Abstract
Cathode erosion continues to be a problem hindering the widespread application of plasma technology. In this work, cathode erosion was studied on titanium, stainless steel 314, copper-nickel 10% and 30%, and copper 122 for magnetically rotated arcs operating in argon, nitrogen, and argon/hydrogen mixtures at a constant magnetic flux density of 0.1 T Titanium and stainless steel gave very low erosion rates in argon (0.2 and 0.3, μg/C respectively). Cupronickels were shown to be suitable for nitrogen and hydrogen plasmas. The slope of hydrogen solubility versus temperature in the cathode material was found to be important in determining hydrogen plasma erosion characteristics. When the plasma gas has a high solubility in the cathode material, or can react with the cathode, a negative erosion rate may result. When gas solubility in the cathode is low, oxide stability and mode of electron emission may govern the erosion rate. A high gas solubility in the cathode material, as with hydrogen, can result in mechanical erosion due to micro-explosions near the cathode surface.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
R. N. Szente, R. J. Munz, and M. G. Drouet,Plasma Chem. Plasma Process. 12, 327–343 (1992).
R. J. Munz and M. Habelrih,Plasma Chem. Plasma Process. 12, 203–218 (1992).
R. J. Munz, R. N. Szente, and M. G. Drouet,Pure Appl. Chem. 64, 657–663 (1992).
J.-L. Meunier, S. Vacquie, and R. J. Munz,Plasma Chem. Plasma Process. 12, 1–16 (1992).
J.-L. Meunier and N. Desaulniers-Soucy, ISPC 11, Conf. Proc., Vol. 1, 422–427 (1993).
R. N. Szente, R. J. Munz, and M. G. Drouet,J. Phys. D. 27, 1443–1447 (1994).
Y. Gao, R. J. Munz, and P. G. Tsantrizos,Plasma Chem. Plasma Process. 14, 73–85 (1994).
J. Kutzner and H. C. Miller,IEEE Trans. Plasma Sci. 17, 688–694 (1989).
S. Anders and A. Anders,IEEE Trans. Plasma Sci. 19, 20–24 (1991).
J. Mostaghimi and R. J. Munz, 9th International Symposium on Plasma Chemistry, sponsored by IUPAC, Pugnochiuso. Italy, September 1989, Vol. 1, 102–108 (1989).
R. N. Szente, PhD thesis, McGill University, Montreal, 1989.
R. N. Szente, R. J. Munz, and M. G. Drouet,Plasma Chem. Plasma Process. 7, 349–364 (1987).
K. Dimoff, A. E. Guile, A. H. Hitchcock, and A. K. Vijh, “An evaluation of arc erosion mechanisms for oxide-covered cathodes in air at atmospheric pressure,” INRS Énergie internal report, 1977.
J. M. Dimoff, A. K. Viij, P. Antoine, and A. Sharah, “Electrode ablation in the presence of surface oxides,” INRS internal report, 1977.
F. M. Page, J. I. Wright, and G. Green, “Thermionic emission of electrodes in the presence of adsorbed gases,” Propulsion and Energetics Panel, Conf. Proc., 34th meeting, 8th colloquium, Paper No. 7, October 1969.
O. Kubaschewski, A. Cibula, and D. C. Moore, “Surface reactions with gases during processing of metals,”Gases and Metals, Elsevier, New York (1970), Chap. 3.
J. Halbritter,IEEE Trans. Electr. Insul. E1-20, 671–681 (1985).
B. M. Smirnov,Negative Ions, Atomizdat, Moscow (1987), p. 176.
Smithells Metals Reference Book 7th edn., Butterworth-Heineman, Oxford (1992).
N. Desaulniers-Soucy, “Spectroscopic study of copper vapours emitted by an arc in rotation in contaminated argon,” M. Eng. Thesis, McGill University, Montreal, Canada, 1992.
J. Siwka, and S. Tochowicz, ISPC 11, Conf. Proc., Vol. 1, 574–579 (1993).
R. Knight and R. W. Smith, ISPC 11, Conf. Proc., Vol. 1, 139–145 (1993).
J. D. Fast,Interaction ofGases and Metals, Vol. 1:Thermodynamics and Phase Relationships, Academic Press, New York (1965).
J. D. Fast,Gases in Metals, Macmillan, New York (1976).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kwak, J.E., Munz, R.J. The behavior of titanium, stainless steel, and copper-nickel alloys as plasma torch cathodes. Plasma Chem Plasma Process 16, 577–603 (1996). https://doi.org/10.1007/BF01447010
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF01447010