In the present paper, the influence of α-Al2O3 seeds and sintering methods on elongated grain growth and fracture toughness is investigated. The preparation of alumina ceramics started with commercial aluminum hydroxide. Abrasives were introduced to the starting materials by wet-grinding of high-purity alumina milling balls. Abrasives, playing the role of seeds, lowered the transformation temperature of aluminum hydroxide to alumina. Microstructures with elongated grains were developed by hot-pressing for the above calcined powders containing α-Al2O3 seeds, and alumina grain shapes changed with the amount of seeds introduced. However, only equiaxed grains were observed for the samples pressureless sintered. Fracture toughness of the alumina ceramics was dramatically improved by elongated grains. For the sample hot-pressed at 1600°C for 2 h under 40 MPa pressure, fracture toughness reached 7.1 MPa·m1/2, which is much higher than that of normal alumina ceramics without elongated grains. In addition, high flexural strength of 630 MPa for the hot-pressed samples was also obtained.
Similar content being viewed by others
References
Graule, T. J., Baader, F. H., Gauckler, L. J., Shaping of ceramic green compacts from suspensions by enzyme catalyzed reaction, Cfi/ber. DKG, 1994, 71: 317–323.
Alford, N. M., Brichall, J. D., Kedall, K., High strength ceramic through colloidal control to remove defects, Nature, 1987, 330: 51–53.
Xue, L. A., Chen, I. W., Influence additives on the γ- to α-transformation of alumina, J. Mater. Sci. Lett., 1992, 11: 443–445.
Park, C. W., Yoon, D. Y., Abnormal grain growth in alumina with anorthic liquid and the effect of MgO addition, J. Am. Ceram. Soc., 2002, 85(6): 1585–1593.
Riu, D. H., Kong, Y. M., Kin, H. E., Effect of Cr2O3 addition on microstructural evolution and mechanical properties of Al2O3, Journal of the European Ceramic Society, 2000, (20): 1475–1481.
Yasuoka, M., Hirao, K., Brito, M. E., et al., High-strength and high fracture toughness ceramics in the Al2O3/LaAl11O18 systems, J. Am. Ceram. Soc., 1995, 78(7): 1853.
Horn, D. S., Messing, G. L., Anisotropic grain growth in TiO2-doped alumina, Mater Sci. Eng. A, 1995, 195: 169–172.
Guo, R. S., Guo, D. L., Qi, H. T. et al., Effects of adding rare earth oxides on properties of zirconia-toughness alumina ceramics Journal of the Chinese Ceramic Society, 2002, 30(1): 112–116.
Guo, R. S., Guo, D. L., Chen, Y. R. et al., Effects of adding rare earth oxides on mechanical properties of ZTA ceramics. Materials Review, 2000, 14(z10): 80–82.
Wu, Y. Q., Zhang, Y. F., Huang, X. X. et al., Microstructural development and mechanical properties of self-reinforced alumina with CAS addition, Journal of the European Ceramic Society, 2001, (21): 581–587.
Hirao, K., Ohashi, M., Brito, M. E. et al., Processing strategy for producing highly anisotropic silicon nitride, J. Am. Ceram. Soc., 1995, 78(6): 1687–1690.
Hirao, K., Nagaoka, T., Brito, M. E. et al., Microstructure control of silicon nitride by seeding with rodlike β-silicon nitride particles, J. Am. Ceram. Soc., 1994, 77(7): 1857–1862.
Messing, G. L., Kumagai, M. et al., Seeded Transformations for Microstructural Control in Ceramics, Science of Ceramic Chemical Processings (eds. Hench, L. L., Ulrich, D. R.), A Wiley-Interscience Publication, New York: John Wiley & Sons, 1986, 259–271.
Kwon, S., Messing, G. L., Sintering of mixtures of seeded boehmite and ultrafine alumina, J. Am. Ceram. Soc., 2000, 83(1): 82–88.
Yoshizawa, Y., Toriyama, M., Kanzaki, S., Preparation of high fracture toughness alumina sintered bodies from Bayer aluminum hydroxide, J. Ceram. Soc. Jpn., 166, 1998, (12): 1172–1176.
Nyvlt, J., Sohnel, O., Matuchovaa, M. et al., Chemical Engineering Monographs 19, New York: Elsevier, 1985.
Kaao Huangchan, Wei Wenchen, Kinetics and microstructural evolution of hetergeneous transformation of θ-alumina to α-alumina, J. Am. Ceram. Soc., 2000, 83(2): 362–368.
Brandon, D., Chen, D., Chan, H. Control of texture in monolithic alumina, Mater. Sci. Eng. A, 1995, (195): 189–196.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Xie, Z., Gao, L., Li, W. et al. High toughness alumina ceramics with elongated grains developed from seeds. Sci. China Ser. E-Technol. Sci. 46, 527–536 (2003). https://doi.org/10.1360/02ye0181
Received:
Issue Date:
DOI: https://doi.org/10.1360/02ye0181