Abstract
Adding mixed K2TiF6-KBF4 salts into mechanical stirred molten A356 alloy (Al-7Si-0.3Mg) provides a simple method to fabricate in situ TiB2/A356 composites via salts-metal reaction. However, some issues, such as the loss of Mg element in A356 alloy and the clustering of TiB2 particles in the matrix, usually occur during the fabricating process. These issues easily result in the degradation of mechanical properties of composites. In this study, a quantitative analysis revealed that the Mg element was almost consumed after the reaction, and a thermodynamic analysis inferred that the loss of Mg resulted from the reaction between Mg and mixed salts. In order to fabricate in situ TiB2/A356 composites with high strength and good ductility, we proposed a developed approach that consisted of supplementing Mg and using ultrasound stirring during the fabricating process. The introduction of ultrasound into the melt could disperse TiB2 particles uniformly in the matrix, leading to more effective refinement of α-Al grains and modification of Si phase. Compared with the untreated A356, both the strength and ductility of the developed sample were improved significantly, and the coefficient of thermal expansion mismatch strengthening was found as the major contributor to the improvement in the yield strength.
Similar content being viewed by others
References
R. Chen, Q.Y. Xu, H.T. Guo, Z.Y. Xia, Q.F. Wu, and B.C. Liu: Mater. Sci. Eng. A, 2017, vol. 685A, pp. 391-402.
S.K. Singh, K. Chattopadhyay, and P. Dutta: Metall. Mater. Trans. A, 2015, vol. 46, pp. 3248-59.
A.M. Samuel, G.H. Garza-Elizondo, H.W. Doty, and F.H. Samuel: Mater. Des., 2015, vol. 80, pp. 99-108.
K. Niranjan, and P.R. Lakshminarayanan: Mater. Des., 2013, vol. 47, pp. 167-173.
P. Davies, J. Kellie, and J. Wood: UK Patent 2257985A, 1992.
L.Lu, M.O. Lai, and F.L. Chen: Acta Materialia, 1997, vol. 45, pp. 4297-4309.
J. Mathew, A. Mandal, S. Deepak Kumar, S. Bajpai, M. Chakraborty, G.D. West, and P. Srirangam: J. Alloys. Compd., 2017, vol. 712, pp.460-467.
T.R. Hong, X.F. Li, H.W. Wang, and D. Chen: Mater. Sci. Eng., 2015, vol. 634 A, pp. 1-4.
Y. Ma, Z. Chen, M.L. Wang, D. Chen, N.H. Ma, and H.W. Wang: Mater. Sci. Eng., 2015, vol.640A, pp. 350-356.
G.H. Gan, B. Yang, B. Zhang, X. Jiang, Y.L. Shi, and Y.P. Wu: Materials, 2017, vol.10, pp.132.
J.V. Wood, P. Davies, and J.L.F. Kellie: Mater. Sci. Tech., 1993,vol. 9, pp.833-840.
M.L. Wang, D. Chen, Z. Chen, Y. Wu, F.F. Wang, N.H. Ma, and H.W. Wang: Mater. Sci. Eng., 2014, vol. 590A, pp. 246-254.
A. Mandal, M. Chakraborty, and B.S. Murty: Mater. Sci. Eng., 2008, vol.489A, pp.220-226.
T.M. Wang, Z.N. Chen, Y.P. Zheng, Y.F. Zhao, H.J Kang, and L. Gao: Mater. Sci. Eng., 2014, vol. 605 A, pp.22-32.
Z.W. Liu, Q.Y. Han, and J.G. Li: Compos. Part B Eng., 2011, vol. 42, pp. 2080-2084.
G.I. Eskin and D.G. Eskin: Ultrason. Sonochem., 2003, vol. 10, pp.297-301.
G.I. Eskin and D.G. Eskin, 2014. Ultrasonic Treatment of Light Alloy Melts (second ed), CRC Press, Boca Raton.
Q. Gao, S.S. Wu, S.L. Lv, X.C. Xiong, R. Du, and P. An: Mater. Sci. Eng., 2017, vol. 680A, pp. 437-443.
Q. Gao, S.S. Wu, S.L. Lv, X.C. Xiong, R. Du, and P. An: J. Alloys. Compd., 2017, vol. 692, pp. 1-9.
H.C. Liao, Y. Sun, and G.X. Sun: Mater. Sci. Eng., 2003, vol. 358A, pp.164-170.
M. A Matin, L Lu, and M Gupta: Scr. Mater., 2001, vol. 45, pp.479-486.
D.L. Ye and J.H. Hu: Handbook of Thermodynamic Data of Inorganic Compounds, 2nd ed. (Metallurgical Industry Press, Beijing, 2002).
A. Manoylov, B. Lebon, G. Djambazov, and K. Pericluous: Metall. Mater. Trans., 2017, vol. 48A, pp. 5616-27.
Z.W. Liu, Q.Y. Han, J.G. Li, and W.D. Huang: J. Mater. Process. Tech., 2012, vol.212, pp.365-371.
T.M. Wang, Y.P. Zheng, Z.G. Chen, Y.F. Zhao, and H.J. Kang: Mater. Des., 2014, vol. 64, pp.185-193.
L.Y. Chen, J.Q. Xu, H. Choi, H. Konishi, S. Jin, and X.C. Li: Nat. Commun., 2014, vol. 5, pp.1-9.
K.Wang, H.Y. Jiang, Y.W. Jia, H. Zhou, Q.Do. Wang, B. Ye, and W.J. Ding: Acta Materialia, 2016, vol. 103, pp. 252-263.
M. Riestra, E. Ghassemali, T. Bogdanoff, S. Seifeddine: Mater. Sci. Eng., 2017, vol. 703A, pp. 270-279.
X. Jian, T.T. Meek, and Q. Han: Scr. Mater. 2006, vol.54, pp.893-896.
P. L. Schaffer, L. Arnberg, and A. K. Dahle: Scr. Mater., 2006, vol. 54, pp. 677-682.
C.H. Caceres, C.J. Davidson, J.R. Griffiths, and Q.G. Wang: Metall. Mater. Trans., 1998, vol. 30A, pp.2611-2618.
M. Yildirim and D. Ozyurek: Mater. Des., 2013, vol. 51, pp.767-774.
S.A. Sajjadi, H.R. Ezatpour, and M. Torabi Parizi: Mater. Des., 2012, vol. 34, pp.106–111.
E. Ghassemali, M. Riestra, T. Bogdanoff, B.S. Kumar, S. Seifeddine: Procedia Engineering, 2017, vol. 207, pp. 19-24.
G. Han, W.Z. Zheng, G.H. Zhang, Z.J. Feng, and Y.J. Wang: Mater. Sci. Eng., 2015, vol. 663A, pp.161-168.
C.S. Kim, I.I. Sohn, M. Nezafati, J.B. Ferguson, B.F. Schultz, Z. Bajestani-Gohari, P.K. Rohatgi, and K. Cho: J. Mater. Sci., 2013, vol. 48, pp. 4191–4204.
S. Deepak Kumar, A. Mandal, and M. Chakraborty: Mater. Sci. Eng., 2015, vol. 636A, pp. 254-262.
Acknowledgments
This research was supported by the National Natural Science Foundation of China (Grant No. 51604211), the Natural Science Foundation of Shaanxi Province (Grant No. 2016JQ5052), China Postdoctoral Science Foundation (Grant No. 2015M580839), Special Financial Grant from China Postdoctoral Science Foundation (Grant No. 2017T100743), Shaanxi Postdoctoral Science Foundation (Grant No. 2016BSHEDZZ05), and the Fundamental Research Funds for Central Universities (Grant No. xjj2018002). We thank the Xi’an Jiaotong University Instrument Analysis Center for the help of the XRD and SEM analyses. We thank Guangyu Chen for his assistance in the casting work, and we also thank Dr. Zhifu Huang, Yimin Gao, and Jiandong Xing for their helpful discussion.
Author information
Authors and Affiliations
Corresponding author
Additional information
Manuscript submitted March 4, 2018.
Rights and permissions
About this article
Cite this article
Liu, Z., Dong, Z., Cheng, X. et al. On the Supplementation of Magnesium and Usage of Ultrasound Stirring for Fabricating In Situ TiB2/A356 Composites with Improved Mechanical Properties. Metall Mater Trans A 49, 5585–5598 (2018). https://doi.org/10.1007/s11661-018-4883-x
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11661-018-4883-x