Abstract
Both Sn addition and pre-ageing are known to be effective in maintaining the artificial ageing potential after natural ageing of Al–Mg–Si alloys. In this study, the combined effects of Sn addition and pre-ageing at 100 °C or 180 °C on natural secondary ageing and subsequent artificial ageing of an alloy AA6014 were investigated using hardness, electrical resistivity, differential scanning calorimetry and transmission electron microscopy characterizations. It is found that pre-ageing can suppress natural secondary ageing and improve the artificial ageing hardening kinetics and response after 1 week of natural secondary ageing in both alloys with and without Sn addition. The effect of pre-ageing at 100 °C is more pronounced in the Sn-free alloy while the combination of pre-ageing at 180 °C and adding Sn shows superiority in suppressing natural secondary ageing and thus avoiding the undesired hardening before artificial ageing. Moreover, when natural ageing steps up to 8 h are applied before pre-ageing at 100 °C, the effect of pre-ageing in Sn-added alloy can be further improved. The influence of Sn on vacancies at different ageing temperatures is discussed to explain the observed phenomena.
Graphical abstract
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
The age-hardenability of Al–Mg–Si alloys is of great importance for their industrial application. Ideally, artificial ageing (AA) at ~ 180 °C is carried out immediately after quenching from the solutionising temperature (~ 540 °C) to strengthen the alloys by the formation of needle-like monoclinic β’’ precipitates [1, 2]. In practice, however, a delay at room temperature (RT) after solutionising is inevitable and leads to a reduction in the hardening kinetics and the achievable strength during the following AA [3,4,5]. One reason for this negative effect of natural ageing (NA) lies in the fact that clusters formed during NA cannot transform into β’’ during AA [6] but rather reduce the solute supersaturation. Another possible explanation might be that the vacancy concentration, which plays a vital role in the diffusion of solute atoms, is lowered by the annihilation of vacancies by sinks [7] and the “vacancy-prison” effect of the formed NA clusters [8]. To compensate the adverse effect of NA, various methods have been developed over the past decades.
One viable method is microalloying the Al alloy with Sn, which can bind with vacancies strongly at RT. As the diffusion of solute atoms requires vacancies, a reduction of available vacancies can greatly retard the undesired NA [9]. Upon subsequent AA, the binding between Sn atoms and vacancies weakens and some of the trapped vacancies are released, thus facilitating the subsequent precipitation and establishment of the vacancy equilibrium at 180 °C [9]. As a result, a significant AA hardening potential can be obtained in a Sn-added alloy even after long NA [10].
Another commonly used method is pre-ageing (PA). In this approach, samples are artificially underaged immediately after solutionising and quenching, which improves the AA response after NA [4, 11,12,13,14,15,16]. The PA temperature is normally above a critical value (~ 67 °C) and favours the formation of PA clusters, which then may further grow into β’’ precipitates during the following AA [17]. Note that in this paper, the term “PA cluster” is used to label the phase formed during PA, regardless of the different notations found in the literature, including PA cluster [15], Cluster (2) [18], GP zone [19, 20] and pre-β’’ [21]. Although pre-ageing has been proved to be efficient in diminishing the negative effect of NA, the accompanying strength increase and also the strengthening during following natural secondary ageing (NSA) reduces formability. Therefore, it has been suggested by some researchers [14, 22] that the PA time and temperature must be controlled in order to achieve a trade-off between an acceptable formability and a good AA response. The above-mentioned potential of added Sn in maintaining the alloy’s stability at RT might provide additional freedom in finding favourable conditions, which has been the motivation for this work.
Moreover, the effect of microalloying (e.g. Cu and Ag) on the performance of PA has been investigated. It was found that Cu addition modifies the cluster composition and enhances the formation of clusters that can act as precursors of elongated precipitates [23]. Weng et al. [24] claimed that the attractive interaction between Cu/Ag and Mg enables the nucleation of Mg-Si-Cu(Ag) co-clusters and therefore increases the number density of PA clusters. Nevertheless, the possibility of combining PA treatment and Sn addition in diminishing the detrimental effect of NA on the subsequent AA (both hardening rate and peak strength) has so far received little attention. A strategy in realizing the potential of these two methods concurrently is still pending. Thus, in the present work, we explore this possibility systematically. PA at both low and high temperatures (100 °C and 180 °C) is carried out on Al–Mg–Si alloys with and without Sn addition, and the mechanism controlling the following natural secondary ageing (NSA) and artificial ageing (AA) is clarified. Moreover, a designed combination of PA and Sn addition should contribute to overcoming the negative effect of NA on AA.
Experimental
Industrial AA6014 alloys with and without Sn were manufactured by the Novelis Research and Technology Center Sierre and received as sheets of 1 mm thickness. The alloy compositions are given in Table 1. The two alloys contain the same total amount (1.35 at.%) of main alloying elements, but differ slightly in Mg, Si and Cu contents. Solution heat treatment (SHT) was performed at 570 °C for 60 min with argon as a protective gas followed by a quench in ice water. Samples were then either stored in an incubator running at 20 °C for NA or immersed into an oil bath held at 100 °C or liquid metal (LM) Bi57Sn43 at 180 °C for PA. After PA, the same incubator was employed for the subsequent NSA. Optional natural ageing at 20 °C for 4 h or 8 h was conducted before PA at 100 °C for alloy 6014-70Sn. Final AA was carried out in LM at 180 °C after 1 week of NA/NSA. 30 min AA is used to simulate a typical paint baking (PB). The heat treatment procedures are described in Fig. 1.
After heat treatments, Brinell hardness was measured by employing a Qness 60 M tester (1 mm diameter tungsten carbide indenter, 10 kg load and 10 s loading time). At least 10 indentations were performed for each sample. In-situ electrical resistivity measurements were performed using a four-point probe system with a current of 100 mA. Sample wires (usually 500 mm long, 0.82 mm in diameter) were kept in an oil bath at 20 °C during the measurements. The change of resistivity (Δρ) during NA/NSA is calculated by subtracting the initial value measured after 2 min to 3 min NA/NSA. Differential scanning calorimetry (DSC) measurements were carried out on 1-mm thick samples of 5 mm diameter in a Netzsch 204 F1 Phoenix, with a reference sample of pure Al (99.999%). To avoid storage at RT, samples were stored in liquid nitrogen immediately after the various heat treatments. After being held for 5 min in the pre-cooled (0 °C) chamber, DSC analyses were performed from 0 to 400 °C with a scanning rate of 10 K min−1. The curve obtained with two empty crucibles was used as the baseline. For TEM characterizations, samples were firstly ground to less than 0.1 mm in thickness, punched into discs (3 mm in diameter) and then electrolytically thinned with electrolyte of 24 vol.% nitric acid and 76 vol.% methanol at − 30 °C. TEM images were obtained using a FEI Tecnai G2 F20 S-TWIN TEM operated at 200 kV. High-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) imagining was performed on a spherical aberration probe corrected FEI Titan G2 80–200 ChemiSTEM operated at 200 kV.
Results
State during natural (secondary) ageing (NA/NSA)
After solutionising and quenching, Sn addition delays hardening during NA. Alloy 6014 shows a continuous hardness increase upon ageing, while alloy 6014-70Sn maintains a nearly constant hardness for 8 h before an increase is observed (grey lines in Fig. 2). After ½ year, both alloys reach ~ 72 HBW. For the PA-treated alloys, the hardness shows substantial increase at both 100 °C and 180 °C, though hardening of alloy 6014 is more pronounced than that of alloy 6014-70Sn, see the insets in Fig. 2. Such PA treatment can greatly retard the following hardening during NSA of both alloys. When the time of PA treatment is ≥ 10 min at 100 °C and ≥ 1 min at 180 °C, respectively, a stage of initially constant hardness appears in alloy 6014.
Figure 3 shows the change of electrical resistivity of 6014(Sn) alloys during NA and NSA. During NA, the resistivity increase of alloy 6014 exhibits distinct stages on the logarithmic time scale, similar to the observations in our previous study [25]. Sn addition markedly slows down the resistivity change and only after ~ 1 week of NA the resistivity increases of these two alloys reach a comparable value. For both alloys, PA not only slows down the resistivity increase but also reduces the value achieved within 1 week of NSA. The initiation of resistivity increase in alloy 6014-70Sn occurs later than the alloy 6014 after the same PA treatment at 100 °C, but eventually reaches higher values than the Sn-free alloy.
State after 1 week of natural (secondary) (NA/NSA) and subsequent artificial ageing (AA)
DSC analysis of 6014(Sn) alloys after various heat treatments is shown in Fig. 4. Right after quenching (“AQ”, grey lines), alloy 6014 exhibits three exothermic peaks caused by the formation of clusters (around 75 °C), β’’ precipitates (around 247 °C) and β’ (around 298 °C). The corresponding DSC curve of the as-quenched alloy 6014-70Sn shows a comparable shape but with evident discrepancy: the cluster peak is much smaller and the β’’ and β’ peaks appear at higher temperatures. The cluster peak of alloy 6014 is reduced strongly by 1 week of NA but besides this NA shows a similar influence on the DSC trace of both alloys: An endothermic cluster dissolution trough [19] appears right before the β’’ peak and both β’’ and β’ peaks are delayed to higher temperatures. When PA is applied to the two alloys, the dissolution trough is gradually diminished and the β’’ and β’ peaks are shifted to lower temperatures as PA times increase.
Figure 5 compares the hardness before and after 1 week of NA/NSA in these two alloys as well as its evolution during subsequent AA. The hardness right after quenching with and without ensuing PA is taken from Fig. 2 and marked with green boxes. After quenching and 1 week of NA, a hardness value ~ 69 HBW is reached for both alloys. When PA is carried out, the hardness after 1 week of NSA is smaller and the reduction is much more pronounced in alloy 6014-70Sn than in alloy 6014 (orange boxes). During subsequent AA, hardnesses of as-quenched 6014(Sn) alloys increase continuously (grey curves), from the initial ~ 40 HBW to a saturation value of ~ 109 HBW for both alloys. After 1 week of prior NA, a hardening stagnation or even a slight hardness drop is observed in the early stage of AA in both alloys (black curves). NA also delays the AA kinetics and reduces the AA hardening response. Compared to the alloys only naturally aged for 1 week, alloys after PA and NSA do not show any initial decrease during AA except for alloy 6014 after 1 min PA at 180 °C. The prior PA also accelerates the hardness increase and improves the achievable hardness.
To unveil the structural origin of hardness evolution, microstructures of 6014(Sn) alloys after different heat treatments were further investigated by bright-field TEM. After 4 h of direct AA, densely distributed precipitates are found in both alloys (Fig. 6a, b), while only few precipitates are observed in the alloys with 1 week of prior NA included (Fig. 6c, d). Additional 30 min PA at 100 °C before NA is found to increase the number density of precipitates, and this behaviour is more pronounced for alloy 6014 (Fig. 6e, f). For both alloys, 10 min PA at 180 °C also promotes the formation of precipitates with even higher number density than for 30 min PA at 100 °C, as illustrated in Fig. 6g, h. The average precipitate cross-section is estimated by measuring at least 200 precipitates and the results are listed in Table 2. It can be found that precipitates in the two alloys after 4 h AA have similar cross-sections, while 1 week of NA notably decreases their size. PA at both 100 °C and 180 °C shows potential in promoting the growth of precipitates, especially for alloy 6014-70Sn pre-aged at 180 °C.
To determine the type of precipitates observed in bright-field TEM, they were characterized by atomic-resolution HAADF-STEM as presented in Fig. 7. “Eye-like” structures (marked by dashed orange circles) are frequently observed for precipitates formed in both alloys after all the treatments. It is also noticed that bright dots can be clearly identified inside the precipitates formed in alloy 6014-70Sn (labelled by red arrows). For the HAADF-STEM technique, the image intensity is proportional to Z1.7–1.9 [27,28,29] with Z as the atomic number, and the bright dots observed will be further discussed in detail and attributed to Sn substitution in “Precipitation during artificial ageing (AA) in the presence of Sn” section. Another interesting finding for the Sn-added alloy is that the precipitate areas surrounding the bright dots show unclear lattice structure and appear to be disordered. Moreover, some PA clusters possess the similar FCC structure as Al matrix (spots in fast Fourier transform patterns are only from Al) can also be found in the alloys after 4 h direct AA (Supplementary Fig. S1). The bright dots indicate the existence of Sn in the PA clusters formed in alloy 6014-70Sn (Supplementary Fig. S1c).
Effects of natural ageing on pre-ageing (PA) of alloy 6014-70Sn
The effect of an additional initial NA step on the various ageing behaviours of alloy 6014-70Sn is shown in Fig. 8. Compared to the as-quenched alloy, the DSC trace obtained for a sample after 8 h NA exhibits a larger peak “1” with a lower peak temperature (Fig. 8a). NA up to 8 h hardly changes hardness (black curve in Fig. 8b), but promotes the hardening response during the subsequent 10 min PA at 100 °C, which becomes more pronounced with an increase of NA time (see dotted arrows in Fig. 8b). Moreover, the delaying effect of PA on the following NSA is further enhanced by NA and the hardness value reached after 1 week of NSA is also notably reduced. Electrical resistivity measurements were also carried out to evaluate the effect of NA (Fig. 8c): The resistivity increase during 1 week of NA (1st bar) is strongly reduced by 10 min PA at 100 °C (2nd bar) and can be further suppressed by NA prior to PA (last 2 bars). Even when we consider the total resistivity increase at RT including NA (green) and NSA (orange), much lower values are still found when NA is performed. In addition, during final AA at 180 °C after 1 week of NSA, NA before PA also gives rise to faster ageing kinetics and superior hardening response (Fig. 8d).
Discussion
Effect of Sn on clustering during natural (secondary) (NA/NSA) and pre-ageing (PA)
During NA of solutionised and quenched alloys, the diffusion of solute atoms leads to the formation of NA clusters with the assistance of quenched-in vacancies. These NA clusters can act as obstacles for moving dislocations and contribute to the hardening of alloys, see Fig. 2. On the other hand, NA clusters also give rise to additional electron scattering [30], which results in an increase in electrical resistivity (Fig. 3). For alloy 6014-70Sn, the found retarded hardness and resistivity increase during NA can be explained by the strong interaction between Sn atoms and vacancies with an energy around 0.25 to 0.28 eV [31, 32]. Our previous work has also revealed that even at a temperature as high as 250 °C vacancies can be bound by Sn for a notable period [26]. As a result, vacancy-assisted solute diffusion is retarded and NA kinetics is slowed down.
PA has been proposed to reduce and even suppress subsequent clustering at RT [11, 33], in agreement with the observed slower kinetics of hardness and resistivity evolution during NSA. Two mechanisms should account for this: first, the decreased solute supersaturation after formation of PA clusters; second, the lowered vacancy concentration after PA (vacancies either go to sinks or are trapped by pre-formed clusters) [26]. For the effect of Sn addition, much slower NSA kinetics is still found in alloy 6014-70Sn than in alloy 6014 after the same PA treatments (Fig. 2 and Fig. 3). Therefore, it appears that although the Sn-vacancy binding might weaken at PA temperatures, Sn atoms interact with vacancies strongly again after quenching and slow down the kinetics of NSA. Despite the slower ageing kinetics during NSA in alloy 6014-70Sn than in alloy 6014, the total increment of resistivity (Fig. 3) after the same PA treatment at 100 °C is eventually larger in alloy 6014-70Sn, i.e. the curves cross. As the formation of PA clusters at 100 °C is still retarded by Sn addition (inset in Fig. 2a), a lower consumption of solutes during PA in alloy 6014-70Sn can be deduced. Moreover, because Sn alters the ageing course only through controlling vacancy migration [34], the larger NSA potential in alloy 6014-70Sn can be attributed to more available residual solutes.
We now analyse the alloy after 1 week of NA/NSA. The reduction of the cluster peak in the DSC traces (Fig. 4a, b) is associated with the reduction of solute atoms and vacancies, which are consumed during formation of NA clusters. Such NA clusters are not stable, as confirmed by the observed dissolution trough. In addition, it can be seen that although Sn addition slows down the formation of NA clusters, both 6014 and 6014-70Sn alloys show a similar hardness increment, resistivity change and area of dissolution trough during 1 week of NA (Fig. 9a), revealing the formation of a comparable amount of NA clusters in the presence of Sn. For PA samples, NA clustering (Fig. 9a) is reduced, in line with the discussion in last paragraph. In addition, both PA temperature and Sn addition are found to have an influence on the effect of PA. Specifically, PA at 100 °C is more effective in alloy 6014 than in alloy 6014-70Sn, while alloy 6014-70Sn is more significantly influenced by PA at 180 °C (as indicated by the orange dashed arrows Fig. 9a). The different vacancy behaviours depending on the PA temperatures in the presence of Sn should be the reason for this. Because a short exposure to 180 °C can release vacancies from Sn, one can expect a faster formation of PA clusters and a faster vacancy loss compared to exposure to 100 °C. At the same time, the difference between the PA clustering rate of alloys with and without Sn is also reduced at 180 °C. During ensuing NSA, Sn atoms become effective again in trapping vacancies. All these factors result in the superior capability of the combination of Sn addition and PA at 180 °C to inhibit NSA for 1 week.
Precipitation during artificial ageing (AA) in the presence of Sn
In the condition “AA right after quenching”, the generally accepted assumption is that high solute supersaturation and, for a very short period, possibly also the high vacancy concentration can promote the formation of precipitates [8, 35]. This is in good agreement with the observed finely dispersed precipitates after 4 h AA (Fig. 6a, b). Atomic-resolution HAADF images (Fig. 7a, b) reveal that precipitates formed in both alloys contain “eye-like” structures, which have been claimed to be the sub-units of the main hardening phase—β’’ [36]. Thus, the fastest hardness increases can be explained (Fig. 5a, b). In addition, different from the pure β’’ found in alloy 6014, bright dots and a surrounding disordered structure are found after adding Sn (Fig. 7b). As heavier atoms can give rise to brighter contrast in the HAADF-STEM mode [27,28,29] the observed brighter dots inside precipitates can be attributed to the incorporation of Sn, Fe and/or Mn atoms. However, if Fe or Mn were included in precipitates, they should also be observable in alloy 6014. Since bright dots are found only in the Sn-added alloy, they must be Sn atoms. The existence of Sn atoms in precipitates formed by artificially ageing Al–Mg–Si–Sn alloys has also been evidenced in previous studies, not only experimentally by atom probe tomography [9, 37] and EDS measurements at near-atomic resolution [38] but also by density functional theory calculations [38]. This finding provides evidence that Sn atoms can capture vacancies, diffuse and participate in AA precipitation. Regarding the disordered structure inside precipitates, Liu et al. [38], who studied the precipitation behaviours of an Al–Mg–Si–Sn alloy aged at 250 °C, attributed it to the formation of β’/β’’ composites. In our study, however, the ageing temperature (180 °C) and time (4 h) applied are apparently not enough to trigger the formation of β’. Moreover, Mørtsell et al. [39] reported that Ge can induce a disordered structure in Al–Mg–Si alloy aged at 180 °C by replacing Si in precipitates. Therefore, considering the chemical similarity between Sn, Ge and Si, the disorder found is assumed to be caused by the replacement of Si with Sn atoms in β’’. This assumption also applies to the precipitate structure formed in artificially aged alloys with prior NA and PA (Fig. 7d, f, h). Due to the attractive interaction between Mg and Sn [40], one may also expect the formation of Mg2Sn. However, no such phase has been identified in the current work, in agreement with a series of previous reports [9, 38, 41]. According to Weng et al. [42], who studied Al–Mg-Si alloys containing Sn ranging from 0 to 0.2 wt. %, the failure to observe Mg2Sn phase might be a result of the extremely low concentration of Sn.
After 1 week of NA, the number density (Fig. 6e–h) and average cross-section (Table 2) of β’’ formed during AA are all reduced, resulting in the reduced hardening response and postponed β’’ DSC peak. Such negative effect is associated with the imprisoned vacancies and reduced solute supersaturation during NA. The potential of Sn in promoting AA of naturally aged Al–Mg–Si alloys is not observed (Fig. 5b and Fig. 6d). This means that although NA clustering is slowed down by Sn generally, its negative effect on the following AA can still set in if sufficient clusters have formed given that the NA time has been long enough. It has also been found that PA in both alloys can significantly increase the precipitate number density (Fig. 6e–h) and average cross-section (Table 2), contributing to the improvement of hardness (Fig. 5a, b) and thus, mitigating the negative effect of NA on AA. One possible reason is the suppression of NSA clustering caused by the reduced solute and vacancy concentrations after PA. This is supported by the correlation between the PB response and the extent of NSA suppression (see thick green arrows in Fig. 9a, b). Another possible reason for the enhanced AA behaviour could be that PA clusters are transformable precursors for β’’. For PA clusters, the average Mg/Si ratio (~ 1.0 [15, 43]) is higher than for NA clusters (~ 0.66 [15]) and closer to that of β’’ (0.9–1.1 [15, 20]). Moreover, their size is larger than the critical size for nucleation at AA temperature [20, 44]. Both factors enable PA clusters to act as nuclei for β’’ during ensuing AA. The broader DSC peak for β’’, the much higher number density and larger average cross-section of β’’ observed after PA are thought to be the result of the existence of nuclei for β’’.
In engineering practice, formability before panel stamping must be considered, which requires a low alloy strength after PA and NSA. It has been shown that alloy 6014 possesses relatively higher hardness after 1 week of NSA than the Sn-added one (orange boxes in Fig. 5a, b), either resulting from the higher PA hardness or from the NSA response. Evidently, in alloy 6014-70Sn the strongly delayed PA and NSA processes help to meet the formability requirement, while the good AA response can be ensured by a higher PA temperature.
A schematic showing the influence of Sn on the ageing behaviour of Al–Mg-Si alloys is given in Fig. 10. In the as-quenched Sn-free alloy, vacancies are free or attached to solutes weakly and transport of solutes during the subsequent PA and the associated formation of PA clusters is facilitated. NA clustering happens during the following NSA with the residual vacancies and solutes. In the final AA step, some NA clusters dissolve and some remain stable, while PA clusters further grow into β’’. In comparison, vacancies are likely to be trapped strongly by added Sn atoms after quenching. When PA treatment is applied, Sn-vacancy binding is weakened but still exists, and the amount of PA clusters formed is reduced. In the following NSA, the diffusion of vacancies is again strongly slowed down in the presence of Sn and therefore NA clustering is suppressed. In the final AA treatment, Sn atoms can participate in the formation of β’’-type precipitates and cause disordered phase by occupying the original Si position.
Sn-induced positive effect of natural ageing (NA)
Surprisingly, the application of NA before PA can improve the performance of PA at 100 °C in alloy 6014-70Sn (Fig. 8). This is contrary to the findings in Sn-free Al–Mg–Si alloy reported by Torsæter et al. [43], where the formation of PA clusters is adversely influenced by 1 week of NA, due to the depletion of solute in the vicinity of the NA clusters formed. However, it has also been speculated that Si-vacancy complexes or small Si clusters formed during quenching are able to promote the formation of PA clusters [11]. Therefore, we suspect that the discrepancy between the different roles of NA clusters during PA might be associated to their size, pointing at the NA clustering process being modified by Sn addition. Compared to the Sn-free alloy, the distance that solutes in the presence of Sn can diffuse in unit time during NA is largely reduced owing to the decreased number of available vacancies (as described in “Effect of Sn on clustering during natural (secondary) (NA/NSA) and pre-ageing (PA)” section). Consequently, smaller but more densely distributed clusters are formed in alloy 6014-70Sn than in alloy 6014. This is supported by our previous resistivity measurements [34], as well as by a comparable phenomenon observed in Al–Mg–Si alloys containing Cu atoms, which also have stronger binding with vacancies than Mg/Si solutes [45]. After 8 h of NA, clusters are formed. Although they are not large enough to induce hardening more than marginally (black curve in Fig. 8b), they can result in an increased electrical resistivity (Fig. 8c). On the one hand, these small clusters will further grow into larger NA clusters at RT, as revealed by the appearance of hardening after an incubation period of 8 h in Fig. 8b. On the other hand, the elevated PA hardness after NA (Fig. 8b) might indicate that these clusters can transform into PA clusters at 100 °C. Moreover, the broadened DSC clustering peak (Fig. 8a), which is related to the formation of PA clusters considering a peak temperature much higher than RT, also points at promoted PA kinetics. As a result, the accelerated formation of PA clusters suppresses NSA (Fig. 8b, c) and promotes AA kinetics and response (Fig. 8d).
Conclusions
We investigated the combined effects of Sn addition and pre-ageing (PA) on the ageing behaviour of Al–Mg–Si alloys, aiming to find a favourable combination that suppresses natural secondary ageing (NSA) and enhances subsequent artificial ageing (AA).
-
1.
PA can suppress the formation of natural ageing (NA) clusters and improve the AA kinetics and response after 1 week of NSA in alloys with and without Sn.
-
2.
The strong interaction between Sn and vacancies notably delays PA kinetics at 100 °C. Therefore, a higher PA temperature (e.g. 180 °C) is required for a more effectively suppressed NSA and a larger AA response in Sn-added alloy by weakening the Sn-vacancy binding.
-
3.
An undesired high hardness for Sn-free alloy after PA and subsequent NSA can be lowered by the addition of Sn while maintaining the AA potential.
-
4.
The effect of PA at 100 °C in 6014-70Sn can be promoted by prior NA, which can be ascribed to the transformation of Sn-induced small clusters formed at RT to PA clusters when aged at 100 °C.
References
Zandbergen HW, Andersen SJ, Jansen J (1997) Structure determination of Mg5Si6: particles in Al by dynamic electron diffraction studies. Science 277:1221–1225. https://doi.org/10.1126/science.277.5330.1221
Miao WF, Laughlin DE (1999) Precipitation hardening in aluminum alloy 6022. Scr Mater 40:873–878. https://doi.org/10.1016/S1359-6462(99)00046-9
Pashley DW, Rhodes JW, Sendorek A (1966) Delayed ageing in aluminium-magnesium-silicon alloys: effect on structure and mechnical properties. J Inst Met London 94:41–49
Brenner P, Kostron H (1939) Über die Vergütung der Aluminium-Magnesium-Silizium- Legierungen (Pantal). Zeitsschrift für Met 31(4):89–97
Martinsen FA, Ehlers FJH, Torsæter M, Holmestad R (2012) Reversal of the negative natural aging effect in Al–Mg–Si alloys. Acta Mater 60:6091–6101. https://doi.org/10.1016/j.actamat.2012.07.047
Aruga Y, Kozuka M, Takaki Y, Sato T (2015) Formation and reversion of clusters during natural aging and subsequent artificial aging in an Al–Mg–Si alloy. Mater Sci Eng A 631:86–96. https://doi.org/10.1016/j.msea.2015.02.035
Falahati A, Lang P, Kozeschnik E (2012) Precipitation in Al-alloy 6016—the role of excess vacancies. Mater Sci Forum 706–709:317–322
Pogatscher S, Antrekowitsch H, Leitner H et al (2011) Mechanisms controlling the artificial aging of Al–Mg–Si alloys. Acta Mater 59:3352–3363. https://doi.org/10.1016/j.actamat.2011.02.010
Pogatscher S, Antrekowitsch H, Werinos M et al (2014) Diffusion on demand to control precipitation aging: application to Al–Mg–Si alloys. Phys Rev Lett 112:225701. https://doi.org/10.1103/PhysRevLett.112.225701
Werinos M, Antrekowitsch H, Ebner T et al (2016) Design strategy for controlled natural aging in Al–Mg–Si alloys. Acta Mater 118:296–305. https://doi.org/10.1016/j.actamat.2016.07.048
Yamada K, Sato T, Kamio A (2000) Effects of quenching conditions on two-step aging behavior of Al–Mg–Si alloys. Mater Sci Forum 331–337:669–674
Ding L, Weng Y, Wu S et al (2016) Influence of interrupted quenching and pre-aging on the bake hardening of Al–Mg–Si Alloy. Mater Sci Eng A 651:991–998. https://doi.org/10.1016/j.msea.2015.11.050
Cao L, Rometsch PA, Couper MJ (2013) Effect of pre-ageing and natural ageing on the paint bake response of alloy AA6181A. Mater Sci Eng A 571:77–82. https://doi.org/10.1016/j.msea.2013.01.065
Yang Z, Liang Z, Leyvraz D, Banhart J (2019) Effect of pre-ageing on natural secondary ageing and paint bake hardening in Al–Mg–Si alloys. Materialia 7:100413. https://doi.org/10.1016/J.MTLA.2019.100413
Zandbergen MW, Xu Q, Cerezo A, Smith GDW (2015) Study of precipitation in Al–Mg–Si alloys by atom probe tomography I. Microstructural changes as a function of ageing temperature. Acta Mater 101:136–148. https://doi.org/10.1016/j.actamat.2015.08.017
Engler O, Marioara CD, Aruga Y et al (2019) Effect of natural ageing or pre-ageing on the evolution of precipitate structure and strength during age hardening of Al–Mg–Si alloy AA 6016. Mater Sci Eng A 759:520–529. https://doi.org/10.1016/j.msea.2019.05.073
Saga M, Sasaki Y, Kikuchi M et al (1996) Effect of pre-aging temperature on the behavior in the early stage of aging at high temperature for Al–Mg–Si alloy. Mater Sci Forum 217–222:821–826
Serizawa A, Hirosawa S, Sato T (2008) Three-dimensional atom probe characterization of nanoclusters responsible for multistep aging behavior of an Al–Mg–Si alloy. Metall Mater Trans A 39:243–251. https://doi.org/10.1007/s11661-007-9438-5
Edwards GA, Stiller K, Dunlop GL, Couper MJ (1998) The precipitation sequence in Al–Mg–Si alloys. Acta Mater 46:3893–3904. https://doi.org/10.1016/S1359-6454(98)00059-7
Murayama M, Hono K (1999) Pre-precipitate clusters and precipitation processes in Al–Mg–Si alloys. Acta Mater 47:1537–1548. https://doi.org/10.1016/S1359-6454(99)00033-6
Marioara CD, Andersen SJ, Jansen J, Zandbergen HW (2003) The influence of temperature and storage time at RT on nucleation of the beta’’ phase in a 6082 Al–Mg–Si alloy. Acta Mater 51:789–796. https://doi.org/10.1016/S1359-6454(02)00470-6
Birol Y (2005) Pre-aging to improve bake hardening in a twin-roll cast Al–Mg–Si alloy. Mater Sci Eng A 391:175–180. https://doi.org/10.1016/j.msea.2004.08.069
Zandbergen MW, Cerezo A, Smith GDW (2015) Study of precipitation in Al–Mg–Si alloys by atom probe tomography II. Influence of Cu additions Acta Mater 101:149–158. https://doi.org/10.1016/j.actamat.2015.08.018
Weng Y, Jia Z, Ding L et al (2018) Combined effect of pre-aging and Ag/Cu addition on the natural aging and bake hardening in Al–Mg–Si alloys. Prog Nat Sci Mater Int 28:363–370. https://doi.org/10.1016/j.pnsc.2018.04.007
Banhart J, Chang CST, Liang ZQ et al (2010) Natural aging in Al–Mg–Si alloys—a process of unexpected complexity. Adv Eng Mater 12:559–571. https://doi.org/10.1002/adem.201000041
Zhang X, Liu M, Sun H, Banhart J (2019) Influence of Sn on the age hardening behavior of Al–Mg–Si alloys at different temperatures. Materialia 8:100441. https://doi.org/10.1016/j.mtla.2019.100441
Pennycook SJ, Jesson DE (1991) High-resolution Z-contrast imaging of crystals. Ultramicroscopy 37:14–38. https://doi.org/10.1016/0304-3991(91)90004-P
Nellist PD, Pennycook SJ (1999) Incoherent imaging using dynamically scattered coherent electrons. Ultramicroscopy 78:111–124. https://doi.org/10.1016/S0304-3991(99)00017-0
Yamazaki T, Kawasaki M, Watanabe K et al (2002) Effect of small crystal tilt on atomic-resolution high-angle annular dark field STEM imaging. Ultramicroscopy 92:181–189. https://doi.org/10.1016/S0304-3991(02)00131-6
Panseri C, Federighi T (1966) A resistometric study of preprecipitation in an aluminium-1.4 percent Mg2Si alloy. J Inst Met London 94:99–197
Wolverton C (2007) Solute-vacancy binding in aluminum. Acta Mater 55:5867–5872. https://doi.org/10.1016/j.actamat.2007.06.039
Lang P, Shan YV, Kozeschnik E (2014) The life-time of structural vacancies in the presence of solute trapping. Mater Sci Forum 794–796:963–970
Yan Y (2014) Investigation of the negative and positive effects of natural aging on artificial aging response in Al–Mg–Si alloys. Technische Universität Berlin
Liu M, Zhang X, Körner B et al (2019) Effect of Sn and In on the natural ageing kinetics of Al–Mg–Si alloys. Materialia 6:100261. https://doi.org/10.1016/j.mtla.2019.100261
Madanat M, Liu M, Zhang X et al (2020) Co-evolution of vacancies and solute clusters during artificial ageing of Al–Mg–Si alloys. Phys Rev Mater 4:063608. https://doi.org/10.1103/PhysRevMaterials.4.063608
van Huis MA, Chen JH, Zandbergen HW, Sluiter MHF (2006) Phase stability and structural relations of nanometer-sized, matrix-embedded precipitate phases in Al–Mg–Si alloys in the late stages of evolution. Acta Mater 54:2945–2955. https://doi.org/10.1016/j.actamat.2006.02.034
Werinos M, Antrekowitsch H, Kozeschnik E et al (2016) Ultrafast artificial aging of Al–Mg–Si alloys. Scr Mater 112:148–151. https://doi.org/10.1016/j.scriptamat.2015.09.037
Liu C, Ma P, Zhan L et al (2018) Solute Sn-induced formation of composite β′/β″ precipitates in Al–Mg–Si alloy. Scr Mater 155:68–72. https://doi.org/10.1016/j.scriptamat.2018.06.028
Mørtsell EA, Marioara CD, Andersen SJ et al (2015) Effects of germanium, copper, and silver substitutions on hardness and microstructure in lean Al–Mg–Si alloys. Metall Mater Trans A Phys Metall Mater Sci 46:4369–4379. https://doi.org/10.1007/s11661-015-3039-5
Hirosawa S, Nakamura F, Sato T (2007) First-principles calculation of interaction energies between solutes and/or vacancies for predicting atomistic behaviors of microalloying elements in aluminum alloys. Mater Sci Forum 561–565:283–286
Tu W, Tang J, Zhang Y et al (2019) Influence of Sn on the precipitation and hardening response of natural aged Al–0.4Mg–1.0Si alloy artificial aged at different temperatures. Mater Sci Eng A 765:138250. https://doi.org/10.1016/j.msea.2019.138250
Weng Y, Xu Y, Ding L et al (2021) Effect of Sn contents on natural aging and precipitation hardening in Al–Mg–Si alloys. Mater Charact 179:111383. https://doi.org/10.1016/j.matchar.2021.111383
Torsæter M, Hasting HS, Lefebvre W et al (2010) The influence of composition and natural aging on clustering during preaging in Al–Mg–Si alloys. J Appl Phys. https://doi.org/10.1063/1.3481090
Aruga Y, Kozuka M, Takaki Y, Sato T (2014) Evaluation of solute clusters associated with bake-hardening response in isothermal aged Al–Mg–Si alloys using a three-dimensional atom probe. Metall Mater Trans A Phys Metall Mater Sci 45:5906–5913. https://doi.org/10.1007/s11661-014-2548-y
Liu M, Banhart J (2016) Effect of Cu and Ge on solute clustering in Al–Mg–Si alloys. Mater Sci Eng A 658:238–245. https://doi.org/10.1016/j.msea.2016.01.095
Acknowledgements
The Deutsche Forschungsgemeinschaft (DFG) partially funded this project (Ba1170/22). Xingpu Zhang thanks the China Scholarship Council (CSC) for a research fellowship (No. 201506170013). We thank Dr. Zeqin Liang and David Leyvraz of Novelis Research and Technology Center Sierre for providing the alloys.
Funding
Open Access funding enabled and organized by Projekt DEAL.
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Conflict of interest
The authors declare no conflict of interest.
Additional information
Handling Editor: Catalin Croitoru.
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhang, X., Liu, M., Wang, J. et al. Combined effect of Sn addition and pre-ageing on natural secondary and artificial ageing of Al–Mg–Si alloys. J Mater Sci 57, 2149–2162 (2022). https://doi.org/10.1007/s10853-021-06654-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-021-06654-y