Abstract
We performed a systematic study of the influence of environmental conditions on the electrical performance characteristics of solution-processed 2,7-dioctyl [1] benzothieno[3,2-b][1]-benzothiophene (C8-BTBT) thin-film transistors (TFTs). Four environmental exposure conditions were considered: high vacuum (HV), O2, N2, and air. The devices exposed to O2 and N2 for 2 h performed in a manner similar to that of the device kept in HV. However, the device exposed to air for 2 h exhibited significantly better electrical properties than its counterparts. The average and highest carrier mobility of the 70 air-exposed C8-BTBT TFTs were 4.82 and 8.07 cm2V-1s-1, respectively. This can be compared to 2.76 cm2V-1s-1 and 4.70 cm2V-1s-1, respectively, for the 70 devices kept in HV. Furthermore, device air stability was investigated. The electrical performance of C8-BTBT TFTs degrades after long periods of air exposure. Our work improves knowledge of charge transport behavior and mechanisms in C8-BTBT OTFTs. It also provides ideas that may help to improve device electrical performance further.
Avoid common mistakes on your manuscript.
Introduction
Due to the advantages of low deposition temperature, high mechanical flexibility, low cost, and large area production, organic semiconductor materials have recently been widely investigated for various electronic device applications such as organic light-emitting diodes, organic photovoltaic devices, and organic field-effect transistors [1,2,3,4]. Organic semiconductors can be divided into two main categories: conjugated polymers and small molecule organic semiconductors [3]. Compared with conjugated polymers, small molecule organic semiconductors offer high degrees of ordering, stacking density, and material purity. These advantages facilitate the fabrication of high-performance devices [5,6,7,8]. C8-BTBT is a representative small molecule organic semiconductor material [5]. Extensive research has been performed to study its charge transport mechanisms [9], low-cost fabrication methods [10, 11], growth and microstructure formation on various substrates [12,13,14], metal/semiconductor contact characteristics [15, 16], and strategies to increase its carrier mobility [11, 17,18,19]. Thus far, there is no systematic study on the impact of ambient gases on the electrical performance of C8-BTBT-based devices. On the one hand, environmentally induced changes to the electrical performance characteristics of such organic devices are a critical problem that must be solved to provide stable operation for future commercial applications. On the other hand, such effects imply the potential for use of C8-BTBT-based devices as gas sensors.
In this study, C8-BTBT organic semiconductor films were fabricated via solution processing. The electrical properties of the C8-BTBT-based OTFTs were investigated in various ambient gases. The C8-BTBT OTFTs exhibited their highest carrier mobilities (~ 8 cm2V-1s-1) after exposure to air for 2 h. This is assumed to be closely related to the moisture in the air. The study also revealed that changes in the internal molecular structure play important roles in the electrical performance of the OTFTs. The present work not only deepened the understanding on the charge transport mechanisms and structural changes in C8-BTBT films but also provides new ideas to further improve their electrical performances.
Methods
C8-BTBT Deposition and OTFT Device Fabrication
A highly doped p-type silicon (100) wafer with a 50 nm thermally oxidized SiO2 layer was used as the substrate for organic thin-film transistor preparation. The Si wafer was used as the bottom gate electrode, and the SiO2 layer acted as the gate insulator. The substrates were cleaned with acetone, isopropanol, and deionized water for 5 min each using an ultrasonic cleaner. To ensure that the substrate surfaces were clean and dry, the substrates were dried on a hot plate in air for 15 min at 120 °C. In order to change the surface hydrophobicity, all the samples received a UV-ozone treatment for 1 min. This treatment time was chosen based on our previous results [10]. In a previous study, a C8-BTBT OTFT exposed to 1 min of UV surface treatment exhibited better electrical performance than those exposed to other UV treatment durations or non-UV treatment. The organic semiconductor layer was made from high-purity C8-BTBT (≥ 99%) (Sigma-Aldrich) and PMMA (Aladdin) dissolved in chlorobenzene. The solution (0.5 wt% C8-BTBT and 0.5 wt% PMMA) was spin-coated onto 50 nm SiO2 covered p++ substrate (2000 rpm for 40 s). Each spin-coating cycle produced one 45 nm layer of C8-BTBT film. After annealing at 60 °C for 2 h in air, MoO3 (5 nm) was deposited via thermal evaporation through a metal mask. This buffer layer was designed to reduce the contact barrier between the Au electrode and C8-BTBT semiconductor and to improve charge injection. Finally, Au source and drain electrodes (40 nm) were fabricated via thermal evaporation using the same MoO3 shadow mask. The resulting transistor devices had various channel lengths that ranged from 50 to 350 μm, but the same channel width of 1200 μm.
Material and Device Characterization
An Agilent B1500A semiconductor device analyzer was used to measure device electrical performance. Surface morphologies and roughnesses were observed via tapping mode atomic force microscopy (Asylum Research). Raman spectroscopy characterizations were performed using a Renishaw in Via Raman Microscope. The C8-BTBT layer thickness was measured using an ellipsometer.
Before their electrical performance measurements, the devices were stored in specific environmental conditions (high vacuum, N2, O2, air) for 2 h so that they would be fully exposed to the desired gases. For convenience, the devices exposed to high vacuum (1.3 × 10−5 Torr), N2, O2, and air will be referred to as the HV, N2, O2, and air devices, respectively. For each environmental condition or ambient gas, 70 devices were measured in order to produce reliable and statistically meaningful electrical performance results. In addition, the electrical performance of one sample was monitored as a function of the air exposure time to study its stability in air.
Results and Discussion
The cross-sectional structure of the OTFT device is shown schematically in Fig. 1a. From bottom to top, it consists of a highly doped Si substrate, 50 nm of silicon oxide, 45 nm of C8-BTBT film, and Au(40 nm)/MoO3(5 nm) electrodes. Au/MoO3 source/drain electrodes were used to reduce the contact barrier between the Au electrodes and C8-BTBT, which can help to increase the charge injection efficiency and produce high-mobility devices [10]. Figure 1b shows the molecular structures of C8-BTBT, MoO3, and PMMA. It should be noticed that PMMA was added into C8-BTBT to make a mixed solution in our work. Blending a polymer into a small molecule organic semiconductor is a common method to improve electrical performances of an organic semiconductor. It helps to form a smooth, continuous semiconductor film. In addition, differences in mass induce vertical phase separation, which is expected to reduce the number of surface traps in the semiconductor [19]. An AFM surface morphology image of the C8-BTBT thin film is shown in Fig. 1c. It indicates large grain-size, good surface continuity, and a smooth surface morphology (RMS value 2.081 nm). Figure 1d shows schematic diagrams of the test procedures used with samples that had been exposed to HV, nitrogen, oxygen, and air. For each ambient gas, 70 devices were measured after 2 h of exposure.
To clarify how the different ambient gases affect device electrical performance, the transfer characteristics of these four device types were compared. Figure 2a and 2b show typical drain current-gate voltage (ID-VG) curves of short channel (L = 50 μm) and long channel (L = 350 μm) devices, respectively. All of the devices have the same channel width of 1200 μm and were measured using the same − 40 V drain voltage. No significant hysteresis loops are observed regardless of gas exposure or channel length. An obvious decrease in the off-state drain current (Ioff) and increase in the on-state drain current (Ion) are observed for the device exposed to air. Its on/off drain current ratio is as high as 107, while those of HV devices, O2 devices, and N2 devices are 106. In addition, the air device exhibits carrier mobility that is almost twice as high as those of the other devices and a VTH that is 5 to 8 V lower. The results shown in Fig. 2a and 2b demonstrate that the device exposed to air for 2 h exhibits better electrical properties than those exposed to other ambient gases. Typical transfer (VD = − 40 V) and output characteristics of air devices with a channel length of 350 μm are shown in Fig. 2c and 2d, respectively. These figures show the outstanding electrical performance characteristics of the solution processed C8-BTBT transistors. A well-saturated ID-VG curve, large Ion/Ioff of 107, and high carrier mobility of 8.07 cm2V-1s-1 are observed. The small hysteresis loop shown in Fig. 2c indicates that an imperfect interface is present between the C8-BTBT and SiO2. The non-linear ID-VD curves at low drain voltage shown in Fig. 2d indicate that the potential barrier at the contact interface is still not low enough for ohmic conduction, despite the use of a MoO3 layer to reduce the interfacial barrier between the S/D electrodes and semiconductor. The electrical performance of the air device can be further improved via future interface optimization.
In order to get reliable and statistical data, we measured a total of 280 devices (70 devices for each environmental condition). The carrier mobility and threshold voltage experimental results are summarized and plotted as histograms in Fig. 3a and 3b. In addition, the average carrier mobilities, highest carrier mobilities, and average threshold voltages of devices exposed to various ambient gases are shown in Table 1. The highest average carrier mobility (4.82 cm2V-1s-1) and lowest threshold voltage (− 20.16 V) are observed with devices exposed to air. Thus, air-exposed devices exhibit the best electrical performances of the device types tested. The HV device, N2 device, and O2 device histograms indicate only slight differences in average carrier mobility, highest carrier mobility, and threshold voltage. It is known that air is composed of nitrogen (78%), oxygen (21%), moisture, etc. The HV, N2, and O2 devices exhibit similar electrical characteristics, which indicates that exposure to N2 and O2 does not produce significant performance differences relative to an HV device. One can assume that moisture plays a key role in improving the electrical performance of the air device. The relative humidity range during these experiments was 40–59%. Consequently, it is likely that H2O in the air affects device performance.
In order to understand gas exposure-based variation in the electrical properties of these C8-BTBT-based transistors, we measured ID-VG curves of devices with channel lengths of 50 to 350 μm. Metal/semiconductor contact resistances (RC) were investigated for all four device types. We performed RC extraction using the transfer line method, which is based on the following linear regime equation (1): [20].
Figure 3c shows the total resistances (Rtotal) of devices exposed to different environmental conditions as functions of channel length. The RC values are extracted from the y-intercepts of the fitting lines and plotted by exposure gas. RC values are compared in Fig. 3d based on the results shown in Fig. 3c. Only small differences between the HV, N2, and O2 devices are noted. However, the air device exhibits a significant reduction in RC. The average carrier mobilities and average threshold voltages are summarized in Fig. 3e and 3f, respectively. The air devices exhibit much higher carrier mobilities and lower threshold voltages than their counterparts. The RC values, average and highest carrier mobilities, and threshold voltages of the four device types are summarized in Table 1. Based on the results shown in Fig. 3d–f and Table 1, we can conclude that the improved electrical properties exhibited by the air devices are closely related to the reduced contact resistance between the C8-BTBT semiconductor and source/drain electrodes. Furthermore, the N2 and O2 device electrical properties do not deviate significantly from each other or those of the HV device. This indicates that the reduced RC values that drive increased carrier mobilities and decreased threshold voltages are caused by H2O in air, rather than N2 or O2 concentrations. The mechanisms of this interaction are not clear, but we assume that hydronium and hydroxyl anions from H2O may passivate traps and defects in C8-BTBT semiconductors. Our present results provide further insights into the role of air in reducing contact resistances and improving overall electrical performance.
To further understand the mechanisms that drive differences in device electrical performance, we performed Raman spectra measurements of C8-BTBT films exposed to various environmental conditions. Figure 4a compares the Raman spectra of C8-BTBT films exposed to HV and air. Only the 1300 cm−1–1600 cm−1 spectral range is shown since these peaks are typically associated with C8-BTBT molecules and all of the charge sensitive bands lie in this region. Typically, C8-BTBT molecules orient themselves with the long-axis (c-axis) direction along the SiO2/Si substrate. A herringbone arrangement of BTBT core parts appears in the in-plane direction [14]. Thiophene peaks are located at 1314 cm−1 and 1465 cm−1, while the C–H in-plane peak appears at 1547 cm−1 [6, 21]. The Raman spectra of C8-BTBT samples exposed to HV, O2, and N2 do not exhibit significant differences. When the sample is exposed to air for a period of time, it exhibits Davydov splitting at 1547 cm−1 due to interactions between the hydroxyl anion from water and hydrogen from C–H groups. [22] The C–H bond from stacking of C8-BTBT molecules is typically suspended on the surface [14]. Thus, it can easily interact with moisture in the air and increase the carrier mobility via enhanced π-π and van der Waals interactions [5, 9]. This result provides further support for our previous assumption that hydroxyl anions passivate traps in the C8-BTBT films.
As Irfan et al. reported [23], the work function (WF) of the thermally evaporated 5.5 nm MoOx is 6.82 eV. However, this decreases by 1.18 to 5.64 eV after 1 h of air exposure. The reduction in WF upon air exposure may be due to moisture adsorption on the film surface. Based on the results shown by Irfan et al., we proposed a model that describes the effect of air exposure on C8-BTBT contact resistance and electrical performance (Fig. 4b) [9, 19, 23]. It is assumed that reducing the height of the contact barrier between the metal and the semiconductor would improve the carrier injection efficiency, reduce the contact resistance, and increase the carrier mobility. Another possible mechanism of RC reduction is passivation of traps in the interface between C8-BTBT and the Au/MoO3 electrode. According to Wang et al., the metal/semiconductor interfacial trap density significantly affects the interfacial contact resistance [24]. In the present work, hydronium from water passivates interfacial traps, producing an RC reduction.
Finally, the air stability of the C8-BTBT OTFTs was investigated. We measured the electrical properties of C8-BTBT devices that had been exposed to air for up to 9120 min (~ 1 week). Figure 5a compares ID-VG characteristics of devices with air exposure times of 0 min, 2 h, and 9120 min. The carrier mobility is shown as a function of air exposure duration in Fig. 5b. The carrier mobility of a non-air exposed device is 1.97 cm2V-1s-1. The mobility increases with the air exposure duration until this duration reaches 4 h. The highest carrier mobility (3.08 cm2V-1s-1) is achieved after an air exposure time of 2 to 4 h. Further monitoring of the carrier mobility shows that it decreases gradually with additional air exposure. The carrier mobility decreases to 1.61 cm2V-1s-1 after the device has been exposed to air for 9120 mins (approximately 1 week). This carrier mobility degradation may occur because the channel is readily oxidized by moisture as shown below in Eq. (2) [25]. In this equation, OSC and OSC+ represent the organic semiconductor and molecular cation, respectively.
After a period of air exposure, moisture adsorption induces unoccupied states above the HOMO and generates deep hole traps, which significantly degrade carrier transport in the channel and increase the contact resistance [24]. Gomes et al. and Peter et al. have demonstrated that water on the surface of SiO2 plays an important role in p-type OTFTs. Due to the Si–O–H ↔ Si–O− + H+ reaction, a significant amount of hydronium is present in the absorbed water layer [26]. In addition, mobile charges in the semiconductor are slowly replaced by immobile charges at the SiO2 surface that can reversibly migrate into bulk SiO2. Therefore, exposure to air for a long time, constant absorption and interaction of moisture will lead to increased transistor instability [27] and reduce its carrier mobility.
Using a comparative study of devices exposed to various gas environments, we demonstrated that moisture in the air has a significant impact on the electrical performance characteristics of C8-BTBT-OTFT devices. We also found that an appropriate air-exposure time can improve device electrical performance but a long exposure time degrades it. It is widely believed that exposing organic devices to air is harmful to their electrical properties. The present work also demonstrates the positive role of moisture in passivating C8-BTBT semiconductor traps and lowering RC values. It also provides useful insights into the ideas that may improve C8-BTBT OTFT device performance and improve knowledge of their air stability.
Conclusions
In summary, we have investigated the effects of ambient gases on the electrical properties of solution-processed C8-BTBT OTFTs. The electrical properties of devices exposed to various ambient gases (HV, O2, N2, and air) were compared. We observed that the electrical properties of the O2 device and N2 device varied little relative to the HV device. However, a significant improvement in electrical properties was observed with the air device. For the 70 devices with 2 h of air exposure, the average and highest carrier mobilities were 4.82 and 8.07 cm2V-1s-1, respectively. This compares to 2.76 and 4.70 cm2V-1s-1 for HV devices. The lowest threshold voltages were also observed using the air devices. The improved electrical performance of the air device is thought to be due to reduced contact resistance and decreased MoO3 work function after air exposure. In addition, C8-BTBT OTFT air-stability was investigated. The electrical performance degraded upon exposure to air for more than 4 h. This work provides a systematic understanding of the influence of environmental conditions on the electrical performance characteristics of solution processed C8-BTBT OTFTs. It aids in the development of high performance, air-stable, printable OTFT devices.
Abbreviations
- AFM:
-
Atomic force microscopy
- Au:
-
Gold
- C8-BTBT:
-
2,7-dioctyl [1] benzothieno[3,2-b][1]-benzothiophene
- HOMO:
-
Highest occupied molecular orbital
- HV:
-
High vacuum
- I D :
-
Drain current
- L:
-
Channel length
- MoO3 :
-
Molybdenum oxide
- OTFTs/OTFT:
-
Organic thin-film transistors
- PMMA:
-
Polymethyl methacrylate
- R C :
-
Contact resistance
- RMS:
-
Root mean square
- R total :
-
Total resistances
- TFTs:
-
Thin-film transistors
- V G :
-
Gate voltage
- W :
-
Channel width
References
Gelinck G, Heremans P, Nomoto K, Anthopoulos TD (2010) Organic transistors in optical displays and microelectronic applications. Adv Mater 22:3778–3798
Paterson AF, Singh S, Fallon K, Hodsden T, Han Y, Schroeder BC, Bronstein H, Heeney M, McCulloch I, Anthopoulos TD (2018) Recent progress in high-mobility organic transistors: a reality check. Adv Mater 30:1–33
Dimitrakopoulos CD, Malenfant PRL (2002) Organic thin film transistors for large area electronics. Adv Mater 14:99–117
Klauk H (2010) Organic thin-film transistors. Chem Soc Rev 39:2643–2666
Izawa T, Miyazaki E, Takimiya K (2008) Molecular ordering of high-performance soluble molecular semiconductors and re-evaluation of their field-effect transistor characteristics. Adv Mater 20:3388–3392
Li Y, Liu C, Lee MV, Xu Y, Wang X, Shi Y, Tsukagoshi K (2013) In situ purification to eliminate the influence of impurities in solution-processed organic crystals for transistor arrays. J Mater Chem C 1:1352–1358
Shao Y, Zhang Y, He WQ, Liu C, Minari T, Wu SJ, Zeng M, Zhang Z, Gao XS, Lu XB, Liu J-M (2015) Role of growth temperature on the frequency response characteristics of pentacene-based organic devices. Semicond Sci Technol 30:035005
Mannsfeld SCB, Virkar A, Reese C, Toney MF, Bao ZN (2009) Precise structure of pentacene monolayers on amorphous silicon oxide and relation to charge transport. Adv Mater 21:2294–2298
Kobayashi H, Kobayashi N, Hosoi S, Koshitani N, Murakami D, Shirasawa R, Kudo Y, Hobara D, Tokita Y, Itabashi M (2013) Hopping and band mobilities of pentacene, rubrene, and 2,7-dioctyl[1] benzothieno[3,2-b][1] benzothiophene (C8-BTBT) from first principle calculations. J Chem Phys 139:014707
Wei WY, Yang C, Mai JY, Gong YF, Yan LS, Zhao K, Ning HL, Wu SJ, Gao JW, Gao XS, Zhou GF, Lu XB, Liu J-M (2017) High mobility solution-processed C8-BTBT organic thin-film transistors via UV-ozone interface modification. J Mater Chem C 5:10652–10659
Yuan YB, Giri G, Ayzner AL, Zoombelt AP, Mannsfeld SCB, Chen JH, Nordlund D, Toney MF, Huang JS, Bao ZN (2014) Ultra-high mobility transparent organic thin film transistors grown by an off-centre spin-coating method. Nat Commun 5:3005
Jiang LF, Liu J, Lu XQ, Fu LL, Shi YJ, Zhang J, Zhang X, Geng H, Hu YY, Dong HL, Jiang L, Yu JS, Hu WP (2018) Controllable growth of C8-BTBT single crystalline microribbon arrays by a limited solvent vapor-assisted crystallization (LSVC) method. J Mater Chem C 6:2419–2423
Liu C, Li Y, Lee MV, Kumatania A, Tsukagoshi K (2013) Self-assembly of semiconductor/insulator interfaces in one-step spin-coating: a versatile approach for organic field-effect transistors. Phys Chem Chem Phys 15:7917–7933
Lyu L, Niu DM, Xie HP, Zhao Y, Cao NT, Zhang H, Zhang YH, Liu P, Gao YL (2017) The correlations of the electronic structure and film growth of 2,7-diocty[1] benzothieno[3,2-b]benzothiophene (C8-BTBT) on SiO2. Phys Chem Chem Phys 19:1669–1676
Kano M, Minari T, Tsukagoshi K (2009) Improvement of subthreshold current transport by contact interface modification in p-type organic field-effect transistors. Appl Phys Lett 94:143304
Wang ST, Niu DM, Lyu L, Huang YB, Wei XH, Wang C, Xie HP, Gao YL (2017) Interface electronic structure and morphology of 2,7-dioctyl[1] benzothieno[3,2-b]benzothiophene (C8-BTBT) on Au film. Appl Surf Sci 416:696–703
He DW, Qiao JS, Zhang LL, Wang JY, Lan T, Qian J, Li Y, Shi Y, Chai Y, Lan W, Ono LK, Qi YB, Xu JB, Ji W, Wang XR (2017) Ultrahigh mobility and efficient charge injection in monolayer organic thin-film transistors on boron nitride. Sci Adv 3:e1701186
Soeda J, Hirose Y, Yamagishi M, Nakao A, Uemura T, Nakayama K, Uno M, Nakazawa Y, Takimiya K, Takeya J (2011) Solution-crystallized organic field-effect transistors with charge-acceptor layers: high-mobility and low-threshold-voltage operation in air. Adv Mater 23:3309–3314
Liu C, Minari T, Lu XB, Kumatani A, Takimiya K, Tsukagoshi K (2011) Solution-processable organic single crystals with bandlike transport in field-effect transistors. Adv Mater 23:523–526
Minari T, Miyata Y, Terayama M, Nemoto T, Nishinaga T, Komatsu K, Isoda S (2006) Alkyl chain length dependent mobility of organic field-effect transistors based on thienyl-furan oligomers determined by the transfer line method. Appl Phys Lett 88:083514
Cheng HL, Chou WY, Kuo CW, Wang YW, Mai YS, Tang FC, Chu SW (2008) Influence of electric field on microstructures of pentacene thin-films in field-effect transistors. Adv Funct Mater 18:285–293
Nikolka M, Nasrallah I, Rose B, Ravva MK, Broch K, Sadhanala A, Harkin D, Charmet J, Hurhangee M, Brown A, Illig S, Too P, Jongman J, McCulloch I, Bredas JL, Sirringhaus H (2017) High operational and environmental stability of high-mobility conjugated polymer field-effect transistors through the use of molecular additives. Nat Mater 16:356–362
Irfan I, Turinske AJ, Bao ZN, Gao YL (2012) Work function recovery of air exposed molybdenum oxide thin films. Appl Phys Lett 101:093305
Wang SD, Minari T, Miyadera T, Tsukagoshi K, Tang JX (2009) Contact resistance instability in pentacene thin film transistors induced by ambient gases. Appl Phys Lett 94:083309
Casalini S, Bortolotti CA, Leonard F, Biscarini F (2017) Self-assembled monolayers in organic electronics. Chem Soc Rev 46:40–47
Bobbert PA, Sharma A, Mathijssen SGJ, Kemerink M, Leeuw DMD (2012) Operational stability of organic field-effect transistors. Adv Mater 24:1146–1158
Sharma A, Mathijssen SGJ, Bobbert PA, Leeuw DMD (2011) Influence of the semiconductor oxidation potential on the operational stability of organic field-effect transistors. Appl Phys Lett 99:103302
Acknowledgements
This work is supported by the National Natural Science Foundation of China (Contracts 51431006 and 51872099). XBL acknowledges the support of the Project for Guangdong Province Universities and Colleges Pearl River Scholar Funded Scheme (2016). This work was also supported by the Guangdong Innovative Research Team Program (No. 2013C102), the Guangdong Provincial Key Laboratory of Optical Information Materials and Technology (Grant No. 2017B030301007), and the 111 Project.
Author information
Authors and Affiliations
Contributions
JYM performed the experiments and drafted the manuscript. XBL directed the study and revised the manuscript. NWT and WEH helped with the data analysis and Raman measurements. ZMZ, CLL, AHZ, ZF, SJW, MZ, JWG, GFZ, and JML provided constructive advice during drafting. All authors read and approved the final manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Mai, J., Tang, N., He, W. et al. Effects of Ambient Gases on the Electrical Performance of Solution-Processed C8-BTBT Thin-Film Transistors. Nanoscale Res Lett 14, 169 (2019). https://doi.org/10.1186/s11671-019-3007-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-019-3007-x