Abstract
In this study, Si x -Sn6-Al(94−x) (x = 40, 50, 60, 70) alloy ribbons were obtained by melt spinning, and the ribbons were ball-milled into fine powders. The powders of −500 mesh (< 25 μm) were screened by sieving, followed by etching the Al element to produce porous Si alloy powders. The Burnauer-Emmett-Teller surface area of the porous Si alloy powder increased with increasing Al content. On the contrary, the Batter-Joyner-Halenda pore radius decreased with increasing Al content, which was caused by the very finely solidified Al phase due to its low latent heat in addition to the effective etching to make the porous structure. Of the Si x -Sn6-Al(94−x) alloy powders, the porous et-Si40Sn6Al54 powder obtained by acid etching showed the best electrochemical properties with a well-developed porous structure.
Similar content being viewed by others
References
W. J. Zhang, J. Power Sources 196, 13 (2011).
M. Winter, J. O. Besenhard, M. E. Spahr and P. Novak, J. Adv. Mater 10, 725 (1998).
Z. Chen, Y. Cao, J. Qian, X. Ai and H. Yang, J. Mater. Chem. 20, 7266 (2010).
C. J. Wen and R. A. Huggins, J. Solid State Chem. 37, 271 (1981).
W. J. Weydanz, M. Wohlfahrt-Mehrens and R. A. Huggins, J. Power Sources 81, 237 (1999).
M. N. Obrovac and L. Christensen, Electrochem. Solid State Lett. 7, 93 (2004).
H. Wu et al., Nat. Nanotechnol. 7, 309 (2012).
G-A. Nazri and G. Pistoia, Lithium Batteries: Science and Technology (Kluwer Academic/Plenum, Boston, 2004).
H. Kim, M. Seo, M. Park and J. Cho, Angewandte Chemie International Edition 49, 2146 (2010).
Z. H. Wen et al., Electrochemistry Communication 29, 67 (2013).
H. P. Jia, P. F. Gao, J. Yang, J. L. Wang, Y. N. Nuli and Z. Yang, Adv Energy Mater 1, 1036 (2011).
I. Hong, B. Scrosati and F. Croce, Solid Sate Ionics 232, 24 (2013).
H. C Tao, M. A. Huang, L. Z. Fan and X. H. Qu, Electrochimica Acta 89, 394 (2013).
W-R. Liu, Z-Z. Guo, W-S. Young, D-T. Shieh, H-C. Wu, M-H. Yang and N-L. Wu, J. Power Sources 140, 139 (2005).
C-M. Hwang and J-W. Park, Surf. Coat. Technol. 205, S439 (2010).
D. Larcher, S. Beattie, M. Morcrette, K. Edstr¨om, J-C. Jumas and J-M. Tarascon, J. Mater. Chem. 17, 3759 (2007).
W-H. Zhang, J. Powder Sources 196, 877 (2011).
M. N. Obrovac and L. Christensen, Electrochem Solid- State Lett. 7, 93 (2004).
S. Arico, P. Bruce, B. Scrosati, J. Tarascon and W. V. Schalkwijk: Nat Mater 4, 66 (2005).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Yoon, H.S., Choi, HR., Sohn, K.Y. et al. The synthesizing of porous anode materials processed via rapid solidification of Si-Sn-Al alloys for Li-ion batteries. Journal of the Korean Physical Society 67, 1986–1991 (2015). https://doi.org/10.3938/jkps.67.1986
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.3938/jkps.67.1986