Abstract
Lead (Pb2+) is among the most toxic heavy metals even in low concentration and cause toxicity to human’s health and other forms of life. It is released into the environment through different industrial activities. The biosorption of Pb2+ from aqueous solutions by biomass of commonly available, marine alga Gelidium amansii was studied. The effects of different variables on Pb2+ removal were estimated by a two-level Plackett–Burman factorial design to determine the most significant variables affecting Pb2+ removal % from aqueous solutions. Initial pH, Pb2+ concentration and temperature were the most significant factors affecting Pb2+ removal chosen for further optimization using rotatable central composite design. The maximum removal percentage (100%) of Pb2+ from aqueous solution by Gelidium amansii biomass was found under the optimum conditions: initial Pb2+ concentration of 200 mg/L, temperature 45 °C, pH 4.5, Gelidium amansii biomass of 1 g/L and contact time of 60 minutes at static condition. FTIR analysis of algal biomass revealed the presence of carbonyl, methylene, phosphate, carbonate and phenolic groups, which are involved in the Pb2+ ions biosorption process. SEM analysis demonstrates the ability of Gelidium amansii biomass to adsorb and removes Pb2+ from aqueous solution. EDS analysis shows the additional optical absorption peak corresponding to the Pb2+ which confirms the involvement of Gelidium amansii biomass in the adsorption of Pb2+ ions from aqueous solution. Immobilized Gelidium amansii biomass was effective in Pb2+ removal (100%) from aqueous solution at an initial concentration of 200 mg/L for 3 h. In conclusion, it is demonstrated that the red marine alga Gelidium amansii biomass is a promising, efficient, ecofriendly, cost-effective and biodegradable biosorbent for the removal of Pb2+ from the environment and wastewater effluents.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Introduction
Heavy metals are the main group of inorganic contaminants. Main sources of heavy metals contamination include agricultural chemicals (pesticides, fertilizers) and industrial activities including plating, petroleum refining, mining activities, smelting industries, car exhausts, battery manufacturing and pigments. Industrial activities and agricultural chemicals often discharge wastes containing heavy metals that flow into streams, lakes, ground water and rivers. The presence of heavy metals in aqueous water streams is hazardous to the environment, poses a potential human health risks and causes harmful effects to living organisms in water and also to the consumers of them1,2.
Lead is among the most toxic heavy metals affecting the environment3. Lead pollution results from textile dyeing, pigments, ceramic and glass industries, petroleum refining, metal plating and finishing, battery manufacturing and mining operations1,4. Lead even at low concentrations can be hazardous and cause toxicity to humans and other forms of life. The USA environmental protection agency regulations for drinking water limits lead in drinking water to 0.015 mg/L. While a drinking-water guideline value for lead of 0.01 mg/L has been established by WHO5. According to India standard drinking water specification, highest desirable limit of lead in drinking water is 0.05 ppm (0.05 mg/L)6. The toxicity of metal ions is owing to their ability to bind with protein molecules and prevent replication of DNA and thus subsequent cell division7. Lead accumulates mainly in bones, brain, kidney and muscles and the increase in lead concentration may cause many serious disorders like anaemia, kidney and liver diseases, gastrointestinal damage, nervous disorders and sickness even death8,9. It is therefore, essential to remove Pb(II) from wastewater before disposal.
Conventional methods applied for lead removal from industrial waste waters and aqueous solutions include coagulation and precipitation, electrochemical treatment, ion exchange, chemical oxidation or reduction, evaporation, electroplating adsorption, and membrane separation. However, these methods have several disadvantages, such as generation of toxic waste products, too expensive, not always effective for metals with low concentrations, high reagent and energy requirements10,11,12. Adsorption by activated carbon is the most efficient classical method, but the cost of its production is expensive and it cannot be recycled13.
Consequently, it is urgent to find cost-effective alternative technologies to remove heavy metal ions from waste water14,15. Biosorption is effective biological treatment of wastewater that utilizes low cost biosorbents for the removal of toxic heavy metals16. Biosorption could be considered as a promising alternative technique for heavy metal ions removal10 as it offers many advantages over traditional treatment methods including cost-effectiveness, high metal binding ability, high efficiency in diluted effluents, environmentally friendly17 and regeneration of biosorbent with possibility of metal recovery.
Biosorbents for lead removal include fungi18, bacteria19 and algae biomass20,21. Algae proved to possess high metal binding capacities22 because of the presence of proteins, polysaccharides or lipid on their cell walls surfaces containing some functional groups such as carboxyl, hydroxyl, amino and sulphate, which can act as binding sites for metals23,24.
Heavy metals biosorption is affected by many environmental variables such as temperature, pH, ionic strength, etc. A statistical approach has been employed in the present study for which a Plackett–Burman design was used for identifying significant variables influencing the biosorption of Pb2+ from aqueous solutions by Gelidium amansii. The levels of the significant variables and the interaction effects between various variables which influence the biosorption of Pb2+ were further analyzed and optimized using rotatable central composite design (RCCD).
The aim of the study was to investigate the efficiency of Gelidium amansii as a cost effective biosorbent for Pb2+ removal from aqueous solutions, the statistical optimization for Pb2+ removal, biomass characterization before and after Pb2+ biosorption using SEM, FTIR and EDS, in addition to Gelidium amansii immobilization in sodium alginate beads and its application in Pb2+ removal.
Results and Discussion
Heavy metals biosorption from aqueous solutions can be considered a promising technique in the treatment of wastewater. It is based on the ability of biological materials (which can include living or dead microorganisms and their components, seaweeds, etc.) to collect heavy metals ions from wastewater through physicochemical absorption or metabolically mediated pathways of uptake25,26. Biosorption is determined by equilibrium, it is largely influenced by the concentration of biomass, pH and the interaction between various metals ions8. A number of physico-chemical factors determine overall biosorption performance27. Since the main mechanism of biosorption was found to be ion exchange, protons compete with metal cations for the binding sites and for this reason; pH is the most important process parameter which influences the availability of the site to the sorbate28. The other factors important in biosorption include the biosorbent nature and the availability of binding sites (type and the concentration of the biomass)29; initial heavy metal concentration which when increased increases the quantity of biosorbed heavy metals per unit weight of the biomass, but decreases removal efficiency; temperature usually enhances heavy metals removal when increased by increasing surface activity and kinetic energy of the adsorbate27. The effects of biomass concentrations, heavy metal concentrations, temperature, pH, agitation/static and contact time on the biosorption of Pb2+ have been studied.
Screening of significant variables affecting the Pb2+ removal % by Gelidium amansii biomass using Plackett–Burman design
The effect of the six variables considered in this study (namely: contact time, initial Pb2+ ions concentration, pH, temperature, biomass and agitation/static) on Pb2+ removal % was statistically analyzed using Plackett–Burman Design (PBD). The Gelidium amansii biomass was dried in oven at 70 °C for 72 hrs, and then milled with a blender, sieved to get particle with the size pass through a laboratory test sieve Endecotts/ Ltd., London, England, with mesh size of 125 µm (Supplementary Fig. S1).
The design matrix of the Plackett-Burman used to determine the most significant variables affecting Pb2+ removal % from aqueous solutions using Gelidium amansii biomass is shown in Table 1. The experiment was conducted in 12 runs. Table 1 shows the levels of coded and actual values of the tested independent variables and the Pb2+ removal % in each run. The data listed in Table 1 indicated a variation on lead removal %, from 92.52 to 99.69, in the 12 trials. This variation suggested that the process optimization was important for improving the removal efficiency of lead to attain maximum Pb2+ removal. Results showed the highest lead removal % (99.69%) in run no. 7. The relationship between Pb2+ removal % and the independent variables was analyzed with regard to their effects on Pb2+ removal % using a Plackett–Burman design (Table 2). The coefficient of each factor represents the effect extent of this factor on Pb2+ removal. Analysis of the regression coefficients of the six factors (Table 2) showed that Pb2+ concentration (B) and temperature (D) with coefficient value 0.67 and 0.86 and percent of contribution 15.80 and 20.28%; respectively) had positive effects on lead removal % which means that the increase in temperature and Pb2+ concentration could exert positive effect on Pb2+ removal. Where, contact time (A), pH (C), biomass concentration (E) and agitation-static (F) (with coefficient value −0.07, −2.06, −0.28 and −0.30 and percent of contribution 1.65%, 48.58%, 6.60% and 7.08%; respectively) had negative effects which means that the decrease in contact time, pH, biomass concentration and agitation/ static levels could exert positive effect on Pb2+ removal.
Table 2 and Fig. 1 show the estimated effect of each variable on Pb2+ removal %. The large effect, either negative or positive, indicates that the variable has a large impact on Pb2+ removal, whereas the near zero effect means that the variable has little or no effect. The results indicated that the high levels of initial Pb2+ ion concentration and temperature positively affected on lead removal %. Whereas, high levels of the other four variables (pH, contact time, biomass and agitation) negatively affected on lead removal %. The contact time (A), biomass (E) and agitation/static (F) are three insignificant variables with lower effects (−0.14, −0.56 and −0.6; respectively). Pareto chart (Supplementary Fig. S2) showed that pH (C) was the most significant variable affecting Pb2+ removal (48.58%) by Gelidium amansii, followed by temperature (D) (20.28%), Pb2+ concentration (B) (15.80%), then agitation/static (F), biomass (E) and contact time (A); respectively.
The normal probability plot (NPP) of the residuals
A normal probability plot is a plot represents the normal distribution of the residuals to check the adequacy of the model30. The residuals are the variation between the experimental values of the responses and the values that expected by the theoretical model. A small residual values shows that model prediction is very accurate31. Figure 2 shows NPP of the residuals plotted against the expected values of the model. The data points (the residuals from the fitted model) are found close to the diagonal line for Pb2+ removal %, however the data appear to be normally distributed and signifying the validity of the model.
The ANOVA of the Plackett-Burman design demonstrated that the model was highly significant as was evident from the Fisher’s F-test (39.45) with a very low P-value (0.00047) and the t-Stat (619.14). The variable with confidence level above 95% is considered as significant parameter. The factors evidencing P-values of less than 0.05 were considered to have significant effects on the Pb2+ removal. The t-values and P-values were estimated for each independent variable as shown in Table 2 and were used as a tool to check the significance of each parameter. The results in Table 2 showed that the most significant variables which affecting in lead removal by Gelidium amansii with confidence level above 95% was pH (C) having a probability value of 0.000042 then temperature (D) and Pb2+ concentration (B) with probability values of 0.0025 and 0.008; respectively. While, contact time, biomass and agitation, with confidence levels below 95%, were considered insignificant.
The fit of the model was checked by the determination of coefficient (R2). The R2 value is always between 0 and 1. If the value of R2 is close to 1, the model is stronger and better to predict the response. In the present study, the R2 value is 0.979 indicated that up to 97.9% variability in lead removal % could be calculated by the model and only 2.1% of the total variability in lead removal % is not explained by the model. In addition, the value of adjusted determination coefficient (adjusted R2 = 0.954) is also very high, showing a high significance of the model (Table 2). Therefore, R2 and R2 adj emphasized that the model is highly significant and suitable to explain of the relationship between the selected variables and the Pb2+ removal %. The value of predicted R2 is also high to support a high significance and accuracy of the model. The predicted R2 value obtained is 0.8809, indicating that the model does not explain only 11.91% of the total variations. This also revealed that predicted R2 of 0.8809, for the Pb2+ removal by Gelidium amansii, is in reasonable agreement with the adjusted R2 of 0.954 indicating that a good agreement between the experimental and predicted values of Pb2+ removal %.
By applying multiple regression analysis on the experimental data, the experimental results of Plackett-Burman design were fitted with the first-order polynomial equation which represent the Pb2+ removal % as a function of the contact time, Pb2+ concentration, pH, temperature, biomass and agitation–static.
In a confirmatory experiment, to evaluate the accuracy of Plackett-Burman, the conditions which expected to be optimum for maximum Pb2+ removal by Gelidium amansii from aqueous solutions were contact time of 60 minutes, initial Pb2+ concentration of 200 mg/L, pH 4, temperature 50 °C, Gelidium amansii biomass of 1 g/L at static condition. Under these conditions, the maximum removal percentage of Pb2+ was 94.3% which is higher than the removal percentage of Pb2+ obtained before applying Plackett Burman (45.9%) by 2.05 times.
In the present study, the agitation is non-significant factors (P-value = 0.107). Our results are in agreement with those reported by Saraf and Vaidya32 in that the agitation had a negative effect on the biosorption. This may be due to the swelling behaviour of the biomass particles of the red algae due to the presence of a high proportion of carrageenan constituting up to 75% of the dry weight of the biomass, making it suspended in the solutions. Whereas, Tahir et al.33 reported that agitation enhances biosorption and facilitates proper contact between the metal ions in solution and the biomass-binding sites and thereby promotes effective transfer of sorbate ions to the sorbent sites.
Statistical optimization of Pb2+ removal by Gelidium amansii using rotatable central composite design (RCCD)
On the basis of P-values (Table 2), initial pH (X1), Pb2+ concentration (X2) and temperature (X3) were chosen for further optimization using rotatable central composite design, where these variables were the most significant factors affecting Pb2+ removal. The RCCD had six axial points, eight factorial and six center points resulting in a total of 20 experiments used to optimize the chosen variables, all in three replicates. The six replicates at the centre points were conducted to determine the experimental errors. A design matrix that contains the three variables, their coded and actual levels and the responses which are percentage removal of Pb2+ was displayed in Table 3. Contact time, biomass and agitation–static which exerted a negative effect on Pb2+ removal and are insignificant variables were maintained in all trials at their low levels of Placket-Burman design for further optimization by RCCD.
Experimental and predicted Pb2+ percentage removals for the twenty trials of the employed RCCD matrix are presented in Table 3. Depending on the differences in the three independent variables, the results show variation in the percentage of Pb2+ removal. Pb2+ removal ranged from 85.88 to 100%. The highest levels of Pb2+ removal were obtained in run no. 3 and 15 with value of 100%, where pH is 4.5, Pb2+ concentration is 200 mg/L and temperature is 45 °C. While the minimum Pb2+ removal was observed in run number 4 with value of pH is 6, Pb2+ concentration is 100 mg/L, and temperature is 60 °C.
Multiple regression analysis and ANOVA
The multiple regression analysis of the model and the analysis of variance (ANOVA) are presented in Tables 4 and 5. A regression model with a determination coefficient (R2) value higher than 0.9 having a very high correlation34. R2 value should not be less than 0.75 until the model is appropriate35. However, Koocheki et al.36 assumed that a large R2 value does not always mean that the regression model is good and such conclusion can only be made based on a high value of adjusted R2. The present R2 and adjusted R2 values for removal of Pb2+ using Gelidium amansii biosorbent were found to be 0.9891 and 0.9792; respectively indicating the fitness of the model for the experimental data. The determination coefficient (R2 = 0.9891) indicated that the model cannot explain only 1.09% of the total variations and 98.91% of Pb2+ removal variations can be described by the selected model. In addition, the adjusted determination coefficient (R2 adj = 0.9792) is also very high, indicating a high significance of the model, which indicated a good agreement between the experimental and predicted values of Pb2+ removal. Predicted R2 is a measure of how model significance in predicting the response value. The predicted R2 (R2 pred = 0.9340) is also high enough to indicate the high significance of the model. The adjusted and predicted R-squared values should be within 20% of each other to be in good agreement37. In our study, the predicted R2 is 0.9340, revealed that it is in a reasonable agreement with the adjusted R2 value of 0.9792. This indicated a good agreement between the observed and predicted values and showing that the model offers 93.40% variability in Pb2+ removal prediction in the range of experimental variables. Thus the model is adequate for prediction in the range of the experimental variables. The negative coefficient values indicate that linear, mutual interactions or quadratic effects of the variables negatively affect Pb2+ removal % by Gelidium amansii (inverse relationship between the factor (s) and the biosorption percentage), whereas positive coefficient values mean that the variables increase Pb2+ removal % by Gelidium amansii in the tested range of the experimental variables (Table 4). Interactions between two factors could appear as an antagonistic effect (negative coefficient) or a synergistic effect (positive coefficient). A low value of the coefficient of variation % (CV = 0.74%) shows a better precision and reliability of the experiments38. Adequate precision value of the present model is 27.62 and this value suggests that the model can be used to navigate the design space. PRESS value in the current study is 29.16. Standard deviation and mean value are 0.69 and 93.76; respectively (Table 4).
The ANOVA results (Table 5) demonstrates that the model is highly significant as evident from the Fisher’s F test (F value of 100.63) with a very low probability value (P-value less than 0.0001). Values of Prob > F less than 0.05 indicate that model terms are significant. The Lack of Fit F-value of 2.74 is not significant as the P‒value is >0.05 (0.1464). Therefore, the high value of adjusted R2 of the model, non-significance lack-of-fit, high F‒value, low standard deviation and coefficient of variance, low PRESS value and high adequate precision indicate high precision and validity of the model used in predicting the Pb2+ removal efficiency using Gelidium amansii biomass.
The significance of each coefficient was determined by the probability values (P-value) and F-value which are listed in Table 5. The coefficient is significant if the F-value is large and P < 0.05. Based on P‒values and F‒values, it can be seen from the degree of significance that the linear coefficients of initial pH (X1), Pb2+ concentration (X2) and temperature (X3), interaction between X1X3 and X2X3, quadratic effect of X1, X2 and X3 are significant as can be seen by the F‒values of 5.27, 8.53, 11.95, 32.69, 87.08, 207.23, 102.90, 567.25; respectively, as well as P‒values of 0.0446, 0.0153, 0.0061, 0.0002, <0.0001, <0.0001, <0.0001, <0.0001; respectively. Furthermore, P‒values of the coefficients suggest that among the three variables studied, the interaction between X2 and X3 had a very significant effect on Pb2+ removal by Gelidium amansii with F‒value of 87.08 and a probability value of <0.0001, indicating that <99.99% of the model affected by Pb2+ concentration (X2) and temperature (X3). On the other hand, the interaction effect between initial pH (X1), Pb2+ concentration (X2) is not significant model term that not contribute to the response (Pb2+ removal).
The fit summary results (Supplementary Table S1) showed that, the quadratic model is a highly significant model fitting the RCCD used for Pb2+ removal by Gelidium amansii with a very low probability value (P‒value < 0.0001), also lack of fit F‒value 2.74 (the lack of fit is not significant, P‒value = 0.1464). The summary statistics of the quadratic model showed the smallest standard deviation of 0.69 and the largest adjusted and predicted R-squared of 0.9792 and 0.9340; respectively.
The coefficients of regression equation were calculated and the data (Table 4) was fitted to a second-order polynomial equation. The Pb2+ removal (Y) by Gelidium amansii biomass can be expressed in terms of the following regression equation:
where Y is the predicted value of Pb2+ removal %, X1, X2 and X3 are the coded levels of initial pH, Pb2+ concentration, and temperature.
Contour and three dimensional (3D) surface plots
To explain the relationship between each pair-wise combination of the three variables (X1X2, X1X3 and X2X3) and the responses, three-dimensional and corresponding contour plots were generated by plotting the response (Pb2+ removal %) on Z-axis against two independent factors while keeping the other factor at its central point (zero level) to determine the optimum conditions for Pb2+ removal %.
The three dimensional surface plot and its corresponding contour plot (Fig. 3A), showing the simultaneous effect of initial pH (X1) and Pb2+ concentration (X2) on Pb2+ removal %, while temperature (X3) was kept at their zero levels (45 °C). Figure 3A shows that the lead removal % increased with an increase in the initial pH up to a certain pH value and then further increase in pH resulted in a gradual decrease in Pb2+ removal percentage. On the other hand, it can be seen from Fig. 3A that the lead removal % increased with increase in Pb2+ concentration (X2) and higher levels of Pb2+ concentration support relatively low percentage of lead removal. By solving the Eqn. (2) and analysis of Fig. 3A, the maximum predicted Pb2+ removal percentage of 99.85% was obtained at the optimum predicted levels of pH and Pb2+ concentration of 4.6 and 211 mg/L; respectively at temperature of 45 °C.
Figure 3A shows that the effect of initial lead ions concentration was significant and had a positive effect on biosorption of metal ions. The biosorption of lead ions increased with increasing lead ions concentration and reached the maximum. However, further increasing in lead concentration leads to a gradual decrease in the removal percentage. This can be attributed to that the adsorption sites on the surface area of algal biomass were free and remain unsaturated at the beginning, resulting in high metal adsorption. Thereafter, with increasing metal concentration, the metal removal percentage decreased due to the adsorption sites on the surface of algae were saturated39. Increasing initial lead ion concentration increased lead removal by the adsorbent, could be attributed to the increase in the mass transfer due to higher driving force40,41.
Figure 3A shows that the biosorption of Pb2+ on the surface of Gelidium amansii is highly pH dependent. Numerous studies show that pH is an important factor affecting heavy metals biosorption42. In the biosorption process, it is well known that pH could affect the functional groups and the metal binding sites on the cell surface of the biomass as well as the metal ion solubility in water43. The cell walls of red algae possess complex cell walls composed of cellulose, xylan or mannan fibrils and extensive matrix polysaccharides including the economically important carrageenan, agar, gelans (mucusy sugars) and proteins together with minerals. Some red algae can absorb calcium from seawater and store calcium carbonate in their bodies44,45. These components can provide different functional groups as binding sites for the metal ions. At low pH, the protons of functional groups give a generally positive charge to the polymer molecules that are unable to adsorb positively charged heavy metal ions. Increasing the pH reduces the electrostatic repulsion, exposing more ligands on the alga cell wall carrying negative charges such as amino, phosphate and carboxylic groups with subsequent attraction and biosorption of metal ions46,47. The functional groups such as hydroxyl and amino groups were found to be responsible for the biosorption of lead ions. This is evidence that the lead biosorption occurs through the ion exchange mechanism where the lead ions is linked to the binding sites by replacing two acid H at low pH48. The increase in availability of the adsorption sites improved the access of lead to the adsorption sites of the adsorbent49. Moreover, the pH value affects the solubility of the metal ions in solution50. Lead is present in its free ionic forms (Pb2+) at pH values less than 5. The significant increase of the biosorption of metal ions by increasing the pH to 4.5 is may be due to the cell walls would have a negative net charge, which promotes electrostatic attractions between positively charged Pb2+ cations and negatively charged binding sites. Thus, higher pH value may affect the number of negatively charged sites, which is highly dependent on the dissociation of functional groups. In addition, H+ competes with Pb2+ for the same adsorption position24,51. The decrease in the biosorption of metal ions at higher pH values could be related to the repulsion between the negative charge of anionic species in solution and negative surface charge of the sorbents52,53. Also, the precipitation of insoluble metal hydroxides occurs restricting the biosorption process. High alkaline pH causes decrease in the solubility of metals, which causes a decrease in absorption rate54. Therefore, the best removal occurs at a pH that ranged from 3 to 5. At pH below 2.5, the positive charge (H+) density on the sites of biomass surface minimizes metal sorption, and above 6, metal precipitations is favored55. The maximum removal of lead on biosorbent by chemically-modified biomass of marine brown alga Laminaria japonica was observed at pH 5.356.
The 3D surface plot and its corresponding contour plot in Fig. 3B shows Pb2+ removal efficiency as function of initial pH (X1) and temperature (X3) while Pb2+ concentration (X2) was kept at their zero levels (200 mg/L). It is evidence from Fig. 3B that the Pb2+ removal increased at pH beyond 4.5 after which Pb2+ removal decreased. Lower and higher levels of temperature (X3) support relatively low percentage of Pb2+ removal and the maximum percentage of Pb2+ removal clearly situated close to the central point of temperature. By solving the Eqn. (2) and analysis of Fig. 3B, the maximum predicted Pb2+ removal of 99.84% was obtained at the optimum predicted levels of pH and temperature of 4.7 and 43 °C; respectively at Pb2+ concentration of 200 mg/L.
Figure 3B shows that with an increase in temperature, the biosorption of lead ions by Gelidium amansii increases. The effect of temperature on the biosorption process found in the literature presents different and opposite behaviours. Patel and Chandel57, Córdova et al.58 and Rathinam et al.59 reported higher uptake capacities in different organisms as temperature increases. On the other hand, Ho et al.60 and Dal Bosco et al.61 reported practically temperature-independent effect on biosorption capacity. In contrast, Cruz et al.62 and Aksu63 obtained a decrease in the uptake capacity with temperature increase. A similar trend to our results was obtained by previous studies. The maximum Pb(II) removal rate by algae was found to increase with an increase in temperature and reached the maximum value (98%) at the temperature of 40 °C64. This means that the binding of Pb (II) on the active sites of the biosorbent becomes stronger at a higher temperature and that the biosorption process is endothermic. The most suitable sorption temperature for the removal of Pb2+ and Cd2+ in aqueous effluent using Caladium bicolor biomass was obtained at 40 °C65. The optimal temperature for completely lead removal from aqueous solutions with Aspergillus terreus was 50 °C58. Patel and Chandel57 reported that 94% Cu ions was removed at 45 °C using Bacillus licheniformis. Rathinam et al.59 reported that the maximum cadmium biosorption from simulated wastewaters has been obtained at 60 °C using red alga Hypnea valentiae biomass.
The increase in biosorption rate can be attributed to the increase in temperature is known to increase the ions diffusion rate of adsorbed molecules from the aqueous solution to the biosorbent surface as a result of the reduced viscosity of the solution66,67. Higher temperatures usually enhance sorption due to the increased surface activity and kinetic energy of the solute28. The increase in biosorption rate may be due to the formation of new adsorption active sites68. Saleem et al.69 reported that with an increase in temperature, the pores of the algae biomass surface enlarge resulting in an increase of the surface area available for the sorption, diffusion and penetration of the metal ions within the pores of surface resulting in an increase in biosorption. Only a small increase in cadmium biosorption by marine macroalga Cystoseira baccata as biosorbent was obtained at 45 °C70. The alginate chains in brown algae yield an array of cavities known as the egg-box structure71 which may stabilize the alga biomass at higher temperature and increase metal biosorption.
However, further increase in temperature above 45 °C results in a decrease in the removal efficiency that can be attributed to deactivating the biosorbent surface, or destructing of some active sites on the biosorbent surface due to rupture of the bonds72 or due to the weakness of biosorption forces between the active sites on the surface of the algae and the lead ions. Physical damage to the biosorbent can be expected at higher temperatures28.
The 3D plot and its corresponding contour plot (Fig. 3C), shows the effects of Pb2+ concentration (X2) and temperature (X3) on Pb2+ removal efficiency, when pH (X1) was kept at their zero levels (4.5). The effect of temperature is found to be more significant than that of the initial Pb2+ concentration. The percentage Pb2+ removal increased with increasing both of initial Pb2+ concentration and temperature to the optimum levels and thereafter the Pb2+ removal decreased. By solving the Eqn. (2) and analysis of Fig. 3C, the maximum predicted Pb2+ removal of 99.84% was obtained at the optimum predicted levels of Pb2+ concentration and temperature of 206 mg/L and 44 °C; respectively at pH 4.5.
According to the results of RCCD, the maximum removal percentage of Pb2+ from aqueous solution by Gelidium amansii biomass (100%) was found under the optimum conditions: initial Pb2+ concentration of 200 mg/L, temperature 45 °C, pH 4.5, Gelidium amansii biomass of 1 g/L and contact time of 60 minutes at static condition. The maximum bioremediation efficiency of 90% of Pb2+ in optimal conditions by using red alga Porphyra leucosticta was at biomass dosage 15 g/L, pH 8 and contact time 120 minutes containing initial 10 mg/L of Pb2+ solution73. The optimum biosorption conditions of lead (II) ions on Sargassum ilicifolium, brown seaweed, were determined as initial pH 3.7, biosorbent concentration 0.2 g/L, and initial Pb2+ ion concentration 200 mg/L74.
Under optimum conditions, the maximum biosorption of Pb2 using Cystoseira trinodis (brown algae) was found to be 49.08 mg/g. These conditions were a pH of 5.2, initial Pb2+ ion concentration of 200 mg/L and a contact time of 60 minutes75. Rajasimman and Murugaiyan76 reported that the maximum removal of lead from aqueous solution on Hypnea valentiae, red macro algae, was found to be 91.97% at the optimum conditions for the sorption pH: 5.1, sorbent dosage: 5.1 g/L, temperature: 36.8 °C, contact time: 30 minutes and metal concentration: 100 mg/L. The feasibility of Spirulina maxima was studied as biosorbent for Pb2+ removal from aqueous solution. The biosorption was pH dependent and the maximum ratio of lead adsorption was about 84% was obtained at pH value of about 5.5 for 60 minutes77. The optimum conditions for lead biosorption by non-living (dried) fresh water algae, Oedogonium sp. and Nostoc sp. are almost same for the two algal biomass (pH 5.0, contact time of 90 and 70 minutes, biosorbent dose of 0.5 g/L and initial Pb2+ concentration 200 mg/L)24.
Verification of the model
According to second-order polynomial models, the maximum removal percentage of Pb2+ from aqueous solution by Gelidium amansii biomass was found under the optimum conditions: initial Pb2+ concentration of 200 mg/L, temperature 45 °C, pH 4.5, Gelidium amansii biomass of 1 g/L and contact time of 60 minutes at static condition. Under these conditions, the maximum Pb2+ removal percentage of 100% was verified and compared with the predicted value from the polynomial model (99.8%). The verification showed a high degree of accuracy of the model, demonstrating the model validation under the concentrations used.
FTIR analysis
The FTIR spectrums of Gelidium amansii biomass samples were analyzed before and after Pb2+ biosorption (Table 6 and Fig. 4) to detect any differences due to the interaction between the functional groups on the Gelidium amansii biomass and Pb2+ ions during biosorption process. The cell walls of red algae generally contain cellulose and sulfated polysaccharides (carrageenan and agar)78. The carrageenan corresponds up to 75% of the dry weight of the biomass79. The carboxylic groups are the most abundant acidic functional group and the adsorption capacity of algae is directly attributed to the presence of these binding sites. The red algae are mainly composed of carrageenan that provides different binding sites (e.g., hydroxyl, carboxyl, amino and sulfhydryl) responsible for Pb2+ ions biosorption.
FTIR spectrum for biomass sample before Pb2+ biosorption showed the characteristic absorption peaks at 3435, 2925, 2524,1807, 1624, 1471, 1417, 1082, 875 and 716 cm−1 were shifted to 3438, 2923, 2525, 1802, 1624,1419, 1036, 876, 719 and 546 cm−1; respectively after lead biosorption by the biomass. These changes in the wave numbers and their intensity were as a result of the interaction between the functional groups on the Gelidium amansii biomass and Pb2+ ions during biosorption process. The broad peak observed at 3435 cm−1 in biomass sample before lead biosorption is assigned to the stretching of O–H group due to molecular hydrogen bonding of polymeric compounds, such as alcohols, phenols and carboxylic acids. The peak at 3438 cm−1 is assigned to O–H groups80. The O–H stretching vibrations occur within a broad range of frequencies indicating the presence of free hydroxyl groups and bonded O–H peaks of carboxylic acids81,82. The peak at 2925 cm−1 is attributed to the symmetric stretching vibration of the aliphatic CH2 group83. While, the peak at 2923 cm−1 is attributed to C–H stretching vibration belonging to lipids and phospholipids fractions84. The minor peak at 2524 cm−1, corresponding to the S–H stretching vibration mode85. Moreover, the peak at 2525 cm−1, assigned to the S–H vibration86.
The FTIR spectrum showed a peak at 1807 cm−1 corresponding to the stretching vibrations of the carbonyl group (C=O)87. The absorption peak at 1802 cm−1 corresponds to C=C bond stretching vibration88. The peak at 1624 cm–1 is assigned to the C=O stretching vibration of the ketone89 or due to the stretching vibrations of C=C90. The peak at 1471 cm−1 in algal biomass before biosorption of Pb2+ was consistent with the bending vibration of the CH2 group91 is shifted by −52 cm−1 to the intense peak at 1419 cm−1 which result due to absorption from carboxyl COO–units92. Furthermore, the interaction between the algal biomass and Pb2+ during biosorption process included a large up shift of the peak at 1417 cm−1 to 1036 cm−1 by −381 cm−1. The peak at 1417 cm–1 is strongly associated with the presence of carbonate minerals (correlated to carbonyl group, C=O)93. The peak at 1036 cm−1 represents the C=O stretching region as complex peaks resulting from C=O and C‒O‒C stretching vibrations, indicating the presence of carbohydrate content in the sample94. Also, the interaction between the algal biomass and Pb2+ during biosorption process included a large up shift of the peak at 1082 cm−1 to sharp peak at 876 cm–1 by −206 cm−1. The peak at 1082 cm−1 was attributed to PO2 − asymmetric and symmetric stretching vibrations of phospholipids95. The presence of sharp peak at 876 cm−1 is due to the C=O stretching vibration96. The absorption peak at 875 cm−1 wave number in algal biomass before biosorption of Pb2+ is the characteristic absorption peak of CO3 vibrations of calcite97 is shifted by −156 cm−1 to the peak observed at 719 cm−1 which corresponds to C–H bend of alkene98. Furthermore, IR spectral data revealed a shift in peak position from716 cm−1 in algal biomass before biosorption of Pb2+ to 546 cm−1 after Pb2+ biosorption. The peak at 716 cm−1 is associated with the C‒O‒C bending vibration separately in glycosidic linkages99 while the peak at 546 cm−1 assigned to asymmetric deformation vibration of P=O in PO43−100.
In conclusion, FITR confirmed that the carboxyl, carbonyl, methylene, phosphate, carbonate, and phenolic groups were the main groups involved in the Pb2+ ions biosorption process. The carboxyl and amino functional groups provide the major biosorption sites for the lead binding. Other functional groups such as alcoholic groups also have an important role in metal uptake101.
Scanning electron microscopy (SEM)
SEM is used to verify the morphological differences between the Gelidium amansii biomass before and after adsorption of Pb2+ ions. Figure 5A shows SEM micrograph of Gelidium amansii biomass before adsorption of Pb2+ ions and Fig. 5B shows SEM micrograph of Gelidium amansii biomass after adsorption of Pb2+ ions. SEM images have clearly shown that the dry Gelidium amansii biomass samples before and after Pb2+ biosorption exhibited different surface morphologies. As shown in Fig. 5A Gelidium amansii biomass exhibited uniform interconnected structure with a continuous surface. Graph in Fig. 5B demonstrate the ability of Gelidium amansii biomass to adsorp and remove Pb2+ from aqueous solutions. After Pb2+ biosorption, the walls of biomass have become fragile, irregular surface with the appearance of bright spots due to the accumulation of Pb2+.
Electron dispersive spectroscopy (EDS)
EDS is a useful tool used for chemical characterization or the elemental analysis of biosorbents102. In the present study, EDS analysis was performed to find out type of the elements present in the sample and confirmation of the presence of Pb2+ attached to the cell surface of Gelidium amansii biomass. Figure 6B shows the additional optical absorption peak corresponding to the Pb2+ is detected in the biomass after adsorption of Pb2+ ions which confirms the involvement of Gelidium amansii biomass in the adsorption of Pb2+ ions from aqueous solution. Kim et al.103 reported that after the contact with lead, the characteristic lead peak was appeared.
Immobilization of Gelidium amansii in alginate beads and its application in Pb2+ removal
The ability to remove Pb2+ in aqueous solution by immobilized Gelidium amansii biomass in sodium alginate beads was studied (Fig. 7) and the results are presented in Fig. 8. The results indicated that the treatment of aqueous solution containing Pb2+ with immobilized Gelidium amansii biomass in sodium alginate-beads removed 100% of Pb2+ at an initial concentration of 200 mg/L for 3 h, which is significantly higher than the removal presented using sodium alginate beads without incorporation of the algal biomass as a control (97.68%) (Fig. 8). Some studies reported that immobilized biomass has the potential to provide a simple technology to remove and recover heavy metals from wastewater, and is suitable for reuse compared to free cells104,105. The size of the bead used for immobilization of biomass is an important factor106. The removal efficiency of Pb2 by immobilized Microcystis aeruginosa reached 80% for Pb2+107. Abdel Hameed108 reported that the efficiency of the immobilized beads over the free cells. The high lead removal by the immobilized beads of Chlorella vulgaris was 92%. However, lead removal was mainly caused by the alginate beads matrix with only a slight contribution by Chlorella vulgaris. Immobilization tends to increase the accumulation of metal by biomass4. Immobilized cells more effective than free cells for metal removal by biomass due to increase in the cell wall permeability109.
Material and Methods
Collection of marine alga and biomass preparation
Gelidium amansii is a red alga, was collected from Abukir beach, Alexandria governorate, Egypt. For removal of the external sand and salts, the collected biomass of Gelidium amansii was washed with tap water and then twice with distilled water. The algal biomass was dried in oven at 70 °C for 72 hours, and then grinded with a blender, sieved to get particle with the size pass through a laboratory test sieve (Endecotts/ Ltd., London, England) with mesh size of 125 µm. 20 g of the dried biomass of Gelidium amansii were thoroughly mixed with 1 L of distilled in 2 L Erlenmeyer flask and the suspension mixed, incubated at room temperature under stirring for about 30 minutes. Then, the homogeneous suspension of Gelidium amansii biomass was filtered and dried at 70 °C for 72 hours or until constant weight was obtained and kept at room temperature for further use in biosorption experiments.
Preparation of lead solution
Pb2+ solutions were prepared by dissolving lead acetate (Pb(CH3COO)2.3H2O) in 100 mL of distilled water to attain the needed concentrations (25‒368.18 mg/L). The initial pH of each solution was adjusted to the required value with 0.1 N H2SO4 and 0.1 N NaOH.
Selection of significant variables for Pb2+ removal by Plackett–Burman design
The Plackett–Burman Design (PBD)110 is an efficient screening method to detect the significant variables among large number of variables that influences a process111,112. PBD was used for the selection of the variables that had a significant effect, either positively or negatively on Pb2+ biosorption out of six variables. The six variables (independent variables) including: different contact times (60 and 180 minutes), Pb2+ ions concentration (25 and 200 mg/L), two different initial pH levels (4 and 7) which was adjusted with 0.1 N H2SO4 and 0.1 N NaOH, temperature (25 and 50 °C), biomass concentration (1 and 4 g/L) and static or agitation condition. Each variable was examined in two levels, low (−) and high (+) level. 12 runs Plackett–Burman design was used to evaluate the effect of the selected six variables on the Pb2+ removal efficiency. In the experimental design each row represents an experiment and each column represents an independent variable (Table 1).
Plackett–Burman experimental design is based on the first order model equation:
where, Y is the measured response (Pb2+ removal %), β0 is the model intercept and βi is the linear coefficient, and Xi is the level of the independent variable.
Dry biomass of Gelidium amansii was thoroughly mixed with the solution of Pb2+ in Erlenmeyer flasks. The suspensions were kept static or with agitation for specific contact time at the selected temperature.
Pb2+ quantification by ICP-AES
The solutions were filtered through disposable 0.2 µm PTFE syringe filters (DISMIC-25HP, Advantec, Tokyo, Japan). The residual Pb2+ concentrations in the solutions were determined by means of inductively coupled plasma–atomic emission spectroscopy (ICP-AES, Thermo Scientific, Germany). Certified reference materials (Merck, Germany) were included in the analyses. The recovery of metals was within the certified limits as 10 ppb to 1000 ppb. To get the final concentration, the solution was diluted with 0.1 mM H2NO3 and the final dilution factors were used113.
All experiments were carried out in triplicate and determination of Pb2+ removal is average of three trials.
Optimization of Pb2+ removal by rotatable central composite design (RCCD)
Based on the results of PBD, a three factor, five levels rotatable central composite design was performed to determine the optimum levels of the significant variables and the individual and interactions between the selected variables with high influence on Pb2+ removal. The three factors selected from PBD, for further optimization using RCCD were pH, Pb2+ concentration (mg/L), and temperature (°C) which were denoted as X1, X2 and X3; respectively. Rotatable CCD had twenty different experiments with six center points was generated with Design Expert version 7 for Windows software. The significant variables were assessed at five coded levels (−1.68, −1, 0,+1 and +1.68), as is shown in Table 3. Linear, quadratic and interaction effects of the three variables on Pb2+ removal were calculated. The relationship between the Pb2+ removal (Y) viz the significant independent variables (X1, X2 and X3) is given using the following second order polynomial equation:
In which Y is the predicted Pb2+ removal, β0 is the regression coefficients, βi is the linear coefficient, βii is the quadratic coefficients, βij is the interaction coefficients, and Xi is the coded levels of independent variables.
Three additional confirmation trials were performed to verify the accuracy of the statistical experimental design.
Statistical analysis of the data
Minitab and Design Expert version 7 for Windows softwares were “used for the experimental designs and statistical analysis. The regression analysis of the obtained experimental data was performed to calculate the analysis of variance (ANOVA). The percentage of contribution of each variable was calculated. The statistical software package, STATISTICA software (Version 8.0, StatSoft Inc., Tulsa, USA) was used to plot the three-dimensional surface plots”. The response surface and contour plots were used to assess the relationship between the significant variables.
Analytical methods
10 mL of filtrate from each trial filtered through disposable 0.2 µm PTFE syringe filters (DISMIC-25HP, Advantec, Tokyo, Japan) and analyzed using inductively coupled plasma – atomic emission spectroscopy (ICP-AES, Thermo Scientific. The efficiency of Gelidium amansii biomass for Pb2+ ions removal from aqueous solutions was calculated quantitatively by using the following equation:
where: Ci is the initial metal ion concentration (mg/L), Cf is the final (residual) metal ion concentration (mg/L). All determinations of Pb2+ ions in the solution were carried out in triplicates.
Fourier transform infrared (FTIR) spectroscopy
FTIR analysis was used to confirm the presence of functional groups in the dry Gelidium amansii biomass samples before and after Pb2+ biosorption. The Gelidium amansii biomass samples were incorporated with KBr pellets and the FTIR spectra were measured using Thermo Fisher Nicolete IS10, USA spectrophotometer within the range of 400–4000 cm−1.
Scanning electron microscopy (SEM)
SEM was used to verify the morphological differences between the dry Gelidium amansii biomass samples before and after Pb2+ biosorption to examine the algal cells surfaces and to evaluate the Pb2+ adsorption. The samples were coated with gold and were examined at different magnifications at 20 kV.
Electron dispersive X- ray spectroscopy (EDS)
EDS helps to find out the type of elements present in the samples. EDS analysis was carried out with “the scanning electron microscope (Oxford X-Max 20) with secondary electron detectors at an operating voltage of 20 kV at Electron Microscope Unit, Faculty of Science, Alexandria University, Alexandria, Egypt”.
Immobilization of Gelidium amansii in alginate beads and its application in Pb2+ removal
The biosorption capacity of Gelidium amansii biomass for lead ions biosorption from aqueous solution was determined using separating funnel packed with immobilized Gelidium amansii biomass in sodium alginate beads. Solution of 4% sodium alginate was prepared by dissolving 4 g sodium alginate (SIGMA-Aldrich) into 100 mL distilled water and mixed thoroughly with continuous stirring for 30 minutes at 60 °C for better dissolution114. After cooling, dried and washed 4 g (4%, W/V) of Gelidium amansii biomass sieved by laboratory test sieve (125 µm Endecotts/ Ltd., London, England) was added with stirring at room temperature for 5 minutes. The beads of 1.5 mm ± 0.2 mm diameter were obtained by dropping the alginate algal mixture using syringe (3 mL) into a cold sterile 2.5% CaCl2 solution in distilled water at room temperature in sterile condition under gentle stirring. The resultant spherical beads were washed several times with autoclaved distilled water to remove unreacted CaCl2 from the beads surfaces and then stored overnight at 4 °C in autoclaved distilled water in order to stabilize and harden the beads. By the same procedure, sodium alginate beads without incorporation of the Gelidium amansii biomass are also prepared and used as the control. For storage, the beads were dipped in 0.2 M of Tris-HCl buffer (pH 7.2) and stored at 4 °C until further use.
The experiment was conducted in 100 mL separating funnel (Simax glass) packed with alginate algal beads. The solution containing Pb2+ ions (200 mg/L) was added to the separating funnel. Samples (5 mL) from the separating funnel effluent were collected regularly (every 30 minutes for up to 3 hours) at a flow rate of 3 mL/minutes and analyzed by inductively coupled plasma – atomic emission spectroscopy (ICP-AES, Thermo Scientific). The biosorption capacity of the Pb2+ ions was determined by the difference in Pb2+ solution concentration before and after adsorption.
Conclusion
The potential of Gelidium amansii dry biomass for removal of lead ions from aqueous solutions has been investigated in the present study. A two-level Plackett–Burman factorial design was used to determine the most significant variables affecting Pb2+ removal %. The most significant variables affecting Pb2+ removal chosen for further optimization using rotatable central composite design. The maximum biosorption of Pb2+ was 100% at optimum operating conditions: initial Pb2+ concentration of 200 mg/L, temperature 45 °C, pH 4.5, Gelidium amansii biomass of 1 g/L and contact time of 60 minutes at static condition. Immobilized Gelidium amansii biomass was effective in Pb2+ removal (100%) from aqueous solution at an initial concentration of 200 mg/L for 3 h. Based on our results, dry biomass of the red marine alga, Gelidium amansii, could be used as a promising, efficient, cheap and biodegradable biosorbent for Pb2+ ions removal from wastewater effluents and the process used is safe, feasible and eco-friendly. Also, Plackett–Burman and rotatable central composite designs have been proved to be useful techniques for optimization of the biosorption conditions to get optimum conditions for maximum Pb2+ ions removal from aqueous solutions using Gelidium amansii dry biomass as adsorbent by significantly reducing the number of experiments, predict the best performance conditions and maintains a good accuracy of the expected response.
References
Volesky, B. Biosorption of heavy metals. (Florida: CRC Press, 2000).
Garbisu, C. & Alkorta, I. Basic concepts on heavy metal soil bioremediation. Eur J Min Proc Environ Protect 3, 58–66 (2003).
Alloway, B. J. & Ayres, D. C. Chemical principles of environmental pollution, second edition. Blackie academic and professional. An imprint of chapman and hall, Oxford, London, (1993).
Aksu, Z. Biosorption of heavy metals by micro algae in batch and continuous systems. In: Wong, Y. S., Tam, N. F. Y.(eds) Wastewater treatment with algae. Biotechnology intelligence unit. Springer, Berlin, Heidelberg 37–53 (1998).
WHO. Guidelines for drinking-water quality, third edition. World Health Organisation, Geneva, Switzerland (2004).
Kumar, M. & Puri, A. A review of permissible limits of drinking water. Indian J Occup Environ Med 16(1), 40–44 (2012).
Kar, R. N., Sahoo, B. N. & Sukla, C. B. Removal of heavy metals from pure water using sulphate-reducing bacteria (SRB). Pollut Res 11, 1–13 (1992).
Ahalya, N., Ramachandra, T. V. & Kanamadi, R. D. Biosorption of heavy metals. Res J Chem Environ 7, 71–78 (2003).
Lo, W., Chua, H., Lam, K. H. & Bi, S. P. A comparative investigation on the biosorption of lead by filamentous fungal biomass. Chemosphere 39, 2723–2736 (1999).
Volesky, B. Sorption and Biosorption. first ed., BV Sorbex, Inc., Quebec, Canada. 2003.
Volesky, B. Detoxification of metal-bearing effluents: biosorption for the next century. Hydromet 59, 203–216 (2001).
Pan, R., Cao, L. & Zhang, R. Combined effects of Cu, Cd, Pb, and Zn on the growth and uptake of consortium of Cu-resistant Penicillium sp. A1 and Cd-resistant Fusarium sp. A19. J Hazard Mater 171, 761–766 (2009).
Farooq, U., Kozinski, J. A., Khan, M. A. & Athar, M. Biosorption of heavy metal ions using wheat based biosorbents – a review of the recent literature. Bioresour Technol 101, 5043–5053 (2010).
Juwarkar, A. A., Singh, S. K. & Mudhoo, A. A comprehensive overview of elements in bioremediation. Rev Environ Sci Biotechnol 9, 215–288 (2010).
Sahan, T., Ceylan, H., Sahiner, N. & Aktas, N. Optimization of removal conditions of copper ions from aqueous solutions by Trametes versicolor. Bioresour Technol 101, 4520–4526 (2010).
Kratochvil, D. & Volesky, B. Advances in the biosorption of heavy metals. Trends Biotechnol 16, 291–300 (1998).
Volesky, B. & Holan, Z. R. Biosorption of heavy metals. Biotechnol Prog 11, 235–250 (1995).
Zulfadhly, Z., Mashitah, M. D. & Bhatia, S. Heavy metals removal in fixed-bed column by the macro fungus Pycnoporus sanguineus. Environ Pollut 112, 463–470 (2001).
Mameri, N. et al. Batch zinc biosorption by a bacterial nonliving Streptomyces rimosus biomass. Water Res 33, 1347–1354 (1999).
Bishnoi, N. R., Kumar, R., Kumar, S. & Rani, S. Biosorption of Cr(III) from aqueous solution using algal biomass Spirogyra spp. J Hazard Mater 145, 142–147 (2007).
Tuzen, M. & Sari, A. Biosorption of selenium from aqueous solution by green algae (Cladophora hutchinsiae) biomass: equilibrium, thermodynamic and kinetic studies. Chem Eng J 158, 200–206 (2010).
Schiewer, S. & Volesky, B. In environmental microbe-metal interactions (Ed: D. R. Lovely), ASM Press, Washington (D. C.) 329–362 (2000).
Deng, L., Su, Y., Su, H., Wang, X. & Zhu, X. Sorption and desorption of lead (II) from wastewater by green algae Cladophora fascicularis. J Hazard Mater 143, 220–225 (2007).
Gupta, V. K. & Rastogi, A. Biosorption of lead from aqueous solutions by green algae Spirogyra species: kinetics and equilibrium studies. J Hazard Mater 152, 407–414 (2008).
Chubar, N., Carvalho, J. R. & Correia, M. J. N. Cork biomass as biosorbent for Cu(II), Zn(II) and Ni(II). Colloids Surf A: Physicochem Eng Asp 230, 57–65 (2003).
Fard, R. F., Azimi, A. A. & Bidhendi, G. R. N. Batch kinetics and isotherms for biosorption of cadmium onto biosolids. Desalin Water Treat 28, 69–74 (2011).
Park, D., Yun, Y. S. & Park, J. M. The past, present, and future trends of biosorption. Biotechnol Bioproc E 15, 86–102 (2010).
Vijayaraghavan, K. & Yun, Y. S. Bacterial biosorbents and biosorption. Biotechnol Adv 26, 266–291 (2008).
Li, P. S. & Tao, H. C. Cell surface engineering of microorganisms towards adsorption of heavy metals. Crit Rev Microbiol 41, 140–149 (2015).
Montgomery, D. C. Design and analysis of experiments, 3rd edn. (Wiley, New York, 1991).
Agarry, S. E. & Ogunleye, O. O. Factorial designs application to study enhanced bioremediation of soil artificially contaminated with weathered bonny light crude oil through biostimulation and bioaugmentation strategy. J Environ Protect 3, 748–759 (2012).
Saraf, S. & Vaidya, V. K. Optimization of biosorption of reactive blue 222 by dead biomass of Rhizopus arrhizus NCIM997 using response surface methodology. Ind Chem 2, 118 (2016).
Tahir, A., Shehzadi, R., Mateen, B., Univerdi, S. & Karacoban, O. Biosorption of nickel (II) from effluent of electroplating industry by immobilized cells of Bacillus species. Eng Life Sci 9(6), 462–467 (2009).
Cui, L. et al. Removal of nutrients from wastewater with Canna indica L. under different vertical-flow constructed wetland conditions. Ecol Eng 36, 1083–1088 (2009).
Le Man, H., Behera, S. K. & Park, H. S. Optimization of operational parameters for ethanol production from Korean food waste leachate. Int J Environ Sci Technol 7, 157–164 (2010).
Koocheki, A., Taherian, A. R., Razavi, S. M. A. & Bostan, A. Response surface methodology for optimization of extraction yield, viscosity, hue and emulsion stability of mucilage extracted from Lepidium perfoliatum seeds. Food Hydrocoll 23, 2369–2379 (2009).
Rai, A., Mohanty, B. & Bhargava, R. Supercritical extraction of sunflower oil: a central composite design for extraction variables. Food Chem 192, 647–659 (2016).
Box, G. E. P., Hunter, W. G. & Hunter, J. S. Statistics for experimenters. (John Wiley & Sons, New York, NY, USA, 1978).
Ho, Y. S., Chiang, C. C. & Hsu, Y. C. Sorption kinetics for dye removal from aqueous solution using activated clay. Sep Sci Technol 36, 2473–2488 (2001).
Javanbakht, V., Zilouei, H. & Karimi, K. Lead biosorption by different morphologies of fungus Mucor indicus. Int Biodeterior Biodegradation 65, 294–300 (2011).
Garg, U., Kaur, M. P., Jawa, G. K., Sud, D. & Garg, V. K. Removal of cadmium (II) from aqueous solutions by adsorption on agricultural waste biomass. J Hazard Mater 154, 1149–1157 (2008).
Lia, Z. Y., Guo, S. Y. & Li, L. Study on the process, thermodynamical isotherm and mechanism of Cr(III) uptake by Spirulina platensis. J Food Eng 75, 129–136 (2006).
Romera, E., Gonzalez, F., Ballester, A., Blazquez, M. L. & Munoz, J. A. Comparative study of heavy metals using different types of algae. Bioresour Tech 98, 3344–3353 (2007).
Domozych, D. S. Algal cell walls. In: els. John Wiley & Sons Ltd., Chichester. (2011).
Cian, R. E., Drago, S. R., de Medina, F. S. & Martínez-Augustin, O. Proteins and carbohydrates from red seaweeds: evidence for beneficial effects on gut function and microbiota. Mar Drugs 13, 5358–5383 (2015).
Bayramoglu, G., Denizli, A., Bektas, S. & Arica, M. Y. Entrapment of Lentinus sajor-caju into ca-alginate gel beads for removal of Cd(II) ions from aqueous solution: preparation and biosorption kinetics analysis. Microchem J 72, 63–76 (2002).
Aksu, Z. Determination of the equilibrium, kinetic and thermodynamic parameters of the batch biosorption of nickel (II) ions onto Chlorella vulgaris. Process Biochem 38, 89–99 (2002).
Ngah, W. S. W., Teong, L. C. & Hanafiah, M. A. K. M. Adsorption of dyes and heavy metal ions by chitosan composites: a review. Carbohydr Polym 83, 1446–1456 (2011).
Tan, Y., Chen, M. & Hao, Y. High efficient removal of Pb (II) by amino-functionalized Fe3O4 magnetic nano-particles. Chem Eng J 191, 104–111 (2012).
Romera, E. et al. Biosorption equilibria with Spirogyra insignis. 15th International Biohydometallurgy Symposium. Athens Hellas Greece pp.784 (2003).
Gupta, V. K., Rastogi, A., Saini, V. K. & Jain, N. Biosorption of copper (II) from aqueous solutions by Spirogyra species. J Colloid Interface Sci 296, 59–63 (2006).
Kumar, Y. P., King, P. & Prasad, V. S. R. K. Removal of copper from aqueous solution using Ulva fasciata sp. a marine green alga. J Hazard Mater 137, 367–373 (2006).
Esmaeili, A. & Beni, A. A. Biosorption of nickel and cobalt from plant effluent by Sargassum glaucescens nanoparticles at new membrane reactor. Int J Environ Sci Technol 12, 2055–2064 (2015).
Kumar, M. et al. Removal of chromium from water effluent by adsorption onto Vetiveria zizanioides and Anabaena species. Nat Sci 5, 341–348 (2013).
Apiratikul, R., Marhaba, T. F., Wattanachira, S. & Pavasant, P. Biosorption of binary mixtures of heavy metals by green macro algae, Caulerpa lentillifera. Songklanakarin J Sci Technol 26, 199–207 (2004).
Luo, F., Liu, Y., Li, X., Xuan, Z. & Ma, J. Biosorption of lead ion by chemically-modified biomass of marine brown algae Laminaria japonica. Chemosphere 64, 1122–1127 (2006).
Patel, R. & Chandel, M. Effect of pH and temperature on the biosorption of heavy metals by Bacillus licheniformis. Int. J Sci Res 4, 2272–2275 (2015).
Córdova, F. J. C. et al. Response surface methodology for lead biosorption on Aspergillus terreus. Int J Environ Sci Tech 8(4), 695–704 (2011).
Rathinam, A., Maharshi, B., Janardhanan, S. K., Jonnalagadda, R. R. & Nair, B. U. Biosorption of cadmium metal ion from simulated wastewaters using Hypnea valentiae biomass: a kinetic and thermodynamic study. Bioresour Technol 101, 1466–1470 (2010).
Ho, Y. S., Chiu, W. T., Hsu, C. S. & Huang, C. T. Sorption of lead ions from aqueous solution using tree fern as a sorbent. Hydrometallurgy 73, 55–61 (2004).
Dal Bosco, S. M., Sarti Jimenez, R. & Alves Carvalho, W. Removal of toxic metals from wastewater by brazilian natural scolecite. J Colloid Interface Sci 281, 424–431 (2005).
Cruz, C. C. V., Costa, A. C. A., Henriques, C. A. & Luna, A. S. Kinetic modeling and equilibrium studies during cadmium biosorption by dead Sargassum sp. biomass. Bioresour Technol 91, 249–257 (2004).
Aksu, Z. Equilibrium and kinetic modelling of cadmium (II) biosorption by C. vulgaris in a batch system: effect of temperature. Sep Purif Technol 21, 285–294 (2001).
Brouers, F. & Al-Musawi, T. J. On the optimal use of isotherm models for the characterization of biosorption of lead onto algae. J Mol Liq 212, 46–51 (2015).
Horsfall, M. & Spiff, A. Effects of temperature on the sorption of Pb2+ and Cd2+ from aqueous solution by Caladium bicolor (Wild Cocoyam) biomass. Electron J Biotechnol 8 (2005).
Bulut, Y., Gul, A., Baysal, Z. & Alkan, H. Asorption of Ni(II) from aqueous solution by Bacillus subtilis. Desalination Water Treat 49, 74–80 (2012).
Khezami, L. & Capart, R. Removal of chromium (VI) from aqueous solution by activated carbons: kinetic and equilibrium studies. J Hazard Mater 123, 223–231 (2005).
Al-Ashed, S. & Duvnjak, Z. Adsorption of copper and chromium by Aspergillus carbonarius. Biotechnol Prog 11, 638–642 (1995).
Saleem, M., Pirzada, T. & Qadeer, R. Sorption of acid violet 17 and direct red 80 dyes on cotton fiber from aqueous solutions. Colloids Surf A: Physicochem Eng Asp 292, 246–250 (2007).
Lodeiro, P., Barriada, J. L., Herrero, R. & Sastre de Vicente, M. E. The marine macroalga Cystoseira baccata as biosorbent for cadmium(II) and lead(II) removal: kinetic and equilibrium studies. Environ Pollu 142, 264–273 (2006).
Davis, A., Volesky, B. & Mucci, A. A review of the biochemistry of heavy metals biosorption by brown algae. J Water Res 37, 4311–4330 (2003).
Meena, A. K., Mishra, G. K., Rai, P. K., Rajagopal, C. & Nagar, P. N. Removal of heavy metals ions from aqueous solution using carbon aerogel as an adsorbent. J Hazard Mat 122, 161–170 (2005).
Ye, J. et al. Bioremediation of heavy metal contaminated aqueous solution by using red algae Porphyra leucosticta. Water Sci Technol 72, 1662–1666 (2015).
Tabaraki, R., Nateghi, A. & Ahmady-Asbchin, S. Biosorption of lead (II) ions on Sargassum ilicifolium: application of response surface methodology. Int Biodeterior Biodegradation 93, 145–152 (2014).
Salehi, P., Tajabadi, F. M., Younesi, H. & Dashti, Y. Optimization of lead and nickel biosorption by Cystoseira trinodis (brown algae) using response surface methodology. Clean (Weinh) 42, 243–250 (2014).
Rajasimman, M. & Murugaiyan, K. Application of the statistical design for the sorption of lead by Hypnea valentiae. J A C E 2 pp.7 (2012).
Gong, R., Ding, Y., Liu, H., Chen, Q. & Liu, Z. Lead biosorption and desorption by intact and pretreated Spirulina maxima biomass. Chemosphere 58, 125–130 (2005).
Wang, J. & Chen., C. Biosorbents for heavy metals removal and their future. Biotechnol Adv 27, 195–226 (2009).
Yuan, Y. Important chemical products from macroalgae (Ascophyllum nodosum) biorefinery by assistance of microwave technology. Doctor of philosophy. Department of Chemistry, University of york, United Kingdom, (2015).
Si, Y. & Samulski, E. T. Synthesis of water soluble graphene. Nano Lett 8, 1679–1682 (2008).
Iqbala, M., Saeeda, A. & Zafarb, S. I. FTIR spectrophotometry, kinetics and adsorption isotherms modeling, ion exchange, and EDX analysis for understanding the mechanism of Cd2+ and Pb2+ removal by mango peel waste. J Hazard Mater 164, 161–171 (2009).
Gnanasambandam, R. & Protor, A. Determination of pectin degree of esterification by diffuse reflectance fourier transform infrared spectroscopy. Food Chem 68, 327–332 (2000).
Vlachos, N. et al. Applications of fourier transform-infrared spectroscopy to edible oils. Anal Chim Acta 573–574, 459–465 (2006).
Li, F. T., Yang, H., Zhao, Y. & Xu, R. Novel modification pectin for heavy metal adsorption. Chin Chem Lett 18, 325–328 (2007).
Cao, H. Synthesis and applications of inorganic nanostructures. Publisher, John Wiley and Sons Ltd. ISBN-10, 3527340270. ISBN-13, 9783527340279. United Kingdom. Wiley-VCH Verlag GmbH. (2017).
Akremi, A., Noubigh, A. & Abualreish, M. J. A. Novel organotin (IV) complexes derived from chiral benzimidazoles: synthesis, molecular structure and spectral properties. Orient J Chem 34 (2018).
Axson, J. L. Hydrating aldehydes in the gas phase: atmospheric consequences. Thesis, University of Colorado, Boulder, Colorado, USA(2012).
Wang, L., Ma, Y., Qu, Y., Gao, Y. & Yin, G. In situ transmission FTIR spectroscopy investigation of the electrolyte oxidation reaction under high-voltage. Lithium battery - electrolyte studies. ECS (2016).
Gu, C. & Karthikeyan, K. G. Sorption of the antimicrobial ciprofloxacin to aluminum and iron hydrous oxides. Environ Sci Technol 39, 9166–9173 (2005).
Sun, W., Shi, S. & Yao, T. Graphene oxide–ru complex for label-free assay of DNA sequence and potassium ions via fluorescence resonance energy transfer. Anal Methods 3, 2472–2474 (2011).
Amiri, A. et al. Mass production of highly-porous graphene for high-performance supercapacitors. Sci Rep 6 (2016).
Barth, A. & Zscherp, C. What vibrations tell us about proteins. Q Rev Biophys 35, 369–430 (2002).
Liu, W., Yan, X., Chen, J., Feng, Y. & Xue, Q. Novel and high-performance asymmetric microsupercapacitors based on graphene quantum dots and polyaniline nanofibers. Nanoscale 5, 6053–6062 (2013).
Mudgil, D., Barak, S. & Khatkar, B. S. X-ray diffraction, IR spectroscopy and thermal characterization of partially hydrolyzed guar gum. Int J Biol Macromol 50, 1035–1039 (2012).
Vodnar, D. C., Pop, O. L. & Socaciu, C. Monitoring lactic acid fermentation in media containing dandelion (Taraxacum officinale) by FTIR spectroscopy. Not Bot Horti Agrobo 40, 65–68 (2012).
Kumara, R. S. & Rajkumarb, P. Characterization of minerals in air dust particles in the state of tamilnadu, india through FTIR spectroscopy. Atmos Chem Phys Discuss 13, 22221–22248 (2013).
Springfield, T. Application of FTIR for quantification of alkali in cement. Thesis, University of North Texas, (2011).
Pilling, S. et al. Formation of unsaturated hydrocarbons in interstellar ice analogs by cosmic ray. Mon Notices Royal Astron Soc 423, 2209–2221 (2012).
Fernando, I. P. S. et al. FTIR characterization and antioxidant activity of water soluble crude polysaccharides of sri lankan marine algae. Algae 32, 75–86 (2017).
Yang, S. S. & Chen, Z. B. The study on aging and degradation mechanism of ammonium polyphosphate in artificial accelerated aging. Procedia Eng 211, 906–910 (2018).
Nessim, R. B., Bassiouny, A. R., Zaki, H. R., Moawad, M. N. & Kandeel, K. M. Biosorption of lead and cadmium using marine algae. Chem Ecol 27, 579–594 (2011).
Dmytryk, A., Saeid, A. & Chojnacka, K. Biosorption of microelements by Spirulina: towards technology of mineral feed supplements. Sci World J Article ID 356328 (2014).
Kim, Y. H., Yoo, Y. J. & Lee, H. Y. Characteristics of lead adsorption by Undaria pinnatifida. Biotechnol Lett 17, 345–350 (1995).
Barquilha, C. E. R., Cossich, E. S., Tavares, C. R. G. & Silva, E. A. Biosorption of nickel (II) and copper (II) ions in batch and fixed-bed columns by free and immobilized marine algae Sargassum sp. J Clean Prod 150, 58–64 (2017).
Rangsayatorn, N., Pokethitiyook, P., Upatham, E. S. & Lanza, G. R. Cadmium biosorption by cells of Spirulina platensis TISTR 8217 immobilized in alginate and silica gel. Environ Int 30, 57–63 (2004).
Mehta, S. K. & Gaur, J. P. Use of algae for removing heavy metal ions from wastewater: progress and prospects. Crit Rev Biotechnol 25, 113–152 (2005).
Chen, J. Z., Tao, X. C., Xu, J., Zhang, T. & Liu, Z. L. Biosorption of lead, cadmium and mercury by immobilized Microcystis aeruginosa in a column. Process Biochem 40, 3675–3679 (2005).
Abdel Hameed, M. S. Continuous removal and recovery of lead by alginate beads, free and alginate-immobilized Chlorella vulgaris. Afr J Biotechnol 5, 1819–1823 (2006).
Brouers, M., Dejong, H., Shi. D. J. & Hall, D. O. Immobilized cells: an appraisal of the methods and applications of cell immobilization techniques. In: Cresswell, RC, Rees, TAV and Shah, N, eds. Algae and cyanobacterial biotechnology. Scientific & technical publishers, New York p 272–290 (1989).
Plackett, R. L. & Burman, J. P. The design of optimum multifactorial experiments. Biometrika 33, 305–325 (1946).
El-Naggar, N. E. Extracellular production of the oncolytic enzyme, L-asparaginase by newly isolated Streptomyces sp. strain NEAE-95 as potential microbial cell factories: Optimization of culture conditions using response surface methodology. Curr Pharm Biotechnol 16, 162–178 (2015).
El-Naggar, N. E., El-Bindary, A. A. & Salah, N. Statistical optimization of process variables for antimicrobial metabolites production by Streptomyces anulatus NEAE-94 against some multidrug-resistant strains. Int J Pharma 9, 322–334 (2013).
American public health association (APHA), standard methods for the examination of water and wastewater 22nded. APHA, Inc. Washington, D.C (2005).
Kumar, S. S. & Saramma, A. V. Nitrate and phosphate uptake by immobilized cells of Gloeocapsa gelatinosa. J Mar Biol Ass India 54, 119–122 (2012).
Acknowledgements
The authors gratefully acknowledge the Science and Technology Development Fund (STDF), Egypt, Grant No. #CB-2741 for their support of this paper for Pb2+ ion analysis using inductively coupled plasma–atomic emission spectroscopy (ICP-AES, Thermo Scientific).
Author information
Authors and Affiliations
Contributions
N.E.E. designed the experiments, experimental instructions, performed the statistical analysis, analyzed and interpreted the data and contributed substantially to the writing and revising of the manuscript. R.A.H. proposed the research concept, providing necessary tools for experiments, experimental instructions, contributed to the manuscript reviewing and had given final approval of the version to be published. IEM perform Pb2+ ion analysis using inductively coupled plasma – atomic emission spectroscopy (ICP-AES, Thermo Scientific). M.S.A. providing some necessary tools for experiments and had given final approval of the version to be published. N.H.R. carried out the experiments, contributed substantially to the writing of the manuscript. All authors read and approved the final manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
El-Naggar, N.EA., Hamouda, R.A., Mousa, I.E. et al. Biosorption optimization, characterization, immobilization and application of Gelidium amansii biomass for complete Pb2+ removal from aqueous solutions. Sci Rep 8, 13456 (2018). https://doi.org/10.1038/s41598-018-31660-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-31660-7
- Springer Nature Limited
This article is cited by
-
Sorption of chromium from aqueous solutions using Fucus vesiculosus algae biosorbent
BMC Chemistry (2024)
-
A review of the application of fungi as an effective and attractive bio-adsorbent for biosorption of heavy metals from wastewater
Environmental Monitoring and Assessment (2023)
-
Removal of lead from aqueous solutions using three biosorbents of aquatic origin with the emphasis on the affective factors
Scientific Reports (2022)
-
Biosorption removal of iron from water by Aspergillus niger
npj Clean Water (2022)
-
An investigation on lead removal with newly isolated Backusella circina
Archives of Microbiology (2022)