The problem of the failure of an elastic rod under cyclic tension/compression is solved. Changes in the state of the rod in each load cycle are modeled. The failure criterion is stated and the cyclic durabilities corresponding to the given initial amplitude load are found. The fatigue curves for EI867 high-temperature oxidation-resistant nickel alloy and D16AT aluminum-based light alloy are plotted and compared with experimental curves.
Similar content being viewed by others
References
N. N. Afanas’ev, Statistical Theory of the Fatigue Strength of Metals [in Russian], Izd. AN USSR, Kyiv (1953).
N. M. Belyaev, Strength of Materials [in Russian], GIFML, Moscow (1959).
V. P. Golub and A. D. Pogrebnyak, High-Temperature Failure of Materials under Cyclic Loading [in Russian], Naukova Dumka, Kyiv (1994).
V. P. Kogaev, N. A. Makhutov, and A. P. Gusenkov, Design of Machine Parts and Structures for Strength and Durability (Handbook) [in Russian], Mashinostroenie, Moscow (1985).
Yu. M. Kobzar’, “Assessment of the fatigue durability of smooth cylindrical rods under uniaxial symmetric tension/compression,” Av.-Kosm. Tekhn. Tekhnol., 126, No. 9, 6–14 (2015).
O. M. Matveev, Mechanics and Theory of Relativity [in Ukrainian], Vyshcha Shkola, Kyiv (1993).
V. T. Troshchenko and L. A. Sosnovskii, “Statistical theory of fractuee in complex state of stress. Communications 1 and 2,” Strength of Materials, 11, No. 7, 669–678 (1979).
V. T. Troshchenko and L. A. Sosnovskii, Fatigue Resistance of Metals and Alloys: Handbook, Naukova Dumka, Kyiv (1987).
J. C. Fisher and J. H. Hollomen, “A statistical theory of fracture,” J. Met. Technol., 14, No. 5, 1–16 (1947).
V. P. Golub and A. V. Plashchynska, “A phenomenological model of fatigue crack growth in perfectly plastic infinite plates under completely reversed uniaxial loading,” Int. Appl. Mech., 41, No. 12, 1426–1436 (2005).
M. Klesnil and H. Lukas, Fatigue of Metallic Materials, Academia, Prague (1980).
S. T. Rolfe and J. M. Barsom, Fracture and Fatigue Control in Structure. Application of Fracture Mechanics, Prentice-Hall, New Jersey (1977).
S. V. Serensen, “Fatigue failure criteria in large member of cycles,” JSME Semi Int. Symp. Proc., No. 1, 91–95 (1967).
E. Z. Stowell, “A study of the energy criterion for fatigue,” Nucl. Eng. Design, 3, No. 1, 32–40 (1966).
T. Tanaka, “Effect of the superimposed stress of high frequency on fatigue strength,” Bull. JSME, 11, No. 43, 77–83 (1968).
W. Veibull, “A statistical theory of the strength of materials,” Proc. Ray. Swed. Inst. Eng. Res., No. 151, 5–48 (1939).
Author information
Authors and Affiliations
Corresponding author
Additional information
This study was sponsored by the budget program “Support for Priority Areas of Scientific Research” (KPKVK 6541230).
Translated from Prikladnaya Mekhanika, Vol. 58, No. 1, pp. 102–114, January–February 2022.
Rights and permissions
About this article
Cite this article
Kobzar, Y.M. Modeling the Multicyclic Fatigue Failure of Rods under Symmetrical Tension/Compression. Int Appl Mech 58, 91–101 (2022). https://doi.org/10.1007/s10778-022-01139-0
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10778-022-01139-0