Abstract
Near-infrared luminescent materials exhibit unique photophysical properties that make them crucial components in photonic, optoelectronic and biological applications. As broadband near infrared phosphors activated by transition metal elements are already widely reported, there is a challenge for next-generation materials discovery by introducing rare earth activators with 4f-5d transition. Here, we report an unprecedented phosphor K3LuSi2O7:Eu2+ that gives an emission band centered at 740 nm with a full-width at half maximum of 160 nm upon 460 nm blue light excitation. Combined structural and spectral characterizations reveal a selective site occupation of divalent europium in LuO6 and K2O6 polyhedrons with small coordination numbers, leading to the unexpected near infrared emission. The fabricated phosphor-converted light-emitting diodes have great potential as a non-visible light source. Our work provides the design principle of near infrared emission in divalent europium-doped inorganic solid-state materials and could inspire future studies to further explore near-infrared light-emitting diodes.
Similar content being viewed by others
Introduction
Near-infrared (NIR) light source has attracted attention for applications in medical fields, bio-sensing, food processing industry, and night-vision technologies1,2,3. Traditional NIR light sources, such as halogen lamps and tungsten-halogen lamps, suffer from large sizes, low efficiency, short lifetime, and heat dissipation4. As an emerging field, researchers have made considerable efforts to explore new NIR emitters, such as InAs-ZnSe polymer nanocrystal, CH3NH3PbI3–xClx organometal halide perovskite, PbS@MAPbX3 (X = I, Br) quantum dots, and Pt(II) complex based organic light-emitting diodes (LED)1,5,6,7. However, the low efficiency, poor stability or complex fabrication technique restrict their development. As a contrast, the high luminous efficiency, long operating life, and compact sizes make NIR LEDs useful, however, a narrow full-width at half maximum (FWHM) below 50 nm seriously limit their applications in 3D sensing, food analyzing, and other specific fields8. Therefore, discovery of broadband-emitting NIR light sources is a necessary and urgent requirement. In this regard, phosphor-converted light-emitting diodes LEDs (pc-LEDs) have attracted increasing interests considering more opportunities for tunable emission during the phosphors’ screening, and availability of simpler strategies for both materials design and fabrication of NIR pc-LEDs9,10,11,12. Furthermore, the low cost of NIR phosphors is beneficial. However, one of the most significant challenges is the discovery of blue light pumped and efficient broadband NIR-emitting phosphors.
Numerous studies on exploring NIR phosphors have been realized by doping transition metal ions (Cr3+, Ni2+, and Mn4+), Bi3+ or rare earth ions (Pr3+, Nd3+, Tm3+, and Yb3+) into inorganic host materials13,14,15,16,17,18,19. However, the sharp line emission of rare earth ions with 4f-4f transition is not broad enough for the desired applications, and the absorption region is also very narrow and weak. The Ni2+ doped materials show broad emission band around NIR region, but the low efficiency and IR laser excitation suspends the application20. Recently, Cr3+ ion has been considered as an ideal NIR luminescent center, which can exhibit broad-band emission ~650–1200 nm with 4T2 → 4A2 transition21,22,23. However, mixed valence of Cr6+ ions simultaneously exist in most Cr3+ doped phosphors, which seriously quench NIR luminescent efficiency21,24. As one of important rare earth activators with 4f-5d transition, Eu2+-activated phosphors normally possess high efficiency and have been applied in the field of commercial white LEDs. More importantly, the tunable emission in the visible range is very popular to discover useful phosphors, and the typical examples include Sr[LiAl3N4]:Eu2+ (red), β-SiAlON:Eu2+ (green) and BaMgAl10O17:Eu2+ (blue)25,26,27. If Eu2+-doped phosphors can realize NIR emissions, it would launch a new era in NIR light source. However, in addition to the recent report on Ca3Sc2Si3O12:Eu2+, no other Eu2+-doped phosphors can achieve NIR emissions with the peak beyond 700 nm28. Unfortunately, though Ca3Sc2Si3O12:Eu2+ gives a broad-band emission ranging from 720 to 1100 nm, it cannot be pumped by blue LEDs due to the lack of blue light absorption of the sample28. Therefore, discovery of Eu2+ activated NIR phosphors for blue light-pumped LEDs is an essential and difficult task for the emerging photonic, optoelectronic and biological applications.
The emission energy distribution of Eu2+ is generally related with the average bond lengths, coordination numbers and the symmetry of the cations and corresponding polyhedron occupied by Eu2+29. Many strategies, including neighboring-cation substitution, chemical unit cosubstitution and cation-size-mismatch have been used to tune visible photoluminescence of Eu2+ ions30. However, there is still a challenge to realize the NIR emission for the difficulties of obtaining strong crystal field splitting (CFS) and large centroid shift originating from Eu2+. Recently, our group has reported a new approach showing that Eu2+ selectively occupies a site with small coordination number, which tends to large redshift as found in Rb3YSi2O7:Eu2+ with red emission31. If the cations’ sites occupied by Eu2+ in Rb3YSi2O7 are substituted by smaller ions, this effect will produce a larger CFS and even realize NIR emission. Accordingly, we have designed a Eu2+-doped K3LuSi2O7 NIR phosphor from isostructural Rb3YSi2O7:Eu2+ by substituting the large Rb+ and Y3+ ions with small K+ and Lu3+ ions to further increase the CFS effect32.
Here in this work, we show that K3LuSi2O7:Eu2+ is the first Eu2+-doped NIR phosphor under 460 nm blue light excitation and gives a broad-band emission peaking at 740 nm in the NIR region (600–900 nm). Structural and spectral analysis results indicate that the selective Eu2+ site occupation in LuO6 and K2O6 polyhedrons contributes to the NIR light emission in K3LuSi2O7:Eu2+. The as-fabricated phosphor-converted LEDs have the potential to be used for non-visible light source, and the result could initiate the exploration of Eu2+-doped NIR phosphors and other NIR spectroscopy applications.
Results
Crystal structure of K3LuSi2O7:Eu2+
Figure 1a shows the simulated X-ray diffraction (XRD) profile of K3LuSi2O7 and the measured XRD patterns for the K3LuSi2O7:xEu2+ (x = 0–0.05) with different Eu2+-doping concentrations. All diffraction peaks can be well indexed by hexagonal cell (P63/mmc), and the parameters are similar to those of K3LuSi2O7 phase, confirming the successful synthesis of K3LuSi2O7:Eu2+ phosphors33. To further understand the phase structure and sites occupation of Eu2+ ions, Rietveld refinement were performed for K3LuSi2O7:xEu2+ (x = 0, 0.01, 0.02, and 0.04), as shown in Fig. 1b and Supplementary Fig. 1. All the refinements demonstrated low R-factors (Supplementary Table 1). Moreover, Supplementary Tables 2 and 3 listed the parameters of atoms’ coordinates and bond lengths of the studied phases for the comparison.
XRD patterns and crystal/local structure descriptions of K3LuSi2O7:Eu. a Simulated and measured XRD patterns of K3LuSi2O7 and K3LuSi2O7:xEu2+ (x = 0.01–0.05). b Rietveld refinement and c crystal structure of K3LuSi2O7. d Cell volume V(x) dependence of the Eu doping concentration (x = 0, 0.01, 0.02, 0.04). Small nonlinear trend can be associated with K → Eu replacement except for Lu → Eu substitution. e Dependence of the average bond length of Lu, K1, and K2 in K3LuSi2O7:xEu2+ (x = 0, 0.01, 0.02, 0.04)
K3LuSi2O7 host (Fig. 1c) offers one Lu sites with 6-fold coordination, and two different K sites: K1 (9-fold) and K2 (6-fold), for the possible occupation by Eu2+ ions. The cell volume increases with x (Fig. 1d), indicating that some Eu2+ ions occupy Lu sites since the radius of Lu3+ is smaller than that of Eu2+ (Supplementary Table 4). However, the unit cell volume, V(x) shows a nonlinear increasing trend with increasing Eu content, thus another occupation mechanism should exist simultaneously, which competes with the main trend and reduces cell volume. Such mechanism can be ascribed to K → Eu replacement because K ion is bigger than Eu ion (Supplementary Table 4)32. To further explore the Eu2+ selective site occupation, Fig. 1e illustrates the average bond lengths of LuO6, K1O9, and K2O6 polyhedron in different concentration of Eu2+ doped K3LuSi2O7 by extracting the data from Rietveld refinement. With increasing Eu2+ doping concentration, the average bond lengths of K1-O remain nearly unchanged, while the bond lengths of K2-O and Lu-O change significantly. In addition, the d(K2-O) and d(Lu-O) exhibit the same trend. It is owing to the fact that the occupation of Eu in Lu sites will lead to longer d(Lu-O) bond length, simultaneously, the amount of Eu in K2 sites is reduced and thus d(K2-O) bond lengths also become longer. Therefore, one can conclude that the main doping mechanism is ascribed to the synergetic effect of Lu → Eu and K → Eu replacements in K3LuSi2O7, which is similar to the site occupation of Eu2+ ions in isomorphic Rb3YSi2O731. The scanning electron microscopy (SEM) images and elemental mapping images in Supplementary Fig. 2 reveal that K3LuSi2O7:Eu2+ microcrystals are in well crystallized and K, Lu, Si, and O elements are homogeneously distributed.
Photoluminescence properties of K3LuSi2O7:Eu2+
Figure 2a gives the room temperature photoluminescence emission (PL) and excitation (PLE) spectra of K3LuSi2O7:0.01Eu2+. When monitored at 740 nm, K3LuSi2O7:0.01Eu2+ gives an ultra-broad excitation band and a maximum excitation peak is found ~460 nm in the range of 250 and 600 nm. Such a broad excitation band should be ascribed to the 4 f → 5d transition of two different Eu2+ sites in K3LuSi2O7, as verified by the structural analysis discussed previously, and some sharp lines are related with the spectrophotometer itself. Supplementary Figure 3a illustrates the diffuse reflection spectra of Eu2+ doped and undoped K3LuSi2O7 samples. K3LuSi2O7 host shows nearly no absorption from 300 to 800 nm, however, K3LuSi2O7:Eu2+ exhibits an ultra-broad absorption band from 250 to 600 nm with the introduction of Eu2+ in the host. K3LuSi2O7 exhibits a white body color under natural light suggesting a band gap of about 5 eV (Supplementary Fig. 3b). The diffuse reflection spectra of K3LuSi2O7:Eu2+ are in accordance with the excitation spectrum discussed above. Such a broad absorption band from ultraviolet to visible light region leads to deep red body color under natural light (the inset of Fig. 2a) and favors its application for blue light-pumped pc-LEDs. Thus, the NIR emission spectrum under 460 nm excitation reveals a broadband emission centered at 740 nm with FWHM ~160 nm (Fig. 2a). This emission is originated from the typical 5d → 4 f transition of Eu2+. The asymmetric spectral profile demonstrates that there exists more than one luminescent center in K3LuSi2O7:Eu2+. To verify this point, the PLE/PL spectra depending on the different experimental conditions are measured in detail. With the increase of excitation wavelengths from 300 to 360 nm, the normalized emission spectra display a large redshift from 695 nm to 745 nm (Fig. 2b). But a small blueshift in emission is observed when the excitation wavelength is increased beyond 360 nm. Also, the peak at 315 nm in the normalized excitation spectra gradually decreased as the monitored wavelength increased from 660 to 800 nm (Supplementary Fig. 4a). These results proved that multiple luminescent centers existed in K3LuSi2O7:Eu2+. Moreover, under the excitation of the laser LED light source with different excitation wavelengths at 375 nm and 450 nm, Supplementary Fig. 4b gives the normalized PL spectra of K3LuSi2O7:0.01Eu2+, suggesting the simillar spectral profiles.
Photoluminescence properties of K3LuSi2O7:Eu2+ phosphors. a PL and PLE spectra of K3LuSi2O7:0.01Eu2+ measured/monitored at 460 and 740 nm, and the inset shows the photograph of K3LuSi2O7:0.01Eu2+ with deep red body color under natural light. b Room temperature PL spectra of K3LuSi2O7:0.01Eu2+ under different excitation wavelength from 300 to 470 nm. c The emission spectrum of the K3LuSi2O7:0.01Eu2+ and Gaussian fitting curves. d Decay curves and fitting results of K3LuSi2O7:0.01Eu measured at 80 K and 300 K under 450 nm pulse laser diode excitation
The broad emission band upon the excitation of 460 nm is exactly deconvoluted into two Gaussian spectral profiles with two peaks at 13900 cm−1 (719 nm) and 12750 cm−1 (784 nm), suggesting that Eu2+ substitute two different cations in K3LuSi2O7 (Fig. 2c). Figure 2d shows the PL decay curves of K3LuSi2O7:0.01Eu2+ measured at low temperature (80 K) and at room temperature (300 K) under 450 nm pulse laser diode excitation. The decay curves were comparatively fitted by mono- (n = 1), bi- (n = 2) and triple- (n = 3) exponential functions:12
where I denotes luminescence intensity, t represents time; τi is lifetime for different components; and Ai is the corresponding fitting constants. As compared in Fig. 2d, the decay curve measured at 80 K is well fitted by both the bi- and triple-exponential function, and two fitting curves nearly overlap. However, the decay curves at 300 K can be only fitted by the triple-exponential function, which is ascribed to an additional room temperature nonradiative transition owing to the lattice thermal vibration. Accordingly, the average lifetime values are 1.58 μs (at 300 K) and 2.28 μs (at 80 K), respectively. The detailed fitting results are presented in Supplementary Table 5. Moreover, the decay times are shortened with increasing Eu concentration (Supplementary Fig. 5a) due to the energy transfer between different Eu2+ luminescent centers. Upon the excitation of 340 nm pulse laser diode, the average lifetime (1.69 μs) is longer than that under 450 nm excitation (1.58 μs) (Supplementary Fig. 5b and Supplementary Table 5), which is attributed to the more contribution of long-lived emitters to average decay time under 340 nm excitation.
To evaluate the robustness of phosphors to heat and moisture, two sets of K3LuSi2O7:Eu samples were exposed to the extremely environmental condition at 80% relative humidity and 80 °C. The results suggest that the chemical stability of K3LuSi2O7:Eu2+ is relatively good (see details in Supplementary Fig. 6). The Eu2+ content rarely changed to Eu3+ depending on the prolonging duration time suggesting the good stability. One can also note that a small amount of Eu3+ can be detected for the freshly prepared materials (Supplementary Fig. 7). Samples with different Eu2+-doping concentrations (x = 0.005–0.05) have been prepared to optimize the PL intensity of K3LuSi2O7:xEu2+. As displayed in Supplementary Fig. 8a, the emission intensities increase slightly till up to x = 0.01 and then decrease with further increase in x. Based on the Dexter’s theory and the Eu-Eu distances in K3LuSi2O7:Eu2+34, energy transfer among the nearest neighbor ions accounts for the observed concentration quenching (see details in Supplementary Fig. 8a). The internal quantum efficiency of selected K3LuSi2O7:0.01Eu2+ is measured to be about 15% (λex = 460 nm). Furthermore, one can find that the normalized emission peaks of K3LuSi2O7:xEu2+ show no shift as Eu2+ doping content increase (Supplementary Fig. 8b).
Mechanism of NIR emission in K3LuSi2O7:Eu2+
First of all, we need to correlate the Eu2+ site contribution and different emission center by considering local environments of activators. The Eu2+ emission is dependent on the CFS. In general, when the average bond length (dav) is shorter and the distortion indices (D) is larger, then there will be a larger CFS35. The average bond lengths, d(Lu-O) and d(K2-O) in K3LuSi2O7 are 2.22 Å and 2.77 Å, respectively. The distortion indices are 0 for both LuO6 and K2O6 polyhedron. Thus, we believe that the higher energy emission (719 nm) peak is associated with Eu2+ occupying K2 sites, while the lower energy emission (784 nm) peak is attributed to Eu2+ occupying Lu sites. The conclusions of the site occupation for Eu2+ in K3LuSi2O7 are consistent with the results in Rb3YSi2O7:Eu2+ phosphor reported by our group31.
It is well-known that the free Eu2+ ions possess a large energy gap (4.2 eV) between the 5d excited state and the 4 f ground state36. Once Eu2+ are introduced into a given compound, the resulting emission wavelengths are affected by centroid shift, crystal splitting, and Stokes shift effects37. For K3LuSi2O7:Eu2+ phosphor, the centroid shift and Stokes shift have weak effect on the redshift because of the low covalence between Eu2+ and O2− ions and the highly symmetric LuO6 and K2O6 polyhedrons, respectively38,39. The CFS depends especially on the coordination numbers, distortion index and size of the polyhedrons28. The substitution of Eu2+ ions in LuO6 and K2O6 polyhedrons, and thus a design principle of selective occupation of Eu2+ at small coordination numbers takes effect. It results in large CFS, which in turn leads to a large redshift. A comparison of the local environment of Eu2+ ions in K3LuSi2O7 and Rb3YSi2O7 benefits further understanding of the abnormal NIR emission in K3LuSi2O7. Firstly, they are isomorphic, and Eu2+ ions occupy the same crystallographic lattices in both materials, and the distortion index of YO6/LuO6 and K2O6 polyhedron are all 031. Thus, the effect of polyhedral distortion on the NIR emission can be neglected. Secondly, the dav values of Lu-O and K2-O in K3LuSi2O7 are 2.22 Å and 2.77 Å, respectively, which are much smaller than that of Y-O and K2-O (2.29 Å and 2.86 Å) in Rb3YSi2O7, resulting in a larger CFS in 5d energy levels and a larger redshift40. Therefore, the NIR light emission (740 nm) in K3LuSi2O7:Eu2+ is reasonable compared with the red emission (622 nm) in Rb3YSi2O7:Eu2+. In summary, the selective occupation of Eu2+ ions in polyhedrons with small coordination numbers and small average bond length contribute to the NIR emission and the broad excitation band in K3LuSi2O7:Eu2+.
Thermal quenching of PL
Normally, the thermal effect of the NIR phosphor is crucial for the LED application, and thus the thermal quenching behavior of K3LuSi2O7:Eu2+ was investigated at different temperature from 80 to 500 K. Figure 3a demonstrates that the emission intensity decreases slowly with the increase of temperature owing to the enhanced nonradiative transition probabilities. As given in Fig. 3b, the integrated intensity at 150 °C retains ~59% of that at room-temperature. According to Dorenbos’s model, the activation energy ∆E was calculated by using the following empirical formula:40,41
where T0.5 denotes the quenching temperature, and it is defined as the temperature when the emission declines to half of its initial intensity. Here, ∆E is calculated to be ~0.65 eV.
Thermal quenching properties of K3LuSi2O7:Eu2+ phosphor. a PL spectra and b normalized emission intensities of K3LuSi2O7:0.01Eu2+ as a function of temperature in 300–500 K under 460 nm excitation. c Normalized temperature-dependent PL spectra in 80–500 K at intervals of 60 K. d Schematic energy level diagram of Eu2+ in K3LuSi2O7. εc(A) denotes the centroid shift of 5d-levels of Eu2+, εcfs(A) shows the CFS effect in connection with coordination number of cations and polyhedrons’ size, ΔEA represents the photoionization barrier
One can find from Fig. 3a that the emission peaks shift to shorter wavelength (blueshift) at evaluated temperature from 300 to 500 K. Furthermore, the temperature-dependent PL spectra under excitation of 460 nm of K3LuSi2O7:0.01Eu2+ were measured from 80 to 500 K, and the normalized spectra are presented in Fig. 3c. The emission peaks demonstrate a remarkable blueshift from 790 nm (80 K) to 710 nm (500 K) with increasing temperature, and the FWHM of emission bands gradually broadens with the increase of temperature. These observations are associated with the different response of Eu2+ ions located at the Lu and K2 sites to the temperature. In addition, the emission peaks at high temperature (790 nm) and low temperature (710 nm) are close to the two Gaussian fitted peaks at room temperature (784 nm, 719 nm) in Fig. 2c. This further validates the feasibility of the previous analysis about the site occupation of Eu2+ ions.
Thus, a simple schematic Eu2+ energy level diagram in K3LuSi2O7 host is depicted in Fig. 3d. Based on the thermal ionization model proposed by Dorenbos, the smaller the gap (photoionization barrier ΔEA) between the bottom of conduction band and the upper edge of 5d energy level, the greater is the thermal quenching40. In K3LuSi2O7:Eu2+, the larger CFS of Eu2+ occupied in Lu site produces a smaller ΔEA, and thus a poor thermal stability compared with Eu2+ in the K2 site (Fig. 3d). Similarly, the larger CFS of Eu2+ in K3LuSi2O7 results in a smaller ΔEA, and thus it enables a poor thermal stability compared with that of Rb3YSi2O7:Eu2+31. Therefore, the blueshift occurred when heated. At low temperature of 80 K, the thermal ionization of 5d electrons becomes weak, and the dominant emission peak centers at longer wavelength (790 nm) associated with the more contribution from Eu2+ ions occupying Lu sites. In contrast, thermal quenching behavior at high temperatures has a much weaker effect on the Eu2+ ions in K2 sites than on the Eu2+ ions in Lu sites, resulting in a relatively stronger emission at short wavelength. Therefore, with temperature increasing, the blueshift and the broadening of emission spectra occur simultaneously.
NIR pc-LED device and applications
A pc-LED with NIR emission was fabricated by combining K3LuSi2O7:Eu2+ phosphor and the commercial blue light-emitting InGaN chip (460 nm). The emission spectrum of the lighted lamp was monitored by a visible-NIR continuous fiber spectrophotometer. The broad-band PL spectrum and the as-obtained and lighted NIR pc-LED lamps are given in Fig. 4a. The slight spectral deviation from the lamp and the powder is related with the calibration difference of the used spectrometers. Figure 4b demonstrates the PL spectra of LED device upon different forward bias currents (20–120 mA). The NIR emission output power increase with the increase of forward currents and reaches 21.5 mW when the forward current is 100 mA (Supplementary Table 6). Figure 4c shows the photographs obtained by different cameras under natural light and NIR pc-LED light, respectively. Nothing can be detected by NIR camera once the NIR pc-LED is off. In contrast, the NIR camera can capture black-and-white images while the NIR pc-LED lamp is lighted. These results indicate the application of the K3LuSi2O7:Eu2+ phosphor in night-vision technologies, and other potential fields including medical and food industries can be also expected for such NIR phosphors.
NIR application of K3LuSi2O7:Eu based pc-LEDs. a Photographs and PL spectrum of as-fabricated pc-LED combining a commercial blue LED and K3LuSi2O7:0.01Eu2+ phosphor. b PL spectra of the pc-LED upon various forward bias currents. c Photographs under natural light and NIR pc-LED light captured by the corresponding visible camera and a NIR camera
Discussion
To conclude, we have designed and successfully synthesized the Eu2+-activated broad-band-emitting NIR phosphor with super-broad excitation band from 250 to 600 nm. Under 460 nm blue light excitation, K3LuSi2O7:Eu2+ shows an unprecedented broad NIR emission band peaking at 740 nm and also demonstrates a high FHWM of 160 nm. Eu2+ selectively occupancy at Lu and K2 sites, and the small coordination numbers and small average bond lengths lead to the as-observed NIR emission with characteristic 4f-5d transition of Eu2+. The as-fabricated NIR pc-LEDs based on K3LuSi2O7:Eu2+ phosphors have been applied in night-vision devices and demonstrated potential applications. This finding gives the feasibility of the feasible strategy to discover Eu2+ doped NIR phosphor with large redshift by occupying polyhedrons with small coordination numbers. More importantly, it initiates a new way to explore NIR phosphors, i.e. achieve NIR emission by Eu2+ doping in the solid-state materials.
Methods
Materials and synthesis of the NIR phosphor
K3LuSi2O7:xEu2+ phosphors with different Eu2+ content (x = 0–0.05) were prepared by employing solid-state reactions. The stoichiometric mixtures of K2CO3 (A.R.), Lu2O3 (99.99%), SiO2 (A.R.), and Eu2O3 (99.99%) were thoroughly grounded and transferred into an alumina crucible. After that, the mixed starting materials were sintered at 1350 °C for 6 h in a forming gas atmosphere (N2:H2 = 80:20), and finally quenched to room temperature. As a typical synthesis, 3.8 g raw materials (K2CO3, Lu2O3, SiO2, and Eu2O3) in the given stoichiometric ratio can produce ~2.3 g products.
Characterization
A D8 Advance X-ray diffractometer (XRD, Bruker Corporation, Germany) was used to collect the XRD patterns, and the operation voltage and current were set as 40 kV and 40 mA, respectively. Structural characterization and Rietveld refinement were conducted using TOPAS 4.2 software42. Diffuse reflectance spectra were collected using a Hitachi UH4150 ultraviolet-visible-near infrared spectrophotometer. Photoluminescence emission and excitation spectra were measured by a FLSP920 fluorescence spectrophotometer, and both visible and NIR PMT detectors were applied. PL spectra of K3LuSi2O7:Eu2+ and as-fabricated NIR pc-LED were comparatively measured by a fiber spectrophotometer (NOVA high sensitive spectrometer, idea optics, China), and the 375-nm and 450-nm laser diode acted as the excitation source. The temperature-dependent spectra were evaluated by a FLS920 spectrophotometer equipped with a MercuryiTc temperature control instrument (OXFORD). Liquid nitrogen was used to cool temperature. The decay time was measured by a FLS920 instrument equipped with 450 nm and 340 nm pulse laser diode. The statistical photons are 5000 and 10,000, respectively, for the measurements at low temperature (80 K) and room temperature (300 K), and the decay curvers were fitted by the FAST software attached with FLS920 spectrophotometer. All the photophysics properties measurements were repeated at least three times to confirm the data. The quantum efficiency was measured using a Hamamatsu absolute photoluminescence quantum yield spectrometer C11347 Quantaurus-QY. The photoelectric properties and emission spectra of the fabricated pc-LEDs were measured by a Morpho 3.2 software equipped with a NOVA Laboratory Class Spectrometer. Photographs for the application of NIR pc-LEDs are taken by a NIR and a visible camera.
Data availability
The data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request.
References
Ly, K. T. et al. Near-infrared organic light-emitting diodes with very high external quantum efficiency and radiance. Nat. Photon. 11, 63–68 (2016).
Eggebrecht, A. T. et al. Mapping distributed brain function and networks with diffuse optical tomography. Nat. Photon. 8, 448–454 (2014).
Zeng, B. et al. Hybrid graphene metasurfaces for high-speed mid-infrared light modulation and single-pixel imaging. Light Sci. Appl. 7, 51 (2018).
Osborne, B. G. Encyclopedia of Analytical Chemistry: Applications, Theory and Instrumentation (John Wiley & Sons, Ltd., New York, 2006).
Tessler, N., Medvedev, V., Kazes, M., Kan, S. & Banin, U. Efficient near-infrared polymer nanocrystal light-emitting diodes. Science 295, 1506–1508 (2002).
Tan, Z. K. et al. Bright light-emitting diodes based on organometal halide perovskite. Nat. Nanotechnol. 9, 687–692 (2014).
Gong, X. et al. Highly efficient quantum dot near-infrared light-emitting diodes. Nat. Photon. 10, 253–257 (2016).
Lukovic, M. et al. LED-based Vis-NIR spectrally tunable light source - the optimization algorithm. J. Eur. Opt. Soc. -Rapid Publ. 12, 19 (2016).
Zhao, M. et al. Next-generation narrow-band green-emitting RbLi(Li3SiO4)2:Eu2+ phosphor for backlight display application. Adv. Mater. 30, e1802489 (2018).
Xia, Z. & Liu, Q. Progress in discovery and structural design of color conversion phosphors for LEDs. Prog. Mater. Sci. 84, 59–117 (2016).
Wang, Z. et al. Mining unexplored chemistries for phosphors for high-color-quality white-light-emitting diodes. Joule 2, 914–926 (2018).
Qiao, J. et al. Eu2+ site preferences in the mixed cation K2BaCa(PO4)2 and thermally stable luminescence. J. Am. Chem. Soc. 140, 9730–9736 (2018).
Chen, J. et al. Li2SrSiO4:Ce3+, Pr3+ phosphor with blue, red, and near-infrared emissions used for plant growth LED. J. Am. Ceram. Soc. 99, 218–225 (2016).
Damasco, J. A. et al. Size-tunable and monodisperse Tm3+/Gd3+-doped hexagonal NaYbF4 nanoparticles with engineered efficient near infrared-to-near infrared upconversion for in vivo imaging. ACS Appl. Mater. Interfaces 6, 13884–13893 (2014).
Benayas, A. et al. Nd:YAG near-infrared luminescent nanothermometers. Adv. Opt. Mater. 3, 687–694 (2015).
Nyk, M., Kumar, R., Ohulchanskyy, T. Y., Bergey, E. J. & Prasad, P. N. High contrast in vitro and in vivo photoluminescence bioimaging using near infrared to near infrared up-conversion in Tm3+ and Yb3+ doped fluoride nanophosphors. Nano Lett. 8, 3834–3838 (2008).
Liu, F., Liang, Y., Chen, Y. & Pan, Z. Divalent nickel-activated gallate-based persistent phosphors in the short-wave infrared. Adv. Opt. Mater. 4, 562–566 (2016).
Du, J., De Clercq, O. Q., Korthout, K. & Poelman, D. LaAlO3:Mn4+ as near-infrared emitting persistent luminescence phosphor for medical imaging: a charge compensation study. Materials 10, 1422 (2017).
Zhang, L. et al. Cr3+‐doped broadband NIR garnet phosphor with enhanced luminescence and its application in NIR spectroscopy. Adv. Opt. Mater. 7, 1900185 (2019).
Feng, G. et al. Transparent Ni2+-doped lithium aluminosilicate glass–ceramics with broadband infrared luminescence. J. Alloy. Compd 457, 506–509 (2008).
Rajendran, V. et al. Super broadband near-infrared phosphors with high radiant flux as future light sources for spectroscopy applications. ACS Energy Lett. 3, 2679–2684 (2018).
Zhang, L. et al. A high efficiency broad-band near-infrared Ca2LuZr2Al3O12:Cr3+ garnet phosphor for blue LED chips. J. Mater. Chem. C 6, 4967–4976 (2018).
Zabiliute, A., Butkute, S., Zukauskas, A., Vitta, P. & Kareiva, A. Sol-gel synthesized far-red chromium-doped garnet phosphors for phosphor-conversion light-emitting diodes that meet the photomorphogenetic needs of plants. Appl. Opt. 53, 907–914 (2014).
Gao, G., Reibstein, S., Spiecker, E., Peng, M. & Wondraczek, L. Broadband NIR photoluminescence from Ni2+-doped nanocrystalline Ba–Al titanate glass ceramics. J. Mater. Chem. 22, 2582–2588 (2012).
Kim, K. B. et al. Structural and optical properties of BaMgAl10O17:Eu2+ phosphor. Chem. Mater. 14, 5045–5052 (2002).
Hirosaki, N. et al. Characterization and properties of green-emitting β-SiAlON:Eu2+ powder phosphors for white light-emitting diodes. Appl. Phys. Lett. 86, 211905 (2005).
Pust, P. et al. Narrow-band red-emitting Sr[LiAl3N4]:Eu2+ as a next-generation LED-phosphor material. Nat. Mater. 13, 891–896 (2014).
Berezovskaya, I. V., Dotsenko, V. P., Voloshinovskii, A. S. & Smola, S. S. Near infrared emission of Eu2+ ions in Ca3Sc2Si3O12. Chem. Phys. Lett. 585, 11–14 (2013).
Wang, L., Xie, R. J., Suehiro, T., Takeda, T. & Hirosaki, N. Down-conversion nitride materials for solid state lighting: recent advances and perspectives. Chem. Rev. 118, 1951–2009 (2018).
Xia, Z. et al. Chemical unit cosubstitution and tuning of photoluminescence in the Ca2(Al1−xMgx)(Al1−xSi1+x)O7:Eu2+ phosphor. J. Am. Chem. Soc. 137, 12494–12497 (2015).
Qiao, J. et al. Site-selective occupancy of Eu2+ toward blue-light-excited red emission in a Rb3YSi2O7:Eu phosphor. Angew. Chem. Int. Ed. 58, 11521–11526 (2019).
Shannon, R. D. Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides. Acta Cryst. Sect. A 32, 751–767 (1976).
Vidican, I., Smith, M. D. & zur Loye, H. C. Crystal growth, structure determination, and optical properties of new potassium-rare-earth silicates K3RESi2O7 (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu). J. Solid State Chem. 170, 203–210 (2003).
Dexter, D. L. A theory of sensitized luminescence in solids. J. Chem. Phys. 21, 836–850 (1953).
Denault, K. A. et al. Consequences of optimal bond valence on structural rigidity and improved luminescence properties in SrxBa2–xSiO4:Eu2+ orthosilicate phosphors. Chem. Mater. 26, 2275–2282 (2014).
Dorenbos, P. Relation between Eu2+ and Ce3+ f ↔ d-transition energies in inorganic compounds. J. Phys. Condens. Matter 15, 4797 (2003).
Dorenbos, P. 5d-level energies of Ce3+ and the crystalline environment. IV. Aluminates and “simple” oxides. J. Lumin. 99, 283–299 (2002).
DiSalvo, F. J. & Clarke, S. J. Ternary nitrides: a rapidly growing class of new materials. Curr. Opin. Solid State Mater. Sci. 1, 241–249 (1996).
Lim, M. A., Park, J. K., Kim, C. H., Park, H. D. & Han, M. W. Luminescence characteristics of green light emitting Ba2SiO4:Eu2+ phosphor. J. Mater. Sci. Lett. 22, 1351–1353 (2003).
Dorenbos, P. Thermal quenching of Eu2+ 5d–4f luminescence in inorganic compounds. J. Phys. Condens. Matter 17, 8103 (2005).
Qiao, J. et al. Engineering of K3YSi2O7 to tune photoluminescence with selected activators and site occupancy. Chem. Mater. 31, 7770–7778 (2019).
Topas, V. 1: General profile and structure analysis software for powder diffraction data (Bruker AXS, Karlsruhe, Germany, 2008).
Acknowledgements
This work is supported by the National Natural Science Foundation of China (Nos.: 51722202 and 51972118), Fundamental Research Funds for the Central Universities (D2190980), and the Guangdong Provincial Science & Technology Project (2018A050506004).
Author information
Authors and Affiliations
Contributions
Z.X. initiated and guided the research. J.Q. synthesized the samples and wrote the manuscript, and Z.X. and Q.Z. revised it. G.Z. and Y.Z. discussed the luminescence properties and made the NIR pc-LED device. All authors discussed the results and commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Eszter Borbas and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International cLicense, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Qiao, J., Zhou, G., Zhou, Y. et al. Divalent europium-doped near-infrared-emitting phosphor for light-emitting diodes. Nat Commun 10, 5267 (2019). https://doi.org/10.1038/s41467-019-13293-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-019-13293-0
- Springer Nature Limited
This article is cited by
-
Laser-driven broadband near-infrared light source with watt-level output
Nature Photonics (2024)
-
Rapid synthesis of phosphor-glass composites in seconds based on particle self-stabilization
Nature Communications (2024)
-
Electrical stimulation for brighter persistent luminescence
Light: Science & Applications (2024)
-
Ceramic phosphor creates broadband infrared source
Nature Photonics (2024)
-
LaMg6Ga6S16: a chemical stable divalent lanthanide chalcogenide
Nature Communications (2024)