Abstract
Multicomponent chalcogenides, such as quasi-binary GeTe–Sb2Te3 alloys, are widely used in optical data storage media in the form of rewritable optical discs. Ge2Sb2Te5 (GST) in particular has proven to be one of the best-performing materials, whose reliability allows more than 106 write–erase cycles. Despite these industrial applications, the fundamental kinetics of rapid phase change in GST remain controversial, and active debate continues over the ultimate speed limit. Here we explore ultrafast structural transformation in a photoexcited GST superlattice, where GeTe and Sb2Te3 are spatially separated, using coherent phonon spectroscopy with pump–pump–probe sequences. By analysing the coherent phonon spectra in different time regions, complex structural dynamics upon excitation are observed in the GST superlattice (but not in GST alloys), which can be described as the mixing of Ge sites from two different coordination environments. Our results suggest the possible applicability of GST superlattices for ultrafast switching devices.
Similar content being viewed by others
Introduction
The rapid phase change in Ge2Sb2Te5 (GST) materials involved in the writing (from crystalline to amorphous) and erasing (from amorphous to crystalline) of data in optical recording media is induced by irradiation with focused nanosecond laser pulses, leading to melt-quenching (amorphization) and annealing (crystallization), respectively1,2,3. The same concept has been applied to electrical memory with electrical pulses replacing optical pulses and resistance differences replacing reflectivity changes4. Thus, the conventional understanding of the dynamics of rapid phase change in optical recording media using GST materials is based on a thermal process, limiting the speed of the write–erase cycle to the nanosecond range1,2. In electronic memories, the terms SET and RESET phases are used to describe the two structural phases4,5. By analogy, we use the same terminology here, although it is not commonly used with respect to optical memory. SET refers to the local structure in the crystalline phase of GST, typically characterized by resonantly bonded atoms with three shorter and three longer bonds, also referred to as octahedrally coordinated6,7 when differences in the bond lengths are neglected, and RESET refers to the covalently bonded amorphous phase, described as having tetrahedral8, defective octahedral9 or pyramidal10 Ge sites. The microscopic mechanism of rapid phase change in GST has been examined using optical absorption11, Raman scattering and X-ray absorption fine-structure (XAFS) measurements8, as well as density functional theory-based ab initio molecular dynamics simulations3,12,13.
Interfacial phase-change memory (iPCM) consists of a superlattice (SL) structure formed from alternating layers of GeTe and Sb2Te3 (refs 7, 14). iPCM was designed to utilize a solid–solid phase transformation between the covalently bonded (RESET) and resonantly bonded (SET) phases, induced predominantly by the displacement of Ge atoms at the interface, to achieve both faster and lower power threshold switching than in conventional GST alloys7. iPCM structures with certain thicknesses and atomic order in the individual blocks were also argued to be topological insulators, and recently, it was reported that iPCM could be switched between the Dirac-semimetal and gapped phases15, an effect that has the potential to lead to novel spin memory devices and also as a platform to study the topological properties of SLs.
Non-thermal phase transitions (electronic excitation-induced phase transitions16,17) induced via strong photoexcitation by femtosecond laser pulses with sub-picosecond time resolution have been reported for a wide variety of materials including semiconductors16, manganites18 and insulators19. Recently, the possibility of non-thermal phase change has been theoretically13,17 and experimentally20,21 proposed for GST alloys. In an important step, Fons et al.21 reported based on time-resolved XAFS measurements that non-thermal optically induced contributions to the amorphization in GST alloy may be present on sub-nanosecond timescales. As a further step, using weak femtosecond laser pulses with pump fluences below 100 μJ cm−2, Makino et al.22 demonstrated that for a prototypical iPCM structure, [Ge2Te2/Sb2Te3]20, a phase change from the RESET into the SET phase could be induced by selectively exciting a phonon mode that involves Ge atoms using a double-pulse excitation. Despite recent activity investigating non-thermal phase transitions in GST alloys and iPCM, the mechanism of the non-thermal phase transformation remains largely unknown, especially at sub-picosecond timescales under strong photoexcitation.
In the following, we report on systematic studies of the structural dynamics in a prototypical iPCM structure, [Ge2Te2/Sb2Te3]20, using coherent phonon spectroscopy (CPS) under strong photoexcitation employing both single- and double-pump-pulse excitation. In the SET phase of iPCM, we observe marked differences between the pre-transitional dynamics induced by single- and double-pulse excitation. Under single-pulse excitation, only phonon softening is observed for an optical phonon mode involving Ge–Te bonds. In contrast, under double-pulse excitation the optical phonon frequency exhibits an unexpected blue shift (hardening), accompanied by the appearance of an additional peak in the coherent phonon spectra when the interval between the two pump-pulses is shorter than a few picoseconds and exceeds a critical total pump fluence. Furthermore, we find that the structural change dynamics in the photoexcited SET phase of iPCM are reversible, while those in the RESET phase of iPCM are irreversible. A metastable pre-phase transformation state with characteristic coherent phonon spectra in the SET phase of iPCM at ultrafast timescales suggests the presence of two different coordination environments around Ge atoms. Exploration of the non-thermal pre-phase transformations in GST materials will enable a deeper understanding of the local lattice structure far from equilibrium, and will potentially make it possible to increase the speed limit of switching in the phase-change process beyond the current limit of nanoseconds down to sub-picosecond timescales.
Results
Transient reflectivity studies of the SET phase of iPCM
Figure 1a depicts a schematic view of the pump–pump–probe experiment22,23. To explore the coherent phonon spectra under non-equilibrium conditions prepared by photoexcitation (Fig. 1b), a stronger initial prepump-pulse (P1=10.6 mJ cm−2) promotes the sample into the excited state, followed by the generation of a coherent phonon in the excited state by another weaker pump (P2=6.9 mJ cm−2), which is monitored by a probe pulse (P3=0.2 mJ cm−2). The weaker pump (P2) acts as a control pulse to coherently launch the vibrational amplitude beyond the threshold of transient local phase change around the Ge atoms22; use of a P2 pulse fluence less than 2.0 mJ cm−2 does not induce phonon hardening (Supplementary Fig. 1). The choice of fluences P1=10.6 mJ cm−2 and P2=6.9 mJ cm−2 was made because of the low-limit threshold for the observation of phonon hardening in iPCM as discussed below and also to allow for matching the phonon amplitude resulting from the initial excitation at the time delay τ=0 fs with the phonon amplitude induced by the second excitation pulse at the separation time (Δt) of Δt=290–870 fs (see Methods). The time delay (τ) between the second pump and the probe pulse was scanned over the full range of the signal, for a variety of separation times (Δt) between P1 and P2 pulses.
Figure 2a shows the transient reflectivity (ΔR/R) observed in the SET phase of an iPCM film without prepump-pulse (P1) excitation (see the bottom trace) and five major traces observed for P1 excitations at different Δt. One can notice that the coherent phonon oscillations in the excited state, highlighted by the rectangular light-blue region, change markedly as the value of Δt is varied; in particular, at Δt=290–870 fs, the coherent phonon after the arrival of the P2 pulse exhibits a strongly damped oscillation. To compare the ΔR/R signal observed in iPCM under irradiation with double pump-pulses with that occurring for irradiation with a single pump-pulse, Fig. 2b presents the transient reflectivity detected in the SET phase of an iPCM film by irradiation with a single P2 pulse at different pump fluences. The coherent phonon oscillations exhibited an increase in amplitude with moderate damping of the phonon oscillation when the P2 pulse fluence was increased up to 18.6 mJ cm−2. To explore the phonon dynamics in the frequency domain, coherent oscillations occurring only after the arrival of the P2 pulse, that is, the time region highlighted by the rectangular light-blue region in Fig. 2a (the entire region for the case of a single P2 pulse in Fig. 2b), were Fourier transformed (FT)24.
Without the P1 excitation, the frequency of the coherent phonon was ΩSET=3.48 THz (see Fig. 3a), and was slightly red-shifted from the literature value22,25, but remained consistent with the optical mode due to the local Ge–Te bonds of the resonantly bonded structure22,25. Similar phonon softening induced by single pump excitation has also been observed in conventional GST alloy films26. The choice of the value of Δt is based on the period of the coherent phonon observed without prepump-pulse excitation; 3.48 THz corresponds to ≈290 fs and therefore multiples of 290 fs were used to excite the SET phase to coherently drive the vibrational amplitude beyond the threshold of transient structural change22,27,28,29 by the P2 pulse. As shown in Fig. 3b, at Δt=290 fs the original peak at 3.48 THz unexpectedly splits into two peaks, one ‘blue-shifts’ to 3.70 THz and an additional peak at 2.55 THz (labelled by ★) appears. The lower-frequency peak position shifts to higher frequency with increasing separation time Δt and gradually disappears after Δt=1,740 fs. By contrast, the peak at 3.70 THz observed in the excited state is very close to the frequency of the RESET phase (ΩRESET=3.74 THz; see Supplementary Fig. 2) and gradually red-shifts to 3.57 THz at Δt=1,740 fs. After the aforementioned pump–pump–probe experiment for Δt=6,090 fs, the coherent phonon spectra were taken at the same sample position without the prepump-pulse (P1), confirming that the excited state reverts to the original SET phase as the peak frequency is observed at the original frequency of 3.48 THz (Fig. 3c). Thus, the structural change observed in the photoexcited SET phase is reversible, but the excited crystal lattice exhibits a characteristic double-peak FT spectra on ultrafast timescales from Δt=290 to 1,160 fs.
For the case of single-pulse excitation, different pre-transitional dynamics are observed as shown in Fig. 3d. The FT spectra obtained from the time-domain data in Fig. 2b exhibit a peak frequency for the optical mode due to the Ge–Te bonds at 3.52 THz for the single pump fluence of 5.3 mJ cm−2, while at 18.6 mJ cm−2 it red-shifts to 3.27 THz with a concomitant broadening of the peak structure. However, there is no frequency blue shift of the optical mode for the case of single-P2-pulse excitation, even if the single P2 pump fluence exceeds the total fluence of the double pump-pulses (17.5 mJ cm−2 in Fig. 3b). This result indicates that the transient state characterized by the double-peak FT spectra is induced only by the coherent action of the optical phonon by virtue of the double pump-pulses.
Fluence dependence for the SET phase of iPCM
To check whether there is a threshold for the observation of the double-peak FT spectra in the SET phase of iPCM, we present the fluence dependence of a pump–pump–probe experiment for Δt=290 fs for a fixed fluence ratio of P1 and P2 pulses (Fig. 4a). At the lowest fluence of P1=5.3 mJ cm−2 and P2=3.5 mJ cm−2 (8.8 mJ cm−2 in total), only a single phonon peak at ≈3.43 THz was observed (Fig. 4b), which is the same peak position as that observed with only P2 pulse excitation at 10.6 mJ cm−2 (see the bottom trace of Fig. 4b). On the contrary, for fluences higher than P1=10.6 mJ cm−2 and P2=6.9 mJ cm−2, the double-peak FT spectra emerge accompanied by a blue shift of the original peak. Thus, the choice of fluences P1=10.6 mJ cm−2 and P2=6.9 mJ cm−2 was made because of the lower threshold limit for the observation of the double-peak FT spectral feature in iPCM. As mentioned earlier, irradiation of the SET phase by a single P2 pulse without P1 irradiation cannot induce a transition into the transient double-peak coherent phonon spectra even if its fluence (P2=18.6 mJ cm−2 in Fig. 3d) exceeds the combined fluence of a P1 and P2 pair above the threshold, the total fluence of P1 (10.6 mJ cm−2)+P2 (6.9 mJ cm−2)=17.5 mJ cm−2 in Fig. 4. This finding demonstrates that the threshold for the appearance of the transient state is substantially decreased by irradiation with double pump-pulses or in all likelihood only double-pulse excitation can provide access to the transient state. It is also noted that the required pump fluence used here (10–20 mJ cm−2) is significantly lower than those used in the experiments using picosecond or nanosecond laser pulses, in which a fluence of 30–60 mJ cm−2 for a 30-ps single pulse30 or a fluence of ≈150 mJ cm−2 for a 8-ns single pulse was applied31.
Transient reflectivity studies of other phases
In contrast to the pre-transitional dynamics in the SET phase of iPCM, the phase transformation from the RESET phase of the iPCM was irreversible (Supplementary Note 1; Supplementary Figs 2–4). The carrier response suggests that the metastable state after irradiation of the RESET phase of iPCM by the P1 pulse is different from that of the so-called laser-crystallized structure26 (Supplementary Note 2; Supplementary Fig. 4), which should show a much different carrier response from the original phase. Note also that for the case of the polycrystalline (SET phase) GST alloy, no frequency blue shift (phonon hardening) was observed in the excited state under double-pump-pulse excitation, but only broadening and a red shift of the optical phonon mode was observed on the timescale of a few picoseconds (Supplementary Note 3; Supplementary Fig. 5). Since photoexcited carriers in semiconductors relax via carrier-phonon scattering (intraband relaxation) and trapping by defects in a few picoseconds32 (Supplementary Fig. 1), the observed frequency red shift is interpreted to be the result of phonon softening induced by electronic excitation26. From the fact that for the polycrystalline GST alloy no frequency blue shift of the optical phonon was observed, it is concluded that the transient state cannot be accessed by the present double-pulse excitation.
Discussion
To discuss the pathways of pre-transitional structural dynamics observed in the excited state, we consider the transient structure of iPCM in terms of its bonding nature7,33. Given that [Ge2Te2/Sb2Te3]20 iPCM sample has the same average composition as Ge2Sb2Te5 (refs 7, 14), we refer to a recent theoretical study based on an ab initio molecular dynamics simulation by Li et al.13, who reported that the phase transformation from the crystalline (SET) to amorphous (RESET) phase in GST alloy occurred over several picoseconds under optical excitation. The authors also claimed that the coordination number of Ge atoms changed from the original sixfold into a mixture of fivefold and fourfold coordination within 450 fs after the removal of 9% of the valence electrons in a GST alloy, followed by the further appearance of threefold coordination at 3 ps. On the other hand, Simpson et al.7 reported for the iPCM system, the presence of a lower coordination for Ge atoms, namely the possibility of fourfold or threefold coordination. These studies suggest that in the early stages of the non-thermal pre-phase transformation from the SET to RESET phases under repetitive photoexcitation by double pump-pulses, the bonding coordination around Ge atoms in the iPCM system is coherently modulated and becomes unstable giving rise to two different coordination environments (possibly fourfold and threefold7), providing a plausible explanation as to why a double-peak spectral feature develops for the earlier time intervals of Δt=290–1,160 fs in Fig. 3b. In contrast to the case of strong photoexcitation by a single pump-pulse, hot-carrier injection on ultrafast timescales of several femtoseconds is suppressed and concurrently similar conditions to a mode-selective vibrational excitation34 are established under double-pump-pulse excitation.
To conclude, we have experimentally explored the photoexcited state of GST phase-change materials, iPCM films, by comparison between the cases of single- and double-pulse excitation using pump–pump–probe femtosecond CPS far from equilibrium. A transient hidden phase characterized by double-peak FT spectra was uncovered for iPCM structures only when a double-pump-pulse sequence was applied, which is interpreted as being due to a mixture of two different Ge coordination environments, which relax within a few picoseconds. Our experimental results also demonstrate that the transition of the SET phase of iPCM to a hidden phase can be achieved with lower total energy using multiple pulse sequences than for the case of single-pulse excitation. These effects will provide a new route for faster and lower threshold phase switching with further testing of the iPCM SL structure. Thus, our finding of a non-thermal ultrafast pre-phase transformation in a iPCM film coupled with femtosecond multiple pulse sequences (Supplementary Fig. 6) or multiple terahertz light-pulse sequences35 will provide highly relevant fundamental knowledge for ultrafast optical data processing36 and for next-generation of ultra-high-speed phase-change random access memory (PCRAM).
Methods
Fabrication of GST SL (iPCM) films
Recently, Chong et al.5 proposed SL-like PCRAM considering the GST system as a composite of the pseudo-binary alloys, namely GeTe and Sb2Te3 alloys, with individual layers thick enough to maintain the characteristics of each composition. Both faster switching times (<5 ns) and lower programming currents were found for the SL-like PCRAM. More recently, motivated by the need to reduce both the switching speed and energy used, iPCM was proposed. Tominaga et al.14 reported the fabrication of a GST SL (iPCM) based on the Ge flip-flop transition mechanism. Using iPCM structures designed from GeTe and Sb2Te3 layers, a few unit cells thick, they experimentally confirmed very low (only 12% compared with GST alloy films7) power operation of phase switching (SET↔RESET) in iPCM. The sample used in this paper was a thin film (20 nm thick) of a prototypical iPCM sample, [Ge2Te2/Sb2Te3]20, which consisted of 20 repetitive sheet blocks from alternatively deposited 0.5-nm-thick GeTe and Sb2Te3 layers on a Si-(100) wafer using helicon-wave radio-frequency magnetron sputtering.
CPS using a pump–pump–probe sequence
CPS is a powerful tool to study the ultrafast dynamics of structural phase transitions occurring on ultrafast timescales. It has been applied to a wide variety of materials, such as semimetals and semiconductors22,25,28,37,38, and Mott insulators19. In CPS, a pump pulse impulsively generates Raman-active collective atomic vibrations through light–matter coupling. We utilized a 40-fs amplified near-infrared optical pulse (800 nm; 1.55 eV and 100 kHz repetition rate) to excite and monitor coherent lattice vibrations in iPCM films after injection of photocarriers across the indirect bandgap of 0.5–0.7 eV (ref. 11). The optical penetration depth at 800 nm was estimated from the absorption coefficient to be ∼20 nm, which matches the film thickness. The size of the probe beam after focusing was ∼50% smaller than the pump, providing for negligibly small inhomogeneous excitation effects. The maximum photogenerated carrier density was estimated to be nexc≈5.1 × 1021 cm−3, induced by a single pump pulse with 10.6 mJ cm−2, whose density corresponds to ≈2.9% of the total number density of valence electrons (ntot≈1.76 × 1023 cm−3)39. A train of two pump-pulses were generated through a Michelson-type interferometer, in which a motorized stage was installed under the mirrors to adjust the time interval (Δt) of the temporally separated pump-pulses. The ratio of the P1 and P2 pulses was set to 10:6.5 (i) to match the phonon amplitude of the initially excited phonon at τ=0 fs to that of the second excited phonon at separation times of Δt=290–870 fs as was used in the previous study28; in the present case, the amplitude of the phonon excited by a P1 pulse at τ=0 fs decays to ≈65–70% in amplitude when Δt=290–870 fs, and (ii) as it was characteristic of the 2-inch beam splitter with a p-polarized incident pump beam. The photoinduced reflectivity change (ΔR/R) was recorded as a function of the time delay (τ) between the pump and probe pulses. The delay was scanned over 10 ps and averaged for 1,000 scans using an oscillating retroreflector with a 10-Hz scan frequency.
Additional information
How to cite this article: Hase, M. et al. Femtosecond structural transformation of phase-change materials far from equilibrium monitored by coherent phonons. Nat. Commun. 6:8367 doi: 10.1038/ncomms9367 (2015).
References
Yamada, N., Ohno, E., Nishiuchi, K. & Akahira, N. Rapid phase transitions of GeTe-Sb2Te3 pseudobinary amorphous thin films for an optical disk memory. J. Appl. Phys. 69, 2849–2856 (1991).
Wuttig, M. & Yamada, N. Phase-change materials for rewritable data storage. Nat. Mater. 6, 824–832 (2007).
Hegedüs, J. & Elliott, S. R. Microscopic origin of the fast crystallization ability of Ge-Sb-Te phase-change memory materials. Nat. Mater. 7, 399–405 (2008).
Ovshinsky, S. R. Reversible electrical switching phenomena in disordered structures. Phys. Rev. Lett. 21, 1450–1453 (1968).
Chong, T. C. et al. Phase change random access memory cell with superlattice-like structure. Appl. Phys. Lett. 88, 122114 (2006).
Shportko, K. et al. Resonant bonding in crystalline phase-change materials. Nat. Mater. 7, 653–658 (2008).
Simpson, R. E. et al. Interfacial phase-change memory. Nat. Nanotechnol. 6, 501–505 (2011).
Kolobov, A. V. et al. Understanding the phase-change mechanism of rewritable optical media. Nat. Mater. 3, 703–708 (2004).
Caravati, S. et al. Coexistence of tetrahedral- and octahedral-like sites in amorphous phase change materials. Appl. Phys. Lett. 91, 171906 (2007).
Huang, B. & Robertson, J. Bonding origin of optical contrast in phase-change memory materials. Phys. Rev. B 81, 081204(R) (2010).
Lee, B.-S. et al. Investigation of the optical and electronic properties of Ge2Sb2Te5 phase change material in its amorphous, cubic, and hexagonal phases. J. Appl. Phys. 97, 093509 (2005).
Akola, J. & Jones, R. O. Structural phase transitions on the nanoscale: The crucial pattern in the phase-change materials Ge2Sb2Te5 and GeTe. Phys. Rev. B 76, 235201 (2007).
Li, Xian-Bin. et al. Role of electronic excitation in the amorphization of Ge-Sb-Te alloys. Phys. Rev. Lett. 107, 015501 (2011).
Tominaga, J. et al. What is the origin of activation energy in phase-change film? Jpn. J. Appl. Phys. 48, 03A053 (2009).
Tominaga, J., Kolobov, A. V., Fons, P., Nakano, T. & Murakami, S. Ferroelectric order control of the Dirac-semimetal phase in GeTe-Sb2Te3 superlattices. Adv. Mater. Interfaces 1, 1300027 (2014).
Sundaram, S. K. & Mazur, E. Inducing and probing non-thermal transitions in semiconductors using femtosecond laser pulses. Nat. Mater. 1, 217–224 (2002).
Kolobov, A. V. et al. Distortion-triggered loss of long-range order in solids with bonding energy hierarchy. Nat. Chem. 3, 311–316 (2011).
Polli, D. et al. Coherent orbital waves in the photo-induced insulator–metal dynamics of a magnetoresistive manganite. Nat. Mater. 6, 643–647 (2007).
Wall, S. et al. Ultrafast changes in lattice symmetry probed by coherent phonons. Nat. Commun. 3, 721 (2012).
Konishi, M. et al. Ultrafast amorphization in Ge10Sb2Te13 thin film induced by single femtosecond laser pulse. Appl. Opt. 49, 3470–3473 (2010).
Fons, P. et al. Photoassisted amorphization of the phase-change memory alloy Ge2Sb2Te5 . Phys. Rev. B 82, 041203(R) (2010).
Makino, K., Tominaga, J. & Hase, M. Ultrafast optical manipulation of atomic arrangements in chalcogenide glass memory materials. Opt. Exp. 19, 1260–1270 (2011).
Yusupov, R. et al. Coherent dynamics of macroscopic electronic order through a symmetry breaking transition. Nat. Phys. 6, 681–684 (2010).
Hase, M. et al. Forcibly driven coherent soft phonons in GeTe with intense THz-rate pump fields. Appl. Phys. Lett. 83, 4921–4923 (2003).
Först, M. et al. Phase change in Ge2Sb2Te5 films investigated by coherent phonon spectroscopy. Appl. Phys. Lett. 77, 1964–1966 (2000).
Hernandez-Rueda, J. et al. Coherent optical phonons in different phases of Ge2Sb2Te5 upon strong laser excitation. Appl. Phys. Lett. 98, 251906 (2011).
Dekorsy, T., Kütt, W., Pfeifer, T. & Kurz, H. Coherent control of LO phonon dynamics in opaque semiconductors by femtosecond laser pulses. Europhys. Lett. 23, 223–228 (1993).
Hase, M. et al. Optical control of coherent optical phonons in bismuth films. Appl. Phys. Lett. 69, 2474–2476 (1996).
Weiner, A. M., Leaird, D. E., Wiederrecht, G. P. & Nelson, K. A. Femtosecond pulse sequences used for optical manipulation of molecular motion. Science 247, 1317–1319 (1990).
Siegel, J., Schropp, A., Solis, J., Afonso, C. N. & Wuttig, M. Rewritable phase-change optical recording in Ge2Sb2Te5 films induced by picosecond laser pulses. Appl. Phys. Lett. 84, 2250–2252 (2004).
Siegel, J. et al. Amorphization dynamics of Ge2Sb2Te5 films upon nano- and femtosecond laser pulse irradiation. J. Appl. Phys. 103, 023516 (2008).
Zhang, G., Gan, F., Lysenko, S. & Liu, H. Observation of ultrafast carrier dynamics in amorphous Ge2Sb2Te5 films induced by femtosecond laser pulses. J. Appl. Phys. 101, 033127 (2007).
Kolobov, A. V., Fons, P., Tominaga, J. & Ovshinsky, S. R. Vacancy-mediated three-center four-electron bonds in GeTe-Sb2Te3 phase-change memory alloys. Phys. Rev. B 87, 165206 (2013).
Rini, M. et al. Control of the electronic phase of a manganite by mode-selective vibrational excitation. Nature 449, 72–74 (2007).
Kampfrath, T., Tanaka, K. & Nelson, K. A. Resonant and nonresonant control over matter and light by intense terahertz transients. Nat. Photonics 7, 680–690 (2013).
Mihailovic, D. et al. Femtosecond data storage, processing, and search using collective excitations of a macroscopic quantum state. Appl. Phys. Lett. 80, 871–873 (2002).
Cho, G. C., Kütt, W. & Kurz, H. Subpicosecond time-resolved coherent-phonon oscillations in GaAs. Phys. Rev. Lett. 65, 764–766 (1990).
Zeiger, H. J. et al. Theory for displacive excitation of coherent phonons. Phys. Rev. B 45, 768–778 (1992).
Steimer, C. et al. Characteristic ordering in liquid phase-change materials. Adv. Mater. 20, 4535–4540 (2008).
Acknowledgements
This work was supported by the X-ray Free Electron Laser Priority Strategy Program (Nos 12013011 and 12013023) from the Ministry of Education, Culture, Sports, Science and Technology of Japan), and by CREST, Japan Science and Technology Agency.
Author information
Authors and Affiliations
Contributions
M.H. and J.T. planned and organized this project. J.T. fabricated the sample. M.H. performed experiments and analysed the data. M.H., P.F., K.M., A.V.K. and J.T. discussed the results. M.H. and P.F. co-wrote the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-6, Supplementary Notes 1-3 and Supplementary References (PDF 1417 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Hase, M., Fons, P., Mitrofanov, K. et al. Femtosecond structural transformation of phase-change materials far from equilibrium monitored by coherent phonons. Nat Commun 6, 8367 (2015). https://doi.org/10.1038/ncomms9367
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms9367
- Springer Nature Limited
This article is cited by
-
Ultra-thin light-weight laser-induced-graphene (LIG) diffractive optics
Light: Science & Applications (2023)
-
Effect of crystallographic orientation on structural response of silicon to femtosecond laser irradiation
Applied Physics A (2021)
-
Coherent control of a surface structural phase transition
Nature (2020)
-
Phase-change like process through bond switching in distorted and resonantly bonded crystal
Scientific Reports (2019)
-
A cascading nonlinear magneto-optical effect in topological insulators
Scientific Reports (2018)