Electrospinning of poly (ε-caprolactone-co-lactide)/Pluronic blended scaffolds for skin tissue engineering

  • Published:
Journal of Materials Science Aims and scope Submit manuscript

Abstract

For skin tissue engineering, an ideal scaffold should mimic the natural extracellular matrix of the native skin. In this study, we reported a novel elastic sub-micron fiber scaffold blending poly (ε-caprolactone-co-lactide) (PLCL) and Pluronic at different ratios by electrospinning. PLCL and Pluronic were co-electrospun with the ratio of 100/0, 99/1, 95/5, 90/10, 85/15, and 75/25. These scaffolds were evaluated in terms of fiber morphology, mechanical properties, and hydrophilicity for the purpose of culturing adipose-derived stem cells (ADSCs). Cell attachment and proliferation on the scaffolds were also evaluated to demonstrate the potential of serving as a skin graft. The results indicated that all of the electrospun fibers possessed smooth surface textures and interconnected porous structures with the average diameter ranging from approximately 750–1140 nm. The higher tensile strength was observed in 95/5 and 90/10 PLCL/Pluronic blended membranes, while further incorporation of Pluronic almost has no effect on tensile strength. The water contact angle was 85° for scaffold with the ratio of 99/1, while 0° for 90/10, 85/15, and 75/25. In addition, the elevation of Pluronic content in composition resulted in a corresponding increase in swelling behavior. Compared with PLCL, the better cell adhesion and proliferation potential of ADSCs was exhibited on all PLCL/Pluronic blended scaffolds. ADSCs on the blended scaffolds were highly elongated and well integrated with the surrounding fibers, indicating the good cytocompatibility of PLCL/Pluronic scaffolds. Thus, these blended scaffolds have the potentially high application prospect in the field of skin tissue engineering.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7

Similar content being viewed by others

References

  1. Lugo LM, Lei P, Andreadis ST (2011) Vascularization of the dermal support enhances wound re-epithelialization by in situ delivery of epidermal keratinocytes. Tissue Eng Part A 17:665–675

    Article  Google Scholar 

  2. Dornseifer U, Lonic D, Gerstung TI, Herter F, Fichter AM et al (2011) The ideal split-thickness skin graft donor-site dressing: a clinical comparative trial of a modified polyurethane dressing and aquacel. Plast Reconstr Surg 128:918–924

    Article  Google Scholar 

  3. Venugopal J, Ramakrishna S (2005) Biocompatible nanofiber matrices for the engineering of a dermal substitute for skin regeneration. Tissue Eng 11:847–854

    Article  Google Scholar 

  4. Lam MT, Nauta A, Meyer NP, Wu JC, Longaker MT (2013) Effective delivery of stem cells using an extracellular matrix patch results in increased cell survival and proliferation and reduced scarring in skin wound healing. Tissue Eng Part A 19:738–747

    Article  Google Scholar 

  5. Christopherson GT, Song H, Mao HQ (2009) The influence of fiber diameter of electrospun substrates on neural stem cell differentiation and proliferation. Biomaterials 30:556–564

    Article  Google Scholar 

  6. Sahay R, Kumar PS, Sridhar R, Sundaramurthy J, Venugopal J et al (2012) Electrospun composite nanofibers and their multifaceted applications. J Mater Chem 22:12953–12971

    Article  Google Scholar 

  7. Kluger PJ, Wyrwa R, Weisser J, Maierle J, Votteler M et al (2010) Electrospun poly (d/l-lactide-co-l-lactide) hybrid matrix: a novel scaffold material for soft tissue engineering. J Mater Sci Mater Med 21:2665–2671

    Article  Google Scholar 

  8. Jeong SI, Lee AY, Lee YM, Shin H (2008) Electrospun gelatin/poly(l-lactide-co-epsilon-caprolactone) nanofibers for mechanically functional tissue-engineering scaffolds. J Biomater Sci Polym Ed 19:339–357

    Article  Google Scholar 

  9. Lee J, Tae G, Kim YH, Park IS, Kim SH et al (2008) The effect of gelatin incorporation into electrospun poly(l-lactide-co-3-caprolactone) fibers on mechanical properties and cytocompatibility. Biomaterials 29:1279–1872

    Google Scholar 

  10. Li S, Sun B, Li XR, Yuan XY (2008) Characterization of electrospun core/shell poly(vinyl pyrrolidone)/poly(l-lactide-co-epsilon-caprolactone) fibrous membranes and their cytocompatibility in vitro. J Biomater Sci Polym Ed 19:245–258

    Article  Google Scholar 

  11. Lim JI, Yu B, Lee YK (2008) Fabrication of collagen hybridized elastic PLCL for tissue engineering. Biotechnol Lett 30:2085–2090

    Article  Google Scholar 

  12. Batrakova EV, Kabanov AV (2008) Pluronic block copolymers: evolution of drug delivery concept from inert nanocarriers to biological response modifiers. J Control Release 130:98–106

    Article  Google Scholar 

  13. Nalbandian RM, Henry RL, Balko KW, Adams DV, Neuman NR (1987) Pluronic F-127 gel preparation as an artificial skin in the treatment of third-degree burns in pigs. J Biomed Mater Res 21:1135–1148

    Article  Google Scholar 

  14. DiBiase MD, Rhodes CT (1991) Investigations of epidermal growth factor in semisolid formulations. Pharm Acta Helv 66:165–169

    Google Scholar 

  15. Singh-Joy SD, McLain VC (2008) Safety assessment of poloxamers 101, 105, 108, 122, 123, 124, 181, 182, 183, 184, 185, 188, 212, 215, 217, 231, 234, 235, 237, 238, 282, 284, 288, 331, 333, 334, 335, 338, 401, 402, 403, and 407, poloxamer 105 benzoate, and poloxamer 182 dibenzoate as used in cosmetics. Int J Toxicol 27:93–128

    Article  Google Scholar 

  16. Hsu SH, Leu YL, Hu JW, Fang JY (2009) Physicochemical characterization and drug release of thermosensitive hydrogels composed of a hyaluronic acid/Pluronic F127 graft. Chem Pharm Bull 57:453–458

    Article  Google Scholar 

  17. Miao Y-E, Zhu H, Chen D, Wang RY, Tjiu WW, Liu TX (2012) Electrospun fibers of biopolymers/layered double hydroxide nanocomposites as effective drug delivery systems. Mater ChemPhys 134:623–630

    Google Scholar 

  18. Ishaug-Riley SL, Okun LE, Prado G, Applegate MA, Ratcliffe A (1999) Human articular chondrocyte adhesion and proliferation on synthetic biodegradable polymer films. Biomaterials 20:2245–2256

    Article  Google Scholar 

  19. Almeida H, Amaral MH, Lobao P, Lobo JMS (2012) Pluronic F-127 and Pluronic lecithin organogel (PLO): main features and their applications in topical and transdermal administration of drugs. J Pharm Pharm Sci 15:592–605

    Google Scholar 

  20. Alsmadi NA, Wadajkar AS, Cui WN, Nguyen KT (2011) Effects of surfactants on properties of polymer-coated magnetic nanoparticles for drug delivery application. J Nanopart Res 13:7177–7186

    Article  Google Scholar 

  21. Kumbar SG, Nukavarapu SP, James R, Nair LS, Laurencin CT (2008) Electrospun poly(lactic acid-co-glycolic acid) scaffolds for skin tissue engineering. Biomaterials 29:4100–4107

    Article  Google Scholar 

  22. Teo WE, Ramakrishna S (2006) A review on electrospinning design and nanofibre assemblies. Nanotechnology 17:R89–R106

    Article  Google Scholar 

  23. Laurent A, Mistretta F, Bottigioli D, Dahel K, Goujon C et al (2007) Echographic measurement of skin thickness in adults by high frequency ultrasound to assess the appropriate microneedle length for intradermal delivery of vaccines. Vaccine 25:6423–6430

    Article  Google Scholar 

  24. Lin HY, Kuo YJ, Chang SH, Ni TS (2013) Characterization of electrospun nanofiber matrices made of collagen blends as potential skin substitutes. Biomed Mater 8:025009

    Article  Google Scholar 

  25. Zhang YZ, Venugopal J, Huang ZM, Lim CT, Ramakrishna S (2006) Crosslinking of the electrospun gelatin nanofibers. Polymer 46:2911–2917

    Article  Google Scholar 

  26. Nagiah N, Madhavi L, Anitha R, Srinivasan NT, Sivagnanam UT (2013) Electrospinning of poly (3-hydroxybutyric acid) and gelatin blended thin films: fabrication, characterization, and application in skin regeneration. Polym Bull 70:2337–2358

    Article  Google Scholar 

  27. Jin GR, Prabhakaran MP, Ramakrishna S (2011) Stem cell differentiation to epidermal lineages on electrospun nanofibrous substrates for skin tissue engineering. Acta Biomater 7:3113–3122

    Article  Google Scholar 

  28. Jang BS, Jung Y, Kwon IK, Mun CH, Kim SH (2012) Fibroblast culture on poly(l-lactide-co-ε-caprolactone) an electrospun nanofiber sheet. Macromol Res 20:1234–1242

    Article  Google Scholar 

  29. Shalumon KT, Anulekha KH, Chennazhi KP, Tamura H, Nair SV et al (2011) Fabrication of chitosan/poly(caprolactone) nanofibrous scaffold for bone and skin tissue engineering. Int J Biol Macromol 48:571–576

    Article  Google Scholar 

  30. Qin YM (2008) The gel swelling properties of alginate fibers and their applications in wound management. Polym Adv Technol 19:6–14

    Article  Google Scholar 

  31. Yoshimura H, Muneta T, Nimura A, Yokoyama A, Koga H et al (2007) Comparison of rat mesenchymal stem cells derived from bone marrow, synovium, periosteum, adipose tissue, and muscle. Cell Tissue Res 327:449–462

    Article  Google Scholar 

  32. Altman AM, Yan YS, Matthias N, Bai XW, Rios C et al (2009) IFATS collection: human adipose-derived stem cells seeded on a silk fibroin-chitosan scaffold enhance wound repair in a murine soft tissue injury model. Stem Cells 27:250–258

    Article  Google Scholar 

  33. Prabhakaran MP, Venugopal J, Ramakrishna S (2009) Electrospun nanostructured scaffolds for bone tissue engineering. Acta Biomater 5:2884–2893

    Article  Google Scholar 

  34. Cao D, Wu YP, Fu ZF, Tian YA, Li CJ et al (2011) Cell adhesive and growth behavior on electrospun nanofibrous scaffolds by designed multifunctional composites. Colloid Surf B Biointerfaces 84:26–34

    Article  Google Scholar 

  35. Raveendran R, Bhuvaneshwar G, Sharma CP (2013) In vitro cytotoxicity and cellular uptake of curcumin-loaded Pluronic/polycaprolactone micelles in colorectal adenocarcinoma cells. J Biomater Appl 27:811–827

    Article  Google Scholar 

  36. Akash MS, Rehman K, Li N, Gao JQ, Sun H et al (2012) Sustained delivery of IL-1Ra from Pluronic F127-based thermosensitive gel prolongs its therapeutic potentials. Pharm Res 29:3475–3485

    Article  Google Scholar 

  37. Oh KS, Song JY, Cho SH, Lee BS, Kim SY et al (2010) Paclitaxel-loaded pluronic nanoparticles formed by a temperature-induced phase transition for cancer therapy. J Control Release 148:344–350

    Article  Google Scholar 

  38. Lee SH, Lee JE, Baek WY, Lim JO (2004) Regional delivery of vancomycin using Pluronic F-127 to inhibit methicillin resistant Staphylococcus aureus (MRSA) growth in chronic otitis media in vitro and in vivo. J Control Release 96:1–7

    Article  Google Scholar 

  39. Dos Santos CA, Ribeiro GB, Knirsch MC, Pessoa Junior A, Penna TC (2011) Influence of Pluronic® F68 on ceftazidime biological activity in parenteral solutions. J Pharm Sci 100:715–720

    Article  Google Scholar 

  40. Raval A, Parmar A, Raval A, Bahadur P (2012) Preparation and optimization of media using Pluronic® micelles for solubilization of sirolimus and release from the drug eluting stents. Colloids Surf B Biointerfaces 93:180–187

    Article  Google Scholar 

  41. Bölgen N, Vargel I, Korkusuz P, Menceloğlu YZ, Pişkin E (2007) In vivo performance of antibiotic embedded electrospun PCL membranes for prevention of abdominal adhesions. J Biomed Mater Res B Appl Biomater 81:530–543

    Article  Google Scholar 

  42. Liu S, Qin M, Hu C, Wu F, Cui W et al (2013) Tendon healing and anti-adhesion properties of electrospun fibrous membranes containing bFGF loaded nanoparticles. Biomaterials 34:4690–4701

    Article  Google Scholar 

Download references

Acknowledgements

We thank Yi-Mei Liu and Bi-Jun Zhu from biomedical research center for technical support, Dr. Zhou-Jun Wang from department of macromolecular science, and the laboratory of advanced materials for his guidance through the work, Dr. Fei Liang from Department of Statistics teaching and research for the assistance of Statistical Analysis.

Author information

Authors and Affiliations

  1. Department of Orthopaedic Surgery, Shanghai Jiao Tong University Affiliated Sixth People’s Hospital, Shanghai, 200233, China

    Ning-hua Liu & Hui Sun

  2. Department of Orthopaedics Surgery, Kunshan Traditional Chinese Medical Hospital, Suzhou, 215300, China

    Ning-hua Liu & Feng Xu

  3. Department of Orthopaedics Surgery, Zhongshan Hospital, Fudan University, Shanghai, 200032, China

    Jian-feng Pan

  4. State Key Laboratory of Molecular Engineering of Polymers, Department of Macromolecular Science, Fudan University, Shanghai, 200433, China

    Yue-E Miao & Tian-xi Liu

Authors
  1. Ning-hua Liu
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Jian-feng Pan
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Yue-E Miao
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Tian-xi Liu
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Feng Xu
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Hui Sun
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Hui Sun.

Additional information

Ning-Hua Liu and Jian-Feng Pan contribute to this article equally.

Electronic supplementary material

Below is the link to the electronic supplementary material.

Supplementary material 1 (AVI 273 kb)

Supplementary material 2 (AVI 348 kb)

Supplementary material 3 (AVI 671 kb)

Supplementary material 4 (AVI 465 kb)

Supplementary material 5 (AVI 1460 kb)

Supplementary material 6 (AVI 922 kb)

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Liu, Nh., Pan, Jf., Miao, YE. et al. Electrospinning of poly (ε-caprolactone-co-lactide)/Pluronic blended scaffolds for skin tissue engineering. J Mater Sci 49, 7253–7262 (2014). https://doi.org/10.1007/s10853-014-8432-8

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10853-014-8432-8

Keywords

Search

Navigation