Abstract
Doped magnetite (SnxFe3-2/3xO4) nanoparticles (NPs) (12–50 nm) with different amount of Sn2+ ions (x) were synthesized using co-precipitation method. Sn2+ doping reduces the anticipated oxidation of Fe3O4 NPs to maghemite (γ-Fe2O3), making them attractive in several magnetic applications. Detailed characterizations during heating–cooling cycles revealed the possibility of tuning the unusual observed magnetization dipping temperature/amplitude, irreversibility, and Curie point of these NPs. We attribute this dip to the chemical reduction of γ-Fe2O3 at the NPs surfaces. Along with an increase in the dipping temperature, we found that doping with Sn2+ reduces the dipping amplitude, until it approximately disappears when x = 0.150. Based on the core-shell structure of these NPs, a phenomenological expression that combines both modified Bloch law (M = M0[1 − γ(T/TC)]β) and a modified Curie–Weiss law (M = − α[1/(T − TC)δ]) is developed in order to explain the observed M-T behavior at different applied external magnetic fields and for different Sn2+ concentrations. By applying high enough magnetic field, the value of the parameters γ and δ ≈ 1 which are the same in modified Bloch and Curie–Weiss laws. They do not change with the magnetic field and depend only on the material structure and size. The power β for high magnetic field was 2.6 which is as expected for this size of nanoparticles with the core dominated magnetization. However, the β value fluctuates between 3 and 10 for small magnetic fields indicating an extra magnetic contribution from the shell structure presented by Curie–Weiss term. The parameter (α) has a very small value and it turns to negative values for high magnetic fields.
Avoid common mistakes on your manuscript.
Introduction
Metal oxide nanoparticles are attractive from both technical and theoretical perspective. Among them, iron oxide nanoparticles are very popular due to their massive applications in the fields of ferrofluids, pigments, information storage disks, and medical applications as magnetically guided drug delivery, cell separation, and cancer diagnoses [1,2,3,4,5,6,7,8,9]. Magnetite (Fe3O4) nanoparticles are particularly well suited for medical applications, due to their biological compatibility and the large saturation magnetization (Ms) of 92 emu/g at 300 K for the bulk [10, 11]. However, the thermal instability of these nanoparticles can be a drawback for these applications since nanoparticles with size of ~ 8–22 nm can be easily oxidized to maghemite (γ-Fe2O3) even at ambient conditions of temperature and pressure—although the bulk can be accomplished at ~ 220 °C [12]. Maghemite is a ferrimagnetic material like magnetite with the same spinel structure but with lower Ms of 78 emu/g at 300 K [10]. By heating up to about 850 K (Curie point), Fe3O4 can be structurally changed to the antiferromagnetic corundum-like structure hematite with zero Ms [13]. These transformations are controlled by particle size, temperature, and pressure. Scarce studies are made for Fe3O4 particles at high temperature because of thermal instability. Recently more attention has been given to the effects of organic capping—such as an oleate-capped Fe3O4 nanoparticles—on the magnetization of the nanoparticles (NPs) [14]. It was found that, in heating–cooling cycles, Fe3O4 NPs exhibited irreversible M behavior with two peculiar effects, namely, dips and loops in their M (T) curves. The dipping and the irreversible magnetization were attributed to the induced reduction of Fe3+ to Fe2+ and sintering upon the decomposition of the capping ligands respectively. Our intention in this study is to thoroughly understand the cause of these peculiar effects, their nature, stability, effects on magnetization, and surface reduction of Fe3+ to Fe2+ and their relationship with sintering process of the NPs at elevated temperatures. Motivated by the fact that Fe3O4 NPs can be easily oxidized to form γ-Fe2O3 shell (i.e., thin layer thereafter called a shell) on the surface which acts as a capping layer and exploiting the knowledge that doping Fe3O4 with certain ions like Sn4+ and Ti4+ shows a decrease in the Fe3+ to Fe2+ reduction process [15, 16], we therefore explore the possibility of tuning those peculiar effects (i.e., dipping and loops) in temperature dependent magnetization curves by Sn2+ doping of Fe3O4 NPs.
In order to study the effect of Sn2+ doping on the stability of magnetite nanoparticles, magnetization dipping, and irreversibility at high temperatures, SnxFe3-2/3xO4 nanoparticles (12–50 nm) with (x = 0.000, 0.045, 0.090, and 0.150), were prepared and characterized using several complementary techniques. The magnetization was measured using a vibrating sample magnetometer (VSM) while repeatedly heating the sample up to 900 K (5 K/min) and cooling back to room temperature (300 K). An irreversible dip in magnetization was noticed at a specific temperature and with certain amplitude during the first heating–cooling cycle. Evidences of the change in dipping temperature, and amplitude, irreversibility, divergence in magnetization (i.e., magnetization values are different at specific temperature in heating and cooling cycles) and Curie point with x were observed and explained. Contrary to the explanation that the observed irreversibility in heating–cooling regime can only be expected for the ligand-free Fe3O4 NPs, we show that divergence can be controlled by the external magnetic field applied to the Fe3O4 NPs during the magnetic measurements and disappears at higher applied field. Furthermore, we show that the M-T of the pristine and the Sn2+-doped Fe3O4 NPs after the first heating–cooling cycle can be predicted by a new approach that combines both a modified Bloch and Curie–Weiss laws for different Sn2+ concentrations and different applied external magnetic fields.
Methods/Experimental
Materials
Aqueous ammonia (Mw = 17.03, 30%) and absolute ethanol were purchased from Merck, ferric chloride hexahydrate (Mw = 270.3, ≥ 99%) and ferrous chloride tetrahydrate (Mw = 198.8, ≥ 99%) were procured from Sigma-Aldrich, and stannous chloride (Mw = 189.60, ≥ 98%) was obtained from Fluka. All the chemicals were used without further purification.
Methods
Nanoparticles of Sn2+ doped Fe3O4 with the nominal composition SnxFe3-2/3xO4 (x = 0.000, 0.045, 0.090, and 0.150), where Sn2+ substitutes Fe3+, were prepared using co-precipitation under reflux at 80 °C for 4 h. Aqueous ammonia was added to stoichiometric solutions of ferric chloride hexahydrate, ferrous chloride tetrahydrate, and stannous chloride at 50 °C until a pH ≈ 10.4 was attained. The precipitates were then removed by filtration, washed with distilled water followed by ethanol, and very carefully dried at room temperature avoiding high temperature that would result in the formation of Sn-doped maghemite as was demonstrated by Berry et al. [16].
The surface of pristine Fe3O4 nanoparticles was covered with 2 nm layer of gold (99.99% gold target, Scotech) using e-beam evaporation (deposition rate ~ 0.47 Å/s) attached to the Nanosys 550 nanoparticle deposition system from Mantis Deposition Ltd. in order to examine the surface effect.
Characterizations
A VSM attached to a quantum design physical property measurement system (Dynacool PPMS) was used for magnetic measurements at temperature ranging from 2 to 900 K with magnetic fields up to 9 (Tesla). Curie point was taken by the extrapolation of M curve to the x-axis during the first heating regime following the procedure used in reference [17]. The morphology of the samples was characterized using JOEL digital high-resolution (JEN-2100F) transmission electron microscope (HRTEM) and (X’Pert PRO) diffractometer for X-ray powder diffraction (XRD) patterns using a standard Cu-Kα radiation. The MAUD software was used to perform simple XRD Rietveld refinements [18]. Elemental mapping (EDX) was carried out using field emission scanning electron microscope (JOEL, JSM 7600F). X-ray photoemission spectra (XPS) were acquired using Omicron Nanotechnology multiprobe photoelectron instrument equipped with a hemispherical electron analyzer where Al Kα radiation (1486.6 eV) was used at 10−9 mbar. Intrinsic carbon peak at 284.6 eV was employed for calibration. The Casa XPS software was used for XPS data analysis [19]. Fourier transform infrared (FTIR) spectrum was obtained from PerkinElmer (SpectraOne) using transmission mode with KBr pellets in the range of 400–4000 cm−1.
Results and Discussion
The Main Features of M-T Curves During the First Heating Cycle
Figure 1a–d shows the change of magnetization (M) as a function of temperature of the samples; pristine Fe3O4- and tin–doped SnxFe3-2/3xO4 nanoparticles with different amount of x. The samples were heated from 300 up to 900 K (Fig. 1 point A to B) and cooled back (point B to C) for the first heating–cooling cycle while applying an external magnetic field of 200 Oe. The heating–cooling cycle’s measurements as depicted from curves D to E were repeated under same magnetic field until stable magnetization data was reached. The pristine Fe3O4 nanoparticles (Fig. 1a) undergo heating–cooling cycle for five times. For clarity, we only present three cycles since after that there were no more changes in magnetization during heating–cooling process. The doped samples (Fig. 1b–d) were heated and cooled for three times only since there was no obvious change in M after the second cycle (two cycles are presented in the figures). Four obvious features were noticed where temperature is ranging from 300 to 900 K. First, there is a dip in magnetization of about 10 emu/g that occurred in the pristine sample (x = 0.000) between T1 (564 K) and T2 (655 K), while going from point A to B in the first heating–cooling cycle. This dip also occurred in the doped samples but with increased dipping temperatures (T1, T2) as x increases (Fig. 2a). This increase may be attributed to the increase in particle size due to Sn-doping as confirmed by HRTEM measurements shown in Fig. S1. To ensure that Sn2+ ions spread uniformly throughout the structure, an elemental mapping for the pure and SnxFe3-2x/3O4 doped sample with x = 0.150 (Figs. S2 and S3).
Change of magnetization (M) with temperature of pristine and SnxFe3-2/3xO4 nanoparticles of Sn2+ (x) amount a 0.000 (pristine Fe3O4), b 0.045, c 0.090, and d 0.150 respectively, for different heating–cooling cycles [for a and b, black indicates 1st; red, 2nd; blue, 3rd and for c and d, only 2-cycles are indicated] (magnetic field H = 200 Oe) (solid line, heating; dotted line, cooling)
Similar dipping was also reported as mentioned above in oleate-capped magnetite nanoparticles with 20 nm in size which is attributed to the thermal decomposition of the capping ligands. Along with the decomposition, a reduction of Fe3+ to Fe2+ after heating was also observed using Raman and Mössbauer spectroscopy [14].
Interestingly, the dipping feature was not detected in the un-capped Fe3O4 sample reported by Kolen’ko et al. [14]. Although, there were no capping ligands used in our sample’s preparation, the surface of nanoparticles was influenced by oxidation either to maghemite (γ-Fe2O3) or Sn2+-related oxides, both of which could act as a capping layer. Consequently, the dipping of M in the first heating–cooling cycles indicates that there was a thermal decomposition of the oxidized layer on the surface of these nanoparticles (i.e., a reduction of Fe3+ and Sn2+, Sn 4+ ions).This decomposition will take place at lower temperature for smaller particles due to their larger specific surface area. This explanation is supported by a previously reported reduction of amorphous γ-Fe2O3 nanoparticles in an evacuated environment at 523 K [20]. The second observed feature is related to the M dipping amplitude (labeled as ΔM in Fig. 1a). ΔM decreases as the amount of Sn2+ increases (Fig. 2a) due to decrease in the amount of γ-Fe2O3 caused by doping process [11, 16].
The third feature is that the heating–cooling curves are irreversible (i.e., M curves during heating are different from cooling). This is related to the blocking features since after heating there is an increase in the particle size confirmed by TEM images (Fig. 3). The increase in particle size will increase the magnetocrystalline anisotropic energy (EA) of a single domain particle according to Wolfarth model as shown below.
where K is the magnetocrystalline anisotropy constant, V is the volume of the nanoparticle, and θ is the angle between the magnetization direction and the easy axis of magnetization of the nanoparticles [21, 22]. Hence, more thermal energy is needed to overcome the magnetic anisotrpic energy and randomize the magnetic spins. The randomly oriented spins as a result of heating will start to be affected by the applied magnetic field at a certain temperature via cooling. When the temperature reaches T2, these aligned spins will be blocked attaining high constant magnetization while approaching room temperature (detailed explanation is in the “The Origin of Divergence in Heating–Cooling Graph” section). The fourth feature is the dependence of Curie temperature (TC) on the amount of Sn2+ doped as shown in Fig. 2a and this is related to the effect of Sn2+ ions on the saturation magnetization (Ms) as shown in Fig. 2b. Hence, it is anticipated that as Ms increases, TC will increase as shown in the inset of Fig. 2b, which is in good agreement to previous reports [11, 16]. All the four aforementioned features suggest a strategy for tuning of Fe3O4 nanoparticles magnetization, dipping temperature/amplitude, irreversibility, and Curie point by Sn2+ doping.
Characterization of the Heated Samples
Although the results of the pristine sample heated to 900 K were obtained and discussed, in order to investigate the origin of the first dipping temperature (T1), additional structural and magnetic measurements were also carried out for the same sample after in situ heating at high-temperature VSM measurements up to 600 K. Figure 4a shows XRD patterns and their Rietveld refinements for the pristine sample before heating, after heating via high-temperature VSM measurements to 600 K and 900 K. The XRD peaks for the cement (glue) used to fix the sample on the heating stick for high-temperature VSM measurements are represented by small filled squares as a reference. Before heating, the pattern is indexed to the spinel related structure (SG# 227). There is an overlap between the 311 and 222 peaks, which normally appear at 2θ equal to 35° and 37° respectively. This is an indication of the existence of γ-Fe2O3 phase, since it has the same spinel structure of magnetite but with a smaller lattice parameter. This overlap disappears after heating to 600 K which indicates a decrease or inhibition of γ-Fe2O3 phase due to a reduction of Fe3+ to Fe2+ (neglecting the peaks topped with the square at about 35° which is referred to the glue). Moreover, since the (220) and (440) peaks appear at about 30° and 62°, respectively, are related solely to ferric oxides without the glue [23], we indicate in Fig. 4b and c enlarge pattern of these peaks. After heating to 600 K, both peaks undergo a shift to a higher reflection angle by about 0.3° which is an indication of a decrease in the (d) spacing values. This decrease is normally associated with the high-temperature annealing of oxide nanoparticles which often results in solvent removal and annihilation of defects and thus leads to a decrease in the values of lattice parameter [14]. The full width half maximum of both peaks decreases as a result of the crystallinity improvement and an increase in the crystallite size according to the Scherrer equation. The shape of the peaks changes from symmetric to asymmetric with steeper low-angle side. As mentioned above, both magnetite and maghemite phases have the same spinel structure but with slightly larger lattice parameter for magnetite (lower reflection angle); the asymmetry indicates an increase in the magnetite phase at 30.3° with the lower angle peak compared to maghemite at 30.5°. This reduction of γ-Fe2O3 phase will increase the value of M at T1 since magnetite has larger saturated magnetization and it is non-repeatable process that occurring at the first heating–cooling cycle which explains the change in the M-T curve for the subsequent heating–cooling cycles. After heating to 900 K, the peaks sharpen while remaining at the same angle indicating a more increase in crystallite size confirmed by TEM images (Fig. 3) (from 12 nm to 30 nm). This sharpness is reflected in M-T curve as an increase in M at T2.
a XRD patterns for pristine Fe3O4 before heating and after heating to 600 K (green), 900 K (red) (black dotted line, experimental data; solid line, fitted; magenta, difference; pars, SG #227 phase) (the small filled squares represent the peaks for the glue used for high-temperature VSM measurements), b enlarge pattern for (220) peak, and c enlarge pattern for (440) peak
Since the asymmetric feature of the two peaks (220) and (440) is not solely providing solid evidence to distinguish between the two-spinel magnetite and maghemite phases using XRD. Thus, the reduction or inhibition of γ-Fe2O3 phase at high annealing temperatures was confirmed by XPS measurements. Figure 5a shows the XPS core-level ionization Fe 2p3/2 spectra obtained from pristine sample before and after heating to 900 K. Two components can be found from the deconvoluted Fe 2p3/2 peak at binding energies of 709 eV and 711 eV representing Fe2+ (22%) and Fe3+ (77%) states, respectively, with a pre-peak low energy tail at 708 eV [24, 25]. Upon heating at 900 K along with the reduction in binding energy of the two components, a certain amount of Fe3+ (72%) states transforms to Fe2+ (19%) and the metallic Fe (9%)—component depicted at 705 eV—as a reflection of the reduction of γ-Fe2O3 phase.
The FTIR spectra of pristine Fe3O4 nanoparticles before and after heating to 900 K are shown at Fig. 5b. The strong peaks at 583 cm−1 and 634 cm−1 are assigned, as indicated in the figure, to the stretching of Fe-O bonds. After heating the sample, these peaks broadened and shifted to higher frequencies indicating a strengthening in the Fe-O bonds due to the crystallinity improvements and the increase in crystallite size proved using XRD measurements. The peaks between 1402 cm−1 and 878 cm−1 are related to adsorbates features [26,27,28] and disappeared after heating at 900 K. The peaks at 3413 cm−1 and 2974 cm−1 are related to the stretching bonds coming from the environmental OH− and CO2 groups, respectively [27]. The intensity of these peaks decreases by heating which is accepted due to sintering process. The peak at 1619 cm−1 is related to the bending of the bond related to the hydroxide group coming from the atmosphere and its intensity also decreases by heating.
Consequently, the change in magnetization due to the reduction process at T1 and sintering process at T2 causes the observed dipping in magnetization. The hysteresis loops for the pristine sample before and after heating up to both 600 K and 900 K (Fig. 6) indicate a little increase in M after heating which is supporting the reduction of Fe3+ ions at T1. The remanence and coercivity (inset of Fig. 6) were increased after heating to 900 K, while they did not change after heating to 600 K, which verifies that the sintering process takes place at T2, hence confirming what was found from XRD and FTIR measurements.
The Origin of Divergence in Heating–Cooling Graph
To investigate the origin of the observed divergence in M while heating and cooling (Fig. 1) and its relationship to the blocking temperatures, more measurements on the pristine sample subjected to different external magnetic fields were performed, while heating and cooling, as shown in Fig. 7. It can be seen clearly that the divergence (labeled as a circular ring) disappeared when the measurements were collected while applying high magnetic field of 2 T (i.e., this divergence simplifies the identification of the blocking temperatures of these nanoparticles at external magnetic fields of 200 Oe).
Based on that, additional low temperature VSM measurements (2–400 K) using the zero field cooling–field cooling (ZFC-FC) protocols with external magnetic field of 200 Oe were made for the pristine sample after subjected to high-temperature VSM measurements up to 600 K and 900 K and compared with the same sample before heating (Fig. 8).
The blocking temperature for the sample heated to 900 K was higher than that of the sample heated to 600 K and to the non-heated sample. This was expected since the sample heated to 600 K shows a very small divergence in heating/cooling regime (Fig. 9a). This reinforces that at 600 K, there is a reduction from Fe3+ to Fe2+ without any increase neither in particle size nor in blocking temperature. Hence, we conclude that the first dipping temperature is referred to the reduction while the second temperature referred to the increase in particle size as shown schematically in Fig. 9. The same feature (increasing M while cooling) is obvious for the sample with x = 0.150 from the first heating–cooling cycle (Fig. 1d), which proves that doping with this amount of Sn will give the same thermomagnetic trend and will block the spins at higher temperatures during cooling regime. This makes SnxFe3-2/3xO4 with x = 0.150 be more practical and applicable when needed to be used at high temperatures. It should be mentioned that the divergence feature in oleate-capped Fe3O4 was previously reported by Kolen’ko et al. and attributed to the existence of γ-Fe2O3 in their sample. However, this is not the case since it is revealed to be related to the externally applied magnetic field as explained and depicted in Fig. 7. Hence, during heating up to the new blocking temperature (T2), the magnetization increased because of the thermal excitations of the blocked magnetic moments. However, while cooling down to the blocking temperature again the spins blocked at high magnetization and the thermal energy could not overcome the magnetic energy caused by the applied magnetic field as indicated by magenta arrows at Fig. 9.
Change of magnetization (M) with temperature (T) for pristine Fe3O4 while heating up to a 600 K and b 900 K using magnetic field of 200 Oe at three heating–cooling cycles. The schematic diagram on top of the figure represents the change of morphology of the NPs as temperature increases from 300 to 900 K (Initially, the Fe3O4 NPs are covered with a thin surface layer of γ-Fe2O3 which acts as a shell. Upon heating to 600 K, the γ-Fe2O3 annihilation takes place and NPs agglomeration start to occur till 900 K, magenta arrows represent spin’s orientation)
The Surface Effect
In order to investigate the effect of agglomeration of these nanoparticles in magnetization, a small amount of the pristine Fe3O4 sample was covered with a thin layer of Au (~ 2 nm) using the evaporation technique. The M-T graphs for the pristine Fe3O4 nanoparticles with and without gold after heating up to 900 K and cooling back for three cycles are shown in Fig. 10.
It can be noticed that the dipping amplitude (ΔM) decreases for the particles covered with gold similar to the behavior observed by doping with Sn2+ and can be attributed to the decrease in the oxidation reaction (i.e. in the amount of γ-Fe2O3 phase) by coating with Au on the surface of these nanoparticles. For the second dipping temperature (T2), there are two observations. First, like the pristine nanoparticles, there is an increase in the magnetization at T2. At this temperature, the thermal energy will unblock the spins of these nanoparticles and align them in the direction of the magnetic field. However, T2 value decreases for the Au/Fe3O4 nanoparticles, since now the interparticle interactions will be less and consequently reduce the energy needed to unblock the spins.
Since Au reduces the agglomeration of these nanoparticles, the divergence in heating–cooling cycles that appeared for the pristine nanoparticles after the second cycle is very small. The hysteresis loops made for Au/Fe3O4 sample before and after heating (Fig. 11) shows a decrease in M after heating which may be referred to the diamagnetic effect of Au. The coercivity and remanence did not change which proves that there is no agglomeration, change in particle size or on the crystallinity of these nanoparticles after coating with gold.
Theoretical Explanation
It is imperative to discuss two challenges faced while trying to understand the observed features of high-temperature NPs magnetization after reaching stable repeatable measurements (≈ 3rd cycles). The first is due to the deviation of the Bloch law normally used for the bulk to explain the observed change of in saturation magnetization with temperature for magnetic nanoparticles [29,30,31]. In this regard, many efforts have been made to modify Bloch law such as that reported by Kodama et al. [32]. They started with Bloch formula:
and allowing the parameters γ and β—equal 1 and 3/2 for the bulk material, respectively—to change. Consequently, the value of β was found to lay between 3/2 and 2 for NPs. The increase in β value compared to that of the bulk is related to the collective thermal excitations of the ordered spin which produces an energy gap (ΔE) between the ordered and disordered spins. This energy gap will reduce the spontaneous magnetization by an amount proportional to exp (− ΔE/kBT). Hence, Kodama et al. suggested to use the same value of β for the bulk (3/2) but by adding exp (− ΔE/kBT) to Eq. 2. The second challenge is that our measurements were done in low magnetic fields and cannot be fitted with Bloch law alone since the spins are not saturated and the energy gap (ΔE) will be affected by the magnetic field leading to change the measured magnetization. Motivated by the aforementioned challenges and in order to fit and justify our observed M-T graphs at different magnetic fields and different Sn2+ concentrations, a simple phenomenological expression that combines both the modified Bloch law and Curie–Weiss law was introduced. This justification is based on a core-shell structure model for these nanoparticles [29]. Hence, we assume that each nanoparticle is composed of a core with saturated spins and a bulk like interchange interactions surrounded by a shell with randomly oriented spins. In the core, the magnetization is given by:
which is the same modified Bloch law in Eq. 2 but by replacing Mo with MH- where the value of M at 300 K and at certain magnetic field. For the shell, there is no interchange interactions between the magnetic spins—like paramagnetic materials—and the M-T relation in this part (MH-Shell) will obey Curie–Weiss law as MH-Shell = C/(T − TC), where C is the Curie constant. Hence, the deviation of our M-T curves from the modified Bloch law is related to the shell effect that decreases the magnetization and will disappear at high magnetic fields and high temperatures. The measured magnetization at each temperature (Mexp) will be the total contribution of both the core and the shell parts. The best fit for the experimental magnetization (M) of the pristine sample with the magnetic field (H) (Fig. 12) and for M of the SnxFe3-2/3xO4 with x (Fig. 13) was reached by applying the formula
where α, β, δ , γ, MH, and TC are parameters to be derived from the fitting. The second term will be positive for T < TC. We free the power (δ) in the second part of Eq. 4 to see how it can affect the quality of our fitting. In order to verify our results, we tested the modified Bloch law proposed by Kodama et al. for the pure sample at high magnetic field of 2 T and the value of β was 2.6. This value is within the suggested range for this size of nanoparticles [32].
Change of magnetization (M) with temperature during heating (after 3rd cycle) of the heated pristine Fe3O4 nanoparticles while applying different magnetic field H of a 50 (Oe), b 100 (Oe), c 200 (Oe), and d 2 T (black dotted, experimental; pink solid, fitted using Eq. 4)
However, as can be seen in Fig. 14, fitting our M-T curves with the core-shell-related expression (Eq. 4) is better than the suggested modified Bloch law specially at high temperatures and low magnetic fields (i.e., for unsaturated magnetic spins).
Change of magnetization (M) with temperature during heating for the 3rd cycle of the heated pristine Fe3O4 nanoparticles while applying a magnetic field H = 2 (Tesla) (pink dotted, experimental; solid, fitted using the new bulk-shell expression (black) and the modified Bloch law proposed by Kodama et al. (green)). Green arrows indicate the temperatures where the modified Bloch law proposed by Kodama et al. failed to fully fit the experimental data
The change of the parameters in Eq. 4 with the applied magnetic field for the pristine Fe3O4 nanoparticles is shown in Fig. 15a. It can be noticed that MH increases as it is expected with the increase in the magnetic field. The values of γ and δ ≈ 1 and do not change with the applied field as they are depending only as mentioned above on the material structure and the particle size.
a Change for the pristine Fe3O4 of MH (left) and TC (right) with the applied external magnetic field H and (the insets show the change in different parameters α (purple), β (blue), and δ (brown) in both cases and with γ (red) with respect to external magnetic field) b for SnxFe3-2/3xO4 samples as a function of x taken at H = 200 Oe (the insets show the change in different parameters α (purple), β (blue), and δ (brown) in both cases and with γ (red) with respect to x)
The (α) parameter is a very small constant. It turns to negative sign for higher field which is reasonable since the high field will saturate the spins at the shell and the paramagnetic effect will be small. The β values fluctuated ranging from 3 to 10 with the magnetic field which is different than the obtained power for nanoparticles using modified Bloch law. This is acceptable since we use MH at 300 K instead of the saturated Ms in Bloch law. The TC values, which are the same as what founded experimentally at 200 Oe in Fig. 2a, also changes with the applied field—a characteristic feature previously reported for magnetic nanoparticles [33].
Figure 15b shows the change of these parameters with the amount of Sn2+ (x). MH does not behave like the previously found saturation magnetization (Ms) (Fig. 2b) since MH is related to the magnetic field and the size of these nanoparticles. It is accepted that MH is larger for the pristine nanoparticles because of the reduction of γ-Fe2O3 phase and the sintering processes that took place during the previous heating–cooling cycles, which increased the saturated magnetization. For the Sn2+-doped sample, MH decreases since the existence of Sn2+ at the surface which can prevent the agglomeration process and the crystal growth (can be verified using TEM or XRD). The value of MH for x = 0.045 is larger than for x = 0.090 which is consistence with the larger value of Ms for this sample. Interestingly, for the larger NPs with x = 0.150, MH increased which opposes the decrease in their Ms and this is due to the larger particle size with larger blocking temperature. The values of (α) and (δ) are constants with average value equals 0.3 and 0.6, respectively. This is predicted since the second part of Eq. 4 is related to the change with the magnetic field which is now constant (200 Oe). The values of TC for different samples are approximately the same as recorded experimentally. γ is a constant with a value equals 1 which is the same as in Bloch law. β is also almost a constant since it is related to the material with an average value of 8.
Conclusions
SnxFe3-2/3xO4 nanoparticles (12–50 nm) with x = 0.000 to 0.0150 were prepared using co-precipitation method. The magnetization was measured using VSM while repeatedly heating and cooling the nanoparticles up to 900 K. An irreversible dip in magnetization with certain amplitude was noticed between two peaks at T1 and T2 during the first heating–cooling cycle. We relate the first peak to a chemical reduction of the oxidized layer at the surface of each nanoparticle. The second peak is referred to a crystal growth due to the sintering process. Coating the surface with Au prevent sintering process and the magnetic exchange interactions between nanoparticles. More stable magnetic behavior was obtained for the high concentration of dopant Sn2+ (x = 0.150) which make it more appropriate for high-temperature applications. Best fitting for M-T graphs were made using a phenomenological expression where a core-shell model with magnetization of a ferrimagnetic core obeying the modified Bloch law and a paramagnetic shell obeying Curie–Weiss law. The results presented in this work present a method to tune the magnetization characteristics of Fe3O4 nanoparticles by Sn2+ doping.
Availability of Data and Materials
Abbreviations
- NPs:
-
Nanoparticles
- VSM:
-
Vibrating sample magnetometer
- PPMS:
-
Physical property measurement system
- HRTEM:
-
High-resolution transmission electron microscope
- XPS:
-
X-ray photoemission spectroscopy
- FTIR:
-
Fourier transform infrared
- XRD:
-
X-ray diffraction
- FC:
-
Field cooling
- ZFC:
-
Zero field cooling
References
Cabellos (2009) Synthesis of γ-Fe2O3-SiO2 composite nanoparticles targeting magnetic resonance imaging and magnetic hyperthemia applications. PhD thesis, Universitat Autonoma de Barcelona, Barcelona
Blaney L (2007) Magnetite (Fe3O4): properties, synthesis, and applications. Lehigh Preserve 15:33–81
Ito A, Shinkai M, Honda H, Kobayashi T (2005) Review medical application of functionalized magnetic nanoparticles. J Biosci Bioeng 100:1–11
Ebner D, Ritter J, James H, Ploehn A, Harry J (1999) Two-particle magnetic hetero-flocculation model for nanolevel high gradient magnetic separation. In: Engineering Foundation Conference, pp 193–204
Rikers R, Rem P, Dalmijn W (1998) Improved method for prediction of heavy metal recoveries from soil using high intensity magnetic separation (HIMS). Int J Miner Process 54:165–182
Chen P, Cai Y, Wang J, Wang K, Tao Y, Xue J, Wang H (2018) Preparation of protonized titanate nanotubes/Fe3O4/TiO2 ternary composites and dye self-sensitization for visible-light-driven photodegradation of Rhodamine B. Powder Technol 326:272–280
Atabaev TS (2018) PEG-coated superparamagnetic dysprosium-doped Fe3O4 nanoparticles for potential MRI imaging. BioNanoScience 8:299–303
Atabaev T, Kim H, Hwang Y-H (2013) Fabrication of bifunctional core-shell Fe3O4 particles coated with ultrathin phosphor layer. Nanoscale Res Lett 8:357–363
Lei Y, Ding J, Yu P, He G, Chen Y, Chen H (2020) Low-temperature preparation of magnetically separable Fe3O4@ZnO-RGO for high-performance removal of methylene blue in visible light. J Alloys Compd 821:153366–153373
Buschow K (2006) Handbook of magnetic materials. Elsevier B. V, Amesterdam
Berry F, Greaves C, Helgason O, McManus J (1999) Synthesis and characterisation of tin-doped iron oxides. J Mater Chem 9:223–226
Haneda K, Morrish A (1977) Magnetite to maghemite transformation in ultrafine particles. J Phys Colloq 38:C1-321–C1-323
Khan U, Amanullah A, Manan N, Khan A, Mahmood A (2015) Rahim, transformation mechanism of magnetite nanoparticles. Mater Sci-Poland 33:278–285
Kolen’ko V, Bañobre-López M, Rodríguez-Abreu C, Carbó-Argibay E, Deepak F, Petrovyk D, Cerqueira M, Kamali S, Kovnir K, Shtansky D, Lebedev O, Rivas J (2014) High-temperature magnetism as a probe for structural and compositional uniformity in ligand-capped magnetite nanoparticles. J Phys Chem C 118:28322–28329
Berry F, Skinner S, Helgason Ö, Bilsborrow B, Marco J (1998) Location of tin and charge balance in materials of composition Fe3-xSnxO4 (x < 0.3). Polyhedron 17:149–152
Berry F, Helgason Ö, Jónsson K, Skinner S (1996) The high temperature properties of tin-doped magnetite. J Solid State Chem 122:353–357
Bhaumik A, Nori S, Sachan R, Gupta S, Kumar D, Majumdar A, Narayan J (2018) Room-temperature ferromagnetism and extraordinary hall effect in nanosrtuctured Q-carbon: implication for potential spintronic devices. ACS Appl Nano Mater 1:807–819
Lutterotti L (2010) Total pattern fitting for the combined size-strain-stress-texture determination in thin film diffraction. Nucl Instrum Methods Phys Res B 268:334–340
Fairly N (1999) CasaXPS application. In: N. CasaXPS (ed.), Casa software ltd, U.K.
Cao X, Prozorov R, Koltypin Y, Kataby G, Felner I, Gedanken A (1997) Synthesis of pure amorphous Fe2O3. J Mater Res 12:402–406
Mørup S, Topsøe H, Lipka J (1976) Modified theory for Mössbauer spectra of superparamagnetic particles: application to Fe3O4. J Phys Colloq 37:C6-287–C6-290
Rondinone AJ, Samia ACS, Zhang ZJ (1999) Superparamagnetic relaxation and magnetic anisotropy energy distribution in CoFe2O4 spinel ferrite nanocrystallites. J Phys Chem B 103:6876–6880
Kim W, Suh C-Y, Cho S-W, Roh K-M, Kwon H, Song K, Shon I-J (2012) A new method for the identification and quantification of magnetite-maghemite mixture using conventional X-ray diffraction technique. Talanta 94:348–352
Grosvenor AP, Kobe BA, McIntyre NS (2004) Studies of the oxidation of iron by water vapour using X-ray photoelectron spectroscopy and QUASES™. Surf Sci 572:217–227
Grosvenor AP, Kobe BA, Biesinger MC, McIntyre NS (2004) Investigation of multiplet splitting of Fe 2p XPS spectra and bonding in iron compounds. Surf Interface Anal 36:1564–1574
Yamaura M, Camilo R, Sampaio L, Maceedo M, Nakamura M, Tomad H (2004) Preparation and characterization of (3-aminopropyl) triethoxysilane-coated magnetite nanoparticles. J Mag Mag Mat 279:210–217
Aliahmad M, Moghaddam N (2013) Synthesis of maghemite (γ-Fe2O3) nanoparticles by thermal-decomposition of magnetite (Fe3O4) nanoparticles. Mater Sci-Poland 31:264–268
Rubim JC, Sousa MH, Silva JCO, Tourinho FA (2001) Raman spectroscopy as a powerful technique in the characterization of ferrofluids. Braz J Phys 31:402–408
Kodama R, Berkowitz A, McNiff E, Foner S (1996) Surface spin disorder in nanoparticles. Phys Rev Lett 77:394–397
Caizer C (2004) Deviations from Bloch law in the case of surfacted nanoparticles. Appl Phys A 80:1745–1751
Cojocaru S, Naddeo A, Citro R (2014) Modification of the Bloch law in ferromagnetic nanostructures. EPL 106:17001–17007
Kodama R (1999) Magnetic nanoparticles. J Magn Magn Mater 200:359–372
Mulyukov K, Musabirov I (2010) Influence of magnetic field intensity on the temperature dependence of magnetization of Ni2.08Mn0.96Ga0.96 Alloy. JEMAA 2:431–435
Acknowledgements
Great thanks to CAARU Center for X-ray diffraction measurement and A. Al-Nabhani, College of Medicine, for HR-TEM images.
Funding
This research is supported by Sultan Qaboos University (research grant: SQU/Sci/Phys/06/2016) U. S. H. Al-Kindi acknowledges the support of Sultan Qaboos University in the form of a PhD scholarship.
Author information
Authors and Affiliations
Contributions
U. S. H. Al-Kindi and Salim H. Al-Harthi design the experiment and write the manuscript. H. M. Widatallah and M. E. Elzain contribute in the discussion and correction of the manuscript. M. T. Z. Myint and H. H. Kyaw contribute in preparation of the manuscript. The author(s) read and approved the final manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Additional file 1: Figure S1.
TEM images of the SnxFe3-2x/3O4 samples with x = a: 0.000, b: 0.045, c: 0.090, d: 0.150 (The scale length = 20nm, insight: size distribution histogram of prepared nanoparticles. Figure S2. SEM/EDS X-ray elemental mapping of (a) Fe (green) (b) O (red) and (c) green/red overlay for pure Fe3O4 nanoparticles. Figure S3. SEM/EDS X-ray elemental mapping of (a) Fe (green) (b) O (red) (c) Sn (yellow) and (d) green/red/yellow overlay.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Al-Kindi, U.S.H., Al-Harthi, S.H., Widatallah, H.M. et al. Sn2+ Doping: A Strategy for Tuning of Fe3O4 Nanoparticles Magnetization Dipping Temperature/Amplitude, Irreversibility, and Curie Point. Nanoscale Res Lett 15, 192 (2020). https://doi.org/10.1186/s11671-020-03423-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-020-03423-9