The effect of Zn/Ca ratio on the microstructure, texture and mechanical properties of dilute Mg–Zn–Ca–Mn alloys that exhibit superior strength

  • Metals & corrosion
  • Published:
Journal of Materials Science Aims and scope Submit manuscript

Abstract

The microstructure, texture and mechanical properties of a series of Mg–Zn–Ca–Mn alloys with three Zn/Ca ratios (2.63, 1.22 and 0.53, by weight ratio) were investigated. The dominant second phase changed from MgZn to Ca2Mg6Zn3 as the Zn/Ca ratio decreased from 2.63 to 1.22. With decreasing Zn/Ca ratio, the grain size of the as-cast alloys was significantly decreased, accompanied by an increase in the volume fraction of second phase. For as-extruded Mg–1.4Zn–2.6Ca–0.5Mn, the finest (~ 0.36 μm) recrystallized grain structures, containing both fine MgZn2 precipitates and α-Mn particles, were obtained at an extrusion speed of 0.01 mm/s. The texture of the deformed structure was more intense (~ 30.39 mud) relative to the recrystallized region (~ 8.33 mud). As the Zn/Ca ratio decreased, basal plane texture was weakened deriving from grain refinement following recrystallization. Superior mechanical properties with a yield strength of ~ 387.8 MPa and ultimate tensile strength of ~ 409.2 MPa were achieved in the Mg–1.4Zn–2.6Ca–0.5Mn alloy extruded at 270 °C at an extrusion speed of 0.01 mm/s. A number of factors were determined to contribute to strengthening including Hall–Petch effects from the fine recrystallized grains (contribution ~ 58.7%), dislocation strengthening of the deformed region (contribution ~ 29.3%) and Orowan strengthening (contribution ~ 12%).

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Figure 1
Figure 2
Figure 3
Figure 4
Figure 5
Figure 6
Figure 7
Figure 8
Figure 9
Figure 10
Figure 11
Figure 12
Figure 13

Similar content being viewed by others

Data availability

The raw/processed data required to reproduce these findings cannot be shared at this time due to technical or time limitations.

References

  1. Pan H, Qin G, Huang Y, Ren Y, Sha X, Han X, Liu ZQ, Li C, Wu X, Chen H, He C, Chai L, Wang Y, Nie JF (2018) Development of low-alloyed and rare-earth-free magnesium alloys having ultra-high strength. Acta Mater 149:350–363

    Article  CAS  Google Scholar 

  2. Zhang H, Wang HY, Wang JG, Rong J, Zha M, Wang C, Ma PK, Jiang QC (2019) The synergy effect of fine and coarse grains on enhanced ductility of bimodal-structured Mg alloys. J Alloys Compd 780:312–317

    Article  CAS  Google Scholar 

  3. Heng X, Zhang Y, Rong W, Wu Y, Peng L (2019) A super high-strength Mg–Gd–Y–Zn–Mn alloy fabricated by hot extrusion and strain aging. Mater Des 169:107666. https://doi.org/10.1016/j.matdes.2019.107666

    Article  CAS  Google Scholar 

  4. Liu X, Zhang Z, Hu W, Le Q, Bao L, Cui J (2016) Effects of extrusion speed on the microstructure and mechanical properties of Mg–9Gd–3Y–1.5Zn–0.8Zr alloy. J Mater Sci Technol 32:313–319

    Article  Google Scholar 

  5. Jiang HS, Qiao XG, Xu C, Zheng MY, Wu K, Kamado S (2016) Ultrahigh strength as-extruded Mg–10.3Zn–6.4Y–0.4Zr–0.5Ca alloy containing W phase. Mater Des 108:391–399

    Article  CAS  Google Scholar 

  6. Li ZT, Zhang XD, Zheng MY, Qiao XG, Wu K, Xu C, Kamado S (2017) Effect of Ca/Al ratio on microstructure and mechanical properties of Mg–Al–Ca–Mn alloys. Mater Sci Eng A 682:423–432

    Article  CAS  Google Scholar 

  7. Robson JD, Paa-Rai C (2015) The interaction of grain refinement and ageing in magnesium–zinc–zirconium (ZK) alloys. Acta Mater 95:10–19

    Article  CAS  Google Scholar 

  8. Xu SW, Oh-ishi K, Sunohara H, Kamado S (2012) Extruded Mg–Zn–Ca–Mn alloys with low yield anisotropy. Mater Sci Eng A 558:356–365

    Article  CAS  Google Scholar 

  9. Ikeo N, Nishioka M, Mukai T (2018) Fabrication of biodegradable materials with high strength by grain refinement of Mg–0 3 at% Ca alloys. Mater Lett 223:65–68

    Article  CAS  Google Scholar 

  10. Du YZ, Qiao XG, Zheng MY, Wang DB, Wu K, Golovin IS (2016) Effect of microalloying with Ca on the microstructure and mechanical properties of Mg–6 mass%Zn alloys. Mater Des 98:285–293

    Article  CAS  Google Scholar 

  11. Ding HL, Zhang P, Cheng GP, Kamado S (2015) Effect of calcium addition on microstructure and texture modification of Mg rolled sheets. Trans Nonferr Metals Soc 25:2875–2883

    Article  CAS  Google Scholar 

  12. Zhang B, Wang Y, Geng L, Lu C (2012) Effects of calcium on texture and mechanical properties of hot-extruded Mg–Zn–Ca alloys. Mater Sci Eng A 539:56–60

    Article  CAS  Google Scholar 

  13. Jiang MG, Xu C, Nakata T, Yan H, Chen RS, Kamado S (2016) Development of dilute Mg–Zn–Ca–Mn alloy with high performance via extrusion. J Alloys Compd 668:13–21

    Article  CAS  Google Scholar 

  14. Somekawa H, Basha DA, Singh A (2018) Room temperature grain boundary sliding behavior of fine-grained Mg–Mn alloys. Mater Sci Eng A 730:355–362

    Article  CAS  Google Scholar 

  15. Li WJ, Deng KK, Zhang X, Nie KB, Xu FJ (2016) Effect of ultra-slow extrusion speed on the microstructure and mechanical properties of Mg–4Zn–0.5Ca alloy. Mater Sci Eng A 677:367–375

    Article  CAS  Google Scholar 

  16. Kang XK, Nie KB, Deng KK, Guo YC (2019) Effect of extrusion parameters on microstructure, texture and mechanical properties of Mg–1.38Zn–0.17Y–0.12Ca (at%) alloy. Mater Charact 151:137–145

    Article  CAS  Google Scholar 

  17. Tong LB, Zheng MY, Cheng LR, Kamado S, Zhang HJ (2013) Effect of extrusion ratio on microstructure, texture and mechanical properties of indirectly extruded Mg–Zn–Ca alloy. Mater Sci Eng A 569:48–53

    Article  CAS  Google Scholar 

  18. Oh-ishi K, Watanabe R, Mendis CL, Hono K (2009) Age-hardening response of Mg–0.3 at%Ca alloys with different Zn contents. Mater Sci Eng A 526:177–184

    Article  Google Scholar 

  19. Maity S, Sinha A, Bera S (2018) A novel study on mechanically alloyed Al–Mg system by X-ray diffraction technique. Nano Struct Nano Objects 16:63–68

    Article  CAS  Google Scholar 

  20. Levi G, Avraham S, Zilberov A, Bamberger M (2006) Solidification, solution treatment and age hardening of a Mg–1.6 wt% Ca–3.2 wt% Zn alloy. Acta Mater 54:523–530

    Article  CAS  Google Scholar 

  21. Kim SH, Lee JU, Kim YJ, Jung JG, Park SH (2018) Controlling the microstructure and improving the tensile properties of extruded Mg–Sn–Zn alloy through Al addition. J Alloys Compd 751:1–11

    Article  CAS  Google Scholar 

  22. Li CJ, Sun HF, Li XW, Zhang JL, Fang WB, Tan ZY (2015) Microstructure, texture and mechanical properties of Mg–3.0Zn–0.2Ca alloys fabricated by extrusion at various temperatures. J Alloys Compd 652:122–131

    Article  CAS  Google Scholar 

  23. Imandoust A, Barrett CD, Oppedal AL, Whittington WR, Paudel Y, El Kadiri H (2017) Nucleation and preferential growth mechanism of recrystallization texture in high purity binary magnesium-rare earth alloys. Acta Mater 138:27–41

    Article  CAS  Google Scholar 

  24. Park SH, Kim S-H, Kim HS, Yoon J, You BS (2016) High-speed indirect extrusion of Mg–Sn–Al–Zn alloy and its influence on microstructure and mechanical properties. J Alloys Compd 667:170–177

    Article  CAS  Google Scholar 

  25. Zhang A, Kang R, Wu L, Pan H, Xie H, Huang Q, Liu Y, Ai Z, Ma L, Ren Y, Qin G (2019) A new rare-earth-free Mg–Sn–Ca–Mn wrought alloy with ultra-high strength and good ductility. Mater Sci Eng A 754:269–274

    Article  CAS  Google Scholar 

  26. Kang JW, Wang CJ, Deng KK, Nie KB, Bai Y, Li WJ (2017) Microstructure and mechanical properties of Mg–4Zn–0.5Ca alloy fabricated by the combination of forging, homogenization and extrusion process. J Alloys Compd 720:196–206

    Article  CAS  Google Scholar 

  27. Du YZ, Qiao XG, Zheng MY, Wu K, Xu SW (2015) The microstructure, texture and mechanical properties of extruded Mg–5.3Zn–0.2Ca–0.5Ce (wt%) alloy. Mater Sci Eng A 620:164–171

    Article  Google Scholar 

  28. Guo YC, Nie KB, Kang XK, Deng KK, Han JG, Zhu ZH (2019) Achieving high-strength magnesium matrix nanocomposite through synergistical effect of external hybrid (SiC + TiC) nanoparticles and dynamic precipitated phase. J Alloys Compd 771:847–856

    Article  CAS  Google Scholar 

  29. Sun XF, Wang CJ, Deng KK, Nie KB, Zhang XC, Xiao XY (2018) High strength SiCp/AZ91 composite assisted by dynamic precipitated Mg17Al12 phase. J Alloys Compd 732:328–335

    Article  CAS  Google Scholar 

  30. Ando D, Koike J, Sutou Y (2010) Relationship between deformation twinning and surface step formation in AZ31 magnesium alloys. Acta Mater 58:4316–4324

    Article  CAS  Google Scholar 

  31. Barnett MR (2007) Twinning and the ductility of magnesium alloys: part II. “Contraction” twins. Mater Sci Eng A 464:8–16

    Article  Google Scholar 

Download references

Acknowledgements

This work was supported by the National Natural Science Foundation of China [Grant Nos. 51771129, 51401144 and 51771128]; the Program for the Outstanding Innovative Teams of Higher Learning Institutions of Shanxi; the Natural Science Foundation of Shanxi Province [Grant Nos. 2015021067 and 201601D011034]; the Projects of International Cooperation in Shanxi [Grant No. 201703D421039] and funded by China Scholarship Council.

Author information

Authors and Affiliations

  1. College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan, 030024, People’s Republic of China

    Kaibo Nie, Zhihao Zhu, Kunkun Deng & Jungang Han

  2. School of Materials Science and Engineering, UNSW Australia, Kensington, NSW, 2052, Australia

    Paul Munroe

Authors
  1. Kaibo Nie
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Zhihao Zhu
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Paul Munroe
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Kunkun Deng
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Jungang Han
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Kaibo Nie.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Nie, K., Zhu, Z., Munroe, P. et al. The effect of Zn/Ca ratio on the microstructure, texture and mechanical properties of dilute Mg–Zn–Ca–Mn alloys that exhibit superior strength. J Mater Sci 55, 3588–3604 (2020). https://doi.org/10.1007/s10853-019-04174-4

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10853-019-04174-4

Search

Navigation