Abstract
Optical properties and growth mechanism of La3Ga5.5Nb0.5O14 oxides by a Pechini process were investigated. The structure and morphology were obtained after sintering at 600–800 °C. This crystallized orthorhombic La3Ga5.5Nb0.5O14 can be obtained by the heat treatment process at 800 °C from XRD. A proposed schematic growth mechanism of La3Ga5.5Nb0.5O14 macroporous based on the details provided is shown. The photo-luminescence spectra shown that under 327 nm excitation spectra, a broad and blue emission peak is observed at 475 nm at 77 K and this spectrum is originated from the [NbO6]7− octahedra group. The optical absorption spectra of the 800 °C sample exhibited a well-crystalline and very low oxygen vacancy, which corresponded to the band gap energies of 3.95 eV.
Avoid common mistakes on your manuscript.
Introduction
The piezoelectric and optical properties of Ca3Ga2Ge4O14 (CGG)-type structure of La3Ga5SiO14 (LGS) [1], La3Ga5.5Nb0.5O14 (LGN) [2], and La3Ga5.5Ta0.5O14 (LGT) [3] compounds have been actively and systematically studied. They have been investigated for bulk acoustic wave (BAW) and surface acoustic wave (SAW) devices for the fabrication of filters with large pass bandwidths and oscillators with a large shift or high-frequency stability [4,5,6,7]. The piezoelectric and dielectric oxide has been applied in the optical field [8, 9]. A promising nonlinear oxide crystal La3Ga5.5Nb0.5O14 (LGN) is proposed and fully characterized in recent years. The mid-infrared spectral range extending from 2 to 6 μm is significant for scientific and technological applications [10]. The phase-matching angles of second-harmonic generation and difference-frequency generation up to 6.5 μm was also measured in the langanate crystal La3Ga5.5Nb0.5O14 (LGN) [11]. Voda et al. [12] reported that it was used both as a laser and a laser host material. Nd:La3Ga5.5Nb0.5O14 laser properties of output power and wavelength temperature tuning under laser diode pumping are also verified [13].
Macroporous materials have porosity ranging from 5 to 90% and pore size ranging more than 100 nm. Macroporous materials have diverse properties like excellent mechanical strength, high thermal conductivity, good chemical resistance, and high thermal shock resistance which led into the industrial applications like filtration for water and gas, thermoelectric convertor, catalytic agent [14]. Due to photonic band gaps, macroporous photonic crystals have been used for advanced applications such as optical communications, light emissions, and gas sensing. Macroporous photonic crystals of different materials can be used in chemical detections, and this led to explore different macroporous materials for gas sensing. Porous ceramics are of great interest due to their numerous potential applications in industries such as catalysis, adsorption and separation, filtration of molten metals or hot gases, refractory insulation of furnaces, and hard tissue repair and engineering [15].
Recently, very few works have been done on LGN-based macroporous ceramic formed by the chemical method. Yu [16] prepared piezoelectric crystal of La3Ga5.5Nb0.5O14 by using the sol-gel process and examined microstructure analysis. The results have shown that LGN nanoparticles were crystallized in the trigonal crystallographic phase. Kong [17] studied the growth of single-crystal La3Ga5.5Nb0.5O14 (LGN) by the Czochralski method which requires high temperature such as more than 1500 °C. In our study, macroporous polycrystal was developed by using the Pechini process which requires low temperature such as 800 °C. The polycrystal and the single crystal have the same orthorhombic phase. The main purpose of this work is to use a Pechini process for the preparation of a single-phase La3Ga5.5Nb0.5O14 LGN ceramic with the calciumgallogermanate (CGC-type) structure (trigonal, space group P321) [18]. The major advantage of the Pechini process is that there is a low-temperature processing [19,20,21]. Chemically synthesized ceramic powders often possess better chemical homogeneity and better size control of particle morphology than those produced by the mixed oxide route [22]. Therefore, the optical properties and growth mechanism of LGN macroporous oxide have been investigated in this study.
Methods/Experimental
Materials Used
Lanthanum nitrate La(NO3)3, gallium nitrate Ga(NO3)3, niobium chloride (NbCl5), citric acid anhydrous (CA), and ethylene glycol (EG).
Preparation of La3Ga5.5Nb0.5O14
The La3Ga5.5Nb0.5O14 macroporous ceramics were prepared by the Pechini process using lanthanum nitrate La(NO3)3, gallium nitrate Ga(NO3)3, niobium chloride (NbCl5), citric acid anhydrous (CA), and ethylene glycol (EG). All materials have over 99.9% purities. According to the reaction, niobium ethoxide, Nb(OC2H5)5 synthesis takes place from niobium chloride NbCl5 and ethanol, C2H5OH.
The stoichiometric amount of lanthanum nitrate, gallium nitrate, and niobium ethoxide was dissolved in water. A chelating agent such as citric acid is added to the solution. The molar ratio of citric acid and metal ions used in this process is 2:1. A stabilizing agent such as ethylene glycol is added to the above solution. The precursor containing La, Ga, and Nb were dried in an oven at 120 °C for 24 h, and then, the La3Ga5.5Nb0.5O14 ceramics were obtained after sintering at 600–800 °C for 3 h in air.
Characterization/Phase Identification
The burnout behaviors of powders were analyzed by differential thermal analysis and thermogravimetry analysis (DTA–TGA, PE–DMA 7). The phase identification was performed by X-ray powder diffraction (Rigaku Dmax-33). The morphology and microstructure were examined by transmission electron microscopy (HR-TEM, HF-2000, Hitachi). The excitation and emission spectra were recorded on a Hitachi-4500 fluorescence spectrophotometer equipped with xenon lamp at 300 K and 77 K. The absorption spectra were measured using a Hitachi U-3010 UV–vis spectrophotometer at room temperature.
Results and Discussion
The amorphous compound is subjected to heat treatment to undergo pyrolysis process to become crystalline structure. In this experiment, the possible chemical reactions for the synthesis of La3Ga5.5Nb0.5O3 powders can be expressed as follows:
This precursor powder is heat-treated for about 3 h at 600–800 °C, and the XRD patterns for this temperature are shown in Fig. 1. At 600 °C calcined temperature, the precursor powder has shown its small amount of microcrystal structure. When the temperature raised to 700 °C, decomposition of amorphous powder takes place and it begins to crystallize. When the sintered temperature reaches 800 °C, the precursor powder sample is shown in a single phase which is orthorhombic La3Ga5.5Nb0.5O14 phase (JCPDS file no. 47-0533) where the peaks are identified. This sharper peak shows that the crystalline form of the La3Ga5.5Nb0.5O14 powder. With the increase in temperature, the intensity of the peaks becomes sharper which indicates the crystalline structure of the La3Ga5.5Nb0.5O14 powder.
The FT-IR spectra of the powder at 600–800 °C are shown in Fig. 2. Figure 2a, b shows the IR spectra of powder at 600 to 700 °C, respectively, where there is a sharp stretch at 2300 nm wavelength which identifies the presence of strong carbon dioxide compound class stretching and there is a bulk stretch at 1500 nm wavelength which indicates the absorbed nitrate ions in the structure [14]. So, these might be the strong stretching vibrations of nitrate ions. From Fig. 2c, there are new peaks formed at 500 to 600 nm when the annealing temperature is increased to 800 °C. This new peak indicates the formation of the La3Ga5.5Nb0.5O14 nanocrystals. The peaks present at 1500 nm and 2300 nm wavelength are calcined at 800 °C. This shows the presence of little residues in the organic compound.
TEM images of the precursor powder at 600 °C for the morphology are shown in Fig. 3. The first image shows the size and shape morphology of the precursor ceramic. From the figure, different sizes of nanofoams are present in the precursor powder. The second image is the enlarged version and side view of the first image. It is shown that bulged nanofoams are present on the surface of the precursor at the beginning of crystal formation. These nanofoams are of different sizes as seen from the image. These nanofoams have a low thickness, and when the temperature increases, these nanofoams form microporous holes. This shows the particles have a semi-circular shape which is hollow inside. This nanoporous material is a nanofoam which contains gas inside of it. When the temperature will increase, these nanofoams will leave a hole of diameter less than 100 nm.
TEM images of different magnification is showed in Fig. 4. In the Fig. 4(a), the magnification is very low which is 100 nm and the structure visibility is not good. In Fig. 4(b) the TEM image is magnified to 10 nm and crystal structure can be seen. In Fig. 4(c) image is enlarged to 5 nm. Fig. 4(d) represents the small amount of micro crystal structure.
TEM analysis for the crystal at 800 °C is shown in Fig. 5. The first Fig. 5a magnification is very low which shows the nanocomposition of the crystal form. Figure 5b is a highly magnified image of the crystal where the structure of the macroporous crystal is seen. The bright images are the air holes which are formed from the nanofoams. Electron diffraction of the La3Ga5.5Nb0.5O14 crystalline structure is shown in Fig. 5c. There are circular bright continuous rings in the electron diffraction pattern. This indicates that the particles were nanosized, and it also confirms the crystalline nature of the nanoparticles [23]. EDX analysis of La3Ga5.5Nb0.5O14 macroporous oxide is shown in Fig. 5d. This analysis shows about the molar ratio of the structure La3Ga5.5Nb0.5O14. The peak of Ga is high which indicates it has more content. Nb has a very low peak since it is very less in content.
A proposed schematic growth mechanism of La3Ga5.5Nb0.5O14 macroporous based on the details provided is shown in Fig. 6. In this process, synthesized macroporous oxide forms crystals at 600 °C as shown in the schematic Fig. 5a. As mentioned, the precursor powder is at 600 °C, and it has nanofoams which are nanostructured porous materials with diameters less than 100 nm. These nanofoams are bulk nanoporous materials with enlarged form and very low thickness. The formation of nanofoams takes place because of heating in the presence of oxygen. At this stage, the precursor is in non-crystalline form. When the annealing temperature is increased to 700 °C, the bulky nanofoams will pop-out due to less thickness, and it leaves a hole of diameter less than 100 nm. These nanofoams are bulk nanoporous materials which are filled with either liquid or gas. In this case, these nanofoams are filled with gas either oxygen or carbon dioxide. At this stage, the precursor is in non-crystalline form. When the annealing temperature is increased to 700 °C, these nanofoams which are hollow inside will pop-out leaving a hole of diameter less than 100 nm. During the 600 to 700 °C annealing process, these nanofoams tend to grow size bigger and eventually form macroporous holes. At the same time, a lot of microcrystals are formed in an irregular order around the nanofoam holes. After the nanofoams collapsed and sintering occurred, the grain size will grow and inter-facial energy will be decreased [24] (Fig. 6).
When the annealing temperature is increased to 800 °C, the microcrystals form into crystal grains which are hard, and these grains are separated by the boundary grains. In this process, the collapse rate of nanofoams is directly proportional to the crystallization process. If the calcined temperatures are increased, it encourages the growth of the oxide crystals. The structure formed will be crystallized, and the macroporous holes will be formed which are of different sizes ranging from 50 to 100 nm.
The emission spectra of the La3Ga5.5Nb0.5O14 samples at 77 K and 300 K are shown in Fig. 7. Photo-luminescence results show that the sample prepared at 77 K have exhibited emission spectra at 475 nm than the sample at room temperature 300 K. The ideal state temperature for the sample is 77 K, and at this temperature, there will be no thermal vibrations which affect the procedure. According to Blasse [25], there are two kinds of absorbing groups in niobate complexes which are [NbO6]7− and [NbO4]3−. At 327 nm excitation spectra, there was only one peak appeared which corresponds to the [NbO6]7− complex group. This indicates that the charge transfer happened in the bands of [NbO6]7− in the La3Ga5.5Nb0.5O14 system. So here, the crystal structure of La3Ga5.5Nb0.5O14 might be built up by the edge-sharing of NbO6 trigonal prisms.
The PL emission spectra showed a strong blue emission spectra peak at 457 nm. Here, the luminescence effect depends on the Nb–O–Nb bonding where the conduction band consists of Nb5+ 4d orbitals and the valance band of O2− 2p orbitals between the corner-sharing octahedral [26]. A strong temperature dependence of the emission peak was observed. The intensity of the emission peak reduced rapidly and nearly disappears when the temperature increased from 77 to 300 K. The quenching of the emission peak should be attributed to two reasons for thermal quenching effect in macroporous La3Ga5.5Nb0.5O14 ceramic. The one is that non-radiative transition results in the heat by transfer of energy to phonons in the lattices; another one is that the elections could be trapped by any possible defects in the lattices; and it is well known that the trap centers in niobate complexes, which could have an important quenching effect on luminescence [27, 28].
UV-Vis absorption spectra of the La3Ga5.5Nb0.5O14 macroporous particles are measured, and band gap is estimated from the absorption spectra in Fig. 8. The absorption luminescence has a maximum intensity of 260 nm which corresponds with the excitation spectra. The absorbance in the vicinity of the onset due to the electronic transition for a given semiconductor is given by the following equation:
where α is the absorption coefficient, C is the constant, hν is the photon energy, and Eg is the band gap. The inset of Fig. 8 shows the relationship of (αhν)2 and hν. The inset in Fig. 8 shows the band gap of 3.95 eV. In the experiment, there are little bumps present at about 320 nm from 600 to 800 °C. These bumps indicate the presence of oxygen vacancy defect [29]. At 800 °C annealing temperature, the organic compound fiercely burnt very rapidly, and this consumed a great amount of oxygen. It is also noted that the defects are high at 600 °C, and with the increase in temperature, these vacancy defects are reduced.
Conclusions
La3Ga5.5Nb0.5O14 macroporous polycrystal is prepared by a Pechini process using NbCl5, Ga(NO3)3, and La(NO3)3. This crystallized orthorhombic La3Ga5.5Nb0.5O14 can be obtained by the heat treatment process at 800 °C from XRD. The excitation wavelength is about 327 nm, and this is associated with charge transfer bands of Nb5+ and O2− ions in a tetrahedral co-ordination. The photo-luminescence spectra shown that under 327 nm excitation spectra, a broad and blue emission peak is observed at 475 nm and this spectrum is originated from the [NbO6]7− octahedra group. The visible light absorption edge of 800 °C sample was at 320 nm, which corresponded to the band gap energies of 3.95 eV.
Availability of data and materials
The authors declare that the materials and data are promptly available to readers without undue qualifications in material transfer agreements. All data generated in this study are included in this article.
Abbreviations
- BAW:
-
Bulk acoustic wave
- CA:
-
Citric acid
- CGC:
-
Calciumgallogermanate
- DTA:
-
Differential thermal analysis
- EDX:
-
Energy dispersive X-ray analysis
- E g :
-
Band gap
- EG:
-
Ethylene glycol
- FTIR:
-
Fourier-transform infrared spectroscopy
- hν:
-
Photon energy
- PL:
-
Photoluminescence
- SAW:
-
Surface acoustic wave
- TEM:
-
Transmission electron microscopy
- TGA:
-
Thermogravimetry analysis
- UV-vis:
-
Ultraviolet-visible
- XRD:
-
X-ray powder diffraction
References
Adachi M, Karaki T, Miyamoto W (1999) Surface acoustic wave properties of La3Ga5SiO14 (LANGASITE) single crystals. Jpn J Appl Phys 38:3283
Takeda H, Shimamura K (1996) Growth and characterization of La3Nb0.5Ga5.5O14 single crystals. Takuya Kohno and Tsuguo Fukuda, J Crystal Growth 169:503
Boutahraoui B, Nehari A, Boy J, Vacheret X, Allani M, Cabane H, Dumortier M, Derbal M, Lebbou K (2017) LGT (La3Ga5.5Ta0.5O14) langatate bulk crystal grown from the melt by Czochralski technique and characterization. Opt Mater 65:103
Fritze H, Tuller HL (2001) Langasite for high-temperature bulk acoustic wave applications. Appl Phys Lett 78:976
Zheng P, Greve DW, Oppenheim IJ (2013) Langasite surface acoustic wave gas sensors: modeling and verification. IEEE Trans Ultrason Ferroelectr Freq Control 60:579
Pereira da Cunha M, Malocha DC, Adler EL, Casey KJ (2002) Surface and pseudo surface acoustic waves in langatate: predictions and measurements. IEEE Trans Ultrason Ferroelectr Freq Control 49(9):1291
Wu S, Yan GJ, Lee MS, Ro RY, Chen KI (2007) Sputtering ZnO films on langasite and its saw properties. IEEE Trans Ultrason Ferroelectr Freq Control 54(12):2456
Long C, Li T, Fan H, YunWu LZ, Li Y, Xiao L, Li Y (2016) Li-substituted K0.5Na0.5NbO3-based piezoelectric ceramics: crystal structures and the effect of atmosphere on electrical properties. J Alloys Compd 658:839e847
Liu Z, Fan H, Zhao Y, Dong G (2016) Optical and tunable dielectric properties of K0.5Na0.5NbO3-SrTiO3 ceramics. J Am Ceram Soc 99:146–151
Lu D, Xu T, Yu H, Fu Q, Zhang H, Segonds P, Boulanger B, Zhang X, Wang J (2016) Acentric langanite La3Ga5.5Nb0.5O14 crystal: a new nonlinear crystal for the generation of mid-infrared parametric light. Optics Express 24(16):17603
Guo F, Lu D, Segonds P, Debray J, Yu H, Zhang H, Wang J, Boulanger B (2018) Phase-matching properties and refined Sellmeier equations of La3Ga5.5Nb0.5O14. Opt Mater Express 8(4):858
Voda M, García Solé J, Jaque F, Vergara I, Kaminskii A, Mill B, Butashin A (1994) Fano antiresonances in the optical-absorption spectra of Cr3+ doped La3Ga5.5Nb0.5O14 and La3Ga5.5Ta0.5O14 crystals. Phys Rev B49:3755
Demidovich AA, Shkadarevich AP, Batay LE, Kuzmin AN, Ryabtsev GI, Strek W, Kaminskii AA (1997) Nd:La3Ga5.5Nb0.5O14 laser properties under LD pumping. In: Proc. SPIE 3176, Tunable Solid State Lasers, pp 269–271
Studart AR, Gonzenbach UT, Tervoort E, Gauckler LJ (2006) Processing routes to macroporous ceramics: a review. J Am Ceram Soc 89(6):1771
Eom JH, Kim YW, Raju S (2013) Processing and properties of macroporous silicon carbide ceramics: a review. J Asian Ceram Soc 1:220
Yu FP, Yuan DR, Duan XL, Kong LM, Shi XZ, Guo SY, Wang LH, Cheng XF, Wang XQ (2008) Citrate sol–gel method to prepare nanoparticles of a piezoelectric crystal material: La3Nb0.5Ga5.5O14 at low temperature. J Alloy and Compd 459:L1–L4
Kong H, Wang J, Zhang H, Yin X (2006) Growth and characterization of La3Ga5.5Nb0.5O14 crystal. J Cryst Growth 292:408
Mill BV, Butashin AV, Kodzhabagian GG, Belokoneva EL, Belov NV (1982) Modified rare earth gallates with Ca3Ga2Ge4O14 structure. Doklady Akademii Nauk SSSR 264:1385
Qiu S, Fan H, Zheng X (2007) Pb(Zr0.95Ti0.05)O3 powders synthesized by Pechini method: effect of molecular weight of polyester on the phase and morphology. J Sol-Gel Sci Techn 42:21
Qiu S, Zheng X, Gao C, Gan X, Chen J, Yang C, Fan H (2009) Pb(Zr0.95Ti0.05)O3 powders and porous ceramics prepared by one-step pyrolysis process using non-aqueous Pechini method. Ceram Inter 35:733
Qiu S, Fan H, Yang C, Chen J (2007) Porous Pb(Zr0.95Ti0.05)O3 ceramics from chemically prepared powders without pore formers. J Am Ceram Soc 10:3293
Hsiao YJ, Chang YH, Chang YS, Fang TH (2007) Low-temperature preparation of Ba5Nb4O15 ceramics through a sol-gel process. J Am Ceram Soc 97:2287
Upadhyay RH, Agrekar AP, Deshmukh RR (2014) Characterization, dielectric and electrical behaviour of BaTiO3 nanoparticles prepared via titanium(IV) triethanolaminato isopropoxide and hydrated barium hydroxide. Bull Mater Sci 37:481
Lai WH, Teoh LG, Su YH, Shieh J, Hon MH (2007) Effect of calcination on crystallinity for nanostructured development of wormhole-like mesoporous tungsten oxide. J Am Ceram Soc 90:4073
Dirksen GJ, Hoffman ANJM, van de Bout TP, Laudy MPG, Blasse G (1991) Luminescence spectra of pure and doped GaBO3 and LiGaO2. J Mater Chem 1:1001
Hsiao YJ, Liu CW, Dai BT, Chang YH (2009) Sol–Gel synthesis and the luminescent properties of CaNb2O6 phosphor powders. J Alloy Compd 475:698
Shi S, Wang P, Cui J, Sun Z (2018) Microstructure and doping/temperature-dependent photoluminescence of ZnO nanospears array prepared by hydrothermal method. Nanoscale Res Lett 13:223
Liu X, Huang X, Li J, Yadav SK, Gleiter H, Kong H, Feng T, Fuchs H (2016) Observation of intrinsic emission in β-BiNbO4 available for excitation of both UV light and high energy irradiation. Phys Chem Chem Phys 18:23702
Zhang A, Lü M, Wang S, Zhou G, Wang S, Zhou Y (2007) Novel photoluminescence of SrZrO3 nanocrystals synthesized through a facile combustion method. J Alloy Compd 433:L7
Acknowledgements
We thank the Taiwan Semiconductor Research Institute (TSRI) and Professor Guo-Ju Chen from I-Shou University for technical support.
Funding
The authors would like to thank the Ministry of Science and Technology of Taiwan for financially supporting this research under contract No. MOST 107-2221-E-218-032-MY2 and MOST 107-2218-E-492-007.
Author information
Authors and Affiliations
Contributions
YJH initiated the idea of the experiment and conducted the experiment. YN and SCW helped with the results and discussion. YJH, YN, and SCW collectively wrote the manuscript and revised the manuscript. All the authors approved the final manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare that they have no competing interests.
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Hsiao, YJ., Nagarjuna, Y. & Wang, SC. Optical Properties and Growth Mechanism of La3Ga5.5Nb0.5O14 Macroporous Ceramic. Nanoscale Res Lett 14, 282 (2019). https://doi.org/10.1186/s11671-019-3104-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-019-3104-x