Abstract
Due to structural and textural heterogeneities and a high content of stored energy, annealing of nanostructured metals is difficult to control in order to avoid non-uniform coarsening and recrystallization. The present research demonstrates a method to homogenize the structure by annealing at low temperature before annealing at high temperature. By this two-step process, the structure is homogenized and the stored energy is reduced significantly during the first annealing step. As an example, high-purity aluminum has been deformed to a total reduction of 98.4% (equivalent strain of 4.8) by accumulative roll-bonding at room temperature. Isochronal annealing for 0.5 h of the deformed samples shows the occurrence of recrystallization at 200 °C and above. However, when introducing an annealing step for 6 h at 175 °C, no significant recrystallization is observed and relatively homogeneous structures are obtained when the samples afterwards are annealed at higher temperatures up to 300 °C. To underpin these observations, the structural evolution has been characterized by transmission electron microscopy, showing that significant annihilation of high-angle boundaries, low-angle dislocation boundaries, and dislocations characterizes the low-temperature annealing step. In a discussion, the observed annealing behavior is related to these structural changes.
Similar content being viewed by others
References
Altan BS, Miskioglu I, Purcek G, Mulyukov RR, Artan R (2006) Severe plastic deformation: towards bulk production of nanostructured materials. NOVA Science Publishers, New York
Valiev RZ, Islamgaliev RK, Alexandrov IV (2000) Prog Mater Sci 45:103. doi:https://doi.org/10.1016/S0079-6425(99)00007-9
Valiev RZ, Langdon TG (2006) Prog Mater Sci 51:881. doi:https://doi.org/10.1016/j.pmatsci.2006.02.003
Horita Z et al (1996) J Mater Res 11:1880. doi:https://doi.org/10.1557/JMR.1996.0239
Segal VM (1995) Mater Sci Eng A 197:157. doi:https://doi.org/10.1016/0921-5093(95)09705-8
Iwahashi Y, Wang J, Horita Z, Nemoto M, Langdon TG (1996) Scr Mater 35:143. doi:https://doi.org/10.1016/1359-6462(96)00107-8
Saito Y, Utsunomiya H, Tsuji N, Sakai T (1999) Acta Mater 47:579. doi:https://doi.org/10.1016/S1359-6454(98)00365-6
Tsuji N, Kamikawa N, Kim HW, Minamino Y (2004) Ultrafine grained materials III. TMS, Ohio, p 219
Meyers MA, Mishra A, Benson DJ (2006) Prog Mater Sci 51:427. doi:https://doi.org/10.1016/j.pmatsci.2005.08.003
Tsuji N, Ito Y, Saito Y, Minamino Y (2002) Scr Mater 47:893. doi:https://doi.org/10.1016/S1359-6462(02)00282-8
Li BL, Godfrey A, Meng QC, Liu Q, Hansen N (2004) Acta Mater 52:1069. doi:https://doi.org/10.1016/j.actamat.2003.10.040
Wang YM et al (2004) Scr Mater 51:1023. doi:https://doi.org/10.1016/j.scriptamat.2004.08.015
Yu CY, Kao PW, Chang CP (2005) Acta Mater 53:4019. doi:https://doi.org/10.1016/j.actamat.2005.05.005
Xing ZP, Kang SB, Kim HW (2002) J Mater Sci 37:717. doi:https://doi.org/10.1023/A:1013879528697
Terada D, Inoue S, Tsuji N (2007) J Mater Sci 42:1673. doi:https://doi.org/10.1007/s10853-006-0909-7
Wang J et al (1996) Acta Mater 44:2973. doi:https://doi.org/10.1016/1359-6454(95)00395-9
Hasegawa H et al (1999) Mater Sci Eng A 265:188. doi:https://doi.org/10.1016/S0921-5093(98)01136-8
Cao WQ, Godfrey A, Hansen N, Liu Q, Metall Mater Trans, accepted for publication
Prangnell PB, Hayes JS, Bowen JR, Apps PJ, Bate PS (2004) Acta Mater 52:3193. doi:https://doi.org/10.1016/j.actamat.2004.03.019
Jazaeri H, Humphreys FJ (2004) Acta Mater 52:3251. doi:https://doi.org/10.1016/j.actamat.2004.03.031
Kamikawa N, Tsuji N, Huang X, Hansen N (2006) Acta Mater 54:3055. doi:https://doi.org/10.1016/j.actamat.2006.02.046
Li XL, Liu W, Godfrey A, Juul Jensen D, Liu Q (2007) Acta Mater 55:3531. doi:https://doi.org/10.1016/j.actamat.2007.02.005
Kamikawa N, Tsuji N, Huang X, Hansen N, Minamino Y (2006) Mater Sci Forum 512:91
Liu Q (1994) J Appl Cryst 27:755. doi:https://doi.org/10.1107/S0021889894002062
Kamikawa N, Tsuji N, Huang X, Hansen N (2007) Mater Trans 48:1978. doi:https://doi.org/10.2320/matertrans.MA200702
Hughes DA, Hansen N (2000) Acta Mater 48:2985. doi:https://doi.org/10.1016/S1359-6454(00)00082-3
Liu Q, Huang X, Lloyd DJ, Hansen N (2002) Acta Mater 50:3789. doi:https://doi.org/10.1016/S1359-6454(02)00174-X
Humphreys FJ, Hatherly M (1995) Recrystallization and related annealing behavior. Pergamon, New York
Nazarov AA, Romanov AE, Valiev RZ (1993) Acta Metall Mater 41:1033. doi:https://doi.org/10.1016/0956-7151(93)90152-I
Lian J, Valiev RZ, Baudelet B (1995) Acta Metall Mater 43:4165. doi:https://doi.org/10.1016/0956-7151(95)00087-C
Horita Z et al (1996) Mater Charact 37:285. doi:https://doi.org/10.1016/S1044-5803(96)00178-7
Valiev RZ (2003) Adv Eng Mater 5:296. doi:https://doi.org/10.1002/adem.200310089
Hansen N, Huang X, Møller MG, Godfrey A (2008) J Mater Sci. doi:https://doi.org/10.1007/s10853-008-2874-9
Acknowledgements
The authors gratefully acknowledge the Danish National Research Foundation for supporting the Center for Fundamental Research: Metal Structures in Four Dimension, within which this work was performed. The authors also thank Prof. B. Ralph for useful comments and language correction.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kamikawa, N., Huang, X. & Hansen, N. Tailoring structures through two-step annealing process in nanostructured aluminum produced by accumulative roll-bonding. J Mater Sci 43, 7313–7319 (2008). https://doi.org/10.1007/s10853-008-2964-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-008-2964-8