Abstract
The slow activity of cathode materials is one of the most significant barriers to realizing the operation of solid oxide fuel cells below 500 °C. Here we report a niobium and tantalum co-substituted perovskite SrCo0.8Nb0.1Ta0.1O3−δ as a cathode, which exhibits high electroactivity. This cathode has an area-specific polarization resistance as low as ∼0.16 and ∼0.68 Ω cm2 in a symmetrical cell and peak power densities of 1.2 and 0.7 W cm−2 in a Gd0.1Ce0.9O1.95-based anode-supported fuel cell at 500 and 450 °C, respectively. The high performance is attributed to an optimal balance of oxygen vacancies, ionic mobility and surface electron transfer as promoted by the synergistic effects of the niobium and tantalum. This work also points to an effective strategy in the design of cathodes for low-temperature solid oxide fuel cells.
Similar content being viewed by others
Introduction
A low-temperature solid oxide fuel cell (LT-SOFC) is a durable energy device that can be deployed to convert the chemical energy stored in various types of fuels into electricity with high efficiency, ease of sealing, and reduced system and operational costs1,2,3. However, the low operating temperature (450-600 °C) typically leads to sluggish kinetics of the oxygen reduction reaction (ORR) at the cathode, with this being a major limitation to LT-SOFC performance4,5,6,7,8,9.
Intensive research has been carried out in an effort to explore cathode compositions suitable for operation at low temperature4,6,7,10,11,12,13,14,15. Oxides offering high mixed ionic and electronic conductivities (MIECs) are considered to be some of the most promising candidates for the next generation of SOFC cathodes due to their extended active sites for ORR when compared with purely electronic conducting materials16,17. Some of these MIEC cathodes have been reported exhibiting relatively low cathode polarization resistance below 600 °C (ref. 11). For example, the in-situ co-assembly of La0.8Sr0.2MnO3 (with a very low O2 dissociation energy barrier) and Bi1.6Er0.4O3 (with fast oxygen incorporation kinetics) leads to a high performance nanocomposite cathode showing a low polarization resistance of ∼0.078 Ω cm2 and ∼0.6 Ω cm2 at 600 and 500 °C, respectively11. Choi et al.12 developed a novel MIEC cathode PrBa0.5Sr0.5Co1.5Fe0.5O5+δ that exhibits a polarization resistance as low as ∼0.33 Ω cm2 at 500 °C, and the NdBa0.75Ca0.25Co2O5+δ material also shows an outstanding ORR activity at reduced temperature7. Another MIEC cathode composition, Ba0.9Co0.7Fe0.2Mo0.1O3−δ, was also reported to show an enhanced cathode performance with a polarization resistance of ∼0.28 Ω cm2 at 500 °C (ref. 18).
Currently, some of the most popular MIEC cathode materials are the stabilized SrCoO3−δ (SC) perovskite oxides, such as Sm0.5Sr0.5CoO3−δ (ref. 19, La,Sr)(Co,Fe)O3−δ (refs 20, 21) and Ba0.5Sr0.5Co0.8Fe0.2O3−δ4,22, which are claimed to exhibit high ORR activity in the intermediate temperature range 600–750 °C because of their relatively high mixed conductivities23,24. The perovskite structure of SC, which is favoured for ORR, is usually stabilized by partial B-site substitution with high oxidation-state cations25, such as Nb26,27, Mo28, Sb29,30 and P31,32, and these cations lead to low area-specific resistances (ASRs) at reduced temperature27,28,29,31,33,34. Besides the single doped SCs, Zhou et al.10 developed a highly active perovskite cathode material, featuring a partial replacement of Co ions with both Sc3+ and Nb5+, and these dopants induce a remarkably high ORR activity at 550 °C. To the best of our knowledge, few studies report the possible synergistic effects of co-doping highly charged dopants on catalysing the ORR in LT-SOFC cathodes.
Herein, we report the study of the synergistic effects of two highly charged B-site dopants on the performance of the perovskite LT-SOFC cathode SrCo0.8Nb0.1Ta0.1O3−δ (SCNT), with this cathode exhibiting outstanding and stable electrochemical performance below 500 °C. A low ASR of ∼0.16 and ∼0.68 Ω cm2 is achieved at 500 and 450 °C, respectively, by the SCNT cathode in a symmetrical cell configuration under open circuit conditions. A LT-SOFC with a pure SCNT cathode exhibits good performance of ∼1.2 and ∼0.7 W cm−2 at 500 and 450 °C, respectively. Our results show that the co-substitution of Nb5+ and Ta5+ can lead to an optimized balance of oxygen vacancies, ionic mobility and surface electron-transfer, which potentially benefit the ORR in the SCNT cathode.
Results
Structure and cation arrangement of SCNT
Joint Rietveld analysis of neutron and X-ray powder diffraction data (Fig. 1a,b) revealed that the SCNT at room temperature exhibits a cubic perovskite structure with space-group symmetry and a lattice constant of 3.9066(1) Å (Table 1). High-resolution transmission electron microscopy combined with selected area electron diffraction (SAED) (Fig. 1c) confirms this structure. Moreover, the binding energies of Nb 3d 5/2 (206.76 eV) and Ta 4f 7/2 (25.58 eV) in SCNT, obtained from X-ray photoelectron spectroscopy, indicate that the dopants are both in 5+ valence35,36 (Supplementary Fig. 1). The cubic structure of SC is maintained by the co-doping of Nb5+ and Ta5+ at the Co-site likely because of their high oxidation states25. Rietveld refinement results show Nb and Ta cation doping levels of 9.7(5) and 6.9(5) mol%, respectively, and an oxygen deficiency level of 5.6(5) mol% in SCNT. Both the cubic perovskite structure and oxygen deficiency are beneficial for oxygen-ion conduction, which is critical for a cathode, particularly for LT-SOFC application. The former makes oxygen vacancies migrate freely among lattice-equivalent oxygen sites37, while the latter facilitates ionic conduction16,38.
ORR activity in symmetrical and single cells
We determined the ORR activity of SCNT in a symmetrical cell configuration between 450 and 700 °C using electrochemical impedance spectroscopy (EIS). The cathode ASR, calculated from the intercept difference of EIS impedance with the real axis (that is, Re_Z in Fig. 2c), is the key variable characterizing the cathode performance, with low ASR indicating high activity. The intercept of the impedance at high frequencies indicates an ohmic resistance arising from the electrolyte, electrode and connection wires39, with only approximately 1–2% of the total ohmic resistance contributed from the SCNT cathode on both sides of the electrolyte Gd0.1Ce0.9O1.95 (GDC)-based symmetrical cell (Supplementary Fig. 2a). The compatibility of SCNT with Sm0.2Ce0.8O1.9 (SDC) and GDC electrolytes was examined by comparing the X-ray diffraction patterns of a 50:50 wt.% powder mixture of the SCNT and electrolyte after heating to the cathode fabrication temperature of 1,000 °C for 2 h (Supplementary Fig. 3). The results reveal no obvious changes to the SCNT after heating with electrolyte, indicating a good chemical compatibility between the two. Since the silver current collector does not significantly affect cathode performance40 and the cathode thickness (∼10 μm) proves to be sufficient (Supplementary Fig. 2b), our measured ASRs reflect the ORR activity of the SCNT cathode. Figure 2a shows that the SCNT cathode exhibits notably high ORR activity at low temperature, with an ASR as low as 0.061–0.086, 0.16–0.23 and 0.68–0.80 Ω cm2 at 550, 500 and 450 °C, respectively. The SCNT cathode outperforms the other reported cathode compositions at below 500 °C. (Supplementary Table 1)7,10,11,12,18,40,41,42 For example, the electroactivity of SCNT cathode is nearly twice that of the highly active SrSc0.175Nb0.025Co0.8O3−δ at 500 °C (ref. 10), and is also higher than that of Ba0.9Co0.7Fe0.2Mo0.1O3−δ at 450 °C (ref. 18).
When examined against other cathodes, the SCNT cathode performance is also found to be higher than that of the isostructural SrCo0.9Nb0.1O3−δ (SCN10), SrCo0.9Ta0.1O3−δ (SCT10), SrCo0.8Nb0.2O3−δ (SCN20) and SrCo0.8Ta0.2O3−δ (SCT20) perovskite cathode materials (Supplementary Fig. 4), having ASRs of 0.476±0.009, 0.353±0.001, 0.63±0.08 (ref. 43) and 0.25±0.02 Ω cm2 (ref. 43), respectively, at 500 °C. In addition, a lower activation energy (103.1±0.8 kJ mol−1) of SCNT is observed relative to that of SCN10 (105.3±1.6 kJ mol−1), SCT10 (105.3±0.5 kJ mol−1), SCN20 (108.5±0.3 kJ mol−1) and SCT20 (105.8±1.5 kJ mol−1), implying its suitability for catalysing oxygen reduction at low temperature.
The performance of the SCNT cathode in a LT-SOFC was evaluated using Ni-SDC|SDC (∼20 μm) |SCNT (∼10 μm; Supplementary Fig. 5a) and Ni-GDC|GDC (∼14 μm)| SCNT (∼10 μm) fuel cells (Fig. 2b). The micrographs of the two single-cell cross sections are shown in Supplementary Fig. 6. At 550, 500 and 450 °C, power densities of 1.13, 0.77 and 0.37 W cm−2 are achieved, respectively, in the former single cell (using SDC as the electrolyte) with ohmic resistances of ∼0.072, 0.113 and 0.193 Ω cm2, which mainly arise from the electrolyte. The electrode polarization resistance (the sum of cathode and anode ASRs) are ∼0.059, 0.132 and 0.271 Ω cm2 at the respective temperature. Given that SCNT has reasonable chemical compatibility with GDC (Supplementary Fig. 3b) and a similar ORR activity with both GDC and SDC electrolyte (Supplementary Fig. 2c), GDC was also used in single cells due to its ease of coating. The cell can generate a peak power density as high as 1.75, 1.22 and 0.7 W cm−2 at 550, 500 and 450 °C, respectively, this being significantly higher than that of Ba0.5Sr0.5Co0.8Fe0.2O3−δ of ∼0.97, 0.52 and 0.316 W cm−2, respectively (Supplementary Fig. 5b). With a thinner GDC electrolyte, the fuel cell ohmic resistance is reduced to 0.033, 0.049 and 0.083 Ω cm2 at these temperatures, less than half of that for the SDC (∼20 μm)-based fuel cell. However, the electrode resistance of the GDC cell is only slightly lower than that of the SDC-based cell, being 0.056, 0.116 and 0.242 Ω cm2 at these respective temperatures. Taking into consideration the ease and low-cost of the ceramic fabrication processes involved in the necessary scale-up5, GDC electrolyte fuel cells can be fabricated to a thickness of approximately 10–14 μm, though further reduction in GDC thickness is expected to boost the single cell performance by lowering its ohmic resistance6,9. Overall, the performance of the SCNT-based fuel cell surpasses the target of 500 mW cm−2 for SOFCs44, suggesting the possibility of practical operation even below 450 °C.
Synergistic effects of Nb and Ta on the ORR
Notably, SCNT shows a higher ORR activity when compared with the iso-structural SCN20 and SCT20 materials with similar lattice constants of 3.9066(1) Å for SCNT (Table 1), 3.8978(2) Å for SCT20 and 3.8971(1) Å for SCN20, obtained from the analysis of the neutron powder diffraction (NPD) data in our previous work43. The oxygen vacancy content of the SCN20, SCT20 and SCNT materials was also determined from NPD data to be 0.102±0.02, 0.159±0.15 and 0.168±0.15, respectively, revealing a similar oxygen vacancy level in SCNT and SCT20, which are both significantly higher than in SCN20. Thermal gravimetric analysis also shows higher oxygen vacancy contents in SCNT and SCT20 than in SCN20 at elevated temperature. (Supplementary Fig. 7) Given the fixed valence of dopants, the valence of reducible Co is likely the main reason for the oxygen vacancy concentration differences, and the average valence of cobalt in samples was calculated from the elemental composition determined from the structural refinement. The average valence of Co is 3.44, 3.33 and 3.41 for SCN20, SCT20 and SCNT, respectively. The lower Co valence in Ta-doped samples can be ascribed to the lower electronegativity of Ta than Nb43. In addition, our first-principles calculation results also show that oxygen formation energies are 1.539, 1.456 and 1.512 eV for the Nb-, Ta- and co-doped models, respectively, which further supports the observed relatively high oxygen deficiency in SCNT as induced by Ta. However, it seems insufficient to explain the better performance of SCNT than SCT20 merely by their oxygen vacancy contents. Given the similar particle size (Supplementary Fig. 8) but slightly lower electrical conductivity (Supplementary Fig. 9) of SCNT compared to SCN20 and SCT20, the superior cathode electroactivity of SCNT is likely attributable to other ORR-related properties such as bulk oxygen ionic conductivity and oxygen surface-exchange kinetics. Hence we estimated the ionic conductivity of the SCN20, SCT20 and SCNT materials by studying the oxygen permeability of dense membranes with similar dimensions from 600 to 475 °C. The higher ionic conductivity (Fig. 3a) of SCNT over SCN20 can be explained by the more oxygen vacancies in SCNT relative to SCN20. Ionic conductivity is also known to be significantly affected by other factors such as lattice geometry, critical radius45, and lattice free-volume available for oxygen ions to pass through46. Because SCNT and SCT20 have similar lattice dimensions, the faster ionic conduction in SCNT may stem from the synergistic effects of Nb and Ta, which potentially decrease the energy barrier for oxygen migration between neighbouring octahedral CoO6 vacancies, as reported for the Sc3+ and Nb5+-doped perovskite oxide by Zhou et al.10 In order to confirm this hypothesis, we investigated the pathways for oxygen vacancy migration through first-principles calculations. We found that our three models have very similar minimum energy pathway, as shown in Fig. 3b, but with different energy barriers. The highest energy barrier along the pathway is 0.433, 0.638 and 0.572 eV for Nb-, Ta- and the co-doped models, respectively, (Supplementary Table 2), indicating an easier vacancy mobility within the co-doped model as compared to Ta-doped model. Although SCNT and SCT20 have similar oxygen vacancy levels, the higher ionic conductivity of SCNT than SCT20 is likely a result of the incorporation of Nb that enhances ionic mobility in the lattice.
Additionally, slightly lower electrical conductivity (σtotal) that includes both electronic and ionic conductivity (σion) is observed for SCNT than for SCN20 and SCT20 (Supplementary Fig. 9). The lower electrical conductivity of SCNT is caused by increased oxygen vacancies that can diminish the charge carriers for hopping process. The ionic transference number (tion=σion × σtotal−1) of SCNT, SCN20 and SCT20 was calculated and shown in Supplementary Fig. 10. As the electronic conductivity dominates, the ionic transference number is very small in the studied temperature range. Nevertheless, SCNT has a larger ionic transference number than SCN20 and SCT20; e.g. SCNT has a transference number of ∼1.33 × 10−5 at 500 °C, which is ∼2.7 and ∼2.1 times that of SCN20 and SCT20, respectively. By extending the oxygen reduction active region and enhancing the ORR kinetics47,48, the higher oxygen vacancy content and improved mobility of SCNT imparted by the co-doping are likely to be more important than the electronic conductivity to the outstanding ORR performance of SCNT.
The oxygen surface exchange kinetics were investigated by comparing the O2-intake time of each sample in response to an atmosphere change from N2 to air at 500 °C. The SCNT mass equilibrates faster (∼188 s) than SCN20 (∼245 s) and SCT20 (∼217 s), suggesting a faster oxygen surface exchange of SCNT at lower temperature (Supplementary Fig. 11). Therefore, the Nb and Ta together could also synergistically enhance the surface-exchange processes by creating more oxygen vacancies and improving ionic mobility.
We also fitted the impedance spectra of SCNT, SCN20 and SCT20 cathodes to an equivalent circuit model consisting of two dominant reaction processes, with an example fitting presented in Fig. 2c. As shown in Supplementary Fig. 12 and from our previous work43, the cathode reciprocal resistances at high and low frequencies show different oxygen partial pressure dependencies m (as shown in equation (5)): m is ∼0.25 at high frequencies (HF) and ∼0.5 at low frequencies (LF) According to the relationship between pO2 dependencies and rate-determining-steps as discussed by other researchers49,50,51, the polarization resistance at HF is likely related to charge transfer and that at LF to non-charge-transfer steps.
Where O2,adsis an adsorbed oxygen molecule on the cathode surface, is an electron, is an oxygen vacancy and is an oxygen. Table 2 summarizes the polarization resistance of these two processes. SCNT exhibits significantly lower ASRs for the charge-transfer process than either SCN20 or SCT20, and nearly half of the resistance of SCN20 and similar resistance to SCT20 for the non-charge transfer process. The fast kinetics of charge transfer can be partly attributed to the high oxygen vacancy content of SCNT induced by Ta, since oxygen vacancies are shown to play an important role in the charge-transfer process (equation (1)).
On the other hand, since Nb5+ and Ta5+ are inert to oxygen surface redox-processes due to their fixed valence, Co plays a vital role in catalysing the oxygen reduction. Therefore, we calculated the atomic orbital-resolved electron density of states projected onto the Co atom in Nb, Ta and Nb/Ta co-doped strontium cobalt oxides using first-principles calculations. As shown in the schematic models (Fig. 4c,f for Nb or Ta single-doped models and Fig. 4i for co-doped model), there are two categories of cobalt atoms: one is the nearest neighbour (NN) Co to the dopant, including Co1 and Co2 in the single-doped model, and Co1, Co2 and Co3 for co-doped model; the other is the next-nearest neighbour (NNN) Co to the dopants, including Co3 in the single-doped model and Co4 in the co-doped model. By comparing the electronic states of these Co atoms, we found that the NN-Co atoms have very similar density of states (DOS) near the Fermi level for these three models. For the NNN-Co atoms, the Ta-doped model (Fig. 4e) exhibits only 60% of DOS of the Nb-doped model (Fig. 4b) near the Fermi level, indicating that Nb is more favourable to increasing the DOS of the NNN-Co near the Fermi level. Due to the beneficial effect of Nb, the DOS of the NNN-Co near the Fermi level of the co-doped model (Fig. 4h) is ∼98% that of Nb-doped model. The enhanced DOS at the Fermi level can increase the efficiency of electron-transfer to the adsorbed oxygen species O2,ads (ref. 52), and it is therefore likely that the higher DOS of NNN-Co atoms near the Fermi level, as induced by Nb, is the reason for the faster kinetics of charge-transfer in SCNT than in SCT20, despite their similar oxygen vacancy concentration.
Our experimental and calculation results reveal that the superior electroactivity of SCNT is a result of a balance of the oxygen vacancy content, oxygen-ion mobility and electron-transfer to O2,ads, which are imparted by co-doping Nb and Ta.
Stability tests
The durability of the cathode was investigated in both symmetrical and single cell configurations, as shown in Fig. 5. The ASR of SCNT in a symmetrical cell configuration was tested under the open circuit condition for ∼200 h. The ORR activity was relatively stable at ∼0.033 Ω cm2 with an ASR increase of ∼0.06% per hour during the testing period. The slight increase of the ASR during the stability test is likely to arise from the densification and reduced porosity of the silver current collector during this testing timeframe, which degrades the overall cathode performance53,54,55. Another short-term stability evaluation of the SCNT cathode in a single-cell configuration with ∼20 μm-thick SDC electrolyte also showed that the SCNT is stable under 0.7 V polarization for at least 150 h at 450 °C in air. The low current density noted in the stability testing arises from the electrolyte thickness, which leads to high ohmic resistance. This stable ORR activity of SCNT is expected given its stable perovskite lattice (Supplementary Fig. 13).
Discussion
In summary, the perovskite composition SrCo0.8Nb0.1Ta0.1O3−δ (SCNT) was synthesized and exhibits the highest reported activity for the reduction of oxygen in an LT-SOFC, to the best of our knowledge, with an ASR of only ∼0.16 and ∼0.68 Ω cm2 at 500 and 450 °C, respectively, in a symmetrical cell configuration. High power density is therefore achieved using a pure SCNT cathode as a result of its outstanding ORR activity. A performance comparison amongst the iso-structural SCNT, SrCo0.8Nb0.2O3−δ (SCN20) and SrCo0.8Ta0.2O3−δ (SCT20) cathodes reveals enhancement of the bulk oxygen ionic-conductivity achieved through co-doping of Nb5+ and Ta5+. Our experimental results and density functional theory calculations both show that co-doping results in a favourable balance of oxygen vacancy content, ion mobility and surface electron transfer, which is consistent with the higher performance of the co-doped SCNT cathode at lower temperature. Therefore, our highly active perovskite cathode not only presents a simple solution to address sluggish cathode kinetics below 500 °C, but could also provide an effective doping strategy for the design of mixed-conducting materials for SOFC and oxygen-ion transport membrane applications at low temperature.
Methods
Sample syntheses
The SCNT material was synthesized through a solid state reaction route by ball milling stoichiometric amounts of SrCO3 (≥99.9%, Aldrich), Co3O4 (≥99.9%, Aldrich), Nb2O5 (≥99.9%, Aldrich) and Ta2O5 (≥99.9%, Aldrich) for 24 h, before pelletizing and sintering the mixture in stagnant air at 1,200 °C for 10 h. Subsequently, the sintered pellets were well ground and re-sintered for another 10 h at 1,200 °C. SrCo0.9Nb0.1O3−δ (SCN10), SrCo0.8Nb0.2O3−δ (SCN20), SrCo0.9Ta0.1O3−δ (SCT10), SrCo0.8Ta0.2O3−δ (SCT20) and Ba0.5Sr0.5Co0.8Fe0.2O3−δ (BSCF) were also prepared through a similar synthesis route.
Structure characterization
The crystal structures of cathode materials were studied by X-ray powder diffraction and NPD. High-resolution NPD data were collected using ECHIDNA, the high-resolution neutron powder diffractometer at the Australian Nuclear Science and Technology Organization (ANSTO)56, with a neutron wavelength of 1.6219(2) Å, determined using the La11B6 NIST standard reference material 660b. NPD data were obtained from SCNT within a 6 mm vanadium can for 6 h in the 2θ angular range 4 to 164° with a step size of 0.125°. GSAS-II (ref. 57) was employed to perform Rietveld analysis of the high-resolution NPD data, using a cubic perovskite33 starting structure. The structure was refined against both the X-ray powder diffraction and NPD data, with atomic displacement parameters for the Co, Nb and Ta, fixed to 0.01. High-resolution electron transmission microscopy (HR-TEM, Tecnai F20) in conjunction with selected area electron diffraction was also used for phase identification.
Conductivity and thermogravimetric analyses
A DC 4-probe method was used to measure electrical conductivity of the specimen in flowing air (200 ml min−1). The samples for the conductivity measurement were dense bars, which were prepared by pressing the cathode powders followed by sintering at 1,200 °C for 5 h. Following this, samples were well milled and polished and silver leads attached as the current and voltage electrodes. Electrical conductivity was measured using an Autolab PGSTAT20 work station.
Ionic conductivities were estimated from oxygen permeability tests carried out by gas chromatography (GC)58. Membranes were fabricated by pelletizing cathode powders (milled for 2 h in alcohol at 400 r.p.m.), followed by sintering at 1,200 °C for 10 h and polishing. The relative densities of all samples were over 95%. Subsequently, the dense pellets were sealed in an alumina tube using silver paste. The effective area of the membranes were∼65 mm2 with a thicknesses of 0.07 cm. Helium was applied at one side as the sweep gas with a rate of 100 ml min−1 and the other side was exposed to air. The overall resistance to oxygen permeation was calculated from the following equation:
where
R=ideal gas constant
F=Faraday constant
S=valid area of the membrane
=oxygen permeation flux
=oxygen partial pressure at the side of membrane exposed to air
=oxygen partial pressure at the sweep side
It was assumed that bulk ionic conduction dominated the oxygen permeation process because of the relative thickness of the membranes, and therefore Roverall is roughly equal to Rionic. Hence, the ionic conductivity of the sample was estimated according the following equation:
Where L=the thickness of the membrane.
The ionic transference (tion) of the samples were calculated using the following equation:
Where σtotal and σion are the total electrical and ionic conductivity, respectively.
Thermal gravimetric analysis was performed by PerkinElmer STA6000 to monitor the mass change of SCNT, SCT20 and SCN20 in flowing air from 200 to 800 °C and also during the abrupt change of atmosphere from flowing air to nitrogen to air at 500 °C. Specimens were pelletized and ground using a mortar and pestle to ensure similar grain size before the test. Samples were first gradually heated to 200 °C and held for 1 h to remove absorbed moisture. The temperature was then increased at a rate of 1 °C min−1 to 500 °C in flowing air (20 ml min−1). Subsequently, the flowing gas was abruptly switched to nitrogen, and this condition remained for 2 h until the sample weight stabilized. Then, the atmosphere was switched back to air and the mass change recorded until equilibrium was reached. The rate of weight change was estimated by:
Where mt is the weight of the sample at time t, Δt is the time interval between two recorded adjacent points.
ORR characterization
Cathode polarization resistance was characterized in a cathode|ceria-based electrolyte|cathode symmetrical cell configuration using electrochemical impedance spectroscopy (EIS) carried out with an Autolab PGSTAT20. The samples were measured at least three times to ensure accuracy. The ceria-based electrolyte was either Sm0.2Ce0.8O1.9 (SDC, from Fuel Cell Materials) or Gd0.1Ce0.9O1.95 (GDC, from Aldrich). The symmetrical cells were fabricated by spraying nitrogen-borne cathode slurries onto both sides of SDC dense disks, followed by calcination at 1,000 °C for 2 h in stagnant air. Cathode slurries were prepared by suspending powder cathodes in isopropyl alcohol. The thicknesses of cathodes were controlled to be around 10 μm, and the active area of each cathode was ∼1.15 cm2. SCNT cathodes with different thicknesses were also fabricated by changing the spraying time. Silver paste was subsequently painted onto both cathode sides as current collector. The symmetrical cell with a silver electrode was fabricated by painting the silver paste onto both sides of the GDC disk, followed by baking at 260 °C for 30 min.
We evaluated the performance of the LT-SOFC using anode-supported button-like single cells. The anode powders were prepared by ball milling the NiO, GDC or SDC, and dextrin (pore former) with a weight ratio of 6:4:1 for 20 h in ethanol. The anode-supported single cells were fabricated by drop coating the GDC slurry onto the surface of the anode disks, which were fabricated by pressing anode powders into disks and sintering at 900 °C for 5 h. The GDC slurry used in drop coating was prepared by suspending the GDC powders in terpineol and ethanol. The coated disks were subsequently sintered at 1,400 °C for 5 h. The fuel cell for SDC-based cell stability test was fabricated using co-press method4. The cathode fabrication was carried out following similar steps to those for producing the symmetrical cell. The mechanisms of the SCNT ORR were studied by fitting the EIS impedance spectra at different pO2 to the Re (R1CPE1) (R2CPE2) equivalent circuit model, where by using the LEVM software. The results are presented in (Supplementary Fig. 12) Re represents the ohmic resistance; (R1CPE1) and (R2CPE2) stand for the two ORR steps at high frequency and low frequency respectively. The rate determining steps of ORR are indicated by a parameter m given as follows50:
Where Rp is the polarization resistance of the corresponding ORR process.
First-principles calculations
First-principles calculations were performed with the Vienna ab initio simulation package (VASP)59,60 using density-functional theory. Ion-electron interactions were treated using projector-augmented-wave potentials61 and a generalized gradient approximation (GGA) in the form of Perdew–Burke–Ernzerhof was adopted to describe electron–electron interactions62. The GGA+U calculations were performed with the simplified spherically averaged approach applied to d electrons, where the coulomb (U) and exchange (J) parameters are combined into the single parameter Ueff (Ueff=U−J), which was set to 0.8 eV in these calculations. Electron wave functions were expanded using plane waves with an energy cut-off of 520 eV. The Kohn–Sham equation was solved self-consistently with a convergence of 10−5. The Brillouin zone was sampled using a 3 × 3 × 3 k-point grid. The stoichiometry of the simulated systems was set to SrCo0.75Nb0.25O3, SrCo0.75Ta0.25O3 and SrCo0.75Nb0.125Ta0.125O3, respectively, due to computational limitation, and the Nb and Ta in SCNT are regarded as ordered instead of randomly distributed for simplification. The formation energy of an oxygen vacancy was calculated from the energy difference between the total energy of the VO-containing sample and sum of the total energy of pristine sample and the chemical potential of an oxygen atom in an O2 molecule. The minimum energy pathway for VO migration was determined using a climbing image nudged band method. (CNBE)63,64 implemented in the VASP code.
Data availability
The data that support the findings of this study are available from the corresponding authors upon reasonable request.
Additional information
How to cite this article: Li, M. et al. A niobium and tantalum co-doped perovskite cathode for solid oxide fuel cells operating below 500 °C. Nat. Commun. 8, 13990 doi: 10.1038/ncomms13990 (2017).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Wachsman, E. D. & Lee, K. T. Lowering the temperature of solid oxide fuel cells. Science 334, 935–939 (2011).
Minh, N. Q. Ceramic fuel cells. J. Am. Ceram. Soc. 76, 563–588 (1993).
Hibino, T. et al. A low-operating-temperature solid oxide fuel cell in hydrocarbon-air mixtures. Science 288, 2031–2033 (2000).
Shao, Z. P. & Haile, S. M. A high-performance cathode for the next generation of solid-oxide fuel cells. Nature 431, 170–173 (2004).
Steele, B. C. & Heinzel, A. Materials for fuel-cell technologies. Nature 414, 345–352 (2001).
Lee, J. G., Park, J. H. & Shul, Y. G. Tailoring gadolinium-doped ceria-based solid oxide fuel cells to achieve 2 W cm−2 at 550 °C. Nat. Commun. 5, 4050 (2014).
Yoo, S. et al. Development of double-perovskite compounds as cathode materials for low-temperature solid oxide fuel cells. Angew. Chem. Int. Ed. 53, 13064–13067 (2014).
Zhang, X. et al. Enhanced oxygen reduction activity and solid oxide fuel cell performance with a nanoparticles-loaded cathode. Nano Lett. 15, 1703–1709 (2015).
An, J., Kim, Y.-B., Park, J., Gür, T. M. & Prinz, F. B. Three-dimensional nanostructured bilayer solid oxide fuel cell with 1.3 W/cm2 at 450 °C. Nano Lett. 13, 4551–4555 (2013).
Zhou, W. et al. A highly active perovskite electrode for the oxygen reduction reaction below 600 °C. Angew. Chem. Int. Ed. 52, 14036–14040 (2013).
Lee, K. T., Lidie, A. A., Yoon, H. S. & Wachsman, E. D. Rational design of lower-temperature solid oxide fuel cell cathodes via nanotailoring of co-assembled composite structures. Angew. Chem. Int. Ed. 53, 13463–13467 (2014).
Choi, S. et al. Highly efficient and robust cathode materials for low-temperature solid oxide fuel cells: PrBa0. 5Sr0. 5Co2-xFexO5+δ . Sci Rep 3, 2426 (2013).
Choi, S., Park, S., Shin, J. & Kim, G. The effect of calcium doping on the improvement of performance and durability in a layered perovskite cathode for intermediate-temperature solid oxide fuel cells. J. Mater. Chem. A 3, 6088–6095 (2015).
Chen, D. et al. Compositional engineering of perovskite oxides for highly efficient oxygen reduction reactions. ACS Appl. Mater. Interf. 7, 8562–8571 (2015).
Chiba, R., Yoshimura, F. & Sakurai, Y. An investigation of LaNi1−xFexO3 as a cathode material for solid oxide fuel cells. Solid State Ionics 124, 281–288 (1999).
Adler, S. B. Factors governing oxygen reduction in solid oxide fuel cell cathodes†. Chem. Rev. 104, 4791–4844 (2004).
Richter, J., Holtappels, P., Graule, T., Nakamura, T. & Gauckler, L. Materials design for perovskite SOFC cathodes. Monatshefte Chem. Chem. Monthly 140, 985–999 (2009).
Huang, S., Lu, Q., Feng, S., Li, G. & Wang, C. Ba0.9Co0.7Fe0.2Mo0.1O3–δ: a promising single-phase cathode for low temperature solid oxide fuel cells. Adv. Energy Mater. 1, 1094–1096 (2011).
Xia, C., Rauch, W., Chen, F. & Liu, M. Sm0.5Sr0.5CoO3 cathodes for low-temperature SOFCs. Solid State Ionics 149, 11–19 (2002).
Esquirol, A., Brandon, N. P., Kilner, J. A. & Mogensen, M. Electrochemical characterization of La0.6Sr0.4Co0.2Fe0.8O3 cathodes for intermediate-temperature SOFCs. J. Electrochem. Soc. 151, A1847–A1855 (2004).
Wang, W. G. & Mogensen, M. High-performance lanthanum-ferrite-based cathode for SOFC. Solid State Ionics 176, 457–462 (2005).
Zhou, W., Ran, R. & Shao, Z. Progress in understanding and development of Ba0. 5Sr0. 5Co0. 8Fe0. 2O3−δ -based cathodes for intermediate-temperature solid-oxide fuel cells: a review. J. Power Sources 192, 231–246 (2009).
Jeen, H. et al. Reversible redox reactions in an epitaxially stabilized SrCoOx Oxygen Sponge. Nat. Mater. 12, 1057–1063 (2013).
Kharton, V. et al. Perovskite-type oxides for high-temperature oxygen separation membranes. J. Membr. Sci. 163, 307–317 (1999).
Nagai, T., Ito, W. & Sakon, T. Relationship between cation substitution and stability of perovskite structure in SrCoO3–δ-based mixed conductors. Solid State Ionics 177, 3433–3444 (2007).
Cascos, V., Martínez-Coronado, R. & Alonso, J. A. New Nb-doped SrCo1−xNbxO3−δ perovskites performing as cathodes in solid-oxide fuel cells. Int. J. Hydrogen Energy 39, 14349–14354 (2014).
Zhou, W., Jin, W. Q., Zhu, Z. H. & Shao, Z. P. Structural, electrical and electrochemical characterizations of SrNb0.1Co0.9O3-δ as a cathode of solid oxide fuel cells operating below 600°C. Int. J. Hydrogen Energy 35, 1356–1366 (2010).
Aguadero, A., Pérez-Coll, D., Alonso, J. A., Skinner, S. J. & Kilner, J. A new family of Mo-doped SrCoO3−δ perovskites for application in reversible solid state electrochemical cells. Chem. Mater. 24, 2655–2663 (2012).
Aguadero, A. et al. SrCo0.95Sb0.05O3−δ as cathode material for high power density solid oxide fuel cells. Chem. Mater. 22, 789–798 (2009).
Aguadero, A. et al. SrCo 1− xSbx O 3− δ perovskite oxides as cathode materials in solid oxide fuel cells. J. Power Sources 192, 132–137 (2009).
Li, M., Zhou, W., Xu, X. & Zhu, Z. SrCo0.85Fe0.1P0.05O3−δ perovskite as a cathode for intermediate-temperature solid oxide fuel cells. J. Mater. Chem. A 1, 13632–13639 (2013).
Hancock, C. A., Slade, R. C. T., Varcoe, J. R. & Slater, P. R. Synthesis, structure and conductivity of sulfate and phosphate doped SrCoO3 . J Solid State Chem 184, 2972–2977 (2011).
Aguadero, A. et al. Structural and electrical characterization of the novel SrCo0.9Sb0.1O3–δ perovskite: evaluation as a solid oxide fuel cell cathode material. Chem. Mater. 19, 6437–6444 (2007).
Zhu, Y., Sunarso, J., Zhou, W., Jiang, S. & Shao, Z. High-performance SrNb0.1Co0.9-xFexO3-δ perovskite cathodes for low-temperature solid oxide fuel cells. J. Mater. Chem. A 2, 15454–15462 (2014).
Bahl, M. K. ESCA studies of some niobium compounds. J. Phys. Chem. Solids 36, 485–491 (1975).
Ho, S. F., Contarini, S. & Rabalais, J. W. Ion-beam-induced chemical changes in the oxyanions (Moyn-) and oxides (Mox) where M=Chromium, molybdenum, tungsten, vanadium, niobium and tantalum. J. Phys. Chem. 91, 4779–4788 (1987).
Adler, S. et al. Local structure and oxide-ion motion in defective perovskites. Solid State Ionics 68, 193–211 (1994).
Iwahara, H. in Perovskite Oxide for Solid Oxide Fuel Cells (ed. Ishihara, T.) (Springer, 2009).
Yan, A., Maragou, V., Arico, A., Cheng, M. & Tsiakaras, P. Investigation of a Ba0.5Sr0.5Co0.8Fe0.2O3-δ based cathode SOFC. II. The effect of CO2 on the chemical stability. Appl. Catal. B Environ. 76, 320–327 (2007).
Shao, Z. P. et al. A thermally self-sustained micro solid-oxide fuel-cell stack with high power density. Nature 435, 795–798 (2005).
Zhou, W. et al. Novel B-site ordered double perovskite Ba2Bi0.1Sc0.2Co1.7O6-x for highly efficient oxygen reduction reaction. Energy Environ. Sci. 4, 872–875 (2011).
Zhou, W., Shao, Z., Ran, R. & Cai, R. Novel SrSc0.2Co0.8O3−δ as a cathode material for low temperature solid-oxide fuel cell. Electrochem. Commun. 10, 1647–1651 (2008).
Li, M., Zhou, W., Peterson, V. K., Zhao, M. & Zhu, Z. A comparative study of SrCo0.8Nb0.2O3-δ and SrCo0.8Ta0.2O3-δ as low-temperature solid oxide fuel cell cathodes: effect of non-geometry factors on the oxygen reduction reaction. J. Mater. Chem. A 3, 24064–24070 (2015).
Brandon, N. P., Skinner, S. & Steele, B. C. H. Recent advances in materials for fuel cells. Annu. Rev. Mater. Res. 33, 183–213 (2003).
Kilner, J. A. & Brook, R. J. A study of oxygen ion conductivity in doped non-stoichiometric oxides. Solid State Ionics 6, 237–252 (1982).
Sammells, A. F., Cook, R. L., White, J. H., Osborne, J. J. & MacDuff, R. C. Rational selection of advanced solid electrolytes for intermediate temperature fuel cells. Solid State Ionics 52, 111–123 (1992).
Adler, S. B. Factors governing oxygen reduction in solid oxide fuel cell cathodes. Chem. Rev. 104, 4791–4844 (2004).
Wang, L., Merkle, R. & Maier, J. Surface kinetics and mechanism of oxygen incorporation into Ba1−xSrxCoyFe1−yO3−δ SOFC microelectrodes. J. Electrochem. Soc. 157, B1802–B1808 (2010).
Etsell, T. H. & Flengas, S. N. Overpotential behavior of stabilized zirconia solid electrolyte fuel cells. J. Electrochem. Soc. 118, 1890–1900 (1971).
Takeda, Y., Kanno, R., Noda, M., Tomida, Y. & Yamamoto, O. Cathodic polarization phenomena of perovskite oxide electrodes with stabilized zirconia. J. Electrochem. Soc. 134, 2656–2661 (1987).
Wang, D. Y. & Nowick, A. S. Cathodic and anodic polarization phenomena at platinum electrodes with doped CeO2 as electrolyte I. Steady-state overpotential. J. Electrochem. Soc. 126, 1155–1165 (1979).
Cai, Z., Kuru, Y., Han, J. W., Chen, Y. & Yildiz, B. Surface electronic structure transitions at high temperature on perovskite oxides: the case of strained La0.8Sr0.2CoO3 thin films. J. Am. Chem. Soc. 133, 17696–17704 (2011).
Camaratta, M. & Wachsman, E. Silver–bismuth oxide cathodes for IT-SOFCs; Part I—microstructural instability. Solid State Ionics 178, 1242–1247 (2007).
Sarikaya, A., Petrovsky, V. & Dogan, F. Silver composites as highly stable cathode current collectors for solid oxide fuel cells. J. Mater. Res. 27, 2024–2029 (2012).
Chen, Y. et al. Role of silver current collector on the operational stability of selected cobalt-containing oxide electrodes for oxygen reduction reaction. J. Power Sources 210, 146–153 (2012).
Liss, K.-D., Hunter, B., Hagen, M., Noakes, T. & Kennedy, S. Echidna—the new high-resolution powder diffractometer being built at OPAL. Phys. B Condens. Matter 385–386, 1010–1012 (2006).
Toby, B. H. & Von Dreele, R. B. GSAS-II: the genesis of a modern open-source all purpose crystallography software package. J. Appl. Crystallogr. 46, 544–549 (2013).
Zeng, P. et al. Re-evaluation of Ba0.5Sr0.5Co0.8Fe0.2O3−δ perovskite as oxygen semi-permeable membrane. J. Membr. Sci. 291, 148–156 (2007).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Henkelman, G. & Jónsson, H. Improved tangent estimate in the nudged elastic band method for finding minimum energy paths and saddle points. J. Chem. Phys. 113, 9978–9985 (2000).
Henkelman, G., Uberuaga, B. P. & Jónsson, H. A climbing image nudged elastic band method for finding saddle points and minimum energy paths. J. Chem. Phys. 113, 9901–9904 (2000).
Acknowledgements
We appreciate the technical support from the Centre for Microscopy and Microanalysis at the University of Queensland, and at the Australian Centre for Neutron Scattering at ANSTO. This work is financially supported by Australian Research Council (DP130102151) and Mengran Li acknowledges additional financial support from the scholarship from China Scholarship Council. Professor Zhu acknowledges the Open Funding from State Key Laboratory of Material-Oriented Chemical Engineering (No. KL15-04). This work was financially supported by the National Nature Science Foundation of China under contract No. 21576135 and the Youth Fund in Jiangsu Province under contract No. BK20150945, and the Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD).
Author information
Authors and Affiliations
Contributions
Z.Z. and W.Z. directed the research projects; M.L. conducted the experiments and summarized the data; V.K.P. conducted the NPD and performed the refinement; M.Z. and F.L. performed the modelling; all authors discussed the results and contributed to the paper.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures, Supplementary Tables and Supplementary References (PDF 1273 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Li, M., Zhao, M., Li, F. et al. A niobium and tantalum co-doped perovskite cathode for solid oxide fuel cells operating below 500 °C. Nat Commun 8, 13990 (2017). https://doi.org/10.1038/ncomms13990
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms13990
- Springer Nature Limited
This article is cited by
-
2D Ca/Nb-based perovskite oxide with Ta doping as highly efficient H2O2 synthesis catalyst
Nano Research (2024)
-
Synthesis, characterization, and electrochemical properties of Sm0.5Sr0.5Zr1−xNixO3.25−x for solid oxide fuel cell applications
Journal of the Australian Ceramic Society (2023)
-
Surface restructuring of a perovskite-type air electrode for reversible protonic ceramic electrochemical cells
Nature Communications (2022)
-
Enhanced cathodic activity by tantalum inclusion at B-site of La0.6Sr0.4CO0.4Fe0.6O3 based on structural property tailored via camphor-assisted solid-state reaction
Journal of Advanced Ceramics (2022)
-
Perovskite Cathode Materials for Low-Temperature Solid Oxide Fuel Cells: Fundamentals to Optimization
Electrochemical Energy Reviews (2022)