Abstract
Biodegradable porous Mg scaffolds are a promising approach to bone repair. In this work, 3D-spherical porous Mg–1.5Zn–0.2Ca (wt.%) scaffolds were prepared by vacuum infiltration casting technology, and MgF2 and fluorapatite coatings were designed to control the degradation behavior of Mg-based scaffolds. The results showed that the pores in Mg-based scaffolds were composed of the main spherical pores (450–600 μm) and interconnected pores (150–200 μm), and the porosity was up to 74.97%. Mg-based porous scaffolds exhibited sufficient mechanical properties with a compressive yield strength of about 4.04 MPa and elastic modulus of appropriately 0.23 GPa. Besides, both MgF2 coating and fluorapatite coating could effectively improve the corrosion resistance of porous Mg-based scaffolds. In conclusion, this research would provide data support and theoretical guidance for the application of biodegradable porous Mg-based scaffolds in bone tissue engineering.
Graphical Abstract
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Tissue engineering scaffolds have been developed as a promising strategy for the regeneration of critical-sized bone defects [1,2,3]. Biomaterials for bone tissue engineering have been supposed as interconnected open-porous structures for cell growth and nutrient transport [4]. In addition, to provide structure support for the ingrowth of new tissue, the scaffold should meet certain mechanical properties. Moreover, bone tissue engineering scaffolds require biocompatibility and biodegradability in terms of biological requirements. Up to now, many biodegradable biomaterials have been developed as tissue engineering scaffolds, such as synthetic polymer materials(e.g. PLLA [5] and PCL [6, 7]), bioactive ceramic materials [8], and biodegradable metals (e.g. Mg [9], Zn [10], Fe [11]).
Mg and its alloys have been paid much attention owing to their suitable mechanical properties (such as elastic modulus and density close to human bone [12]), favorable biodegradability [13, 14], and good biocompatibility [15]. Besides, Mg is one of the macro elements in the human body, playing an osteoinductive and osteoconductive role in the growth of bone tissue and the healing of bone fractures [16]. Thus, based on the overall consideration of mechanical properties, biodegradation, and biocompatibility, Mg-based scaffolds are expected to be a new generation of tissue engineering scaffolds.
Recently, many studies have been carried out to evaluate the effects of the preparation process and pore structure regulation of porous Mg-based scaffolds on the chemical-physical properties [17,18,19]. The preparation methods of Mg scaffolds include vacuum infiltration casting [17], powder metallurgy [20], additive manufacturing [21, 22], laser perforation [23], and so on. Herein, in vacuum infiltration casting technology, the pore size and porosity of Mg-based scaffolds are relatively controllable [18]. Mg-based scaffolds with spherical pores exhibited better resistance to the deterioration of the interconnectivity and higher porosity compared with irregular pores [19]. However, Mg scaffolds exhibited enhanced biodegradation rate owing to their chemical nature and large exposed surface from pore structure. Therefore, surface modifications should be introduced to regulate the degradation rate. Yu et al. [23] reported that MgF2 coatings simultaneously enhanced the corrosion resistance, biocompatibility, osteoconductivity and osteoinductivity of Mg-based scaffolds.
Based above, this work investigated Mg scaffolds with spherical pore structures and introduced surface coatings for controlling the degradation rate. The pore structure, mechanical properties, and in vitro degradability of porous Mg-based scaffolds were comprehensively evaluated.
2 Materials and methods
2.1 Materials
In this study, the raw materials for Mg–Zn–Ca alloy were pure Mg (≥99.95 wt%), pure Zn (≥99.95 wt%), and Mg-30wt.% Ca alloy. Mg–1.5Zn–0.2Ca (wt.%) scaffolds were prepared by vacuum infiltration casting. The pore former for preparation of porous materials was spherical NaCl particles with a mean size of 450–600 μm. The schematic diagram of preparation, including NaCl pretreatment, infiltration casting of Mg-based scaffolds, and NaCl removal, is shown in Fig. 1a.
2.2 Scaffolds
Firstly, NaCl templates were put into a casting mold (Ф 60 mm × 260 mm) and heated to 400 °C. Secondly, the mold containing the NaCl templates was heated to 660 °C under a mixed protective gas of CO2 and SF6. Thirdly, Mg ingots were cleaned with NaOH solution (approximately 1 mol/L) to remove NaCl templates.
2.3 Characterizations
The surface morphologies were observed by scanning electron microscopy (SEM, Sirion 200) with an energy dispersive X-ray spectrometer (EDS, Oxford). The phase composition was analyzed by an X-ray diffractometer (XRD, Bruker D8-Discover) with a scan angle of 20°–90°. The 3D model of the porous Mg-based scaffold was collected and reconstructed by computerized tomography (CT, CT, YXLON CT Precision). The pore size distribution in the as-prepared scaffolds was collected by the Image-Pro Plus 6.0 program and the porosity was calculated by VGSTUDIO MAX software.
2.4 Mechanical properties
The compression performance was measured by an electronic universal testing machine (SANS CMT4503). Cylindrical samples with a dimension of Ф 10 mm × 10 mm were used for the evaluation of mechanical properties. The compression tests were carried out at a compression speed of 0.5 mm/min at room temperature, and repeated at least three times in each case.
2.5 Simulation analysis
Digital image correlation technology (DIC) was utilized to achieve the real strain distribution of porous Mg-based scaffolds. Finite element analysis (FEA) was applied to simulate the strain distribution of Mg-based scaffolds under compressive loading. The model for FEA was selected from CT analysis to reliably simulate the mechanical behavior of Mg scaffolds. The meshes were divided into triangular elements with a size of 0.1 mm. The main parameters of the material were set (0.23 GPa for elastic modulus, 0.3 for Poisson’s ratio, and 4.0 MPa for compressive yield strength, respectively). Herein, the ultimate compression distance was 1.2 mm to ensure that the material reached the plastic deformation stage.
2.6 Scaffold degradation
Hanks’ solution (NaCl (8.00 g/L), KCl (0.40 g/L), CaCl2 (0.14 g/L), NaHCO3 (0.35 g/L), MgCl2·6H2O (0.10 g/L), MgSO4·7H2O (0.06 g/L), Na2HPO4 (0.06 g/L), KH2PO4 (0.06 g/L) and C6H12O6 (1.00 g/L) [24, 25]) was used for evaluation of in vitro degradation behaviors. The specimens for corrosion tests were cut into a dimension of Ф 10 mm × 2 mm. The degradation behavior was evaluated in Hank’s solution at 37 ± 0.5 oC, and the degradation performance was comprehensively characterized in terms of the hydrogen evolution curve, pH curve, and the change of surface morphology before and after degradation. After immersion, the corrosion products were removed in a solution containing 200 g/L CrO3 and 10 g/L AgNO3. The fluorination treatment was performed by immersing the Mg-based scaffolds in a poly tetra fluoroethylene reaction vessel filled with 40 wt.% HF solution, immersed at 80 °C for 40 h. The calcium phosphate coating was designed to grow on the surface of the MgF2 coating. The porous Mg-based scaffolds were immersed for 2 h in the flowing treatment solution containing 0.06 mol/L NH4H2PO4, 0.1 mol/L Ca(NO3)2·4H2O, as shown in Fig. 1b.
3 Results and discussion
3.1 Structure characterization
As shown in Fig. 2a, NaCl templates are typical 3D spheres of Ф 450–600 μm. The pore size of Mg-based scaffolds mainly ranges from 50 to 800 μm, which was collected by Image-Pro Plus 6.0 program. Figure 2b, c shows pore structure characterizations of porous Mg-based scaffolds. The open-pore structures (in Fig. 2b) are composed of two main pores, including main pores (450–600 μm) and interconnected pores (150–200 μm), as displayed in Fig. 2a, c. Figure 2d, e shows the micromorphology of porous Mg-based scaffolds with MgF2 coating. The coating on the outer surface is relatively flat with directional strip microcracks. Figure 2f, g shows the morphologies of fluorapatite coating. It can be observed that the fine particles are composed of needle-like clusters of 3–6 μm, and the inclusions are distributed with rectangular thick lamellar crystal clusters shown in Fig. 2g. Besides, X-ray diffuse peaks of MgF2 and fluorapatite phases were detected on Mg-based scaffolds with MgF2 and fluorapatite coatings, respectively, as shown in Fig. 2j.
The 3D model of the as-prepared porous Mg-based scaffolds was reconstructed in Fig. 2h by CT. Figure 2i is the cross-section view of Mg-based scaffolds from Fig. 2h. It displays that the pores are uniformly distributed with suitable connectivity between the pores. Herein, the central area (Ф 8 mm × 8 mm) is selected to calculate pore structural parameters. The measured porosity is 74.97%, close to 75%, and the specific surface area is 8.36 mm2/mm3.
3.2 Mechanical properties
Figure 3 shows the mechanical properties of as-prepared Mg-based scaffolds. Figure 3a exhibits the strain distribution process of porous Mg-based scaffolds. Figure 3b, c displays compressive strain distribution obtained by FE modeling. During the entire compression process, the maximal strain is distributed at both ends of the specimens, while the lower strain is inside.
A typical compression stress-strain curve is illustrated in Fig. 3d, which consists of the elastic stage, yield stage and densification stage [17]. During the elastic stage, the inhomogeneity of the porous structure leads to local stress concentration under the lower strain. The weakest part of the pore walls undergoes bending, stretching, and compression. The pore walls are not bent and fractured until the local stress exceeds the yield stress of the material, which leads to early local plastic instability. However, the curve shows roughly linear changes due to the stable pore structure. With the further increase of the compressive load, most pore walls are buckled and collapsed, which is corresponding to the yield stage. In the densification stage, the compressive stress continues to increase so that the porous structure is collapsed completely. Meanwhile, the slope of the stress-strain curve increased rapidly. According to Fig. 3d, the compressive yield strength and compressive elastic modulus of the porous Mg-based scaffolds are 4.04 ± 0.85 MPa and 0.23 ± 0.12 GPa, respectively. Table 1 summarizes the characterizations of porous Mg scaffolds. Alloying and pore structure are both important factors in mechanical properties [17]. Owing to alloying strengthening, Mg-Zn-Ca scaffold in the present work exhibited higher mechanical properties than Mg scaffold reported by Jia et al. [18]. In this present work, the porous Mg-based scaffolds showed advantages in the comprehensive evaluation of porosity and mechanical properties, which are matched with human cancellous bone [26].
3.3 Degradation behavior
Degradation of Mg-based alloys is always accompanied by hydrogen evolution, as shown in Eq. (1) [27, 28].
Figure 4 shows the degradation test results. Figure 4m, n displays the hydrogen evolution curves and pH curves, and the hydrogen evolution rate is consistent with pH. Mg-based scaffolds with MgF2 coating and fluorapatite coating both exhibit a lower degradation rate than the uncoated Mg-based scaffolds, while the corrosion rate of coated Mg-based scaffolds increases in the later stage. In summary, the anti-corrosion properties of the coated Mg-based scaffolds are significantly improved.
Figure 4a–c are the macroscopic corrosion morphologies of three porous Mg-based scaffolds immersed in Hanks’ solution for 300 h. The 3D-spherical porous structure characteristics remain intact, but MgF2 and fluorapatite are covered on the surface. Herein, fluorapatite, as a representative bioceramic, exhibited enhanced bio bioactivity [29]. Figure 4g–i reveal the corrosion morphologies and EDS results. For fluorapatite coating, there are more calcium-phosphorus products covering on the scaffold, as shown in EDS analysis of area A and B. The pores are gradually covered by corrosion products, protecting the porous Mg alloy substrate from further corrosion. The calcium-phosphorus compounds in area A has grown massively on the surface of the fluorapatite coating, which is corresponding to fewer Mg elements. Figure 4j–l are the morphologies of porous Mg-based scaffolds immersed for 300 h after removing corrosion products. The porous structure characteristics of three Mg-based scaffolds remain intact. However, the increase in biodegradation rate at the late immersion stage is ascribed to cracks growth (in Fig. 4h). There are a small number of corrosion pits and thick needle-like clusters observed on the surface of the fluorapatite film, as shown in Fig. 4i. Although the fluorapatite coating exhibits local failure, the majority of the coating still perfectly adheres to the porous Mg substrate. Both MgF2 and fluorapatite enhance the corrosion resistance of Mg-based scaffolds.
4 Conclusions
In this work, 3D-spherical Mg-based scaffolds for bone repair were prepared with an average pore size of 450–600 µm and a porosity of 74.97%. The Mg-based scaffolds exhibited a compressive yield strength of 4.04 MPa and a compressive elastic modulus of 0.23 GPa. In addition, the real and simulated strain distributions were in good agreement. The Mg-based scaffolds meet the mechanical requirements for cancellous bone repair. In terms of degradation behavior, both MgF2 coating and fluorapatite coating effectively improve the corrosion resistance of Mg-based scaffolds. The pore structure of the scaffolds remains intact with tiny corrosion products when immersed in Hanks’ solution for 300 h. The fluorapatite coating provided better protection for Mg-based scaffolds. Biodegradable Mg-based scaffolds for bone tissue engineering are still in their infancy. The related alloying elements, preparation process, and surface coating need further research to control the degradation rate of Mg. Furthermore, combining Mg scaffolds with biopolymers, bioactive ceramics, and drugs will be a direction of future development.
References
Jang JW, Min KE, Kim C, Sjom J, Lee J, Yi S. Review: scaffold characteristics, fabrication methods, and biomaterials for the bone tissue engineering. Int J Precis Eng Man. 2023;24:511–29. https://doi.org/10.1007/s12541-022-00755-7
Preethi SS, Haritha MA, Viji CS, Selvamurugan N. Bone tissue engineering: scaffold preparation using chitosan and other biomaterials with different design and fabrication techniques. Int J Biol Macromol. 2018;119:1228–39. https://doi.org/10.1016/j.ijbiomac.2018.08.056
Roseti L, Parisi V, Petretta M, Cavallo C, Desando G, Bartolotti L, et al. Scaffolds for bone tissue engineering: state of the art and new perspectives. Mater Sci Eng C. 2017;78:1246–62. https://doi.org/10.1016/j.msec.2017.05.017
Gómez S, Vlad MD, López J, Fernández E. Design and properties of 3D scaffolds for bone tissue engineering. Acta Biomater. 2016;42:341–50. https://doi.org/10.1016/j.actbio.2016.06.032
Singh M, Johnalagadda S. Design and characterization of 3D printed, neomycin-eluting poly-L-lactide mats for wound-healing applications. J Mater Sci Mater Med. 2021;32:44. https://doi.org/10.1007/s12541-022-00755-7
Rezania N, Asadi-Eydivand M, Abolfathi N, Bonakdar S, Mehrjoo M, Solati-Hashjin M. Three-dimensional printing of polycaprolactone/hydroxyapatite bone tissue engineering scaffolds mechanical properties and biological behavior. J Mater Sci Mater Med. 2022;3:31. https://doi.org/10.1007/s10856-022-06653-8
Dong Q, Zhang M, Zhou X, Shao Y, Li J, Wang L, et al. 3D-printed Mg-incorporated PCL-based scaffolds: a promising approach for bone healing. Mater Sci Eng C. 2021;129:112372. https://doi.org/10.1016/j.msec.2021.112372
Sonbolekar H, Alireza J, Ahmad A, Hesaraki S, Akbarzadeh A. Assessment of tricalcium phosphate/titanium dioxide (TCP/TiO2) nanocomposite scaffold compared with bone autograft and hydroxyapatite (HA) on the healing of segmental femur bone defect in rabbits. J Mater Sci Mater Med. 2022;33:80. https://doi.org/10.1007/s10856-022-06694-z
Zhang N, Zhao D, Liu N, Wu Y, Yang J, Xie H, et al. Assessment of the degradation rates and effectiveness of different coated Mg-Zn-Ca alloy scaffolds for in vivo repair of critical-size bone defects. J Mater Sci-Mater Med. 2018;29:138. https://doi.org/10.1007/s10856-018-6145-2
Qin Y, Liu A, Huo H, Shen Y, Wen P, Lin H, et al. Additive manufacturing of Zn-Mg alloy porous scaffolds with enhanced osseointegration: In vitro and in vivo studies. Acta Biomater. 2022;145:403–15. https://doi.org/10.1016/j.actbio.2022.03.055
Nie Y, Chen G, Peng H, Tang S, Zhou Z, Pei F, et al. In vitro and 48 weeks in vivo performances of 3D printed porous Fe-30Mn biodegradable scaffolds. Acta Biomater. 2021;121:724–40. https://doi.org/10.1016/j.actbio.2020.12.028
Staiger MP, Pietak AM, Huadmai J, Dias G. Magnesium and its alloys as orthopedic biomaterials: a review. Biomaterials. 2006;27:1728–34. https://doi.org/10.1016/j.biomaterials.2005.10.003
Zhang Y, Cao J, Wang X, Liu H, Shao Y, Chu C, et al. The effect of enzymes on the in vitro degradation behavior of Mg alloy wires in simulated gastric fluid and intestinal fluid. Bioact Mater. 2022;7:217–26. https://doi.org/10.1016/j.bioactmat.2021.05.047
Zhang Y, Cao J, Lu M, Shao Y, Jiang K, Yang X, et al. A biodegradable magnesium surgical staple for colonic anastomosis: In vitro and in vivo evaluation. Bioact Mater. 2023;22:225–38. https://doi.org/10.1016/j.bioactmat.2022.09.023
Serre CM, Papillard M, Chavassieux P, Voegel JC, Boivin G. Influence of magnesium substitution on a collagen-apatite biomaterial on the production of a calcifying matrix by human osteoblasts. J Biomed Mater Res. 1998;42:626–33. https://doi.org/10.1002/(SICI)1097-4636(19981215)42:43.0.CO;2-S.
Zhang Y, Xu J, Ruan Y, Yu M, O’Laughlin M, Wise H, et al. Implant-derived magnesium induces local neuronal production of CGRP to improve bone-fracture healing in rats. Nat Med. 2016;22:1160–9. https://doi.org/10.1038/nm.4162
Dong Q, Li Y, Jiang H, Zhou X, Bai J. 3D-cubic interconnected porous Mg-based scaffolds for bone repair. J Magnes Alloy. 2021;9:1329–38. https://doi.org/10.1016/j.jma.2020.05.022
Jia G, Hou Y, Chen C, Niu J, Zhang H, Huang H, et al. Precise fabrication of open porous Mg scaffolds using NaCl templates: relationship between space holder particles, pore characteristics and mechanical behavior. Mater Des. 2017;140:106–13. https://doi.org/10.1016/j.matdes.2017.11.064
Jia G, Chen CX, Zhang J, Wang Y, Yue R, Luthringer-Feyerabend B, et al. In vitro degradation behavior of Mg scaffolds with three-dimensional interconnected porous structures for bone tissue engineering. Corros Sci. 2018;144:301–12. https://doi.org/10.1016/j.corsci.2018.09.001
Yan Y, Kang YJ, Li D, Yu K, Xiao T, Wang QY, et al. Microstructure, mechanical properties and corrosion behavior of porous Mg-6 wt.% Zn scaffolds for bone tissue engineering. J Mater Eng Perform. 2018;27:970–84. https://doi.org/10.1007/s11665-018-3189-x
Lin T, Dong J, Wang X, Deng X, Shao H. Effect of Zn content on 3D gel-printed porous Mg–Zn scaffolds for bone engineering. J Mater Sci. 2023;58:1229–42. https://doi.org/10.1007/s10853-022-08108-5
Wang Y, Huang H, Jia G, Zeng H, Yuan G. Fatigue and dynamic biodegradation behavior of additively manufactured Mg scaffolds. Acta Biomater. 2021;135:705–22. https://doi.org/10.1016/j.actbio.2021.08.040
Yu W, Zhao HK, Ding ZY, Zhang ZW, Sun BB, Shen J, et al. In vitro and in vivo evaluation of MgF2 coated AZ31 magnesium alloy porous scaffolds for bone regeneration. Colloid Surf B. 2017;149:330–40. https://doi.org/10.1016/j.colsurfb.2016.10.037
Dong Q, Zhou X, Feng Y, Qian K, Liu H, Lu M, et al. Insights into self-healing behavior and mechanism of dicalcium phosphate dihydrate coating on biomedical Mg. Bioact Mater. 2021;6:158–68. https://doi.org/10.1016/j.bioactmat.2020.07.019
Dong Q, Dai J, Qian K, Liu H, Zhou X, Yao Q, et al. Dual self-healing inorganic-organic hybrid coating on biomedical Mg. Corros Sci. 2022;200:110230. https://doi.org/10.1016/j.corsci.2022.110230
Bose S, Roy M, Bandyopadhyay A. Recent advances in bone tissue engineering scaffolds. Trends Biotechnol. 2012;30:546–54. https://doi.org/10.1016/j.tibtech.2012.07.005
Dong Q, Jia Y, Ba Z, Tao X, Wang Z, Xue F, et al. Exploring the corrosion behavior of Mn-implanted biomedical Mg. J Alloy Compd. 2021;873:159739. https://doi.org/10.1016/j.jallcom.2021.159739
Zhou X, Dong Q, Wei D, Bai J, Xue F, Zhang B, et al. Smart corrosion inhibitors for controlled release: a review. Corros Eng Sci Technol. 2023;58:190–204. https://doi.org/10.1080/1478422X.2022.2161122
Li J, Han P, Ji W, Song Y, Zhang S, Chen Y, et al. The in vitro indirect cytotoxicity test and in vivo interface bioactivity evaluation of biodegradable FHA coated Mg-Zn alloys. Mater Sci Eng B. 2011;176:1785–8. https://doi.org/10.1016/j.mseb.2011.05.029
Lin T, Wang X, Jin L, Li W, Zhang Y, Wang A, et al. Manufacturing of porous magnesium scaffolds for bone tissue engineering by 3D gel-printing. Mater Des. 2021;209:109948. https://doi.org/10.1016/j.matdes.2021.109948
Wang W, Jiang G, Wang Q, Huang H, Li X, Zeng H, et al. The in vitro and in vivo biological effects and osteogenic activity of novel biodegradable porous Mg alloy scaffolds. Mater Des;189:108514. https://doi.org/10.1016/j.matdes.2020.108514
Witting LM, Waselau AC, Feichtner F, Wurm L, Julmi S, Klose C, et al. Influence of coatings on degradation and osseointegration of open porous Mg scaffolds in vivo. Materialia. 2020;14:100949. https://doi.org/10.1016/j.mtla.2020.100949
Bonithon R, Kao AP, Fernández MP, Dunlop JN, Dunlop JN, Blunn GW, et al. Multi-scale mechanical and morphological characterisation of sintered porous magnesium-based scaffolds for bone regeneration in critical-sized defects. Acta Biomater. 2021;127:338–52. https://doi.org/10.1016/j.actbio.2021.03.068
Acknowledgements
This research was supported by the National Natural Science Foundation of China (51971062), the Industry Foresight and Key Technologies Project of Suzhou (SYC2022136, SYC2022135), the Open Research Fund of Jiangsu Key Laboratory for Advanced Metallic Materials (AMM2021A01), the Scientific Research Project of Jiangsu Provincial Health Commission (Z2021083), the Science and Technology Development Project of Traditional Chinese Medicine of Taizhou City (TZ202107), the Social Development Project of Science and Technology Support Plan of Taizhou (SSF20220134), and Fifth Scientific Research Funding Project of Taizhou 311 Project Training Object (RCPY202128).
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Conflict of interest
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Huo, L., Li, Q., Jiang, L. et al. Porous Mg–Zn–Ca scaffolds for bone repair: a study on microstructure, mechanical properties and in vitro degradation behavior. J Mater Sci: Mater Med 35, 22 (2024). https://doi.org/10.1007/s10856-023-06754-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s10856-023-06754-y