High temperature mechanical and material properties of burnt masonry bricks

  • Original Article
  • Published:
Materials and Structures Aims and scope Submit manuscript

Abstract

Recently, there have been an increased research in fire performance of both normal strength concrete (NSC) and high strength concrete (HSC) for structural members in buildings and built infrastructure. On the contrary, burnt masonry bricks (BBs) are used in structures due to advantages these provide, however, the studies on fire performance of BBs as a structural material are scarce. Further, limited studies are available on comparative fire performance studies of BBs to that of NSC or HSC. A test program was designed to undertake high temperature tests on BBs commonly used in buildings and domestic constructions. Mechanical properties namely compressive strength, tensile strength, and elastic modulus were investigated at elevated temperatures (hot state) from 20 to 800 °C following ASTM and RILEM test procedures. Results show that BBs lose compressive strength similarly to that of NSC and HSC. The measured tensile strength of BBs is quite low as compared to compressive strength, with a slight gain around 200 °C. High temperature properties also exhibit significant change in stress–strain response with increasing temperatures. Scanning electron microscope and X-ray fluorescence analysis revealed that microstructural and mineral transformations occur in BBs at elevated temperatures. To provide high temperature material properties of BBs for analytical studies, data generated from mechanical property tests were applied to develop simplified mathematical expressions as a function of temperature.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11

Similar content being viewed by others

References

  1. Castillo C, Durrani A (1990) Effect of transient high temperature on high-strength concrete. ACI Mater J 87(1):47–53

    Google Scholar 

  2. Bažant ZP, Kaplan MF (1996) Concrete at high temperatures: material properties and mathematical models. Longman (Addison-Wesley), London

    Google Scholar 

  3. Noumowe A (2005) Mechanical properties and microstructure of high strength concrete containing polypropylene fibres exposed to temperatures up to 200°C. Cem Concr Res 35(11):2192–2198

    Article  Google Scholar 

  4. Khaliq W, Kodur V (2011) Thermal and mechanical properties of fiber reinforced high performance self-consolidating concrete at elevated temperatures. Cem Concr Res 41(11):1112–1122

    Article  Google Scholar 

  5. ACI Committee 216 (1997) Standard method for determining fire resistance of concrete and masonry construction assemblies

  6. Masonry Standards Joint Committee (2005) Building code requirements for masonry structures (ACI 530-05ASCE 5-05TMS 402-05)

  7. Al Nahhas F, Saada RA, Bonnet G, Delmotte P (2007) Resistance to fire of walls constituted by hollow blocks: experiments and thermal modeling. Appl Therm Eng 27(1):258–267

    Article  Google Scholar 

  8. Andreini M, Caciolai M, La Mendola S, Mazziotti L, Sassu M (2015) Mechanical behavior of masonry materials at high temperatures. Fire Mater 39(1):41–57

    Article  Google Scholar 

  9. Andreini M, De Falco A, Sassu M (2014) Stress–strain curves for masonry materials exposed to fire action. Fire Saf J 69:43–56

    Article  Google Scholar 

  10. Nguyen TD, Meftah F, Chammas R, Mebarki A (2009) The behaviour of masonry walls subjected to fire: modelling and parametrical studies in the case of hollow burnt-clay bricks. Fire Saf J 44(4):629–641

    Article  Google Scholar 

  11. Cultrone G, Sebastián E, Elert K, De la Torre MJ, Cazalla O, Rodriguez-Navarro C (2004) Influence of mineralogy and firing temperature on the porosity of bricks. J Eur Ceram Soc 24(3):547–564

    Article  Google Scholar 

  12. Elert K, Cultrone G, Navarro CR, Pardo ES (2003) Durability of bricks used in the conservation of historic buildings: influence of composition and microstructure. J Cult Herit 4(2):91–99

    Article  Google Scholar 

  13. Pérez-Villarejo L, Eliche-Quesada D, Iglesias-Godino FJ, Martínez-García C, Corpas-Iglesias FA (2012) Recycling of ash from biomass incinerator in clay matrix to produce ceramic bricks. J Environ Manag 95:S349–S354

    Article  Google Scholar 

  14. Kodur V, Khaliq W (2010) Effect of temperature on thermal properties of different types of high-strength concrete. J Mater Civ Eng 23(6):793–801

    Article  Google Scholar 

  15. Khaliq W (2012) Performance characterization of high performance concretes under fire conditions. Michigan State University, East Lansing

    Google Scholar 

  16. Husem M (2006) The effects of high temperature on compressive and flexural strengths of ordinary and high-performance concrete. Fire Saf J 41(2):155–163

    Article  Google Scholar 

  17. Khaliq W, Kodur V (2012) High temperature mechanical properties of high-strength fly ash concrete with and without fibers. ACI Mater J 109(6):665–674

    Google Scholar 

  18. Mbumbia L, Mertens de Wilmars A, Tirlocq J (2000) Performance characteristics of lateritic soil bricks fired at low temperatures: a case study of Cameroon. Constr Build Mater 14(3):121–131

    Article  Google Scholar 

  19. Nadjai A, Garra MO, Ali F (2003) Finite element modelling of compartment masonry walls in fire. Comput Struct 81:1923–1930

    Article  Google Scholar 

  20. Johari I, Said S, Hisham B, Bakar A, Ahmad ZA (2010) Effect of the change of firing temperature on microstructure and physical properties of clay bricks from Beruas (Malaysia). Sci Sinter 42:245–254

    Article  Google Scholar 

  21. Andreini M, Sassu M (2011) Mechanical behaviour of full unit masonry panels under fire action. Fire Saf J 46(7):440–450

    Article  Google Scholar 

  22. Ayala FRR (2011) Mechanical properties and structural behaviour of masonry at elevated temperatures. University of Manchester, Manchester

    Google Scholar 

  23. Russo S, Sciarretta F (2013) Masonry exposed to high temperatures: mechanical behaviour and properties—an overview. Fire Saf J 55(1):69–86

    Article  Google Scholar 

  24. Xiao Z, Ling T-C, Poon C-S, Kou S-C, Wang Q, Huang R (2013) Properties of partition wall blocks prepared with high percentages of recycled clay brick after exposure to elevated temperatures. Constr Build Mater 49(1):56–61

    Article  Google Scholar 

  25. Cultrone G, Sebasti E, de la Torre J (2005) Mineralogical and physical behaviour of solid bricks with additives. Constr Build Mater 19(1):39–48

    Article  Google Scholar 

  26. ASTM C1314-14 (2014) Standard test method for compressive strength of masonry prisms. ASTM International, West Conshohocken

    Google Scholar 

  27. ASTM C1006-07 (2013) Standard test method for splitting tensile strength of masonry units. ASTM International, West Conshohocken

    Google Scholar 

  28. Phan LT (1996) Fire performance of high-strength concrete: a report of the state-of-the art, vol Report No. NISTIR 5934. National Institute of Standards and Technology, Gaithersburg

  29. ASTM C67-14 (2014) Standard test methods for sampling and testing brick and structural clay tile. ASTM International, West Conshohocken

    Google Scholar 

  30. Mbumbia L, de Wilmars AM (2002) Behaviour of low-temperature fired laterite bricks under uniaxial compressive loading. Constr Build Mater 16(2):101–112. doi:10.1016/S0950-0618(01)00035-6

    Article  Google Scholar 

  31. RILEM (1995) 129-MHT: test methods for mechanical properties of concrete at high temperatures. Mater Struct 28:410–414

    Article  Google Scholar 

  32. Brownell WE (2012) Structural clay products (applied mineralogy). Springer Science & Business Media, Wien

    Google Scholar 

  33. Mezencevova A, Yeboah NN, Burns SE, Kahn LF, Kurtis KE (2012) Utilization of Savannah Harbor river sediment as the primary raw material in production of fired brick. J Environ Manag 113(1):128–136

    Article  Google Scholar 

  34. EN 1996-1-2 (2005) Eurocode 6—design of masonry structures—part 1-2: general rules—structural fire design. Brussels

  35. Fu Y, Wong Y, Poon C, Tang C (2005) Stress–strain behaviour of high-strength concrete at elevated temperatures. Mag Concr Res 57(9):535–544

    Article  Google Scholar 

  36. Tang W, Lo T (2009) Mechanical and fracture properties of normal-and high-strength concretes with fly ash after exposure to high temperatures. Mag Concr Res 61(5):323–330

    Article  Google Scholar 

  37. Fu Y-F, Wong Y-L, Poon C-S, Tang C-A, Lin P (2004) Experimental study of micro/macro crack development and stress–strain relations of cement-based composite materials at elevated temperatures. Cem Concr Res 34(5):789–797. doi:10.1016/j.cemconres.2003.08.029

    Article  Google Scholar 

  38. Behnood A, Ghandehari M (2009) Comparison of compressive and splitting tensile strength of high-strength concrete with and without polypropylene fibers heated to high temperatures. Fire Saf J 44(8):1015–1022

    Article  Google Scholar 

  39. Felicetti R, Gambarova P, Rosati G, Corsi F, Giannuzzi G (1996) Residual mechanical properties of high-strength concretes subjected to high-temperature cycles. In: Proceedings, 4th international symposium on utilization of high-strength/high-performance concrete, Paris, pp 579–588

  40. Khaliq W, Kodur V (2011) Effect of high temperature on tensile strength of different types of high-strength concrete. ACI Mater J 108(4):394–402

    Google Scholar 

  41. Russo S, Sciarretta F (2012) Experimental and theoretical investigation on masonry after high temperature exposure. Exp Mech 52:341–359

    Article  Google Scholar 

  42. Phan LT, Carino NJ (2000) Fire performance of high strength concrete: research needs. National Institute of Standards and Technology, Gaithersburg

    Google Scholar 

  43. Deer WA, Howie RA, Zussman J (1992) An introduction to the rock-forming minerals, vol 696. Longman, London

    Google Scholar 

  44. Aramide FO (2012) Effect of firing temperature on mechanical properties of fired masonry bricks produced from ipetumodu clay. Leonardo J Sci 11(21):70–82

    Google Scholar 

  45. Seynou M, Millogo Y, Ouedraogo R, Traoré K, Tirloc J (2011) Firing transformations and properties of tiles from a clay from Burkina Faso. Appl Clay Sci 51(1):499–502

    Article  Google Scholar 

  46. Klosek-Wawrzyna E, Malolepszy J, Murzyn P (2013) Sintering behavior of kaolin with calcite. Proced Eng 57(1):572–582

    Article  Google Scholar 

  47. Paterson MS, T-f Wong (2005) Experimental rock deformation: the brittle field, 2nd edn. Springer Science & Business Media, Berlin

    Google Scholar 

  48. Bellotto M, Gualtieri A, Artioli G, Clark S (1995) Kinetic study of the kaolinite-mullite reaction sequence. Part I: kaolinite dehydroxylation. Phys Chem Miner 22(4):207–217

    Article  Google Scholar 

  49. Lie TT (1992) Structural fire protection. ASCE Committee on Fire Protection Structural Division, New York, pp 225–229

    Google Scholar 

  50. Minitab (2013) http://www.minitab.com/en-us/. Release 17

  51. Wackerly DD, Mendenhall W III, Scheaffer RL (2008) Mathematical statistics with applications. Thomson Higher Education, Belmont

    MATH  Google Scholar 

Download references

Acknowledgments

The research presented in this paper was supported by NUST Institute of Civil Engineering, School of Civil and Environmental Engineering at National University of Science and Technology, Islamabad, Pakistan. All opinions, findings and conclusions explained in this paper are those of the authors’ and do not necessarily reflect the views of the sponsors.

Author information

Authors and Affiliations

  1. NICE (SCEE), National University of Sciences and Technology (NUST), Islamabad, 44000, Pakistan

    Wasim Khaliq

  2. National University of Sciences and Technology (NUST), Islamabad, 44000, Pakistan

    Muhammad Farrukh Bashir

Authors
  1. Wasim Khaliq
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Muhammad Farrukh Bashir
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Wasim Khaliq.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Khaliq, W., Bashir, M.F. High temperature mechanical and material properties of burnt masonry bricks. Mater Struct 49, 5195–5208 (2016). https://doi.org/10.1617/s11527-016-0854-0

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1617/s11527-016-0854-0

Keywords

Search

Navigation