Abstract
We report the observation of a propounced peak in surface resistance at microwave frequencies of 4.88 GHz and 9.55 GHz and its disappearance after irradiation with swift ions in laser ablated DyBa2Cu3O7-δ (DBCO) thin films. The measurements were carried out in zero field as well as in the presence of magnetic fields (up to 0.8 T). The films were irradiated using 90 MeV oxygen ions at Nuclear Science Centre, New Delhi at a fluence of 3×1013 ions/cm2. Introduction of point defects and extended defects after irradiation suppresses the peak at 9.55 GHz whereas no suppression is observed at 4.88 GHz. These results and the vortex dynamics in the films at microwave frequencies before and after irradiation are discussed.
Similar content being viewed by others
References
G Blatter et al, Rev. Mod. Phys. 66, 1125 (1994)
S Bhattacharya and M Higgins, Phys. Rev. Lett. 70, 2617 (1993); Phys. Rev. B52, 64 (1995); Physica C257, 232 (1996)
A B Pippard, Philos. Mag. 19, 217 (1969)
C Tang, X S Ling, S Bhattacharya and P M Chaikin, Europhys. Lett. 35, 597 (1996)
A I Larkin and Y N Ovchinnikov, J. Low Temp. Phys. 34, 409 (1979)
A R Bhangale, P Raychaudhuri, S Sarkar, T Banerjee, S S Bhagwat, V Shirodhkar and R Pinto, Phys. Rev. B63, 180502R (2001)
J I Gittleman and B Rosenblum, Phys. Rev. Lett. 16, 734 (1966)
R Pinto et al, J. Appl. Phys. 73, 5105 (1993)
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Ail, U., Banerjee, T., Bhangale, A.R. et al. Effect of swift heavy ion irradiation on surface resistance of DyBa2Cu3O7-δ thin films at microwave frequencies. Pramana - J Phys 58, 959–963 (2002). https://doi.org/10.1007/s12043-002-0200-7
Issue Date:
DOI: https://doi.org/10.1007/s12043-002-0200-7