Abstract
A thermoelectric thin-film device of the cross-plane configuration was fabricated by flip-chip bonding of the top electrodes to 242 pairs of electrodeposited n-type Bi2Te3 and p-type Sb2Te3 thin-film legs on the bottom substrate. The electrodeposited Bi2Te3 and Sb2Te3 films of 20-μm thickness exhibited Seebeck coefficients of −59 μV/K and 485 μV/K, respectively. The internal resistance of the thin-film device was measured as 3.7 kΩ, most of which was attributed to the interfacial resistance of the flip-chip joints. The actual temperature difference ΔT G working across the thin-film legs was estimated to be 10.4 times smaller than the apparent temperature difference ΔT applied across the thin-film device. The thin-film device exhibited an open-circuit voltage of 0.294 V and a maximum output power of 5.9 μW at an apparent temperature difference ΔT of 22.3 K applied across the thin-film device.
Similar content being viewed by others
References
J.P. Carmo, J.F. Ribeiro, M.F. Goncalves, and J.H. Correia, J. Micromech. Microeng. 20, 1 (2010).
W. Glatz, E. Schwyter, L. Durrer, and C. Hierold, J. Microelectromech. Syst. 18, 763 (2009).
Z. Wang, B. Leonov, P. Fiorini, and C.V. Hoof, Sens. Actuators A 156, 95 (2009).
J. Xie, C. Lee, and H. Feng, J. Microelectromech. Syst. 19, 317 (2010).
M. Takashiri, T. Shirakawa, K. Miyazaki, and H. Tsukamoto, Sens. Actuators A 138, 329 (2007).
G.J. Snyder, J.R. Lim, C.-K. Huang, and J.-P. Fleurial, Nat. Mater. 2, 528 (2003).
H. Bottner, J. Nurnus, A. Gavrikov, G. Kuhner, M. Jagle, C. Kunzel, D. Eberhard, G. Plescher, A. Schubert, and K.-H. Schlereth, J. Microelectromech. Syst. 13, 414 (2004).
T.S. Oh, K.Y. Lee, Y.H. Lee, and B.Y. Jung, Met. Mater. Int. 15, 479 (2009).
T.S. Oh, K.Y. Lee, and H.Y. Won, IEEE Trans. Comp. Packag. Technol. 32, 909 (2009).
M.Y. Kim and T.S. Oh, Thin Solid Films 518, 6550 (2010).
S.K. Lim, M.Y. Kim, and T.S. Oh, Thin Solid Films 517, 4199 (2009).
M.Y. Kim and T.S. Oh, Mater. Trans. 53, 2160 (2012).
M.S. Gonzalez, A.L. Prieto, R. Gronsky, T. Sands, and A.M. Stacy, J. Electrochem. Soc. 149, C546 (2002).
K. Tittes, A. Bund, W. Plieth, A. Bentien, S. Paschen, M. Plotner, H. Grafe, and W.-J. Fischer, J. Solid State Electrochem. 7, 714 (2003).
S. Michel, S. Diliberto, C. Boulanger, and B. Bolle, J. Cryst. Growth 296, 227 (2006).
T.S. Oh, D.B. Hyun, and N.V. Kolomoets, Scripta Mater. 42, 849 (2000).
W.M. Yim and F.D. Rosi, J. Solid State Electron. 15, 1121 (1972).
Y. Kim, A. DiVenere, G.K.L. Wong, J.B. Ketterson, S. Cho, and J.R. Meyer, J. Appl. Phys. 91, 715 (2002).
L.M. Goncalves, P. Alpuim, A.G. Rolo, and J.H. Correia, Thin Solid Films 519, 4152 (2011).
S.A. Baily and D. Emin, Phys. Rev. B 73, 165211 (2006).
V.D. Das, N. Soundararajan, and M. Pattabi, J. Mater. Sci. 22, 3522 (1987).
Y.A. Cengel, Introduction to Thermodynamics and Heat Transfer, Vol. II (Boston: McGraw-Hill, 2001), p. A-25.
K. Miyazaki, M. Takashiri, J. Kurosaki, B. Lenoir, A. Dauscher, and H. Tsukamoto, 26th Int. Conf. on Thermoelectrics (2007), p. 294.
G.-H. Dong, Y.-J. Zhu, and L.-D. Chen, J. Mater. Chem. 20, 1976 (2010).
D.M. Rowe, Thermoelectrics Handbook: Macro to Nano (New York: CRC Press, 2006), p. 16.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kim, MY., Oh, TS. Thermoelectric Power Generation Characteristics of a Thin-Film Device Consisting of Electrodeposited n-Bi2Te3 and p-Sb2Te3 Thin-Film Legs. J. Electron. Mater. 42, 2752–2757 (2013). https://doi.org/10.1007/s11664-013-2671-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-013-2671-3