Abstract
Graphene, a two-dimensional nanomaterial, has shown tremendous promising applications in a broad range of fields. Mass production of defect-free graphene is a prerequisite for its applications. In this work, by using a needle valve, we propose a simple hydrodynamic-assisted exfoliation method to produce high-quality few-layer graphene flakes. The prepared graphene flakes, with an average layer of 5 (~ 71% less than five layers) and a Raman D/G intensity ratio as low as 0.1, are free of defects and oxidation. The average thickness and length of the few-layer graphene flakes are 2.3 nm (~ 90% < 4 nm) and 1.9 μm (~ 50% in the range of 1–7 μm), respectively. In a lab-scale trial, the concentration of graphene can reach 0.40 g/ml under mild operating conditions (working pressure 20 MPa, 16 cycles), and the corresponding production rate is 0.40 g/h. The hydrodynamic-assisted exfoliation by needle valve potentially offers a simple and efficient method for large-scale production of high-quality graphene.
Avoid common mistakes on your manuscript.
Introduction
Graphene, a single layer of graphite, has been attracting growing attention since its discovery in 2004 [1]. Owning to its impressive physical and chemical properties [2], graphene has shown tremendous promising applications in a broad range of fields, such as electronics [3], photonics [4], catalysis [5, 6], energy conversion/storage [7,8,9], and polymer nanocomposites [10, 11]. To fulfill these exciting potential applications, particular attention has been drawn to the production of high-quality graphene on large-scale.
To date, many methods such as micromechanical cleavage [12], chemical vapor deposition [13, 14], solvothermal synthesis [15], chemical exfoliation [16, 17], and liquid phase exfoliation [18, 19] have been proposed to produce graphene. Among these, liquid phase exfoliation, namely exfoliation of graphite for preparation of graphene in a liquid media, is considered to be one of the most promising and simplest approaches to achieve mass production of graphene at low cost [19]. Liquid phase exfoliation is usually implemented by ultrasonication. However, the ultrasonic exfoliation is highly dependent on the geometry of ultrasonic vessel size and shape, which makes this method possess low yield, time consuming, and particularly, impossibility of scale-up [20, 21]. In addition, recent studies indicated that the graphene produced by ultrasonic exfoliation has many more structure defects than expected [22].
Recently, as an alternative pathway, fluid dynamics-assisted liquid phase exfoliation, has been proposed to produce graphene with low defect content on large-scale [21, 23,24,25,26,27,28,29,30,31,32,33]. By using a jet cavitation device, Liang et al. [29] prepared a series of graphene dispersions with the maximum concentration of 0.12 mg/ml, whereas the processing time was long up to 8 h. Liu et al. [26] produced a graphene dispersion with the concentration of 0.27 mg/ml using a specially designed high shear mixer. Nacken et al. [31] showed the production of graphene dispersion with the concentration of 0.223 mg/ml by a high pressure homogenizer. Yi et al. [27] demonstrated the feasibility of exfoliation by a kitchen blender, and graphene with the concentration of 0.22 mg/ml was produced. Using the kitchen blender, a higher concentration of 1 mg/ml was achieved by Varrla et al. [30]. Previous studies have shown that the fluid dynamics-assisted exfoliation has a good prospect for scalable production of graphene. However, because intensive operating conditions and long processing time are usually required for this technique, the obtained graphene are characterized by high Raman D/G intensity ratios (ID/IG, a measure of defect content) and low aspect ratios. For example, Liang et al. [29] reported an ID/IG value of 0.38 for jet cavitation exfoliated graphene, while the length was unknown. The graphene produced by kitchen blender (ID/IG = 0.3–0.7, length = 0.63 μm) and high-pressure homogenizer (ID/IG = 0.52–0.78, length = 0.02–0.58 μm) were also featured with high ID/IG values and low aspect ratios [30, 31]. Different fluid dynamics-assisted exfoliation methods give ID/IG and length in the range of 0.14–0.78 and 0.02–1.41 μm [26,27,28,29,30,31,32,33], respectively. Therefore, a more efficient method in terms of both higher graphene concentration and high aspect ratio is of great significance.
In this work, a simple method based on hydrodynamic mechanism was proposed for scalable production of high-quality few-layer graphene flakes. A simple needle valve was used as exfoliation device. The exfoliation process was exemplified using 80 wt% N-methyl pyrrolidone aqueous solution as solvent [34, 35]. Quality of the products were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), atomic force microscopy (AFM), Raman spectroscopy, and X-ray photoelectron spectroscopy (XPS). The effects of operating parameters on graphene concentrations were also investigated.
Materials and Methods
Materials
N-methyl pyrrolidone (NMP) (purity 99.5%) and graphite powder (≤ 325 mesh, purity 99.9%) were purchased from Aladdin Industrial Corporation in Shanghai (China). Deionized water was purified by a laboratory water purification system (SZ-97A, Shanghai, China).
Exfoliation of Graphite into Few-Layer Graphene Flakes
A schematic view of the needle valve used for exfoliation is shown in Fig. 1. When a liquid passes through the narrow gap in the valve, cavitation and velocity gradient can be generated due to abrupt velocity and geometrical change, which may induce normal force and shear force for exfoliation. By simply adjusting the width of the valve gap, the working conditions can be varied and controlled. Figure 2 shows a flow diagram of the hydrodynamic-assisted exfoliation process by needle valve. In a typical experiment, graphite powder was dispersed in 80 wt% NMP aqueous solution to obtain graphite suspension with the concentration of 10 mg/ml. Then, the suspension was pumped by a plunger pump (model 2-JW, Zhijiang Petrochemical, China) through the needle valve. By adjusting the opening of the valve, the working pressure was controlled at 20 MPa. After 16 cycles, the dispersion was collected and subsequently centrifuged at 500 rpm for 60 min (SC-3610, USTC Zonkia, China) to remove unexfoliated graphite. Subsequently, the supernatant dispersion was decanted and retained for further use.
Characterization
The morphology and size of graphene were analyzed by SEM (VEGA3, TESCAN). Samples for SEM were coated with gold in an argon atmosphere. TEM was performed by a Tecnai G2 F30 S-Twin and operated at 300 kV. The samples were prepared by dropping the graphene dispersion onto holey carbon grids. AFM images were captured in tapping mode using a Bruker Dimension Icon. A newly cleaved mica was used as substrate for AFM analysis. Raman spectroscopy was conducted with a Lab RAM HR800 (λ = 532 nm) at room temperature. XPS was employed to detect the oxidation defect of graphene using an ESCALAB 250Xi analyzer. UV-Vis absorption was performed to measure graphene concentration by a Lambda 35 spectrophotometer (PerkinElmer) at a wavelength of 660 nm.
Results and Discussion
Quality of Graphene Flakes
Figure 3 displays typical SEM images of the bulk graphite and the prepared graphene powder. The bulk graphite was flake-like powder with a lateral size and a thickness of approximately 5–20 μm and 10 μm, respectively. In comparison, the prepared graphene powder contains considerably thinner flakes with a lateral size that decreased to approximately 1–7 μm, while the thickness was far below 1 μm. Clearly, the bulk graphite was exfoliated into small flakes. Note that several flakes with folded edges were appeared, which were believed as mono-layer or few-layer graphene flakes [26].
To identify the formation of mono-layer or few-layer graphene, TEM analysis was performed to visually observe the number of graphene layers. Figure 4 presents typical TEM images of the prepared graphene flakes. Figure 4a shows a mono-layer graphene flake with folded edge. A high-resolution TEM image of the blue box in Fig. 4a is displayed in Fig. 4b. Smooth edge that dominated by one dark line was observed clearly, indicating the formation of mono-layer graphene [23]. A more definitive identification of mono-layer graphene was further confirmed by selected-area electron diffraction patterns (selected from the black box in Fig. 4a). As shown in Fig. 4c, a typical diffraction of mono-layer graphene was presented, that is, the inner spots {1100} were more intense than the outer spots {2110} [18, 36, 37]. The hexagonal diffraction pattern indicates a good crystallinity of the prepared graphene [18]. Figure 4d–f are typical TEM images of bilayer, trilayer, and five-layer graphene flakes. Figure 4g is an image of several individual graphene flakes stack together due to the tendency of agglomeration. A statistical analysis of the layer distribution was obtained from TEM analysis of at least 100 graphene flakes. As shown in Fig. 4h, ~ 71% of the flakes were less than five layers, and the average layer was 5, indicating a high quality of graphene. Note, due to the fact that graphene flakes with very small size would be lost through the holey TEM grids, the statistical results of layer were probably higher than the corresponding actual value.
To further identify the thickness and length of graphene, AFM analysis was performed by using mica wafer as the substrate. Shown in Fig. 5a is a typical AFM image of mono-layer graphene flakes. The cross-sectional analysis indicated that the topographic height of the flakes is approximately 1 nm, which could be considered as mono-layer flakes according to the fact that the mono-layer graphene is usually measured to be 0.4–1 nm by AFM due to the analysis equipment and substrates and residual water [38]. Few-layer graphene flakes could be observed from Fig. 5b. The thickness of these flakes was ~ 3.6 nm, while the length was as high as 3–5 μm. Further statistical analyses of the thickness/length distributions were obtained from AFM analysis of at least 200 graphene flakes. As shown in Fig. 5c, d, ~ 90% of the graphene flakes were less than 4 nm. Only a minority of ~ 5% flakes with the thickness of more than 5 nm were observed. Further, ~ 50% of the flakes had the length in the range of 1–7 μm. The average thickness and length of the flakes were 2.3 nm and 1.9 μm, respectively, confirming the high quality of graphene.
Raman spectroscopy was performed to detect the defect content of graphene. Figure 6 shows typical Raman spectra of the prepared graphene along with the bulk graphite as a reference sample. Three characteristic peak, i.e., D band (~ 1350 cm−1), G band (~ 1580 cm−1), and 2D band (~ 2700 cm−1) were observed for these two graphitic materials. For graphene, the 2D band was in the shape of symmetric peak. The full width at half maximum (FWHM) of G band was 13 cm−1, well matching with the previous reports for thin graphene flakes (12–14 cm−1) [39]. Moreover, the intensity ratio of D/G (ID/IG) for the prepared graphene was 0.10, lower than that of ultrasonication exfoliated graphene (0.29) [32], shear force exfoliated graphene (0.17–0.37) [24, 26], and other fluid dynamics exfoliated graphene (0.21–0.78) [31, 32], further verifying the high quality of graphene.
The oxides content of the prepared graphene flakes was investigated by XPS. As shown in Fig. 7, the XPS spectra of the prepared graphene displayed the same bonds and similar composition with that of the bulk graphite, indicating the absence of chemical modification or oxidization during the exfoliation process. The above results demonstrated that hydrodynamic-assisted exfoliation by needle valve is an efficient method to produce unoxidized few-layer graphene with high quality.
Effects of Operating Parameters on the Concentration of Graphene
To maximize the productivity of few-layer graphene, the effects of operating parameters, that is, working pressure (P), number of cycles (N), and initial concentration of bulk graphite (Ci), on the concentration of few-layer graphene dispersion were investigated.
As shown in Fig. 8a (N = 16, Ci = 10 mg/ml), the concentration obviously increased with increasing working pressure from 1 to 20 MPa, and a concentration as high as 0.40 mg/ml was reached at 20 MPa. However, further increasing the working pressure to 30 MPa, no significant increase in the concentration was observed. Such results may be explained by the following reasons. In hydrodynamic-assisted exfoliation process, increasing in the working pressure results in an increase in the collapse intensity of cavity, due to which there is an increase in the magnitude of the stress derived from cavitation and turbulent, thereby favoring the delamination of graphite. The concentration did not change appreciably above 20 MPa, probably due to the agglomeration and re-stacking of graphene flakes caused by the rise of temperature under higher working pressure [31].
Figure 8b shows the dependence of number of cycles on graphene concentration (P = 20 MPa, Ci = 10 mg/ml). As expected, the concentration was increased with increasing number of cycles. With 16 cycles, the concentration reached a maximum value of 0.4 mg/ml. However, further increasing the number of cycles, the concentration was basically unchanged. In the exploitation process by needle valve, passing the suspension through the valve more than once could result in the fragmentation of graphite, which was favorable for exploitation due to the fact that smaller graphite pieces are easier to delaminate into graphene than larger ones [25]. However, as the graphite flakes become smaller, the size of graphite was comparable with that of cavitation bubbles [39]. Therefore, the formation of new graphene flakes becomes difficult.
Initial concentration of bulk graphite also had a significant influence on graphene concentration [40]. As shown in Fig. 8c (P = 20 MPa, N = 16), the concentration increased from 0.146 to 0.40 mg/ml with increasing the initial concentration of graphite from 2 to 10 mg/ml. In liquid phase exfoliation process, particle-particle collisions are beneficial to the delamination of graphite. A higher initial concentration of graphite leads to the reinforcement of particle collision, thereby contributes to the self-exfoliation of graphene [26]. When the initial concentration of graphite further increased to 12 mg/ml, the graphene concentration decreased slightly. Similar results were observed by Liang et al. [29] and Arao et al. [32], indicated that over-concentrated graphite dispersion would hinder instead of promote graphene concentration.
Comparison of Few-Layer Graphene Produced by Different Fluid Dynamics Methods
Table 1 presents a summary of the concentration, length, and ID/IG of the few-layer graphene produced by different fluid dynamics methods. The graphene produced by needle valve had a concentration as high as 0.40 mg/ml, which was higher than most of the reported values. In a lab-scale trial, the production rate was calculated to be 0.40 g/h. The concentrations reported by Varrla et al. [30] and Arao et al. [32] could reach up to 1 mg/ml and 7 mg/ml, respectively. However, the length of their products was smaller (0.63 μm, 1.41 μm). In contrast, the graphene obtained in this study had an average length of 1.9 μm (larger than the reported sizes) and Raman ID/IG as low as 0.1 (lower than the reported ratios). Therefore, it can be concluded that the hydrodynamic-assisted exfoliation by needle valve was an efficient approach to produce few-layer graphene flakes with high quality.
Possible Exfoliation Mechanisms
We suggest the superiority of the hydrodynamic-assisted exfoliation be ascribed to the exfoliation mechanism. Considering the structure of the needle valve, the flowing fluid dynamics effects are responsible for the delamination of graphite: First, when the suspension containing graphite passes through the narrow gap of the valve, the total pressure of the liquid falls sharply below its vapor pressure. As a result, a turbulent jet that causes huge hydrodynamic stress is formed at the outlet of the valve and generating a large volume of cavitation bubbles. The bubbles then grow from micro gas nucleuses and subsequently collapse intensely. With the collapse of bubbles, intensive microjets and shock waves that surround the graphite are generated, thus resulting in the delamination [41]. Second, the velocity gradient and collision also contribute to the exfoliation. When liquid jets out from the narrow gap of the valve, viscous shear force, which is preferable for the delamination, can be induced by velocity gradient due to abrupt velocity and geometrical change [32]. In addition, the self-exfoliation of graphene caused by the collision of graphite particles is also favorable for the exfoliation [26].
Conclusions
In summary, we have demonstrated the production of high-quality few-layer graphene using a simple hydrodynamic-assisted exfoliation method. The results indicated that ~ 71% of the prepared graphene flakes were less than five layers, while the average thickness and length of the flakes were 2.3 nm (~ 90% < 4 nm) and 1.9 μm (~ 50% in the range of 1–7 μm), respectively. The flakes with ID/IG ratio as low as 0.1 were free of defects and oxidation. In a lab-scale trial, the concentration of few-layer graphene could reach 0.40 mg/ml under mild operating conditions (working pressure 20 MPa, 16 cycles), and the corresponding production rate was 0.40 g/h. Hydrodynamic-assisted exfoliation by needle valve was potentially an efficient method for scalable production of high-quality graphene.
Abbreviations
- AFM:
-
Atomic force microscopy
- C i :
-
Initial concentration of bulk graphite
- FWHM:
-
Full width at half maximum
- I D/I G :
-
Raman D/G intensity ratio
- N :
-
Number of cycles
- NMP:
-
N-methyl pyrrolidone
- P :
-
Working pressure
- SEM:
-
Scanning electron microscopy
- TEM:
-
Transmission electron microscopy
- XPS:
-
X-ray photoelectron spectroscopy
References
Novoselov KS, Geim AK, Morozov SV, Jiang D, Zhang Y, Dubonos SV, Grigorieva IV, Firsov AA (2004) Electric field effect in atomically thin carbon films. Science 306:666–669
Geim AK, Novoselov KS (2007) The rise of graphene. Nature Mater 6:1–14
Castro Neto AH, Guinea F, Peres NMR, Novoselov KS, Geim AK (2009) The electronic properties of graphene. Rev Mod Phys 81:4106–4111
Bonaccorso F, Sun Z, Hasan T, Ferrari AC (2010) Graphene photonics and optoelectronics. Nature Photon 4:611–622
Hu M, Yao Z, Wang X (2017) Graphene-based nanomaterials for catalysis. Ind Eng Chem Res 56:3477–3350
Sun Z, Masa J, Liu Z, Schuhmann W, Muhler M (2012) Highly concentrated aqueous dispersions of graphene exfoliated by sodium Taurodeoxycholate: dispersion behavior and potential application as a catalyst support for the oxygen-reduction reaction. Chem Eur J 18:6972–6978
Ye M, Zhang Z, Zhao Y, Qu L (2018) Graphene platforms for smart energy generation and storage. Joule 2:245–268
Zhao MQ, Zhang Q, Huang JQ, Tian GL, Nie JQ, Peng HJ, Wei F (2014) Unstacked double-layer templated graphene for high-rate lithium-sulphur batteries. Nat Commun 5:1–8
Edwards RS, Coleman KS (2013) Graphene synthesis: relationship to applications. Nanoscale 5:38–51
Liu Z, Liu J, Cui L, Wang R, Luo X, Barrow CJ, Yang W (2013) Preparation of graphene/polymer composites by direct exfoliation of graphite in functionalised block copolymer matrix. Carbon 51:148–155
Huang X, Qi X, Boey F, Zhang H (2012) Graphene-based composites. Chem Soc Rev 41:666–686
Novoselov KS, Jiang D, Schedin F, Booth TJ, Khotkevich VV, Morozov SV, Geim AK (2005) Two-dimensional atomic crystals. PNAS 102:10451–10453
Reina A, Jia X, Ho J, Nezich D, Son H, Bulovic V, Dresselhaus MS, Kong J (2008) Large area, few-layer graphene films on arbitrary substrates by chemical vapor deposition. Nano Lett 9:30–35
Li X, Cai W, An J, Kim S, Nah J, Yang D, Piner R, Velamakanni A, Jung I, Tutuc E, Banerjee SK, Colombo L, Ruoff RS (2009) Large-area synthesis of high-quality and uniform graphene films on copper foils. Science 324:1312–1314
Qian W, Hao R, Hou Y, Tian Y, Shen C, Gao H, Liang X (2009) Solvothermal-assisted exfoliation process to produce graphene with high yield and high quality. Nano Res 2:706–712
Stankovich S, Dikin DA, Richard DP, Kevin AK, Kleinhammes A, Jia Y, Wu Y, Nguyen SBT, Ruof RS (2007) Synthesis of graphene-based nanosheets via chemical reduction of exfoliated graphite oxide. Carbon 45:1558–1565
Zhang L, Li X, Huang Y, Ma YF, Wan XJ, Chen YS (2010) Controlled synthesis of few-layered graphene sheets on a large scale using chemical exfoliation. Carbon 48:2367–2371
Hernandez Y, Nicolosi V, Lotya M, Blighe FM, Sun ZY, De S, McGovern IT, Holland B, Byrne M, Gun'ko YK, Boland JJ, Niraj P, Duesberg G, Krishnamurthy S, Goodhue R, Hutchison J, Scardaci V, Ferrari AC, Coleman JN (2008) High-yield production of graphene by liquid-phase exfoliation of graphite. Nature Nanotech 3:563–568
Parviz D, Irin F, Shah SA, Das S, Sweeney CB, Green MJ (2016) Challenges in liquid-phase exfoliation, processing, and assembly of pristine graphene. Adv Mater 28:8796–8818
Khan U, O’Neill A, Lotya M, De S, Coleman JN (2010) High-concentration solvent exfoliation of graphene. Small 6:864–871
Yi M, Shen Z (2015) A review on mechanical exfoliation for the scalable production of graphene. J Mater Chem A 3:11700–11715
Bracamonte MV, Lacconi GI, Urreta SE, Torres LEFF (2014) On the nature of defects in liquid-phase exfoliated graphene. J Phys Chem C 118:15455–15459
Zhao W, Fang M, Wu F, Wu H, Wang L, Chen G (2010) Preparation of graphene by exfoliation of graphite using wet ball milling. J Mater Chem 20:5817–5819
Shen Z, Li J, Yi M, Zhang X, Ma S (2011) Preparation of graphene by jet cavitation. Nanotechnology 22:365306
Chen X, Dobson JF, Raston CL (2012) Vortex fluidic exfoliation of graphite and boron nitride. Chem Commun 48:3703–3075
Liu L, Shen Z, Yi M, Zhang X, Ma S (2014) A green, rapid and size-controlled production of high-quality graphene sheets by hydrodynamic forces. RSC Adv 4:36464
Yi M, Shen Z (2014) Kitchen blender for producing high-quality few-layer graphene. Carbon 78:622–626
Paton KR, Varrla E, Backes C, Smith RJ, Khan U, O’Neill A et al (2014) Scalable production of large quantities of defect-free few-layer graphene by shear exfoliation in liquids. Nature Mater 13:624–630
Liang S, Shen Z, Yi M, Liu L, Zhang X, Cai C, Ma S (2015) Effects of processing parameters on massive production of graphene by jet cavitation. J Nanosci Nanotechnol 15:2686–2694
Varrla E, Paton KR, Backes C, Harvey A, Smith RJ, McCauley J, Coleman JN (2014) Turbulence-assisted shear exfoliation of graphene using household detergent and a kitchen blender. Nanoscale 6:11810–11819
Nacken TJ, Damm C, Walter J, Ruger A, Peükert W (2015) Delamination of graphite in a high pressure homogenizer. RSC Adv 5:57328–57338
Arao Y, Mizuno Y, Araki K, Kubouchi M (2016) Mass production of high-aspect-ratio few-layer-graphene by high-speed laminar flow. Carbon 102:330–338
Xu Q, Zhao W, Zhi J, Yin J (2018) Exfoliation of graphite in CO2 expanded organic solvents combined with low speed shear mixing. Carbon 135:180–186
Manna K, Huang HN, Li WT, Ho YH, Chiang WH (2016) Toward understanding the efficient exfoliation of layered materials by water-assisted cosolvent liquid-phase exfoliation. Chem Mater 28:7586–7593
Arao Y, Mori F, Kubouchi M (2017) Efficient solvent systems for improving production of few-layer graphene in liquid phase exfoliation. Carbon 118:18–24
Meyer JC, Geim AK, Katsnelson MI, Novoselov KS, Booth TJ, Roth S (2007) The structure of suspended graphene sheets. Nature 446:60–63
Meyer JC (2014) Graphene, transmission electron microscopy (TEM) of graphene. Woodhead Publishing, Cambridge, pp 101–123
Ochedowski O, Bussmann BK, Schleberger M (2014) Graphene on Mica - intercalated water trapped for life. Sci Rep 4:6003
Alaferdov AV, Gholamipour-Shirazi A, Canesqui MA, Danilov YA, Moshkalev SA (2014) Size-controlled synthesis of graphite nanoflakes and multi-layer graphene by liquid phase exfoliation of natural graphite. Carbon 69:525–535
Nuvoli D, Valentini L, Alzari V, Scognamillo S, Bon SB, Piccinini M, Illescas J, Mariani A (2011) High concentration few-layer graphene sheets obtained by liquid phase exfoliation of graphite in ionic liquid. J Mater Chem 21:3428–3431
Hammitt FG (1980) Cavitation and Multiphase Flow Phenomena. McGraw-Hill Inc, New York, p 229
Funding
This work was supported by the National Natural Science Foundation of China (21406198) and Zhejiang Provincial Natural Science Foundation of China (LQ14B060003).
Availability of Data and Materials
The datasets generated during and/or analyzed during the current study are available from the corresponding authors on reasonable request.
Author information
Authors and Affiliations
Contributions
The experiments were guided by ZZ. HJ and CW prepared and characterized the graphene. JJ participated in the discussion and gave useful suggestions. The manuscript was composed by ZZ. All authors approved the final manuscript.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Zhang, Z., Jin, H., Wu, C. et al. Efficient Production of High-Quality Few-Layer Graphene Using a Simple Hydrodynamic-Assisted Exfoliation Method. Nanoscale Res Lett 13, 416 (2018). https://doi.org/10.1186/s11671-018-2830-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-018-2830-9