Abstract
Magnetite (Fe3O4) is an important magnetic mineral to Earth scientists, as it carries the dominant magnetic signature in rocks, and the understanding of its magnetic recording fidelity provides a critical tool in the field of palaeomagnetism. However, reliable interpretation of the recording fidelity of Fe3O4 particles is greatly diminished over time by progressive oxidation to less magnetic iron oxides, such as maghemite (γ-Fe2O3), with consequent alteration of remanent magnetization potentially having important geological significance. Here we use the complementary techniques of environmental transmission electron microscopy and off-axis electron holography to induce and visualize the effects of oxidation on the magnetization of individual nanoscale Fe3O4 particles as they transform towards γ-Fe2O3. Magnetic induction maps demonstrate a change in both strength and direction of remanent magnetization within Fe3O4 particles in the size range dominant in rocks, confirming that oxidation can modify the original stored magnetic information.
Similar content being viewed by others
Introduction
Magnetic minerals in rocks record the direction and intensity of the Earth’s ambient magnetic field during formation, providing, for example, information on past tectonic plate motion and the evolution of the geodynamo. In order to reliably interpret palaeomagnetic data, the mechanisms that induce and influence magnetic remanence within rocks must be fully understood. Some mechanisms such as thermoremanent magnetization are broadly understood1; however, the wide class of mechanisms that come under the heading of chemical remanent magnetization (CRM) requires more detailed study. Current models for CRM processes are, with one exception2, presently restricted to small, uniformly magnetized, single-domain (SD) grains3. Models for other types of chemical alterations are at best phenomenological4, and CRM processes in larger grains containing nonuniform magnetization states (that is, multidomain (MD) states) are little understood. Nevertheless, magnetic signals from rocks are often dominated by small MD grains that exhibit magnetic recording fidelities similar to those of SD grains (termed pseudo-SD (PSD)). For PSD grains, there are two key palaeomagnetic questions: does chemical alteration affect the directional record? To what extent does chemical alteration affect magnetization intensity?
Magnetite (Fe3O4) is probably the most important magnetic mineral on Earth because of its high abundance and strong, dominating magnetization. However, its ability to preserve the remanence of the Earth's magnetic field is greatly influenced by progressive oxidation, at ambient pressures and temperatures, to less magnetic iron oxides such as maghemite (γ-Fe2O3) or haematite (α-Fe2O3). Hence, oxidation of PSD Fe3O4 grains is a critical component of the CRM process and must be fully understood to allow for reliable interpretation of palaeomagnetic data.
Off-axis electron holography in the transmission electron microscope (TEM) allows nanometre-scale imaging of magnetic induction within and around materials as a function of applied field and temperature5,6,7,8,9. For example, Feinberg et al.10 used off-axis electron holography to show how the un-mixing of a titanomagnetite inclusion within a natural clinopyroxene matrix resulted in the development of an internal microstructure consisting of Fe3O4 prisms and ulvöspinel Fe2TiO4 lamellae, transforming it from an individual MD grain structure into an assemblage of magnetostatically interacting SD prisms. In particular, it was shown that the overall remanence direction was dependent on both the inclusion’s elongation direction and the prism arrangements therein10, thereby demonstrating the ability of chemical alterations to affect the magnetic remanence of natural magnetic recorders.
To fully appraise the effects of chemical alterations on CRM processes, it becomes necessary to investigate changes of magnetic domain structures in grains, directly, under controlled conditions. In this context, we present the application of a range of complementary electron microscopy techniques to examine local changes in the magnetization of PSD Fe3O4 grains, as they chemically alter during in situ heating within a controlled oxidizing atmosphere. The technique of environmental TEM (ETEM), combined with spherical aberration (CS) correction, enables localized chemical reactions under gas atmospheres to be observed with an interpretable spatial resolution on the sub-ångström scale11, while complementary electron energy-loss spectroscopy (EELS) investigations allow changes in material oxidation state to be appraised12. Off-axis electron holography enables nanometre-scale imaging of magnetic induction within and around magnetic grains, as a function of oxidation, through the generation of magnetic induction maps.
We show here the combined use of ETEM and off-axis electron holography to directly visualize the effect of oxidation on the recording fidelity of individual PSD Fe3O4 grains. Construction of magnetic induction maps demonstrates a change in both strength and direction of remanent magnetic states within the Fe3O4 grains, as a consequence of oxidation, and we discuss how it can lead to an underestimation of the ancient geomagnetic field strength and the geodynamo magnetic moment.
Results
Effect of oxidation on strength of magnetization
Figure 1 illustrates the effect of accelerated oxidation on the magnetization of an individual, equiaxed synthetic Fe3O4 grain, as assessed using TEM, selected area electron diffraction (SAED) and EELS, along with associated magnetic induction maps. The bright-field TEM image of Fig. 1a shows a native, smooth-surfaced, ~200 nm diameter Fe3O4 grain, as indicated by SAED (Fig. 1a, inset). EELS analysis of the Fe 2p L2,3 edge, in the region 704–726 eV (Fig. 1c), confirmed the assignment of pure Fe3O4. The L2 edge for this sample shows the typical shape of a mixed-valence compound, that is, three visible features of differing intensities (Fig. 1c, black arrows), while the almost-shapeless L3 edge is attributed to the combined spectral contributions of different iron sites (that is, Fe2+ at octahedral B-sites and Fe3+ at both tetrahedral A and octahedral B-sites), consistent with the more delocalized structure of Fe3O4, as compared with other mixed iron oxides13,14. The corresponding magnetic induction map of Fig. 1d exhibits evenly spaced magnetic contours, spanning from the surface to the centre of the grain, flowing in a counterclockwise direction (denoted by arrows), characteristic of a vortex state.
Bright-field TEM images acquired (a) before and (b) after in situ heating to 700 °C under 9 mbar of O2 for 8 h in an ETEM, with associated SAED patterns inset, indexed to Fe3O4 (Joint Committee on Powder Diffraction Standards (JCPDS) No. 75–449). (c) Associated EEL spectra of the Fe 2p L2,3 edge acquired from the Fe3O4 particle before (blue) and after (red) annealing within the ETEM. Black arrows emphasize three differing intensities from the mixed-valence compound of Fe3O4, while the red arrows highlight formation of pre- and post-peaks that indicate oxidation towards γ-Fe2O3. (d,e) Magnetic induction maps determined from the magnetic contribution to the phase shift, reconstructed from holograms taken (d) before and (e) after in situ heating, revealing the vortex nature of the particle. The contour spacing is 0.79 radians for both magnetic induction maps. The magnetization direction is shown using arrows, as depicted in the colour wheel. (f,g) Magnetic contributions to the phase shift, as used to reconstruct the magnetic induction maps in (d,e), respectively, and (h) line profiles across their centers before (blue) and after (red) annealing. Black arrows in h illustrate the loss in overall magnetic remanence. Scale bars represent 100 nm.
The bright-field TEM image of Fig. 1b shows the same Fe3O4 grain after exposure to 9 mbar O2 atmosphere at 700 °C for 8 h within the ETEM. Degradation of the surface of the grain is apparent, while the associated SAED pattern (Fig. 1b, inset) does not present any evidence for the formation of additional crystalline phases, with brightening of some planar reflections (for example, the −2 8 6 reflection) being attributable to slight tilting of the grain during annealing. However, the development of fine features in the associated EEL spectrum of the heated grain, taking the form of a small pre-peak in the L3 edge and post-peak in the L2 edge (Fig. 1c, red arrows), is indicative of a change in the Fe oxidation state towards γ-Fe2O3 or α-Fe2O3 (refs 15, 16, 17), as illustrated by the reference iron oxide EEL spectra displayed in Fig. 2. It is recognized that progressive oxidation induces the development of these small peaks, with complete oxidation to γ-Fe2O3 being associated with an ~1.3 eV splitting in the L3 edge15. Similarly, the Fe 2p edge in an α-Fe2O3 EEL spectrum is associated with a strong pre-peak located ~1.6 eV in front of the L3 edge16,17. Various iron hydroxides can also present similar pre-peaks in their Fe L3 edges; however, O2 is the only gas introduced into the system between acquisitions of EEL spectra, and hence the evolution of pre-peaks in this case is attributed solely to the effects of oxidation. The spacings between the central magnetic contours in the corresponding magnetic induction map (Fig. 1e), again flowing in a counterclockwise direction, were found to widen, most markedly towards the particle edge. Figure 1f,g presents magnetic contributions to the phase shifts used to construct Fig. 1d,e, respectively, and the reduction in amplitudes of the line profiles across their centres (dashed lines) is a strong indicator for loss of overall magnetic remanence in the Fe3O4 particle, as a consequence of oxidation (Fig. 1h, arrowed), again consistent with the progressive conversion of Fe3O4 towards γ-Fe2O3.
Effect of oxidation on the direction of magnetization
Figure 3 illustrates the effect of accelerated oxidation on the magnetization of an elongated (~250 nm long, ~150 nm wide) Fe3O4 grain. The bright-field TEM image of Fig. 3a shows the grain morphology, while the associated SAED pattern (Fig. 3a, inset) indexes to Fe3O4, again supported by the complementary characteristic EEL spectrum of Fig. 3c. The corresponding magnetic induction map of Fig. 3d reveals closely spaced magnetic contours flowing from left to right through the elongated particle, interacting with a small vortex located at the bottom, along with a component of stray magnetic field, which is indicative of a PSD state.
Bright-field TEM images acquired (a) before and (b) after in situ heating to 700 °C under 9 mbar of O2 for 8 h in an ETEM, with associated SAED patterns (inset) indexed to Fe3O4 (JCPDS No. 75–449). (c) Associated EEL spectra of the Fe 2p L2,3 edge acquired from the Fe3O4 particle before (blue) and after (red) annealing within the ETEM. Red arrows highlight the formation of pre- and post-peaks that indicate oxidation towards γ-Fe2O3. (d,e) Magnetic induction maps determined from the magnetic contribution to the phase shift reconstructed from holograms taken (d) before and (e) after in situ heating, revealing the PSD nature of the particle. The contour spacing is 0.20 radians for both magnetic induction maps. The magnetization direction is shown using arrows, as depicted in the colour wheel. Scale bars represent 100 nm.
The bright-field TEM image of Fig. 3b shows the same Fe3O4 grain after in situ heating in the ETEM at 700 °C under 9 mbar O2 atmosphere for 8 h. In a similar manner to the Fe3O4 grain shown in Fig. 1b, the elongated particle has degraded, while brightening of various planar reflections (for example, the −4 −4 6 and 4 4 2 reflections) in the associated SAED pattern (Fig. 3b, inset) was attributable to slight tilting of the particle during annealing. The additional development of a small pre-peak in the L3 edge and post-peak in the L2 edge of the corresponding EEL spectrum (Fig. 3c, red arrows) are again strong indicators for the effects of progressive oxidation towards γ-Fe2O3 or α-Fe2O3. The associated magnetic induction map (Fig. 3e) notably exhibits two vortices with widened magnetic contour spacings, flowing in opposite directions around a central transverse axis.
Discussion
This combined ETEM and off-axis electron holography investigation has provided a visual representation of the effects of accelerated chemical oxidation on the magnetization (direction and intensity) of PSD Fe3O4 particles. Bright-field TEM imaging showed the native Fe3O4 particles to undergo degradation following in situ heating under an O2 atmosphere, while development of additional peaks in the Fe 2p L2,3 edges provides compelling evidence for the process of oxidation12, with the Fe 2p L2,3 edge acquired from the oxidized equiaxed Fe3O4 grain resembling that of pure γ-Fe2O3 (Fig. 2), as distinct from α-Fe2O3. Intriguingly, the SAED data from the oxidized Fe3O4 particles provided no evidence for the development of additional crystallographic reflections. This can be expected during the bulk conversion of an inverse spinel ferrite Fe3O4 towards the crystallographically similar Fe2+ cation-deficient γ-Fe2O3 phase, through topotactic transformation initiated at the surface, where faint extra spots characteristic of γ-Fe2O3 would only appear in the SAED pattern along specific zone axes.
The widening of the magnetic contours around the vortex in the oxidized elongated Fe3O4 grain (Fig. 1e) compared with its initial state, supported by line profile differences across the magnetic contributions to the phase shift (Fig. 1h), demonstrates that chemical alteration indeed leads to a loss of magnetization intensity. Clockwise rotation of the central magnetic contours from along the major axis of the elongated Fe3O4 particle (Fig. 3d) to a transverse axis (Fig. 3e) demonstrates the strong effect of oxidation on the magnetization direction, an effect previously considered to be dominated by shape anistropy18. In this case, the EEL peaks characteristic of γ-Fe2O3 in the Fe 2p L2,3 edge of the oxidized elongated grain were notably less pronounced, in comparison with the equiaxed grain, suggesting that a significant proportion of Fe3O4 was still present. In this case, it is proposed that the tips of elongated grains are more susceptible to oxidation because of their larger exposed surface areas and shorter diffusion pathways. Preferential tip oxidation towards the less magnetic γ-Fe2O3 phase would alter the overall oxide phase distribution, with chemical modification of the elongated pure Fe3O4 grain to a PSD grain, containing a lower aspect ratio Fe3O4 core, prompting a shift towards lower energy and a more favourable direction of magnetization, the in-plane component of which is represented by the magnetic induction map of Fig. 3e. Indeed, magnetic domain states exist in three dimensions, and the shift in magnetization direction between the initial and oxidized elongated Fe3O4 grain suggests a greater degree of complexity associated with this process than can be fully accessed by two-dimensional (2D) in-plane representations of magnetization. Comparison between experimental and simulated magnetic induction maps, derived from multiphase three-dimensional (3D) micromagnetic models, could in future elucidate the 3D nature of the transformation observed in these magnetic domain states with chemical oxidation, providing fundamental insight into its effect on magnetic recording fidelity.
This combined ETEM and off-axis electron holography investigation has demonstrated changes in both remanent magnetic field strength and direction of magnetization within individual PSD particles as a consequence of accelerated chemical oxidation. When averaged over the millions of grains within a bulk palaeomagnetic sample, it is likely that the original directional information will be retained within the palaeomagnetic sample as not all grains will re-orientate their magnetization, although it is probable that some magnetic moments will re-align with the ambient field, giving rise to a CRM contribution to the total remanence. Certainly, the natural remanent magnetization intensity of a palaeomagnetic sample will most likely be decreased as a consequence of the oxidation process, resulting in an underestimate of ancient geomagnetic field intensity. Accordingly, palaeomagnetic data from samples showing evidence for chemical oxidation should be interpreted with care. The magnetic signal from natural rocks is inherently complex, comprising contributions from a mixture of low coercivity nonuniform MD magnetic grains, magnetically stronger nonuniform or vortex state PSD grains, and more stable high coercivity uniformly magnetized SD grains. As a step forward towards a better understanding of palaeomagnetic signals from the geomagnetic record, this study provides fundamental insight into the effect of chemical alteration on magnetic recording fidelity of the strongest magnetic mineral (magnetite) in the most commonly occurring domain state (PSD grains).
Methods
Sample details
Fe3O4 particles of diameter <200 nm (hydrothermally synthesized by Nanostructured and Amorphous Materials, USA) were cleaned with acetone and centrifuged for 6 min at 6,000 r.p.m. For the purpose of ETEM investigation, the particles were dispersed in distilled water using an ultrasonic bath before deposition on an Aduro E-chip TEM sample holder (Protochips, USA).
Environmental TEM
Investigation of the in situ oxidation of Fe3O4 particles, under 9 mbar O2 atmosphere, at elevated temperature, established using a Protochips heating holder (room temperature to 700 °C at 1 °C s−1, as displayed by the Protochips temperature control), was performed using an FEI Titan E-Cell TEM with CS corrector on the objective lens, operated at 300 kV. The high temperature of 700 °C was established to help compensate for the low pressure used during ETEM, being distinct from the ambient pressure conditions found in nature. EELS analysis was performed at a spectral resolution of ~0.3 eV, achieved through excitation of the monochromator, providing information on sample oxidation state. All TEM imaging and EEL spectra acquisition were performed on grains stabilized under high-vacuum conditions at ambient temperature, with in situ oxidation being performed in the absence of the electron beam to avoid any sample degradation through electron beam/material interaction during annealing.
Magnetic imaging
Off-axis electron holograms were acquired at 300 kV using an FEI Titan 80–300 TEM in Lorentz mode, with a charge-coupled device camera and an electron biprism operated typically at 160 V. These experiments were performed at room temperature, with an acquisition time of 4 s. The total phase shift recorded using electron holography is sensitive to both the electrostatic potential and the in-plane component of the magnetic induction in the specimen. To isolate the magnetic contribution to the phase shift, the direction of magnetization in each particle was reversed in situ in the TEM by tilting the sample ±30° and turning on the conventional microscope objective lens to apply a magnetic field of 2 T to the sample, parallel to the direction of the electron beam. The objective lens was then turned off and the sample tilted back to 0° for hologram acquisition in field-free conditions (residual field <0.2 mT) with the particles at remanence. Following this procedure, holograms were recorded with the particles magnetized in opposite directions, while the mean inner potential was separated from the magnetic potential, as described by Dunin–Borkowski et al.6 For the construction of magnetic induction maps, the cosine of the magnetic contribution to the phase shift was amplified to produce magnetic phase contours. Colours were added to the contours to show the direction of the projected induction, as denoted by the colour wheels.
Sample handling
In order to isolate the effects of chemical oxidation on the magnetization of the Fe3O4 grains, rather than possible temperature effects, samples were initially heated up to 700 °C within the Titan 80–300 TEM for 1 h and then cooled under vacuum, before acquisition of off-axis electron holograms from the native Fe3O4 grains. The Protochips TEM holder was then transferred to the Titan ETEM for the purpose of in situ chemical oxidation, with heating at 700 °C in a 9-mbar O2 atmosphere for 8 h, followed by imaging and EELS analysis under vacuum at ambient temperature conditions. The Protochips TEM holder and oxidized Fe3O4 grains were then transferred back to the Titan 80–300 TEM for acquisition of complementary off-axis electron holograms to appraise the magnetic response of the PSD grains.
Additional information
How to cite this article: Almeida, T. P. et al. Visualized effect of oxidation on magnetic recording fidelity in pseudo-single-domain magnetite particles. Nat. Commun. 5:5154 doi: 10.1038/ncomms6154 (2014).
References
Dunlop, D. J. Magnetic recording in rocks. Phys. Today 65, 31 (2012).
Ge, K., Williams, W., Liu, Q. & Yu, Y. Effects of the core‐shell structure on the magnetic properties of partially oxidized magnetite grains: experimental and micromagnetic investigations. Geochem. Geophys. Geosyst. 15, 2021–2038 (2014).
McClelland, E. Theory of CRM acquired by grain growth, and its implications for TRM acquisition and paleointensity determination in igneous rocks. Geophys. J. Inter. 126, 271–280 (1996).
Fabian, K. Thermochemical remanence acquisition in single-domain particle ensembles: A case for possible overestimation of the geomagnetic paleointensity. Geochem. Geophys. Geosyst. 10, Q06Z03 (2009).
Harrison, R., Dunin-Borkowski, R. E. & Putnis, A. Direct imaging of nanoscale magnetic interactions in minerals. Proc. Natl Acad. Sci. USA 99, 16556–16561 (2002).
Dunin-Borkowski, R. E. et al. Magnetic microstructure of magnetotactic bacteria by electron holography. Science 282, 1868–1870 (1998).
Kasama, T., Church, N., Feinberg, J. M., Dunin-Borkowski, R. E. & Harrison, R. J. Direct observation of ferromagnetic/ferroelastic domain interactions in magnetite below the Verwey transition. Earth Planet Sci. Lett. 297, 10–17 (2010).
Kasama, T. et al. Ferrimagnetic/ferroelastic domain interactions in magnetite below the Verwey transition. Part I: electron holography and Lorentz microscopy. Phase Transit. 86, 67–87 (2013).
Kasama, T. et al. Reversal of flux closure states in cobalt nanoparticle rings with coaxial magnetic pulses. Adv. Mater. 20, 4248–4252 (2008).
Feinberg, J. M. et al. Effects of internal mineral structures on the magnetic remanence of silicate-hosted titanomagnetite inclusions: an electron holography study. J. Geophys. Res. 11, B12S15 (2006).
Hansen, T. W., Wagner, J. B. & Dunin-Borkowski, R. E. Aberration corrected and monochromated environmental transmission electron microscopy: challenges and prospects for materials science. Mater. Sci. Technol. 26, 1338–1344 (2010).
Chen, S.-Y. et al. Electron energy loss spectroscopy and ab initio investigation of iron oxide nanomaterials grown by a hydrothermal process. Phys. Rev. B 79, 104103 (2009).
Fujii, T. et al. In situ XPS analysis of various iron oxide films grown by NO2-assisted molecular-beam epitaxy. Phys. Rev. B 59, 3195–3202 (1999).
Crocombette, J. P., Pollak, M., Joliet, F., Thromat, N. & Gautier-Soyer, M. X-ray-absorption spectroscopy at the Fe L2,3 threshold in iron oxides. Phys. Rev. B 52, 3143–3150 (1995).
Chen, J. et al. Magnetic circular dichroism in Fe 2p resonant photoemission of magnetite. Phys. Rev. B 69, 085107 (2004).
van Aken, P. A. & Lauterbach, S. Strong magnetic linear dichroism in Fe L23 and O K electron energy-loss near-edge spectra of antiferromagnetic hematite α-Fe2O3 . Phys. Chem. Miner. 30, 469–477 (2003).
Gloter, A., Douiri, A., Tence, M. & Colliex, C. Improving energy resolution of EELS spectra: an alternative to the monochromator solution. Ultramicroscopy 96, 385–400 (2003).
Tarling, D. & Hrouda, F. Magnetic Anisotropy of Rocks 217Chapman and Hall (1993).
Acknowledgements
The authors would like to thank the Natural Environment Research Council (NERC grant NE/H00534X/1) and the European Research Council for funding. We also thank the Center for Electron Nanoscopy at the Technical University of Denmark for use of their microscopy facilities.
Author information
Authors and Affiliations
Contributions
T.P.A. designed and carried out the experiments; A.R.M., W.W. and R.E.D.-B. conceived the study and supervised the research; T.K., T.W.H. and L.N. assisted with the experimental work and analysis; T.P.A. led the writing of the paper with contributions from A.R.M., P.D.B. and R.E.D.-B.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Almeida, T., Kasama, T., Muxworthy, A. et al. Visualized effect of oxidation on magnetic recording fidelity in pseudo-single-domain magnetite particles. Nat Commun 5, 5154 (2014). https://doi.org/10.1038/ncomms6154
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms6154
- Springer Nature Limited
This article is cited by
-
Palaeomagnetic and mineral magnetic analyses of the Deckenschotter of northern Switzerland and southern Germany
Swiss Journal of Geosciences (2023)
-
Multi-domain structures in spheroidal Co nanoparticles
Scientific Reports (2020)
-
Insight on thermal stability of magnetite magnetosomes: implications for the fossil record and biotechnology
Scientific Reports (2020)
-
Oxidation induced strain and defects in magnetite crystals
Nature Communications (2019)
-
A chemical, crystallographic and magnetic characterisation of individual iron-oxide grains in Hawaiian lavas
Scientific Data (2018)