt-N-CNT with different Pt site density but a fixed catalyst loading of 0.1 mg cm−2.
To probe the Pt sites density effect on H2O2 selectivity, 2 variables are considered in our RRDE measurements, i.e., one with fixed Pt-N-CNT catalyst loading of 0.1 mg cm−2 but different Pt content from 0.7 wt.% to 7.0 wt.% and the other one with gradually increased catalyst loading but a fixed Pt content. As shown in Supplementary Fig. 23, the maximum H2O2 selectivity for all n-Pt-N-CNTs significantly decreases with increasing catalyst loading from 0.1 to 0.4 mg cm−2. Increasing catalyst loading could lead to a thicker catalyst layer and thus a longer diffusion path for H2O2 product. During its diffusion process, a further reduction of H2O2 into H2O is expected which reduces the final peroxide selectivity64,67. Moreover, we normalize the surface Pt sites density from XPS survey results and plot the Pt loading dependence of maximum H2O2 selectivity in Fig. 5c. By increasing the Pt active sites density, the 2e− ORR pathway could be successfully shifted toward the 4e− pathway, with the H2O2 selectivity decreasing from 70 to 20% and the electron transfer number increasing from 2.55 to 3.62. Figure 5d plots the overall catalyst loading effect on TOFH2O2 over 200-Pt-N-CNT, i.e., the thinner diffusion layer thickness, the higher H2O2 generation rate per Pt site. Similarly, at a fixed catalyst loading of 0.1 mg cm−2, TOFH2O2 decreases with increasing electrochemical active Pt site density from 0.29 wt.% to 0.51 wt.% as derived from CO stripping measurements (Fig. 5e). Taken together the Pt loading dependence of apparent H2O2 selectivity and the intrinsic TOF quantification, it can be rationalized that the densely distributed Pt sites are beneficial for the total reduction of O2 into H2O rather than H2O2 generation.
Discussion
Through a combined experimental and theoretical approach, we demonstrate that manipulating the local coordination environment of Pt single atoms could effectively regulate the ORR pathway. Pt-S-C moiety is inclined to the 2e− pathway of O2-to-H2O2 conversion while Pt-C moiety is mostly favorable to the totally reduction of O2 into H2O. In addition, the peroxide selectivity is further correlated with the Pt active sites density, with a tunable electron transfer number from 2.55 to 3.62 successfully demonstrated on Pt-N-C prototype. These understandings will aid to the development of more efficient and selective Pt single atom catalysts for both 4e− ORR in fuel cell applications and 2e− ORR in green peroxide synthesis. Given the wide application scenarios of Pt and the abundant coordination motif structures, the present approach sheds light on the design of more delicate (electro-)catalyst, which is of great importance to both fundamental surface catalysis studies and practical energy conversion process.
Methods
Material synthesis and characterization
The Pt-X-CNT catalyst (X = N, S, C) was prepared by the impregnation-reduction method. In a typical Pt-N-CNT synthesis, K2PtCl4 (AR, Sinopharm) precursor was firstly dissolved in Millipore water (18.2 MΩ·cm) to prepare a 3 mg mL−1 stock solution. A carbon suspension was then prepared by mixing 40 mg of multi-walled carbon nanotubes (Carbon Nanotubes Plus GCM389, used as received) with 25 mL of Millipore water, and tip sonicated for 30 min. Thereafter, 200 μL of Pt stock solution was added dropwise to the CNT suspension under vigorous stirring for a 0.7 wt.% Pt target loading and got quickly frozen in liquid nitrogen. The amount of Pt stock solution was adjusted accordingly to regulate the different Pt loadings. The prepared K2PtCl4/CNT powder was grinded with urea (AR, Sinopharm) at a mass ratio of 1:10, then heated up to 800 °C within 60 min in a tube furnace under an Ar (99.999%, Shanghai Coogee) flow of 100 sccm, and kept at the same temperature for another 60 min before cooling down to room temperature37. The preparation method of Pt-S-CNT and Pt-C-CNT is similar to that of Pt-N-CNT, except the pretreatment of CNT. To prepare S-doped CNT in Pt-S-CNT, CNT and diphenyl disulfide (PDS, 99%, Macklin) were mixed at a mass ratio of 1:4, heated up to 900 °C within 30 min under 100 sccm Ar flow in a tube furnace, and kept at the same temperature for another 30 min before cooling down45. The K2PtCl4/S-CNT powder was heated to 250 °C with 100 sccm Ar within 30 min and kept for another 120 min before cooling down to obtain the Pt-S-CNT. As to Pt-C-CNT, 50 mg of CNT were uniformly dispersed in 12.5 mL of absolute ethanol (AR, Sinopharm) + 12.5 mL of Millipore water + 250 μL of H2O2 (GR, Sinopharm), then got transferred to a 100-mL autoclave for reaction at 200 °C for 6 h. The obtained defective CNT38 was centrifuged and washed intensively with Millipore water for 2 times. The K2PtCl4/defective-CNT powder was heated to 900 °C within 60 min under 100 sccm Ar flow, kept at 900 °C for another 60 min and then cooled to room temperature to obtain the Pt-C-CNT.
The SEM images were taken on a FEI Sirion 200 Field-Emission scanning electron microscopy, using an electron beam energy of 5 kV and a spot size of 3.0 nm with magnification ranging from 5 to 80 k. A bright field transmission electron microscope, Talos F200X G2, was used to characterize the morphology of Pt-X-CNT. Dark field STEM characterizations were carried out using a JEM ARM200F aberration-corrected transmission electron microscope under 200 kV. Drift correction was applied during acquisition. X-ray photoelectron spectroscopy was obtained with a Kratos AXIS Ultra DLD spectrometer, using a monochromatic Al Kα radiation (1486.6 eV) and a low energy flood gun as neutralizer. The binding energies were calibrated by referencing to C 1 s peak at 284.8 eV. Casa XPS program was employed for surface component analysis, with detailed fitting parameters tabulated in Supplementary Table 2. X-ray absorption spectroscopy (XAS) at Pt L3-edge of Pt-S-CNT and Pt-N-CNT was measured at beamline 7-BM (QAS) of National Synchrotron Light Source II (NSLSI-II) in Brookhaven National Laboratory (BNL), and Pt-N-CNT was measured at the beamline BL14W1 of Shanghai Synchrotron Radiation Facility (XAFS station, SSRF). The data were collected in the fluorescence mode and the reference spectrum of Pt metal foil was also collected during the measurement for energy calibration. XANES and EXAFS data were processed and analyzed using the Athena and Artemis software package68. MicroCT was performed on a Zeiss Xradia 520 Versa X-ray microscopy. The distances of the sample to the X-ray source (12.53 mm) or to the X-ray detector (72.09 mm) result in a voxel (volume pixel) size of 1 μm. The field of view was approximately 1012.3 μm × 1012.3 μm, and the reconstruction of MicroCT data was conducted using the TXM Reconstructor software (Xradia). XRD spectra were recorded on a Rigaku Mini Flex 600 spectrometer using a Cu Kα radiation (40 kV, 15 mA) at a scan rate of 0.02° per step and a holding time of 4 s per step. ICP-MS was measured on a Thermo Scientific iCAP-Q spectrometer to quantify the potential Pt leaching ratio during electrolysis with a detection limit of 0.001 ppbPt.
Electrochemical measurements
0.1 M HClO4 was used as the electrolyte, which was obtained by dissolving 14.315 g of concentrated HClO4 (70%, Sigma) in 1 L Millipore water. The electrochemical measurements were run in a standard three-electrode system, with signals recorded by a CHI 760e working station. An RRDE component (AFE7R9, Pine Instruments) consisting of a glassy carbon rotating disk electrode (Φ = 5.61 mm) and a Pt ring (Φ = 6.25 mm) was used, with a theoretical collection efficiency of 37%. Experimentally, the apparent collection efficiency (N) was determined to be 37.1% by using the ferrocyanide/ferrocyanide half-reaction system at rotation rate between 400 and 2025 rpm. A high-purity graphite rod (99.995%, Sigma-Aldrich) and a fresh prepared reversible hydrogen electrode (RHE) was used as the counter and the reference electrode, respectively. To prepare RHE, a capillary tube sealed with platinum wire was first filled with 0.1 M HClO4, and then a part of hydrogen was generated through electrolysis, forming a saturated Pt/H2 interface. To prepare the catalyst cast RRDE, typically 3.3 mg of Pt-X-CNT was firstly mixed with 0.5 mL of Millipore water, 0.5 mL of isopropanol (AR, Sinopharm) and 15 μL of Nafion 117 solution (5 wt.%, Sigma-Aldrich), ultrasonicated for 30 min till a homogeneous catalyst ink. Then 7.5 μL of the catalyst ink was pipetted onto mirror-polished carbon disk (0.247 cm2, ca. 0.1 mg cm−2 mass loading). The hydrogen peroxide selectivity was calculated using the following equation: H2O2(%) = 200 × \(\frac{{I}_{{Ring}}/N}{\left|{I}_{{Disk}}\right|\,+\,{I}_{{Ring}}/N}\), the number of electrons transferred on the disk electrode in the ORR process n through the equation: n = 4 × \(\frac{\left|{I}_{{Disk}}\right|}{\left|{I}_{{Disk}}\right|\,+\,{I}_{{Ring}}/N}\), where \({I}_{{Ring}}\) is the ring current, \({I}_{{Disk}}\) is the disk current, and N is the determined collection efficiency.
The bulk electrolysis of ORR was performed in a customized H-type cell, Pt-S-CNT was sprayed onto a 1 × 1 cm2 carbon fiber paper (HCP010N, Hesen) as the cathode (catalyst loading of 0.5 mg cm−2), and the high-purity graphite rod was used as the anode, with the two chambers separated by Nafion 212 cation exchange membrane. 1 mL of the cathodic electrolyte was extracted every 30 min during the electrolysis, and the generated H2O2 concentration was quantified by potassium permanganate (0.02 M KMnO4 solution, AR, Sinopharm) titration method60 with a detection limit of ca. 8.5 ppm (Supplementary Fig. 24):
Electrochemical CO stripping measurements were carried out on Pt-X-CNT cast RDE working electrode, starting with bubbling CO (99.9%, Air Liquide) in 0.1 M HClO4 for 20 min at 0.25 V vs. RHE. Then, the dissolved CO was removed from the electrolyte by Ar purging for 60 min while maintaining the electrode potential at 0.25 V. Finally, we recorded the CO stripping voltammograms by scanning the potential from 0.25 to 1.30 V at 5 mV s−1.
Computational details
The density functional theory (DFT) calculation is performed by Vienna ab initio Simulation Program (VASP)69,70,71,72. The PBE functional with projector augmented wave pseudo-potential is used to calculate all models73,74. A Gaussian smearing technique is used with a smearing parameter of kBT = 0.1 eV for the fractional occupation of the one-electron energy levels to accelerate SCF convergence and calculated energies are extrapolated to kBT = 0 eV.
The surface of CNT is described by the monolayer graphite model, of which lattice parameters are α = 14.760 Å, β = 17.0434 Å, c = 20.0 Å. Carbon-based slab calculations are sampled by a Monkhorst-Pack k-point net of 5 × 4 × 1 with cutoff energy of 500 eV. (111) facet of Pt consists of 5 slabs and sampled by a Monkhorst-Pack k-point net of 5 × 5 × 1 with cutoff energy of 500 eV. Molecule calculations are sampled by Gamma point with cutoff energy of 400 eV.
The energy of (H+ + e−) is defined as two times of that of H2 on the standard condition, i.e., U = 0 and pH=075,76. The free energy was calculated as:
where E is the DFT energy of the model, ZPE is the zero-point energy which is calculated by ∑(hvi/2) (h is the Planck constant and vi is the vibrational frequency), T is the temperature (298.15 K), S is the entropy of the structure which is given by vibrational frequency, n is the number of electrons transferred in elementary reaction, e is the charge constant and U is the potential75,76. The energy of H2O is calculated by GH2O(l)=GH2O(g) + RT × In(P/P0), where GH2O(g) is given by free energy as above, R is gas constant with P0 = 1 bar and P = 0.035 bar75,76. The free energy of O2 is calculated according to the thermodynamic energy (4.92 eV) released by the reaction of 2H2 + O2 → 2H2O. The thermodynamic energy released by the reaction of H2 + O2 → H2O2 is −1.39 eV. To testify if any curvature effect on the calculated ORR free energy diagrams, a representative 2D Pt-S4-C motif is plotted against 3D Pt-S4-CNT model as shown in Supplementary Fig. 25. Nearly identical *OOH binding strength is observed on the two cases, suggestive a minor curvature effect on H2O2 generation.
Data availability
The data generated in this study are provided in the Supplementary Information. Source data are provided with this paper.
References
Debe, M. K. Electrocatalyst approaches and challenges for automotive fuel cells. Nature 486, 43–51 (2012).
Dai, L., Xue, Y., Qu, L., Choi, H.-J. & Baek, J.-B. Metal-free catalysts for oxygen reduction reaction. Chem. Rev. 115, 4823–4892 (2015).
Shao, M., Chang, Q., Dodelet, J.-P. & Chenitz, R. Recent advances in electrocatalysts for oxygen reduction reaction. Chem. Rev. 116, 3594–3657 (2016).
Siahrostami, S. et al. Enabling direct H2O2 production through rational electrocatalyst design. Nat. Mater. 12, 1137–1143 (2013).
Kulkarni, A., Siahrostami, S., Patel, A. & Norskov, J. K. Understanding catalytic activity trends in the oxygen reduction reaction. Chem. Rev. 118, 2302–2312 (2018).
Yang, S. et al. Toward the decentralized electrochemical production of H2O2: a focus on the catalysis. ACS Catal. 8, 4064–4081 (2018).
Melchionna, M., Fornasiero, P. & Prato, M. The rise of hydrogen peroxide as the main product by metal-free catalysis in oxygen reductions. Adv. Mater. 31, 1802920 (2019).
Siahrostami, S. et al. A review on challenges and successes in atomic-scale design of catalysts for electrochemical synthesis of hydrogen peroxide. ACS Catal. 10, 7495–7511 (2020).
Montemore, M. M., van Spronsen, M. A., Madix, R. J. & Friend, C. M. O2 activation by metal surfaces: Implications for bonding and reactivity on heterogeneous catalysts. Chem. Rev. 118, 2816–2862 (2018).
Yuan, Q. et al. Electrochemical hydrogen peroxide synthesis from selective oxygen reduction over metal selenide catalysts. Nano Lett. https://doi.org/10.1021/acs.nanolett.1c04420 (2022).
Jiang, K., Zhao, J. & Wang, H. Catalyst design for electrochemical oxygen reduction toward hydrogen peroxide. Adv. Funct. Mater. 30, 2003321 (2020).
Wang, Y., Wang, D. & Li, Y. A fundamental comprehension and recent progress in advanced Pt‐based ORR nanocatalysts. SmartMat 2, 56–75 (2021).
Wang, X. X., Sokolowski, J., Liu, H. & Wu, G. Pt alloy oxygen-reduction electrocatalysts: synthesis, structure, and property. Chin. J. Catal. 41, 739–755 (2020).
Markovic, N., Gasteiger, H. & Ross, P. N. Kinetics of oxygen reduction on Pt(hkl) electrodes: implications for the crystallite size effect with supported Pt electrocatalysts. J. Electrochem. Soc. 144, 1591–1597 (1997).
Gara, M. et al. Oxygen reduction at sparse arrays of platinum nanoparticles in aqueous acid: hydrogen peroxide as a liberated two electron intermediate. PhysChemChemPhys 15, 19487–19495 (2013).
Yang, H., Kumar, S. & Zou, S. Electroreduction of O-2 on uniform arrays of Pt nanoparticles. J. Electroanal. Chem. 688, 180–188 (2013).
von Weber, A., Baxter, E. T., White, H. S. & Anderson, S. L. Cluster size controls branching between water and hydrogen peroxide production in electrochemical oxygen reduction at Pt-n/ITO. J. Phys. Chem. C. 119, 11160–11170 (2015).
Choi, C. H. et al. Hydrogen peroxide synthesis via enhanced two-electron oxygen reduction pathway on carbon-coated Pt surface. J. Phys. Chem. C. 118, 30063–30070 (2014).
Genorio, B. et al. Selective catalysts for the hydrogen oxidation and oxygen reduction reactions by patterning of platinum with calix 4 arene molecules. Nat. Mater. 9, 998–1003 (2010).
Stamenkovic, V., Markovic, N. M. & Ross, P. N. Structure-relationships in electrocatalysis: oxygen reduction and hydrogen oxidation reactions on Pt(111) and Pt(100) in solutions containing chloride ions. J. Electroanal. Chem. 500, 44–51 (2001).
Schmidt, T. J., Paulus, U. A., Gasteiger, H. A. & Behm, R. J. The oxygen reduction reaction on a Pt/carbon fuel cell catalyst in the presence of chloride anions. J. Electroanal. Chem. 508, 41–47 (2001).
Ciapina, E. G. et al. Surface spectators and their role in relationships between activity and selectivity of the oxygen reduction reaction in acid environments. Electrochem. Commun. 60, 30–33 (2015).
Mahata, A. & Pathak, B. Bimetallic core-based cuboctahedral core-shell nanoclusters for the formation of hydrogen peroxide (2e(-) reduction) over water (4e(-) reduction): Role of core metals. Nanoscale 9, 9537–9547 (2017).
Zheng, Z., Ng, Y. H., Wang, D.-W. & Amal, R. Epitaxial growth of Au-Pt-Ni nanorods for direct high selectivity H2O2 production. Adv. Mater. 28, 9949–9955 (2016).
Felix-Navarro, R. M. et al. Bimetallic Pt-Au nanoparticles supported on multi-wall carbon nanotubes as electrocatalysts for oxygen reduction. Renew. Energy 87, 31–41 (2016).
Brimaud, S., Engstfeld, A. K., Alves, O. B. & Behm, R. J. Structure-reactivity correlation in the oxygen reduction reaction: activity of structurally well defined AuxPt1-x/Pt(111) monolayer surface alloys. J. Electroanal. Chem. 716, 71–79 (2014).
Felix-Navarro, R. M. et al. Pt-Pd bimetallic nanoparticles on mwcnts: catalyst for hydrogen peroxide electrosynthesis. J. Nanopart. Res. 15, 1802 (2013).
Yang, S., Kim, J., Tak, Y. J., Soon, A. & Lee, H. Single-atom catalyst of platinum supported on titanium nitride for selective electrochemical reactions. Angew. Chem. Int. Ed. 55, 2058–2062 (2016).
Yang, S., Tak, Y. J., Kim, J., Soon, A. & Lee, H. Support effects in single-atom platinum catalysts for electrochemical oxygen reduction. ACS Catal. 7, 1301–1307 (2017).
Kim, J. H. et al. A general strategy to atomically dispersed precious metal catalysts for unravelling their catalytic trends for oxygen reduction reaction. ACS Nano 14, 1990–2001 (2020).
Choi, C. H. et al. Tuning selectivity of electrochemical reactions by atomically dispersed platinum catalyst. Nat. Commun. 7, 10922 (2016).
Shi, Q. et al. Highly dispersed platinum atoms on the surface of aucu metallic aerogels for enabling H2O2 production. ACS Appl. Energy Mater. 2, 7722–7727 (2019).
Shen, R. et al. High-concentration single atomic Pt sites on hollow cusx for selective O-2 reduction to H2O2 in acid solution. Chem 5, 2099–2110 (2019).
Liu, J. et al. Reconstructing the coordination environment of platinum single-atom active sites for boosting oxygen reduction reaction. ACS Catal. 11, 466–475 (2021).
Song, Z. et al. Engineering the low coordinated Pt single atom to achieve the superior electrocatalytic performance toward oxygen reduction. Small 16, 2003096 (2020).
Li, T., Liu, J., Song, Y. & Wang, F. Photochemical solid-phase synthesis of platinum single atoms on nitrogen-doped carbon with high loading as bifunctional catalysts for hydrogen evolution and oxygen reduction reactions. ACS Catal. 8, 8450–8458 (2018).
Liu, J. et al. High performance platinum single atom electrocatalyst for oxygen reduction reaction. Nat. Commun. 8, 15938 (2017).
Liu, J. et al. Carbon-supported divacancy-anchored platinum single-atom electrocatalysts with superhigh Pt utilization for the oxygen reduction reaction. Angew. Chem. Int. Ed. 58, 1163–1167 (2019).
Tang, C. et al. Tailoring acidic oxygen reduction selectivity on single-atom catalysts via modification of first and second coordination spheres. J. Am. Chem. Soc. 143, 7819–7827 (2021).
Speck, F. D. et al. Single-atom catalysts: a perspective toward application in electrochemical energy conversion. JACS Au 1, 1086–1100 (2021).
Zhang, J., Yang, H. & Liu, B. Coordination engineering of single‐atom catalysts for the oxygen reduction reaction: a review. Adv. Energy Mater. 11, 2002473 (2020).
Tang, C. et al. Coordination tunes selectivity: two-electron oxygen reduction on high-loading molybdenum single-atom catalysts. Angew. Chem. Int. Ed. Engl. 59, 9171–9176 (2020).
Jiang, K. et al. Highly selective oxygen reduction to hydrogen peroxide on transition metal single atom coordination. Nat. Commun. 10, 3997 (2019).
Wang, X. X. et al. Nitrogen-coordinated single cobalt atom catalysts for oxygen reduction in proton exchange membrane fuel cells. Adv. Mater. 30, 1706758 (2018).
Hoque, M. A. et al. Web-like 3d architecture of Pt nanowires and sulfur-doped carbon nanotube with superior electrocatalytic performance. ACS Sustain. Chem. Eng. 6, 93–98 (2018).
Jiang, K. et al. Local coordination and reactivity of a Pt single-atom catalyst as probed by spectroelectrochemical and computational approaches. CCS Chem. 3, 241–251 (2021).
Paulus, U. A., Schmidt, T. J., Gasteiger, H. A. & Behm, R. J. Oxygen reduction on a high-surface area Pt/Vulcan carbon catalyst: a thin-film rotating ring-disk electrode study. J. Electroanal. Chem. 495, 134–145 (2001).
Fellinger, T.-P., Hasche, F., Strasser, P. & Antonietti, M. Mesoporous nitrogen-doped carbon for the electrocatalytic synthesis of hydrogen peroxide. J. Am. Chem. Soc. 134, 4072–4075 (2012).
Park, J., Nabae, Y., Hayakawa, T. & Kakimoto, M. Highly selective two-electron oxygen reduction catalyzed by mesoporous nitrogen-doped carbon. ACS Catal. 4, 3749–3754 (2014).
Chen, S. et al. Defective carbon-based materials for the electrochemical synthesis of hydrogen peroxide. ACS Sustain. Chem. Eng. 6, 311–317 (2018).
Lu, Z. et al. High-efficiency oxygen reduction to hydrogen peroxide catalysed by oxidized carbon materials. Nat. Catal. 1, 156–162 (2018).
Bae, G. et al. Quantification of active site density and turnover frequency: from single-atom metal to nanoparticle electrocatalysts. JACS Au 1, 586–597 (2021).
Li, J. & Jaouen, F. Structure and activity of metal-centered coordination sites in pyrolyzed metal–nitrogen–carbon catalysts for the electrochemical reduction of O2. Curr. Opin. Electrochem. 9, 198–206 (2018).
Mojet, B. L., Ebbesen, S. D. & Lefferts, L. Light at the interface: the potential of attenuated total reflection infrared spectroscopy for understanding heterogeneous catalysis in water. Chem. Soc. Rev. 39, 4643–4655 (2010).
Nayak, S., McPherson, I. J. & Vincent, K. A. Adsorbed intermediates in oxygen reduction on platinum nanoparticles observed by in situ ir spectroscopy. Angew. Chem. Int. Ed. Engl. 57, 12855–12858 (2018).
Hansen, H. A., Viswanathan, V. & Norskov, J. K. Unifying kinetic and thermodynamic analysis of 2 e(-) and 4 e(-) reduction of oxygen on metal surfaces. J. Phys. Chem. C. 118, 6706–6718 (2014).
Kou, R. et al. Stabilization of electrocatalytic metal nanoparticles at metal-metal oxide-graphene triple junction points. J. Am. Chem. Soc. 133, 2541–2547 (2011).
Gao, J. & Liu, B. Progress of electrochemical hydrogen peroxide synthesis over single atom catalysts. ACS Mater. Lett. 2, 1008–1024 (2020).
Jung, E., Shin, H., Antink, W. H., Sung, Y.-E. & Hyeon, T. Recent advances in electrochemical oxygen reduction to H2O2: catalyst and cell design. ACS Energy Lett. 5, 1881–1892 (2020).
Xia, C. et al. Confined local oxygen gas promotes electrochemical water oxidation to hydrogen peroxide. Nat. Catal. 3, 125–134 (2020).
Xu, W. et al. Fast and stable electrochemical production of H2O2 by electrode architecture engineering. ACS Sustain. Chem. Eng. 9, 7120–7129 (2021).
Xia, C., Xia, Y., Zhu, P., Fan, L. & Wang, H. Direct electrosynthesis of pure aqueous H2O2 solutions up to 20% by weight using a solid electrolyte. Science 366, 226–231 (2019).
Song, X. et al. Promotion of hydrogen peroxide production on graphene-supported atomically dispersed platinum: effects of size on oxygen reduction reaction pathway. J. Power Sources 435, 226771 (2019).
Inaba, M., Yamada, H., Tokunaga, J. & Tasaka, A. Effect of agglomeration of Pt/C catalyst on hydrogen peroxide formation. Electrochem. Solid-State Lett. 7, A474–A476 (2004).
Bonakdarpour, A. et al. Impact of loading in rrde experiments on Fe–N–C catalysts: two- or four-electron oxygen reduction? Electrochem. Solid-State Lett. 11, B105–B108 (2008).
Wang, X. et al. Review of metal catalysts for oxygen reduction reaction: from nanoscale engineering to atomic design. Chem 5, 1486–1511 (2019).
Bonakdarpour, A., Dahn, T. R., Atanasoski, R. T., Debe, M. K. & Dahn, J. R. H(2)O(2) release during oxygen reduction reaction on Pt nanoparticles. Electrochem. Solid-State Lett. 11, B208–B211 (2008).
Ravel, B. & Newville, M. Athena, artemis, hephaestus: data analysis for X-ray absorption spectroscopy using ifeffit. J. Synchrotron Rad. 12, 537–541 (2005).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B: Condens. Matter 47, 558–561 (1993).
Kresse, G. & Hafner, J. Ab initio molecular-dynamics simulation of the liquid-metal-amorphous-semiconductor transition in germanium. Phys. Rev. B: Condens. Matter 49, 14251–14269 (1994).
Kresse, G. & Furthmuller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B: Condens. Matter 54, 11169–11186 (1996).
Kresse, G. & Furthmuller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).
Blochl, P. E. Projector augmented-wave method. Phys. Rev. B: Condens. Matter 50, 17953–17979 (1994).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Norskov, J. K. et al. Origin of the overpotential for oxygen reduction at a fuel-cell cathode. J. Phys. Chem. B 108, 17886–17892 (2004).
Norskov, J. K. et al. Trends in the exchange current for hydrogen evolution. J. Electrochem. Soc. 152, J23–J26 (2005).
Acknowledgements
This work was supported by the National Natural Science Foundation of China (NSFC, No. 22002088), the Shanghai Sailing Program (No. 20YF1420500) and the Oceanic Interdisciplinary Program of Shanghai Jiao Tong University (No. SL2020MS007). F.J. acknowledges the support from NSFC under the Grant No. 21802095. This research used resources at beamline 7-BM (QAS) of the National Synchrotron Light Source II, a U.S. Department of Energy (DOE) Office of Science User Facility operated for the DOE Office of Science by Brookhaven National Laboratory under Contract No. DE-SC0012704. The authors would like to thank BL14W1 in Shanghai Synchrotron Radiation Facility (SSRF) for providing the beam time to perform part of XAFS measurements.
Author information
Authors and Affiliations
Contributions
K.J. conceptualized the project. Ji.Z. and K.J. developed and performed catalyst synthesis, conducted the electrochemical tests and the related data processing. Ji.Z. performed materials characterization with the help of K.Y., Z.L. and X.Z. XAFS experiments and relevant analysis were carried out by F.J., L.M. and Z.S. and X.W. C.F., S.S. and Ju.Z. performed the DFT simulations. Ji.Z., C.F. and K.J. wrote the paper. K.J. and Ju.Z. supervised the project. All authors discussed the results and commented on the paper.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. Peer reviewer reports are available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhao, J., Fu, C., Ye, K. et al. Manipulating the oxygen reduction reaction pathway on Pt-coordinated motifs. Nat Commun 13, 685 (2022). https://doi.org/10.1038/s41467-022-28346-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-022-28346-0
- Springer Nature Limited
This article is cited by
-
Synthesis of ultrahigh-metal-density single-atom catalysts via metal sulfide-mediated atomic trapping
Nature Synthesis (2024)
-
Atomically dispersed asymmetric cobalt electrocatalyst for efficient hydrogen peroxide production in neutral media
Nature Communications (2024)
-
Constructing sulfur and oxygen super-coordinated main-group electrocatalysts for selective and cumulative H2O2 production
Nature Communications (2024)
-
Oxygen reduction electrocatalysis: From conventional to single-atomic platinum-based catalysts for proton exchange membrane fuel cells
Frontiers in Energy (2024)
-
The reformation of catalyst: From a trial-and-error synthesis to rational design
Nano Research (2024)