  • Published:
Journal of Materials Engineering and Performance Aims and scope Submit manuscript

Abstract

In this study, dissimilar joining between SAF 2205 duplex stainless steel and Inconel X-750 superalloy produced by TLP process was investigated. This process was done at temperature of 1100 °C for different bonding times of 1, 15, 30, 45 and 60 min. The effect of different bonding times on the microstructure and mechanical properties of the welded samples was studied. Microstructure of the samples was analyzed by optical microscopy and scanning electron microscopy equipped with energy-dispersive x-ray spectroscopy. X-ray diffraction analysis was used to determine the formed phases in the bonding area. Microhardness and shear strength tests were done to evaluate the mechanical properties of the joints. It was found that the joint area contains the γ-Ni solid solution, eutectic compounds with intermetallic phases beside precipitated secondary phases. The γ-Ni solid solution, BN, BCN, CrB, Ni3Si and Ni3B were the main phases in the joining area. Maximum microhardness was found in athermally solidified zone, due to the presence of hard and brittle intermetallic and boride phases. The maximum shear strength (368 MPa) was obtained for the sample with the bonding time of 45 min, due to the completion of isothermal solidification and removal of eutectic compounds.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10

Similar content being viewed by others

References

  1. K.D. Ramkumar, A. Singh, S. Raghuvanshi, A. Bajpai, T. Solanki, M. Arivarasu, N. Arivazhagan, and S. Narayanan, Metallurgical and Mechanical Characterization of Dissimilar Welds of Austenitic Stainless Steel and Super-Duplex Stainless Steel—A Comparative Study. J. Manuf. Process., 2015, 19, p 212–232

    Article  Google Scholar 

  2. J.S. Ku and N.J. Ho, Properties of Electron Beam Welded SAF 2205 Duplex Stainless Steel. J. Mater. Process. Technol., 1997, 63, p 770–775

    Article  Google Scholar 

  3. X. Wu, R.S. Chandel, H. Li, H.P. Seow, and S. Wu, Induction Brazing of Inconel 718 to Inconel X-750 Using Ni-Cr-Si-B Amorphous Foil. Mater. Sci. Eng., 2000, 104, p 34–43

    Google Scholar 

  4. G.O. Cook and C.D. Sorensen, Overview of Transient Liquid Phase and Partial Transient Liquid Phase Bonding. J. Mater. Sci., 2011, 46, p 5305–5323

    Article  CAS  Google Scholar 

  5. R.A. Patterson and J.O. Milewski, GTA Weld Cracking—Alloy 625to304L. Weld. Res. Suppl., 1985, 64, p 227–231

    Google Scholar 

  6. R.S.K. Devendranath and R.N. Arivazhagan, Characterization of Microstructure, Strength and Toughness of Dissimilar Weldments of Inconel 625 and Duplex Stainless Steel SAF 2205. J. Acta Metall. Sin., 2014, 27, p 1018–1030

    Article  Google Scholar 

  7. K.D. Ramkumar, R. Sridhar, S. Periwal, S. Oza, V. Saxena, P. Hidad, and N. Arivazhagan, Investigations on the Structure—Property Relationships of Electron Beam Welded Inconel 625 and UNS 32205. J. Mater. Des., 2015, 68, p 158–166

    Article  Google Scholar 

  8. X. Wu, R.S. Chandel, S.H. Pheow, and H. Li, Brazing of Inconel X-750 to Stainless Steel 304 Using Induction Process. J. Mater. Sci. Eng. A., 2000, 288, p 84–90

    Article  Google Scholar 

  9. T.I. Khan, N. Orhan, and M. Eroglu, Transient Liquid Phase Bonding of a Microduplex Stainless Steel Using Amorphous Interlayers. J. Mater. Sci. Tecnol., 2016, 18, p 396–400

    Article  Google Scholar 

  10. A. Negemiya, S. Rajakumar, and V. Balasubramanian, A Study on the Interface Microstructure of Diffusion Bonded AISI 410/ SU 718 Dissimilar Joints. J. Adv. Microsc. Res., 2018, 13, p 61–64

    Article  Google Scholar 

  11. M. Mosallaee, A. Ekrami, K. Ohsasa, and K. Matsuura, Microstructural Evolution in the Transient Liquid Phase Bonding Area of IN-738LC/BNi-3/IN-738LC. J. Metall. Mater. Trans. A., 2008, 39, p 2389–2402

    Article  Google Scholar 

  12. R. Abdolvand, M. Atapour, M. Shamanian, and A. Allafchian, The Effect of Bonding Time on the Microstructure and Mechanical Properties of Transient Liquid Phase Bonding Between SAF 2507. J. Manuf. Process., 2017, 25, p 172–180

    Article  Google Scholar 

  13. M. Pouranvari, A. Ekrami, and A.H. Kokabi, Transient Liquid Phase Bonding of Wrought IN718 Nickel Based Superalloy Using Standard Heat Treatment Cycles: Microstructure and Mechanical Properties. J. Mater. Des., 2013, 50, p 694–701

    Article  CAS  Google Scholar 

  14. C. Hawk, S. Liu, and S. Kottilingam, Effect of Processing Parameters on the Microstructure and Mechanical Properties of Wide-Gap Braze Repairs on Nickel-Superalloy René 108. J. Weld. World., 2017, 61, p 391–404

    Article  CAS  Google Scholar 

  15. A. Ghoneim and O.A. Ojo, On the Influence of Boron-Addition on TLP Bonding Time in a Ni3Al-Based Intermetallic. J. Intermet., 2010, 18, p 582–586

    Article  CAS  Google Scholar 

  16. M. Pouranvari, A. Ekrami, A.H. Kokabi, and H.N. Han, Microstructural Characteristics of a Cast IN718 Superalloy Bonded by Isothermal Solidification. J. Met. Mater. Int., 2013, 19, p 1091–1099

    Article  CAS  Google Scholar 

  17. Handbook A. Volume 3: Alloy Phase Diagrams. (ASM International, Materials Park, 1992)

  18. X. Yuan, C.Y. Kang, and M.B. Kim, Characterization of Transient Liquid Phase Bonded Joints in a Duplex Stainless Steel with a Ni-Cr-B Insert Alloy. J. Mater. Charact., 2009, 60, p 1289–1297

    Article  CAS  Google Scholar 

  19. X. Yuan, C.Y. Kang, and M.B. Kim, Microstructure and XRD Analysis of Brazing Joint for Duplex Stainless Steel Using a Ni-Si-B Filler Metal. J. Mater. Charact., 2009, 60, p 923–931

    Article  CAS  Google Scholar 

  20. X.J. Yuan, M.B. Kim, and C.Y. Kang, Effects of Boron and Silicon on Microstructure and Isothermal Solidification during TLP Bonding of a Duplex Stainless Steel Using Two Ni-Si-B Insert Alloys. J. Mater. Sci. Technol., 2011, 27, p 1191–1197

    Article  CAS  Google Scholar 

  21. B. Kurt and A. Calik, Interface Structure of Diffusion Bonded Duplex Stainless Steel and Medium Carbon Steel Couple. J. Mater. Charact., 2009, 60(9), p 1035–1040

    Article  CAS  Google Scholar 

  22. A.T. Egbewande, C. Chukwukaeme, and O.A. Ojo, Joining of Superalloy Inconel 600 by Diffusion Induced Isothermal Solidification of a Liquated Insert Metal. J. Mater. Charact., 2007, 9, p 3–10

    Google Scholar 

  23. B. Binesh and A.J. Gharehbagh, Transient Liquid Phase Bonding of IN738LC/MBF-15/IN738LC: Solidification Behavior and Mechanical Properties. J. Mater. Sci. Technol., 2016, 32, p 1137–1151

    Article  Google Scholar 

  24. E. Norouzi, M. Atapour, and M. Shamanian, Effect of Bonding Time on the Joint Properties of Transient Liquid Phase Bonding Between Ti-6Al-4V and AISI 304. J. Alloys Compd., 2017, 701, p 335–341

    Article  CAS  Google Scholar 

  25. V. Jalilvand, H. Omidvar, M.R. Rahimipour, and H.R. Shakeri, Influence of Bonding Variables on Transient Liquid Phase Bonding Behavior of Nickel Based Superalloy IN-738LC. J. Mater. Des., 2013, 52, p 36–46

    Article  CAS  Google Scholar 

  26. L.X. Zhang, Z. Sun, Q. Xue, M. Lei, and X.Y. Tian, Transient Liquid Phase Bonding of IC10 Single Crystal with GH3039 Superalloy Using BNi-2 Interlayer: Microstructure and Mechanical Properties. J. Mater. Des., 2016, 90, p 949–957

    Article  CAS  Google Scholar 

  27. T. Vigraman, R. Narayanasamy, and D. Ravindran, Microstructure and Mechanical Property Evaluation of Diffusion-Bonded Joints Made Between SAE 2205 Steel and AISI 1035 Steel. J. Mater. Des., 2012, 35, p 156–169

    Article  CAS  Google Scholar 

  28. B. Rhee, S. Roh, and D. Kim, Transient Liquid Phase Bonding of Nitrogen Containing Duplex Stainless Steel UNS S31803 Using Ni-Cr-Fe-Si-B Insert Metal. Mater. Trans., 2003, 44, p 1014–1023

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran

    E. Baharzadeh & M. Rafiei

  2. Department of Materials Engineering, Isfahan University of Technology, 84156-83111, Isfahan, Iran

    M. Shamanian

  3. Department of Materials and Metallurgical Engineering, Faculty of Engineering, Arak University, Arāk, Iran

    H. Mostaan

Authors
  1. E. Baharzadeh
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. M. Shamanian
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. M. Rafiei
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. H. Mostaan
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to M. Rafiei.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Baharzadeh, E., Shamanian, M., Rafiei, M. et al. Microstructural and Mechanical Evaluations of Transient Liquid Phase Bonded In X-750/BNi-3/SAF 2205. J. of Materi Eng and Perform 29, 1090–1100 (2020). https://doi.org/10.1007/s11665-020-04620-4

Download citation

  • Received:

  • Revised:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11665-020-04620-4

Keywords

Search

Navigation