Abstract
Three different types of zinc ferrite nanoparticles (ZnFe2O4 NPs) were successfully synthesized through the co-precipitation route. The synthesized ZnFe2O4 NPs were structurally characterized by Fourier transform infrared (FT-IR), Scanning electron microscopy (SEM), X-ray diffraction (XRD), and Brunauer Emmet Teller spectroscopic analyses. FT-IR analysis confirmed that the (3-APTES) is well grafted on the ZnFe2O4 NPs surface. XRD analysis shows the crystalline structure of calcined and modified ZnFe2O4 NPs, while the amorphous nature of bare ZnFe2O4 NPs was observed. SEM micrographs displayed a flat surface morphology with almost monodispersed grain size and irregular shape structure for all ZnFe2O4 NPs. The grain size of the synthesized ZnFe2O4 NPs was found to be 106.5, 23.3, and 13.9 nm for bare, calcined, and modified ZnFe2O4 NPs, respectively. Optical bandgap energy (LUMO–HOMO gap) was experimentally calculated in acidic and basic mediums (2.47 and 2.70 eV) using a taulc plot. The photocatalytic performance of the synthesized ZnFe2O4 NPs was investigated under visible irradiation in an aqueous medium against bromophenol blue dye. The influence of various parameters like irradiation time, photocatalyst dose, dye dose, pH effect, and H2O2 on the degradation efficiency was investigated. Results showed that all the three types of ZnFe2O4 NPs exhibited excellent photocatalytic properties, where the highest degradation (95.4%) was displayed by modified ZNFe2O4 NPs, followed by calcined (90.2%) and bare ZnFe2O4 84.6%). The synthesized ZnFe2O4 NPs were reused and recycled, retaining the excellent photocatalytic property for four consecutive cycles. Kinetic models demonstrate that the degradation rate was pseudo 1st order of kinetics. The turnover number reached up to 21.3 × 106, 22.5 × 106, and 23.8 × 106 for bare, annealed, and functionalized ZNFe2O4 nanoparticles, respectively. In short, the developed spongy zinc ferrite nanoparticles indicate a high potential of photo-driven catalytic remediation of tested bromophenol blue drained into the water systems.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Akpan UG, Hameed BH (2009) Parameters affecting the photocatalytic degradation of dyes using TiO2-based photocatalysts: a review. J Hazard Mater 170(2–3):520–529. https://doi.org/10.1016/j.jhazmat.2009.05.039
Ali N, Ali F, Said A et al (2020a) Characterization and deployment of surface: engineered cobalt ferrite nanospheres as photocatalyst for highly efficient remediation of alizarin red S dye from aqueous solution. J Inorg Organomet Polym Mater. https://doi.org/10.1007/s10904-020-01654-y
Ali F, Ali N, Altaf M, Said A, Shah SS, Bilal M (2020b) Epoxy polyamide composites reinforced with silica nanorods: fabrication, thermal and morphological investigations. J Inorg Organomet Polym Mater. https://doi.org/10.1007/s10904-020-01518-5
Ali N, Said A, Ali F et al (2020c) Photocatalytic degradation of congo red dye from aqueous environment using cobalt ferrite nanostructures: development, characterization, and photocatalytic performance. Water Air Soil Pollut. https://doi.org/10.1007/s11270-020-4410-8
Ali N, Said A, Ali F, Khan M, Sheikh ZA, Bilal M (2020d) Development and characterization of functionalized titanium dioxide-reinforced sulfonated copolyimide (SPI/TiO2) nanocomposite membranes with improved mechanical, thermal, and electrochemical properties. J Inorg Organomet Polym Mater. https://doi.org/10.1007/s10904-020-01636-0
Ameen S, Akhtar MS, Seo HK, Shin HS (2014) Solution processed CeO2/TiO2 nanocomposite as potent visible light photocatalyst for the degradation of BPB dye. Chem Eng J 247:193–198
Anchieta C, Cancelier A, Mazutti M et al (2014) Effects of solvent diols on the synthesis of ZnFe2O4 particles and their use as heterogeneous Photo-Fenton catalysts. Materials (basel) 7(9):6281–6290. https://doi.org/10.3390/ma7096281
Bouanimba N, Zouaghi R, Laid N, Sehili T (2011) Factors influencing the photocatalytic decolorization of Bromophenol blue in aqueous solution with different types of TiO2 as photocatalysts. Desalination 275(1–3):224–230. https://doi.org/10.1016/j.desal.2011.03.005
Buthiyappan A, Abdul Raman AA, Daud WMAW (2016) Development of an advanced chemical oxidation wastewater treatment system for the batik industry in Malaysia. RSC Adv 6(30):25222–25241. https://doi.org/10.1039/c5ra26775g
Cao SW, Zhu YJ, Cheng GF, Huang YH (2009) ZnFe2O4 nanoparticles: microwave-hydrothermal ionic liquid synthesis and photocatalytic property over phenol. J Hazard Mater 171(1–3):431–435. https://doi.org/10.1016/j.jhazmat.2009.06.019
Dehghani MH, Dehghan A, Alidadi H, Dolatabadi M, Mehrabpour M, Converti A (2017) Removal of methylene blue dye from aqueous solutions by a new chitosan/zeolite composite from shrimp waste: kinetic and equilibrium study. Korean J Chem Eng 34(6):1699–1707. https://doi.org/10.1007/s11814-017-0077-2
Dhiman M, Sharma R, Kumar V, Singhal S (2016) Morphology controlled hydrothermal synthesis and photocatalytic properties of ZnFe2O4 nanostructures. Ceram Int 42(11):12594–12605. https://doi.org/10.1016/j.ceramint.2016.04.115
Dlamini LN, Krause RW, Kulkarni GU, Durbach SH (2011) Photo-degradation of bromophenol blue with fluorinated TiO2 composite. Appl Water Sci 1(1–2):19–24. https://doi.org/10.1007/s13201-011-0004-3
Emmanuel KT, Sudesh R (2021) Adsorption and photocatalytic mineralization of bromophenol blue dye with TiO2 modified with clinoptilolite/activated carbon. Catalysts MDPI 11:7. https://doi.org/10.3390/catal11010007
Fan GL, Gu ZJ, Yang L, Li F (2009) Nanocrystalline zinc ferrite photocatalyst formed using the colloid mill and hydrothermal technique. Chem Eng J 155:534–541
Fu YS, Wang X (2011) Magnetically separable ZnFe2O4 graphene catalyst and its high photocatalytic performance under visible light irradiation. Ind Eng Chem Res 50:7210–7218
Fuku X, Matinise N, Masikini M, Kasinathan K, Maaza M (2017) An electrochemically active green synthesized polycrystalline NiO/MgO catalyst: use in photocatalytic applications. Mater Res Bull 2018(97):457–465. https://doi.org/10.1016/j.materresbull.2017.09.022
Haider S, Bukhari N, Park SY, Iqbal Y, Al-Masry WA (2011) Adsorption of bromo-phenol blue from an aqueous solution onto thermally modified granular charcoal. Chem Eng Res Des 89(1):23–28. https://doi.org/10.1016/j.cherd.2010.04.022
Hankare PP, Patil RP, Jadhav AV, Garadkar KM, Sasikala R (2011) Enhanced photocatalytic degradation of methyl red and thymol blue using titania-alumina-zinc ferrite nanocomposite. Appl Catal B Environ 107(3–4):333–339. https://doi.org/10.1016/j.apcatb.2011.07.033
He Y, Dai C, Zhou X (2017) Magnetic cobalt ferrite composite as an efficient catalyst for photocatalytic oxidation of carbamazepine. Environ Sci Pollut Res 24(2):2065–2074. https://doi.org/10.1007/s11356-016-7978-1
Jadhav SD, Hankare PP, Patil RP, Sasikala R (2011) Effect of sintering on photocatalytic degradation of methyl orange using zinc ferrite. Mater Lett 65(2):371–373. https://doi.org/10.1016/j.matlet.2010.10.004
Jayaraman A, Mas S, Tauler R, de Juan A (2012) Study of the photo-degradation of 2-bromophenol under UV and sunlight by spectroscopic, chromatographic and chemometric techniques. J Chromatogr B Anal Technol Biomed Life Sci 910:138–148. https://doi.org/10.1016/j.jchromb.2012.03.038
Jia Z, Ren D, Liang Y, Zhu R (2011) A new strategy for the preparation of porous zinc ferrite nanorods with subsequently light-driven photocatalytic activity. Mater Lett 65(19–20):3116–3119. https://doi.org/10.1016/j.matlet.2011.06.101
Khan A, Wahid F, Ali N, Badshah S, Airoldi C (2015) Single-step modification of chitosan for toxic cations remediation from aqueous solution. Desalin Water Treat 56(4):1099–1109. https://doi.org/10.1080/19443994.2014.944575
Khan H, Khalil AK, Khan A, Saeed K, Ali N (2016) Photocatalytic degradation of bromophenol blue in aqueous medium using chitosan conjugated magnetic nanoparticles. Korean J Chem Eng 33(10):2802–2807. https://doi.org/10.1007/s11814-016-0238-8
Li X, Zhao Q, Quan X (2010) New photocatalyst electrodes and their photocatalytic degradation properties of organics. Curr Org Chem 14(7):709–727. https://doi.org/10.2174/138527210790963412
Li X, Hou Y, Zhao Q, Wang L (2011) A general, one-step and template-free synthesis of sphere-like zinc ferrite nanostructures with enhanced photocatalytic activity for dye degradation. J Colloid Interface Sci 358(1):102–108. https://doi.org/10.1016/j.jcis.2011.02.052
Magdalane CM, Kaviyarasu K, Vijaya JJ et al (2017) Evaluation on the heterostructure CeO2/Y2O3 binary metal oxide nanocomposites for UV/Vis light induced photocatalytic degradation of Rhodamine-B dye for textile engineering application. J Alloys Compd 727:1324–1337. https://doi.org/10.1016/j.jallcom.2017.08.209
Mohsen VN, Razieh SK, Davoud SK (2021) Enhanced photocatalyst activity of Ni-doped BiFeO3 nanoparticles for degradation of bromophenol blue (BPB) in aqueous solutions. J React Kinet Mech Catal 134:951–970. https://doi.org/10.1007/s11144-021-02102-9
Nezamzadeh-Ejhieh A, Banan Z (2011) A comparison between the efficiency of CdS nanoparticles/zeolite A and CdO/zeolite A as catalysts in photodecolorization of crystal violet. Desalination 279(1–3):146–151. https://doi.org/10.1016/j.desal.2011.06.006
Nezamzadeh-Ejhieh A, Banan Z (2012) Sunlight assisted photodecolorization of crystal violet catalyzed by CdS nanoparticles embedded on zeolite A. Desalination 284:157–166. https://doi.org/10.1016/j.desal.2011.08.050
Nezamzadeh-Ejhieh A, Moazzeni N (2013) Sunlight photodecolorization of a mixture of Methyl Orange and Bromocresol green by CuS incorporated in a clinoptilolite zeolite as a heterogeneous catalyst. J Ind Eng Chem 19(5):1433–1442. https://doi.org/10.1016/j.jiec.2013.01.006
Posa VR, Annavaram V, Koduru JR, Ammireddy VR, Somala AR (2016) Graphene-ZnO nanocomposite for highly efficient photocatalytic degradation of methyl orange dye under solar light irradiation. Korean J Chem Eng 33(2):456–464. https://doi.org/10.1007/s11814-015-0145-4
Rauf MA, Ashraf SS (2009) Radiation induced degradation of dyes-an overview. J Hazard Mater 166(1):6–16. https://doi.org/10.1016/j.jhazmat.2008.11.043
Rishikeshi SN, Joshi SS, Temgire MK, Bellare JR (2013) Chain length dependence of polyol synthesis of zinc ferrite nanoparticles: why is diethylene glycol so different? Dalt Trans 42(15):5430–5438. https://doi.org/10.1039/c2dt32026f
Ruttink PJA, Dekker LJM, Luider TM, Burgers PC (2012) Complexation of divalent metal ions with diols in the presence of anion auxiliary ligands: zinc-induced oxidation of ethylene glycol to glycolaldehyde by consecutive hydride ion and proton shifts. J Mass Spectrom 47(7):869–874. https://doi.org/10.1002/jms.3039
Sakthivel S, Neppolian B, Shankar MV, Arabindoo B, Palanichamy M, Murugesan V (2003) Solar photocatalytic degradation of azo dye: comparison of photocatalytic efficiency of ZnO and TiO2. Sol Energy Mater Sol Cells 77(1):65–82. https://doi.org/10.1016/S0927-0248(02)00255-6
Sehar S, Naz I, Perveen I, Ahmed S (2019) Superior dye degradation using SnO2-ZnO hybrid heterostructure catalysts. Korean J Chem Eng 36(1):56–62. https://doi.org/10.1007/s11814-018-0159-9
Shah T, Gul T, Saeed K (2019) Photodegradation of BPB in aqueous medium using graphene nanoplates-supported TiO2. Appl Water Sci 9(4):1–7
Shams-Ghahfarokhi Z, Nezamzadeh-Ejhieh A (2015) As-synthesized ZSM-5 zeolite as a suitable support for increasing the photoactivity of semiconductors in a typical photo-degradation process. Mater Sci Semicond Process 39:265–275. https://doi.org/10.1016/j.mssp.2015.05.022
Skrabalak SE, Wiley BJ, Kim M, Formo EV, Xia Y (2008) On the polyol synthesis of silver nanostructures: glycolaldehyde as a reducing agent. Nano Lett 8(7):2077–2081. https://doi.org/10.1021/nl800910d
Srinivasan SS, Wade J, Stefanakos EK (2006) Synthesis and characterization of photocatalytic TiO2 - ZnFe2O4 nanoparticles. J Nanomater. https://doi.org/10.1155/JNM/2006/45712
Tashtoush AM (2021) Non-invasive blood glucose measurement using laser technology (NIBGM). Int J Comput Digit Syst 10(1):297–307
Tourinho F, Franck R, Massart R, Perzynski R (2007) Synthesis and mangeitc properties of managanese and cobalt ferrite ferrite ferrofluids. Trends Colloid Interface Sci 134:128–134. https://doi.org/10.1007/bfb0116198
Ullah I, Ali F, Ali Z, Humayun M, Wahab ZU (2018) Glycol stabilized magnetic nanoparticles for photocatalytic degradation of xylenol orange. Mater Res Express. https://doi.org/10.1088/2053-1591/aac3b8
Valizadeh S, Rasoulifard MH, Dorraji MSS (2016) Adsorption and photocatalytic degradation of organic dyes onto crystalline and amorphous hydroxyapatite: optimization, kinetic and isotherm studies. Korean J Chem Eng 33(2):481–489. https://doi.org/10.1007/s11814-015-0172-1
Wu Q, Zhang H, Zhou L, Bao C, Zhu H, Zhang Y (2016) Synthesis and application of rGO/CoFe2O4 composite for catalytic degradation of methylene blue on heterogeneous Fenton-like oxidation. J Taiwan Inst Chem Eng 67:484–494. https://doi.org/10.1016/j.jtice.2016.08.004
Xie YB, Li XZ (2006) Interactive oxidation of photoelectrocatalysis and electro-Fenton for azo dye degradation using TiO2-Ti mesh and reticulated vitreous carbon electrodes. Mater Chem Phys 95(1):39–50. https://doi.org/10.1016/j.matchemphys.2005.05.048
Xie T, Liu C, Xu L, Yang L, Zhou W (2013) Novel heterojunction Bi2O3/SrFe12O19 magnetic photocatalyst with highly enhanced photocatalytic activity. J Phys Chem C 117(46):24601–24610. https://doi.org/10.1021/jp408627e
Yang J, Cui S, Qiao JQ, Lian HZ (2014) The photocatalytic dehalogenation of chlorophenols and bromophenols by cobalt doped nano TiO2. J Mol Catal A Chem 395:42–51. https://doi.org/10.1016/j.molcata.2014.08.001
Acknowledgments
The authors wish to thank all who assisted in conducting this work.
Funding
The financial supporters of this work are "National & Local Joint Engineering Research Center for Mineral Salt Deep Utilization (No. SF 202109)”.
Author information
Authors and Affiliations
Contributions
FA: Conceptualization, Data analysis and curation, Project administration, Supervision, Validation, Writing—original draft, review & editing. LF, AS, NT, FR: Investigation, Methodology, Data analysis and curation. UA, MSA: Validation, Writing—review & editing. AR: Data analysis, Writing—review & editing. NA: Formal analysis, Writing—review & editing. NA, MB: Data analysis, Formal analysis, Writing—review & editing.
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Editorial responsibility: Shahid Hussain.
Rights and permissions
About this article
Cite this article
Fei, L., Ali, F., Said, A. et al. Surface-functionalized spongy zinc ferrite as a robust visible-light driven nanocatalyst for wastewater remediation: characterization, kinetic, and mechanistic insight. Int. J. Environ. Sci. Technol. 20, 1007–1018 (2023). https://doi.org/10.1007/s13762-022-04026-w
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13762-022-04026-w