Abstract
The rheological behavior of Cr2O3-containing slags was investigated using a rotating cylinder viscometer and the solid fraction and phases of Cr2O3 in molten slags were also calculated and observed at different temperatures. Furthermore, the viscosities of CaO–SiO2–Cr2O3(–10%Al2O3) slags were measured from 1703 to 1953 K and the influence of Cr2O3 content on the viscosity and rheological behavior of molten slags was investigated. The calculation revealed that the solid fraction of the molten slags varied with the Cr2O3 content and maximum temperature, and the fluid properties transitioned from Newtonian to non-Newtonian behavior when the solid fraction reached 5%. Moreover, the increase in Cr2O3 content led to an increase in the viscosity as the slags displayed Newtonian flow characteristics and a decrease in the viscosity when slags exhibited non-Newtonian flow characteristics. The viscosity results of Cr2O3-containing slag from 1703 to 1953 K and from 1703 to 1813 K were also discussed with the morphologies.
Similar content being viewed by others
References
K.I. Miyamoto, K. Kato, T. Yuki, Tetsu-to-Hagané 88 (2002) 838–844.
X.T. Zeng, C.H. Yuan, H. Xu, J.X. Han, Y. Tian, China Mining (2015) No. 8, 16–22.
M. Kekkonen, H. Oghbasilasie, S. Louhenkilpi, Viscosity models for molten slag, Aalto University, Helsinki, Finland, 2012.
L. Wang, S. Seetharaman, Metall. Mater. Trans. B 41 (2010) 946–954.
M. Allibert, V.D. Eisenhüttenleute, Slag atlas, 2nd ed., Verlag Stahleisen CmbH, Germany, 1995.
C. Feng, M.S. Chu, J. Tang, Y.T. Tang, Z.G. Liu, Steel Res. Int. 87 (2016) 1274–1283.
K.X. Jiao, J.L. Zhang, Z.Y. Wang, C.L. Chen, Y.X. Liu, Steel Res. Int. 88 (2017) 1600296.
C.Y. Sun, X.H. Liu, J. Li, X.T. Yin, S. Song, Q. Wang, ISIJ Int. 57 (2017) 978–982.
J. Qi, C.J. Liu, C. Zhang, M.F. Jiang, Metall. Mater. Trans. B 48 (2017) 11–16.
L. Wang, C. Zhang, D.X. Cai, J.Q. Zhang, Y. Sasaki, O. Ostrovski, Metall. Mater. Trans. B 48 (2017) 516–526.
J.X. Gao, G.H. Wen, T. Huang, P. Tang, Q. Liu, J. Non-Cryst. Solids 435 (2016) 33–39.
E.Z. Gao, W.L. Wang, L. Zhang, J. Non-Cryst. Solids 473 (2017) 79–86.
L. Zhang, W.L. Wang, S.L. Xie, K.X. Zhang, II. Sohn, J. Non-Cryst. Solids 460 (2017) 113–118.
T. Talapaneni, N. Yedla, S. Pal, S. Sarkar, Metall. Mater. Trans. B 48 (2017) 1450–1462.
R. Xu, J. Zhang, X. Fan, W. Zheng, Y. Zhao, ISIJ Int. 57 (2017) 1887–1894.
Z.M. Yan, X.W. Lv, D. Liang, J. Zhang, C.G. Bai, Metall. Mater. Trans. B 48 (2017) 1092–1099.
R.Z. Xu, J.L. Zhang, R.Y. Ma, K.X. Jiao, Y.A. Zhao, Steel Res. Int. 89 (2017) 1700353.
X.F. Zhang, T. Jiang, X.X. Xue, B.S. Hu, Steel Res. Int. 87 (2016) 87–94.
E. Minami, M. Amatatsu, N. Sano, Tetsu-to-Hagané 73 (1987) S871.
G.B. Qiu, L. Chen, J.Y. Zhu, X.W. Lv, C.G. Bai, ISIJ Int. 55 (2015) 1367–1376.
C. Xu, W.L. Wang, L.J. Zhou, S.L. Xie, C. Zhang, Metall. Mater. Trans. B 46 (2015) 882–892.
W.J. Huang, Y.H. Zhao, S. Yu, L.X. Zhang, Z.C. Ye, N. Wang, M. Chen, ISIJ Int. 56 (2016) 594–601.
R.Z. Xu, J.L. Zhang, Z.Y. Wang, K.X. Jiao, Steel Res. Int. 87 (2016) 1–7.
Q.H. Li, J.T. Gao, Y.L. Zhang, Z.Q. An, Z.C. Guo, Metall. Mater. Trans. B 48 (2017) 346–356.
L. Forsbacka, L. Holappa, in: VII International Conference on Molten Slags, Fluxes and Salts, The South African Institute of Mining and Metallurgy, Johannesburg, South Africa, 2004, pp. 129–136.
L. Forsbacka, L. Holappa, A. Kondratiev, E. Jak, Steel Res. Int. 78 (2007) 676–684.
L. Forsbacka, Experimental study and modelling of viscosity of chromium containing slags, Helsinki University of Technology, Helsinki, Finland, 2007.
K.C. Mills, L. Yuan, Z. Li, G.H. Zhang, K.C. Chou, High Temp. Mater. Process. 31 (2012) 301–221.
T.S. Kim, J.H. Park, ISIJ Int. 54 (2014) 2031–2038.
K. Wu, W. Qian, S.J. Chu, Y. Wang, J. Univ. Sci. Technol. Beijing 2 (1999) 150–153.
L. Forsbacka, Experiences in slag viscosity measurement by rotation cylinder method, Helsinki University of Technology, Helsinki, Finland, 2015.
M. Chen, S. Raghunath, B. Zhao, Metall. Mater. Trans. B 44 (2013) 820–827
Z. Kalicka, E. Kawecka-Cebula, K. Pytel, Arch. Metall. Mater. 54 (2009) 179–187.
L. Forsbacka, L. Holappa, T. Iida, Y. Kita, Y. Toda, Scand. J. Metall. 32 (2003) 273–280.
L. Forsbacka, L. Holappa, Scand. J. Metall. 33 (2004) 61–68.
S. Arrhenius, Zeitschrift für Physikalische Chemie 1 (1887) 285–298.
F. Yuan, Z. Zhao, Y.L. Zhang, J.T. Gao, T. Wu, ISIJ Int. 60 (2020) 613–615.
T. Wu, F. Yuan, Y.L. Zhang, ISIJ Int. 58 (2018) 367–370.
K. Mills, Southern African Pyrometallurgy 2011 (2011) No. 3, 1–52.
A. Einstein, Ann. Phys. 34 (1911) 591–592.
R. Roscoe, J. Appl. Phys. 3 (1952) 267–269.
Acknowledgements
The authors would like to express appreciation to the National Natural Science Foundation of China (No. U1960201) and National Key R&D Program of China (No. 2019YFC1905701) for their financial support of this research.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Yuan, F., Zhao, Z., Zhang, Yl. et al. Influence of Cr2O3 content on viscosity and rheological behavior of Cr2O3-containing slags. J. Iron Steel Res. Int. 29, 601–611 (2022). https://doi.org/10.1007/s42243-021-00679-y
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s42243-021-00679-y