Phase composition and magnetic properties of Pr–Nd–MM–Fe–B nanocrystalline magnets prepared by spark plasma sintering

  • Published:
Rare Metals Aims and scope Submit manuscript

Abstract

The isotropic nanocrystalline [(PrNd)0.8MM0.2]29.8Fe68.7Al0.1Cu0.12Co0.88B magnets (MM: mischmetal) were prepared by single-main phase and double-main phase methods using spark plasma sintering (SPS). Melt-spinning method was used to prepare initial powder and avoid component deviations caused by longtime ball milling. The magnetic properties of the magnet prepared by double-main phase method (called double-main phase magnet, DMP magnet) are remanence of Br = 0.75 T, intrinsic coercivity of Hcj = 909.83 kA·m−1, maximum magnetic energy product of (BH)max = 95.48 kJ·m−3, which are better than those of the magnet prepared by single-main phase method (called single-main phase magnet, SMP magnet). The diffraction peaks of the main phase of DMP magnet split in X-ray diffractometer (XRD) pattern, indicating that R2Fe14B phases with different distributions of La/Ce elements exist in the magnet. This speculation is confirmed by transmission electron microscopy (TEM) observation. The La/Ce-rich main phase and La/Ce-lean main phase are present in DMP magnets. The heterogeneity of rare earth elements suppresses the magnetic dilution effect in DMP magnet, and the magnetic properties are improved. Though the DMP magnet contains different main phases, it presents unitary Curie temperature (TC) of 577 K, which is higher than that of SMP magnet. This result suggests that the TC of the magnets can be promoted by double-main phase method and SPS.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4

Similar content being viewed by others

References

  1. Sagawa M, Fujimura S, Togawa N, Yamamoto H, Matsuura Y. New material for permanent magnets on a base of Nd and Fe. J Appl Phys. 1984;55(6):2083.

    Article  CAS  Google Scholar 

  2. Bai G, Gao RW, Sun Y, Han GB, Wang B. Study of high-coercivity sintered NdFeB magnets. J Magn Magn Mater. 2007;308(1):20.

    Article  CAS  Google Scholar 

  3. Li JJ, Guo CJ, Zhou TJ, Qi ZQ, Yu X, Yang B, Zhu MG. Effects of diffusing DyZn film on magnetic properties and thermal stability of sintered NdFeB magnets. J Magn Magn Mater. 2018;454:215.

    Article  CAS  Google Scholar 

  4. Zhang XF, Zhang WK, Li YF, Liu YL, Li ZB, Ma Q, Shi MF, Liu F. Magnetic properties of melt-spun MM–Fe–B ribbons with different wheel speeds and mischmetal contents. Rare Met. 2017;36(12):992.

    Article  CAS  Google Scholar 

  5. Sagawa M, Fujimura S, Yamamoto H, Matsuura Y, Hiraga K. Permanent magnet materials based on the rare earth–iron–boron tetragonal compounds. IEEE Trans Magn. 1984;20(5):1584.

    Article  Google Scholar 

  6. Ma TY, Yan M, Wu KY, Wu B, Liu XL, Wang XJ, Qian ZY, Wu C, Xia WX. Grain boundary restructuring of multi-main-phase Nd–Ce–Fe–B sintered magnets with Nd hydrides. Acta Mater. 2018;142:18.

    Article  CAS  Google Scholar 

  7. Li ZB, Shen BG, Zhang M, Hu FX, Sun JR. Substitution of Ce for Nd in preparing R2Fe14B nanocrystalline magnets. J Alloys Compd. 2015;628:325.

    Article  CAS  Google Scholar 

  8. Herbst JF. R2Fe14B materials: intrinsic properties and technological aspects. Rev Mod Phys. 1991;63(63):819.

    Article  CAS  Google Scholar 

  9. Alam A, Khan M, McCallum RW, Johnson DD. Site-preference and valency for rare-earth sites in (R-Ce)2Fe14B magnets. Appl Phys Lett. 2013;102(4):4176.

    Article  Google Scholar 

  10. Alam A, Johnson DD. Mixed valency and site-preference chemistry for cerium and its compounds: a predictive density-functional theory study. Phys Rev B. 2014;89(23):2495.

    Article  Google Scholar 

  11. Yan CJ, Guo S, Chen RJ, Liu J, Lee D, Yan AR. Effect of Ce on the magnetic properties and microstructure of sintered didymium–Fe–B magnets. IEEE Trans Magn. 2014;50(10):1.

    Article  Google Scholar 

  12. Pathak AK, Khan M, Gschneidner KA, McCallum RW, Zhou L, Sun K, Dennis KW, Zhou C, Pinkerton FE, Kramer MJ, Pecharsky VK. Cerium: an unlikely replacement of dysprosium in high performance Nd–Fe–B permanent magnets. Adv Mater. 2015;27(16):2663.

    Article  CAS  Google Scholar 

  13. Yang MN, Wang H, Hu YF, Yang LYM, Aimee M, Yang B. Relating atomic local structures and Curie temperature of NdFeB permanent magnets: an X-ray absorption spectroscopic study. Rare Met. 2018;37(11):983.

    Article  CAS  Google Scholar 

  14. Jin JY, Zhang YJ, Bai GH, Qian ZY, Wu C, Ma TY, Shen BG, Yan M. Manipulating Ce valence in RE2Fe14B tetragonal compounds by La–Ce co-doping: resultant crystallographic and magnetic anomaly. Sci Rep. 2016;6:30194.

    Article  CAS  Google Scholar 

  15. Zhu MG, Li W, Wang JD, Zheng LY, Li YF, Zhang K, Feng HB, Liu T. Influence of Ce content on the rectangularity of demagnetization curves and magnetic properties of Re–Fe–B magnets sintered by double main phase alloy method. IEEE Trans Magn. 2014;50(1):1000104.

    Google Scholar 

  16. Gong W, Hadjipanayis GC. Misch-metal-iron based magnets. J Appl Phys. 1988;63(8):3513.

    Article  CAS  Google Scholar 

  17. Zhu MG, Han R, Li W, Huang SL, Zheng DW, Song LW, Shi XN. An enhanced coercivity for (CeNdPr)–Fe–B sintered magnet prepared by structure design. IEEE Trans Magn. 2015;51(11):2014604.

    Google Scholar 

  18. Jin JY, Ma TY, Zhang YJ, Bai GH, Yan M. Chemically inhomogeneous RE–Fe–B permanent magnets with high figure of merit: solution to global rare earth criticality. Sci Rep. 2016;6:32200.

    Article  CAS  Google Scholar 

  19. Fan XD, Guo S, Chen K, Chen RJ, Lee D, You CY, Yan AR. Tuning Ce distribution for high performance Nd–Ce–Fe–B sintered magnets. J Magn Magn Mater. 2016;419:394.

    Article  CAS  Google Scholar 

  20. Tang J, Yang LR, Zhang L, Wei CF, Mei Y, Wen YG. Succession law of Nd–Fe–B alloys with different coercivities. Rare Met. 2015;34(9):657.

    Article  CAS  Google Scholar 

  21. Lai RS, Chen RJ, Yin WZ, Tang X, Wang ZX, Jin CX, Lee D, Yan AR. High performance (La, Ce, Pr, Nd)–Fe–B die-upset magnets based on misch-metal. J Alloys Compd. 2017;724:275.

    Article  CAS  Google Scholar 

  22. Niu E, Chen ZA, Chen GA, Zhao YG, Zhang J, Rao XL, Hu BP, Wang ZX. Achievement of high coercivity in sintered R–Fe–B magnets based on mischmetal by dual alloy method. J Appl Phys. 2014;115(11):113912.

    Article  Google Scholar 

  23. Xiong JF, Shang RX, Liu YL, Zhao X, Zuo WL, Hu FX, Sun JR, Zhao TY, Chen RJ, Shen BG. Magnetic properties of misch-metal partially substituted Nd–Fe–B magnets sintered by dual alloy method. Chin Phys B. 2018;27(7):077504.

    Article  Google Scholar 

  24. Lu QM, Niu J, Liu WQ, Yue M, Altounian Z. Enhanced magnetic properties of spark plasma sintered (La/Ce)–Fe–B magnets. IEEE Trans Magn. 2017;53(11):2100603.

    Article  Google Scholar 

  25. Yue M, Zhang JX, Xiao YF, Wang GP, Li T. New kind of NdFeB magnet prepared by spark plasma sintering. IEEE Trans Magn. 2003;39(6):3551.

    Article  CAS  Google Scholar 

  26. Chu LH, Liu Y, Li J, Ma YL, Li CY. Structural and magnetic study of hot-pressed and hot-deformed Nd13.5−xCexFe80.4Ga0.5B5.6 (x = 0, 0.5, 1) prepared by spark plasma sintering. IEEE Trans Magn. 2012;48(6):2092.

    Article  CAS  Google Scholar 

  27. Ma YL, Liu Y, Li J, Du HL, Gao J. Anisotropic nanocomposite Nd2Fe14B/α-Fe magnets prepared by spark plasma sintering. IEEE Trans Magn. 2009;45(6):2605.

    Article  CAS  Google Scholar 

  28. Yue M, Zhang JX, Tian M. Microstructure and magnetic properties of isotropic bulk NdxFe94−xB6 (x = 6, 8, 10) nanocomposite magnets prepared by spark plasma sintering. J Appl Phys. 2006;99(8):601.

    Google Scholar 

  29. Zhao W, Liu Y, Li J, Wang RQ, Qiu YC. Microstructure and magnetic properties of hot-deformed anisotropic Nd–Fe–B magnets prepared from amorphous precursors with different crystallization proportions. Rare Met. 2017;36(4):268.

    Article  CAS  Google Scholar 

  30. Huang YL, Liu ZW, Zhong XC, Yu HY, Zeng DC. NdFeB based magnets prepared from nanocrystalline powders with various compositions and particle sizes by spark plasma sintering. Powder Metall. 2012;55(2):124.

    Article  CAS  Google Scholar 

Download references

Acknowledgements

This work was financially supported by the National Key Research and Development Program of China (No. 2016YFB0700903) and the National Natural Science Foundation of China (Nos. 51571064 and 51571126).

Author information

Authors and Affiliations

  1. Division of Functional Materials, Central Iron and Steel Research Institute, Beijing, 100081, China

    Xin Wang & Ming-Gang Zhu

  2. School of Science, Inner Mongolia University of Science and Technology, Baotou, 014010, China

    Zeng-Ru Zhao, Fei Liu, Yan-Li Liu & Xue-Feng Zhang

  3. Key Laboratory of Integrated Exploitation of Bayan Obo Multi-Metal Resources, Inner Mongolia University of Science and Technology, Baotou, 014010, China

    Gao-Feng Wang

Authors
  1. Xin Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Zeng-Ru Zhao
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Fei Liu
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Yan-Li Liu
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Gao-Feng Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Ming-Gang Zhu
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Xue-Feng Zhang
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding authors

Correspondence to Ming-Gang Zhu or Xue-Feng Zhang.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Wang, X., Zhao, ZR., Liu, F. et al. Phase composition and magnetic properties of Pr–Nd–MM–Fe–B nanocrystalline magnets prepared by spark plasma sintering. Rare Met. 39, 36–40 (2020). https://doi.org/10.1007/s12598-019-01265-8

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12598-019-01265-8

Keywords

Search

Navigation