Abstract
The 450 °C isotherm of the Zn-Fe-Al ternary phase diagram has been revised based on the findings in a number of recent studies. The Γ′ phase was included as an equilibrium compound in the system, the boundaries of the ζ, δ, Γ′, and Γ′ phases were more accurately outlined, and the invariant of the ι-η-θ three phase equilibrium has been placed at 1.3%A1 on the liquid phase boundary.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
Cited References
S. Yamaguchi, H. Makino, A. Sakatoku, and Y. Iguchi,Prvc., Galvatech '95, ISS, 787–794 (1995).
P. Perrot, J.C. Tissier, and J.Y. Dauphin,Z. Metallkd, 83, 11,786–790 (1992).
Z.W. Chen, R.M. Sharp, and J.T. Gregory,Mater. Sci. Technol, 6(12), 1173–1176 (1990).
T.Q. Coddington and D.C. Cook,Proc., Galvatech '95, ISS, 787–794 (1995).
M.Dauzat, F.Stouvenot, and T.Moreau,Proc., Galvatech '92, Amsterdam, The Netherlands, 449–454 (1992).
P. Bièle,Proc, Galvatech '95, ISS, 769–775 (1995).
S. Belisle, V. Lezon, and M. Gagne,J. Phase Equilibria, 12(3), 259–265 (1991).
N.-Y. Tang,Mater. Sci Technol, 11, 870–873 (1995).
N.-Y. Tang, “Comment on Fe-Al-Zn Diagram,”J. Phase Equilibria, 15(3), 237–238 (1994).
N.-Y. Tang, G.R. Adams, and P.S. Kolisnyk,Prvc., Galvatech '95, ISS, 777–782 (1995).
R.G. Grant and D.C. Cook, “Mössbauer Effect and XRD Studies of Iron-Zinc Binary Alloys,”Hyperfine Interactions, 94, 2309–2316 (1994).
N. Qiang, File Note, Project 641-020, Cominco Ltd., Product Technology Centre, Sept 14,1995
J. Grandjean, P. Detourney, and B. Renaux,ATB Metall, 29, 16–18 (1989).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Tang, N.Y. 450 °C isotherm of Zn-Fe-Al phase diagram update. JPE 17, 396–398 (1996). https://doi.org/10.1007/BF02667629
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF02667629