Abstract
In antiferromagnetic spintronics, the read-out of the staggered magnetization or Néel vector is the key obstacle to harnessing the ultra-fast dynamics and stability of antiferromagnets for novel devices. Here, we demonstrate strong exchange coupling of Mn2Au, a unique metallic antiferromagnet that exhibits Néel spin-orbit torques, with thin ferromagnetic Permalloy layers. This allows us to benefit from the well-established read-out methods of ferromagnets, while the essential advantages of antiferromagnetic spintronics are only slightly diminished. We show one-to-one imprinting of the antiferromagnetic on the ferromagnetic domain pattern. Conversely, alignment of the Permalloy magnetization reorients the Mn2Au Néel vector, an effect, which can be restricted to large magnetic fields by tuning the ferromagnetic layer thickness. To understand the origin of the strong coupling, we carry out high resolution electron microscopy imaging and we find that our growth yields an interface with a well-defined morphology that leads to the strong exchange coupling.
Similar content being viewed by others
Introduction
A basic concept of antiferromagnetic (AFM) spintronics is to store information by the alignment of the staggered magnetization or Néel vector N, typically along one out of two perpendicular easy axes1,2,3,4. The major benefits of using AFMs as active elements in spintronics are their intrinsically fast THz dynamics5 and their stability against external magnetic fields, e.g., up to 30 T in the case of Mn2Au6.
Regarding the manipulation of the Néel vector orientation, the application of short current pulses creating spin-orbit torques (SOT) is a promising approach. These can be created at interfaces with heavy metal layers7,8,9 or for metallic compounds in the bulk of the AFM itself10. In the latter case, only CuMnAs and Mn2Au have been identified to combine the required crystallographic and magnetic structure with strong spin-orbit coupling, such that a current along a specific direction can create a bulk Néel spin-orbit torque (NSOT) acting on the Néel vector10. Indeed, for both compounds, current pulse-induced magnetoresistance effects of the order of 1% and below were observed and associated with a rotation of the Néel vector11,12,13,14,15. Furthermore, the current pulse-induced reorientation of the Néel vector of CuMnAs(001) and Mn2Au(001) was directly demonstrated by magnetic microscopy16,17. From these only two available compounds with a bulk NSOT, Mn2Au stands out concerning potential memory applications due to its metallic conductivity, high Néel temperature (>1000 K)18, and magnetocrystalline anisotropy, which results in a long term room temperature stability of Néel vector aligned states6.
Having established current-induced writing, still, the read-out of the Néel vector orientation in a potential device poses a major challenge. The magnitude of the anisotropic magnetoresistance effects (AMR) associated with the reorientation of N of metallic antiferromagnets amounts to only 0.1–1%13,19,20,21,22. The spin-Hall magnetoresistance, most often utilized for insulating AFMs, is even smaller7,8,9. However, most applications require magnetoresistance (MR) effects above 20%23.
In contrast to the case of AFM spintronics, such MR values are easily obtained in ferromagnetic (FM) spintronics, e.g., based on tunnel magnetoresistance (TMR) of FM/MgO/FM junctions24,25. Thus, coupling AFM layers to thin FM films enabling e.g., TMR-based read-out is highly desirable, provided that the fast dynamics of the AFM, as well as its resistance against disturbing magnetic fields, is only moderately diminished. The former requires sufficiently strong coupling forcing the magnetization to follow the Néel vector, the latter is obtained by using very thin FM layers as we show in this work. Additionally, the sensitivity to external fields could be further reduced by replacing the single FM layer by a synthetic antiferromagnetically coupled FM bilayer with zero net magnetization26.
Here, we demonstrate a strong exchange coupling of 40-nm-thick Mn2Au(001) epitaxial thin films with very thin (down to 2 nm) Permalloy (Py) layers. The coupling of the magnetization vector MF of the FM and of N results in the perfect imprinting of the AFM domain pattern of the Mn2Au film on the FM domain pattern of the soft Py layer. Similar imprinting was only reported for insulating AFM/ metallic FM bilayers such as 1.2 nm of Co on 40 nm of LaFeO327 or Fe(5 nm) on NiO (15 nm)28. However, in these cases, it was associated with a coercive field of only ≃100 Oe. In contrast, we show that 5000 Oe are required to reverse the magnetization of 2 nm of Py on 40 nm of Mn2Au(001). This, at room temperature, represents a coercive field corresponding to a field stability range, which is more than an order of magnitude larger than that in related CuMnAs/Fe(2 nm) bilayers, where a long term stable remanent magnetization was reported measuring at 200 K29. We show that in Mn2Au(001)/Py even at the coercive field of 5000 Oe MF and N do not decouple, but rotate together driven by the Zeeman energy of the FM layer. Thus, Mn2Au(001)/Py represents an excellent system for read-out in AFM spintronics. Furthermore, we identify the morphological origin of the exceptionally strong magnetic coupling between these AFM and FM layers.
Results
Mn2Au/Py samples
Mn2Au has a tetragonal crystal structure and orders antiferromagnetically well above 1000 K18. It shows collinear AFM order consisting of antiparallel stacked planes with FM order, as indicated in Fig. 1c. Within the easy (001)-plane, there are four equivalent easy <110> -directions, which results for our as-grown Mn2Au(001) thin films in the formation of AFM domains with a typical size of 1 μm corresponding to all four associated orientations of N6.
a Cross section HAADF STEM image of the entire stack viewed along the [\(\bar{1}\)10]-direction of Mn2Au(001). The inset shows a local Fourier transform of the Mn2Au region. b Magnified image of the Mn2Au/Py interface (region indicated by a rectangle in a), where Au atom columns have bright contrast. The inset shows a higher magnification image overlaid with a model of the crystal structure. c Crystal structure of Mn2Au with the magnetic moments pointing along the easy [\(\bar{1}\)10]-direction. d STM image of a pristine Mn2Au(001) thin film surface with steps corresponding to half unit cells (0.42 nm) indicated by the yellow lines, one unit cell (0.85 nm) indicated by the blue lines, and three unit cells (2.55 nm) indicated by the gray line.
Here, we investigate Mn2Au(001)(40 nm)/Ni80Fe20 (Py) (2 to 10 nm) bilayers, which are grown on Al2O3(r-plane) substrates with a Ta(001)-buffer layer and a capping layer of 2 nm of SiNx. Scanning transmission electron microscopy with high-angle annular dark-field imaging (STEM-HAADF) of the complete multilayer is shown in Fig. 1a. The Fourier transform of the epitaxial Mn2Au(001) thin film region (inset in Fig. 1a) shows regularly-spaced Bragg peaks, which confirm that the layer is monocrystalline. Most importantly, Fig. 1b shows a magnification of the interface between Mn2Au(001) and Py, where we find that our growth leads to a defined Au termination of the AFM thin film. This is supported by UHV STM-images of a pristine Mn2Au surface, which show atomically flat terraces with steps corresponding to the half or the full length of the c-axis (Fig. 1d). Such steps are consistent with the well-defined Au termination. This, as we demonstrate later, implies that the same AFM sub-lattice couples to the FM at the interface, which generates a very strong coupling and leads to a one-to-one correspondence of the AFM and FM domain patterns.
Hysteresis loops
We quantified the coupling between the Mn2Au(001) and Py layers by measuring magnetic hysteresis loops. Single Py films are in general magnetically soft with coercive fields of the order of a few Oe, which, as we will show below, drastically increases if they are coupled to AFM Mn2Au films.
Figure 2 shows hysteresis loops of a Mn2Au(40 nm)/Py(4 nm) bilayer measured in a superconducting quantum interference device (SQUID) with the easy [110] axis of the Mn2Au(001) thin film aligned parallel to the magnetic field direction.
Inset a shows subsequent hysteresis loops, i.e., measurements of the magnetization m of a Mn2Au(001)(40 nm)/Py(4 nm) sample taken with increasing applied magnetic fields H up to 103 Oe (aligned parallel to the easy [110] direction of Mn2Au). The main panel shows the subsequent loop up to 104 Oe (also aligned parallel to [110]). Inset b shows the coercive field Hc vs. the inverse saturation magnetization (with linear fit) obtained from Mn2Au(40 nm)/Py bilayers with the Py thickness varying from 2 to 10 nm.
After the as-grown sample consisting of an AFM multidomain state was placed in the SQUID, subsequent hysteresis loops with increasing maximum fields from 300 to 1000 Oe were measured as shown in the left inset of Fig. 2. In this field range, we obtained smooth hysteresis loops with almost zero remanent magnetization. This is consistent with a strong coupling of the Py magnetization to the AFM domain configuration of Mn2Au, which either remains unaffected by the magnetic field or restores the original domain configuration when the field is zero again.
However, once the magnetic field exceeds a threshold value, square-shaped easy axis loops with a coercive field Hc ≃ 1600 Oe were obtained, as shown in Fig. 2. This behavior can be readily explained by assuming a strong exchange coupling of MF and N, which results in the Zeeman energy of the FM layer driving a reorientation of N. Measuring hysteresis loops of Mn2Au(40 nm)/Py bilayers with various Py thicknesses varying from 2 to 10 nm, we observed linear scaling of the coercive field Hc with the inverse saturation magnetic moment 1/mF, as shown in the right inset of Fig. 2. This is consistent with the assumption that the Zeeman energy MF ⋅ H of the Py layer sets the remanent reorientation of both MF and N.
To check if this holds, we next probe the orientation of the magnetization and the Néel vector:
Probing the Néel vector orientation
We investigated the orientation of N and MF of a Mn2Au(40 nm)/Py(4 nm)/ SiNx(2 nm) sample by x-ray absorption spectroscopy (XAS), in the surface-sensitive total electron yield (TEY) as well as in the bulk sensitive substrate fluorescence yield (FY) mode. The magnetic contrast was obtained based on the x-ray magnetic linear and circular dichroism (XMLD/XMCD) effects, as described in the Methods section (the experimental geometry is shown in Fig. 3a).
Signal averaged over the x-ray illumination spot of ≃360 μm2 × 530 μm2. a Experimental geometry showing the x-ray polarization directions and orientation of the Mn2Au(001) epitaxial thin film. For measuring the XMCD with in-plane sensitivity, the sample is rotated by Θ = 60∘ around the y-axis. b TEY-XMCD at the Ni-L2,3-edge obtained with Θ = 60∘. c TEY-XMLD at the Mn-L2,3-edge obtained from the difference between XAS recorded with linear horizontal (lh) and XAS with linear vertical (lv) x-ray polarization, Θ = 0∘. d Bulk sensitive substrate FY-XMLD at the Mn-L2,3-edge, Θ = 0∘.
In the as-grown state of the sample, due to the relatively large diameter of the x-ray beam (≃500 μm), we average over many AFM/FM domains canceling both the XMLD and XMCD to zero. We then apply a magnetic field of 1 T (i.e., well below the spin-flop field of ≃30 T6,20) parallel to the x-axis, i.e., to the easy [110]-direction of Mn2Au(001) and subsequently reduce the field to zero again. In agreement with the hysteresis loops discussed above, this results in a significant Ni-L2,3 edge XMCD signal (measured at a tilt angle of Θ = 60∘) showing a sizable remanent in-plane magnetization of Py (Fig. 3b). Additionally, we demonstrate that the Néel vector of the AFM becomes aligned as well, both at the interface and in the bulk parallel to MF of the FM. The corresponding XMLD spectra (measured at Θ = 0∘) are shown in Fig. 3, obtained in the surface-sensitive TEY mode (Fig. 3c) as well as in the bulk sensitive substrate FY mode (Fig. 3d). From the characteristic sign change of the XMLD signal, we can conclude that N becomes aligned parallel to MF as deduced by comparison with previous results30. After applying the magnetic field parallel to the \([\bar{1}10]\)-direction of Mn2Au(001) and subsequently reducing the field to zero, the XMCD (Θ = 60∘) becomes zero since the remanent magnetization is oriented perpendicular to the direction of photon incidence. Consistently, the XMLD signal (Θ = 0∘) is inverted both at the interface and in the bulk as expected for a 90∘ rotated Néel vector.
With this strong parallel coupling of N and MF, we expect the AFM domain pattern of Mn2Au, as formed during thin film growth, to be imprinted into the FM domain pattern of the Py layer, which we verify by XMLD-photoelectron emission microscopy (PEEM).
Imaging the AFM/FM domain pattern
XMLD-photoelectron emission microscopy (PEEM) of the FM domain pattern of the Py layer and simultaneously of the AFM domain pattern of the Mn2Au(001) layer of a Mn2Au(40 nm)/Py(4 nm)/SiNx(2 nm) sample was performed with a perpendicular incidence of the photon beam, as described in the Methods section.
We first discuss samples in the as-grown state, which were not exposed to a magnetic field. As shown in Fig. 4, panels a (AFM domains) and b (FM domains), the AFM domain pattern of Mn2Au(001) is perfectly imprinted on the FM domain pattern of the Py layer. Note that we have chosen also the FM XMLD contrast mechanism. As a result, also for the FM domains, only the axis along which MF is aligned produces a brightness contrast, not its direction, allowing for a direct comparison.
The horizontal and vertical edges correspond to the four easy <110> directions of the epitaxial Mn2Au(001) thin film. The field of view is 10 μm2 × 10 μm2. a XMLD-PEEM image of the Mn2Au AFM domains in the as-grown state. b Corresponding XMLD-PEEM image of the Py FM domains. Both in a and b dark corresponds to N and MF right-left and bright to up-down. c SEMPA image showing the x-component of the FM contrast. d SEMPA image showing the y-component of the FM contrast. e is generated from d and e showing the orientation of MF by a color code, which indicates that MF of the Py domains is pointing parallel to all four easy <110> directions of the Mn2Au(001) thin film.
The size of the AFM/FM domains of ≃1 μm, is at least one order of magnitude larger than the typical distance between the steps at the surface shown in Fig. 1. Due to the well-defined Au termination of the Mn2Au(001) layer as discussed above, crossing a morphological step at the interface does not change the AFM sub-lattice to which the MF of Py couples. This enables a strong planar exchange coupling at the interface, as indicated in Fig. 5, which we address in more detail in the Discussion section.
This schematic cut through the bilayer shows a side view of two 90∘ domains and visualizes the morphological origin of the imprinting of the AFM domain pattern into the FM. Due to the specific interface morphology with a well-defined Au termination, MF is always aligned parallel with N and couples with the same relative orientation, despite the existence of atomic steps.
Due to the associated one-to-one correspondence of the AFM and FM domain pattern, we can indirectly obtain microscopic images of the Mn2Au AFM domains using scanning electron microscopy with polarization analysis (SEMPA)31 (Fig. 4c–e). Horizontal (Fig. 4c) and vertical (Fig. 4d) in-plane components of MF of Py are measured separately, revealing the direction of MF (Fig. 4e). Furthermore, SEMPA shows the same characteristics of the domain structure as the XMLD-PEEM images discussed above, but with the experimental advantage of the enhanced availability of a lab-based technique.
By SEMPA, we also verified that Mn2Au(40 nm)/Py(4 nm)/ SiNx(2 nm) samples, which were previously exposed to magnetic fields above Hc (see Fig. 2), are homogeneously magnetized.
Discussion
The initial AFM domain pattern of the 40 nm Mn2Au(001) thin films forms during growth driven by an intrinsic mechanism such as the minimization of elastic energy32 and couples to the Py magnetization during the room temperature deposition of this thin layer. No exchange bias is present or obtainable in the bilayers investigated here, because of the high Néel temperature >1000 K of Mn2Au18, which prevents the creation of exchange bias by standard field cooling procedures33.
Nevertheless, for a discussion of the magnetic coupling mechanism of the Mn2Au/Py bilayers, the physics of exchange bias systems34 is a good starting point. Such systems can be used as references for the magnitude of the coupling of the Py magnetization MF to the Néel vector N of Mn2Au(001): The coercive fields presented above are at least one order of magnitude larger than those of typical exchange bias systems with a comparable Py-layer thickness35,36,37,38. Regarding other work on Mn2Au/FM bilayers, coercive fields of the order of only 100 Oe or less were reported, which could be related to different growth directions of these Mn2Au thin film39,40 as well as to the selection of Fe as the FM layer33,39, or do a different morphology.
An explanation for the substantially different coercive fields is obtained by considering the morphology of the interface between the AFM and FM layers. Whereas in the general framework of exchange bias, typically interface irregularities of the AFM such as roughness or random alloy effects associated with uncompensated spins are discussed as pinning centers for FM domain walls41,42,43,44,45, a planar exchange interaction at the AFM-FM interface is able to couple the Néel and magnetization vectors of the respective layers much more strongly46. This necessarily requires ferromagnetically ordered atomic layers of one defined AFM sub-lattice forming the surface of the AFM. Nevertheless, just the appropriate type of magnetic ordering is not sufficient, as depending on the interface morphology atomic steps can result in an alternating sign of the exchange coupling if different sub-lattices are present at the AFM/FM interface.
However, we find that our growth of the Mn2Au(001)/Py bilayers leads to a well-defined Au termination of the surface of the Mn2Au(001) thin films (Fig. 1). This means that everywhere at the surface the same AFM sub-lattice couples to the FM resulting in the same sign of exchange coupling over each AFM domain as shown schematically in Fig. 5. This leads to a maximum coupling strength and thus enables the perfect imprinting of the AFM domain pattern of the Mn2Au(001) thin film on the FM domain structure of the Py layer, which by itself would be magnetically highly isotropic and soft.
The coupling of the Py magnetization MF to the Néel vector N is so strong that the layers are not even decoupled at the large coercive field but jointly rotated. We describe this reorientation under the action of the magnetic field using a macrospin model. Within this model, we describe the density of the magnetic energy per unit area of the Mn2Au/Py bilayer by
where the first term contains the magnetocrystalline anisotropy energy of Mn2Au (Han > 0 is the in-plane anisotropy field, Ms = ∣N∣), and the second term describes the exchange coupling of the Néel and Py magnetization vectors. tAF and tF are the thicknesses of the antiferromagnetic and ferromagnetic layers, Jcoup > 0, and ξ describe the strength and the characteristic length of the exchange coupling between the AFM and FM layers. The third term represents the Zeeman energy of the Py layer in a magnetic field H. The coordinate axes x and y are aligned along the easy magnetic axes of Mn2Au.
The equilibrium configurations are obtained by minimizing (1) with respect to the magnetic vectors MF and N. In zero field MF↑↑N are both parallel to \(\hat{x}\) or \(\hat{y}\). A magnetic field \({{{{{{{\bf{H}}}}}}}}\uparrow \uparrow \hat{x}\) splits the degeneracy between the states with MF↑↑H, MF↑↓H, and MF⊥H and creates a ponderomotive force ∝ BMF, which acts on the domain walls47. This force shifts the domain walls thus reducing the fraction of the energetically unfavorable states (domains). This process shows up in the smooth growth of the magnetization as shown in Fig. 2a. As long as the value of the applied field is not sufficient to remove all domain walls from the sample, the process is reversible, corresponding to the minor hysteresis loops.
However, above a threshold field value, the sample develops a single domain state and further cycling of the magnetic field induces switching between the states MF↑↑H and MF↑↓H. From the stability conditions for these states we obtain the coercive field
In the limit of strong exchange coupling, JcoupMFξ ≫ HantAF, the coercive field Hcoer → 4HanMstAF/(MFtF) is associated with the magnetocrystalline anisotropy of the Mn2Au layer and shows a linear dependence on the inverse magnetization 1/mF = 1/(MFtF) as observed experimentally (see Fig. 2b).
Inserting the experimentally determined magnetization of the Py layers of MF = 1.8μB per Ni80Fe20-atom and taking MS = 4μB per Mn-atom from18, we obtain Han ≃ 40 Oe, which corresponds to an anisotropy energy K4 = 2 ⋅ 4μB ⋅ 40 ⋅ 10−4T = 1.8 μeV per formula unit (f.u.). This is in good agreement with our previous estimation of K4 > 1 μeV/f.u.6, thereby supporting the validity of our model assumptions.
Hcoer should also increase with the thickness tAF of the Mn2Au layer, which we indeed observed experimentally (e.g., Hcoer = 2000 Oe for Mn2Au(60 nm)/Py(4 nm)). However, this increase is not linear, presumably due to a thickness dependence of the crystallographic order.
In summary, we demonstrated an extremely strong exchange coupling between the Néel vector N of the metallic antiferromagnet Mn2Au and the magnetization MF of ferromagnetic Py thin films. This results in the perfect imprinting of the AFM domain patterns of 40 nm Mn2Au(001) thin films on the FM domain pattern of thin (2–10 nm) Py layers, while maintaining high stability in external magnetic fields. The strong coupling results from the particular morphology that we obtain from our growth at the Mn2Au/Py interface, identified by TEM and STM, where within every domain always the same AFM sub-lattice couples to the FM thus maximizing the exchange coupling. This strong coupling of N and MF enables the electric detection of the Néel vector orientation via standard techniques used for ferromagnetic thin films, thereby providing a solution for the challenging read-out in antiferromagnetic spintronics.
Methods
All layers of the Al2O3(r-plane)/Ta(001)(13 nm)/Mn2Au(001)(40 nm)/Ni80Fe20 (Py)(2 to 10 nm)/SiNx(2 nm) samples were prepared by rf sputtering. The epitaxial Ta(001) buffer layers were sputtered with a substrate temperature of 700 ∘C, the epitaxial Mn2Au(001) thin films were deposited at 500 ∘C followed by an annealing procedure at 700 ∘C as described in refs. 48,49. All other layers are polycrystalline and were deposited at room temperature. SiNx(2 nm) sputtered from a Si3N4 target in Ar provides a very effective capping layer, which prevents sample oxidation while being highly transparent for photoemitted electrons50.
The magnetic hysteresis loops of the samples were measured in a Quantum Design MPMS SQUID-magnetometer.
The antiferromagnetic order in Mn2Au causes an x-ray magnetic linear dichroism (XMLD), i.e., an asymmetry in the absorption of linear polarized x-rays at the Mn-L2,3-edge for the polarization direction parallel and perpendicular to N30. It is sensitive to the components of N, which are parallel versus perpendicular to the electric field vector of the x-ray beam, but it does not change sign upon reversal of N. Thus we were able to investigate the orientation of N of a Mn2Au(40 nm)/Py(4 nm)/SiNx(2 nm) sample by x-ray absorption spectroscopy (XAS) at the I06 branch line at Diamond Light Source, which is equipped with a superconducting vector magnet. In parallel to probing the Néel vector orientation by XMLD, we were also able to probe the orientation of the magnetization of the Py layer using the x-ray circular dichroism (XMCD) at the Ni-L2,3 edge. The XMCD is an asymmetry in the absorption of circular polarized x-rays determined by the component of MF parallel to the direction of the incoming x-ray beam51. It does change sign upon reversal of MF. In the surface-sensitive total electron yield (TEY) mode, the sample current induced by the photoemitted electrons with an escape depth of 2–3 nm is probed52. In the bulk sensitive substrate fluorescence yield (FY) mode, the measurement signal originates from the x-rays transmitted through the magnetic layer stack generating fluorescence in the MgO substrates, which is probed by a photo diode53. The experimental geometry is shown in Fig. 3a.
XMLD-photoelectron emission microscopy (PEEM) was performed with a perpendicular incidence of the photon beam at the MAXPEEM beamline of MAX IV, Lund. The FM XMLD contrast was obtained at the L3 edge of Fe54, the AFM XMLD contrast at the L3 edge of Mn30. The SPELEEM microscope (Elmitec GmbH) of the MAXPEEM beamline provides, due to its perpendicular photon incidence on the sample surface, the highest possible AFM contrast for the in-plane orientation of the Néel vector of Mn2Au.
A SEMPA31 differs from an ordinary SEM in that it is additionally equipped with a spin detector to analyse the net spin of outgoing secondary electrons from ferromagnetic materials. This enables a spatial mapping of the spin polarization and by extension of the domain structure with a spatial resolution of less than 30 nm. As a ferromagnet possesses an inherent spin asymmetry in its density of states, the outgoing population of secondary electrons (which are ejected from a broad binding energy range) is spin-polarized. These secondary electrons undergo spin-dependent scattering at a W(100) single crystal via spin-polarized low-energy electron diffraction (SPLEED)55. Thus, up and down spin electrons are preferentially deflected towards separate electron counters and the difference of the count rates reflects the local magnetization direction.
Data availability
The magnetic hysteresis (Fig. 2) and XMCD/XMLD (Fig. 3) data generated in this study have been deposited in the Zenodo database under accession code https://doi.org/10.5281/zenodo.5588122.
References
MacDonald, A. H. & Tsoi, M. Antiferromagnetic metal spintronics. Philos. Trans. R. Soc. A 369, 3098 (2011).
Jungwirth, T. et al. The multiple directions of antiferromagnetic spintronics. Nat. Phys. 14, 200 (2018).
Baltz, V. et al. Antiferromagnetic spintronics. Rev. Mod. Phys. 90, 015005 (2018).
Jungfleisch, M. B., Zhang, W. & Hoffmann, A. Perspectives of antiferromagnetic spintronics. Phys. Lett. A 382, 865 (2018).
Kampfrath, T. et al. Coherent terahertz control of antiferromagnetic spin waves. Nat. Phot. 5, 31 (2011).
Sapozhnik, A. A. et al. Direct imaging of antiferromagnetic domains in Mn2Au manipulated by high magnetic fields. Phys. Rev. B 97, 134429 (2018).
Chen, X. Z. et al. Antidamping-torque-induced switching in biaxial antiferromagnetic insulators. Phys. Rev. Lett. 120, 207204 (2018).
Moriyama, T., Oda, K., Ohkochi, T., Kimata, M. & Ono, T. Spin torque control of antiferromagnetic moments in NiO. Sci. Rep. 8, 14167 (2018).
Baldrati, L. et al. Mechanism of Néel order switching in antiferromagnetic thin films revealed by magnetotransport and direct imaging. Phys. Rev. Lett. 123, 177201 (2019).
Železný, J. et al. Relativistic Néel-order fields induced by electrical current in antiferromagnets. Phys. Rev. Lett. 113, 157201 (2014).
Wadley, P. et al. Electrical switching of an antiferromagnet. Science 351, 587 (2016).
Wadley, P. et al. Current polarity-dependent manipulation of antiferromagnetic domains. Nat. Nanotechnol. 13, 362–365 (2018).
Bodnar, S. Y. et al. Writing and reading antiferromagnetic Mn2Au by Néel spin-orbit torques and large anisotropic magnetoresistance. Nat. Commun. 9, 348 (2018).
Zhou, X. F. et al. Strong orientation-dependent spin-orbit torque in thin films of the antiferromagnet Mn2Au. Phys. Rev. Appl. 9, 054028 (2018).
Meinert, M., Graulich, D. & Matalla-Wagner, T. Electrical switching of antiferromagnetic Mn2Au and the role of thermal activation. Phys. Rev. Appl. 9, 064040 (2018).
Grzybowski, M. et al. Imaging current-induced switching of antiferromagnetic domains in CuMnAs. Phys. Rev. Lett. 118, 057701 (2017).
Bodnar, S. Y. et al. Imaging of current induced Néel vector switching in antiferromagnetic Mn2Au. Phys. Rev. B 99, 140409(R) (2019).
Barthem, V. M. T. S., Colin, C. V., Mayaffre, H., Julien, M.-H. & Givord, D. Revealing the properties of Mn2Au for antiferromagnetic spintronics. Nat. Commun. 4, 2892 (2013).
Marti, X. et al. Room-temperature antiferromagnetic memory resistor. Nat. Mater. 13, 368 (2014).
Bodnar, S. Y. et al. Magnetoresistance effects in the metallic antiferromagnet Mn2Au. Phys. Rev. Appl. 14, 014004 (2020).
Volný, J. et al. Electrical transport properties of bulk tetragonal CuMnAs. Phys. Rev. Mat. 4, 064403 (2020).
Wang, M. et al. Spin flop and crystalline anisotropic magnetoresistance in CuMnAs. Phys. Rev. B 101, 094429 (2020).
Bhatti, S. et al. Spintronics based random access memory: a review. Mater. Today 20, 530 (2017).
Parkin, S. S. P. et al. Giant tunnelling magnetoresistance at room temperature with MgO (100) tunnel barriers. Nat. Mater. 12, 862 (2004).
Yuasa, S., Nagahama, T., Fukushima, A., Suzuki, Y. & Ando, K. Giant room-temperature magnetoresistance in single-crystal Fe/MgO/Fe magnetic tunnel junctions. Nat. Mater. 3, 868 (2004).
Yakushiji, K., Sugihara, A., Fukushima, A., Kubota, H. & Yuasa, S. Very strong antiferromagnetic interlayer exchange coupling with iridium spacer layer for perpendicular magnetic tunnel junctions. Appl. Phys. Lett. 110, 092406 (2017).
Nolting, F. et al. Direct observation of the alignment of ferromagnetic spins by antiferromagnetic spins. Nature 405, 767 (2000).
Slezak, M. et al. Fine tuning of ferromagnet/antiferromagnet interface magnetic anisotropy for field-free switching of antiferromagnetic spins. Nanoscale 12, 18091 (2020).
Wadley, P. et al. Control of antiferromagnetic spin axis orientation in bilayer Fe/CuMnAs films. Sci. Rep. 7, 11147 (2017).
Sapozhnik, A. A. et al. Manipulation of antiferromagnetic domain distribution in Mn2Au by ultrahigh magnetic fields and by strain. Phys. Stat. Sol. 11, 1600438 (2017).
Oepen, H.-P., Steierl, G. & Kirschner, J. Scanning electron microscope with polarization analysis: micromagnetic structures in ultrathin films. J. Vac. Sci. Technol. B 20, 2535 (2002).
Gomonay, H. & Loktev, V. M. Magnetostriction and magnetoelastic domains in antiferromagnets. J. Phys. Cond. Mat. 14, 3959 (2002).
Sapozhnik, A. A., Jourdan, M., Zabel, H., Kläui, M. & Elmers, H.-J. Exchange bias in epitaxial Mn2Au(001)/Fe(001) bilayers. J. Phys. D Appl. Phys. 52, 465003 (2019).
Nogués, J. & Schuller, I. K. Exchange bias. J. Magn. Mag. Mat. 192, 203 (1999).
Farrow, R. F. C., Marks, R. F., Gider, S., Parkin, S. S. P. & Mauri, D. MnxPt1−x: a new exchange bias material for permalloy. J. Appl. Phys. 81, 4986 (1997).
Pokhil, T., Linville, E. & Mao, S. Exchange anisotropy and micromagnetic properties of PtMn/NiFe bilayers. J. Appl. Phys. 89, 6599 (2001).
Rickart, M. & Freitas, P. P. Exchange bias of MnPt/CoFe films prepared by ion beam deposition. J. Appl. Phys. 95, 6317 (2004).
O’Grady, K., Fernandez-Outon, L. E. & Vallejo-Fernandez, G. A new paradigm for exchange bias in polycrystalline thin films. J. Magn. Mag. Mat. 322, 883 (2010).
Wu, H.-C. et al. Mn2Au: body-centered-tetragonal bimetallic antiferromagnets grown by molecular beam epitaxy. Adv. Mater. 24, 6374 (2012).
Chen, X. et al. Observation of the antiferromagnetic spin Hall effect. Nat. Mater. 20, 800 (2021).
Malozemoff, A. P. Random-field model of exchange anisotropy at rough ferromagnetic-antiferromagnetic interfaces. Phys. Rev. B 35, 3679 (1987).
Nowak, U. et al. Domain state model for exchange bias. I. Theory. Phys. Rev. B 66, 014430 (2002).
Keller, J. et al. Domain state model for exchange bias. II. Experiments. Phys. Rev. B 66, 014431 (2002).
Radu, F. & Zabel, H. Exchange bias effect of ferro-/antiferromagnetic heterostructures. Springe. Tracts Mod. Phys. 227, 97 (2008).
Gruyters, M. & Schmitz, D. Microscopic nature of ferro- and antiferromagnetic interface coupling of uncompensated magnetic moments in exchange bias systems. Phys. Rev. Lett. 100, 077205 (2008).
Meiklejohn, W. H. Exchange anisotropy-A review. J. Appl. Phys. 33, 1328 (1962).
Gomonay, O., Jungwirth, T. & Sinova, J. High antiferromagnetic domain wall velocity induced by Néel spin-orbit torques. Phys. Rev. Lett. 117, 017202 (2016).
Jourdan, M. et al. Epitaxial Mn2Au thin films for antiferromagnetic spintronics. J. Phys. D Appl. Phys. 48, 385001 (2015).
Bomammaboyena, S. P., Bergfeldt, T., Heller, R., Kläui, M. & Jourdan, M. High quality epitaxial Mn2Au (001) thin tilms grown by molecular beam epitaxy. J. Appl. Phys. 127, 243901 (2020).
Elmers, H.-J. et al. Néel vector induced manipulation of valence states in the collinear antiferromagnet Mn2Au. ACS Nano 14, 17554 (2020).
Schütz, G. et al. Absorption of circularly polarized x rays in iron. Phys. Rev. Lett. 58, 737 (1987).
O’Brien, W. L. & Tonner, B. P. Surface-enhanced magnetic moment and ferromagnetic ordering of Mn ultrathin films on fcc Co(001). Phys. Rev. B 50, 2963 (1994).
Kallmayer, M. et al. Interface magnetization of ultrathin epitaxial Co2FeSi(110)/Al2O3 films. J. Phys. D. Appl. Phys. 40, 1557 (2007).
Nolting, F. et al. Anisotropy of the L2,3 x-ray magnetic linear dichroism of Fe films on GaAs: experiment and ab initio theory. Phys. Rev. B 82, 184415 (2010).
Lofink, F., Hankemeier, S., Frömter, R., Kirschner, J. & Oepen, H. P. Long-time stability of a low-energy electron diffraction spin polarization analyzer for magnetic imaging. Rev. Sci. Inst. 83, 023708 (2012).
Acknowledgements
Funded by the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) - TRR 173 - 268565370 (projects A01, A05, and B12), by the Horizon 2020 Framework Program of the European Commission under FET-Open Grant No. 863155 (s-Nebula), and by the European Research Council (ERC) under the Horizon 2020 research and innovation program Grant No. 856538 (3D MAGIC). K.E.-S. acknowledges funding from the DFG project No. 320163632. We acknowledge MAX IV Laboratory for time on Beamline MAXPEEM under Proposal 20200160. Research conducted at MAX IV, a Swedish national user facility, is supported by the Swedish Research council under contract 2018-07152, the Swedish Governmental Agency for Innovation Systems under contract 2018-04969, and Formas under contract 2019-02496. We acknowledge Diamond Light Source for time on I06-1 under proposal MM29305. We would like to thank S. Jenkins for preparing Fig. 5.
Funding
Open Access funding enabled and organized by Projekt DEAL.
Author information
Authors and Affiliations
Contributions
S.P.B. and M.J. primarily wrote the paper with contributions from O.G. and M.K.; S.P.B prepared the samples and performed the SQUID as well as the SEMPA investigations; D.B., S.S.D., and L.S.I.V. performed and evaluated the XMCD-/XMLD-experiments; Y.R.N. and B.S. obtained the PEEM images; T.D. and A.K. contributed the STEM investigation; T.M. obtained the STM image; D.S. and R.M.R. supported the SEMPA investigations; H.-J.E., K.E.-S., and J.S. contributed to the discussion of the results; M.J. coordinated the project.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Cheng Song and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Bommanaboyena, S.P., Backes, D., Veiga, L.S.I. et al. Readout of an antiferromagnetic spintronics system by strong exchange coupling of Mn2Au and Permalloy. Nat Commun 12, 6539 (2021). https://doi.org/10.1038/s41467-021-26892-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-021-26892-7
- Springer Nature Limited
This article is cited by
-
Antiferromagnetic tunnel junctions for spintronics
npj Spintronics (2024)
-
Simulations of magnetization reversal in FM/AFM bilayers with THz frequency pulses
Scientific Reports (2023)
-
Current-driven writing process in antiferromagnetic Mn2Au for memory applications
Nature Communications (2023)
-
Terahertz Néel spin-orbit torques drive nonlinear magnon dynamics in antiferromagnetic Mn2Au
Nature Communications (2023)
-
Magnetic order and disorder environments in superantiferromagnetic \(\hbox {NdCu}_{\mathbf{2}}\) nanoparticles
Scientific Reports (2022)