Abstract
Three types of aluminum alloys such as AlSi7Mg, AlSi12Cu2MgNi and AlZn4 are refined by introducing nanoparticles of high melting temperature compounds—nitrides and carbides as well as diamonds in the melt. Their influence on microstructure, mechanical and some electrochemical properties of castings of these alloys is investigated. It is established that the microstructure is refined, the porosity is decreased, and some mechanical and electrochemical properties such as protection potential in drinking water are increased. The mechanism of grain refinement and silicon modification is discussed.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Nanosized particles (NP) are used as inoculants for refining the metal microstructure and improving the mechanical properties of products in the last years.1 – 5 Powders of high melting temperature (2000–3000 °C) compounds, nitrides, carbides, borides, etc. with nanodimensions, are introduced in the molten metal. They are obtained usually by means of plasma chemical synthesis and are covered with metal protector. When a homogenous introduction of nanopowders is reached, a local overcooling and volume crystallization conditions are created and the nanoparticles become active centers of crystallization. The investigations of refined with nanoparticles metal alloys show that the mechanical properties (tensile strength and specific elongation1–5) as well as the corrosion and abrasive resistance6 increase. Nanoparticles increase the part of the surface energy in the total energetical balance of an alloy which determines the phase transformations. Most of the nanoparticles have low wettability, and so it is difficult to be wet by the melts. For this reason, they are clad with metal protector. Most of the existing studies are performed on Al alloys,1 , 5 , 7 – 10 Mg alloys,11 , 12 cast iron4 – 6 , 13 and some on steels with specific application.3 – 5 This work enriches the investigations on castings of three types of aluminum alloys refined with nanoparticles.
Aim: The aim of the present work was to investigate the influence of some types of nanoparticles on the structure and properties of aluminum alloys castings.
Experimental
Production of Nanopowders
High melting temperature compounds in form of nanopowders are obtained by plasma chemical synthesis. Nanopowders of TiCN, SiC, TiN and AlN are produced by Neomat CO, Latvija and the Institute of Theoretical and Applied Mechanics—Siberian Branch of RAS. They are passivated with oleic acid for atmospheric influence protection. In order to reach better wettability, the nanoparticles are clad with metal protector (Ni, Cr, Fe, Al, Cu, etc.). This is realized by mechanical and chemical processing in planetary mills or free-current method.14
For refining, aluminum alloys could be used also diamond nanopowders (ND). They are obtained by detonation technology and are clad with metal protector using free-current method.
NP of SiC clad with Cu by free-current method is shown in Figure 1. The presence of larger particles with diameter up to 600 nm as well as smaller ones with diameter up to 100 nm is observed.
Investigated Alloys Castings
Three aluminum alloys castings are investigated, namely “Boat” of AlSi7Mg alloy, piston of AlSi12Cu2MgNi alloy and anode, protector of AlZn4 alloy, as given in Table 1.
AlSi7Mg is refined with:
-
0.05 % AlN and cladding metals Al + Cu
-
0.1 % SiC and cladding metal Cu
AlSi12Cu2MgNi is refined with:
-
0.1 % ND + Ag
-
0.1 % SiC + Cu
-
0.1 % SiC + Cu + 0.03 % AlN + Al [ultrasonic dispersion (USD)]
AlZn4 is refined with:
-
0.05 % AlN + Al (USD)
-
0.1 % ND + Ag.
Technology of Nanoparticles Addition and Casting with and Without Nanoparticles
The technology of NP introduction and casting “Boat” of AlSi7Mg alloy consists in:
-
Melting the Al alloy in electric-resistance furnace with crucible capacity of 2.5 kg;
-
Degassing molten metal at 730–740 °C by means of blow-through with argon through graphite tube with flow 1 l/min for 5 min;
-
Introducing NP wrapped in aluminum foil and capsulated in aluminum cartridge in the melt at 720–740 °C and mechanical stirring with Ti-mixer for 3–5 min (rotational speed—up to 150 min−1);
-
Casting in metal mold.
Castings for pistons with 45 mm diameter and 0.17 kg weight of AlSi12Cu2MgNi alloy are produced by direct squeeze casting. This method assures high crystallization rate which means fine microstructure. The castings are designed for pistons with diameter 38–40 mm for racing motorcycles and carting engines with 50 cm3 volume, air cooling and velocity up to 12,000 rpm.
The castings with and without NP are produced in the following conditions:
-
Melting the Al alloy in furnace with capacity of 6 kg;
-
Temperature of the melt in the furnace 730–740 °C;
-
Molten metal degassing by means of blow-through with argon through graphite tube for 3–5 min;
-
Temperature of the mold and the punch 150–160 °C;
-
Pressing pressure during crystallization—188 MPa;
-
Time from the end of pouring up to applying pressure 3–4 s;
-
Time of applying pressure 20 s.
The technology of introducing NP and casting anode—protector of AlZn4 alloy—consists in:
-
Obtaining AlZn4 alloy in electric-resistance furnace with crucible capacity of 2.5 kg;
-
Melt degassing at 730–740 °C by means of blow-through with argon through graphite tube for 3–6 min;
-
Introducing NP, wrapped in aluminum foil and capsulated in aluminum cartridge in the melt at 740–750 °C and mechanical stirring melt with Ti-mixer for 3–5 min (rotational speed—up to 150 min−1);
-
The as-obtained alloy is cast according to15 in bi-seat metal mold at melt temperature 720–725 °C and mold temperature 150–160 °C.
Investigation of Microstructures, Mechanical and Electrochemical Characteristics of Samples from Castings
Metallographic samples are prepared by standard procedure consisting in wet grinding and mechanical polishing. The microstructure of AlSi7Mg and AlSi12Cu2MgNi samples is revealed with 0.5 % water solution of HF. The microstructure of AlZn4 samples is revealed by means of electrolytic etching. The microstructure is characterized by means of metallographic microscope PolyvarMet at magnifications up to 1000×. The quantitative metallographic analysis is carried out by automatic image analyzing system “Olympus MicroImage.” The dendrite arm spacing (DAS), domain and grain size are determined. Si crystals size control is performed. The microhardness of specimens is measured by means of the device MicroDuromat 4000 with load of 10 g, time for reaching the load 10 s and hold time 10 s.
The mechanical properties are determined by standard procedure.
The density d of the melts is measured using gravimetric method. The theoretical density (d 0 = 2.7050 g/cm3) of the melts is calculated via additive approach based on the densities and concentrations of components. The porosity P (%) is defined through the formula:
The installation for obtaining polarization curves and thus estimating electrochemical properties is shown in Figure 2. The polarization curves present the dependence of potential on density of polarization current [E = f(i)].
The anode polarization potential is determined at a current density of 5 A/m2
The investigations held at current density 5 A/m2 gave a possibility to determine the anode current density at which starts and ends the fast polarization. As-received experimental data showed that at anode current density i a = 0.01 mA/cm2 fast anode polarization starts. Based on these data, we chose as an anode current density i a = 12 μA/cm2. The testing temperatures are 20, 30, 40, 50, 60, 70, 80 and 90 °C.
After measuring the potential at a given temperature, the next higher temperature is set using a thermostat. The time for reaching needed temperature is from 12 to 15 min. To make sure that the temperature in the thermostat and the voltaic cell is equalized as well as to reach the equilibrium potential, it is put on hold for another 45 min—i.e., the measured potential is per hour. The thermostat and galvanic cell temperature control is held via tarred and tested immersion thermocouple with precision of 0.5 °C.
The potential of anode alloys at a given current density which is equal or higher than the one taken for a minimum borderline potential (E min = −980 mV) could be used as protectors. It shall be noticed that according to international standards, the minimum necessary protective potential for low-alloyed steels is as follows: E = −720 to 760 mV at 20 °C and E = −920 mV at 85 °C.
Results and Discussion
Casting “Boat” of AlSi7Mg Alloy
The investigated casting called “Boat” is a detail of a power-transmission network, as shown in Figure 3.
The microstructure of samples from casting “Boat” before heat treatment is investigated in Dimitrova et al.9 In the present work, we have investigated the microstructure, physical and mechanical properties of casting “Boat” after heat treatment (HT). Castings without NP (Nr 1) and with NP (Nr 2 and 3) are treated according to regime T6:
-
homogenization at 535 ± 3 °C—6 h
-
water quenching at 25–40 °C
-
aging at 160 ± 3 °C—6 h.
The microstructures are shown in Figure 4. They present dendrites of α-solid solution and eutectic of α-solid solution, Si particles and intermetallic compounds. The microstructure, physical and mechanical characteristics of initial and refined castings “Boat” after HT (regime T6) are given in Table 2. It could be seen that the nanoparticles introducing in the melt lead to microstructure refinement. Both modifiers reduce DAS values with 26 %. The length of Si particles is decreased with 16.5 % by AlN modifier and 26.4 % by SiC comparing with Si particles length of non-modified sample. It could be supposed that the refining effect of used in this case nanoparticles is based on their properties after the metal covering is melted in the molten metal. They have (1) high melting temperature, (2) low reactivity and (3) extremely high sedimentation stability because of their small size and specific surface.16 The energy of Brownian motion is sufficient to ensure the particles with size up to 1 micron to be in permanent movement and not to be settled under gravity.17 Thereby, the nanoparticles act as nucleation centers. According to the known and generally recognized principle of orientation and size matching formulated by Dankov,18 the crystalline lattice of the new phase is oriented relative to the initial phase so that the arrangement of atoms between lattices in both phases achieves maximum similarity and that the lattice atoms underwent minimal displacement. The crystal structure of SiC (β, which is used by us) is cubic with lattice parameter a = 4.3596 Å. The Al one is also cubic with a = 4.046 Å. The difference between lattice constants is 7.19 % < 10 %, so the requirement for orientation and size matching is fulfilled and the SiC particles could be substrate on which the Al crystals generate. It could be assumed that this requirement is not obligatory for nanomodifiers since the AlN does not fulfill it, but the microstructure is refined. Such a finding is made in Stanev et al.19 where diamond nanopowder is used as modifier for AlSi7Mg, and although its crystalline constant differs with 12 % from Al one, the grains are refined. Proving or disproving this assumption requires further research on crystal lattice level. We suppose the Si particles are refined and rounded because of diminished volumes between dendrite arms (DAS) where the particles grow. Nanoparticles have a double-modifying effect: firstly, they serve as centers of crystallization, and secondly, being very numerous in number and being a long time in a suspended state, they block the diffusion of the respective atoms to emerging and growing crystals that in the end contributes to a fine-grained structure formation.17 , 20 It is found that irrespective of the chemical composition of the NP, their crystal system, crystal lattice constants, density, melting temperature and other parameters, they all have similar modifying effect.20
As a result of NP introducing in the melt of AlSi7Mg, microstructure refinement is obtained and mechanical properties are improved. In the case of AlN using as modifier, the mechanical characteristics are raised with several percent, as given in Table 2. The elongation increases mostly with 60 %. That is due especially to the Si particles length reduction with 26.4 %.
The influence of NP on porosity and quality index Q of casting “Boat” is presented in Figure 5. The quality index Q is calculated by the formula:21
It is noted that both modifiers reduce the porosity significantly from about 1 to 0.4 %. The presence of a sufficient quantity of nanoparticles leads to the emergence of smaller crystals and thus assures greater density of the casting.
After introducing 0.05 % AlN + Al + Cu and 0.1 % SiC + Cu in AlSi7Mg alloy, it could be seen:
-
refining microstructure—DAS decreases with 26 %;
-
decreasing porosity up to 70 %. The values are smaller than 0.5 % and the requirements for casting density are satisfied;
-
increasing yield strength with 7 % and elongation up to 60 %;
-
tensile strength changes less. More favorable is the influence of 0.1 % SiC + Cu addition;
-
effect of NP influence on the microstructure and properties after HT is less compared to this one before the HT;
-
HB > 80 in all zones of casting and meets the requirements;
-
values of quality index Q increase with 7–14 % and surpass 400 MPa. This is sufficient to assure 107 cycles fatigue endurance at load 70–80 MPa, which is usually required for dynamic loaded parts and proves increased reliability of castings with NP addition.
All this means that nanopowder introducing in the melt of AlSi7Mg alloy leads to mechanical properties and total quality of castings improvement.
AlSi12Cu2MgNi Alloy
The microstructure of this alloy consists also of dendrites of α-solid solution, Al15(FeMn)3Si2 phase—primary particles and eutectic of α-solid solution, Al15(FeMn)3Si2 phase particles and intermetallic compounds,22 as shown in Figure 6. The results from measuring microstructure parameters and mechanical testing the pistons before and after heat treatment are shown in Table 3.
NP addition leads to decreasing DAS up to 25 %. In cast state, R m increases with 3–6 % and A 5 with 75 %. After HT, the increasing is less: R m is up to 4 % and A 5 is up to 60 %. The hardness changes insignificantly. After HT, HB > 150 and fulfills the requirements. SiC + AlN has stronger influence than other investigated nanoparticles.
AlZn4 Alloy
Investigation of Castings “Anode Protector” of AlZn4 Alloy with NP Addition
The influence of nanosized AlN particles and nanodiamonds on the microstructure and electrochemical characteristics of “Anode protector” AlZn4 casting is investigated. It is designed for corrosion protection of enamel tank water heater and hulls of ships.
It is seen that the nanosized powders, AlN and ND + Ag added in AlZn4 alloy, influence on the electric potential of the protector alloy increasing the potential electronegativity as follows:
-
The influence of both NP in drinking water after 1-h stabilization occurs up to 50 °C (E increases with 5–9 %). Then the values reach the values of initial alloy. Since we do not know other publications related to the electrochemical behavior of nanomodified alloys, the explanation for the changes above 60° we could give after conducting further research in this direction;
-
The protective potential E of alloys with NP addition after 10 h in drinking water is higher than the initial one in whole temperature range (20–90 °C). Its increasing at 85 °C reaches 1.6 %;
-
The protective potential E of all investigated alloys at 85 °C is higher than the accepted by us minimal limitrophe potential (E min = −980 mV). It means that the cast anodes can serve as protectors.
The microstructure characteristics and density of AlZn4 castings designed for protectors are shown in Table 6.
Macro- and microstructures of AlZn4 castings designed for protectors are shown in Figure 8. It is visible that the structure is refined after NP addition. The values of mean diameter of the domains decrease with 37.2 % and the mean grain diameter with 23 % (Table 6).
The grains after NP addition are more rounded (1—ideal circle) that means more equal axed which is prerequisite for increasing protective potential. There is a tendency of raising density. The increase in density is also beneficial for the potential. The microhardness increases with 7 %. It could be concluded that the protective potential is structurally sensitive property.
Conclusions
-
1.
After introducing NP in AlSi7Mg, it is established that microstructure is refined (DAS decreases with 26 %). Porosity is decreased (up to 70 %). The values are smaller than 0.5 % so they satisfy the requirements for casting density. Yield strength is increased with 7 % and specific elongation up to 60 %. Tensile strength changes less. Most favorable is the influence of 0.1 % SiC + Cu addition. NP influence on microstructure and properties after HT is less compared to the one before HT. HB > 80 in all zones of casting and requirements are met. Values of quality index Q increase (with 7–14 %) and surpass 400 MPa. This is sufficient for dynamic loaded parts.
-
2.
NP addition leads to decreasing DAS (up to 25 %) in AlSi12Cu2MgNi alloy. In cast state, R m increases (with 3–6 %) and A 5 too (with 75 %). After heat treatment, the increasing is less (R m raises up to 4 % and A 5 up to 60 %). The hardness changes insignificantly. HB increases (over 150) and fulfills the requirements.
-
3.
The influence of NP in AlZn4 alloy on its electrochemical characteristics as well as on the microstructure is established. There is a tendency towards an increasing of these characteristics. The increasing protection potential at 80–85 °C in drinking water reaches 1.5–1.6 %. The microstructure is refined. The mean diameter of domains decreases (up to 51.5 %) and the mean grain diameter too (up to 23 %). After nanodiamond addition, the microhardness increases (up to 7 %). The density increases too.
-
4.
The carried out investigation affirms the statement that the nanoparticles introduced in the melt of aluminum alloys act as centers of crystallization refining the microstructure. As a result, the microstructure susceptible mechanical end electrochemical properties are improved.
-
5.
The mechanism of grain refining is discussed.
References
N.E. Kalinina., O.A. Kavatz, V.T. Kalinin, Technological properties improvement of cast aluminum alloys after modifying with nanodispersed particles. Airsp. Tech. Technol. 4(4), 17–21 (2010) (in Russian)
N.E. Kalinina et al., Nanomaterials and Nanotechnologies: Obtaining, Structure, Application (Publishing Hous U.V. Makovetskiy, Dnepropetrovsk, 2012)
R. Lazarova, R.H. Petrov, V. Gaydarova, A. Davidkov, A. Alexeev, M. Manchev, V. Manolov, Microstructure and mechanical properties of P265GH cast steel, after modification with TiCN particles. Mater. Des. 32, 2734–2741 (2011)
R. Lazarova, P. Kuzmanov, R. Dimitrova, A. Cherepanov, V. Manolov, Properties of 110Γ13LЛ steel and SCh 25 cast iron modified by refractory nanopowder. Steel Transl. 42(4), 298–301 (2012)
P. Kuzmanov, R. Dimitrova, R. Lazarova, A. Cherepanov, S. Popov, R. Petrov, V. Manolov, Investigation of the structure and mechanical properties of castings of alloy AlSi7Mg, cast irons GG15 and GG25 and steel GX120Mn12, modified by nanosized powders. Proc. Inst. Mech. Eng., Part N: J. Nanoeng. Nanosyst. 228(1), 11–18 (2014)
M. Razavi, M.R. Rahimipour, A.H. Rajabi-Zamani, Effect of nanocrystalline TiC powder addition on the hardness and wear resistance of cast iron. Mater. Sci. Eng., A 454–455, 144–147 (2007)
R. Dimitrova, P. Kuzmanov, R. Lazarova, V. Manolov, Investigation of nanopowders application in metal casting. Adv. Mater. Res. 629, 284–291 (2013)
K. Borodianskiy, M. Zinigrad, A. Gedanken, Aluminum A356 reinforcement by carbide nanoparticles. J. Nano Res. 13, 41–46 (2011)
R. Dimitrova, S. Stanev, A. Velikov, A. Cherepanov, R. Lazarova, N. Bojanova, Investigation of AlSi7Mg casting refined with SiC nano-powder. J. Mater. Sci. Technol. 20(4), 319–326 (2012)
K. Borodianskiy, A. Kossenko, M. Zinigrad, Improvement of the mechanical properties of Al–Si alloys by TiC nanoparticles. Metall. Mater. Trans. A 44(11), 4948–4953 (2013)
M. Habibnejad-Korayem, R. Mahmudi, W.J. Poole, Enhanced properties of Mg based nano-composites reinforced with Al2O3 nano-particles. Mater. Sci. Eng., A 519, 198–203 (2009)
M. Habibnejad-Korayem, R. Mahmudi, H.M. Ghasemi, W.J. Poole, Tribological behavior of pure Mg and AZ31 magnesium alloy strengthened by Al2O3 nanoparticles. Wear 268, 405–412 (2010)
Y. Hou, Y. Wang, Z. Pan, L. Yu, Influence of rare earth nanoparticles and inoculants on performance and microstructure of high chromium cast iron. J. Rare Earths 30(3), 283–288 (2012)
S. Stavrev, Z. Karaguiozova, Formation of Nickel Layer—Covers on Nanodiamond Powder, Nanoscience & Nanotechnology, 7 (Heron Press, Sofia, 2007), pp. 219–221
V. Kovachev, I. Panov, Investigation of the possibility for electrical and chemical characteristics improvement of aluminum protectors. Scientific Announcements of NTUM VI (17), pp. 85–106. ISSN 1310-3946 (1998)
G.G. Krushenko, S.N. Reshetnikova, A.A. Mishin, The mechanism of aluminium–silicon alloys inoculation by nanopowders (at nanopowder of titanium nitride example), in Proceedings from XIV International Scientific Conference “Reshetnev Readings”, Krasnoyarsk, 10-12.11.2010, Part 2, pp. 586–587 (in Russian)
A. Einstein, M. Smoluchowski, Brownian Motion. Translated by K. I. Fedchenko, ed. by B. I. Davidov (ONTI Home Edition of General Technical Literature, 1936), p. 607 (in Russian)
P.D. Dankov, Crystal-chemical mechanism of crystal surface interaction with alien elementary particles. J. Phys. Chem. 20(8), 853–867 (1946). (in Russian)
S. Stanev, R. Lazarova, S. Konstantinova, V. Manolov, Investigation of the effect from AlS7Mg alloy modification with nanopowders by thermal and metallographic analyses, in Proceedings from XXVI International Scientific Conference 65 Years Faculty of Machine Technology, 13-16 September 2010, Sozopol, Bulgaria, pp. 277–282
S.N. Reshetnikova, Ph.D. thesis, http://www.dissercat.com/content/primenenie-nanoporoshkov-khimicheskikh-soedinenii-dlya-povysheniya-fiziko-mekhanicheskikh-kh (in Russian)
M. Drouzy, S. Jacob, M. Richard, Interpretation of tensile results by means of quality index and probable yield strength. AFS Int. Cast Met. J. 45, 43–50 (1980)
M.E. Samoshina, N.A. Belov, S.V. Savchenko, The features of phase composition and microstructure of piston alloys AlSi12CuMgNi and AlSi12Cu2MgNi. Non-ferr. Met. (9) (2012). http://www.rudmet.ru/journal/946/article/14803/
Acknowledgments
This work is financially supported by the Fund “Scientific Researches” at the Ministry of Education, Youth and Science, Project TK01/076.
Author information
Authors and Affiliations
Corresponding author
Additional information
Dedicated to his Eminence Photius—Bishop of Triaditsa on the Occasion of His 60th Birthday.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Lazarova, R., Bojanova, N., Dimitrova, R. et al. Influence of Nanoparticles Introducing in the Melt of Aluminum Alloys on Castings Microstructure and Properties. Inter Metalcast 10, 466–476 (2016). https://doi.org/10.1007/s40962-016-0033-7
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40962-016-0033-7