Solid-state phase transformations have been observed to occur in polytypic crystals of cadmium iodide, grown from solution, upon cooling them down to — 175 °C. In addition, structural changes with respect to streaking, arcing, and diffuseness of diffraction spots and the background intensity on the x-ray photographs have been observed. The results have been interpreted on the basis of movement of unit and partial edge dislocations generated during crystal growth. The movement of dislocations is possibly caused by internal strains produced upon cooling.
Similar content being viewed by others
References
Gulzari Lal and G. C. Trigunayat, J. Solid State Chem. 9, 132 (1973).
R. S. Tiwari and O. N. Srivastava, J. Crystal Growth 21, 277 (1974).
T. Minagawa, in International Conference on Crystal Growth—4, Japan (1974).
G. C. Trigunayat, Nature 212, 808 (1966).
V. K. Agrawal and G. C. Trigunayat, Acta Cryst. A25, 401, 407 (1969).
Ajit Ram Verma and P. Krishna, Polytypism and Polymorphism in Crystals (Wiley, New York, 1966), Chapter 6.
E. Alexander, Z. H. Kalman, S. Mardix, and I. T. Steinberger, Phil. Mag. 21, 1237 (1970).
R. W. James, The Optical Principles of the Diffraction of X-Rays (G. Bell and Sons Ltd., London, 1965), Chapter 5.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Arora, R.M., Trigunayat, G.C. Phase transformations at −175 °C in polytypic crystals of cadmium iodide. J Low Temp Phys 23, 231–239 (1976). https://doi.org/10.1007/BF00117253
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF00117253