Abstract
Functional spinel ferrite fibers are attractive for high-tech applications. The spinel NiFe2O4 fibres have been successfully prepared by the organic gel-thermal decomposition process from raw materials of Ni, Fe nitrate salts and citric acid. The gel spinning performance was a major factor for preparation of uniform gel fibrous precursors. The gel spinnability was related to the citrate-metal complex structure and linear-type structural molecules [(C6H6O7)4NiFe2]n for the gel precursor was possibly formed during the complexation reaction between the citric acid and metal ions at pH 5. The composition, structure of the gel precursors and products derived from thermal decomposition of these precursors were characterized by FTIR, XRD, and SEM. The thermal decomposition process of the gel precursors was investigated by TG-DSC. The prepared spinel NiFe2O4 fibres having grain sizes of 60–70 nm were featured with diameters of about 1 μm, and aspect ratios up to 106 (length/diameter).
Similar content being viewed by others
References
Giannakopoulou T, Kompotiatis L, Kontogeorgakos A, Kordas G (2002) Microwave behavior of ferrites prepared via sol-gel method. J Magnetism Magn Mater 246:360–365
Toshiyuki S, Terumitsu T, Kaoru I (2001) High density recording capability for advanced particulate media. J Magnetism Magn Mater 235:159–164
Sudakar C, Subbanna GN, Kutty TRN (2004) Nanoparticle composites having structural intergrowths of hexaferrite and spinel ferrites prepared by gel-to-crystallite conversion and their magnetic properties. J Magnetism Magn Mater 268:75–88
John Berchmans L, Kalai Selvan R, Selva Kumar PN, Augustin CO (2004) Structural and electrical properties of Ni1-XMgXFe2O4 synthesized by citrate gel process. J Magnetism Magn Mater 279:103–110
Hale DK (1976) Physical properties of composite materials. J Mater Sci 11:2105–2141
Harris A. Goldberg (1988) High magnetic permeability composites containing fibres with ferrite fill.US States Patent, (4725490)
Pullar RC, Taylor MD, Bhattacharya AK (1997) Novel aqueous sol-gel preparation and characterization of barium M ferrite, BaFe12O19 fibres. J Mater Sci 32:349–352
Tsai MT (2003) Preparation and Crystallization of Forsterite Fibrous Gels. J Eur Ceramic Soc 23:1283–1291
Pullar RC, Appleton SG, Bhattacharya AK (1998) The manufacture,characterization and microwave properties of aligned M ferrite fibres. J Magnetism Magn Mater 186:326–332
Sileo Elsa E, Ramiro R, Jacobo Silvia E (2002) Nickel zinc ferrites prepared by the citrate precursor method. Physica B 320:257–260
Panda RN, Shih JC, Chin TS (2003) Magnetic properties of nano-crystalline Gd- or Pr-substituted CoFe2O4 synthesized by the citrate precursor technique. J Magnetism Magn Mater 257:79–86
Zhang H, Jia X, Yan Y, Liu Z (2004) The effect of the concentration of citric acidand pH values on thepreparation of MgAl2O4 ultrafine powder by citrate sol-gel process. Mater Res Bull 39:839–850
Song HJ, Oh JH, Chol SC, Lee JC (2002) Preparation and characterization of Ni ferrite powders by urea decomposition. Phy Status Solidi A 189(3):849–852
Nakamoto K. Huang Deru (1986) Wang Renqing. Infrared and Raman Spectra of Inorganic and Coordination Compounds[M]. Beijing:The Press Co of Chemical Industry 231–244
Timothy Strathmann J, Myneni Satish CB (2004) Speciation of aquous Ni(ii)-Fulyic acid solution: combined ATR-FTIR and XAFS analysis. Geochimica et Cosmochimica Acta 68(17):3441–3458
Zhenxing Yue, Ji Zhou, Longtu Li, Hongguo Zhang, Zhilun Gui (2000) Sythesis of nanocrystalline NiCuZn ferrite powders by sol-gel auto-combustion method. J Magnetism Magn Mater 208:55–60
Wu KH, Yu CH, Chang YC et al. (2004) Effect of pH on the formation and combustion process of sol-gel auto-combustion derived NiZn ferrite/SiO2 composites. J Solid State Chem 177:4119–4125
Acknowledgments
This study was supported by the National Nature Science Foundation of China (No. 50474038).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zhang, CY., Shen, XQ., Zhou, JX. et al. Preparation of spinel ferrite NiFe2O4 fibres by organic gel-thermal decomposition process. J Sol-Gel Sci Technol 42, 95–100 (2007). https://doi.org/10.1007/s10971-006-1515-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10971-006-1515-5