Abstract
Poor thermostability of Sb2S3 in vacuum hinders the possibility of achieving high-quality crystalline films. In order to enhance the photovoltaic properties of Sb2S3 planar heterojunction solar cells, a selenylation-based post-treatment approach has been employed. Selenylation performed over 15 min on the Sb2S3 film resulted in an enhancement in the conversion efficiency from ~ 0.01 to 2.20%. Effect of the selenylation on the evolution of morphology, crystal structure, composition distributions, and photovoltaic behavior has been investigated. The variation in the energy levels of Sb2S3/CdS junction has been also been discussed. Results show that selenylation not only enhanced the crystallinity of Sb2S3 film but also provided a suitable energy level which facilitated charge transport from absorber to the buffer layer.
Avoid common mistakes on your manuscript.
Background
Inorganic thin film solar cells have received much attention owing to the advantages of being low cost and lightweight as compared to their silicon counterparts [1, 2]. They are chemically and physically stable in air in contrast to organic and organic–inorganic hybrid perovskite solar cells and have achieved very long operating lifetimes under practical settings [3,4,5]. Among them, copper indium gallium selenide (CIGS)-based and cadmium telluride (CdTe)-based solar cells are promising and have realized a conversion efficiency of 21.7% and 19.6% [6, 7], respectively. In recent years, another candidate material Cu2ZnSnSxSe4 − x (CZTSSe) has been investigated as it is earth-abundant and has an environment-friendly composition [8, 9]. Although an impressive conversion efficiency of 12.6% has been achieved by a hydrazine-based solution process, this compound encountered complexities in terms of phase and defect control [10]. Additionally, the toxicity of hydrazine has seriously limited its further application [11,12,13]. Recently, binary antimony sulfide (Sb2S3) has gained importance as a thin film solar cell application, owing to its earth abundance, low cost, and the relatively low toxic composition of Sb and S elements [14, 15].
Sb2S3 exhibits a tunable energy bandgap (1.1–1.7 eV) when S elements are partly or completely replaced by Se, suggesting good designability of Sb2S3 for photovoltaic device preparation [16,17,18]. To date, various approaches have been reported to fabricate Sb2S3 absorber layers. Sb2S3-sensitized inorganic–organic heterojunction solar cells exhibit a high solar energy harvesting ability and have demonstrated conversion efficiency of 7.5% [19]. However, the device fabrication is complicated, and the lifetime of organic hole transporting materials is low. In comparison, planar heterojunction solar cells are advantageous in terms of simplified absorber preparation as well as device fabrication. Both physical vapor-deposited and solution-processed Sb2S3 films have been previously applied in planar heterojunction solar cell fabrication. All-inorganic Sb2S3 planar heterojunction devices with a simple structure of FTO/n-type buffer layer/Sb2S3/electrode have achieved a power conversion efficiency (PCE) of 1.27–4.17% [20,21,22,23,24]. Vacuum-based film deposition methods like magnetron sputtering are convenient to operate and provide accurate thickness control, reproducibility, and smooth surface building. Due to these advantages, they have been widely applied in industrial manufacturing of CIGS and CdTe solar cells. Sb2S3 has a low melting point (550 °C) and high vapor pressure, favoring thermal evaporation instead of magnetron sputtering. However, Sb2S3 exhibits a poor thermostability in vacuum resulting in significant deviations in the composition [25], and the tendency for surface oxidation. Currently, component preserving rapid thermal evaporation (RTP) has been employed in the fabrication of all-inorganic Sb2S3 solar cells having achieved a maximum PCE of 4.17% [23]. Compared with the rapid thermal evaporation technique, regular thermal evaporation has some advantages in terms of providing accurate thickness and variable morphology control. Also, the substrate rotation is easier to realize and beneficial for uniform preparation of large-area thin film specimen. Since the distance between substrate and source is greater, the required evaporation power is lower than rapid evaporation. This ensures that the source has less thermal effect on the substrate during evaporation process. It consumes less material and has better prospect in flexible solar cell fabrication. However, this approach has some limitations that need to be addressed. To avoid decomposition and surface oxidation, Sb2S3 films can only be prepared at a low substrate temperature (~ 200 °C) by regular thermal evaporation. However, the low substrate temperature resulted in poor crystallinity of the films, which was not suitable for the preparation of efficient photovoltaic devices.
Post-treatments including vacuum annealing and selenization for thermally evaporated Sb2S3 have been considered. In this study, rapid thermal processing technique has been utilized for the thermal treatment. Photovoltaic properties of Sb2S3 planar heterojunction device showed a considerable enhancement after several minutes of selenization. Processing conditions and the effect on the crystal structure and surface morphology were investigated. The formation of gradient composition, evolution of energy levels, and electronic behavior in device has also been discussed in detail. After the optimization of the technique, the PCE of planar photovoltaic devices showed a satisfactory improvement from ~ 0.01 to 2.20%.
Methods/Experimental
A simple superstrate device structure (FTO (SnO2:F)/CdS/ Sb2S3/Au) was applied for the Sb2S3 films solar cells. FTO-coated glass (Pilkington, Toledo, USA) with a sheet resistance of 7 Ω/□ was used as the bottom electrode to collect electrons. A CdS buffer layer with a thickness of 90 nm was deposited on the FTO glass using the chemical bath deposition (CBD) method [26]. Sb2S3 films were thermally evaporated using Sb2S3 powder (aladin, 99.9%, Aladdin) at less than 5 × 10−4 Pa when the substrate temperature was kept at 175 °C, and then cooled down to room temperature naturally. The sample was then transferred into a two-zone tube RTP furnace at 103 Pa in protective N2 atmosphere. Excess selenium powder was placed in a quartz boat in the low temperature zone (350 °C) whereas the sample was placed in the high temperature zone (400 °C). Subsequently, 60-nm Au electrode was deposited on the surface of absorber layer using DC magnetron sputtering.
Current density–voltage (J-V) characteristics were measured using a Keithley 2400 unit under an AM 1.5 (100 W/cm2) xenon lamp illumination (Newport 94043A). External quantum efficiency (EQE) of Sb2S3(Se) thin films were obtained using an integrated measurements system (Beijing SOFN 7-SCSpecIII). The crystal structure and composition were characterized by X-ray diffraction (XRD, Bruker D8). Optical property was characterized by ultraviolet–visible near infrared transmission spectroscopy (UV-Vis, Agilent Cary5000). Ultraviolet photoelectron spectroscopy (UPS, Thermo ESCALAB 250Xi) was used to determine the energy levels of the important photovoltaic layers. Surface morphology of Sb2S3(Se) films growth on CdS was characterized by scanning electron microscopy (SEM, FEI Helios Nanolab 600i). Carrier transporting behavior was investigated by electrochemical impedance spectrum (EIS) under a suitable open-circuit voltage.
Results and Discussion
The schematic of the entire device fabrication procedure is shown in Fig. 1a. Each sample comprised of eight cells with a 4-mm2 active area that was tested under the same condition. Typical J-V characters of untreated, vacuum-annealed (A) and selenized (S) Sb2S3 are shown in Fig. 1b and their corresponding performance is summarized in Table 1. Untreated Sb2S3 device showed a low average PCE < 0.01% with an open-circuit voltage (VOC) of 0.31 V and a short current density (JSC) of 0.14 mA/cm2. After a 10-min vacuum annealing step, a minor improvement was obtained with JSC = 0.66 mA/cm2 and a PCE = 0.08%. In contrast, selenized devices showed a significant enhancement in both VOC and JSC as compared to the untreated device with JSC = 7.80 mA/cm2 and PCE = 1.57%. The best performance of device with a maximum PCE = 2.20% and a JSC = 9.04 mA/cm2 was obtained when the selenization time was increased to 15 min. Increasing the selenization time beyond 15 min did not bring a further improvement of performance. For a selenization time of 20 min, the average PCE decreased to 0.61% due to the degeneration of both VOC and JSC. Further extension of selenization time beyond 30 min resulted in a poor yield. EQE of the devices with the selenization effect is shown in Fig. 1c, where it is evident that the spectral response of the treated devices is significantly higher as compared to the untreated devices. This trend is well consistent with J-V characteristics of devices. Devices selenized for 15 min have the highest EQE, indicating a good spectral response in visible range. EQE peaks also show gradual red shift, and the spectral response ranges become wider with increasing selenization time. For the devices selenized for 20 min, a much wider EQE range from 350 to 400 nm is observed, which can be attributed to the composition change near p-n junction in the Se atmosphere annealing.
XRD analysis was used to determine the overall crystal structure of the films under annealing and selenization treatment. As shown in Fig. 2a, untreated Sb2S3 films showed weak and indistinct XRD peaks indicative of low crystallinity, which explains the poor PCE with the low JSC. Vacuum-annealed and selenized films showed better crystallinity with distinguishable diffraction peaks, which was approximately matched to orthorhombic Sb2S3 (JCPDS NO. 15-0861). All diffraction peaks of selenized films gradually shifted to smaller 2θ angle as the selenization time increased. From the magnified (120) diffraction peaks shown in Fig. 2b, the 2θ value of Sb2S3 was found to be 17.50°, which shifted to 16.95° after a 15-min selenization time. The diffraction patterns tend to match the standard Sb2Se3 PDF card (JCPDS NO. 73-0393). Hence, it can be concluded that there was an increase in the lattice constant after selenization, where smaller S atoms (1.84 Å) were partly replaced by larger Se atoms (1.98 Å).
Further selenization (20 min) was observed to bring about a minor shift in the (120) XRD from 16.95° to 16.90°. We deduced that the replacement reaction rate decreased rapidly in the selenization process. The untreated film exhibited an amorphous textured surface, and the small-sized grains on the surface became more prominent when the film was vacuum annealed to 400 °C. A 15-min selenization treatment led to the formation of micron-sized large grains, indicating selenization can effectively promote the growth of grains which is consistent with XRD results. The compact surface hindered the replacement diffusion of Se, thus decreasing the reaction rate rapidly. The film selenized for 20 min showed large grains with distinct edges in the SEM image in Fig. 3. However, some bulges (red ellipse in Fig. 3d) can be observed on the surface that were responsible for the poor contact between absorber and the buffer layer. Accordingly, the 20-min selenized device exhibits a poor JSC with a high series resistance (Rs) as shown in Table 1. Further, prolonging the selenization time resulted in bulges evolving into cracks and short-circuiting the device.
To investigate the treatment effect on Sb2S3 energy level, the absorption spectrum from 500 to 1100 nm was measured by UV-Vis spectroscopy. As shown in Fig. 4a, both vacuum-annealed and selenized films show improved optical absorption. The absorbance profile showed a gradually increasing and long wave absorption edge with a continuous red shift as the selenization time increased. This indicates that the selenization process decreases the energy gaps. Since Sb2S3 is a direct band gap semiconductor, the band gap (Eg) can be calculated by the Tauc formula [27]:
Energy level analysis of Sb2S3(Se) solar cells. a Ultraviolet–visible near infrared transmission spectroscopy (b) variation of (αhv)2 as a function of the photon energy (hv) of Sb2S3 films under different treatment conditions. c PL spectrum of vacuum prepared Sb2S3, Sb2S3(Se), and Sb2Se3 films. UPS spectra of d Sb2Se3, e Sb2S3, and f CdS. g Model of composition distribution and h energy levels along vertical depth of selenized Sb2S3 film. i An image of selenized Sb2S3 devices sample
where A is a constant, h is the Planck’s constant, and ν is the frequency of the incident photon. Eg was determined from the linear fit of (αhv)2 versus (hv), as shown in Fig. 4b. Eg of untreated Sb2S3 film is 2.03 eV which decreased to 1.60 eV after annealing. The Eg gradually decrease to 1.44 eV as the selenization time increased to 20 min. To verify this, photoluminescence (PL) spectrum of films excited by a 325-nm laser was carried out. As shown in Fig. 4c, the PL peak of Sb2S3 was observed at 772 nm (1.61 eV) with a very small Stokes shift (0.01 eV), which is consistent with the optical band gap. Interestingly, PL spectrum of Sb2S3 selenized for 15 min splits into two peaks, one of which is located at 765 nm (1.62 eV) and the other located at 948 nm (1.31 eV). The 765-nm PL peak is very close to Sb2S3 peak (772 nm), implying that the composition deep within the Sb2S3 film remains virtually unchanged after 15 min of selenization. To study the energy level as well as carrier transport properties of photovoltaic devices, UPS analysis of Sb2Se3, Sb2S3, and CdS was carried out as shown in Fig. 4c–f. The energy level conduction band minimum (EC) and valence band maximum (EV) was determined as listed in Table 2. In accordance with the XRD and PL results, a replacement diffusion model is proposed, in which a substantial proportion of S in the surface is replaced by Se while the composition near p-n junction remains as Sb2S3 (Fig. 4g). The energy levels can be represented as shown in Fig. 4h. A group of selenized Sb2S3 devices is shown in Fig. 4i. Compared with vacuum-annealed Sb2S3/CdS device, selenized device had a satisfactory built-in electrical field at the p-n junction due to the favorable Eg of Sb2S3 (1.61 eV) which provided a higher VOC than Sb2Se3 (Eg = 1.2 eV) [28, 29]. Due to the gradient distribution of composition, selenized Sb2S3 showed a continuous Ev varying from − 5.37 to − 5.08 eV and a lower barrier for photogenerated positive carrier transport from p-n junction vicinity to the anode. Accordingly, a considerable improvement of JSC was realized, resulting in a higher PCE.
To validate the selenization effect on the electronic behavior in the photovoltaic device, electrochemical impedance measurements were carried out, as shown in Fig. 5 along with simulations. For the planar heterojunction device, testing curves obey a semi-circular profile. Resistance-constant phase element (R-CPE) series equivalent electrical circuit model was applied to simulate the test results [30,31,32]. Series resistance R1 represents all factors that affect photogenerated carrier transport to electrodes, mainly the carrier transport resistance of photovoltaic films and electrodes. In this study, interface effect on resistance between Au and absorber is negligible due to the ohmic contact, and the major differences arise due to the absorber being treated under different conditions. Accordingly, R1 value is only related to positive carrier transport from absorber to Au electrode. The shunt pair R2 and CPE1 are associated with the interface between absorber and CdS buffer layer. CPE can be defined by the capacitance (CPE-T) and a non-homogeneity constant (CPE-P). All computed parameters from the fitted plot are listed in Table 3. There is no noticeable difference of CPE-T between the tested samples, and the value is in the 0.94–0.96 range, indicating all the devices could be treated as ideal capacitors with ideal interfaces. The magnitude of R1 was observed to be largely dependent on the treatment conditions. For the untreated device, R1 = 519.8 × 10−3 Ω cm2, which decreased to 10.0 × 10−3 Ω cm2 after a vacuum annealing process. For the device selenized for 15 min, the minimum R1 of 0.4 × 10−3 Ω cm2 was determined. The decreasing of R1 indicates vacuum annealing or selenization facilitated charge transport from absorber to the buffer layer. For the device selenized for 15 min, R1 increased to 815.5 × 10−3 Ω cm2 with a lower CPE-T of 0.84 10−7 F cm−2. The degradation was likely caused by poor interface contact between bulged absorber and the CdS buffer layer.
Conclusions
The selenization approach enhanced the crystallinity of Sb2S3 film and resulted in an improvement in the photovoltaic performance of device. Selenized Sb2S3 films exhibit a gradient composition distribution due to the partial replacement of S atoms by Se atoms in near surface while the bulk composition remains virtually unchanged. Thus, selenized film showed a consecutive Sb2S3/Sb2S3(Se)/Sb2Se3 structure that decreased the potential barrier for photogenerated positive carrier transport from the p-n junction vicinity to the anode. The optimal selenization conditions involves maintaining Se at 350 °C and Sb2S3 at 400 °C, with a selenization time of approximately 15 min. Excessive selenization time tends to introduce some bulges leading to a poor interface contact between absorber and CdS buffer layer, resulting in a poor performance and yield.
Abbreviations
- A:
-
Annealed
- CBD:
-
Chemical bath deposition
- CIGS:
-
Copper indium gallium selenide
- CZTSSe:
-
Cu2ZnSnSxSe4 − x
- EIS:
-
Electrochemical impedance spectrum
- EQE:
-
External quantum efficiency
- FTO:
-
(SnO2:F)
- J SC :
-
Short current density
- J-V :
-
Current density–voltage
- PCE:
-
Power conversion efficiency
- PL:
-
Photoluminescence
- R-CPE:
-
Resistance-constant phase element
- RTP:
-
Rapid thermal processing
- S:
-
Selenized
- SEM:
-
Scanning electron microscopy
- UPS:
-
Ultraviolet photoelectron spectroscopy
- UV-Vis:
-
Ultraviolet–visible near infrared transmission spectroscopy
- V OC :
-
Open-circuit voltage
- XRD:
-
X-ray diffraction
References
Aberle AG (2009) Thin-film solar cells. Thin Solid Films 517:4706–4710
Dross F, Baert K, Bearda T, Deckers J, Depauw V, El Daif O et al (2012) Crystalline thin-foil silicon solar cells: where crystalline quality meets thin-film processing. Progress in Photovoltaics Research & Applications 20:770–784
Polman A, Knight M, Garnett EC, Ehrler B, Sinke WC (2016) Photovoltaic materials: present efficiencies and future challenges. Science 352:d4424
Green MA, Emery K, Hishikawa Y, Warta W, Dunlop ED (2016) Solar cell efficiency tables (version 48): solar cell efficiency tables (version 48). Progress in Photovoltaics Research & Applications 24:905–913
Niu G, Guo X, Wang L (2014) Review of recent progress in chemical stability of perovskite solar cells. J Mater Chem A 3:8970–8980
Jackson P, Hariskos D, Wuerz R, Kiowski O, Bauer A, Friedlmeier TM et al (2015) Properties of Cu(In,Ga)Se2 solar cells with new record efficiencies up to 21.7%. Physica Status Solidi (RRL) - Rapid Research Letters 9:28–31
Martin A, Emery, Keith, Hishikawa, Yoshihiro, Warta et al (2013) Solar cell efficiency tables (version 42). Progress in Photovoltaics Research & Applications 21:827–837
Winkler MT, Wang W, Gunawan O, Hovel HJ, Todorov TK, Mitzi DB (2013) Optical designs that improve the efficiency of Cu2ZnSn(S,Se)4 solar cells. Energy Environ Sci 7:1029–1036
Li J, Wang H, Luo M, Tang J, Chen C, Liu W et al (2016) 10% Efficiency Cu2ZnSn(S,Se)4 thin film solar cells fabricated by magnetron sputtering with enlarged depletion region width. Sol Energy Mater Sol Cells 149:242–249
Wang W, Winkler MT, Gunawan O, Gokmen T, Todorov TK, Zhu Y et al (2014) Device characteristics of CZTSSe thin-film solar cells with 12.6% efficiency. Adv Energy Mater 4:7
Lewis NS, Nocera DG (2006) Powering the planet: chemical challenges in solar energy utilization. Proc Natl Acad Sci U S A 103:15729–15735
Fthenakis V (2009) Sustainability of photovoltaics: the case for thin-film solar cells. Renew Sust Energ Rev 13:2746–2750
Wadia C, Alivisatos AP, Kammen DM (2009) Materials availability expands the opportunity for large-scale photovoltaics deployment. Environ Sci Technol 43:2072–2077
Yang RX, Butler KT, Walsh A (2015) Assessment of hybrid organic-inorganic antimony sulfides for earth-abundant photovoltaic applications. J Phys Chem Lett 6:5009
Darga A, Mencaraglia D, Longeaud C, Savenije TJ, O’Regan B, Bourdais S et al (2013) On charge carrier recombination in Sb2S3 and its implication for the performance of solar cells. J Phys Chem C 117:20525–20530
Versavel MY, Haber JA (2007) Structural and optical properties of amorphous and crystalline antimony sulfide thin-films. Thin Solid Films 515:7171–7176
Choi YC, Seok SI (2015) Efficient Sb2S3-sensitized solar cells via single-step deposition of Sb2S3 using S/Sb-ratio-controlled SbCl3-thiourea complex solution. Adv Funct Mater 25:2892–2898
Mane RS, Lokhande CD (2003) Thickness-dependent properties of chemically deposited Sb2S3 thin films. Materials Chemistry & Physics 82:347–354
Choi YC, Lee DU, Noh JH, Kim EK, Seok SI (2014) Highly improved Sb2S3 sensitized-inorganic–organic heterojunction solar cells and quantification of traps by deep-level transient spectroscopy. Adv Funct Mater 24:3587–3592
Escorcia-García J, Becerra D, Nair MTS, Nair PK (2014) Heterojunction CdS/Sb2S3 solar cells using antimony sulfide thin films prepared by thermal evaporation. Thin Solid Films 569:28–34
Yuan S, Deng H, Dong D, Yang X, Qiao K, Hu C et al (2016) Efficient planar antimony sulfide thin film photovoltaics with large grain and preferential growth. Sol Energy Mater Sol Cells 157:887–893
Zimmermann E, Pfadler T, Kalb J, Dorman JA, Sommer D, Hahn G et al (2015) Toward high-efficiency solution-processed planar heterojunction Sb2S3 solar cells. Adv Sci 2:5
Yuan S, Deng H, Yang X, Hu C, Khan J, Ye W et al (2017) Post-surface selenization for high performance Sb2S3 planar thin film solar cells. Acs Photonics 4:2862–2870
Kondrotas R, Chen C, Tang J (2018) Sb2S3 solar cells. Joule 5:857–878
Osorio Mayon Y, White TP, Wang R, Yang Z, Catchpole KR (2016) Evaporated and solution deposited planar Sb2S3 solar cells: a comparison and its significance. Phys Status Solidi 213:108–113
Contreras MA, Romero MJ, To B, Hasoon F, Noufi R, Ward S et al (2002) Optimization of CBD CdS process in high-efficiency Cu(In,Ga)Se2-based solar cells. Thin Solid Films 403:204–211
Tauc J, Grigorovici R, Vancu A (1966) Optical properties and electronic structure of amorphous germanium. Phys Status Solidi 15:627–637
Yang B, Qin S, Xue DJ, Chen C, He YS, Niu D et al (2017) In situ sulfurization to generate Sb2(Se1 -x Sx)3 alloyed films and their application for photovoltaics. Progress in Photovoltaics Research & Applications 25:113–122
Zhou Y, Wang L, Chen S, Qin S, Liu X, Chen J et al (2015) Thin-film Sb2Se3 photovoltaics with oriented one-dimensional ribbons and benign grain boundaries. Nat Photonics 9:409–415
Paul Weiss T, Redinger A, Luckas J, Mousel M, Siebentritt S (2013) Admittance spectroscopy in kesterite solar cells: defect signal or circuit response. Appl Phys Lett 102:512–519
Wang X, Li J, Liu W, Yang S, Zhu C, Chen T (2017) A fast chemical approach towards Sb2S3 film with a large grain size for high-performance planar heterojunction solar cells. Nanoscale 9:10
Song J, Zheng E, Wang XF, Tian W, Miyasaka T (2016) Low-temperature-processed ZnO-SnO2 nanocomposite for efficient planar perovskite solar cells. Sol Energy Mater Sol Cells 144:623–630
Funding
This work was supported by the National Natural Science Foundation of China (Grant Nos. 61505018,51503022, 21603020, and 21703124), Chongqing Science & Technology Commission (Grant Nos. cstc2015jcyjA50036, cstc2016jcyjys50001 and cstc2016jcyj0367), Basic and Frontier Research Program of Chongqing Municipality (cstc2016jcyjA0451), the research project for Chongqing University of Arts and Sciences (No. z2016xc16), and the Open Foundation of State Key Laboratory of Electronic Thin Films and Integrated Devices (No. kfjj201507).
Availability of Data and Materials
All data are fully available without restriction.
Author information
Authors and Affiliations
Contributions
KW carried out the experiments. KW and JC designed the experiments and prepared the manuscript. JC gave materials and equipment supporting. RH, XY, and JH participated in the work to analyze the data. LF helped to prepare the samples. LL and JY helped to revise the manuscript. All authors read and approved the final manuscript.
Corresponding author
Ethics declarations
Ethics Approval and Consent to Participate
Not applicable
Consent for Publication
Not applicable
Competing Interests
The authors declare that they have no competing interests.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Wang, K., Cheng, J., Yang, X. et al. Enhanced Photovoltaic Properties in Sb2S3 Planar Heterojunction Solar Cell with a Fast Selenylation Approach. Nanoscale Res Lett 13, 270 (2018). https://doi.org/10.1186/s11671-018-2651-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-018-2651-x