Abstract
The primary purpose of this research is investigating the effect of increasing temperature on mechanical properties and formability of Al 5083 produced by equal channel angular rolling (ECAR) process. The present work also aims to study the feasibility of increasing temperature as an approach for solving the ductility problem of ultrafine-grained Al 5083, although some strength of the material might be sacrificed. So, the quantitative and qualitative analysis of the effect of temperature increase on mechanical properties and formability has been done. In this paper, the ECAR process has been performed at three different temperatures (i.e., 25 °C, 200 °C, and 300 °C(. Then, the investigation of mechanical properties such as yield strength, ultimate tensile strength, and microhardness after each pass of the ECAR at different temperatures has been performed. The results showed that by applying the ECAR process at a specified temperature, the mechanical and microhardness properties of the samples improved, while elongation to fracture reduced. At ambient temperature, and after the 3rd pass of the ECAR process, yield strength, ultimate tensile strength, and microhardness compared with the annealed sample increased by 94%, 19%, and 52%, respectively. Also, the mechanical properties of samples after the ECAR process in a specified pass at different temperatures have been evaluated. The obtained results showed that by increasing temperature, the yield strength, ultimate tensile strength, and microhardness of the samples decreased, but the elongation to fracture as well as the forming limit diagram (FLD) improved. The results illustrated that by applying the ECAR process at a specified temperature, the level of the FLDs moved downward. Also, the FLDs after the 3rd pass of the ECAR at different temperature have been compared. The results showed that the FLD0 (the major forming limit strain in-plane strain mode) at a temperature of 200 °C and 300 °C compared with the ambient temperature increased by 5% and 20%, respectively.
Similar content being viewed by others
References
Rahmatabadi D, Hashemi R, Mohammadi B, Shojaee T (2017) Experimental evaluation of the plane stress fracture toughness for ultra-fine grained aluminum specimens prepared by accumulative roll bonding process. Mater Sci Eng A 708:301–310
Rahmatabadi D, Hashemi R (2017) Experimental evaluation of forming limit diagram and mechanical properties of nano/ultra-fine grained aluminum strips fabricated by accumulative roll bonding. Int J Mater Res 108(12):1036–1044
Javidikia M, Hashemi R (2017) Mechanical anisotropy in ultra-fine grained aluminium tubes processed by parallel-tubular-channel angular pressing. Mater Sci Technol 33(18):2265–2273
Rahmatabadi D, Tayyebi M, Hashemi R, Faraji G (2018) Microstructure and mechanical properties of Al/Cu/Mg laminated composite sheets produced by the ARB process. Int J Miner Metall Mater 25(5):564–572
Rahimi H, Sedighi M, Hashemi R (2018) Forming limit diagrams of fine-grained Al 5083 produced by equal channel angular rolling process. Proc Inst Mech Eng L J Mater Des Appl 232(11):922–930
Chung YH, Park JW, Lee KH (2006) An analysis of accumulated deformation in the equal channel angular rolling (ECAR) process. Met Mater Int 12(4):289
Lee J-C, Seok H-K, Suh J-Y (2002) Microstructural evolutions of the Al strip prepared by cold rolling and continuous equal channel angular pressing. Acta Mater 50(16):4005–4019
Nam C, Han J, Chung Y, Shin M (2003) Effect of precipitates on microstructural evolution of 7050 Al alloy sheet during equal channel angular rolling. Mater Sci Eng A 347(1-2):253–257
Han J-H, Seok H-K, Chung Y-H, Shin M-C, Lee J-C (2002) Texture evolution of the strip cast 1050 Al alloy processed by continuous confined strip shearing and its formability evaluation. Mater Sci Eng A 323(1-2):342–347
Mahmoodi M, Sedighi M, Tanner DA (2014) Experimental study of process parameters’ effect on surface residual stress magnitudes in equal channel angular rolled aluminium alloys. Proc Inst Mech Eng B J Eng Manuf 228(12):1592–1598
Cheng YQ, Chen ZH, Xia WJ (2007) Drawability of AZ31 magnesium alloy sheet produced by equal channel angular rolling at room temperature. Mater Charact 58(7):617–622
Cheng YQ, Chen ZH, Xia WJ, Zhou T (2007) Effect of channel clearance on crystal orientation development in AZ31 magnesium alloy sheet produced by equal channel angular rolling. J Mater Process Technol 184(1-3):97–101
Cheng YQ, Chen ZH, Xia WJ (2007) Effect of crystal orientation on the ductility in AZ31 Mg alloy sheets produced by equal channel angular rolling. J Mater Sci 42(10):3552–3556
Cheng YQ, Chen ZH, Xia WJ, Zhou T (2008) Improvement of drawability at room temperature in AZ31 magnesium alloy sheets processed by equal channel angular rolling. J Mater Eng Perform 17(1):15–19
Hassani F, Ketabchi M (2011) Nano grained AZ31 alloy achieved by equal channel angular rolling process. Mater Sci Eng A 528(21):6426–6431
Habibi A, Ketabchi M, Eskandarzadeh M (2011) Nano-grained pure copper with high-strength and high-conductivity produced by equal channel angular rolling process. J Mater Process Technol 211(6):1085–1090
Noor SV, Eivani AR, Jafarian HR, Mirzaei M (2016) Inhomogeneity in microstructure and mechanical properties during twist extrusion. Mater Sci Eng A 652:186–191
Teymoory P, Zarei-Hanzaki A, Farabi E, Monajati H, Abedi HR (2018) Grain refinement through shear banding in severely plastic deformed A206 aluminum alloy. Adv Eng Mater 20(1):1700502
Kalahroudi FJ, Eivani AR, Jafarian HR, Amouri A, Gholizadeh R (2016) Inhomogeneity in strain, microstructure and mechanical properties of AA1050 alloy during twist extrusion. Mater Sci Eng A 667:349–357
Mahdavian MM, Khatami-Hamedani H, Abedi HR (2017) Macrostructure evolution and mechanical properties of accumulative roll bonded Al/Cu/Sn multilayer composite. J Alloys Compd 703:605–613
Valipour S, Eivani AR, Jafarian HR, Seyedein SH, Aboutalebi MR (2016) Effect of pre-deformation thermomechanical processing on the development of ultrafine grain structure during equal channel angular extrusion. Mater Des 89:377–384
Naka T, Torikai G, Hino R, Yoshida F (2001) The effects of temperature and forming speed on the forming limit diagram for type 5083 aluminum–magnesium alloy sheet. J Mater Process Technol 113(1-3):648–653
Hashemi R, Faraji G, Abrinia K, Dizaji AF (2010) Application of the hydroforming strain-and stress-limit diagrams to predict necking in metal bellows forming process. Int J Adv Manuf Technol 46(5-8):551–561
Ozturk F, Lee D (2005) Experimental and numerical analysis of out-of-plane formability test. J Mater Process Technol 170(1):247–253
Zhan M, Li Y, Chen W, Chen W (2007) Microstructure and mechanical properties of Mg–Al–Zn alloy sheets severely deformed by accumulative roll-bonding. J Mater Sci 42(22):9256–9261
Saito Y, Tsuji N, Utsunomiya H, Sakai T, Hong R (1998) Ultra-fine grained bulk aluminum produced by accumulative roll-bonding (ARB) process. Scr Mater 39(9):1221–1227
Rahmatabadi D, Mohammadi B, Hashemi R, Shojaee T (2018) An experimental study of fracture toughness for nano/ultrafine grained Al5052/Cu multilayered composite processed by accumulative roll bonding. J Manuf Sci Eng 140(10):101001–101001-11
Rahmatabadi D, Tayyebi M, Hashemi R, Faraji G (2018) Evaluation of microstructure and mechanical properties of multilayer Al5052–Cu composite produced by accumulative roll bonding. Powder Metall Met Ceram 57(3):144–153
McQueen H, Jonas J (1975) Recovery and recrystallization during high temperature deformation. In: Treatise on Materials Science & Technology. Elsevier, pp 393–493
Rajaram G, Kumaran S, Rao TS (2010) High temperature tensile and wear behaviour of aluminum silicon alloy. Mater Sci Eng A 528(1):247–253
Shaarbaf M, Toroghinejad MR (2008) Nano-grained copper strip produced by accumulative roll bonding process. Mater Sci Eng A 473(1):28–33
Alizadeh M, Samiei M (2014) Fabrication of nanostructured Al/Cu/Mn metallic multilayer composites by accumulative roll bonding process and investigation of their mechanical properties. Mater Des 56:680–684
Rahmatabadi D, Tayyebi M, Sheikhi A, Hashemi R (2018) Fracture toughness investigation of Al1050/Cu/MgAZ31ZB multi-layered composite produced by accumulative roll bonding process. Mater Sci Eng A 734:427–436
Naseri M, Hassani A, Tajally M (2015) Fabrication and characterization of hybrid composite strips with homogeneously dispersed ceramic particles by severe plastic deformation. Ceram Int 41(3):3952–3960
F. J. Humphreys, M. Hatherly, Recrystallization and related annealing phenomena: Elsevier, 2012.
Sedighi M, Mahmoodi M (2012) Residual stresses evaluation in equal channel angular rolled Al 5083 by IHD technique: investigation of two calculation methods. Mater Manuf Process 28(1):85–90
Mahmoodi M, Sedighi M, Tanner DA (2012) Investigation of through thickness residual stress distribution in equal channel angular rolled Al 5083 alloy by layer removal technique and X-ray diffraction. Mater Des 40:516–520
Hakimian H, Sedighi M, Asgari A (2016) Experimental and numerical study on the ECARed magnesium AZ31 alloy. Mech Ind 17(1):110–116
Reihanian M, Hadadian FK, Paydar MH (2014) Fabrication of Al–2 vol% Al2O3/SiC hybrid composite via accumulative roll bonding (ARB): an investigation of the microstructure and mechanical properties. Mater Sci Eng A 607:188–196
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher’s note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Bozcheloei, J.E., Sedighi, M. & Hashemi, R. The effect of temperature on the mechanical properties and forming limit diagram of Al 5083 produced by equal channel angular rolling. Int J Adv Manuf Technol 105, 4389–4400 (2019). https://doi.org/10.1007/s00170-019-04586-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00170-019-04586-1