Abstract
In this research for the first time, SrCrO4 nanoparticles were prepared using sol–gel procedure in which amino acid was used as stabilization agent. Different amino acids were used as capping, stabilizer, or reduction agent. In this regard, the effect of Glycine, Alanine, Valin, and Leucine were evaluated on the morphology and crystalline degree of the SrCrO4 nanoparticles. The amino acid has both roles of reduction and capping agent. The molar ratio for Sr3+: Cr3+: amino acid was 1: 1: 4, respectively. In the next step, photodeposition process was used for preparation of SrCrO4/Ag nanostructures. The prepared products were evaluated by using TGA, XRD, EDS, SEM, TEM, DRS, and BET. XRD result indicated that crystalline degree and purity of the nanostructures prepared in the presence of leucine were more when compared with the other samples. On the other hand, based on the Scherrer equation, the average particle size for the optimum specimen was nearly 9 nm. The SrCrO4/Ag nanocomposite which was obtained using leucine showed a high activity in organic dye degradation. We think that this high catalytic activity can be attributed to the synergistic effect between Ag and SrCrO4 nanoparticles.
Similar content being viewed by others
References
Y.B. Mao, S.S. Wong, J. Am. Chem. Soc. 126, 15245 (2004)
M. Kobayashi, M. Ishii, Y. Usuki, Nucl. Instrum. Methods Phys. Res. Sect. A 406, 442 (1998)
J.H. Xiang, S.H. Yu, X. Geng, B.H. Liu, Y. Xu, Cryst. Growth. Des. 3, 1157 (2005)
S. Driscoll, U.S. Ozkan, Stud. Surf. Sci. Catal. 82, 367 (1994)
J.H. Xiang, S.H. Yu, Z.L. Xu, Cryst. Growth Des. 6, 1311 (2004)
S.H. Yu, M. Antonietti, H. Colfen, M. Giersig, Angew. Chem. Int. Ed. 41, 2356 (2002)
S.M. Pourmortazavi, M. Rahimi-Nasrabadi, S.S. Hajimirsadeghi, J. Dispersion Sci. Technol. 33, 254 (2012)
W.S. Wang, C.Y. Xu, L. Zhen, L. Yang, W.Z. Shao, Chem. Lett. 35, 268 (2006)
D. Chen, K.B. Tang, S.Y. Zhang, H.G. Zheng, Y.T. Qian, J. Nanosci. Nanotechnol. 6, 738 (2006)
X.H. Yang, Q.S. Wu, J.K. Lju, Cryst. Res. Technol. 42, 211 (2007)
Y. Jiang, Z. Zhigang, Y. Jinhua, Chem. Phys. Lett. 378, 24–28 (2003)
Gh.K. Tanmay, B. Niladri, J. Mater. Res. Technol. 2, 10–17 (2013)
A. Abbasi, H. Khojasteh, M. Hamadanian, M. Salavati-Niasari, Sep. Pure Technol. 195, 37–49 (2018)
A. Abbasi, H. Khojasteh, M. Hamadanian, M. Salavati-Niasari, J. Mater. Sci. 27, 4972–4980 (2016)
A. Abbasi, D. Ghanbari, M. Hamadanian, M. Salavati-Niasari, J. Mater. Sci. 27, 4800–4809 (2016)
A. Abbasi, M. Hamadanian, T. Gholami, M. Salavati-Niasari, N. Sadri, Sep. Pure Technol. 209, 79–87 (2019)
M.A. Marsooli, M. Fasihi-Ramandi, K. Adib, S. Pourmasoud, F. Ahmadi, M.R. Ganjali, A. Sobhani Nasab, M. Rahimi Nasrabad, M. Plonska-Brzezinska, Materials 12, 3274 (2019)
A. Ziarati, A. Badiei, R. Grillo, T. Burgi, A.C.S. Appl, Mater. Interfaces 11, 5903 (2019)
A. Ziarati, A. Badiei, R. Luque, Appl. Catal. B 240, 72 (2019)
E.M. Chan, R.A. Mathies, A.P. Alivisatos, Nano Lett. 3, 199 (2003)
D.J. Milliron, S.M. Hughes, Y. Cui, L. Manna, J. Li, L.W. Wang, A.P. Alivisatos, Nature 430, 190 (2004)
S.M. Pourmortazavi, S.S. Hajimirsadeghi, M. Rahimi-Nasrabadi, Mater. Sci. Semicond. Process. 16, 131 (2013)
E. Sohouli, M. Ghalkhani, M. Rostami, M. Rahimi-Nasrabadi, F. Ahmadi, Mater. Sci. Eng. C 117, 111300 (2020)
M. Rahimi-Nasrabadi, S.M. Pourmortazavi, M. Aghazadeh, M.R. Ganjali, M.S. Karimi, P. Norouzi, J. Mater. Sci. Mater. Electron. 28, 9478 (2017)
H. Khojasteh, V. Mirkhani, M. Moghadam, S. Tangestaninejad, I. Mohammadpoor-Baltork, J. Nanostruct. 5, 271 (2015)
M. Rahimi-Nasrabadi, F. Ahmadi, M. Eghbali-Arani, J. Mater. Sci. Mater. Electron. 27, 13294 (2016)
M. Rahimi-Nasrabadi, A. Ghaderi, H.R. Banafshe, M. Eghbali-Arani, M. Akbari, S. Pourmasoud, A. Sobhani-Nasab, J. Mater. Sci. Mater. Electron. 30, 15854 (2019)
S.M. Peymani-Motlagh, A. Sobhani-Nasab, M. Rostami, H. Sobati, M. Eghbali-Arani, M. Fasih-Ramandi, M.R. Ganjali, M. Rahimi-Nasrabadi, J. Mater. Sci. Mater. Electron. 30, 6902 (2019)
X.M. Sun, Y.D. Li, J. Chem. Eur. 9, 2229 (2003)
S. Kar, S. Chaudhuri, J. Phys. Chem. B 109, 3298 (2005)
S. Mortazavi-Derazkola, M. Salavati-Niasari, M.-P. Mazhari, H. Khojasteh, M. Hamadanian, S. Bagheri, J. Mater. Sci. 28, 14271 (2017)
M. Wysokowski, M. Motylenko, D. Rafaja, I. Koltsov, H. Stöcker, T.J. Szalaty, V.V. Bazhenov, A.L. Stelling, J. Beyer, J. Heitmann, T. Jesionowski, S. Petovic, M. Đurović, H. Ehrlich, Mater. Chem. Phys. 188, 115 (2017)
M. Rahimi-Nasrabadi, J. Mater. Sci. Mater. Electron. 28, 6373 (2017)
A. Abbasi, A.H. Keihan, M. Rahimi-Nasrabadi, M. Wysokowski, T. Jesionowski, Y. Joseph, H. Ehrlich, S.M. SafarSajadi, J. Mater. Sci. Mater. Electron. 30, 13994 (2019)
S. Rohani, A. Ziarati, G.M. Ziarani, A. Badiei, T. Bürgi, Catal. Sci. Technol. 9, 3820 (2019)
S. Rohani, G.M. Ziarani, A. Ziarati, A. Badiei, Appl. Surf. Sci. 496, 143599 (2019)
M. Rahimi-Nasrabadi, S.M. Pourmortazavi, M. Aghazadeh, M.R. Ganjali, M. SadeghpourKarimi, P. Novrouzi, J. Mater. Sci. Mater. Electron. 28, 5574 (2017)
X.-H. Yang, Q.-S. Wu, J.-K. Liu, Cryst. Res. Technol. 42, 211–215 (2007). https://doi.org/10.1002/crat.200610801
A. Abbasi, H. Khojasteh, M. Hamadanian, M. Salavati-Niasari, Sep. Purif. Technol. 195, 37–49 (2018)
H. Khojasteh, M. Salavati-Niasari, M.-P. Mazhari, M. Hamadanian, RSC Adv. 6, 78043 (2016)
Author information
Authors and Affiliations
Corresponding authors
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Katouli, H., Khojasteh, H., Ahmadi Golsefidi, M. et al. Grafting of Ag nanoparticles on SrCrO4 nanostructures: green synthesis, characterization, and photocatalytic study for organic dye degradation. J Mater Sci: Mater Electron 32, 384–396 (2021). https://doi.org/10.1007/s10854-020-04788-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-020-04788-4