Nano-Micro Letters

, 10:51 | Cite as

Computational Study of Ternary Devices: Stable, Low-Cost, and Efficient Planar Perovskite Solar Cells

  • Sajid Sajid
  • Ahmed Mourtada Elseman
  • Jun Ji
  • Shangyi Dou
  • Dong Wei
  • Hao Huang
  • Peng Cui
  • Wenkang Xi
  • Lihua Chu
  • Yingfeng Li
  • Bing Jiang
  • Meicheng LiEmail author
Open Access


Although perovskite solar cells with power conversion efficiencies (PCEs) more than 22% have been realized with expensive organic charge-transporting materials, their stability and high cost remain to be addressed. In this work, the perovskite configuration of MAPbX (MA = CH3NH3, X = I3, Br3, or I2Br) integrated with stable and low-cost Cu:NiO x hole-transporting material, ZnO electron-transporting material, and Al counter electrode was modeled as a planar PSC and studied theoretically. A solar cell simulation program (wxAMPS), which served as an update of the popular solar cell simulation tool (AMPS: Analysis of Microelectronic and Photonic Structures), was used. The study yielded a detailed understanding of the role of each component in the solar cell and its effect on the photovoltaic parameters as a whole. The bandgap of active materials and operating temperature of the modeled solar cell were shown to influence the solar cell performance in a significant way. Further, the simulation results reveal a strong dependence of photovoltaic parameters on the thickness and defect density of the light-absorbing layers. Under moderate simulation conditions, the MAPbBr3 and MAPbI2Br cells recorded the highest PCEs of 20.58 and 19.08%, respectively, while MAPbI3 cell gave a value of 16.14%.


Perovskite solar cells Copper-doped nickel oxide Zinc oxide Simulation 

1 Highlights

  • Simulation study of perovskite solar cells with pin structure in the configuration Cu:NiO x /MAPbX/ZnO/Al.

  • Solar cells with MAPbI2Br photoactive layers exhibit best conversion efficiency and show promise of high thermal stability.

  • Simulation results provide a better understanding of the defect density and thickness of the active perovskite layer.

2 Introduction

Since the emergence of organic–inorganic halide perovskite materials as efficient light harvesters, perovskite solar cells (PSCs) have been widely investigated in terms of their power conversion efficiencies (PCEs). Fundamental studies on perovskite materials [1, 2], device architectures [3, 4, 5], fabrication processes [6, 7], and material engineering [8, 9] have assisted the rapid development of PSCs. Consequently, PCEs greater than 22% have been achieved, as certified by National Renewable Energy Laboratory (NREL) [10]. Presently, the PSC is considered as one of the most promising alternative energy conversion devices in terms of high efficiency and low cost. However, despite the major achievements in scaling efficiency levels in the laboratory ambient, the concern of long-term stability and performance of these solar cells under severe humidity and light illumination conditions as well as the requirement of expensive organic charge-transporting materials (OCTMs) remain critical. In order to achieve high performance and improved stability, several material refinements have been attempted by substituting a mixture of suitable materials in the organic and halide sites (organic site: MA, HC(NH2)2; halide site: I, Br, Cl) [8, 9, 11, 12, 13, 14, 15]. Despite their application in most efficient devices, the expensive OCTMs are limited in use by a tendency to absorb water, difficulty in synthesizing, and inability to manage charge carriers effectively. Use of p-type and n-type inorganic materials would be a long-term solution for constructing stable PSCs more economically [16, 17, 18, 19]. In this context, metal oxide semiconductors are considered chemically stable and highly transparent with tunable energy band levels [20, 21, 22, 23, 24]. They are nontoxic and abundantly available in the earth’s crust for universal use as photovoltaic materials. More attractively, thin layers of these materials have been deposited using low-cost techniques such as spin coating, doctor blading, and spray pyrolysis in ambient atmosphere. However, low charge carrier mobility and fill factor (FF) associated with inorganic HTMs, particularly by the use of NiO x and Cu2O, are deterrents compared to organic HTMs. Highly efficient planar PSCs incorporated with solution-processed copper-doped NiO x as HTMs have been demonstrated by many researchers [25, 26, 27]. These studies revealed that the high conductivities (of HTM/ETM) obtained by doping or managing the charge carrier collection and valence/conduction band matching with perovskite absorber have a positive impact on PCE [6, 26, 28, 29]. In this work, we engaged a one-dimensional software program (wxAMPS), which is widely used for simulating carrier transport in solid-state devices, to derive continuity and Poisson equations from first principles and to analyze the transport behavior of perovskite device structures. From the simulation output, solar cell parameters such as current–voltage characteristics in the dark and, if desired, under illumination can be obtained. For numerical simulation of PSCs such as the TiO2/MAPbI3/spiro-OMeTAD/Au, an effective method has been described by Liu et al. [30], which helps in identifying the optimal operating conditions.

In this context, we were inspired by Cu:NiO x as a hole-transporting layer (HTL) and ZnO as electron-transporting layer (ETL), which are highly conducting, environmental-friendly, and economically fabricable materials, together with Al back contact for integrating MAPbI3, MAPbI2Br, and MAPbBr3 thin layers to a pin configuration. It was required to understand the role of each component and their combined effect so as to achieve incremental improvement in the photovoltaic characteristics of the PSC thus designed. In this endeavor, a theoretical study was performed to identify the optimal conditions of device operation using the simulation software wxAMPS and by employing intra-band and trap-assisted tunneling models for heterojunction analysis. This study represents the first (in our knowledge) numerical simulation of a PSC based on the perovskite series MAPbX (MA = CH3NH3, X = I3, Br3, or I2Br) in conjunction with Cu:NiO x (HTL), ZnO (ETL), and Al counter electrode and is aimed at improving the design of PSCs which are highly efficient, stable, and economical to fabricate.

3 Modeling of Perovskite Solar Cell

In the simulation process, device models were constructed with thin film stacks of glass/FTO/Cu:NiO x /MAPbX/ZnO/Al (MA = CH3NH3, X = I3, Br3, or I2Br) which are illustrated in Fig. 1a, and the corresponding energy band diagrams are shown in Fig. 1b. The paths of generation and recombination of charge carriers in PSCs are shown in Fig. 1c. The charge generation, separation, and extraction processes shown as steps (1), (2), and (3), respectively, are dynamic processes that are favorable for high-performance PSCs. In order to manage the charge collection efficiently, these processes should occur at a much faster rate than that of the recombination process (undesirable), which are shown in steps (4)–(6). For any further optimization and enhancement in photovoltaic parameters, one needs to address the timescale and charge carrier kinetics occurring at different interfaces in PSCs. In this context, three device layouts were created and labeled as devices A, B, and C using MAPbI3, MAPbI2Br, and MAPbBr3 active layers, respectively. The AM1.5G solar spectrum was adopted as the illumination source for the simulation. The light reflectance at the top and bottom contacts was set to 0 and 1, respectively. The material parameters used for the simulation are summarized in Table 1; these were carefully chosen from earlier experimental reports [14, 23, 31]. Capture cross sections of both electrons and holes were set to 1 × 10−16 cm2 which resulted in a carrier diffusion length of ~ 1 μm in light-absorbing materials. The thicknesses of the active layer were set to 0.4 μm for device A and 0.5 μm for devices B and C, respectively, for efficient charge carrier collection. The possibility of Gaussian states that are either donor-like or acceptor-like and which are located anywhere in the bandgap can be predicted by wxAMPS. The donor-like tail states coming out of the valence band can be modeled in wxAMPS by Eq. 1,
$$g_{\text{d}} (E_{1} ) = G_{{{\text{d}}0}} { \exp }^{{\left( {{\raise0.7ex\hbox{${ - E_{1} }$} \!\mathord{\left/ {\vphantom {{ - E_{1} } {E_{\text{d}} }}}\right.\kern-0pt} \!\lower0.7ex\hbox{${E_{\text{d}} }$}}} \right)}}$$
where gd is donor-like tail Gaussian state, E1 is measured positively from the valence band edge (Ev) upward to the point located at x, Ed is the characteristic energy that determines the slope of the tail, and Gd0 represents the density of states. Similarly, the acceptor-like tail states coming out of the conduction band can be modeled by Eq. 2,
$$g_{\text{a}} (E_{2} ) = G_{{{\text{a}}0}} { \exp }^{{\left( {{\raise0.7ex\hbox{${ - E_{2} }$} \!\mathord{\left/ {\vphantom {{ - E_{2} } {E_{\text{a}} }}}\right.\kern-0pt} \!\lower0.7ex\hbox{${E_{\text{a}} }$}}} \right)}} ,$$
where ga is acceptor-like tail Gaussian state, E2 is measured negatively from the conduction band edge (Ec) downward to the same point x, Ea is the characteristic energy that determines the slope of the tail, and Ga0 represents the density of states.
Fig. 1

a Schematic crosssection of pin perovskite solar cells. b Energy band diagram of the corresponding heterojunctions. c Charge generation, separation, and extraction processes. d Simulated JV characteristic curves under AM1.5G illumination at 100 mW cm−2 irradiance

Table 1

Basic material parameters used for the simulation, which were carefully chosen from experimental reports [14, 23, 31]



E g


Nc (conduction band)

Nv (valence band)

μe (cm2/Vs)

μh (cm2/Vs)

Nd (donor conc.) cm−3

Na (acceptor conc.) cm−3






2.8 × 1018

3.9 × 1018



1 × 109

1 × 109

[30, 34, 35]





3 × 1018

4.0 × 1018



1 × 1010

1 × 1010






3.5 × 1018

4.0 × 1019



2.14 × 1017

2.14 × 1017

[14, 36]





2.2 × 1018

1.8 × 1019



1 × 1018







1.6 × 1018

2.9 × 1020




1.5 × 1018


According to Eqs. 1 and 2, the defect energy levels in the simulated thin film materials are located at the center of the bandgap with the Gaussian-type energy distribution (characteristic energy of 0.1 eV). The tail characteristic energy is 0.01 eV with density of band-tail states of 1 × 1014 cm−3 eV−1 [30, 32, 33].

Since the performance of the solar cell is influenced by bimolecular electron–hole recombination rate, two assumptions have been made to understand the bimolecular recombination rate. In the first assumption, the conduction band electrons are directed to empty states in the valence band, a process known as band-to-band or direct recombination RD (also called intrinsic recombination). In the second assumption, electrons and holes recombine through intermediate gap states known as recombination centers or by a process of extrinsic recombination. The latter is labeled as indirect recombination RI or Shockley–Read–Hall recombination. The total recombination term R(x) in the continuity equation takes into account both these processes as a sum of the two components (Eq. 3).
$$R\left( x \right) \, = \, R_{\text{D}} \left( x \right) \, + \, R_{\text{I}} \left( x \right)$$
Additionally, the bimolecular recombination rate simply relies on an overlap of electron and hole wavefunctions, while Auger processes involve transfer of energy and momentum of the recombining electron–hole pair to a third charge carrier. On the other hand, experimental results of THz photoconductivity transients for perovskite materials have been documented [34] which lead to bimolecular and monomolecular charge recombination rates according to Eq. 4,
$$\frac{{{\text{d}}n}}{{{\text{d}}t}} = - \gamma np - \gamma np_{0}$$
where n denotes the photoinduced charge carrier density. The first term on the RHS of Eq. 4 represents bimolecular recombination rate of photogenerated carriers, while the second term denotes monomolecular recombination rate. In addition, the recombination dynamics associated with the free charge carrier density (n) could be described by the following differential equation (Eq. 5) [35],
$$\frac{{{\text{d}}n}}{{{\text{d}}t}} = - k_{3} n^{3} - k_{2} n^{2} - k_{1} n$$
where k3, k2, and k1 represent the decay constants describing Auger recombination, the bimolecular recombination constant, and the rate for monomolecular processes such as trap-assisted charge recombination, respectively. Applying the above equations, the value of the bimolecular recombination rate was approximated to 1 × 10−11 cm3 s−1 in the baseline simulation model as reported for the rates of recombination ranging from 10−11 to 10−9 cm3 s−1 [36, 37]. Further, the interface recombination velocity (S) was evaluated by a numerical approach using the expression given below (Eq. 6).
$$S_{m} = \frac{{\mathop \smallint \nolimits_{\text{int}} R{\text{d}}x}}{m}$$
Here R, int, and m describe the recombination rate within the interface layer, the whole interface layer, and the concentration of holes and electrons, respectively. The values of R and m are estimable from the numerical solution, and the integral of R across the whole interface layer represents the total interface recombination as described in Eq. 3. The surface recombination velocities of electrons and holes at the top and bottom electrodes are estimated from Eq. 6 as 1 × 107 cm s−1. The interface recombination losses in each device configuration could be regulated by introducing two thin interfacial defect layers hypothetically at the HTL/perovskite and ETL/perovskite interfaces [38, 39] as outlined in Table S1. This approach facilitates performance evaluation of the device as also determines the compatibility between theoretical and experimental data by interface engineering [39, 40, 41, 42].

4 Results and Discussions

The motivation to optimize efficiency and durability of PSCs emerged from the need to design a thermally stable perovskite with all-inorganic charge-transporting layers [43, 44, 45, 46]. Using the codified AMPS-1D simulation tool, first-principle calculations were performed to find solutions for continuity and Poisson equations. The software was tweaked to simulate carrier transport in devices with single- and multi-junction formats. This approach allows the researcher to implement optimized structures for microelectronic, photovoltaic, or optoelectronic applications [30, 39, 41, 47].

The modeling process and results have led to a better understanding of the fabrication process and perovskite material stability. The simulated current–voltage (JV) characteristic curves of the devices A, B, and C are given in Fig. 1d. Device A (MAPbI3) showed the lowest PCE of 16.14%, open-circuit voltage (Voc) of 0.964 V, short-circuit current density (Jsc) of 20.87 mA cm−2, and fill factor (FF) of 79%. Devices B (MAPbI2Br) and C (MAPbBr3) yielded the highest PCE values of 19.08 and 20.58%, Voc of 1.098 and 1.107 V, Jsc of 22.53 and 22.99 mA cm−2, and FF of 79.45 and 81.67%, respectively. The simulated values of PCE of devices B and C are nearly consistent with the experimental value of 18.94% as reported by Kim et al. [46]. Notably, the realization of high Voc and FF in devices B and C was attributed to the use of absorber materials with large energy bandgap and low mismatch between the work functions of Cu:NiO x valence band, ZnO conduction band, and the perovskite layer [27, 48, 49]. Hole extraction from the perovskite layer is considered a key process in enhancing photovoltaic performance. The incorporation of halide (Br) in perovskite materials results in rapid hole extraction and low carrier recombination rate by precisely tuning the bandgap [46, 50]. As an added advantage, the long carrier diffusion lengths in such mixed-halide devices yield higher values of FF and PCE. With this in mind, we further investigated the photoelectric behavior of the best devices, namely MAPbI2Br and MAPbBr3 (in lieu of MAPbI3). It can be clearly seen in Fig. 2a that the recombination rate is reduced and the efficiency of charge carrier collection is improved by the application of Br-doped perovskites; the Cu:NiO x (HTM) and ZnO (ETM) layers remained the same in both cases. A relatively small trap-assisted recombination was evident in MAPbI2Br. The above findings are consistent with the experimental results obtained using transient THz spectroscopy [51]. It is also in agreement with the studies of Liu et al. [6] and Liu and Kelly [28] who reported that the high degree of crystallinity in their perovskites helped to minimize the trap density within the material, thus lowering charge recombination and realizing high Voc values. That a low recombination rate corresponds to high Voc is referenced to the results of transient open-circuit voltage decay (OCVD) and intensity-modulated photovoltage spectroscopy (IMVS) measurements [52]. The enhanced device performance is also credited to low series resistance, efficient carrier transport, and absence of Schottky barrier in the charge carrier materials (HTM and ETM) and electrode interfaces [25, 53, 54]. In the following sections, we will discuss specific factors that influence the device performance, namely film thickness, defect density, operating temperature, and bandgap energy of perovskite materials. There is also evidence that the crystal structure and morphology play an important role in the optimization process and in further improvements of device performance.
Fig. 2

a Simulated values of carrier recombination and generation rates in MAPbX (MA = CH3NH3, X = I3, I2Br, or Br3) layers designed with Cu:NiO x (HTM) and ZnO (ETM). bd Simulated JV characteristic curves for different defect densities in the absorber film

4.1 Effect of Defect Density

The number of defects in the absorber material is crucial to the device performance. By effectively managing the generation–recombination rate of the photogenerated carriers within the absorber layer, the Voc of the device can be maximized. The simulated JV curves in Fig. 2b–d illustrate that the defect states present in perovskite films cause a noticeable reduction in Voc, while its effect on Jsc is much less discernible; this is in accordance with experimental results related to Br-doped perovskites [46]. A high degree of crystallinity in experimentally formed perovskite layers results in low trap density, thus reducing charge recombination and realizing high Voc values [6, 28]. It was earlier confirmed that the creation of a Br-rich layer within the tri-iodide perovskite structure enhanced moisture resistance, without sacrificing current density proving that the latter was less susceptible to defect density [55]. However, this resulted in a reduction in Voc. In our study, the Voc of device B (MAPbI2Br) and device C (MAPbBr3) are higher than that of device A (MAPbI3) as shown in Fig. 2c–d. These results clearly establish that the relatively larger bandgap of the perovskite, especially in devices B and C (than in device A), has been effective in lowering the charge recombination rate and is responsible for improving charge extraction as depicted in Fig. 2a [6, 14, 28, 46, 56, 57].

4.2 Effect of Active Layer Thickness

The thickness of the photoactive perovskite layer also has a major role in improving the device performance. If the light-absorbing layer is too thin, the number of photons absorbed is small which will, in turn, give rise to low photocurrents; however, if a very thick perovskite layer is used, it results in low charge carrier extraction efficiency, and losses due to charge recombination become significant. Consequently, optimization of the absorber layer thickness assumes much importance in determining carrier generation and spectral response of the solar cells. Figure 3a shows the variation of PCE of the simulated devices as a function of the perovskite layer thickness. When the thickness was increased progressively in the range from 0.1 to 0.8 μm, the highest value of PCE was obtained for thicknesses of 0.4 for device A and 0.5 μm for devices B and C, respectively. The increase in efficiency is attributed to the increased number of electron–hole pairs generated in the photoactive layer. However, a decrease in efficiency at large thicknesses is due to increase in the recombination of charge carriers within the material before they reach the contact electrode. From the simulated results, which are summarized in Table 2, the thicknesses of 0.4 and 0.5 μm for perovskite layers were deduced as optimum values for achieving the highest PCE. Integrating the perovskite materials with suitable charge-transporting layers such as Cu:NiO x (HTM) and ZnO (ETL), especially in the MAPbI2Br configuration, might serve as an effective method to collect charge carriers at low recombination rate using a specific absorber layer thickness(as illustrated in Fig. 2a). The process of accelerated hole extraction and improved carrier lifetime due to the Br concentration gradient in MAPb(I1−xBr x )3 has been verified by Kim et al. by observing photoluminescence properties in this material [14, 46, 58]. Additionally, the large photocurrents generated in these materials were attributed to the high absorption coefficient of the perovskite layers. We noticed a discrepancy between the simulated and experimental results at large values of thickness beyond the optimized thickness values (0.4 and 0.5 μm) which, we believe, is due to large variations in structure and thickness of the absorber layer in actual devices, which was also reported by Sum and Mathews [59]. Additionally, we found supporting evidence in the reports on planar heterojunction devices that employed higher layer thicknesses in the range of 0.4–0.8 μm for fabricating highly efficient devices. Besides, large carrier diffusion lengths of up to 1 μm have been observed in mixed-halide perovskites which also lends support to the claim that thicker absorber layers can be used [60]. Benefiting from the long carrier diffusion length, perovskite semiconductors possess long carrier diffusion length and a high charge collection efficiency [61]. Therefore, design of a thicker perovskite layer may serve as an effective solution to absorb more photons than that in solution-processed photovoltaic materials [62, 63, 64, 65]. While our simulations have predicted the use of 0.4- and 0.5-μm-thick absorber layers for enhancing the device performance, available experimental data suggest that further increase in thickness may also help to achieve high values of PCE [61, 66, 67].
Fig. 3

a Variation (simulated) of PCE obtained as a function of thickness of photoactive materials. b Variation (simulated) of PCE as a function of operating temperature. c, d Variation (simulated) of photovoltaic parameters as a function of bandgap energy in perovskite materials

Table 2

Simulated photovoltaic characteristics of solar cells measured under standard AM1.5G illumination at 100 mW cm−2 irradiance


Voc (V)

Jsc (mA cm−2)

FF (%)

η (%)

Defect density (cm−3)

Optimized thickness (μm)






1 × 1018







1 × 1018







1 × 1018


4.3 Effect of Operating Temperature

The performance of a PSC implicitly depends on its operating temperature. The standard test temperature (300 K) is generally used for performing simulations, but the operating temperatures in actual conditions are much higher. In this study, the simulation models considered the working temperature of 300 K as listed in Tables 1, 2 and S1. It is worthwhile to note that high temperature often leads to increased stress and deformation in devices which is likely to create more interfacial defects and cause poor inter-connectivity between the layers. Consequently, a high recombination rate prevails which is accompanied by reduction in carrier diffusion length and increase in series resistance [68, 69]. It has been previously reported that increase in temperature will significantly affect the electron and hole concentration, charge carrier mobility, material bandgap, and also device power conversion efficiency. This is illustrated by our simulation results as shown in Fig. 3b. However, it was found that the decrease in PCE can be controlled to a certain extent by incorporating a homogeneous layer of mixed-halide perovskite (Br-substituted perovskite). Kim et al. [27, 46] fabricated a thermally stable Br-doped perovskite solar cell with PCE of 18.94% under high humid conditions (40 − 90%) and retained its efficiency without encapsulation for 28 days. The use of inorganic HTLs and ETLs have established that, by optimizing thermal and chemical stability, improved performance can be realized in PSCs at lower material and processing cost [16, 17, 23, 25, 31, 70, 71].

4.4 Effect of Energy Levels

Incident photon harvesting in a solar cell plays a large role in achieving high photovoltaic performance [72, 73]. Photoactive materials are broadly defined as those capable of responding to light or electromagnetic radiation. The optical absorption can be varied by tuning the bandgap energy of perovskite materials to achieve high device performance [14, 74]. The bandgap of MAPbX3 is considered to be one of the major factors that influence the magnitude of electronegativity difference between the metal cation and the anion in perovskite materials. An increase in the anion electronegativity is likely to diminish the covalent character of the halogen bond with Pb2+ ion and, consequently, result in an increase in the bandgap energy [14, 75]. Changes in composition with respect to the halide ion such as in MAPbI3, MAPbI2Br, and MAPbBr3 are likely to influence the optical properties of the perovskite materials as shown in Fig. S1. The simulated variation in the photovoltaic parameters obtained by changing the bandgap energy of the absorber material from 1.5 to 2.2 eV under optimized conditions is illustrated in Fig. 3c–d. It is clearly seen that with increasing bandgap energy, Voc also increases in all cases. In a previous study related to the wide-bandgap perovskite (MAPb(I1−xBr x )3) solar cell, the results showed an increase in Voc from 1.08 to 1.11 V and improvement of FF from 71 to 74% with thermally stable PCE of 18.94% [46]. The simulation results obtained in this study show an enhancement in FF and Jsc which are consistent with the energy band alignment of HTM and ETM with the absorber layer which can be seen in Figs. 1c and 2a, respectively [26]. These improvements have been attributed to increase in bandgap, reduced radiative recombination, and energy band matching [11, 23, 25, 27, 31, 46].

5 Conclusion

In summary, the configurationally design of the perovskite solar cell MAPbX (MA = CH3NH3, X = I3, Br3, or I2Br) was systematically simulated using the simulation software wxAMPS which is an update of the popular solar cell simulation tool (AMPS; Analysis of Microelectronic and Photonic Structures). Various models were constructed with thin film stacks in the format, glass/FTO/Cu:NiO x /MAPbX/ZnO/Al. The shortcomings in each device configuration were overcome by introducing thin defect layers at the interfaces of HTL/absorber layer and ETL/absorber layer hypothetically. The simulated photovoltaic characteristics yielded the highest PCE value of 20.58% for the device C (MAPbBr3), 19.08% for device B (MAPbI2Br), and the lowest value of 16.14% for device A (MAPbI3). The simulation results also indicated that thicker perovskite layers realized higher values of PCE in relation to thinner ones due to enhanced photon harvesting. The JV characteristics provided evidence that the defect states present in perovskite films cause a noticeable reduction in Voc. However, this has very nominal effect on Jsc value, particularly for the MAPbI2Br perovskite cell. The increase in bandgap energy is responsible for the enhanced photovoltaic parameters such as PCE, FF, Jsc, and Voc. These findings are likely to serve as important inputs and guide to the design of new mixed-halide perovskite structures with Cu:NiO x -HTM and ZnO ETM for achieving high stability and low fabrication cost in perovskite solar cells.



This work is supported partially by National Natural Science Foundation of China (Grant Nos. 51772096, 51372082, 51402106, and 11504107), Beijing Natural Science Foundation (17L20075), Joint Funds of the Equipment Pre-Research and Ministry of Education (6141A020225), National High-tech R&D Program of China (863 Program, No. 2015AA034601), Par-Eu Scholars Program, Beijing Municipal Science and Technology Project (Z161100002616039), and the Fundamental Research Funds for the Central Universities (2016JQ01, 2017ZZD02).

Supplementary material

40820_2018_205_MOESM1_ESM.pdf (128 kb)
Supplementary material 1 (PDF 128 kb)


  1. 1.
    A. Kojima, K. Teshima, Y. Shirai, T. Miyasaka, Organometal halide perovskites as visible-light sensitizers for photovoltaic cells. J. Am. Chem. Soc. 131(17), 6050–6051 (2009). CrossRefGoogle Scholar
  2. 2.
    D. Song, P. Cui, T. Wang, D. Wei, M. Li et al., Managing carrier lifetime and doping property of lead halide perovskite by postannealing processes for highly efficient perovskite solar cells. J. Phys. Chem. C 119(40), 22812–22819 (2015). CrossRefGoogle Scholar
  3. 3.
    H.S. Kim, C.R. Lee, J.H. Im, K.B. Lee, T. Moehl et al., Lead iodide perovskite sensitized all-solid-state submicron thin film mesoscopic solar cell with efficiency exceeding 9%. Sci. Rep. 2, 591 (2012). CrossRefGoogle Scholar
  4. 4.
    M.M. Lee, J. Teuscher, T. Miyasaka, T.N. Murakami, H.J. Snaith, Efficient hybrid solar cells based on meso-superstructured organometal halide perovskites. Science 338(6107), 643–647 (2012). CrossRefGoogle Scholar
  5. 5.
    J. Burschka, N. Pellet, S.J. Moon, R. Humphry-Baker, P. Gao, M.K. Nazeeruddin, M. Gratzel, Sequential deposition as a route to high-performance perovskite-sensitized solar cells. Nature 499(7458), 316–319 (2013). CrossRefGoogle Scholar
  6. 6.
    M. Liu, M.B. Johnston, H.J. Snaith, Efficient planar heterojunction perovskite solar cells by vapour deposition. Nature 501(7467), 395–398 (2013). CrossRefGoogle Scholar
  7. 7.
    N.J. Jeon, J.H. Noh, Y.C. Kim, W.S. Yang, S. Ryu, S.I. Seok, Solvent engineering for high-performance inorganic–organic hybrid perovskite solar cells. Nat. Mater. 13(9), 897–903 (2014). CrossRefGoogle Scholar
  8. 8.
    N.J. Jeon, J.H. Noh, W.S. Yang, Y.C. Kim, S. Ryu, J. Seo, S.I. Seok, Compositional engineering of perovskite materials for high-performance solar cells. Nature 517(7535), 476–480 (2015). CrossRefGoogle Scholar
  9. 9.
    W.S. Yang, J.H. Noh, N.J. Jeon, Y.C. Kim, S. Ryu, J. Seo, S.I. Seok, High-performance photovoltaic perovskite layers fabricated through intramolecular exchange. Science 348(6240), 1234–1237 (2015). CrossRefGoogle Scholar
  10. 10.
    M.A. Green, K. Emery, Y. Hishikawa, W. Warta, E.D. Dunlop, Solar cell efficiency tables (version 46). Prog. Photovolt: Res. Appl. 23, 805–812 (2015). CrossRefGoogle Scholar
  11. 11.
    F. Zhang, B. Yang, X. Mao, R. Yang, L. Jiang et al., Perovskite CH3NH3PbI3−xBrx single crystals with charge-carrier lifetimes exceeding 260 μs. ACS Appl. Mater. Interfaces 9(17), 14827–14832 (2017). CrossRefGoogle Scholar
  12. 12.
    D.P. McMeekin, G. Sadoughi, W. Rehman, G.E. Eperon, M. Saliba et al., A mixed-cation lead mixed-halide perovskite absorber for tandem solar cells. Science 351(6269), 151–155 (2016). CrossRefGoogle Scholar
  13. 13.
    N. Pellet, P. Gao, G. Gregori, T.Y. Yang, M.K. Nazeeruddin, J. Maier, M. Gratzel, Mixed-organic-cation perovskite photovoltaics for enhanced solar-light harvesting. Angew. Chem. Int. Ed. 53(12), 3151–3157 (2014). CrossRefGoogle Scholar
  14. 14.
    A.M. Elseman, A.E. Shalan, M.M. Rashad, A.M. Hassan, Experimental and simulation study for impact of different halides on the performance of planar perovskite solar cells. Mater. Sci. Semicond. Process. 66, 176–185 (2017). CrossRefGoogle Scholar
  15. 15.
    Z. Zhang, X. Yue, D. Wei, M. Li, P. Fu, B. Xie, D. Song, Y. Li, DMSO-based PbI2 precursor with PbCl2 additive for highly efficient perovskite solar cells fabricated at low temperature. RSC Adv. 5(127), 104606–104611 (2015). CrossRefGoogle Scholar
  16. 16.
    J.A. Christians, R.C.M. Fung, P.V. Kamat, An inorganic hole conductor for organo-lead halide perovskite solar cells. Improved hole conductivity with copper iodide. J. Am. Chem. Soc. 136(2), 758–764 (2014). CrossRefGoogle Scholar
  17. 17.
    J. You, L. Meng, T.B. Song, T.F. Guo, Y.M. Yang et al., Improved air stability of perovskite solar cells via solution-processed metal oxide transport layers. Nat. Nanotechnol. 11(1), 75–81 (2016). CrossRefGoogle Scholar
  18. 18.
    D. Wei, J. Ji, D. Song, M. Li, P. Cui et al., A TiO2 embedded structure for perovskite solar cells with anomalous grain growth and effective electron extraction. J. Mater. Chem. A 5(4), 1406–1414 (2017). CrossRefGoogle Scholar
  19. 19.
    S. Seo, I.J. Park, M. Kim, S. Lee, C. Bae, H.S. Jung, N.G. Park, J.Y. Kim, H. Shin, An ultra-thin, un-doped NiO hole transporting layer of highly efficient (16.4%) organic–inorganic hybrid perovskite solar cells. Nanoscale 8(22), 11403–11412 (2016). CrossRefGoogle Scholar
  20. 20.
    L. Hu, J. Peng, W. Wang, Z. Xia, J. Yuan et al., Sequential deposition of CH3NH3PbI3 on planar NiO film for efficient planar perovskite solar cells. ACS Photonics 1(7), 547–553 (2014). CrossRefGoogle Scholar
  21. 21.
    H.-T. Lien, D.P. Wong, N.-H. Tsao, C.-I. Huang, C. Su, K.-H. Chen, L.-C. Chen, Effect of copper oxide oxidation state on the polymer-based solar cell buffer layers. ACS Appl. Mater. Interfaces 6(24), 22445–22450 (2014). CrossRefGoogle Scholar
  22. 22.
    X. Du, Y. Wang, Z.G. Xia, H. Zhou, Perovskite CH3NH3PbI3 heterojunction solar cells via ultrasonic spray deposition. Appl. Mech. Mater. 748, 39–43 (2015). CrossRefGoogle Scholar
  23. 23.
    M.-K. Son, L. Steier, M. Schreier, M.T. Mayer, J. Luo, M. Grätzel, A copper nickel mixed oxide hole selective layer for Au-free transparent cuprous oxide photocathodes. Energy Environ. Sci. 10(4), 912–918 (2017). CrossRefGoogle Scholar
  24. 24.
    Sajid, A.M. Elseman, J. Ji, S. Dou, H. Huang, P. Cui, D. Wei, M. Li, Novel hole transport layer of nickel oxide composite with carbon for high-performance perovskite solar cells. Chin. Phys. B 27(1), 017305 (2018). CrossRefGoogle Scholar
  25. 25.
    J.W. Jung, C.-C. Chueh, A.K.Y. Jen, A low-temperature, solution-processable, Cu-doped nickel oxide hole-transporting layer via the combustion method for high-performance thin-film perovskite solar cells. Adv. Mater. 27(47), 7874–7880 (2015). CrossRefGoogle Scholar
  26. 26.
    S. Yue, K. Liu, R. Xu, M. Li, M. Azam et al., Efficacious engineering on charge extraction for realizing highly efficient perovskite solar cells. Energy Environ. Sci. 10(12), 2570–2578 (2017). CrossRefGoogle Scholar
  27. 27.
    J.H. Kim, P.W. Liang, S.T. Williams, N. Cho, C.C. Chueh, M.S. Glaz, D.S. Ginger, A.K. Jen, High-performance and environmentally stable planar heterojunction perovskite solar cells based on a solution-processed copper-doped nickel oxide hole-transporting layer. Adv. Mater. 27(4), 695–701 (2015). CrossRefGoogle Scholar
  28. 28.
    D. Liu, T.L. Kelly, Perovskite solar cells with a planar heterojunction structure prepared using room-temperature solution processing techniques. Nat. Photonics 8(2), 133–138 (2014). CrossRefGoogle Scholar
  29. 29.
    G.E. Eperon, V.M. Burlakov, P. Docampo, A. Goriely, H.J. Snaith, Morphological control for high performance, solution-processed planar heterojunction perovskite solar cells. Adv. Funct. Mater. 24(1), 151–157 (2014). CrossRefGoogle Scholar
  30. 30.
    F. Liu, J. Zhu, J. Wei, Y. Li, M. Lv, S. Yang, B. Zhang, J. Yao, S. Dai, Numerical simulation: toward the design of high-efficiency planar perovskite solar cells. Appl. Phys. Lett. 104(25), 253508 (2014). CrossRefGoogle Scholar
  31. 31.
    K. Sato, S. Kim, S. Komuro, X. Zhao, Characteristics of Cu-doped amorphous NiO thin films formed by RF magnetron sputtering. Jpn. J. Appl. Phys. 55(6S1), 06GJ10 (2016). CrossRefGoogle Scholar
  32. 32.
    N. Hernández-Como, A. Morales-Acevedo, Simulation of hetero-junction silicon solar cells with AMPS-1D. Sol. Energy Mater. Sol. Cells 94(1), 62–67 (2010). CrossRefGoogle Scholar
  33. 33.
    I. Vurgaftman, J.R. Meyer, L.R. Ram-Mohan, Band parameters for III–V compound semiconductors and their alloys. J. Appl. Phys. 89(11), 5815–5875 (2001). CrossRefGoogle Scholar
  34. 34.
    N.K. Noel, S.D. Stranks, A. Abate, C. Wehrenfennig, S. Guarnera et al., Lead-free organic–inorganic tin halide perovskites for photovoltaic applications. Energy Environ. Sci. 7(9), 3061–3068 (2014). CrossRefGoogle Scholar
  35. 35.
    C. Wehrenfennig, M. Liu, H.J. Snaith, M.B. Johnston, L.M. Herz, Charge-carrier dynamics in vapour-deposited films of the organolead halide perovskite CH3NH3PbI3−xClx. Energy Environ. Sci. 7(7), 2269–2275 (2014). CrossRefGoogle Scholar
  36. 36.
    Y. Wang, Y. Liu, H. Zhou, Z. Xia, Simulation of perovskite solar cells with inorganic hole transporting materials, in 2015 IEEE 42nd Photovoltaic Specialist Conference (PVSC) (2015).
  37. 37.
    Y. Wang, Z. Xia, Y. Liu, H. Zhou, Uniform perovskite photovoltaic thin films via ultrasonic spray assisted deposition method, in 2015 IEEE 42nd Photovoltaic Specialist Conference (PVSC) (2015).
  38. 38.
    J. Cuiffi, T. Benanti, W.J. Nam, S. Fonash, Modeling of bulk and bilayer organic heterojunction solar cells. Appl. Phys. Lett. 96(14), 143307 (2010). CrossRefGoogle Scholar
  39. 39.
    T. Wang, J. Chen, G. Wu, M. Li, Optimal design of efficient hole transporting layer free planar perovskite solar cell. Sci. Chin. Mater. 59(9), 703–709 (2016). CrossRefGoogle Scholar
  40. 40.
    K.W. Kemp, A.J. Labelle, S.M. Thon, A.H. Ip, I.J. Kramer, S. Hoogland, E.H. Sargent, Interface recombination in depleted heterojunction photovoltaics based on colloidal quantum dots. Adv. Energy Mater. 3(7), 917–922 (2013). CrossRefGoogle Scholar
  41. 41.
    T. Wang, J. Chen, G. Wu, D. Song, M. Li, Designing novel thin film polycrystalline solar cells for high efficiency: sandwich CIGS and heterojunction perovskite. J. Semicond. 38(1), 014005 (2017). CrossRefGoogle Scholar
  42. 42.
    P. Liao, X. Zhao, G. Li, Y. Shen, M. Wang, A new method for fitting current–voltage curves of planar heterojunction perovskite solar cells. Nano-Micro Lett. 10(1), 5 (2018). CrossRefGoogle Scholar
  43. 43.
    A.E. Shalan, A. Mourtada Elseman, M. Rasly, M.M. Moharam, M. Lira-Cantu, M.M. Rashad, Concordantly fabricated heterojunction ZnO–TiO2 nanocomposite electrodes via a co-precipitation method for efficient stable quasi-solid-state dye-sensitized solar cells. RSC Adv. 5(125), 103095–103104 (2015). CrossRefGoogle Scholar
  44. 44.
    D. Song, D. Wei, P. Cui, M. Li, Z. Duan et al., Dual function interfacial layer for highly efficient and stable lead halide perovskite solar cells. J. Mater. Chem. A 4(16), 6091–6097 (2016). CrossRefGoogle Scholar
  45. 45.
    H.S. Kim, I. Mora-Sero, V. Gonzalez-Pedro, F. Fabregat-Santiago, E.J. Juarez-Perez, N.G. Park, J. Bisquert, Mechanism of carrier accumulation in perovskite thin-absorber solar cells. Nat. Commun. 4, 2242 (2013). CrossRefGoogle Scholar
  46. 46.
    M.-C. Kim, B.J. Kim, D.-Y. Son, N.-G. Park, H.S. Jung, M. Choi, Observation of enhanced hole extraction in Br concentration gradient perovskite materials. Nano Lett. 16(9), 5756–5763 (2016). CrossRefGoogle Scholar
  47. 47.
    A.A. Boussettine, Y. Belhadji, A. Benmansour, Modeling of tandem solar cell a-Si/a-SiGe using AMPS-1D program. Energy Proc. 18, 693–700 (2012). CrossRefGoogle Scholar
  48. 48.
    J. He, H. Windstorm, A. Hagfeldt, S.-E. Lindquist, Dye-sensitized nanostructured tandem cell-first demonstrated cell with a dye-sensitized photocathode. Sol. Energy Mater. Sol. Cells 62(3), 265–273 (2000). CrossRefGoogle Scholar
  49. 49.
    S. Ryu, J.H. Noh, N.J. Jeon, Y.C. Kim, W.S. Yang, J. Seo, S.I. Seok, Voltage output of efficient perovskite solar cells with high open-circuit voltage and fill factor. Energy Environ. Sci. 7(8), 2614–2618 (2014). CrossRefGoogle Scholar
  50. 50.
    B. Suarez, V. Gonzalez-Pedro, T.S. Ripolles, R.S. Sanchez, L. Otero, I. Mora-Sero, Recombination study of combined halides (Cl, Br, I) perovskite solar cells. J. Phys. Chem. Lett. 5(10), 1628–1635 (2014). CrossRefGoogle Scholar
  51. 51.
    C. Wehrenfennig, G.E. Eperon, M.B. Johnston, H.J. Snaith, L.M. Herz, High charge carrier mobilities and lifetimes in organolead trihalide perovskites. Adv. Mater. 26(10), 1584–1589 (2014). CrossRefGoogle Scholar
  52. 52.
    D. Bi, L. Yang, G. Boschloo, A. Hagfeldt, E.M. Johansson, Effect of different hole transport materials on recombination in CH3NH3PbI3 perovskite-sensitized mesoscopic solar cells. J. Phys. Chem. Lett. 4(9), 1532–1536 (2013). CrossRefGoogle Scholar
  53. 53.
    W. Chen, Y. Wu, Y. Yue, J. Liu, W. Zhang et al., Efficient and stable large-area perovskite solar cells with inorganic charge extraction layers. Science 350(6263), 944–948 (2015). CrossRefGoogle Scholar
  54. 54.
    W. Chen, F.Z. Liu, X.Y. Feng, A.B. Djurišić, W.K. Chan, Z.B. He, Cesium doped NiOx as an efficient hole extraction layer for inverted planar perovskite solar cells. Adv. Energy Mater. 7(19), 1700722 (2017). CrossRefGoogle Scholar
  55. 55.
    J.H. Noh, S.H. Im, J.H. Heo, T.N. Mandal, S.I. Seok, Chemical management for colorful, efficient, and stable inorganic–organic hybrid nanostructured solar cells. Nano Lett. 13(4), 1764–1769 (2013). CrossRefGoogle Scholar
  56. 56.
    E. Edri, S. Kirmayer, D. Cahen, G. Hodes, High open-circuit voltage solar cells based on organic–inorganic lead bromide perovskite. J. Phys. Chem. Lett. 4(6), 897–902 (2013). CrossRefGoogle Scholar
  57. 57.
    W.-J. Yin, T. Shi, Y. Yan, Unusual defect physics in CH3NH3PbI3 perovskite solar cell absorber. Appl. Phys. Lett. 104(6), 063903 (2014). CrossRefGoogle Scholar
  58. 58.
    P. Cui, P. Fu, D. Wei, M. Li, D. Song et al., Reduced surface defects of organometallic perovskite by thermal annealing for highly efficient perovskite solar cells. RSC Adv. 5(92), 75622–75629 (2015). CrossRefGoogle Scholar
  59. 59.
    T.C. Sum, N. Mathews, Advancements in perovskite solar cells: photophysics behind the photovoltaics. Energy Environ. Sci. 7(8), 2518–2534 (2014). CrossRefGoogle Scholar
  60. 60.
    D. Liu, M.K. Gangishetty, T.L. Kelly, Effect of CH3NH3PbI3 thickness on device efficiency in planar heterojunction perovskite solar cells. J. Mater. Chem. A 2(46), 19873–19881 (2014). CrossRefGoogle Scholar
  61. 61.
    W.A. Laban, L. Etgar, Depleted hole conductor-free lead halide iodide heterojunction solar cells. Energy Environ. Sci. 6(11), 3249–3253 (2013). CrossRefGoogle Scholar
  62. 62.
    G. Xing, N. Mathews, S. Sun, S.S. Lim, Y.M. Lam, M. Grätzel, S. Mhaisalkar, T.C. Sum, Long-range balanced electron- and hole-transport lengths in organic-inorganic CH3NH3PbI3. Science 342(6156), 344–347 (2013). CrossRefGoogle Scholar
  63. 63.
    P. Cui, D. Wei, J. Ji, D. Song, Y. Li et al., Highly efficient electron-selective layer free perovskite solar cells by constructing effective pn-heterojunction. Solar RRL 1(2), 1600027 (2017). CrossRefGoogle Scholar
  64. 64.
    D. Song, J. Ji, Y. Li, G. Li, M. Li et al., Degradation of organometallic perovskite solar cells induced by trap states. Appl. Phys. Lett. 108(9), 093901 (2016). CrossRefGoogle Scholar
  65. 65.
    H. Luo, X. Lin, X. Hou, L. Pan, S. Huang, X. Chen, Efficient and air-stable planar perovskite solar cells formed on graphene-oxide-modified PEDOT:PSS hole transport layer. Nano-Micro Lett. 9(4), 39 (2017). CrossRefGoogle Scholar
  66. 66.
    L. Etgar, P. Gao, Z. Xue, Q. Peng, A.K. Chandiran, B. Liu, M.K. Nazeeruddin, M. Grätzel, Mesoscopic CH3NH3PbI3/TiO2 heterojunction solar cells. J. Am. Chem. Soc. 134(42), 17396–17399 (2012). CrossRefGoogle Scholar
  67. 67.
    C. Zhang, Y. Luo, X. Chen, Y. Chen, Z. Sun, S. Huang, Effective improvement of the photovoltaic performance of carbon-based perovskite solar cells by additional solvents. Nano-Micro Lett. 8(4), 347–357 (2016). CrossRefGoogle Scholar
  68. 68.
    S.R. Raga, E.M. Barea, F. Fabregat-Santiago, Analysis of the origin of open circuit voltage in dye solar cells. J. Phys. Chem. Lett. 3(12), 1629–1634 (2012). CrossRefGoogle Scholar
  69. 69.
    B. Shin, O. Gunawan, Y. Zhu, N.A. Bojarczuk, S.J. Chey, S. Guha, Thin film solar cell with 8.4% power conversion efficiency using an earth abundant Cu2ZnSnS4 absorber. Prog. Photovolt. 21(1), 72–76 (2013). CrossRefGoogle Scholar
  70. 70.
    Y. Hou, W. Chen, D. Baran, T. Stubhan, N.A. Luechinger et al., Overcoming the interface losses in planar heterojunction perovskite-based solar cells. Adv. Mater. 28(25), 5112–5120 (2016). CrossRefGoogle Scholar
  71. 71.
    Z. Liu, B. Sun, X. Liu, J. Han, H. Ye, T. Shi, Z. Tang, G. Liao, Efficient carbon-based CsPbBr3 inorganic perovskite solar cells by using Cu-phthalocyanine as hole transport material. Nano-Micro Lett. 10(2), 34 (2018). CrossRefGoogle Scholar
  72. 72.
    Z. Zhang, D. Wei, B. Xie, X. Yue, M. Li, D. Song, Y. Li, High reproducibility of perovskite solar cells via a complete spin-coating sequential solution deposition process. Sol. Energy 122, 97–103 (2015). CrossRefGoogle Scholar
  73. 73.
    Z. Zhang, M. Li, W. Liu, X. Yue, P. Cui, D. Wei, CH3NH3PbI3 converted from reactive magnetron sputtered PbO for large area perovskite solar cells. Sol. Energy Mater. Sol. Cells 163, 250–254 (2017). CrossRefGoogle Scholar
  74. 74.
    S. Albrecht, M. Saliba, J.-P. Correa-Baena, K. Jäger, L. Korte, A. Hagfeldt, M. Grätzel, B. Rech, Towards optical optimization of planar monolithic perovskite/silicon-heterojunction tandem solar cells. J. Opt. 18(6), 064012 (2016). CrossRefGoogle Scholar
  75. 75.
    A.M. Elseman, A.E. Shalan, S. Sajid, M.M. Rashad, A.M. Hassan, M. Li, Copper substituted lead perovskites materials constructed with different halides for working (CH3NH3)2CuX4 based perovskite solar cells from experimental and theoretical view. ACS Appl. Mater. Interfaces. 10(14), 11699–11707 (2018). CrossRefGoogle Scholar

Copyright information

© The Author(s) 2018

Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (, which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.

Authors and Affiliations

  • Sajid Sajid
    • 1
  • Ahmed Mourtada Elseman
    • 2
  • Jun Ji
    • 1
  • Shangyi Dou
    • 1
  • Dong Wei
    • 1
  • Hao Huang
    • 1
  • Peng Cui
    • 1
  • Wenkang Xi
    • 1
  • Lihua Chu
    • 1
  • Yingfeng Li
    • 1
  • Bing Jiang
    • 1
  • Meicheng Li
    • 1
    Email author
  1. 1.State Key Laboratory of Alternate Electrical Power, System with Renewable Energy Sources, School of Renewable EnergyNorth China Electric Power UniversityBeijingPeople’s Republic of China
  2. 2.Electronic and Magnetic Materials Department, Advanced Materials DivisionCentral Metallurgical Research and Development Institute (CMRDI)Helwan, CairoEgypt