Abstract
A modified tempering treatment has been designed in order to avoid the direct transformation of retained austenite (Ar) during tempering of a low-alloy Cr–Mo–V steel. Instead of the direct transformation of Ar into ferrite and M23C6 carbides during conventional tempering at 700 °C, transformation into aggregate of ferrite and cementite has been forced by a pre-tempering at 455 °C before conventional tempering. Experiments have been performed on specimens quenched with cooling rates 1.5, 3 and 12 °C/s, providing different types of Ar within the as-quenched microstructures. The results show that the tempering modification does not improve the Charpy impact toughness at the highest quenching rate of 12 °C/s, where the specimens cannot incur cleavage cracking induced from fine and discontinuous M23C6 carbides along lath interfaces. For the lowest quenching rate 1.5 °C/s, the Charpy impact toughness can be improved, and the failure is dominated by carbide aggregates, which originate from the decomposed products of blocky Ar. This is because the tempering modification effectively suppresses the formation of coarse M23C6 carbides at interfaces between the carbide aggregate and bainitic matrix, thereby resulting in a relatively homogeneous distribution of M23C6 carbides inside carbide aggregates. Therefore, the tempering modification is recommended for large-scale forgings, in which relatively high quenching rates are difficult to achieve.
Similar content being viewed by others
References
Z. Jiang, P. Wang, D. Li, Y. Li, Mater. Sci. Eng. A 742, 540 (2019)
Z. Jiang, P. Wang, D. Li, Y. Li, Effects of rare earth on microstructure and impact toughness of low alloy Cr–Mo–V steels for hydrogenation reactor vessels. J. Mater. Sci. Technol. (2019). https://doi.org/10.1016/j.jmst.2019.03.012
C. Lerchbacher, S. Zinner, H. Leitner, Metall. Trans. A 43, 4989 (2012)
G. Yan, L. Han, C. Li, X. Luo, J. Gu, J. Nucl. Mater. 483, 167 (2017)
C. Lerchbacher, S. Zinner, H. Leitner, Mater. Sci. Eng. A 564, 163 (2013)
D.E. Kaputkin, L.M. Kaputkina, S.D. Prokoshkin, J. Phys. IV France 112, 275 (2003)
F.G. Caballero, M.K. Miller, C. Garcia-Mateo, C. Capdevila, S.S. Babu, Acta Mater. 56, 188 (2008)
S.Y. Han, S.Y. Shin, S. Lee, N.J. Kim, J.H. Kwak, K.G. Chin, Metall. Mater. Trans. A 42, 138 (2011)
S.S. Sohn, B.J. Lee, J.H. Kwak, S. Lee, Metall. Mater. Trans. A 45, 3844 (2014)
S.S. Sohn, B.J. Lee, S. Lee, J.H. Kwak, Acta Mater. 61, 5626 (2013)
G. Yan, L. Han, C. Li, X. Luo, J. Gu, Metall. Mater. Trans. A 48, 3470 (2017)
P. Bala, J. Pacyna, Arch. Mater. Sci. Eng. 28, 581 (2007)
H.S. Park, J.B. Seol, N.S. Lim, S.I. Kim, C.G. Park, Mater. Des. 82, 173 (2015)
G. Speich, W. Leslie, Metall. Trans. 3, 1043 (1972)
S. Dépinoy, C. Toffolon-Masclet, S. Urvoy, J. Roubaud, B. Marini, F. Roch, E. Kozeschnik, A.F. Gourgues-Lorenzon, Metall. Mater. Trans. A 48, 2164 (2017)
Z. Jiang, P. Wang, D. Li, Y. Li, Mater. Sci. Eng. A 699, 165 (2017)
Z. Jiang, P. Wang, D. Li, Y. Li, Acta Metall. Sin. 51, 925 (2015)
L.E. Miller, G.C. Smith, J. Iron Steel Inst. 208, 998 (1970)
R. Cao, G. Li, X.Y. Fang, J. Song, J.H. Chen, Mater. Sci. Eng. A 564, 509 (2013)
Z. Li, N. Xiao, D. Li, J. Zhang, Y. Luo, R. Zhang, Mater. Sci. Eng. A 604, 103 (2014)
K. Wallin, T. Saario, K. Törrönen, Int. J. Fract. 32, 201 (1986)
A. Saha Podder, Dissertation, University of Cambridge, 2011
Z.P. Xiong, A.A. Saleh, R.K.W. Marceau, A.S. Taylor, N.E. Stanford, A.G. Kostryzhev, E.V. Pereloma, Acta Mater. 134, 1 (2017)
H. Okada, F. Matsuda, K. Ikeuchi, Z. Li, Weld. Int. 9, 211 (1995)
G. Thomas, Metall. Trans. A 9, 439 (1978)
R. Horn, R.O. Ritchie, Metall. Trans. A 9, 1039 (1978)
Acknowledgements
The authors acknowledge the TEM experimental assistance by S.Y. He from Institute of Metal Research, Chinese Academy of Sciences. This work was financially supported by the Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences (Grant No. L2019F48).
Author information
Authors and Affiliations
Corresponding author
Additional information
Available online at http://link.springer.com/journal/40195.
Rights and permissions
About this article
Cite this article
Li, YH., Jiang, ZH., Yang, ZD. et al. Effect of Indirect Transformation of Retained Austenite During Tempering on the Charpy Impact Toughness of a Low-Alloy Cr–Mo–V Steel. Acta Metall. Sin. (Engl. Lett.) 33, 1346–1358 (2020). https://doi.org/10.1007/s40195-020-01055-7
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40195-020-01055-7