Abstract
Polycrystalline \({\hbox {La}}_{1-x}{\hbox {Sr}}_x{\hbox {ZnAsO}}\) (0.00 \(\le \) x \(\le \) 0.075 ) was synthesized by solid-state reactions followed by hot pressing. The sign of the Seebeck coefficient changed from negative to positive by Sr doping, indicating that holes were successfully doped as a result of Sr substitutions. The maximum power factor of 0.118 mW/m K\(^2\) was attained at \(T = 747\) K in \(x = 0.05\). The thermal conductivity was relatively low at \(T = 773\) K, with a value of approximately 1.9 W/m K independent of Sr doping. These results led to a dimensionless figure-of-merit ZT of 0.044 at \(T = 747\) K in \(x = 0.05\).
Similar content being viewed by others
References
Y. Kamihara, T. Watanabe, M. Hirano, and H. Hosono, J. Am. Chem. Soc. 130, 3296 (2008).
T. Suzuki, M.S. Bahramy, R. Arita, Y. Taguchi, and Y. Tokura, Phys. Rev. B 83, 035204 (2011).
K. Guo, Z.Y. Man, X.J. Wang, H.H. Chen, M.B. Tang, Z.J. Zhang, Y. Grin, and J.T. Zhao, Dalton Trans. 40, 10007 (2011).
M. Pan, K. Wang, W. Lv, D. Hu, K. Guo, X. Yang, and J.T. Zhao, J. Alloys Compd. 688, 153 (2016).
J. Liu, J. Wang, C.L. Wang, and S.Q. Xia, J. Alloys Compd. 688, 849 (2016).
L.D. Zhao, D. Berardan, Y.L. Pei, C. Byl, L. Pinsard-Gaudart, and N. Dragoe, Appl. Phys. Lett. 97, 092118 (2010).
J. Li, J. Sui, Y. Pei, C. Barreteau, D. Berardan, N. Dragoe, W. Cai, J. He, and L.D. Zhao, Energy Environ. Sci. 5, 8543 (2012).
J.L. Lan, Y.C. Liu, B. Zhan, Y.H. Lin, B. Zhang, X. Yuan, W. Zhang, W. Xu, and C.W. Nan, Adv. Mater. 25, 5086 (2013).
J. Sui, J. Li, J. He, Y.L. Pei, D. Berardan, H. Wu, N. Dragoe, W. Caia, and L.D. Zhao, Energy Environ. Sci. 6, 2916 (2013).
K. Kihou, C.H. Lee, K. Miyazawa, P.M. Shirage, A. Iyo, and H. Eisaki, J. Appl. Phys. 108, 033703 (2010).
T. Okuda, W. Hirata, A. Takemori, S. Suzuki, S. Saijo, S. Miyasaka, and S. Tajima, J. Phys. Soc. Jpn. 80, 044704 (2011).
K. Kihou, H. Nishiate, A. Yamamoto, and C.H. Lee, Inorg. Chem. 56, 3709 (2017).
H. Kunioka, K. Kihou, H. Nishiate, A. Yamamoto, H. Usui, K. Kuroki, and C.H. Lee, Dalton Trans. 47, 16205 (2018).
A.T. Nientiedt and W. Jeitschko, Inorg. Chem. 37, 386 (1998).
R. Pöttgen and D. Johrendt, Z. Naturforsch. B 63, 1135 (2008).
H. Lincke, R. Glaum, V. Dittrich, M.H. Möller, and R. Pöttgen, Z. Anorg. Allg. Chem. 635, 936 (2009).
S. Muir and M.A. Subramanian, Prog. Solid State Chem. 40, 41 (2012).
F. Izumi and K. Momma, Solid State Phenom. 15–20, 130 (2007).
P. Blaha, K. Schwarz, G.K.H. Madsen, D. Kvasnicka, and J. Luitz, WIEN2K: An Augmented Plane Wave Plus Local Orbitals Program for Calculating Crystal Properties (Technische Universität Wien, Vienna, 2001).
A.D. Becke and E.R. Johnson, J. Chem. Phys. 124, 221101 (2006).
F. Tran and P. Blaha, Phys. Rev. Lett. 102, 226401 (2009).
K. Kayanuma, R. Kawamura, H. Hiramatsu, H. Yanagi, M. Hirano, T. Kamiya, and H. Hosono, Thin Solid Films 516, 5800 (2008).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
About this article
Cite this article
Kimura, Y., Kunioka, H., Kihou, K. et al. Thermoelectric Properties of \({\hbox {La}}_{1-x}{\hbox {Sr}}_x{\hbox {ZnAsO}}\). J. Electron. Mater. 49, 6715–6720 (2020). https://doi.org/10.1007/s11664-020-08439-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-020-08439-6