Abstract
The synthesis of well-defined block copolymers from a mixture of monomers without additional actions (“one-pot/one-step”) is an ideal and industrially valuable method. In addition, the presence of controlled alternating sequences in one or both blocks increases the structural diversity of polymeric materials, but, at the same time, the synthetic difficulty. Here we show that the “one-pot/one-step” ring-opening terpolymerization of a mixture of three monomers (N-sulfonyl aziridines; cyclic anhydrides and epoxides), with tert-butylimino-tris(dimethylamino)phosphorene (t-BuP1) as a catalyst, results in perfect diblock dialternating terpolymers having a sharp junction between the two blocks, with highly-controllable molecular weights and narrow molecular weight distributions (Ð < 1.08). The organocatalyst switches between two distinct polymerization cycles without any external stimulus, showing high monomer selectivity and kinetic control. The proposed mechanism is based on NMR, in-situ FTIR, SEC, MALDI-ToF, reactivity ratios, and kinetics studies.
Similar content being viewed by others
Introduction
Block copolymerization technology has attracted considerable interest in commercial applications as it combines in the same molecule the unique characteristics of each segment1,2,3,4. By controlling the composition, molecular weight/molecular weight distribution, and structure of each segment, the properties of the final block copolymers can be adjusted5. This is why block copolymers are widely used in thermoplastic elastomer6,7, drug delivery8, membrane9, lithography10, and mesoporous material11 industrial sectors. The synthesis of well-defined block copolymers is achieved using a living or controlled/living polymerization to ensure predictable molecular weight/structure and a high degree of molecular, structural, and compositional homogeneity.
Diblock copolymers via a living/controlled polymerization can be synthesized by (a) “two-pot/two-step”, (b) “one-pot/two-step”, and (c) “one-pot/one-step” procedures. In the “two-pot/two-step” procedure, the first segment synthesized in one reactor requires complex and costly modification/purification processes before being used for the second polymerization in another reactor. The “one-pot/two-step” procedure avoids the isolation of the first block and requires either a perfect living polymerization (stability of the living chains and complete conversion of monomer to polymer) compatible with both monomers, as is the case of anionic polymerization, or a switching procedure after the total consumption of the first monomer, such as catalyst switch (Lewis acid/base-12,13 or redox-14,15 switchable), or experimental condition switch (thermal16,17, electricity18, photochemistry19,20, and gas atmosphere21,22). Switching between two polymerizations is both critical and challenging; an early switch leads to a gradient/random sequence, and a delayed switch can cause other harmful side reactions (such as transesterification23 and decomposition24). If an auto-switch occurs after the complete consumption of the first monomer, we have the “one-pot/one-step” procedure, and thus the synthesis of diblock copolymers is simple and industrially valuable. A few diblock copolymers are synthesized by the “one-pot/one-step” procedure due to strict requirements regarding monomer reactivity ratios and activity/selectivity of initiating/catalytic system. Another way to “one-pot/one-step” synthesis of block copolymers requires heterofunctional initiators for polymerizations that can proceed simultaneously25,26,27.
On the other hand, the “one-pot/one-step” alternating copolymerization of two monomers is an excellent, but challenging method to synthesize polymers with a rich diversity in structures and properties28,29,30. The following monomer pairs of epoxide/CO231,32,33, epoxide/cyclic anhydride28,34, epoxide/isocyanate35,36, and aziridine/cyclic anhydride37,38, resulted in polycarbonates, polyesters, polyurethanes, and poly(ester amide)s, respectively. However, the synthesis of diblock copolymers with two controlled alternating sequences in both blocks with a sharp boundary by the “one-pot/one-step” procedure is extremely challenging.
In 2008, Coates and co-workers were the first to report the terpolymerization of cyclohexene oxide (CHO), diglycolic anhydride, and carbon dioxide towards diblock dialternating terpolymers using metal catalysts39, but, unfortunately like a few others40,41,42,43, the obtained dialternating polyester-b-polycarbonate terpolymers, were contaminated by about 10% of a tapered structure. It is well known that the tapered chain between the two neat blocks affects their mechanical properties44.
In this work, we extend our previous work on the ring-opening copolymerization (ROCOP) of N-sulfonyl aziridines and cyclic anhydrides leading to either alternating copolymers or (alternating copolymer)-b-homopolymer37, to ring-opening terpolymerization of N-sulfonyl aziridines, cyclic anhydrides, and epoxides. We discovered that tert-butylimino-tris(dimethylamino)phosphorene (t-BuP1) catalyst shows high selectivity in monomers and kinetic control for two alternating copolymerization cycles without competitive side reactions leading to perfect diblock dialternating poly(ester amide)-b-polyester via a “one-pot/one-step” with a sharp boundary, controlled molecular weight and narrow molecular weight distribution.
Results
Terpolymerization of N-tosylaziridine (TAz), phthalic anhydride (PA), and epoxide
As a starting point for the current investigations, the terpolymerization of TAz, PA, and propylene oxide (PO) with the initiator [BnN(H)Ts] without catalyst was performed at 100 °C in tetrahydrofuran (THF) or bulk (entries 1 and 2 in Table 1 and Fig. 1). No polymer signals were detected by proton nuclear magnetic resonance (1H NMR) spectroscopy, indicating the absence of any polymerization. t-BuP1 was then selected as the catalyst for the terpolymerization because, even in small amounts, it catalyzes the controlled ROCOP of TAz/PA37 and PO/PA45. After the addition of t-BuP1 ([BnN(H)Ts]/[t-BuP1] = 1/0.5), the ROCOP of TAz/PA started immediately (entry 3 in Table 1, Supplementary Table 1, and Supplementary Fig. 1) as evidenced by the 1H NMR spectra of samples (Supplementary Fig. 1) collected during the terpolymerization. The aromatic peaks (7.81 and 7.33 p.p.m.) decreased rapidly with the simultaneous increase of the methylene signals of poly(TAz-alt-PA) (4.42 and 4.19 p.p.m.). TAz and PA conversions reached 91 and 30% within 45 min ([TAz]0/[PA]0 = 1/3), respectively. The characteristic signals of poly(PA-alt-PO) (5.41 p.p.m.) and poly(propylene oxide) (PPO, 3.30–3.60 p.p.m.) were not observed in the 1H NMR spectra (Supplementary Fig. 1), indicating that insertion of PO was completely suppressed. The size-exclusion chromatography (SEC, Supplementary Fig. 1) traces were shifted to high molecular weight, but maintained unimodal/narrow distributions (Ð < 1.07), supporting that ROCOP of TAz/PA is well controlled without any transesterification reaction. Since ROCOP of TAz/PA has a first-order dependence on the TAz concentration37, slow copolymerization rates were observed at high TAz conversions (Supplementary Fig. 1 and Supplementary Table 1). Complete TAz consumption was reached in 1.5 h, and interestingly, without any PO insertion into the chain. The signal from the second-stage alternating units in poly(PA-alt-PO) (5.41 p.p.m.) was observed by 1H NMR only after 5 h (Supplementary Fig. 1). There is no overlap between the two copolymerization cycles, indicating the absence of a tapered sequence at the junction between the two alternating blocks. However, the SEC traces gradually widen with increasing PA conversion in the second copolymerization cycle and eventually split into two peaks, the lower corresponding to the unreacted first block (Supplementary Fig. 1).
Then, experiments under the same feed ratios were carried out in bulk (entries 5 and 6 in Table 1, Supplementary Table 2, and Supplementary Fig. 2). The increased monomer concentration accelerates the ROCOP of TAz/PA, with the total TAz consumption reached at 30 min (Supplementary Fig. 2). SEC traces and 1H NMR spectra show that the first-segment poly(TAz-alt-PA) is well defined with narrow molecular weight distributions (Ð < 1.06) without any PO insertion. However, during the second copolymerization cycle of PA/PO, the same problem was observed: the SEC traces are split into two peaks (Supplementary Fig. 2), with molecular weight distributions of each peak remaining narrow (1.03 and 1.05). The increased monomer concentration only accelerates the two copolymerization rates, but the bimodal peaks on SEC traces are consistent with the previous ones. The low molecular weight peaks appear at the same retention volume as the one of the first-segment poly(TAz-alt-PA) (macroinitiator) with almost the same molecular weight distributions (Supplementary Figs. 1 and 2), suggesting that part of it cannot participate in the second copolymerization cycle. The diffusion-ordered spectroscopy (DOSY) NMR spectrum of the precipitated polymer (Supplementary Fig. 3) shows two diffusion coefficients, corresponding to poly(TAz-alt-PA)-b-poly(PA-alt-PO) and unreacted poly(TAz-alt-PA) and thus supporting the SEC results.
The unreacted first-segment poly(TAz-alt-PA) may be the cause of insufficient t-BuP1. Thus, an equivalent t-BuP1 to BnN(H)Ts was then used for the terpolymerization of TAz, PA, and PO in bulk (entries 7 and 8 in Table 1, Fig. 2, and Supplementary Table 3). The increased t-BuP1 concentration accelerates the rates of both copolymerization cycles. The ROCOP of TAz/PA was completed quickly within 10 min, and after an additional 50 min, the second ROCOP of PA/PO was started (Fig. 2a and Supplementary Table 3). Therefore, there is no overlap between the two copolymerization cycles, leading to a sharp boundary instead of a tapered sequence at the conjunction between the two alternating blocks. In addition, no ether (3.30–3.60 p.p.m.) or amine linkage (3.20–3.30 p.p.m.) was observed, indicating the absence of TAz and PO self-homopolymerization. Narrow and symmetric SEC traces were observed during the two alternating copolymerization cycles (Fig. 2b, Ð < 1.06), indicating that the entire first living alternating block participated in the second copolymerization. All results reveal that increased t-BuP1 concentration accelerates both copolymerization rates and activates the entire first block (macroinitiator) for the second copolymerization without inserting any PO into the first-stage copolymerization.
Chain microstructure of poly(TAz-alt-PA)-b-poly(PA-alt-PO)
FTIR was used to confirm the structure of the first- and second-stage copolymers. After complete consumption of TAz, the first-stage copolymer was precipitated in methanol for FTIR characterization (Fig. 3a). The absorption peaks at 1721 and 1691 cm−1 correspond to the stretching vibration of C=O in esters and of amide groups, respectively, whereas at 1276 and 1252 cm−1 to the stretching vibration of C–N and C–O, respectively. The results confirm the presence of ester and amide linkages in the first-stage copolymer, indicating the presence of an alternating sequence of TAz and PA. After complete consumption of PA, the final diblock dialternating terpolymer was isolated and characterized by FTIR spectroscopy (Fig. 3b). The stretching vibration of C=O at 1721 and C–O at 1252 cm−1 in ester groups become significantly stronger (Fig. 3a, b, e), confirming the alternating sequence of PA and PO in the second stage.
The chemical structures of the diblock dialternating terpolymers were further analyzed by 1H NMR and 13C{1H} NMR spectroscopy (Fig. 4 and Supplementary Fig. 5). The characteristic signal peaks of the methylene protons of poly(TAz-alt-PA) between ester and amide groups were observed at 4.44 and 4.21 p.p.m. (a and b in Fig. 4a). We did not observe any amine linkage signal at 3.15–3.34 p.p.m., indicating the perfect alternating copolymerization of TAz/PA. The characteristic signal peaks of the second-stage copolymer poly(PA-alt-PO) were observed at 5.41 and 4.37 p.p.m., corresponding to the methine and methylene signals, respectively (j and k in Fig. 4a). There are no ether linkage signals at 3.30–3.60 p.p.m., indicating that there is no PO self-propagation. The carbonyl regions of the 13C{1H} NMR spectrum (Supplementary Fig. 5) at 169.9 and 164.7 p.p.m. represent the amide and ester groups of poly(TAz-alt-PA), respectively. The characteristic signal peaks of the carbonyl group from poly(PA-alt-PO) were observed at 167.0 and 168.8 p.p.m. The absence of any other peaks of heterosequences excludes the presence of tapered sequence and transesterification reactions during terpolymerization.
The final diblock dialternating terpolymer was also analyzed by DOSY NMR spectra (Fig. 4b), showing a single diffusion coefficient corresponding to the product and not either to a blend of poly(TAz-alt-PA) and poly(TAz-alt-PA)-b-poly(PA-alt-PO) (Supplementary Fig. 3) or poly(TAz-alt-PA) and poly(PA-alt-PO) (Supplementary Fig. 4). The DOSY NMR spectroscopy supports the sharp connection of the two copolymer segments.
Matrix-assisted laser desorption ionization time-of-flight mass spectroscopy (MALDI-ToF MS) was used to confirm further the structure and terminal functional group of the first-stage poly(TAz-alt-PA) (Fig. 5). The first-stage copolymer was obtained after complete TAz conversion at a low molar ratio TAz:PA = 15:45 in PO. The two series of peaks obtained correspond to the sodium- or potassium-cationized poly(TAz-alt-PA), containing BnN(H)Ts at one chain end and TAz or PA at the other chain end. The molecular mass of the adjacent peaks shows a fixed interval of 345.07, which is the molecular mass of a repeating unit of TAz and PA. The results show that the copolymers have a perfectly alternating unit of TAz and PA, indicating the absence of any transesterification side reaction during terpolymerization. There is no insertion of PO into the copolymer, indicating that there is no tapered sequence between the two copolymerization cycles. All analytical and spectroscopy techniques support the formation of the desired diblock dialternating terpolymer poly(TAz-alt-PA)-b-poly(PA-alt-PO) without any tapered sequences.
Kinetic analysis
The kinetics of the terpolymerization of TAz, PA, and PO was also studied by NMR and in-situ FTIR. Since the low-boiling point of PO (34 °C) easily causes changes in the reaction concentration, we conducted a series of parallel experiments monitored by 1H NMR spectra by quenching aliquots for convincing experimental results (repeat all results three times). As shown in Fig. 6a, the first-stage copolymerization of TAz and PA (Supplementary Table 3) is very fast, with 97% TAz and 32% PA conversion in 5 min as monitored by 1H NMR ([TAz]0/[PA]0 = 1/3). The molecular weight of the copolymer calculated by 1H NMR increases with the reaction time, in agreement with the theoretical molecular weight of poly(TAz-alt-PA) (Fig. 6b). All the SEC traces are symmetrical, monomodal, and narrow (Fig. 6b, Ð < 1.06). These results suggest a living copolymerization behavior. After TAz was completely consumed, the second-stage copolymerization of PA and PO proceeded (Fig. 6a). A linear relationship is observed between the reaction time and the PA conversion, indicating a zero-order dependence on the PA concentration, which is consistent with previously reported work46. The molecular weight of the copolymers against reaction time shows a linear increase in the second stage, and the diblock dialternating terpolymers maintain the narrow molecular weight distribution (Fig. 6b, Ð < 1.04).
In order to investigate the terpolymerization behavior, a study was performed at 60 °C under the same conditions and monitored by in situ FTIR and 1H NMR (Fig. 6c). The decreased temperature slows down the reaction rates of both the first-stage (kobs,first stage = 11.7196 mol L−1 h−1 in 100 °C; kobs,first-stage = 0.4773 mol L−1 h−1 in 60 °C) and the second-stage copolymerization (kobs,second stage = 0.4500 mol L−1 h−1 in 100 °C; kobs,second stage = 0.0682 mol L−1 h−1 in 60 °C) (Supplementary Figs. 45–48). Monomers conversions by in situ FTIR are consistent with those of 1H NMR. After complete consumption of TAz, a dormant period is observed by both in situ FTIR and 1H NMR specrtoscopy. The trace amount of TAz in the reaction solution may suppress the insertion of PO. Only after all TAz has been converted to copolymers does the second copolymerization of PA/PO begin. In order to verify the relationship between TAz and the dormant period, another part of TAz was fed during the second stage of the copolymerization (PA/PO ROCOP) (Supplementary Figs. 43 and 49 and Supplementary Table 20). It was found that the ROCOP of PA/PO was immediately transferred to ROCOP of TAz/PA. Another new dormant period was observed after the total consumption of TAz, suggesting that residual TAz inhibits the ROCOP of PA/PO. As a result, no tapered sequence is observed at the junction of the two block copolymers.
Proposed terpolymerization mechanism
Based on the above experiments, two plausible copolymerization pathways are proposed (Fig. 7 and Supplementary Fig. 50). The two alternating blocks come from the two alternating copolymerization cycles: TAz/PA ROCOP and PA/PO ROCOP, with PA to participate in both copolymerization cycles. In the first cycle, TAz/PA ROCOP takes place, and kinetic studies show that the PA ring-opening is fast. The resulting phosphazenium carboxylate intermediate (–COO−/t-BuP1-H+, Supplementary Fig. 51) from PA reacts with TAz instead of PO. After ring opening of TAz, the proton on the t-BuP1-H+ is transferred to the new chain end, forming –N(Ts)H/t-BuP1 (Supplementary Fig. 53), due to the stronger basicity of –N(Ts)−. The generated amine –N(Ts)H rapidly attacks PA instead of PO (Fig. 7, cycle 1). The fast proton exchange between the t-BuP1 and t-BuP1-H+ is plausible and supported by Supplementary Fig. 5347. TAz/PA ROCOP proceeds quickly until TAz is almost completely consumed. At the end-point of the first copolymerization cycle, slow copolymerization rates were observed at high TAz conversions, and finally, a dormant period. The t-BuP1/t-BuP1-H+ complex corresponds to dormant species that can suppress the activation of t-BuP1-H+ to PO (Supplementary Fig. 53). After the complete consumption of TAz, the t-BuP1-H+ released from t-BuP1 switches to activated species and starts the second copolymerization cycle (PA/PO ROCOP). Similar proton shuttling between the catalysts and growing chain end is considered key to promoting selectivity and control for the copolymerization45. For both copolymerization cycles, the phosphazenium shows high monomer selectivity and polymerization controllability.
The reactivity ratios were determined by real-time 1H NMR kinetics using the Fineman–Ross and Mayo–Lewis methods. The alternating characteristic is observed for TAz/PA copolymerization cycle (rTAz = 0.0089 and rPA = 0.0052, Supplementary Figs. 68 and 69), showing that the copolymerization rate of TAz/PA is faster than the homopolymerization rate of TAz. The PA/PO copolymerization shows a perfect alternating characteristic (rPA = rPO = 0) because the PA and PO cannot be homopolymerized by t-BuP1 at 100 °C for 5 h. The extreme reactivity difference of TAz/PO indicates that the homopolymerization rate of TAz is faster than the copolymerization rate of TAz/PO48. All the reactivity ratios support the following: copolymerization rate of TAz/PA > homopolymerization rate of TAz » copolymerization rate of TAz/PO > homopolymerization rate of PA or homopolymerization rate of PO.
Extension to other monomers, initiators, and catalysts
Other epoxides were used in the terpolymerization to synthesize diverse diblock dialternating terpolymers by a “one-pot/one-step” procedure. Ethylene oxide (EO) with higher monomer reactivity than PO accelerates the second-stage copolymerization rate (entries 9–11 in Table 1 and Supplementary Table 5). The 1H NMR, 13C{1H} NMR spectra, SEC traces, and DOSY spectrum (Supplementary Figs. 8–12) confirm the successful synthesis of diblock dialternating terpolymer poly(TAz-alt-PA)-b-poly(PA-alt-EO). A little transesterification reaction is observed at high PA conversion at 100 °C because of the high nucleophilic character of chain-end alkoxide from EO ring opening. But the transesterification reaction can be successfully avoided by decreasing the reaction temperature to 60 °C (Supplementary Fig. 9). Butylene oxide (BO) with similar reactivity with PO can be used too in the terpolymerization with TAz and PA, to synthesize diblock dialternating terpolymer (Supplementary Figs. 13–16). Styrene oxide (SO), 1,2-epoxy-3-phenoxypropane, n-buty glycidyl ether, and CHO were evaluated in the terpolymerization with TAz and PA (Supplementary Figs. 26–29). Incomplete diblock dialternating terpolymers [a mixture of poly(TAz-alt-PA)-b-poly(PA-alt-epoxides) and poly(TAz-alt-PA)] and a decrease in the alternating degree for TAz/PA ROCOP were observed by 1H NMR and SEC. We attempted to prepare perfect diblock dialternating terpolymers by changing temperature (60 °C), solvent (THF and DMF), and amount of t-BuP1 (t-BuP1:In = 2:1) without success. The polarity of the epoxides, including dielectric constant and dipole moment, may be the reason for the slow or incomplete dissociation of the chain end in the second copolymerization cycles, resulting in inefficient initiation and the formation of incomplete diblock dialternating terpolymers. The substitution groups on the epoxides may hinder the nucleophilic attack of the chain end and lead to incomplete initiation. Two more N-sulfonyl aziridines were synthesized and used in the terpolymerization with PA and PO. The high active N-brosylaziridine (BAz) and N-(4-nitrobenzenesulfonyl) aziridine (NAz) accelerate the first copolymerization stage (Supplementary Tables 14 and 15). The 1H NMR, 13C{1H} NMR spectra, SEC traces, and DOSY spectrum (Supplementary Figs. 30–36) confirm the successful synthesis of diblock dialternating terpolymers. Bifunctional initiators, 1,4-benzenedimethanol and polyethylene glycol (Mn = 8000, PEG8000), were used to synthesize ABCBA-type pentablock terpolymers (entries 18–21 in Table 1). We did not observe any methylene signal peak of the 1,4-benzenedimethanol (4.73 ppm, Supplementary Fig. 19) on the terpolymers (Supplementary Fig. 18), indicating that both hydroxyl groups on the 1,4-benzenedimethanol can initiate the terpolymerization. Well-controlled diblock alternating terpolymers with narrow molecular weight distributions are obtained in the absence of a tapered sequence (Supplementary Figs. 17–24).
Other catalysts (t-BuP4, t-BuP2, DBU, and TBD) were evaluated in the terpolymerization (entries 22–27 in Table 1, Supplementary Figs. 37–40, and Supplementary Tables 16 and 17). t-BuP4 and t-BuP2 possessing higher basicity than t-BuP1 accelerate the first copolymerization cycle of TAz/PA and remain the controlled polymerization behavior (entries 22–25 in Table 1, Supplementary Tables 16 and 17, and Supplementary Figs. 37 and 38). However, the SEC traces show broad molecular weight distributions (Ð: 1.13–1.77) in the second copolymerization of PA/PO, indicating the presence of extensive transesterification. In the case of terpolymerization catalyzed by DBU and TBD (entries 26–27 in Table 1 and Supplementary Figs. 39 and 40), the ether (3.30–3.60 p.p.m.) and amine linkage (3.20–3.30 p.p.m.) were observed by NMR in both copolymerizations, indicating poor alternating characteristics.
Initial monomers feed ratios (TAz/PA) were changed to 1/2 and 1/4 in the terpolymerization (entries 28–31 in Table 1 and Supplementary Figs. 41 and 42). The 1H NMR and SEC traces (Supplementary Figs. 41 and 42) confirm the successful synthesis of diblock dialternating terpolymers.
Thermal analysis
The diblock dialternating terpolymers were analyzed by differential scanning calorimetry (DSC, Supplementary Figs. 64 and 65) and thermogravimetric analysis (Supplementary Figs. 66 and 67). Poly(TAz-alt-PA)30-b-poly(PA-alt-PO)60 shows a single glass transition temperature (Tg) of 72 °C between the Tg of poly(TAz-alt-PA)30 (114 °C) and poly(PA-alt-PO)60 (59 °C), indicating a complete mixing of the two alternating blocks, due to the common PA monomer. Decreasing the polymerization degrees of second block increases the Tg value [Tg of Poly(TAz-alt-PA)30-b-poly(PA-alt-PO)30 is 78 °C], and vice versa [Tg of Poly(TAz-alt-PA)30-b-poly(PA-alt-PO)90 is 64 °C]. Diblock dialternating terpolymers synthesized by other organic base catalysts(t-BuP4, t-BuP2, DBU, and TBD) showed lower Tg values (61–68 °C, Supplementary Fig. 65). Compared with homopolymer poly(PA-alt-PO)60 (Td 5% = 327 °C), all the diblock dialternating terpolymers show lower thermal stability (Td 5% = 251–266 °C) (Supplementary Figs. 66 and 67).
In summary, diblock terpolymers with two alternating sequences, poly(N-sulfonyl aziridine-alt-phthalic anhydride)-b-poly(phthalic anhydride-alt-epoxide), were synthesized by terpolymerization of N-sulfonyl aziridines, PA, and epoxides without additional actions (“one-pot/one-step”). Two alternating copolymerization cycles have been proposed, which include ROCOP of N-sulfonyl aziridines/PA and ROCOP of PA/epoxides. The proposed organocatalyst t-BuP1 auto-switches between two different alternating copolymerization cycles resulting in high monomer selectivity and kinetic controllability. The obtained diblock dialternating terpolymers have a sharp junction between the two block segments rather than tapered sequences. Terpolymers with two precise alternating structures, controllable molecular weights, and narrow molecular weight distributions (Ð < 1.08) were obtained through the terpolymerization process. The synthetic strategy of diblock terpolymers with two alternating sequences in a “one-pot/one-step” procedure is promising and profound for industrial development. Furthermore, with the use of multifunctional initiators, as in the case of the synthesized pentablock, this methodology opens new horizons to dialternating-based complex macromolecular architectures.
Methods
Materials
t-BuP1 was supplied by Aldrich Chemicals and used without further purification. TAz (98%), 1,4-benzenedimethanol, and PEG8000 were supplied by Aldrich Chemicals and were dried over phosphorus pentoxide overnight twice. PA (Aldrich ≥99%) was provided by Aldrich Chemicals and was purified by heating a 10 wt.% solution in CHCl3 under reflux for 30 min, followed by hot filtration through Celite. The filtrated PA was recrystallized at room temperature, and the obtained PA crystal was sublimated at 100 °C twice under a dynamic vacuum. Then, the PA was freeze-dried in dry 1,4-dioxane, followed by removal of water traces under vacuum in the presence of phosphorus pentoxide. 1,4-Dioxane, PO, and BO were dried over calcium hydride overnight, distilled, and then dried over n-butyllithium for 2 h, distilled, and then stored in a glovebox before use. EO was dried over sodium flakes overnight, distilled, and then stored in the refrigerator inside the glovebox. BAz and NAz were synthesized by ethanolamine and corresponding sulfonyl chloride in Supplementary Methods.
General procedure for the terpolymerization of N-sulfonyl aziridine, PA, and epoxide
As an example, the procedure corresponding to entry 7 (Table 1) is given below. Eleven 100 mL dry Schlenk thick reactors were prepared and charged, in an argon-filled glovebox, with the same feed ratio, which is PA (0.264 g, 1.8 mmol), TAz (0.116 g, 0.6 mmol), initiator (N-benzyl-4-methylbenzenesulfonamide) (0.0052 g, 0.02 mmol), and anhydrous epoxides (0.6 mL) (ideal gas law was used to estimate internal pressure). After stirring for 5 min, t-BuP1 (4.6 µL, 0.02 mmol) was added to each mixture. The reactors were sealed and then removed from the glovebox and stirred at 100 °C to initiate the polymerization. At a specific time, a reactor was taken out of the oil bath and quickly cooled down in an ice-water bath. A sample was taken from the crude product for SEC and NMR analysis. The produced terpolymer was precipitated by the slow addition of the diluted reaction solution (CHCl3) to an excess of methanol. The precipitation process was repeated three times, and the terpolymers were dried in a vacuum oven at 40 °C overnight. Isolated yield = 0.40 g, 87% (before taking samples). The procedure was repeated three times and the average values, as well the standard error bars, are given in the graphs.
Another example of the procedure corresponding to entry 11 (Table 1) is the following. Eleven 100 mL dry Schlenk thick reactors were prepared and charged, in an argon-filled glovebox, with the same feed ratio, which is PA (0.264 g, 1.8 mmol), TAz (0.116 g, 0.6 mmol), and initiator (N-benzyl-4-methylbenzenesulfonamide) (0.0052 g, 0.02 mmol) (ideal gas law is used to estimate internal pressure). The reactors were placed in a freezer inside a glovebox (−20 °C) for 60 min. The reactors were removed from the freezer, and anhydrous EO (0.6 mL) was added to each reactor. After stirring for 5 min, the reactors were placed back in the freezer (−20 °C) for 60 min, and then t-BuP1 (4.6 µL, 0.02 mmol) was added to each cold mixture. The reactors were sealed and then taken out of the glovebox and stirred at 100 °C to initiate the polymerization. At a specific time, a reactor was taken out of the oil bath and quickly cooled down in an ice-NaCl bath. A sample was taken from the crude product for SEC and NMR analysis. The produced terpolymer was precipitated by the slow addition of the diluted reaction solution (CHCl3) to an excess of methanol. The precipitation process was repeated three times, and the terpolymers were dried in a vacuum oven at 40 °C overnight. Isolated yield = 0.39 g, 89% (before taking samples). The procedure was repeated three times, and the average value, as well the standard error bars, are given in the graphs.
In situ FTIR study was conducted using a ReactIR 45m (Mettler Toledo) and equipped with a dip probe. The background was collected after an empty Schlenk flask was flame-dried under a vacuum. The probe was transferred into the argon-filled glovebox. The tip of the probe was immersed in the reaction mixture (the mixture prepared by the entry 7 procedure). The reactors were sealed and then taken out of the glovebox and stirred at 100 °C to start the polymerization. The spectra were collected every 1 min, and each spectrum was scanned 256 times.
Characterization
Nuclear magnetic resonance (1H NMR and 13C{1H} NMR) measurements were recorded on a Bruker AVANCE III-400 Hz instrument in CDCl3 at room temperature. DOSY measurements were recorded on a Bruker AVANCE III-600 Hz instrument in CDCl3 at room temperature. SEC measurements were performed at 35 °C with THF as an eluent at a flow rate of 1.0 mL min−1, with a Viscotek GPCmax VE2001 System, and PSS columns (Styragel HR 3, 4, and 5). The molecular weight distributions (Mw/Mn, Ð) were determined by conventional SEC analysis using a calibration curve from polystyrene standards. MALDI-ToF mass measurements were recorded in linear mode, using 2,5-dihydroxybenzoic acid as the matrix in THF (sample/matrix: 1/50). In situ FTIR study was conducted using a ReactIR 45m (Mettler Toledo). The samples were collected every 1 min, and each spectrum was scanned 256 times. DSC measurements were performed at a heating rate of 10 °C min−1 on a Mettler Toledo DSC1/TC100 system under a nitrogen atmosphere. The curve of the second heating scan was adopted to determine the Tg. NMR titration experiments were performed in Young’s NMR tubes using anhydrous toluene-d8 solvent under argon.
Data availability
The authors declare that the data supporting this study are available within the paper and the Supplementary information File. All other data is available from the authors upon request.
References
Hadjichristidis, N., Pispas, S. & Floudas, G. Block Copolymers: Synthetic Strategies, Physical Properties, and Applications (Wiley, 2003).
Matyjaszewski, K. Architecturally complex polymers with controlled heterogeneity. Science 333, 1104–1105 (2011).
Eagan, J. M. et al. Combining polyethylene and polypropylene: enhanced performance with PE/iPP multiblock polymers. Science 355, 814–816 (2017).
Bates, C. M. & Bates, F. S. 50th Anniversary Perspective: block polymers—pure potential. Macromolecules 50, 3–22 (2017).
Hadjichristidis, N., Hirao, A., Tezuka, Y. & Du Prez, F. Complex Macromolecular Architectures: Synthesis, Characterization, and Self-assembly (Wiley, 2011).
Domski, G. J., Rose, J. M., Coates, G. W., Bolig, A. D. & Brookhart, M. Living alkene polymerization: new methods for the precision synthesis of polyolefins. Prog. Polym. Sci. 32, 30–92 (2007).
Spontak, R. J. & Patel, N. P. Thermoplastic elastomers: fundamentals and applications. Curr. Opin. Colloid Interface Sci. 5, 333–340 (2000).
Kumar, N., Ravikumar, M. N. V. & Domb, A. J. Biodegradable block copolymers. Adv. Drug Deliv. Rev. 53, 23–44 (2001).
Krausch, G. & Magerle, R. Nanostructured thin films via self-assembly of block copolymers. Adv. Mater. 14, 1579–1583 (2002).
Boyd, D. A. in New and Future Developments in Catalysis (ed. Suib, S. L.) 305–332 (Elsevier, 2013).
Soler-Illia et al. Block copolymer-templated mesoporous oxides. Curr. Opin. Colloid Interface Sci. 8, 109–126 (2003).
Wang, X. et al. Traceless switch organocatalysis enables multiblock ring-opening copolymerizations of lactones, carbonates, and lactides: by a one plus one approach in one pot. Polym. Chem. 7, 6297–6308 (2016).
Zhao, J., Pahovnik, D., Gnanou, Y. & Hadjichristidis, N. A “catalyst switch” strategy for the sequential metal-free polymerization of epoxides and cyclic esters/carbonate. Macromolecules 47, 3814–3822 (2014).
Chen, C. Redox-controlled polymerization and copolymerization. ACS Catal. 8, 5506–5514 (2018).
Wang, X. et al. Redox control of group 4 metal ring-opening polymerization activity toward l-lactide and ε-caprolactone. J. Am. Chem. Soc. 136, 11264–11267 (2014).
Puga, J. B. et al. Novel thermal switch based on magnetic nanofluids with remote activation. Nano Energy 31, 278–285 (2017).
Olsén, P., Odelius, K., Keul, H. & Albertsson, A.-C. Macromolecular design via an organocatalytic, monomer-specific and temperature-dependent “on/off switch”. High precision synthesis of polyester/polycarbonate multiblock copolymers. Macromolecules 48, 1703–1710 (2015).
Qi, M., Dong, Q., Wang, D. & Byers, J. A. Electrochemically switchable ring-opening polymerization of lactide and cyclohexene oxide. J. Am. Chem. Soc. 140, 5686–5690 (2018).
Eisenreich, F. et al. A photoswitchable catalyst system for remote-controlled (co)polymerization in situ. Nat. Catal. 1, 516–522 (2018).
Ihrig, S. P., Eisenreich, F. & Hecht, S. Photoswitchable polymerization catalysis: state of the art, challenges, and perspectives. Chem. Commun. 55, 4290–4298 (2019).
Coulembier, O., Moins, S., Todd, R. & Dubois, P. External and reversible CO2 regulation of ring-opening polymerizations based on a primary alcohol propagating species. Macromolecules 47, 486–491 (2014).
Hu, C., Duan, R., Yang, S., Pang, X. & Chen, X. CO2 controlled catalysis: switchable homopolymerization and copolymerization. Macromolecules 51, 4699–4704 (2018).
Diaz, C. & Mehrkhodavandi, P. Strategies for the synthesis of block copolymers with biodegradable polyester segments. Polym. Chem. 12, 783–806 (2021).
Storey, R. F., Chisholm, B. J. & Masse, M. A. Morphology and physical properties of poly(styrene-b-isobutylene-b-styrene) block copolymers. Polymer 37, 2925–2938 (1996).
Mecerreyes, D. et al. Simultaneous dual living polymerizations: a novel one-step approach to block and graft copolymers. Angew. Chem. Int. Ed. 37, 1274–1276 (1998).
Weimer, M. W., Scherman, O. A. & Sogah, D. Y. Multifunctional initiators containing orthogonal sites. one-pot, one-step block copolymerization by simultaneous free radical and either cationic ring-opening or anionic ring-opening polymerization. Macromolecules 31, 8425–8428 (1998).
Bielawski, C. W., Louie, J. & Grubbs, R. H. Tandem catalysis: three mechanistically distinct reactions from a single ruthenium complex. J. Am. Chem. Soc. 122, 12872–12873 (2000).
Longo, J. M., Sanford, M. J. & Coates, G. W. Ring-opening copolymerization of epoxides and cyclic anhydrides with discrete metal complexes: structure–property relationships. Chem. Rev. 116, 15167–15197 (2016).
Paul, S. et al. Ring-opening copolymerization (ROCOP): synthesis and properties of polyesters and polycarbonates. Chem. Commun. 51, 6459–6479 (2015).
Jeske, R. C., DiCiccio, A. M. & Coates, G. W. Alternating copolymerization of epoxides and cyclic anhydrides: an improved route to aliphatic polyesters. J. Am. Chem. Soc. 129, 11330–11331 (2007).
Zhang, D., Boopathi, S. K., Hadjichristidis, N., Gnanou, Y. & Feng, X. Metal-free alternating copolymerization of CO2 with epoxides: fulfilling “green” synthesis and activity. J. Am. Chem. Soc. 138, 11117–11120 (2016).
Inoue, S., Koinuma, H. & Tsuruta, T. Copolymerization of carbon dioxide and epoxide. J. Polym. Sci. B 7, 287–292 (1969).
Raman, S. K., Raja, R., Arnold, P. L., Davidson, M. G. & Williams, C. K. Waste not, want not: CO2 (re)cycling into block polymers. Chem. Commun. 55, 7315–7318 (2019).
Diment, W. T. et al. Ortho-vanillin derived Al(iii) and Co(iii) catalyst systems for switchable catalysis using ε-decalactone, phthalic anhydride and cyclohexene oxide. Catal. Sci. Technol. 11, 1737–1745 (2021).
Jurrat, M., Pointer-Gleadhill, B. J., Ball, L. T., Chapman, A. & Adriaenssens, L. Polyurethanes and polyallophanates via sequence-selective copolymerization of epoxides and isocyanates. J. Am. Chem. Soc. 142, 8136–8141 (2020).
Jia, M., Hadjichristidis, N., Gnanou, Y. & Feng, X. Polyurethanes from direct organocatalytic copolymerization of p-tosyl isocyanate with epoxides. Angew. Chem. Int. Ed. 60, 1593–1598 (2021).
Xu, J. & Hadjichristidis, N. Well-defined poly(ester amide)-based homo- and block copolymers by one-pot organocatalytic anionic ring-opening copolymerization of N-sulfonyl aziridines and cyclic anhydrides. Angew. Chem. Int. Ed. 60, 6949–6954 (2021).
Xia, T. et al. Copolymerization of aziridines and cyclic anhydrides by metal-free catalysis strategy. Eur. Polym. J. 136, 109900 (2020).
Jeske, R. C., Rowley, J. M. & Coates, G. W. Pre-rate-determining selectivity in the terpolymerization of epoxides, cyclic anhydrides, CO2: a one-step route diblock copolymers. Angew. Chem. Int. Ed. 47, 6041–6044 (2008).
Darensbourg, D. J., Poland, R. R. & Escobedo, C. Kinetic studies of the alternating copolymerization of cyclic acid anhydrides and epoxides, and the terpolymerization of cyclic acid anhydrides, epoxides, and CO2 catalyzed by (salen)CrIIICl. Macromolecules 45, 2242–2248 (2012).
Zhang, J., Wang, L., Liu, S., Kang, X. & Li, Z. A Lewis pair as organocatalyst for one-pot synthesis of block copolymers from a mixture of epoxide, anhydride, and CO2. Macromolecules 54, 763–772 (2021).
Ye, S. et al. Metal-free approach for a one-pot construction of biodegradable block copolymers from epoxides, phthalic anhydride, and CO2. ACS Sustain. Chem. Eng. 8, 17860–17867 (2020).
Chidara, V. K., Boopathi, S. K., Hadjichristidis, N., Gnanou, Y. & Feng, X. Triethylborane-assisted synthesis of random and block poly(ester-carbonate)s through one-pot terpolymerization of epoxides, CO2, and cyclic anhydrides. Macromolecules 54, 2711–2719 (2021).
Hodrokoukes, P., Floudas, G., Pispas, S. & Hadjichristidis, N. Microphase separation in normal and inverse tapered block copolymers of polystyrene and polyisoprene. 1. Phase state. Macromolecules 34, 650–657 (2001).
Li, H., Zhao, J. & Zhang, G. Self-buffering organocatalysis tailoring alternating polyester. ACS Macro Lett. 6, 1094–1098 (2017).
Fieser, M. E. et al. Mechanistic insights into the alternating copolymerization of epoxides and cyclic anhydrides using a (Salph)AlCl and iminium salt catalytic system. J. Am. Chem. Soc. 139, 15222–15231 (2017).
Kadota, J. et al. Ring-opening polymerization of l-lactide catalyzed by an organocatalytic system combining acidic and basic sites. Macromolecules 43, 8874–8879 (2010).
Gleede, T., Rieger, E., Blankenburg, J., Klein, K. & Wurm, F. R. Fast access to amphiphilic multiblock architectures by the anionic copolymerization of aziridines and ethylene oxide. J. Am. Chem. Soc. 140, 13407–13412 (2018).
Acknowledgements
The research work was supported by King Abdullah University of Science and Technology (KAUST), Thuwal, Saudi Arabia.
Author information
Authors and Affiliations
Contributions
J.X. and N.H. conceived the idea and designed the experiments. J.X. performed the experiments. J.X. and X.W. performed the mechanism verification. All authors analyzed the results and co-wrote the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interest.
Additional information
Peer review information Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Xu, J., Wang, X. & Hadjichristidis, N. Diblock dialternating terpolymers by one-step/one-pot highly selective organocatalytic multimonomer polymerization. Nat Commun 12, 7124 (2021). https://doi.org/10.1038/s41467-021-27377-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-021-27377-3
- Springer Nature Limited
This article is cited by
-
One-pot synthesis of hyperbranched polymers via visible light regulated switchable catalysis
Nature Communications (2023)