Abstract
Deterioration of buried metal pipes due to corrosive soil environment is a major issue worlwide. Although failures of buried pipe due to corrosive soil is an old problem, yet such failures are still uncontrollable even with the application of advanced corrosion protection technologies. Therefore, understanding factors causing corrosion of buried pipes is necessary. This article reviews factors causing corrosion of buried pipes in soils. Factors include moisture content, soil resistivity, pH, dissolved oxygen, temperature and microbial activity. Moreover, we discuss the influence of manufacturing method and the comparison of corrosion behaviour of cast iron, ductile and mild steel pipes. We found that corrosion rate of pipes increases with moisture contents up to the critical moisture value. Although pH affects corrosion, there is no relationship between corrosion and pH and the corrosion rates of buried pipes are inversely proportional to soil resistivity. Soils containing more organic matter show high resistivity. Dissolved oxygen in soil develops differential cell which accelerates corrosion of metallic pipe. Different types of bacteria present in soil develop biofilms on metallic pipes, which deteriorates pipes with time.
Similar content being viewed by others
References
Abedi S, Abdolmaleki A, Adibi N (2007) Failure analysis of SCC and SRB induced cracking of a transmission oil products pipeline. Eng Fail Anal 14:250–261. https://doi.org/10.1016/j.engfailanal.2005.07.024
Adeosun SO, Sanni OS (2013) Degradation propensity of welded mild steel in coastal soil of University of Lagos. World Acad Sci Eng Technol Int J Chem Mol Nucl Mater Metall Eng 7(1):92–96. https://doi.org/10.5281/zenodo.1088888
Alamilla JL, Espinosa-Medina MA, Sosa E (2009) Modelling steel corrosion damage in soil environment. Corros Sci 51:2628–2638. https://doi.org/10.1016/j.corsci.2009.06.052
Asadi ZS, Melchers RE (2017) Long-term external pitting and corrosion of buried cast iron water pipes. Corros Eng Sci Technol. https://doi.org/10.1080/1478422x.2017.1400291
Atkinson K, Whiter J, Smith P, Mulheron M (2002) Failure of small diameter cast iron pipes. Urban Water 4:263–271. https://doi.org/10.1016/S1462-0758(02)00004-3
Barbalat M, Lanarde L, Caron D, Meyer M, Vittonato J, Castillon F, Fontaine S, Refait P (2012) Electrochemical study of the corrosion rate of carbon steel in soil: evolution with time and determination of residual corrosion rates under cathodic protection. Corros Sci 55:246–253. https://doi.org/10.1016/j.corsci.2011.10.031
Beech IB, Cheung CS, Chan CP, Hill MA, Franco R, Lino AR (1994) Study of parameters implicated in the biodeterioration of mild steel in the presence of different species of sulphate-reducing bacteria. Inter Biodeterior Biodegrad 34:289–303. https://doi.org/10.1016/0964-8305(94)90089-2
Beese P, Venzlaff H, Srinivasan J, Garrelfs J, Stratmann M, Mayrhofer KJ (2013) Monitoring of anaerobic microbially influenced corrosion via electrochemical frequency modulation. Electrochim Acta 105:239–247. https://doi.org/10.1016/j.electacta.2013.04.144
Bell RG, Lim CK (1981) Corrosion of mild and stainless steel by four tropical Desulfovibrio desulfuricans strains. Can J Microbiol 27:242–245. https://doi.org/10.1139/m81-036
Belmokre K, Azzouz N, Kermiche F, Wery M, Pagetti J (1998) Corrosion study of carbon steel protected by a primer, by electrochemical impedance spectroscopy (EIS) in 3% NaCl medium and in a soil simulating solution. Mater Corros 49:108–113. https://doi.org/10.1002/(SICI)1521-4176(199802)49:2%3C108::AID-MACO108>3.0.CO;2-P
Belmonte H, Mulheron M, Smith P, Ham A, Wescombe K, Whiter J (2008) Weibull-based methodology for condition assessment of cast iron water mains and its application. Fatigue Fract Eng Mater Struct 31:370–385. https://doi.org/10.1111/j.1460-2695.2008.01233.x
Benmoussa A, Hadjel M, Traisnel M (2006) Corrosion behavior of API 5L X-60 pipeline steel exposed to near-neutral pH soil simulating solution. Mater Corros 57:771–777. https://doi.org/10.1002/maco.200503964
Booth GH, Tiller AK (1962) Polarization studies of mild steel in cultures of sulphate-reducing bacteria. Part 3.—Halophilic organisms. Trans Faraday Soc 58: 2510–2516. https://doi.org/10.1039/TF9625802510
Booth G (1964) Sulphur bacteria in relation to corrosion. J Appl Bacteriol 27:174–181. https://doi.org/10.1111/j.1365-2672.1964.tb04825.x
Bradley WL, Srinivasan MN (1990) Fracture and fracture toughness of cast irons. Int Mater Rev 35(1):129–161. https://doi.org/10.1179/095066090790324028
Casanova T, Soto F, Eyraud M, Crousier J (1997) Hydrogen absorption during zinc plating on steel. Corros Sci 39:529–537. https://doi.org/10.1016/S0010-938X(97)86101-X
Cheng Y (2007) Fundamentals of hydrogen evolution reaction and its implications on near-neutral pH stress corrosion cracking of pipelines. Electrochim Acta 52:2661–2667. https://doi.org/10.1016/j.electacta.2006.09.024
Cole I, Marney D (2012) The science of pipe corrosion: a review of the literature on the corrosion of ferrous metals in soils. Corros Sci 56:5–16. https://doi.org/10.1016/j.corsci.2011.12.001
Costerton JW, Cheng K, Geesey GG, Ladd TI, Nickel JC, Dasgupta M, Marrie TJ (1987) Bacterial biofilms in nature and disease. Ann Rev Microbiol 41:435–464. https://doi.org/10.1146/annurev.mi.41.100187.002251
Dafter MR (2014) Electrochemical testing of soils for long-term prediction of corrosion of ferrous pipes. https://doi.org/10.14773/cst.2016
Dasgupta M, Marrie TJ (1987) Bacterial biofilms in nature and disease. Ann Rev Microbiol 41:435–464. https://doi.org/10.1146/annurev.mi.41.100187.002251
Davalos J, Gracia M, Marco JF, Gancedo JR (1992) Corrosion of weathering steel and iron under wet-dry cycling conditions: influence of the rise of temperature during the dry period. Hyperfine Interact 69:871–874. https://doi.org/10.1007/BF02401965
Dehghan A, Mcmanus K, Gad E (2008) Probabilistic failure prediction for deteriorating pipelines: nonparametric approach. J Perform Constr Facil 22:45–53. https://doi.org/10.1061/(ASCE)0887-3828(2008)22:1(45)
Denison IA, Darniellec RB (1939) Observations on the behavior of steel corroding under cathodic control in soils. J Electrochem Soc 76:199–214. https://doi.org/10.1149/1.3500261
Devanathan MAV, Stachurski Z (1962) The adsorption and diffusion of electrolytic hydrogen in palladium. In: Proceedings of the Royal Society of London A: Mathematical, Phys Eng Sci 270: 90–102. https://doi.org/10.1098/rspa.1962.0205
Doyle G, Seica MV, Grabinsky MW (2003) The role of soil in the external corrosion of cast iron water mains in Toronto, Canada. Can Geotech J 40:225–236. https://doi.org/10.1139/t02-106
El Hajj H, Abdelouas A, El Mendili Y, Karakurt G, Grambow B, Martin C (2013) Corrosion of carbon steel under sequential aerobic–anaerobic environmental conditions. Corros Sci 76:432–440. https://doi.org/10.1016/j.corsci.2013.07.017
Eslami A, Fang B, Kania R, Worthingham B, Been J, Eadie R, Chen W (2010) Stress corrosion cracking initiation under the disbonded coating of pipeline steel in near-neutral pH environment. Corros Sci 52:3750–3756. https://doi.org/10.1016/j.corsci.2010.07.025
Eslami A, Kania R, Worthingham B, Boven GV, Eadie R, Chen W (2011) Effect of CO2 and R-ratio on near-neutral pH stress corrosion cracking initiation under a disbonded coating of pipeline steel. Corros Sci 53:2318–2327. https://doi.org/10.1016/j.corsci.2011.03.017
Evans UR, Taylor CAJ (1972) Mechanism of atmospheric rusting. Corros Sci 12:227–246. https://doi.org/10.1016/S0010-938X(72)90671-3
Gaylarde CC (1992) Sulfate-reducing bacteria which do not induce accelerated corrosion. Int Biodeterior Biodegrad 30:331–338. https://doi.org/10.1016/0964-8305(92)90037-O
Gould SJF, Boulaire FA, Burn S, Zhao XL, Kodikara JK (2011) Seasonal factors influencing the failure of buried water reticulation pipes. Water Sci Technol 63:2692–2699. https://doi.org/10.2166/wst.2011.507
Grigg NS (2006) Condition assessment of water distribution pipes. J infrastruct Syst 12:147–153. https://doi.org/10.1061/(ASCE)1076-0342(2006)12:3(147)
Gupta S, Gupta B (1979) The critical soil moisture content in the underground corrosion of mild steel. Corros Sci 19:171–178. https://doi.org/10.1016/0010-938X(79)90015-5
Hamilton HL (1960) Effects of soil corrosion on cast-iron pipe. J Am Water Works Assoc 52(5):638–650. https://doi.org/10.1002/j.1551-8833.1960.tb00515.x
Hamilton WA (1985) Sulphate-reducing bacteria and anaerobic corrosion. Annu Rev Microbiol 39:195–217. https://doi.org/10.1146/annurev.mi.39.100185.001211
Hassel AW, Stratmann M, Widdel F (2012) Marine sulfate-reducing bacteria cause serious corrosion of iron under electroconductive biogenic mineral crust. Environ Microbiol 14:1772–1787. https://doi.org/10.1111/j.1462-2920.2012.02778.x
He B, Han P, Lu C, Bai X (2015) Effect of soil particle size on the corrosion behavior of natural gas pipeline. Eng Fail Anal 58:19–30. https://doi.org/10.1016/j.engfailanal.2015.08.027
Higuchi M, Iida K (1991) Fatigue strength correction factors for carbon and low-alloy steels in oxygen-containing high-temperature water. Nucl Eng Des 129:293–306. https://doi.org/10.1016/0029-5493(91)90138-8
Hino S, Watanabe F, Takahashi N (1997) Isolation and characterization of slime-producing bacteria capable of utilizing petroleum hydrocarbons as a sole carbon source. J Ferment Bioeng 84:528–531. https://doi.org/10.1016/S0922-338X(97)81906-X
Hou Y, Deqing L, Li S, Yang W, Li CQ (2016) Experimental investigation on corrosion effect on mechanical properties of buried metal pipes. Inter J Corros. https://doi.org/10.1155/2016/5808372
Hu J, Shun-An C, Xie J (2013) EIS study on the corrosion behavior of rusted carbon steel in 3% NaCl solution. Anti-Corros Methods Mater 60:100–105. https://doi.org/10.1108/00035591311308074
Hubert C, Nemati M, Jenneman G, Voordouw G (2005) Corrosion risk associated with microbial souring control using nitrate or nitrite. Appl Microbiol Biotechnol 68:272–282. https://doi.org/10.1007/s00253-005-1897-2
Javaherdashti R (1999) A review of some characteristics of MIC caused by sulfate-reducing bacteria: past, present and future. Anti-Corros Methods Mater 46:173–180. https://doi.org/10.1108/00035599910273142
Javaherdashti R, Raman RS, Panter C, Pereloma E (2006) Microbiologically assisted stress corrosion cracking of carbon steel in mixed and pure cultures of sulfate-reducing bacteria. Inter J Biodeterior Biodegrad 58:27–35. https://doi.org/10.1016/j.ibiod.2006.04.004
Javed MA, Stoddar PR, Palombo EA, Mcarthur SL, Wade SA (2014) Inhibition or acceleration: bacterial test media can determine the course of microbiologically influenced corrosion. Corros Sci 86:149–158. https://doi.org/10.1016/j.corsci.2014.05.003
Javed MA, Stoddart PR, Wade SA (2015) Corrosion of carbon steel by sulphate reducing bacteria: initial attachment and the role of ferrous ions. Corros Sci 93:48–57. https://doi.org/10.1016/j.corsci.2015.01.006
Jiang G, Li Y (2011) A model for calculating hydrogen solubility in liquid transition metals. Metall Mater Trans 42A:1038–1043. https://doi.org/10.1007/s11661-010-0513-y
Jin T, Liu Z, Cheng Y (2010) Effect of non-metallic inclusions on hydrogen-induced cracking of API5L ×100 steel. Inter J Hydrog Energy 35:8014–8021. https://doi.org/10.1016/j.ijhydene.2010.05
Kelly DJ, Robinson MJ (1993) Influence of heat treatment and grain shape on exfoliation corrosion of Al-Li Alloy 8090. Corrosion 49:787–795. https://doi.org/10.5006/1.3316001
Kentish P (2007) Stress corrosion cracking of gas pipelines—effect of surface roughness, orientations and flattening. Corros Sci 49:2521–2533. https://doi.org/10.1016/j.corsci.2006.12.014
Kleiner Y, Rajani B (2001) Comprehensive review of structural deterioration of water mains: statistical models. Urban Water 3:131–150. https://doi.org/10.1016/S1462-0758(01)00033-4
Krauss G, Thompson SW (1995) Ferritic microstructures in continuously cooled low-and ultralow-carbon steels. ISIJ Inter 35:937–945. https://doi.org/10.2355/isijinternational.35.937
Kritzer P (2004) Corrosion in high-temperature and supercritical water and aqueous solutions, a review. J Supercrit Fluids 29:1–29. https://doi.org/10.1016/S0896-8446(03)00031-7
Kuch A (1988) Investigations of the reduction and re-oxidation kinetics of iron (III) oxide scales formed in waters. Corros Sci 28:221–231. https://doi.org/10.1016/0010-938X(88)90106-0
Lee W, Lewandowski Z, Morrison M, Characklis WG, Avci R, Nielsen PH (1993) Corrosion of mild steel underneath aerobic biofilms containing sulfate-reducing bacteria. Part I: at high dissolved oxygen concentrations. Biofouling 7:217–239. https://doi.org/10.1080/08927019309386255
Lee W, Lewandowski Z, Nielsen PH, Hamilton WA (1995) Role of sulfate reducing bacteria in corrosion of mild steel: a review. Biofouling 8:165–194. https://doi.org/10.1080/08927019509378271
Li SY, Kim YG, Jeon KS, Kho YT, Kang T (2001) Microbiologically influenced corrosion of carbon steel exposed to anaerobic soil. Corrosion 57:815–828. https://doi.org/10.5006/1.3280616
Li S, Jung S, Park KW, Lee SM, Kim YG (2007) Kinetic study on corrosion of steel in soil environments using electrical resistance sensor technique. Mater Chem Phys 103:9–13. https://doi.org/10.1016/j.matchemphys.2007.02.076
Li QX, Wang ZY, Han W, Han EH (2008) Characterization of the rust formed on weathering steel exposed to Qinghai salt lake atmosphere. Corros Sci 50:365–371. https://doi.org/10.1016/j.corsci.2007.06.020
Li M, Liu Z, Chen Y, Ha Y (2016) Characteristics of iron corrosion scales and water quality variations in drinking water distribution systems of different pipe materials. Water Res 106:593–603. https://doi.org/10.1016/j.watres.2016.10.044
Liu ZY, Li XG, Du CW, Zhai GL, Cheng YF (2008) Stress corrosion cracking behavior of ×70 pipe steel in an acidic soil environment. Corros Sci 50:2251–2257. https://doi.org/10.1016/j.corsci.2008.05.011
Liu ZY, Li XG, Du CW, Cheng YF (2009a) Local additional potential model for effect of strain rate on SCC of pipeline steel in an acidic soil solution. Corros Sci 51:2863–2871. https://doi.org/10.1016/j.corsci.2009.08.019
Liu ZY, Li XG, Du CW, Lu L, Zhang YR, Cheng YF (2009b) Effect of inclusions on initiation of stress corrosion cracks in ×70 pipeline steel in an acidic soil environment. Corros Sci 51:895–900. https://doi.org/10.1016/j.corsci.2009.01.007
Liu ZY, Li XG, Cheng YF (2012) Mechanistic aspect of near-neutral pH stress corrosion cracking of pipelines under cathodic polarization. Corros Sci 55:54–60. https://doi.org/10.1016/j.corsci.2011.10.002
Lloyd JR, Mabbett AN, Williams DR, Macaskie LE (2001) Metal reduction by sulphate-reducing bacteria: physiological diversity and metal specificity. Hydrometallurgy 59:327–337. https://doi.org/10.1016/S0304-386X(00)00175-4
Lu X, Chen Z, Gu Z, Han Y (2008) Isolation of -aminobutyric acid-producing bacteria and optimization of fermentative medium. Biochem Eng J 41:48–52. https://doi.org/10.1016/j.bej.2008.03.005
Mabuchi K, Horn Y, Takahashi H, Nagayama M (1991) Effect of temperature and dissolved oxygen on the corrosion behavior of carbon steel in high-temperature water. Corrosion 47:500–508. https://doi.org/10.5006/1.3585285
Makar JM, Rajani B (2000) Gray cast-iron water pipe metallurgy. J Mater Civil Eng 12:245–253. https://doi.org/10.1061/(ASCE)0899-1561(2000)12:3(245)
Malvin R (1958) Underground corrosion: part I: corrosion mechanism of metals in soil. Anti-Corros Methods Mater 5(1):5–9. https://doi.org/10.1108/eb019420
Mao SX, Li M (1998) Mechanics and thermodynamics on the stress and hydrogen interaction in crack tip stress corrosion: experiment and theory. J Mech Phys Solids 46:1125–1137. https://doi.org/10.1016/S0022-5096(97)00054-9
Martin C (2013) Corrosion of carbon steel under sequential aerobic–anaerobic environmental conditions. Corros Sci 76:432–440. https://doi.org/10.1016/j.corsci.2013.07.017
Mcneill LS, Edwards M (2002) The importance of temperature in assessing iron pipe corrosion in water distribution systems. Environ Monit Assess 77:229–242. https://doi.org/10.1023/A:1016021815596
Melchers R, Jeffrey R (2008) The critical involvement of anaerobic bacterial activity in modeling the corrosion behavior of mild steel in marine environments. Electrochim Acta 54:80–85. https://doi.org/10.1016/j.electacta.2008.02.107
Moglia M, Davis P, Burn S (2008) Strong exploration of a cast iron pipe failure model. Reliab Eng Syst Saf 93(6):885–896. https://doi.org/10.1016/j.ress.2007.03.033
Mohebbi H, Li C (2011) Experimental investigation on corrosion of cast iron pipes. Inter J Corros. https://doi.org/10.1155/2011/506501
Moore T, Hallmark C (1987) Soil properties influencing corrosion of steel in Texas soils. Soil Sci Soc Am J 51:1250–1256. https://doi.org/10.2136/sssaj1987.03615995005100050029x
Murray JN, Moran PJ (1987) Influence of moisture on corrosion of pipeline steel in soils using in situ impedance spectroscopy. Corrosion 45:34–43. https://doi.org/10.5006/1.3577885
Naderi M, Ketabchi M, Abbasi M, Bleck W (2011) Analysis of microstructure and mechanical properties of different high strength carbon steels after hot stamping. J Mater Process Technol 211:1117–1125. https://doi.org/10.1016/j.proeng.2011.04.078
Neira J, Ortiz M, Morales L, Acevedo E (2015) Oxygen diffusion in soils: understanding the factors and processes needed for modeling. Chilean J Agric Res 75:35–44. https://doi.org/10.4067/S0718-58392015000300005
Nie X, Li X, Du C, Cheng Y (2009a) Temperature dependence of the electrochemical corrosion characteristics of carbon steel in a salty soil. J Appl Electrochem 39:277–282. https://doi.org/10.1007/s10800-008-9669-1
Nie X, Li X, Du C, Huang Y, Du H (2009b) Characterization of corrosion products formed on the surface of carbon steel by Raman spectroscopy. J Raman Spectrosc 40:76–79. https://doi.org/10.1002/jrs.2082
Noor EA, Al-Moubaraki AH (2014) Influence of soil moisture content on the corrosion behavior of ×60 steel in different soils. Arab J Sci Eng. https://doi.org/10.1007/s13369-014-1135-2
Norin M, Vinka TG (2003) Corrosion of carbon steel in filling material in an urban environment. Mater Corros 54:641–651. https://doi.org/10.1002/maco.200303680
Obuekwe CO, Westlake DWS, Plambeck JA (1987) Evidence that available energy is a limiting factor in the bacterial corrosion of mild steel by a Pseudomonas sp. Can J Microbiol 33:272–275. https://doi.org/10.1139/m87-046
Pelletier R, Allaire C (2003) Corrosion in potlining refractories: effect of cathode material interpreted using a unified approach. J Mater Sci Eng 55:58–62. https://doi.org/10.1007/s11837-003-0212-x
Pelletier G, Mailhot A, Villeneuve JP (2003) Modeling water pipe breaks—three case studies. J Water Resour Plan Manag 129:115–123. https://doi.org/10.1061/(ASCE)0733-9496(2003)129:2(115)
Penhale HR (1984) Corrosion of mild steel plates in some New Zealand Soils, after 20 years. N Z J Sci 27:57–68. https://doi.org/10.7931/DL1-SBP-0134
Petersen RB, Melchers RE (2012) Long-term corrosion of cast iron cement lined pipes. Cent Infrastruct Perform Reliab 23:1–10. http://hdl.handle.net/1959.13/1327302
Postgate JR, Kent HM, Robson RL, Chesshyre JA (1984) The genomes of Desulfovibrio gigas and D. vulgaris. Microbiol 130(7):1597–1601. https://doi.org/10.1099/00221287-130-7-1597
Qin F, Jiang C, Cui X, Wang Q, Wang J, Huang R, Yu D, Qu Q, Zhang Y, Peng PD (2018) Effect of soil moisture content on corrosion behavior of ×70 steel. Int J Electrochem Sci 13:1603–1613. https://doi.org/10.20964/2018.02.32
Rajani B, Kleiner Y (2003) Protecting ductile-iron water mains: what protection method works best for what soil condition? J Am Water Works Assoc 95(11):110–125. https://doi.org/10.1002/j.1551-8833.2003.tb10497.x
Rajani B, Makar J (2000) A methodology to estimate remaining service life of grey cast iron water mains. Can J Civ Eng 27(6):1259–1272. https://doi.org/10.1139/l00-073
Ralston K, Birbilis N (2010) Effect of grain size on corrosion: a review. Corrosion 66:075005–075013. https://doi.org/10.5006/1.3462912
Raman RS, Javaherdashti R, Panter C, Pereloma EV (2005) Hydrogen embrittlement of a low carbon steel during slow strain testing in chloride solutions containing sulphate reducing bacteria. Mater Sci Technol 21(9):1094–1098. https://doi.org/10.1179/174328405X51811
Rebak RB, Xia Z, Safruddin R, Szklarska-Smialowska Z (1996) Effect of solution composition and electrochemical potential on stress corrosion cracking of x-52 pipeline steel. Corrosion 52:396–405. https://doi.org/10.5006/1.3292126
Romer AE, Bell GE (2001) Causes of external corrosion on buried water mains. Pipelines Adv Pipelines Eng Constr. https://doi.org/10.1061/40574(2001)20
Sadiq R, Rajani B, Kleiner Y (2004) Probabilistic risk analysis of corrosion associated failures in cast iron water mains. Reliab Eng Syst Saf 86:1–10. https://doi.org/10.1016/j.ress.2003.12.007
Schwerdtfeger W (1954) Laboratory measurement of the corrosion of ferrous metals in soils. Corrosion 10(1):30–36. https://doi.org/10.5006/0010-9312-10.1.30
Schwerdtfeger WJ, Mcdorman ON (1952) Potential and current requirements for the cathodic protection of steel in soils. Corrosion 8:391–399. https://doi.org/10.5006/0010-9312-8.11.391
Serra ET, Mannheimer WA (1981) On the estimation of the corrosion rates of metals in soils by electrochemical measurements underground. Corrosion 741:111
Song Y, Jiang G, Chen Y, Zhao P, Tian Y (2017) Effects of chloride ions on corrosion of ductile iron and carbon steel in soil environments. Sci Rep 7:1–13. https://doi.org/10.1038/s41598-017-07245-1
Surnin DV (2008) The effect of the structure-phase state of iron-cementite nanocomposites on local activation processes. Prot Met 44:367–371. https://doi.org/10.1134/S0033173208040097
Tang X, Cheng YF (2011) Quantitative characterization by microelectrochemical measurements of the synergism of hydrogen, stress and dissolution on near-neutral pH stress corrosion cracking of pipelines. Corros Sci 53:2927–2933. https://doi.org/10.1016/j.corsci.2011.05.032
Trillo E, Beltran R, Maldonado J, Romero R, Murr L, Fisher W, Advani A (1995) Combined effects of deformation (strain and strain state), grain size, and carbon content on carbide precipitation and corrosion sensitization in 304 stainless steel. Mater Charact 35:99–112. https://doi.org/10.1016/1044-5803(95)00072-0
Videla HA (1996) Manual of biocorrosion. CRC Press, Boca Raton
Videla HA, Herrera LK (2009) Understanding microbial inhibition of corrosion. A comprehensive overview. Int Biodeterior Biodegrad 63:896–900. https://doi.org/10.1016/j.ibiod.2009.02.002
Wang S, Dun C, Li X, Liunn Z, Zhu M, Zhang D (2015) Field corrosion characterization of soil corrosion of ×70 pipeline steelin a red clay soil. Prog Nat Sci Mater Inter 25:242–250. https://doi.org/10.1016/j.pnsc.2015.06.006
Whitman W, Russell R, Davis G (1925) The solubility of ferrous hydroxide and its effect upon corrosion. J Am Chem Soc 47:70–79. https://doi.org/10.1021/ja01678a009
Wu YH, Liu TM, Luo SX, Sun C (2010) Corrosion characteristics of Q235 steel in simulated Yingtan soil solutions. Materialwiss Werkstofftech 41:142–146. https://doi.org/10.1002/mawe.201000559
Yan M, Sun C, Xu J, Dong J, Ke W (2014) Role of Fe oxides in corrosion of pipeline steel in a red clay soil. Corros Sci 80:309–317. https://doi.org/10.1016/j.corsci.2013.11.03
Yang Y, Cheng YF (2016) Effect of stress on corrosion at crack tip on pipeline steel in a near-neutral ph solution. J Mater Eng Perform 25(11):4988–4995. https://doi.org/10.1007/s11665-016-2369-9
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
About this article
Cite this article
Wasim, M., Shoaib, S., Mubarak, N.M. et al. Factors influencing corrosion of metal pipes in soils. Environ Chem Lett 16, 861–879 (2018). https://doi.org/10.1007/s10311-018-0731-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10311-018-0731-x