Abstract
In this study, CoFe, CoFeP and CoFeCr thin films were electrodeposited at different current densities and the relation between their microstructure and electrical resistivity were studied. In order to characterize deposited films, field emission scanning electron microscope (FE-SEM) equipped with energy dispersive X-ray spectrometer, X-ray diffraction system and four probe-point methods were utilized. The results showed that an increase in the applied current density results in increasing iron, phosphorus and chromium contents in the coatings. FE-SEM and SEM micrographs illustrated that addition of phosphorous and chromium to CoFe changes the surface morphologies. Increasing current density caused formation of BCC (Fe) phase structure along with FCC (Co) phase in CoFe coatings. However, all CoFeP and CoFeCr thin films were consisted of only BCC (Fe). Estimation of crystallite size of the deposited films by Scherrer formula showed that all coatings had nanocrystalline structures and decreasing of crystallite size led to significant increase in electrical resistivity of the films, which was according to “scattering hypothesis”. CoFeP thin films showed higher electrical resistivity than those of CoFe and CoFeCr films.
Similar content being viewed by others
References
S. Mehrizi, M. HeydarzadehSohi, E. Shafahian, A.A. Khangholi, Studies of electrical resistivity and magnetic properties of nanocrystalline CoFeCu thin films electrodeposited from citrate-added baths. J. Mater. Sci. Mater. Electron. 23, 1174–1181 (2012)
P.C. Andricacos, N. Robertson, Future directions in electroplated materials for thin-film recording heads. IBM J. Res. Dev. 42, 671–680 (1998)
E. Kalu, Properties of nanocrystalline electrodeposited CoFeP alloy with low phosphorus content. J. Solid State Electrochem. 11, 1145–1156 (2007)
G. Herzer, Grain size dependence of coercivity and permeability in nanocrystalline feromagnets. IEEE Trans. Magn. 26, 1397–1402 (1990)
T. Osaka, T. Yokoshima, T. Nakanishi, Effects of impurities on resistivity of electrodeposited high-BsCoNiFe-based soft magnetic thin films. IEEE Trans. Magn. 37, 1761–1763 (2001)
T. Osaka, Electrodeposition of highly functional thin films for magnetic recording devices of the next century. Electrochim. Acta 45, 3311–3321 (2000)
P. Wissmann, H. Ulrich Finzel, Electrical resistivity of thin metal films, 7th edn. (Springer, Berlin, 2007)
Y. Zhang, D.G. Ivey, Electroplating of nanocrystalline CoFeNi soft magnetic thin films from a stable citrate-based bath. Chem. Mater. 16, 1189–1194 (2004)
S. Mehrizi, M. Heydarzadeh Sohi, S.A. Seyyed Ebrahimi, Study of microstructure and magnetic properties of electrodeposited nanocrystalline CoFeNiCu thin films. Surf. Coat. Technol. 205, 4757–4763 (2011)
A. Brenner, Electrodeposition of Alloys (Academic Press Inc., Waltham, 1963)
H. Adelkhania, M.R. Arshadi, Properties of Fe–Ni–Cr alloy coatings by using direct and pulse current electrodeposition. J. Alloys Compd. 476, 234–237 (2009)
B. Crozier, Q. Liu, D.G. Ivey, Formation and transformation of meta stable phases during electrodeposition and annealing of cobalt–iron alloy films. J. Mater. Sci. Mater. Electron. 22, 614–625 (2011)
T. Yokoshima, K. Imai, T. Hiraiwa, T. Osaka, Preparation of high-Bs Co–Fe soft magnetic thin films by electrodeposition. IEEE Trans. Magn. 40, 2332–2334 (2004)
Acknowledgments
The authors would like to thank the University of Tehran and the Iranian Nanotechnology Initiative Council for financial support of this research.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Taslimi, H., Heydarzadeh Sohi, M., Mehrizi, S. et al. Studies of the effects of addition of P and Cr on microstructure and electrical resistivity of nanocrystalline CoFe thin films. J Mater Sci: Mater Electron 26, 2962–2968 (2015). https://doi.org/10.1007/s10854-015-2783-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-015-2783-z