Abstract
A new hexaferrite composition, BaCo x Si x+y Fe12−2x−y O19 (x=0·90;y=0·05), in fine (∼μ size) powder form, is prepared. Ferrite paint formulations are made by dispersing this powder in different weight proportions in an epoxy resin. X-band (8–12 GHz) microwave absorption behaviour of the paint coatings of different thicknesses is studied. Remarkably high value, ≥10 dB, of signal absorption at 9·5 GHz is observed for a coating thickness of 0·60 mm with a ferrite fill factor of 57 wt%.
Similar content being viewed by others
References
Aiyar R, Rao N S H, Uma S, Rane S A and Srivastava C M 1989Proceedings int. conf. ferrites (ICF-5), Bombay (eds) C M Srivastava and M J Patni (New Delhi: Oxford & IBH Publishing Co.) p. 955
Amin M B and James J R 1981Radio Electron. Eng. 51 209
Goldman A 1990Modern ferrite technology (New York: Van Nostrand Reinhold) p. 386
John D 1988Aviation Week & Space Technol. 129 28
Mohammed N A 1989Proceedings int. conf. ferrites (ICF-5), Bombay (eds) C M Srivastava and M J Patni (New Delhi: Oxford & IBH Publishing Co.) p. 983
Naito Y and Suetake K 1971IEEE Trans. Microwave Theory Tech. MTT-19 65
Raju J S 1997Development of epoxies suitable as high temperature insulation resins, M. Tech. Thesis, IIT Bombay (unpublished)
Severin H and Stoll J P 1967Z. Angew. Phys. 23 209
Author information
Authors and Affiliations
Additional information
Most of this work, in a poster form, was presented at the 8th AGM of MRSI, BARC, Mumbai, February 10–12, 1997. The paper was adjudged the best for poster paper award
Rights and permissions
About this article
Cite this article
Abbas, S.M., Aiyar, R.P.R.C. & Prakash, O. Synthesis and microwave absorption studies of ferrite paint. Bull Mater Sci 21, 279–282 (1998). https://doi.org/10.1007/BF02744952
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02744952