A thermal imaging technique for studying crack development in wood under torsional loading

  • Published:
Journal of Materials Science Aims and scope Submit manuscript

Abstract

A thermal imaging system has been used for monitoring fracture in wood under both static and fatigue torsional loading. The thermal images of softwood test-pieces containing a knot under torsional loading predicted the cracking time and crack position that agreed well with visual observation. The thermal images obtained under torsional fatigue loading indicated a temperature increase during the unloading part of a loading cycle, which meant that thermal energy was dissipated during the relaxation stage of the loading cycle. The maximum temperature reached also increased as the loading cycles increased. Results from thermal images of a softwood indicated that the earlywood exchanged more thermal energy than latewood. Optical microscopy and SEM confirmed that in earlywood the region near a growth ring is the weaker area. For all the test pieces, whether softwood or hardwood, with or without a knot, the hotspots revealed during thermal imaging appeared before the load dropped sharply and these were confirmed to be the positions for crack initiation. This shows that it is possible to predict and depict failure and its progress using thermal imaging techniques.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. V. BUCUR, in “Acoustics of Wood” (CRC Press, Boca Raton, New York, USA, 1995) p. 221.

    Google Scholar 

  2. Z. CHEN and B. GABBITAS, in First international conference of the Europe Society of Wood Mechanics, Lausanne, Switzerland, 19–21 April, 2001, p. 393.

  3. R. W. RICE and C. SKAAR, Wood Sci. Techn. 24 (1990) 123.

    Google Scholar 

  4. D. WU and G. BUSSE, TAPPI 1995 Europ. Plast. Lamin. Symp. 79(8) (1995) 119.

    Google Scholar 

  5. G. DILL-LANGER and S. AICHER, in Proceedings of COST Action E8 on Wood and Wood Fiber Composites, Stuttgart, Germany, 13–15 April, 2000, p. 93.

  6. S. G. BURNAY, T. L. WILLIAMS and C. H. JONES, in “Applications of Thermal Imaging” (Hilger Ltd., Bristol, UK, 1988) p. 1.

    Google Scholar 

  7. A. CHRYSOCHOOS, O. MAISONNEUVE, G. MARTIN, H. CAUMON and J. C. CHEZEAUX, Nucl. Engns. Design 114 (1989) 323.

    Google Scholar 

  8. G. GAUSSORGUES, in “Infrared Thermography” (Chapman & Hall, University Press, Cambridge, UK, 1994) p. xv.

    Google Scholar 

  9. V. P. VAVILOV, in “Subjective Remarks on the Terminology used in Thermal/Infrared Nondestructive Testing” in Thermosense XVIII, edited by D. D. Burleigh and J. W. M. Spicer, SPIE Proc., 2766 (1996) 276.

  10. W. N. REYNOLDS and G. M. WELLS, Brit. J. NDT 26(1) (1984) 40.

    Google Scholar 

  11. S. K. LAU, D. P. ALMOND and J. M. MILNE, NDT Eval. Intern. 24(4) (1991) 195.

    Google Scholar 

  12. R. L. THOMAS, L. D. FAVRO, P. K. KUO, T. AHMED, X. HAN, L. WANG, X. WANG and S. M. SHEPARD, in Proceedings of 15th International Congress on Acoustics, Trondheim, Norway, June 26–30, 1995 p. 433.

  13. G. BUSSE, D. WU and W. KARPEN, J. Appl. Phys. 71(8) (1992) 3962.

    Article  Google Scholar 

  14. J. SEMBACH, D. WU, A. SALERNO, G. HORA and G. BUSSE, in Proceedings of Workshop on Nondestructive Testing of Panel Products, Llandudno, UK, 11 October, 1997 (J. Hague 1997) p. 41.

  15. D. WU and G. BUSSE, in TAPPI 1995 Europ. Plast. Lamin. Symp. 79(8) (1995) 119.

    Google Scholar 

  16. Y. XU, S. OKUMURA and M. NOGUCHI, Mukuzai gakkaishi-J. 39(5) (1993) 544.

    Google Scholar 

  17. H. BERGLIND and A. DILLENZ, in 12th International Symposium on Nondestructive Testing of Wood, Sopron, Hungary, 2000 p. 413.

  18. A. CHRYSOCHOOS and F. BELMAHJOUB, Arch. Mech. 44 (1992) 55.

    Google Scholar 

  19. A. CHRYSOCHOOS, H. LOUCHE, J. M. MURACCIOLE, M. NÉMOZ-GAILLARD, J. L. SAUREL and B. WATTRISSE, in IUTAM Symposium on Advanced Optical Methods and Applications in Solid Mechanics, Netherland, 2000, p. 313.

  20. S. BARDET, in “Comportment thermoviscoelastique transverse du bois humide,” Ph.D Thesis (Montpellier University, France, 2001) p. 49.

    Google Scholar 

  21. K. PERSSON, Swedish Lund University/Lund Institute of Technology Report TVSM-3020 (1997)

Download references

Author information

Authors and Affiliations

  1. University of New Brunswick, Fredericton, NB, Canada

    Zheng Chen

  2. University of Waikato, Hamilton, New Zealand

    B. Gabbitas

  3. London South Bank University, London, UK

    D. Hunt

Authors
  1. Zheng Chen
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. B. Gabbitas
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. D. Hunt
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Zheng Chen.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Chen, Z., Gabbitas, B. & Hunt, D. A thermal imaging technique for studying crack development in wood under torsional loading. J Mater Sci 40, 1929–1935 (2005). https://doi.org/10.1007/s10853-005-1213-7

Download citation

  • Received:

  • Accepted:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10853-005-1213-7

Keywords

Search

Navigation