The fine structure of submicron iron particles

Summary

High resolution electron micrographs are shown of samples of colloidal alpha iron. According to the conditions of manufacture the samples occur as (1) large, well-formed dendrites, (2) shorter, more fragile dendrites, (3) serrated rods, (4) needles and (5) cubic particulates. The central stem is a line-up of single cubic crystals. Representative dimensions are given for the various measurable units. A fine laminar structure in the cubic particulates, and some of the side branches and main stems is noted. The same laminar structure is observed in some of the background platelet material from the mother liquor. Stereoscopic studies show that the dendrites are three dimensional with their branches and main stem not in the same plane. X-ray diffraction detects alpha iron plus some form of Fe₂O₃ in most samples.

Zusammenfassung

Es werden elektronenmikroskopische Aufnahmen mit hohem Auflösungsvermögen von kolloiden α-Eisenteilchen gezeigt. Entsprechend den Herstellungsbedingungen fallen die Teilchen als gro\e, gut ausgebildete Dendriten, als kürzere schwÄchere Dendriten, als gezackte Stangen, als Nadeln und als kubische Partikeln an. Der zentrale Stamm ist eine lineare Anordnung aus einzelnen kubischen Kristallen. ReprÄsentative Dimensionen sind für die verschiedenen me\baren Einheiten eingezeichnet. Eine fein laminierte Struktur der kubischen Teilchen und von einigen SeitenÄsten und Hauptachsen ist zu erkennen. Dieselbe Laminarstruktur wird teilweise an dem plÄttchenartigen Material, das als Untergrund aus der Mutterflüssigkeit dazwischen liegt, beobachtet. Stereoskopische Aufnahmen zeigen, da\ die Dendriten dreidimensional sind und da\ Seitenzweige und Hauptachsen nicht in der gleichen Ebene liegen. Röntgeninterferenzen lassen aufα-Eisen, sowie eine Form von Fe₂O₃ in den meisten Proben schlie\en.