Evaluation of the effect of grain refiners on the solidification characteristics of an Sr-modified ADC12 die-casting alloy by cooling curve thermal analysis

  • Published:
Journal of Thermal Analysis and Calorimetry Aims and scope Submit manuscript

Abstract

The influence of grain refinement—with the addition of 6 mass% Al–5Ti–B and 10 mass% Al–3Ti–B master alloys—on the temperature-based parameters of a commercial ADC12 die-casting alloy, modified with 0.04 mass% Sr, was investigated using computer-aided cooling curve thermal analysis. Results show that the addition of grain refiners caused the reaction area of the aluminium dendrite to shift up. With the addition of refiner reagents, the nucleation temperature and growth temperature for the evolution of the primary Al dendrite increased, while the recalescence temperature decreased. The dendrite coherency temperature (T DCP), time (t DCP), temperature (T N–T DCP), and time (t N–t DCP) interval for dendrite coherency and solid fraction at coherency point increased with the addition of Al–3Ti–B and Al–5Ti–B grain refiners. Nevertheless, the growth temperature of the eutectic aluminium–silicon phase remained at the modified range (563.5–565 °C) even after the addition of grain refiners. A grain-refined and modified structure was obtained after the addition of refiners, but no obvious mutual effect was found in terms of the coarsening of grain size or silicon demodification in the range of concentrations used in this study.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7

Similar content being viewed by others

References

  1. Knuutinen A, Nogita K, McDonald SD, Dahle AK. Modification of Al–Si alloys with Ba, Ca, Y and Yb. Light Met. 2001;1:229–40.

    Article  Google Scholar 

  2. Liu L, Samuel AM, Samuel FH, Doty HW, Valtierra S. Influence of oxides on porosity formation in Sr-treated Al–Si casting alloys. J Mater Sci. 2003;38:1255–67.

    Article  CAS  Google Scholar 

  3. Djurdjevic M, Jiang H, Sokolowski JH. On-line prediction of aluminum–silicon eutectic modification level using thermal analysis. Mater Charact. 2001;46:31–8.

    Article  CAS  Google Scholar 

  4. Nafisi S, Ghomashchi R. Combined grain refining and modification of conventional and rheo-cast A356 Al–Si alloy. Mater Charact. 2006;57:371–85.

    Article  CAS  Google Scholar 

  5. Samuel AM, Doty HW, Valtierra S, Samuel FH. Effect of grain refining and Sr-modification interactions on the impact toughness of Al–Si–Mg cast alloys. Mater Des. 2014;56:264–73.

    Article  CAS  Google Scholar 

  6. Prasada Rao AK. Das K, Murty BS, Chakraborty M. Microstructural features of as-cast A356 alloy inoculated with Sr, Sb modifiers and Al–Ti–C grain refiner simultaneously. Mater Lett. 2008;62:273–5.

    Article  Google Scholar 

  7. Lu L, Dahle AK. Effects of combined additions of Sr and AlTiB grain refiners in hypoeutectic Al–Si foundry alloys. Mater Sci Eng A. 2006;435–436:288–96.

    Article  Google Scholar 

  8. Liao H, Sun GX. Mutual poisoning effect between Sr and B in Al–Si casting alloys. Scr Mater. 2003;48:1035–9.

    Article  CAS  Google Scholar 

  9. Golbahar B, Samuel FH, Samuel AM, Doty HW, Valtierra S. Effect of grain refiner–modifier interaction on the microstructure and mechanical properties of A356.2 alloys. AFS Trans. 2007;115:7–12.

    Google Scholar 

  10. Emadi D, Whiting LV, Nafisi S, Ghomashchi R. Application of thermal analysis in quality control of solidification process. J Therm Anal Calorim. 2005;81:235–42.

    Article  CAS  Google Scholar 

  11. Heusler L, Schneider W. Influence of alloying elements on the thermal analysis results of Al–Si cast alloys. Light Met. 2002;2:17–26.

    Article  Google Scholar 

  12. Farahany S, Ourdjini A, Idris MH, Shabestari SG. Computer-aided cooling curve thermal analysis of near eutectic Al–Si–Cu–Fe alloy—effect of silicon modifier/refiner and solidification conditions on the nucleation and growth of dendrites. J Therm Anal Calorim. 2013;114(2):705–17.

    Article  CAS  Google Scholar 

  13. Malekan M, Shabestari SG. Computer-aided cooling curve thermal analysis used to predict the quality of aluminum alloys. J Therm Anal Calorim. 2011;103:453–8.

    Article  CAS  Google Scholar 

  14. Mahfoud M, Emadi D, Prasada Rao AK. The role of thermal analysis in detecting impurity levels during aluminum recycling. J Therm Anal Calorim. 2010;100:847–51.

    Article  CAS  Google Scholar 

  15. Farahany S, Ourdjini A, Idris MH. The usage of computer-aided cooling curve thermal analysis to optimize eutectic refiner and modifier in Al–Si alloys. J Therm Anal Calorim. 2012;109(1):105–11.

    Article  CAS  Google Scholar 

  16. Barlow JO, Stefanescu DM. Computer aided cooling curve analysis revisited. AFS Trans. 1997;97–04:349–54.

    Google Scholar 

  17. Nafisi S, Ghomashchi R. Grain refining of conventional and semi-solid A356 Al–Si alloy. J Mater Process Technol. 2006;174:371–83.

    Article  CAS  Google Scholar 

  18. Shabestari SG, Malekan M. Assessment of the effect of grain refinement on the solidification characteristics of 319 aluminum alloy using thermal analysis. J Alloy Compd. 2010;492:134–42.

    Article  CAS  Google Scholar 

  19. Malekan M, Shabestari SG. Effect of grain refinement on the dendrite coherency point during solidification of the A319 aluminium alloy. Metall Mater Trans A. 2009;40(13):3196–203.

    Article  Google Scholar 

  20. Arnberg L, Chai G, Bäckerud L. Determination of dendritic coherency in solidifying melts by rheological measurements. Mater Sci Eng A. 1993;173:101–3.

    Article  Google Scholar 

  21. MacKay RI, Djurdjevic MB, Sokołowski JH. Effect of cooling rate on fraction solid of metallurgical reactions in 319 alloy. AFS Trans. 2000;00–25:521–30.

    Google Scholar 

  22. Veldman NLM, Dahle AK, StJohn DH, Arnberg L. Dendrite coherency of Al–Si–Cu alloys. Metall Mater Trans A. 2001;32:147–55.

    Article  Google Scholar 

  23. Farahany S, Ourdjini A, Abu Bakar TA, Idris MH. A new approach to assess the effects of Sr and Bi interaction in ADC12 Al–Si die casting alloy. Thermochim Acta. 2014;575:179–87.

    Article  CAS  Google Scholar 

  24. Apelian D, Sigworth GK, Whaler KR. Assessment of grain refinement and modification of Al–Si foundry alloys by thermal analysis. AFS Trans. 1984;92:297–307.

    CAS  Google Scholar 

  25. Chen X, Geng H, Li Y. Study on the eutectic modification level of Al–7Si Alloy by computer aided recognition of thermal analysis cooling curves. Mater Sci Eng A. 2006;419:283–9.

    Article  Google Scholar 

  26. Bäckerud L, Chai G, Tamminen J. Foundry alloys. In: Solidification characteristics of aluminum alloys, Vol 2. Stockholm, Sweden: AFS/Skanaluminium; 1990.

  27. Djurdjevic MB, Odanovic Z, Talijan N. Characterization of the solidification path of AlSi5Cu (1–4 wt%) alloys using cooling curve analysis. JOM. 2011;63(11):51–7.

    Article  CAS  Google Scholar 

  28. Liao H, Sun Y, Sun GX. Correlation between mechanical properties and amount of dendrite Al phase in as-cast near-eutectic Al-11.6 % Si alloys modified with strontium. Mater Sci Eng A. 2002;335:62–6.

    Article  Google Scholar 

Download references

Acknowledgements

The authors would like to thank Universiti Teknologi Malaysia (UTM) for their financial support of this study under the Vote No. Q.J130000.2524.08H36.

Author information

Authors and Affiliations

  1. Department of Materials, Manufacturing and Industrial Engineering, Faculty of Mechanical Engineering, Universiti Teknologi Malaysia (UTM), 81310, Johor Bahru, Malaysia

    Saeed Farahany, Mohd. Hasbullah Idris, Ali Ourdjini, Fadi Faris & Hamidreza Ghandvar

Authors
  1. Saeed Farahany
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Mohd. Hasbullah Idris
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Ali Ourdjini
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Fadi Faris
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Hamidreza Ghandvar
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Mohd. Hasbullah Idris.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Farahany, S., Idris, M.H., Ourdjini, A. et al. Evaluation of the effect of grain refiners on the solidification characteristics of an Sr-modified ADC12 die-casting alloy by cooling curve thermal analysis. J Therm Anal Calorim 119, 1593–1601 (2015). https://doi.org/10.1007/s10973-014-4367-1

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10973-014-4367-1

Keywords

Search

Navigation