Effect of Oxidation with Lanthanum Sol–Gel Coating on the 330Cb Carburization at 900 °C

  • Original Paper
  • Published:
Oxidation of Metals Aims and scope Submit manuscript

Abstract

Corrosion and carburization are the main reasons for the degradation of mechanical properties of conveyor units. In order to improve alloy carburization resistance, an adherent oxide scale can act as a carbon diffusion barrier. Oxidation of Alloy 330Cb in air at 900 °C was performed in order to grow a protective chromia scale. Nevertheless, after oxidation some scale spallation occurred during cooling. Then, argon-annealed lanthanum sol–gel coatings were applied in order to improve the oxide scale adherence. This led to a thinner chromia scale. The convoluted scale structure suggested that a mixed diffusion process was induced by lanthanum. After carburization during 22 h at 900 °C under Ar/10 % CH4, the Cr2O3 scale was converted into carbides and it appears that is necessary to have a thick oxide scale to get a good protection.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6

Similar content being viewed by others

References

  1. R. Stevens, Oxidation of Metals 13, 353 (1979).

    Article  CAS  Google Scholar 

  2. F. I. Wei and F. H. Stott, High Temperature Technology 7, 59 (1989).

    CAS  Google Scholar 

  3. H. B. Grubmeier, A. Naoumidis, and H. A. Schulze, Journal of Vacuum Science & Technology A4–6, 2565 (1986).

    Google Scholar 

  4. M. Yamawaki, M. Mito, and M. Kanno, Transactions of the Japan Institute of Metals 18, 567 (1977).

    CAS  Google Scholar 

  5. D. V. Miley and G. R. Smolik, Microstructural Science 10, 43 (1982).

    CAS  Google Scholar 

  6. K. T. Voisey, Z. Liu, and F. H. Stott, Applied Surface Science 252, 3658 (2006).

    Article  CAS  Google Scholar 

  7. J. Zhang and D. J. Young, Corrosion Science 49, 1450 (2007).

    Article  CAS  Google Scholar 

  8. Y. Nishiyama, K. Kitamura, and N. Otsuka, Materials Science Forum 595–598, 649 (2008).

    Article  Google Scholar 

  9. P. S. N. Stokes, F. H. Stott, and G. C. Wood, Materials Science and Engineering A121, 549 (1989).

    Google Scholar 

  10. G. H. Meier, W. C. Coons, and R. A. Perkins, Oxidation of Metals 17, 235 (1982).

    Article  CAS  Google Scholar 

  11. J. Kallqvist and H.-O. Andrén, Materials Science and Engineering A270, 27 (1999).

    CAS  Google Scholar 

  12. O. Yoo, Y.-J. Oh, B.-S. Lee, and S. W. Nama, Materials Science and Engineering A405, 147 (2005).

    CAS  Google Scholar 

  13. F. J. Pérez, E. Otero, M. P. Hierro, C. Gomez, F. Pedraza, J. L. de Segovia, and E. Roman, Surface and Coating Technology 108–109, 127 (1998).

    Article  Google Scholar 

  14. E. Lang, M. J. Bennett, and C. F. Knights, Materials Science and Engineering 88, 37 (1987).

    Article  CAS  Google Scholar 

  15. B. Gleeson and M. A. Harper, Oxidation of Metals 49, 373 (1998).

    Article  CAS  Google Scholar 

  16. S. Fontana, R. Amendola, S. Chevalier, P. Piccardo, G. Caboche, M. Viviani, R. Molins, and M. Sennour, Journal of Power Sources 171, 652 (2007).

    Article  CAS  Google Scholar 

  17. L. V. Ramanathan, M. F. Pillis, and S. M. C. Fernandes, Journal of Materials Science 43, 530 (2008).

    Article  CAS  Google Scholar 

  18. J. S. Yoon, J. Lee, H. J. Hwang, C. MungWhang, J.-W. Moon, and D.-H. Kim, Journal of Power Sources 181, 281 (2008).

    Article  CAS  Google Scholar 

  19. G.-M. Zhao and K.-L. Wang, Surface and Coating Technology 190, 249 (2005).

    Article  CAS  Google Scholar 

  20. H. Buscail, C. Issartel, F. Riffard, R. Rolland, S. Perrier, A. Fleurentin, and C. Josse, Applied Surface Science 258, 678 (2011).

    Article  CAS  Google Scholar 

  21. A. Paúl and J. A. Odriozola, Materials Science and Engineering A300, 22 (2001).

    Google Scholar 

  22. A. Paúl, S. Elmrabet, and J. A. Odriozola, Journal of Alloys and Compounds 323–324, 70 (2001).

    Article  Google Scholar 

  23. A. Paúl, S. Elmrabet, F. J. Ager, J. A. Odriozola, M. A. Respaldiza, M. F. da Silva, and J. C. Soares, Oxidation of Metals 57, 33 (2002).

    Article  Google Scholar 

  24. Q. Zhang, J. Lu, and F. Saito, Powder Technology 122, 145 (2002).

    Article  CAS  Google Scholar 

  25. A. Paúl, R. Sanchez, O. M. Montes, and J. A. Odriozola, Oxidation of Metals 67, 87 (2007).

    Article  Google Scholar 

  26. W. Qu, J. Li, and D. G. Ivey, Journal of Power Sources 138, 162 (2004).

    Article  CAS  Google Scholar 

  27. B. A. Pint, Oxidation of Metals 45, 1 (1996).

    Article  CAS  Google Scholar 

  28. F. H. Stott, G. C. Wood, and J. Stringer, Oxidation of Metals 44, 113 (1995).

    Article  CAS  Google Scholar 

  29. V. K. Tolpygo and D. R. Clarke, Acta Materialia 46, 5153 (1998).

    Article  CAS  Google Scholar 

  30. F. A. Golightly, G. C. Wood, and F. H. Stott, Oxidation of Metals 14, 217 (1980).

    Article  CAS  Google Scholar 

  31. P. Y. Hou and J. Stringer, Journal of Physique IV C9, 231 (1993).

    Google Scholar 

  32. A. G. Evans, G. B. Crumley, and R. E. Demaray, Oxidation of Metals 20, 193 (1983).

    Article  Google Scholar 

  33. F. Riffard, H. Buscail, E. Caudron, R. Cueff, C. Issartel, and S. Perrier, Journal of Materials Science 37, 3925 (2002).

    Article  CAS  Google Scholar 

  34. F. J. Pérez, M. J. Cristobal, M. P. Hierro, and F. Pedraza, Surface and CoatingTechnology 120–121, 442 (1999).

    Article  Google Scholar 

  35. A. T. Allen and D. L. Douglass, Oxidation of Metals 51, 199 (1999).

    Article  CAS  Google Scholar 

  36. K. Bongartz, W. J. Quadakkers, R. Schulten, and H. Nickel, Metallurgical Transactions A20, 1021 (1989).

    Google Scholar 

  37. D. Young, High Temperature Oxidation and Corrosion of Metals, (Elsevier, Amsterdam, 2008), pp. 403.

    Google Scholar 

  38. I. Wolf and H. J. Grabke, Solid State Communications 54, 5 (1985).

    Article  CAS  Google Scholar 

  39. H. J. Grabke and I. Wolf, Materials Science and Engineering 87, 23 (1987).

    Article  CAS  Google Scholar 

  40. T. Gheno, D. Monceau, J. Zhang, and D. Young, Corrosion Science 53, 2767 (2011).

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. LVEEM, Université d’Auvergne, 8 rue J.B. Fabre, BP 219, 43006, Le Puy en Velay, France

    Christophe Issartel, Henri Buscail, Raphael Rolland & Sébastien Perrier

  2. CETIM, 52 Avenue Félix Louat, BP 80067, 60304, Senlis, France

    Alexandre Fleurentin

Authors
  1. Christophe Issartel
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Henri Buscail
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Raphael Rolland
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Sébastien Perrier
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Alexandre Fleurentin
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Christophe Issartel.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Issartel, C., Buscail, H., Rolland, R. et al. Effect of Oxidation with Lanthanum Sol–Gel Coating on the 330Cb Carburization at 900 °C. Oxid Met 80, 467–478 (2013). https://doi.org/10.1007/s11085-013-9390-2

Download citation

  • Received:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11085-013-9390-2

Keywords

Search

Navigation