Spectral, electrical, magnetic and radiation shielding studies of Mg-doped Ni–Cu–Zn nanoferrites

  • Published:
Journal of Materials Science: Materials in Electronics Aims and scope Submit manuscript

Abstract

Nanoferrites of Ni0.1Cu0.2MgxZn(0.7−x)Fe2O4 (x = 0.0, 0.15, 0.25, 0.35, 0.45, 0.55 and 0.70 wt%) system fabricated using flash auto combustion technique. All investigated samples annealed for 2 h at 600 °C. XRD, FTIR and TEM were utilized to evaluate the structural characterization of as-prepared samples. The electrical DC resistivity of the investigated samples is evaluated as a function of frequency and temperature. The initial magnetic permeability (μi) is dependent on the temperature and was measured at constant frequency 1 kHz and 10 kHz of the sinusoidal wave. A single-phase of spinel structure was formed and with increasing Mg content the peak (311) of 100% intensity decreases, which demonstrates the presence of Mg, which slows down the growth of the crystal as X-ray result. The FTIR spectra of the prepared ferrite samples are distinguished by the presence of two strong absorption bands (ν1 = 554 cm−1) and (ν2 = 449 cm−1). The morphological observation is determined by the transmission electron microscopy (TEM) and shows that the particles size ranged between 26 and 39 nm. It can notice shifted Curie temperature (Tc) to a higher temperature by increasing Mg content. Mass attenuation coefficient (μm), mean free path (λ), half value layer (X1/2), tenth value layer (X1/10) and effective atomic numbers (Zeff) for the studied samples, have been simulated using FLUKA (2020.0beta.2), while energy change from 15 × 10–3 to 153+ keV with increasing Mg concentration, both μm and Zeff decrease. The largest value of μm and Zeff when x = 0% while sample x = 0.35% has a minimum value of λ, X1/10 and X1/2.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13
Fig. 14
Fig. 15

Similar content being viewed by others

References

  1. K. Jalaiah, K.V. Babu, K. Chandramouli, P.S. Rao, Phys. B 534, 125 (2018)

    Article  CAS  Google Scholar 

  2. A. Gholizadeh, J. Am. Ceram. Soc. 100, 3577 (2017)

    Article  CAS  Google Scholar 

  3. W. Li, W. Wang, J. Lv, Y. Ying, J. Yu, J. Zheng, L. Qiao, S. Che, J. Magn. Magn. Mater. 456, 333 (2018)

    Article  CAS  Google Scholar 

  4. A. Ramakrishna, N. Murali, T.W. Mammo, K. Samatha, V. Veeraiah, Phys. B 534, 134 (2018)

    Article  CAS  Google Scholar 

  5. A.V. Trukhanov, S.V. Trukhanov, L.V. Panina, V.G. Kostishyn, I.S. Kazakevich, A.V. Trukhanov, E.L. Trukhanova, V.O. Natarov, V.A. Turchenko, M.M. Salem, A.M. Balagurov, J. Magn. Magn. Mater. 426, 487 (2017)

    Article  CAS  Google Scholar 

  6. D.I. Tishkevich, I.V. Korolkov, A.L. Kozlovskiy, M. Anisovich, D.A. Vinnik, A.E. Ermekova, A.I. Vorobjova, E.E. Shumskaya, T.I. Zubar, S.V. Trukhanov, M.V. Zdorovets, A.V. Trukhanov, J. Alloys Compd. 797, 573 (2019)

    Article  CAS  Google Scholar 

  7. K. Dukenbayev, I.V. Korolkov, D.I. Tishkevich, A.L. Kozlovskiy, S.V. Trukhanov, Y.G. Gorin, E.E. Shumskaya, E.Y. Kaniukov, D.A. Vinnik, M.V. Zdorovets, M. Anisovich, A.V. Trukhanov, D. Tosi, C. Molardi, Nanomaterials 9, 494 (2019)

    Article  CAS  Google Scholar 

  8. M.A. Almessiere, A.V. Trukhanov, F.A. Khan, Y. Slimani, N. Tashkandi, V.A. Turchenko, T.I. Zubar, D.I. Tishkevich, S.V. Trukhanov, L.V. Panina, A. Baykal, Ceram. Int. 46, 7346 (2020)

    Article  CAS  Google Scholar 

  9. A.L. Kozlovskiy, I.E. Kenzhina, M.V. Zdorovets, Ceram. Int. 46, 10262 (2020)

    Article  CAS  Google Scholar 

  10. M.A. Almessiere, Y. Slimani, H. Güngüneş, A. Baykal, N.A. Alhamed, A.V. Trukhanov, S.V. Trukhanov, Ceram. Int. 45, 11615 (2019)

    Article  CAS  Google Scholar 

  11. M.A. Almessiere, Y. Slimani, H. Güngüneş, V.G. Kostishyn, S.V. Trukhanov, A.V. Trukhanov, A. Baykal, Ceram. Int. 46, 11124 (2020)

    Article  CAS  Google Scholar 

  12. M.V. Zdorovets, A.L. Kozlovskiy, J. Alloys Compd. 815, 152450 (2020)

    Article  CAS  Google Scholar 

  13. X. Qi, J. Zhou, Z. Yue, Z. Gui, L. Li, J. Magn. Magn. Mater. 251, 316 (2002)

    Article  CAS  Google Scholar 

  14. M.A. Gabal, J. Magn. Magn. Mater. 321, 3144 (2009)

    Article  CAS  Google Scholar 

  15. N. Varalaxmi, N.R. Reddy, M.V. Ramana, E. Rajgopal, V.R. Murthy, K.V. Sivakumar, J. Mater. Sci. Mater. Electron. 19, 399 (2008)

    Article  CAS  Google Scholar 

  16. P.K. Roy, J. Bera, J. Magn. Magn. Mater. 298, 38 (2006)

    Article  CAS  Google Scholar 

  17. O.M. Hemeda, A. Tawfik, M. Mostafa, M. Zaki, M.I. Abd El Ati, J. Phys. Conf. Ser. 1253, 012026 (2019)

    Article  CAS  Google Scholar 

  18. O.M. Hemeda, A.M.A. Henaish, S.F. Mansour, T. Sharshar, M.A. Hamad, Appl. Phys. A 126, 1 (2020)

    Google Scholar 

  19. A.M.A. Henaish, M. Mostafa, B.I. Salem, O.M. Hemeda, Phase Transit 93, 470 (2020)

    Article  CAS  Google Scholar 

  20. A. Gholizadeh, E. Jafari, J. Magn. Magn. Mater. 422, 328 (2017)

    Article  CAS  Google Scholar 

  21. A. Ferrari, P.R. Sala, A. Fasso, J. Ranft, CERN-2005–10 INFN/TC 05/11 (2005)

  22. T.T. Böhlen, F. Cerutti, M.P.W. Chin, A. Fassò, A. Ferrari, P.G. Ortega, A. Mairani, P.R. Sala, G. Smirnov, V. Vlachoudis, Nucl. Data Sheets 120, 211 (2014)

    Article  CAS  Google Scholar 

  23. F. Özkalaycı, M.R. Kaçal, O. Agar, H. Polat, A. Sharma, F. Akman, J. Phys. Chem. Solids 145, 109543 (2020)

    Article  CAS  Google Scholar 

  24. A.I. Elazaka, H.M. Zakaly, S.A. Issa, M. Rashad, H.O. Tekin, H.A. Saudi, V.H. Gillette, T.T. Erguzel, A.G. Mostafa, J. Hazard. Mater. (2020). https://doi.org/10.1016/j.jhazmat.2020.123738

    Article  Google Scholar 

  25. A.S. Abouhaswa, H.M. Zakaly, S.A. Issa, M. Rashad, M. Pyshkina, H.O. Tekin, R. El-Mallawany, M.Y. Mostafa, Ceram. Int. (2020). https://doi.org/10.1016/j.ceramint.2020.08.122

    Article  Google Scholar 

  26. H.M. Zakaly, A.S. Abouhaswa, S.A.M. Issa, M.Y.A. Mostafa, M. Pyshkina, R. El-Mallawany, J. Non. Cryst. Solids 543, 120151 (2020)

    Article  CAS  Google Scholar 

  27. A.S. Abouhaswa, H.M.H. Zakaly, S.A.M. Issa, M. Pyshkina, R. El-Mallawany, M.Y.A. Mostafa, J. Mater. Sci. Mater. Electron. 31, 14494 (2020)

  28. A. Tawfik, O.M. Hemeda, A.M.A. Henaish, A.M. Dorgham, Mater. Chem. Phys. 211, 1 (2018)

    Article  CAS  Google Scholar 

  29. A. Gholizadeh, J. Magn. Magn. Mater. 452, 389 (2018)

    Article  CAS  Google Scholar 

  30. W.A. Bayoumy, M.A. Gabal, J. Alloys Compd. 506, 205 (2010)

    Article  CAS  Google Scholar 

  31. O.M. Hemeda, A.M.A. Henaish, B.I. Salem, F.S. El-Sbakhy, M.A. Hamad, Appl. Phys. A 126, 121 (2020)

    Article  CAS  Google Scholar 

  32. M. Khairy, M.E. Gouda, J. Adv. Res. 6, 555 (2015)

    Article  CAS  Google Scholar 

  33. B. Thangjam, I. Soibam, Adv. Mater. Proc. 2, 205 (2017)

    Article  Google Scholar 

  34. R. Sharma, P. Thakur, P. Sharma, V. Sharma, J. Alloys Compd. 704, 7 (2017)

    Article  CAS  Google Scholar 

  35. K. El Maalam, M.B. Ali, H. El Moussaoui, O. Mounkachi, M. Hamedoun, R. Masrour, E.K. Hlil, A. Benyoussef, J. Alloys Compd. 622, 761 (2015)

    Article  CAS  Google Scholar 

  36. D.M. Hemeda, A. Tawfik, O.M. Hemeda, S.M. Dewidar, Solid State Sci. 11, 1350 (2009)

    Article  CAS  Google Scholar 

  37. A.M. Shaikh, C.M. Kanamadi, B.K. Chougule, Mater. Chem. Phys. 93, 548 (2005)

    Article  CAS  Google Scholar 

  38. M.J. Iqbal, M.R. Siddiquah, J. Magn. Magn. Mater. 320, 845 (2008)

    Article  CAS  Google Scholar 

  39. S.V. Trukhanov, I.O. Troyanchuk, N.V. Pushkarev, H. Szymczak, J. Exp. Theor. Phys. 95, 308 (2002)

    Article  CAS  Google Scholar 

  40. M.V. Zdorovets, A.L. Kozlovskiy, Ceram. Int. 46, 14548 (2020)

    Article  CAS  Google Scholar 

  41. S.V. Trukhanov, A.V. Trukhanov, A.N. Vasilev, A. Maignan, H. Szymczak, JETP Lett. 85, 507 (2007)

    Article  CAS  Google Scholar 

  42. I.O. Troyanchuk, S.V. Trukhanov, D.D. Khalyavin, H. Szymczak, J. Magn. Magn. Mater. 208, 217 (2000)

    Article  CAS  Google Scholar 

  43. S.V. Trukhanov, V.A. Khomchenko, L.S. Lobanovski, M.V. Bushinsky, D.V. Karpinsky, V.V. Fedotova, I.O. Troyanchuk, A.V. Trukhanov, S.G. Stepin, R. Szymczak, C.E. Botez, A. Adair, J. Exp. Theor. Phys. 103, 398 (2006)

    Article  CAS  Google Scholar 

  44. M.V. Zdorovets, I.E. Kenzhina, V. Kudryashov, A.L. Kozlovskiy, Ceram. Int. 46, 10521 (2020)

    Article  CAS  Google Scholar 

  45. S.G. Bachhav, R.S. Patil, P.B. Ahirrao, A.M. Patil, D.R. Patil, Mater. Chem. Phys. 129, 1104 (2011)

    Article  CAS  Google Scholar 

  46. O.M. Hemeda, M.A. Hamad, A.M.A. Henaish, Mater. Res. Express 5, 076102 (2018)

    Article  CAS  Google Scholar 

  47. M. Kaiser, S.S. Ata-Allah, Mater. Res. Bull. 44, 1249 (2009)

    Article  CAS  Google Scholar 

  48. A.M. Shaikh, S.C. Watawe, S.S. Bellad, S.A. Jadhav, B.K. Chougule, Mater. Chem. Phys. 65, 46 (2000)

    Article  CAS  Google Scholar 

  49. N. Varalaxmi, K.V. Siva Kumar, J. Mater. Sci. Mater. Electron. 22, 555 (2011)

    Article  CAS  Google Scholar 

  50. Y. Elmahroug, B. Tellili, C. Souga, Ann. Nucl. Energy 75, 268 (2015)

    Article  CAS  Google Scholar 

  51. E. Kavaz, H.O. Tekin, O. Agar, E.E. Altunsoy, O. Kilicoglu, M. Kamislioglu, M.M. Abuzaid, M.I. Sayyed, Ceram. Int. 45, 15348 (2019)

    Article  CAS  Google Scholar 

  52. S.A.M. Issa, H.O. Tekin, T.T. Erguzel, G. Susoy, Appl. Phys. A 125, 640 (2019)

    Article  CAS  Google Scholar 

  53. S.A.M. Issa, Radiat. Phys. Chem. 120, 33 (2016)

    Article  CAS  Google Scholar 

  54. M.I. Sayyed, S.I. Qashou, Z.Y. Khattari, J. Alloys Compd. 696, 632 (2017)

    Article  CAS  Google Scholar 

  55. A.A.A. Darwish, S.A.M. Issa, M.M. El-Nahass, Synth. Met. 215, 200 (2016)

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Physics Department, Faculty of Science, Tanta University, Tanta, 31527, Egypt

    A. M. A. Henaish, M. Mostafa, B. I. Salem & O. M. Hemeda

  2. NANOTECH Center, Ural Federal University, Yekaterinburg, 620002, Russia

    A. M. A. Henaish & I. A. Weinstein

  3. Institute of Physics and Technology, Ural Federal University, Yekaterinburg, 620002, Russia

    Hesham M. H. Zakaly

  4. Faculty of Science, Al-Azhar University, Assuit Branch, Assuit, 71524, Egypt

    Hesham M. H. Zakaly & Shams A. M. Issa

  5. Physics Department, Faculty of Science, University of Tabuk, Tabuk, 71451, Saudi Arabia

    Shams A. M. Issa

Authors
  1. A. M. A. Henaish
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. M. Mostafa
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. B. I. Salem
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Hesham M. H. Zakaly
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Shams A. M. Issa
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. I. A. Weinstein
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. O. M. Hemeda
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Shams A. M. Issa.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Henaish, A.M.A., Mostafa, M., Salem, B.I. et al. Spectral, electrical, magnetic and radiation shielding studies of Mg-doped Ni–Cu–Zn nanoferrites. J Mater Sci: Mater Electron 31, 20210–20222 (2020). https://doi.org/10.1007/s10854-020-04541-x

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10854-020-04541-x

Search

Navigation