Abstract
Oxidation of magnetite (Fe3O4) has broad implications in geochemistry, environmental science and materials science. Spatially resolving strain fields and defect evolution during oxidation of magnetite provides further insight into its reaction mechanisms. Here we show that the morphology and internal strain distributions within individual nano-sized (~400 nm) magnetite crystals can be visualized using Bragg coherent diffractive imaging (BCDI). Oxidative dissolution in acidic solutions leads to increases in the magnitude and heterogeneity of internal strains. This heterogeneous strain likely results from lattice distortion caused by Fe(II) diffusion that leads to the observed domains of increasing compressive and tensile strains. In contrast, strain evolution is less pronounced during magnetite oxidation at elevated temperature in air. These results demonstrate that oxidative dissolution of magnetite can induce a rich array of strain and defect structures, which could be an important factor that contributes to the high reactivity observed on magnetite particles in aqueous environment.
Similar content being viewed by others
Introduction
Redox cycling of iron (Fe) is an essential chemical process in geo- and bio-spheres1,2,3. Magnetite (Fe3O4) is an iron oxide mineral with an inverse spinel-type structure containing both Fe(II) and Fe(III)4. Magnetite is commonly observed in igneous and metamorphic rocks on Earth and has been found in meteorites and rocks on Mars, and it can also be formed through biomineralization processes5,6,7. In aqueous environments, magnetite plays an important role as a recyclable geochemical battery, where electrons are stored/released in the redox active Fe(II)/Fe(III) couple that serves as the main energy reservoir for Fe-metabolizing bacteria1,8. Oxidative dissolution of magnetite releases Fe(II), a critical reductant for immobilizing heavy metals and radionuclides in subsurface environment9,10. Both oxidative dissolution and oxidation with increasing O2 fugacity and temperature lead to a decrease in the Fe(II)/Fe(III) ratio from 0.5 in stoichiometric magnetite to 0 in maghemite (γ-Fe2O3)11. Understanding such a phenomenon can provide insights into controlling the reactivity of magnetite used for groundwater remediation and can benefit the proper interpretation of magnetic fields recorded in its domain structure when the mineral was formed (i.e., a paleomagnetic proxy)12,13,14.
Several issues regarding magnetite oxidation mechanisms remain unresolved. Observed oxidation kinetics in both dissolution and heated magnetite crystals are in agreement with a spherical diffusion model involving outward diffusion of Fe(II) to the mineral surfaces15,16,17. This is consistent with a core–shell structure model where a partially oxidized magnetite crystal has a magnetite core and a maghemite-like shell18. However, there is limited experimental evidence to test this structure because the crystal structures of magnetite and maghemite are nearly identical: their lattice constants differ by ~1%, and the spinel lattice is preserved, while the extra charge left by Fe (II) vacancies is neutralized by oxidation of Fe(II) to Fe(III) in maghemite19,20. Eq. (1) represented the oxidative dissolution of magnetite, where Fe(II) and Fe(III) in different sites are denoted by T (tetrahedral) and O (octahedral) with □ representing the cation vacancies.
Since there is a continuous solid solution between magnetite and maghemite, removal of Fe(II) from magnetite leads to the formation of off-stoichiometric magnetite (Fe(II)/Fe(III) ratio between 0.5 and 0) and lattice contraction19,20, but three-dimensional (3D) observations of the lattice spacing variation with associated strain and defect structures remain limited16,17. Strain and defects in minerals are important factors in controlling kinetics of geochemical reactions, such as mineral dissolution/growth and isotope exchange reactions21,22,23. In particular, off-stoichiometric magnetite can undergo a reverse reaction, i.e., reductive growth in the presence of aqueous Fe(II)24. Both reductive growth and oxidative dissolution reactions are controlled by diffusion of Fe(II) in and out of the spinel lattice25.
Structural characterization of magnetite crystals has been conducted using various experimental methods8,16,17,26,27,28. X-ray diffraction and Mössbauer spectroscopy have been widely used to measure the average unit-cell parameters and stoichiometry of magnetite powders17,19. Electron diffraction and surface probe microscopies have resolved ordered cation vacancies and surface reconstructions in magnetite26,27,29,30,31. Spatially resolving the strain structure related by Fe(II) movement could potentially provide new insights into the Fe(II) diffusion pathways and its relationship to diffusion kinetics32,33. However, the full 3D strain structures associated with off-stoichiometric domains within individual magnetite crystals cannot be achieved using traditional techniques. Synchrotron-based Bragg coherent diffractive imaging (BCDI) uses a coherent X-ray beam and phase-retrieval algorithms to image the morphology of crystals with high spatial resolution (i.e., tens of nanometers) and internal displacement fields (strain) with subangstrom sensitivity in the displacement magnitude34,35,36,37,38,39,40,41,42. The current BCDI measurement has a time resolution of several minutes, and therefore can be utilized to probe slow dynamic changes in strain and defect distributions within a single nm-scale magnetite crystal, providing an opportunity to gain new insights into its oxidation mechanisms.
Here, we compare the structural changes of magnetite crystals of a few hundred nm in size between two oxidation processes: oxidative dissolution at ambient conditions and thermal oxidation at high temperature (up to 250 °C). We seek to explore how the formation of strain and defect structures during oxidative dissolution of magnetite plays a role in heavy metal–mineral interactions. We find that oxidative dissolution of magnetite in aqueous solutions leads to the formation of nonuniformly distributed strain fields induced by localized lattice contraction/expansion, including the formation/dissociation of dislocation defects. In contrast, thermally oxidized magnetite crystals exhibit strain relief with substantially more homogenous internal strain fields. This stark difference in structural response to oxidation likely results from thermal effects, where high temperatures facilitate Fe(II) diffusion that can heal defects in the spinel lattice.
Results
Oxidative dissolution of magnetite in acidic solutions
Pristine magnetite crystals synthesized under hydrothermal conditions mostly have the morphology of octahedra, as seen by electron microscopy (Supplementary Fig. 1). These crystals were normally less than 500 nm across with face-sharing twins forming chains of interconnected crystals. The synthesized crystals were transferred onto a silicon wafer substrate for X-ray measurements. The measured lattice spacings of the pristine magnetite crystals matched those of stoichiometric magnetite (Supplementary Fig. 2a). Only the crystals that were stable on the substrate over repeated acid treatments are reported here. These crystals were mostly twinned crystals with common faces shared with nearby neighbors, as typical for hydrothermally synthesized magnetite samples28.
Pristine magnetite crystals were first imaged in air by BCDI and then reacted in a 0.1 M HCl solution for specific time periods. The acid was removed and the same crystal was imaged in air again. This process was repeated to record changes on the crystal as a function of reaction time. Among these, two magnetite crystals having morphologies of a pyramid and octahedron are shown in Figs 1 and 2, respectively. Here, the crystal shape imaged by BCDI corresponds to part of the crystal that has the crystallographic orientation satisfying a Bragg condition (that is, the (311) reflection for this study). This is referred to as the Bragg electron density. For example, a BCDI-determined shape can appear to be a pyramid with a square base, instead of an octahedron, when the upper and lower half of a magnetite octahedron are twinned crystals with different orientations, and therefore one half of the crystal becomes “invisible” to the BCDI measurement.
Both pyramid- and octahedron-shaped magnetite exhibit similar morphological changes by oxidative dissolution, primarily shown as volume reduction and surface roughening (Figs 1a, b and 2a, b). The coherent fringes of the 3D diffraction patterns were weakened (Supplementary Fig. 3), primarily due to increases in disorder (e.g., surface roughening). We also find an apparent loss of magnetite volume close to the crystal surface as indicated by the dashed arrows in Figs 1, 2, and in Supplementary Fig. 4 for another crystal. This volume reduction is likely caused by either dissolution or a localized solid-state transformation from crystalline magnetite to either maghemite or amorphous phases. In contrast, a pair of (111) surfaces indicated by the solid arrows in Fig. 2a, b maintained a relatively smooth surface morphology throughout the reaction (also see Supplementary Fig. 5 from two different views). This is indicated by a pair of relatively long coherent fringes observed in the 3D coherent diffraction pattern at all reaction time steps (Supplementary Fig. 3b). We, therefore, expect that these paired smooth surfaces were likely embedded surfaces shared by nearby twinned crystals (see an example twinned crystal in Supplementary Fig. 6).
In contrast to the similarities in changes of the external morphology, significant differences are observed in the internal displacement fields and strain structures between the pyramid and octahedron-shaped crystals. Increases in strain magnitude and extent were observed after the acid treatment in the pyramid-shaped crystal (Fig. 1c). Here, the strain was calculated from the first order derivative of the displacement field, which is the measured phase (from –π to π) scaled to the units of the lattice spacing (i.e., with values ranging from –d311/2 to d311/2; here, d311 = 2.5314 Å for magnetite43). Intrinsic strain was observed in the pristine pyramid-shaped magnetite (Fig. 1c, d). Regions of high local strains—both tensile and compressive strains that deviated significantly from the average—increased in the crystal after 4–9 min reactions, and then decreased slightly in 14 min (Fig. 1c). Regions of high compressive strain (blue), localized mostly at the bottom of the crystal, likely correspond to lattice contraction due to leaching of Fe(II). Removal of Fe was also indicated from the statistical distribution of the local amplitude (as seen in the Bragg electron density histograms, Fig. 3a), where the fractional volume of high amplitudes (i.e., from 0.7 to 1.0) decreased with increasing reaction time. The measured d311 spacing of the pyramid-shaped crystal was reduced slightly (by 0.04%) accompanied with increasing FWHM of the (311) Bragg peak (Supplementary Fig. 2), indicative of minor lattice contraction and decreasing crystallinity after dissolution, respectively. Increasing regions of high tensile strain (orange, lattice expansion) were observed in the same crystal (Fig. 1c). However, they were normally separated from regions of compressive strain (blue). These high-tensile strain regions exhibited stripe patterns in 2D (Fig. 1d) and clustered structures in 3D (Fig. 1c).
Changes in strain were more dramatic in the octahedron-shaped magnetite crystal (Fig. 2). Highly strained regions (both compressive and tensile strain) increased more rapidly in magnitude after the same acid treatment compared with those of the pyramid-shaped magnetite (Fig. 2c vs. Fig. 1c and see data outside the dashed lines in Fig. 3b, d). After 1 min of reaction in acidic solution, the crystal exhibited a significant increase in high-strain regions (Fig. 2c, d). The defect structure associated with this high-strain field was extracted using a gradient calculation method36,39. This analysis reveals a dislocation loop located approximately in the middle of the crystal (Fig. 4a, b). The strain field around this dislocation loop has opposite signs (Fig. 4c), consistent with strain generated from a pair of positive- and negative-edge dislocations associated with a single loop44. The coherent diffraction pattern of this magnetite grain (reacted for 1 min) was measured repeatedly (about 18 min measurement time in total) and all measurements showed the presence of a dislocation loop located roughly at the same location (Supplementary Fig. 7), but this loop disappeared with subsequent acid treatments for 3 min (i.e., total 4 min of reaction) (Fig. 2d). The formation of a linear dislocation defect that went through the crystal was observed in another magnetite crystal (Fig. 4d–f) and this linear defect also disappeared in subsequent acid treatments (Supplementary Fig. 8). The crystal shown in Fig. 2a had a 30% decrease in the apparent volume from 1 to 4 min reaction. Considering the Bragg peak intensity of this crystal after 4 min of reaction did not decrease compared with that at 1 min (Supplementary Fig. 2d), and the same amplitude threshold was used for plotting the 3D volume, the volume reduction is likely related to the formation of an amorphous surface layer, which was recrystallized in the subsequent acid treatment (Fig. 2a).
Electron microscopy was performed on the BCDI imaged crystals as well as separately prepared magnetite samples after similar dissolution reactions (Supplementary Fig. 9). The acid-treated crystals after the BCDI experiment maintained their original crystal morphologies under scanning electron microscopy (Supplementary Fig. 9a and b). Some crystals having rounded edges were observed under transmission electron microscopy (Supplementary Fig. 9c and d). The results indicate minor morphological and structural changes after the oxidative dissolution. These observations contrast with the significant changes in the structure and morphology of the BCDI-determined crystals, which is due to the selective sensitivity of BCDI to the crystalline portion of the magnetite satisfying the measured Bragg condition (i.e., reflections from the magnetite {311} planes).
Oxidation of magnetite in air with increasing temperature
We now compare the thermal oxidation of three magnetite crystals in air at elevated temperatures (up to 250 °C) with that observed in the low-temperature aqueous dissolution of magnetite. Unlike oxidative dissolution in solution, oxidation in air induced no significant changes on surface roughness and strain for T < 220 °C (Fig. 5a–c; also see complete temperature series of this crystal in Supplementary Fig. 10). The volume of the crystal showed no significant change while increasing the temperature up to 250 °C. A partial loss of volume was observed in the crystal shown in Fig. 5a while holding the temperature at 250 °C for 1.5 h. This morphological change is likely related to the phase transformation of magnetite to maghemite, which occurs at ~220 °C17. This phase transition was also confirmed by changes in the measured d spacing. Magnetite d311 exhibited a similar lattice spacing from room temperature to 220 °C, followed by an abrupt decrease in lattice spacing above the phase transition temperature and simultaneous increase in FWHM of the Bragg peak (Supplementary Fig. 11). Similar changes in strain were observed in another smaller magnetite crystal (Fig. 5d), which exhibited a tensile strained core with a compressive strained shell after the same heat treatment in air (Fig. 5e, f). Heating caused strain relief below the phase transformation temperature (see the complete temperature series of this crystal in Supplementary Fig. 12). Neither significant increases in internal strain nor the formation of the defect structures were observed during the oxidation of magnetite at elevated temperatures.
Thermal oxidation of a twinned magnetite crystal was also investigated (Fig. 6). The two domains have opposite phase signs (Fig. 6a), presumably resulting from a stacking fault defect at the boundary28,45,46. This boundary layer initially had a higher tensile strain than other parts (Fig. 6b, c), and the strain was relieved after heating at elevated temperatures (see complete temperature series of this crystal in Supplementary Fig. 13). Overall, heated magnetite crystals had smaller variations in morphology and strain below the phase transition temperature compared with those observed during the oxidative dissolution in acidic solutions.
Discussion
Magnetite undergoes a topotactic transformation to off-stoichiometric magnetite and maghemite in oxidation reactions, which involves minimal changes in crystal size, morphology, and structure15,16,20,47,48. Here, the measured average d311 spacing of individual magnetite crystals in both oxidative dissolution and thermal heating experiments showed minor decreases representing a mild-oxidation process of magnetite. The primary oxidized phases that were present consisted of off-stoichiometric magnetite, i.e., solid-solution phases between magnetite and maghemite. The magnetite crystals reacted in acidic solutions showed not only signs of oxidative dissolution, as indicated by d spacing decrease and volume reduction, but also local reductive growth. For example, the embedded surfaces showed area decrease/increase (dissolution/growth) during the reaction with acidic solutions (Fig. 2a, b surfaces pointed by arrows, and Supplementary Fig. 5). As mentioned above, these surfaces are likely shared by neighboring twin crystals. Fe(II) liberated during the oxidative dissolution from nearby crystals is likely responsible for the growth. Fe(II) is an active electron donor and can induce recrystallization of iron oxide minerals2,25,49. Fe(II) ions likely induced amorphization/recrystallization of part of the existing (111) surfaces, which contributed to the observed surface roughening and volume loss/gain as seen by BCDI. At the same time, Fe(II) adsorbed on magnetite surfaces might diffuse into the spinel lattice which indirectly induced the growth of the embedded surfaces25.
The measured amplitude (Bragg electron density) and phase (strain) were based on signals from the magnetite {311} planes, which is the most intense Bragg peak of magnetite. Full three-dimensional electron density and strain field maps can be obtained if three independent Bragg peaks from the same crystal are imaged37. However, measurements from a single plane are still sensitive to the Fe(II) motion induced structural changes. Magnetite {111} planes are parallel to vacancy sites where Fe(II) atoms can diffuse in the spinel lattice32,50. Changes in electron density and strain of the {111} planes can be effectively projected on the measured {311} planes. This helps to explain the observed large range of volume and morphological changes on the amplitude based volume in BCDI compared with that obtained by the electron microscopy. It is likely that other secondary phases, such as iron (oxy)hydroxides and iron oxides were present during the oxidation of magnetite17,20,48. We could only identify these phases if their d spacing values are close to the d311 of magnetite and if they were oriented nearly parallel to the d311 plane of the imaged magnetite crystal. While these restrictions limited our ability to image other secondary phases, it helped us to focus the measurements on magnetite crystals without the interference from other signals.
The formation of dislocation loop defects has been observed during the dissolution of silver nanoparticles and calcite crystals, phase transformation of palladium crystals, and mechanical indentation of gold nanocrystals by BCDI40,51,52,53. A dislocation loop is a defect structure whose dislocation line is closed inside the crystal44. Magnetite, (FeIII)T[FeII,FeIII]OO4, has oxygen anions forming a face-centered cubic (fcc) lattice with Fe(III) that occupies one-eighth of the tetrahedral sites and Fe(II) and Fe(III) together occupy one-half of the octahedral sites4. Defects and dislocations are expected and have been observed in the cubic close packed {111} planes, which are defined by alternating layers of Fe and O atoms31,54,55. A dislocation loop can be produced by the collapse of local vacancies and is commonly observed during rapid quenching and displacement cascades generated by irradiation44,56,57. As the oxidative dissolution of magnetite involves removal of Fe(II) by creating cation vacancies in the spinel lattice, vacancy accumulation may have occurred and favors a dislocation loop formation within the magnetite {111} planes. A similar observation on the appearance/disappearance of a dislocation loop was also reported during the phase transformation of palladium nanocrystals52. Such dislocation loops can be highly mobile as observed in metallic iron under transmission electron microscope (TEM) (diffusion coefficient of around 50 nm2/s)58,59. Current BCDI measurements took a few minutes to capture a single coherent diffraction pattern, and therefore do not yet have the appropriate temporal resolution to visualize their movement.
Spatially resolving strain fields and associated defect evolution provide new insights into understanding the oxidation mechanism of magnetite and its role in various geochemical processes. A previous model suggested that partially oxidized magnetite crystals would adopt a simple core–shell structure, where the changes would occur within a thin, but otherwise unobserved, surface layer17,18. Our results are ambiguous with respect to whether such a surface shell is formed during oxidation of magnetite as they probe, instead, the evolution of the unreacted magnetite core. The present results highlight the unexpected behavior in which the oxidative dissolution of magnetite induces highly strained regions within the interior of the crystal and can induce discrete dislocations, thereby revealing that such reactions are more structurally complex than previously expected. Numerous studies indicate that strain and defects can influence kinetics in geochemical reactions. For example, Fe(II) can donate electrons to goethite (α-FeOOH) to induce growth/dissolution reactions2,60. Such reactions between aqueous Fe(II) and poorly crystalline defect-rich goethite are much faster compared with those occurring on defect-free goethite21. In another example, an Fe isotope exchange reaction was observed between aqueous Fe(II) and magnetite25. The dissolution induced defects observed by BCDI may facilitate isotope exchange reactions in magnetite, which can influence the reactivity of magnetite used for environmental remediation and the proper interpretations of stable Fe isotope data extracted from magnetite14,61. In addition, nano-sized magnetite has been used to sequester heavy metals, such as U, from groundwater14. Strain and defects formed during the initial dissolution of magnetite may contribute to the fast metal removal rate observed at the earliest stage of U–magnetite interaction, in addition to factors such as surface area and stoichiometry of magnetite9,62,63. In general, BCDI provides a new opportunity to expand investigations on the influences of strain and defects on mineral reactivity to a large number of aqueous geochemical reactions.
Methods
Sample preparations
Magnetite crystals were synthesized using a wet chemistry method4. In brief, 0.3 M Fe(II) solution (FeSO4·H2O, Sigma-Aldrich) prepared in N2 degassed deionized (DI) water was heated to 90 °C in N2 atmosphere. 3.33 M KOH and 0.27 M KNO3 was then added with stirring for 5 h. The black precipitate was cooled and washed with N2 degassed DI water. The crystals were centrifuged and dried in N2 atmosphere. A droplet of magnetite-containing methanol solution was dripped on a Si wafer, where particles formed clusters containing aggregated magnetite crystals as the solvent evaporated. Magnetite nanoparticles were stabilized on the substrate by Van der Waals and magnetic forces.
Solutions and thermal treatment
Totally, 0.02–0.05 ml of 0.1 M HCl solution was dripped onto well-isolated magnetite clusters to encapsulate all the crystals inside the solution droplet. The acid was then removed at designated reaction times for BCDI measurements in air and was periodically applied/removed to further react the crystals. For the thermal treatment in air, magnetite crystals on Si wafer were mounted on a heating stage, where the temperature was increased from room temperature up to 250 °C at a step of 50 °C. A total of seven crystals were imaged by BCDI, including four crystals after acid treatment and three crystals by thermal heating.
BCDI experiment and electron microscopy
Bragg coherent diffractive imaging was performed at beamline 34-ID-C of the Advanced Photon Source at Argonne National Laboratory. Coherent X-ray beam with energy of 9 keV and flux of 5 × 109 photons/s was focused to 1.37 μm × 0.7 μm (horizontal × vertical) by the Kirkpatrick–Baez mirrors. The detector was preset to a Bragg position satisfying the diffraction condition from the magnetite (311) plane, and the sample stage was then translated horizontally until an isolated Bragg peak from a single magnetite crystal was observed on the detector. The 3D coherent X-ray diffraction pattern in the vicinity of the magnetite (311) Bragg peak (2θ = 31.2°) was measured through rocking curve scan in the range of ±0.3° in steps of 0.01°. The 2D slices of the 3D diffraction pattern were collected with the exposure time of 1–5 s per image using either a PILATUS (Dectris, pixel size of 172 μm, 487 × 195 pixels) or a Timepix (Amsterdam Scientific Instruments, pixel size of 55 μm, 256 × 256 pixels) detector placed 2.5 or 1.4 m away from the sample, respectively. Total data collection time per sample per coherent pattern was about 2–6 min. The diffraction geometry allowed us to measure a well separated diffraction signal originating from a single magnetite crystal among the aggregates of a large number of crystals. Each measurement was repeated 3–10 times. Phase-retrieval results show consistency for consecutive measurements indicating the minor impact of radiation damage, if any.
An iterative phase-retrieval algorithm is used to reconstruct the real space image of a crystal64. The amplitude is proportional to the Bragg electron density (for the crystal planes satisfying the chosen Bragg condition), which yields the morphology of the crystalline material45. The real space phase is proportional to the lattice displacement field projected along the measured scattering vector, which provides sensitivity to both strain and defect structures65. Details on the phase-retrieval algorithms can be found elsewhere36,66,67,68. In brief, error reduction combined with the hybrid input–output algorithm was used for five random starts of the guided analysis. The support was updated using the Shrink-wrap algorithm69. Three generations, each with five individual random started phases, were optimized and the model that showed the lowest error was selected from total of 15 reconstructions70. The voxel size was 8.14 × 8.14 × 8.14 and 12.33 × 12.33 × 12.33 nm3 with a conservative estimation on the resolution of 25.67 × 25.67 × 25.67 nm3 based on the phase-retrieval transfer function (Supplementary Fig. 14 and Supplementary Table 1). Electron microscopy images of pristine and reacted magnetite were recorded by Hitachi S4700 scanning electron microscope and Philips CM30 TEM.
Data availability
The data that support the findings of this study are available from the corresponding author upon reasonable request.
References
Byrne, J. M. et al. Redox cycling of Fe(II) and Fe(III) in magnetite by Fe-metabolizing bacteria. Science 347, 1473–1476 (2015).
Beard, B. L. et al. Iron isotope fractionation between aqueous ferrous iron and goethite. Earth Planet. Sci. Lett. 295, 241–250 (2010).
Rosso, K. M., Yanina, S. V., Gorski, C. A., Larese-Casanova, P. & Scherer, M. M. Connecting observations of hematite (alpha-Fe2O3) growth catalyzed by Fe(II). Environ. Sci. Technol. 44, 61–67 (2010).
Cornell, R. M., Schwertmann, U. The Iron Oxides 2nd Edition. (WILEY-VCH, Weinheim, 2003).
Devouard, B. et al. Magnetite from magnetotactic bacteria: size distributions and twinning. Am. Mineral. 83, 1387–1398 (1998).
Golden, D. C. et al. A simple inorganic process for formation of carbonates, magnetite, and sulfides in martian meteroite ALH84001. Am. Mineral. 86, 370–375 (2001).
Buseck, P. R. et al. Magnetite morphology and life on Mars. Proc. Natl Acad. Sci. USA 98, 13490–13495 (2001).
Byrne, J. M. et al. Size dependent microbial oxidation and reduction of magnetite nano- and micro-particles. Sci. Rep. 6, 30969 (2016).
Gorski, C. A., Nurmi, J. T., Tratnyek, P. G., Hofstetter, T. B. & Scherer, M. M. Redox behavior of magnetite: Implications for contaminant reduction. Environ. Sci. Technol. 44, 55–60 (2010).
Yuan, K. et al. Electrochemical and spectroscopic evidence on the one-electron reduction of U(VI) to U(V) on magnetite. Environ. Sci. Technol. 49, 6206–6213 (2015).
Vogt, K., Dohmen, R. & Chakraborty, S. Fe–Mg diffusion in spinel: New experimental data and a point defect model. Am. Mineral. 100, 2112–2122 (2015).
Yamazaki, T. & Solheid, P. Maghemite-to-magnetite reduction across the Fe-redox boundary in a sediment core from the Ontong–Java Plateau: influence on relative palaeointensity estimation and environmental magnetic application. Geophys. J. Int. 185, 1243–1254 (2011).
Almeida, T. P. et al. Visualized effect of oxidation on magnetic recording fidelity in pseudo-single-domain magnetite particles. Nat. Commun. 5, 5154 (2014).
Latta, D. E. et al. Influence of magnetite stoichiometry on U-VI reduction. Environ. Sci. Technol. 46, 778–786 (2012).
Tang, J., Myers, M., Bosnick, K. A. & Brus, L. E. Magnetite Fe3O4 nanocrystals: spectroscopic observation of aqueous oxidation kinetics. J. Phys. Chem. B 107, 7501–7506 (2003).
Sidhu, P. S., Gilkes, R. J. & Posner, A. M. Mechanism of low-temperature oxidation of synthetic magnetites. J. Inorg. Nucl. Chem. 39, 1953–1958 (1977).
Gallagher, K. J., Feitknecht, W. & Mannweiler, U. Mechanism of oxidation of magnetite to γ-Fe2O3. Nature 217, 1118–1121 (1968).
Frison, R. et al. Magnetite–maghemite nanoparticles in the 5–15 nm range: correlating the core–shell composition and the surface structure to the magnetic properties. A total scattering study. Chem. Mater. 25, 4820–4827 (2013).
Gorski, C. A. & Scherer, M. M. Determination of nanoparticulate magnetite stoichiometry by Mossbauer spectroscopy, acidic dissolution, and powder X-ray diffraction: a critical review. Am. Mineral. 95, 1017–1026 (2010).
White, A. F., Peterson, M. L. & Hochella, M. F. Electrochemistry and dissolution kinetics of magnetite and ilmenite. Geochim. Cosmochim. Acta 58, 1859–1875 (1994).
Notini, L. et al. The role of defects in Fe(II)-goethite electron transfer. Environ. Sci. Technol. 52, 2751–2759 (2018).
Schott, J. et al. Dissolution kinetics of strained calcite. Geochim. Cosmochim. Acta 53, 373–382 (1989).
Sethmann, I., Wang, J. W., Becker, U. & Putnis, A. Strain-induced segmentation of magnesian calcite thin films growing on a calcite substrate. Cryst. Growth Des. 10, 4319–4326 (2010).
Cismasu, C., Ona-Nguema, G., Bonnin, D., Menguy, N. & Brown, G. E. Zinc and arsenic immobilization and magnetite formation upon reduction of maghemite by shewanella putrefaciens ATCC 8071. Geochim. Cosmochim. Acta 72, A165–A165 (2008).
Gorski, C. A. et al. Fe atom exchange betweenaqueous Fe2+ and magnetite. Environ. Sci. Technol. 46, 12399–12407 (2012).
Kelm, K. & Mader, W. The symmetry of ordered cubic gamma-Fe2O3 investigated by TEM. Z. Naturforsch. B 61, 665–671 (2006).
Banfield, J. F., Wasilewski, P. J. & Veblen, D. R. TEM study of relationships between the microstructures and magnetic-properties of strongly magnetized magnetite and maghemite. Am. Mineral. 79, 654–667 (1994).
Recnik, A., Nyiro-Kosa, I., Dodony, I. & Posfai, M. Growth defects and epitaxy in Fe3O4 and gamma-Fe2O3 nanocrystals. Crystengcomm 15, 7539–7547 (2013).
McKenna, K. P. et al. Atomic-scale structure and properties of highly stable antiphase boundary defects in Fe3O4. Nat. Commun. 5, 5740 (2014).
Bliem, R. et al. Subsurface cation vacancy stabilization of the magnetite (001). Surf. Sci. 346, 1215–1218 (2014).
Lindquist, A. K., Feinberg, J. M., Harrison, R. J., Loudon, J. C. & Newell, A. J. Domain wall pinning and dislocations: Investigating magnetite deformed under conditions analogous to nature using transmission electron microscopy. J. Geophys. Res. 120, 1415–1430 (2015).
Hallstrom, S., Hoglund, L. & Agren, J. Modeling of iron diffusion in the iron oxides magnetite and hematite with variable stoichiometry. Acta Mater. 59, 53–60 (2011).
Dieckmann, R. & Schmalzried, H. Defects and cation diffusion in magnetite(II). Ber. Bunsen. Phys. Chem. 81, 414–419 (1977).
Robinson, I. & Harder, R. Coherent X-ray diffraction imaging of strain at the nanoscale. Nat. Mater. 8, 291–298 (2009).
Cha, W. et al. Core-shell strain structure of zeolite microcrystals. Nat. Mater. 12, 729–734 (2013).
Ulvestad, A. et al. Topological defect dynamics in operando battery nanoparticles. Science 348, 1344–1347 (2015).
Newton, M. C., Leake, S. J., Harder, R. & Robinson, I. K. Three-dimensional imaging of strain in a single ZnO nanorod. Nat. Mater. 9, 120–124 (2010).
Jiang, H. D. et al. Three-dimensional coherent X-ray diffraction imaging of molten iron in mantle olivine at nanoscale resolution. Phys. Rev. Lett. 110, 205501 (2013).
Clark, J. N. et al. Three-dimensional imaging of dislocation propagation during crystal growth and dissolution. Nat. Mater. 14, 780784 (2015).
Ihli, J. et al. Strain-relief by single dislocation loops in calcite crystals grown on self-assembled monolayers. Nat. Commun. 7, 11878 (2016).
Yang, W. G. et al. Coherent diffraction imaging of nanoscale strain evolution in a single crystal under high pressure. Nat. Commun. 4, 1680 (2013).
Yau, A., Cha, W., Kanan, M. W., Stephenson, G. B. & Ulvestad, A. Bragg coherent diffractive imaging of single-grain defect dynamics in polycrystalline films. Science 356, 739–742 (2017).
Wechsler, B. A., Lindsley, D. H. & Prewitt, C. T. Crystal structure and cation distribution in titanomagnetites (Fe3–xTixO4). Am. Mineral. 69, 754–770 (1984).
Hull, D., Bacon, D. J. Introduction to Dislocations, Fifth Edition. (Butterworth-Heinemann, Oxford, 2011).
Ulvestad, A., Clark, J. N., Harder, R., Robinson, I. K. & Shpyrko, O. G. 3D Imaging of twin domain defects in gold nanoparticles. Nano Lett. 15, 4066–4070 (2015).
Labat, S. et al. Inversion domain boundaries in GaN wires revealed by coherent bragg imaging. ACS Nano 9, 9210–9216 (2015).
Castro, P. A., Vago, E. R. & Calvo, E. J. Surface electrochemical transformations on spinel iron oxide electrodes in aqueous solutions. J. Chem. Soc. Faraday Trans. 92, 3371–3379 (1996).
Mancey, D. S., Shoesmith, D. W., Lipkowski, J., McBride, A. C. & Noel, J. An electrochemical investigation of the dissolution of magnetite in acidic electrolytes. J. Electrochem. Soc. 140, 637–642 (1993).
Williams, A. G. B. & Scherer, M. M. Spectroscopic evidence for Fe(II)–Fe(III) electron transfer at the iron oxide–water interface. Environ. Sci. Technol. 38, 4782–4790 (2004).
Dieckmann, R. & Schmalzried, H. Defects and cation diffusion in magnetite(I). Ber. Bunsen. Phys. Chem. 81, 344–347 (1977).
Liu, Y. et al. Stability limits and defect dynamics in Ag nanoparticles probed by bragg coherent diffractive imaging. Nano Lett. 17, 1595–1601 (2017).
Ulvestad, A. & Yau, A. The self-healing of defects induced by the hydriding phase transformation in palladium nanoparticles. Nat. Commun. 8, 1376 (2017).
Dupraz, M. et al. 3D imaging of a dislocation loop at the onset of plasticity in an indented nanocrystal. Nano Lett. 17, 6696–6701 (2017).
Hornstra, J. Dislocations, stacking faults and twins in the spinel structure. J. Phys. Chem. Solids 15, 311–323 (1960).
Charpentier, P., Rabbe, P. & Manenc, J. Mise en evidence de la plasticite de la magnetite mesure de la durete en fonction de la temperature. Mater. Res. Bull. 3, 69–78 (1968).
Cristiano, F. et al. Formation energies and relative stability of perfect and faulted dislocation loops in silicon. J. Appl. Phys. 87, 8420–8428 (2000).
Zinkle, S. J. Effect of irradiation spectrum on the microstructural evolution in ceramic insulators. J. Nucl. Mater. 219, 113–127 (1995).
Arakawa, K. et al. Observation of the one-dimensional diffusion of nanometer-sized dislocation loops. Science 318, 956–959 (2007).
Matsukawa, Y. & Zinkle, S. J. One-dimensional fast migration of vacancy clusters in metals. Science 318, 959–962 (2007).
Handler, R. M., Beard, B. L., Johnson, C. M. & Scherer, M. M. Atom exchange between aqueous Fe(II) and goethite: an Fe isotope tracer study. Environ. Sci. Technol. 43, 1102–1107 (2009).
Frierdich, A. J., Beard, B. L., Scherer, M. M. & Johnson, C. M. Determination of the Fe(II)-magnetite equilibrium iron isotope fractionation factor using the three-isotope method and a multi-direction approach to equilibrium. Earth. Planet. Sci. Lett. 391, 77–86 (2014).
Crane, R. A., Dickinson, M., Popescu, I. C. & Scott, T. B. Magnetite and zero-valent iron nanoparticles for the remediation of uranium contaminated environmental water. Water Res. 45, 2931–2942 (2011).
Das, D., Sureshkumar, M. K., Koley, S., Mithal, N. & Pillai, C. G. S. Sorption of uranium on magnetite nanoparticles. J. Radioanal. Nucl. Chem. 285, 447–454 (2010).
Chapman, H. N. et al. High-resolution ab initio three-dimensional X-ray diffraction microscopy. J. Opt. Soc. Am. A 23, 1179–1200 (2006).
Ulvestad, A. et al. Three-dimensional imaging of dislocation dynamics during the hydriding phase transformation. Nat. Mater. 16, 565–571 (2017).
Chou, C. I. & Lee, T. K. A guided simulated annealing method for crystallography. Acta Crystallogr. A 58, 42–46 (2002).
Gerchberg, R. W. & Saxton, W. O. A practical algorithm for the determination of phase from image and diffraction plane pictures. Optik 35, 237–246 (1972).
Fienup, J. R. Phase retrieval algorithms—a comparison. Appl. Opt. 21, 2758–2769 (1982).
Marchesini, S. et al. X-ray image reconstruction from a diffraction pattern alone. Phys. Rev. B 68, 140101R (2003).
Chen, C. C., Miao, J., Wang, C. W. & Lee, T. K. Application of optimization technique to noncrystalline x-ray diffraction microscopy: guided hybrid input–output method. Phys. Rev. B 76, 064113 (2007).
Acknowledgments
This work was supported by U.S. Department of Energy (DOE), Office of Science, Office of Basic Energy Sciences, Chemical Sciences, Geosciences, and Biosciences Division under Contract DE-AC02-06CH11357 to UChicago Argonne, LLC, Operator of Argonne National Laboratory (“Argonne”). Argonne, a U.S. Department of Energy Office of Science laboratory. This research used resources of the Advanced Photon Source, a U.S. DOE Office of Science User Facility, beamline 34-ID-C, operated for the DOE Office of Science by Argonne National Laboratory under Contract No. DE-AC02-06CH11357. Use of the Center for Nanoscale Materials, an Office of Science user facility, was supported by the U.S. Department of Energy, Office of Science, Office of Basic Energy Sciences, under Contract no. DE-AC02-06CH11357. The U.S. Government retains for itself, and others acting on its behalf, a paid-up nonexclusive, irrevocable worldwide license in said article to reproduce, prepare derivative works, distribute copies to the public, and perform publicly and display publicly, by or on behalf of the Government. The Department of Energy will provide public access to these results of federally sponsored research in accordance with the DOE Public Access Plan. H.K. thanks the support by the National Research Foundation of Korea (NRF-2014R1A2A1A10052454 and 2015R1A5A1009962). Finally, we thank Dr. Brian Stephenson (Argonne National Laboratory) for helpful discussions and Kyuseok Yun (Sogang University) for data visualization.
Author information
Authors and Affiliations
Contributions
K.Y., S.S.L., and P.F. designed the study. K.Y., S.S.L., W.C., B.A., and P.F. carried out the experimental measurements. K.Y., W.C., A.U., S.S.L., and P.F. did the phase-retrieval analysis. All authors discussed the results and contributed to the interpretation of data. All authors contributed to editing the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Journal peer review information Nature communications Thanks the anonymous reviewers for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Yuan, K., Lee, S.S., Cha, W. et al. Oxidation induced strain and defects in magnetite crystals. Nat Commun 10, 703 (2019). https://doi.org/10.1038/s41467-019-08470-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-019-08470-0
- Springer Nature Limited
This article is cited by
-
In-situ and wavelength-dependent photocatalytic strain evolution of a single Au nanoparticle on a TiO2 film
Nature Communications (2024)
-
Effects of water-induced aging on iron (oxyhydr)oxides nanoparticles: linking crystal structure, iron ion release, and toxicity
Chemical Papers (2024)
-
Iron (hydr)oxide formation in Andosols under extreme climate conditions
Scientific Reports (2023)
-
Characterization and identification of Au pathfinder minerals from an artisanal mine site using X-ray diffraction
Journal of Materials Science (2021)
-
Interfacial X-Ray Scattering From Small Surfaces: Adapting Mineral-Fluid Structure Methods for Microcrystalline Materials
Clays and Clay Minerals (2021)