Abstract
In this work, the oxidation of an azo dye (Acid Yellow 99) by H2O2 in aqueous solution with the Dawson-type heteropolyanion [H1.5Fe1.5P2W12Mo6O61, 22H2O] acting as a catalyst was studied. The effects of different parameters—the initial pH, the initial H2O2 concentration, the mass of the catalyst, and the initial dye concentration—on the oxidation of the dye were investigated. The optimal conditions that led to maximum decolorization were found to be: pH 3, catalyst mass = 0.05 g, and [H2O2]0 = 0.03 mM for an initial dye concentration of 30 mg L−1.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
The textile industry’s production of dyestuffs creates large volumes of waste water. The World Bank estimates that 17–20% of all industrial water pollution emanates from textile dyeing and treatment processes (Kant 2012). There are serious concerns about the discharge of dye-contaminated waste waters into the environment from both aesthetic and environmental perspectives; the color of the dye is often visible in the waste water, even at concentrations as low as 1 mg L−1 (Fernández et al. 2004).
Acid Yellow 99 (AY99) is an anionic dye used in the paint, printing, and textile industries. It is appreciated for its color fastness and weather stability, and is used to dye nylon, wool, and silk (Elwakeel et al. 2016). However, AY99 can cause hard skin and eye irritation (Elwakeel et al. 2016). In addition, the inhalation of Acid Yellow 99 may irritate the respiratory tract, and its ingestion causes irritation to the gastrointestinal tract (Elwakeel et al. 2016).
Various physical and chemical treatment processes have been used for dyes in waste water. Among the methods applied to AY99 is decolorization, such as adsorption with coir pith. It was found that 1 g of coir pith can adsorb 442.13 mg of AY99. This adsorption process is found to be pH dependent; the optimum pH value for the process is 2.0, and it follows the Langmuir–Freundlich dual isotherm model (Khan et al. 2011).
The adsorption of AY99 onto dodecylethyldimethylammonium (DEDMA)-sepiolite was investigated in aqueous solution (Ozcan and Ozcan 2008). The photocatalytic decolorization of Acid Yellow 99 solutions under the action of solar radiation using ZnO as a photocatalyst has also been studied (Pitchaimuthu et al. 2014). 98.0% decolorization of an AY99 dye solution was achieved within 180 min using this method. The extraction of AY99 by a liquid surfactant membrane was also studied (Bahloul et al. 2014). The membrane consisted of the surfactant SPAN 80 (sorbitan monooleate) and the extractant Aliquat 366. Cyclohexane was used as the thinner, and sulfuric acid as the internal phase. Extraction yields of 99.09–99.12% were obtained experimentally.
Recently, the development of inexpensive water remediation technologies has attracted considerable interest (Kant 2012). One such method may be the oxidation of organic textile dyes by hydrogen peroxide using polyoxometalates (POMs) as catalysts. H2O2 is an environmentally benign oxidant that is cheap, readily available, and produces a nontoxic substance—water—during oxidation (Qiu and Liu 2005). Polyoxometalates (POMs) are a diverse class of anionic metal oxide clusters that contain early transition metals in their highest oxidation states (Pope 1983). These compounds, which are minerals, are generally easy to synthesize from relatively environmentally friendly simple reagents. Many POMs are known to be effective catalysts of the oxidation of a wide range of organic compounds. They are also potentially applicable in the photodegradation, degradation, and mineralization of organic pollutants in waste water (Hu and Burns 2002; Troupis et al. 2009; Lee and Sedlak 2009; Bechiri et al. 2013). Dawson-type heteropolyanions (Fig. 1) are a family of interesting and selective recyclable POM catalysts (Gustavo et al. 2008).
Given the discussion above, we decided to study the catalytic oxidation of Acid Yellow 99 in contaminated water by H2O2 using the recyclable Dawson-type iron-substituted heteropolyanion H1.5Fe1.5P2W12Mo6O61, 22H2O (P2W12Mo6 Fe3+) as catalyst. We examined how parameters such as the initial pH, the initial H2O2 concentration, the mass of the catalyst, and the initial dye concentration affect the oxidation of AY99, and the results are reported in the present paper.
Experimental section
Reagents
The catalyst HFe1.5P2W12Mo6O61, 22H2O was prepared starting from H6P2W12Mo6O62.24H2O according to the protocol described in Bechiri et al. (2014).
The heteropolyanion precursor H6P2W12Mo6O62 24H2O was synthesized according to the procedure outlined in Ciabrini et al. (1983). The purity of the synthesized heteropolyanions was confirmed by 31P NMR spectroscopy (Bechiri et al. 2014).
The anionic dye Acid Yellow 99 was supplied by Sigma–Aldrich (St. Louis, MO, USA). The chemical structure and other characteristics of this dye are shown in Table 1.
H2O2 35% (w/w) was obtained from Merck (Darmstadt, Germany).
NaOH, H2SO4, and ammonium heptamolybdate (NH4)6Mo7·4H2O were procured from Sigma–Aldrich. Potassium iodide (KI) was supplied by Riedel-de Haën (Seelze, Germany).
Procedure and analysis
The experiments were performed in a 500-mL batch reactor. Various solutions of AY99 were prepared at different concentrations, which were then homogenized by stirring until the dye was completely dissolved. The pH was adjusted using 0.1 N H2SO4 or NaOH. In all of the experiments, 100 mL of a 30 mg L−1 dye solution containing the appropriate quantities of catalyst and H2O2 were magnetically stirred at room temperature. The decrease in the concentration of AY99 was monitored by a model 6705 Jenway UV visible spectrophotometer (Cole-Parmer, London, UK); the wavelength of maximum absorbance λ max was 450 nm (Pitchaimuthu et al. 2014).
Wavelength and bandwidth resolutions were 1 and 0.5 nm. The cell used during the experiments was made of 1-cm-thick quartz.
The concentration of H2O2 was determined spectrophotometrically using potassium iodide and ammonuim heptamolybdate salt as the catalyst (Kormann et al. 1988).
The oxidation of AY99 by H2O2 using H1.5Fe1.5P2W12Mo6O61, 22H2O as catalyst was studied by monitoring the effects of varying the initial pH of the solution, the H2O2 concentration, the mass of the catalyst, and the dye concentration on the oxidation reaction. The oxidation efficiency (i.e., the discolorization efficiency) was determined via the equation (Sasmaz et al. 2011)
where DE is the discolorization efficiency, C i is the initial dye concentration, and C f is the final dye concentration.
Results and discussion
Effect of the solution pH
The effect of pH on the discolorization efficiency was investigated by varying the pH from 3 to 8. At a strongly acidic pH (<3), there is a risk that the catalyst will dimerize, while the catalyst is likely to deteriorate when the pH is above 8 (Bechiri et al. 2012).
The results presented in Fig. 2 show that the optimum pH value for the oxidation of AY99 by H2O2 using the iron-substituted Wells–Dawson-type heteropolyanion HFe2.5P2W12Mo6O62.22H2O as catalyst is 3. This result agrees with those reported in Bechiri et al. (2014), in which the oxidation of an azo dye (methyl violet) by H2O2 in aqueous solution using a Dawson-type heteropolyanion (HFe2.5P2W12Mo6O62.22H2O) as catalyst was studied; in that work, the optimum pH was found to be about 3.
This result can be explained by the enhanced stability of the catalyst at this pH (Bechiri et al. 2013). It has also been shown that the catalytic efficiency of the Fe3+/H2O2 system during the oxidation of organic dyes is highest at pH 3 (Strukul 1992). H2O2 molecules are unstable in alkaline solution, so dye degradation decreases in alkaline solution (Gould et al. 2005).
Possible reaction mechanism
Figure 3 shows the evolution of the H2O2 concentration during the oxidation catalyzed by (HFe2.5P2W12Mo6O62.22H2O)/H2O2. The H2O2 concentration decreases during the oxidation process, suggesting that HFe2.5P2W12Mo6O62.22H2O catalyzes the decomposition of H2O2. The action of H2O2 on the Fe2+ complex leads to the generation of hydroxyl radicals (OH·). These hydroxyl radicals degrade the dye (Bechiri et al. 2013).
Therefore, we can propose the following mechanism:
Effect of the catalyst concentration
The mass of the catalyst is a critical parameter in catalytic oxidation processes (Bechiri et al. 2012). Thus, the effect of varying the catalyst mass on the AY99 decolorization efficiency was investigated in this work by varying the concentration of P2W12Mo6Fe3+ from 0 to 0.45 mM. The results are shown in Fig. 4. The concentration of hydrogen peroxide was fixed at 0.006 mM and the AY99 concentration was 30 mg/L.
It is clear from the results that the AY99 decolorization efficiency increases as the catalyst mass is increased up to a certain level. This is due to the fact that P2W12Mo6Fe3+ plays a very important role in the decomposition of H2O2 into hydroxyl radicals. The low degradation capacity at low P2W12Mo6 Fe3+ concentrations is probably due to the relative scarcity of OH· radicals. As the concentration of the catalyst increases, the number of radicals increases, increasing the decolorization efficiency; however, when the catalyst concentration exceeds a certain value, the decolorization efficiency begins to decrease. This decrease in AY99 decolorization efficiency at large catalyst concentrations can be explained by the occurrence of reaction (4) below, which becomes competitive with the AY99 oxidation reaction at high P2W12Mo6Fe3+ concentrations:
Consequently, a P2W12Mo6Fe3+ concentration of 0.23 mM was chosen for AY99 oxidation.
Effect of the initial H2O2 concentration
The initial H2O2 concentration is an important influence on the degradation of AY99 and thus the decolorization efficiency. The effect of this parameter was studied by varying the initial H2O2 concentration from 0.006 to 0.1 mM under the following optimal conditions: pH 3, [NBB] = 30 mg L−1, [catalyst] = 0.23 mM.
Based on the results shown in Fig. 5, the optimal initial H2O2 concentration for the degradation of 30 mg/L AY99 is about 0.03 mM.
The activation of hydrogen peroxide by homogeneous catalysts has been attributed to the formation of highly active hydroxyl radicals (Anipsitakis and Dionysiou 2004). A highly concentrated H2O2 solution (0.03–0.1 mM) presents self-quenching of OH· radicals and the formation of hydroperoxyl radicals (HO2·). Although HO2· is an effective oxidant, it is a less effective oxidant than OH·, so the AY99 decolorization efficiency drops when the concentration of H2O2 exceeds a threshold value (Liu et al. 2005).
Effect of the AY99 concentration
From Fig. 6, it is clear that the discolorization efficiency decreases with increasing initial concentration of the dye. This result is in good agreement with results reported in the literature, and can be explained by the fact that increasing the initial dye concentration increases the ratio of AY99 molecules to hydroxyl radicals (as the concentrations of H2O2 and the catalyst are fixed), thereby decreasing the discolorization efficiency (Ramirez et al. 2007; Li et al. 2006; Ji et al. 2011).
Monitoring the catalyzed oxidative degradation of AY99 over time using visible spectroscopy
Under the optimal experimental conditions determined above (pH 3; [H2O2] = 0.03 mM; C 0 = 30 mg L−1; [H1.5Fe1.5P2W12Mo6O61, 22H2O] = 0.23 mM; T = 25 °C), we used visible spectroscopy to follow the catalyzed oxidative degradation of AY99 over time. The results are depicted in Fig. 7. The figure shows that the catalytic oxidation process is fast: the color of the dye disappears quickly. The azo dye absorbance peak at λ = 450 nm that was used to monitor the discolorization decreases in intensity over time and disappears completely 60 min after the start of the reaction.
The decrease in this peak is caused by the cleavage of –N=N– bonds due to attack by hydroxyl radicals (Pitchaimuthu et al. 2014).
Conclusion
Textile dyes are a large group of organic compounds that can have undesirable effects when released into the environment. In this work, the oxidation of the azo dye AY99 by H2O2 in aqueous solution and in the presence of the iron-substituted Dawson-type heteropolyanion catalyst HFe2.5P2W12Mo6O62.22H2O was studied. The optimal parameter values for this oxidation were found to be: initial pH 3; [H2O2]0 = 0.03 mM; [catalyst] = 0.23 mM. Note that it is easy to separate and recover (i.e., recycle) this catalyst so that it can be used again. To do this, the catalyst is precipitated as its potassium salt by adding KCl to the solution following complete discolorization. The catalyst can also be separated out by extraction using a liquid surfactant membrane (Bechiri et al. 2008).
References
Anipsitakis GP, Dionysiou DD (2004) Radical generation by the interaction of transition metals with common oxidants. Environ Sci Technol 38:3705–3712
Bahloul L, Ismail F, Samar ME, Meradi H (2014) Removal of AY99 from an aqueous solution using an emulsified liquid membrane. Application of Plackett–Burman design. Energy Proced 50:1008–1016
Bechiri O, Ismail F, Abbessi M, Samar MH (2008) Stability of the emulsion (W/O): application to the extraction of a Dawson type heteropolyanion complex in aqueous solution. J Hazard Mate 152:895–902
Bechiri O, Abbessi M, Ouahab L (2012) The oxidation study of methyl orange dye by hydrogen peroxide using Dawson-type heteropolyanions as catalysts. Res Chem Intermed 39:2945–2954
Bechiri O, Abbessi M, Samar ME (2013) Decolorization of organic dye (NBB) using Fe(III)P2W12Mo5/H2O2 system. Desalination Water Treat 51:31–33
Bechiri O, Abbessi M, Belghiche R, Ouahab L (2014) Wells–Dawson polyoxometelates [HP2W18−nMonO62]Fe2.5, xH2O; n = 0, 6: synthesis, spectroscopic characterization and catalytic application for dyes oxidation. C R Chim 17:135–140
Carraro M, Gross S (2014) Hybrid materials based on the embedding of organically modified transition metal oxoclusters or polyoxometalates into polymers for functional applications: a review. Materials 7:3956–3989
Ciabrini JP, Contant R, Fruchart M (1983) Heteropolyblues: relationship between metal-oxygen-metal bridges and reduction behaviour of octadeca(molybdotungsto)diphosphate anions. Polyhedron 2:1229–1233
Elwakeel KZ, El-Bindary A, El-Sonbati AZ, HawasA R (2016) Adsorption of toxic acidic dye from aqueous solution onto diethylenetriamine functionalized magnetic glycidyl methacrylate-N,N′-methylenebisacrylamide. RSC Adv 6:3350–3361
Fernández J, Kiwi J, Baeza J, Freer J, Lizama C, Mansilla HD (2004) Orange II photocatalysis on immobilised TiO2: effect of the pH and H2O2. Appl Catal B 48:205–211
Gould DM, Spiro M, Griffith WP (2005) Mechanism of bleaching by peroxides: part 7. The pH dependence of the oxometalate catalysed bleaching of methyl orange. J Mol Cat A Chem 242:176–181
Gustavo R, Bennardi DO, Autino J, Baronetti G, Thomas H (2008) A simple and mild acylation of alcohols, phenols, amines, and thiols with a reusable heteropoly acid catalyst (H6P2W18O62.24H2O). Eur J Chem 5:641–647
Hu J, Burns RC (2002) Homogeneous-phase catalytic H2O2 oxidation of isobutyraldehyde using Keggin, Dawson and transition metal-substituted lacunary heteropolyanions. J Mol Cat A Chem 184:451–464
Ji F, Li C, Zhang J, Deng L (2011) Efficient decolorization of dye pollutants with LiFe (WO4)2 as a reusable heterogeneous Fenton-like catalyst. Desalination 269:284–290
Kant R (2012) Textile dyeing industry an environmental hazard. Nat Sci 1:22–26
Khan MM, Ray M, Guha AK (2011) Mechanistic studies on the binding of Acid Yellow 99 on coir pith. Bioresour Technol 102:2394–2399
Kormann C, Bahnemann DW, Hoffmann MR (1988) Photocatalytic production of H2O2 and organic peroxides in aqueous suspensions of TiO2, ZnO, and desert sand. Environ Sci Technol 22:798–806
Lee DL, Sedlak C (2009) A novel homogeneous Fenton-like system with Fe(III)–phosphotungstate for oxidation of organic compounds at neutral pH values. J Mol Catal A Chem 311:1–6
Li G, Qu J, Zhang X, Liu H, Liu H (2006) Electrochemically assisted photocatalytic degradation of Orange II: influence of initial pH values. J Mol Catal A Chem 259:238–244
Liu RM, Chen SH, Hung MY, Hsu CS, Lai JY (2005) Fe III supported on resin as effective catalyst for the heterogeneous oxidation of phenol in aqueous solution. Chemosphere 59:117–125
Ozcan S, Ozcan A (2008) Adsorption of Acid Yellow 99 onto DEDMA-sepiolite from aqueous solutions. Int J Environ Pollut 34:308–324
Pitchaimuthu S, Subramanian R, Nagarathinam K, Ponnusamy V (2014) Enhanced photocatalytic activity of titanium dioxide by β-cyclodextrin in decoloration of Acid Yellow 99 dye. Desalin Water Treat 52:3392–3402
Pope MT (1983) Heteropoly and isopoly oxometalates. Springer, New York
QiuZ HeY, LiuX YuS (2005) Catalytic oxidation of the dye wastewater with hydrogen peroxide. Chem Eng Process 44:1013–1017
Ramirez HJ, Costa CA, Madeira M, Mata G, Vicente MA, Rojas-Cervantes ML, Lopez-Peinado AJ, Martin-Aranda RM (2007) Fenton-like oxidation of Orange II solutions using heterogeneous catalysts based on saponite clay. Appl Catal B 71:44–56
Şaşmaz JS, Gedikli S, Aytar P, Güngörmedi G, Evrim AÇ, Ünal HA, Kolankaya N (2011) Decolorization potential of some reactive dyes with crude laccase and laccase-mediated system. Appl Biochem Biotechnol 163:346–361
Strukul G (1992) Catalytic oxidations with hydrogen peroxide as oxidant. Kluwer Academic, Dordrecht, The Netherlands
Troupis A, Triantis TM, Gkika E, Hiskia A, Papaconstantinou E (2009) Photocatalytic: reductive–oxidative degradation of Acid Orange 7 by polyoxometalates. Appl Catal B Environ 86:98–107
Acknowledgements
This work was supported by the Engineering Environmental Laboratory of Badji Mokhtar University (Annaba, Algeria), and is dedicated to the late Professor Mostefa Abbessi, God rest his soul.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
All authors declare that they have no conflict of interest.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Tabaï, A., Bechiri, O. & Abbessi, M. Study of the degradation of a toxic dye by the catalytic system (H1.5Fe1.5P2W12Mo6O61, 22H2O)/H2O2 . Euro-Mediterr J Environ Integr 2, 8 (2017). https://doi.org/10.1007/s41207-017-0017-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s41207-017-0017-x